Name: synthesis of ionic liquid based electrolytes, assembly of li-ion batteries, and measurements of performance at high temperature
Uploaded: 2016-12-20T13:00:00
Description: Watch this Scientific Journal Video about Synthesis of Ionic Liquid Based Electrolytes, Assembly of Li-ion Batteries, and Measurements of Performance at High Temperature at JoVE.com

This article was supported in part by BU and by the Advanced Energy Consortium:

1.Synthesis of Mono- and Di-phosphonium Ionic Liquids Paired with Chloride (Cl) and Bis(trifluoromethane)sulfonimide (TFSI) Anions
NOTE: The procedure for the mono-phosphonium ionic liquid possessing three hexyl and one decyl alkyl chain surrounding the phosphonium cation is described, and this ionic liquid is abbreviated as mono-HexC10Cl. The same procedure is repeated using 1,10-dichlorodecane to obtain the di-phosphonium ionic liquid in high yield, and this ionic liquid is abbreviated as di-H...

<ol>
	<li>Armand, M., Tarascon, J. -. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Building+better+batteries.">Building better batteries.</a> Nature (London). 451, 652-657 (2008).</li><li>Linden, D., Reddy, T. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Handbook of batteries. , (2002).</li><li>Scrosati, B., Garche, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lithium+batteries:+Status,+prospects+and+future.">Lithium batteries: Status, prospects and future.</a> J. Power Sources. 195, 2419-2430 (2010).</li><li>Goodenough, J. B., Park, K. -. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Li-Ion+Rechargeable+Battery:+A+Perspective.">The Li-Ion Rechargeable Battery: A Perspective.</a> J. Am. Chem. Soc. 135, 1167-1176 (2013).</li><li>Scrosati, B., Hassoun, J., Sun, Y. -. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lithium-ion+batteries.+A+look+into+the+future.">Lithium-ion batteries. A look into the future.</a> Energ. Environ. Sci. 4, 3287-3295 (2011).</li><li>Tarascon, J. -. M., Armand, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Issues+and+challenges+facing+rechargeable+lithium+batteries.">Issues and challenges facing rechargeable lithium batteries.</a> Nature. 414, 359-367 (2001).</li><li>Goodenough, J. B., Kim, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Challenges+for+Rechargeable+Li+Batteries.">Challenges for Rechargeable Li Batteries.</a> Chem. Mater. 22, 587-603 (2010).</li><li>Etacheri, V., Marom, R., Elazari, R., Salitraa, G., Aurbach, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Challenges+in+the+development+of+advanced+Li-ion+batteries:+a+review.">Challenges in the development of advanced Li-ion batteries: a review.</a> Energ. Environ. Sci. 4, 3243-3262 (2011).</li><li>Feng, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermal+runaway+features+of+large+format+prismatic+lithium+ion+battery+using+extended+volume+accelerating+rate+calorimetry.">Thermal runaway features of large format prismatic lithium ion battery using extended volume accelerating rate calorimetry.</a> J. Power Sources. 255, 294-301 (2014).</li><li>Hammami, A., Raymond, N., Armand, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lithium-ion+batteries:+Runaway+risk+of+forming+toxic+compounds.">Lithium-ion batteries: Runaway risk of forming toxic compounds.</a> Nature. 424, 635-636 (2003).</li><li>Xu, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nonaqueous+liquid+electrolytes+for+lithium-based+rechargeable+batteries.">Nonaqueous liquid electrolytes for lithium-based rechargeable batteries.</a> Chem. Rev. 104, 4303-4417 (2004).</li><li>Ohno, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Electrochemical Aspects of Ionic Liquids. , (2005).</li><li>Wasserscheid, P., Welton, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Ionic Liquids in Synthesis. , (2003).</li><li>Wathier, M., Grinstaff, M. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+properties+of+supramolecular+ionic+networks.">Synthesis and properties of supramolecular ionic networks.</a> Journal of the American Chemical Society. 130, 9648-9649 (2008).</li><li>Gebresilassie Eshetu, G., Armand, M., Scrosati, B., Passerini, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Energy+storage+materials+synthesized+from+ionic+liquids.">Energy storage materials synthesized from ionic liquids.</a> Angew. Chem. Int. Ed. 53, 13342-13359 (2014).</li><li>Armand, M., Endres, F., MacFarlane, D. R., Ohno, H., Scrosati, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ionic-liquid+materials+for+the+electrochemical+challenges+of+the+future.">Ionic-liquid materials for the electrochemical challenges of the future.</a> Nat. Mater. 8, 621-629 (2009).</li><li>Xu, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrolytes+and+interphases+in+Li-ion+batteries+and+beyond.">Electrolytes and interphases in Li-ion batteries and beyond.</a> Chem. Rev. 114, 11503-11618 (2014).</li><li>Sakaebe, H., Matsumoto, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=N-Methyl-N-propylpiperidinium+bis(trifluoromethanesulfonyl)imide+(PP13-TFSI)+-+novel+electrolyte+base+for+Li+battery.">N-Methyl-N-propylpiperidinium bis(trifluoromethanesulfonyl)imide (PP13-TFSI) - novel electrolyte base for Li battery.</a> Electrochem. Commun. 5, 594-598 (2003).</li><li>Paillard, E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+and+Physicochemical+Properties+of+PY14FSI-Based+Electrolytes+with+LiFSI.">Electrochemical and Physicochemical Properties of PY14FSI-Based Electrolytes with LiFSI.</a> J. Electrochem. Soc. 156, A891-A895 (2009).</li><li>Tsunashima, K., Sugiya, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physical+and+electrochemical+properties+of+low-viscosity+phosphonium+ionic+liquids+as+potential+electrolytes.">Physical and electrochemical properties of low-viscosity phosphonium ionic liquids as potential electrolytes.</a> Electrochem. Commun. 9, 2353-2358 (2007).</li><li>Nakagawa, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Application+of+nonflammable+electrolyte+with+room+temperature+ionic+liquids+(RTILs)+for+lithium-ion+cells.">Application of nonflammable electrolyte with room temperature ionic liquids (RTILs) for lithium-ion cells.</a> J. Power Sources. 174, 1021-1026 (2007).</li><li>Fuller, J., Carlin, R. T., Osteryoung, R. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Room+Temperature+Ionic+Liquid+1-Ethyl-3-methylimidazolium+Tetrafluoroborate:+Electrochemical+Couples+and+Physical+Properties.">The Room Temperature Ionic Liquid 1-Ethyl-3-methylimidazolium Tetrafluoroborate: Electrochemical Couples and Physical Properties.</a> J. Electrochem. Soc. 144, 3881-3886 (1997).</li><li>Mun, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+stability+of+bis(trifluoromethanesulfonyl)imide-based+ionic+liquids+at+elevated+temperature+as+a+solvent+for+a+titanium+oxide+bronze+electrode.">Electrochemical stability of bis(trifluoromethanesulfonyl)imide-based ionic liquids at elevated temperature as a solvent for a titanium oxide bronze electrode.</a> J. Power Sources. 194, 1068-1074 (2009).</li><li>Garcia, B., Lavall&#233;e, S., Perron, G., Michot, C., Armand, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Room+temperature+molten+salts+as+lithium+battery+electrolyte.">Room temperature molten salts as lithium battery electrolyte.</a> Electrochim. Acta. 49, 4583-4588 (2004).</li><li>Lewandowski, A., &#346;widerska-Mocek, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ionic+liquids+as+electrolytes+for+Li-ion+batteries-an+overview+of+electrochemical+studies.">Ionic liquids as electrolytes for Li-ion batteries-an overview of electrochemical studies.</a> J. Power Sources. 194, 601-609 (2009).</li><li>Gali&#324;ski, M., Lewandowski, A., St&#281;pniak, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ionic+liquids+as+electrolytes.">Ionic liquids as electrolytes.</a> Electrochim. Acta. 51, 5567-5580 (2006).</li><li>Lin, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermally-responsive,+nonflammable+phosphonium+ionic+liquid+electrolytes+for+lithium+metal+batteries:+operating+at+100+degrees+celsius.">Thermally-responsive, nonflammable phosphonium ionic liquid electrolytes for lithium metal batteries: operating at 100 degrees celsius.</a> Chem. Sci. 6, 6601-6606 (2015).</li><li>Xu, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nonaqueous+Liquid+Electrolytes+for+Lithium-Based+Rechargeable+Batteries.">Nonaqueous Liquid Electrolytes for Lithium-Based Rechargeable Batteries.</a> Chem. Rev. 104, 4303-4418 (2004).</li><li>Armand, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polymer+solid+electrolytes-an+overview.">Polymer solid electrolytes-an overview.</a> Solid State Ionics. 9-10, 745-754 (1983).</li><li>Meyer, W. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polymer+electrolytes+for+lithium-ion+batteries.">Polymer electrolytes for lithium-ion batteries.</a> Adv. Mater. 10, 439-448 (1998).</li></ol>

Our approach to develop non-flammable and high temperature functional Li-ion batteries involves the synthesis of new ionic liquid electrolytes and their subsequent evaluation in prototypical coin cells. Specifically, mono-HexC10TFSI and di-HexC10TFSI based electrolytes were tested in a coin cell possessing a Li metal anode and LiCoO2 cathode. The critical steps within this approach are to: 1) identify the lead electrolyte according to a set of design specifications; 2) maintain dryness and ensure water does no...

Li-ion batteries are devices that transform energy between electrical energy and chemical energy and provide a convenient means to store and to deliver energy on demand and on-the-go. Today, Li-ion batteries dominate the portable electronics market because of their high energy density and re-chargeability, and are of interest for large-scale and specialty applications, such as down-hole drilling and automotive.1-5 Batteries are composed of four primary components: cathode, anode, separator, and electrolyte. While the chemistry of the two electrodes dictates the theoretical energy density of the battery, the safety and working temperature are mainly limited by the electrolyte material.6-9 Carbonate based organic solvent electrolytes (e.g., dimethyl carbonate (DMC) and ethylene carbonate (EC)) are widely used in Li-ion batteries due to their low viscosity, high conductivity, and high lithium salt solubility. Moreover, certain combinations of the carbonate solvents (DMC/EC) also form a stable solid electrolyte interface (SEI), thereby preventing degradation reactions between the electrolyte and the electrode, and extending battery life. However, carbonate solvents suffer from low boiling points and flash points, limiting the operation temperature of Li-ion batteries to below 55 &#176;C, with potentially severe safety issues when there is a short-circuit.10,11
Ionic liquids are a class of salts that have melting temperatures below 100 &#176;C.12 In contrast to typical inorganic salts, ionic liquids possess a wide liquid range and can be liquid at room temperature. Ionic liquids are composed of one or multiple organic cationic centers, such as imidazolium, phosphonium, pyridinium, or ammonium and paired with an inorganic or organic anion, such as methansulfonate, hexafluorophosphate, or halide.13,14 The wide variety of possible cation and anion combinations allows for a large number of compositions with tunable properties. In addition, the strong ionic interactions within ionic liquids result in negligible vapor pressure, non-flammability, and high thermal and electrochemical stability.15,16
Replacing conventional electrolytes with ionic liquids is one solution that addresses the inherent safety issues in current Li-ion batteries, and could enable high temperature applications.17-27 To illustrate the general synthetic and material processing methods utilized to construct lithium ion batteries containing ionic liquids for high temperature applications, we describe the synthesis, thermal properties, and electrochemical characterization of mono- and di-phosphonium ionic liquids paired with either the chloride (Cl) or bis(trifluoromethane)sulfonimide (TFSI) anion. Different concentrations of lithium bis(trifluoromethane)sulfonimide (LiTFSI) are subsequently added to the phosphonium ionic liquids to give electrolytes. Based on the performance of the phosphonium TFSI electrolytes with added LiTFSI compared to the chloride analogs, a coin cell is constructed with either the mono- or di-phosphonium TFSI electrolytes along with a Li metal anode and LiCoO2 cathode. Finally, battery performance is evaluated at 100 &#176;C for the two different coin cell batteries. The detailed procedures, the challenges in execution, and the insights gained from performing these experiments are described below.

<table border="0" cellpadding="0" cellspacing="0" width="653">
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Silicone oil</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td style="width:119px;">85409</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Potassium hydroxide</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td align="right" style="width:119px;">221473</td>
			<td>Corrosive</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Rotary evaporator</td>
			<td style="width:108px;">Buchi</td>
			<td style="width:119px;">R-124</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">High-vacuum pump</td>
			<td style="width:108px;">Welch</td>
			<td align="right" style="width:119px;">8907</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Nitrogen, ultra high purity</td>
			<td style="width:108px;">Airgas</td>
			<td style="width:119px;">NI UHP300</td>
			<td>Compressed gas</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Tetrahydrofuran, stabilized with BHT</td>
			<td style="width:108px;">Pharmaco-Aaper</td>
			<td align="right" style="width:119px;">346000</td>
			<td>Flammable. Dried through column of XXX</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Dichloromethane</td>
			<td style="width:108px;">Pharmaco-Aaper</td>
			<td align="right" style="width:119px;">313000</td>
			<td>Flammable, toxic.</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Separatory funnel (1 L)</td>
			<td style="width:108px;">Fisher Scientific</td>
			<td style="width:119px;">13-678-606</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Sodium sulfate</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td align="right" style="width:119px;">239313</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Ethanol, absolute</td>
			<td style="width:108px;">Pharmaco-Aaper</td>
			<td style="width:119px;">111USP200</td>
			<td>Flammable, toxic.</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Buchner funnel</td>
			<td style="width:108px;">Fisher Scientific</td>
			<td style="width:119px;">FB-966-F</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Methanol</td>
			<td style="width:108px;">Pharmaco-Aaper</td>
			<td style="width:119px;">339000ACS</td>
			<td>Flammable, toxic.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Triethylamine (anhydrous)</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td align="right" style="width:119px;">471283</td>
			<td>Toxic, flammable, harmful to environment</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Glass syringe</td>
			<td style="width:108px;">Hamilton Company</td>
			<td style="width:119px;">1700-series</td>
			<td></td>
		</tr>
		<tr height="84">
			<td height="84" style="height:84px;width:259px;">Deuterated chloroform</td>
			<td style="width:108px;">Cambridge Isotopes Laboratories, Inc.</td>
			<td style="width:119px;">DLM-29-10</td>
			<td>Toxic</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Nuclear magnetic resonance instrument</td>
			<td style="width:108px;">Varian</td>
			<td style="width:119px;">V400</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Hydrogen</td>
			<td style="width:108px;">Airgas</td>
			<td style="width:119px;">HY HP300</td>
			<td>Highly flammable.</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Hexanes</td>
			<td style="width:108px;">Pharmaco-Aaper</td>
			<td style="width:119px;">359000ACS</td>
			<td>Toxic, flammable.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Differential scanning calorimeter</td>
			<td style="width:108px;">TA Instruments</td>
			<td style="width:119px;">Q100</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">N,N-dimethylformamide</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td align="right" style="width:119px;">227056</td>
			<td>Toxic, flammable.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Trihexylphosphone</td>
			<td style="width:108px;">TCI America</td>
			<td style="width:119px;"></td>
			<td>Toxic, flammable.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">1-Chlorodecane</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td style="width:119px;"></td>
			<td>Toxic, flammable.</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Bis(trifluoromethane)sulfonimide lithium salt</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td style="width:119px;"></td>
			<td>Hydrophilic</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">1, 10-dichlorodecane</td>
			<td style="width:108px;">Sigma-Aldrich</td>
			<td style="width:119px;"></td>
			<td>Toxic, flammable.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Thermal Gravemetric Analysis (TGA)</td>
			<td style="width:108px;">TA Q50</td>
			<td style="width:119px;">TA instruments</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Differential scanning calorimeter (DSC)</td>
			<td style="width:108px;">TA Q100</td>
			<td style="width:119px;">TA instruments</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Controlled Strain Rheometer</td>
			<td style="width:108px;">AR 1000&#160;</td>
			<td style="width:119px;"></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Conductivity Meter&#160;</td>
			<td style="width:108px;">Consort</td>
			<td style="width:119px;">K912</td>
			<td>4-electrode cell</td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;">Potentiostate/Galvanostat</td>
			<td style="width:108px;">Princeton Applied Research&#160;</td>
			<td style="width:119px;">VersaStat MC4&#160;</td>
			<td style="width:167px;">Electrochemical testing</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;">Separators&#160;</td>
			<td style="width:108px;">Celgard&#160;</td>
			<td style="width:119px;">C480&#160;</td>
			<td style="width:167px;">polypropylene/polyethylene</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;">CR2032 coin cells</td>
			<td style="width:108px;">MTI Corp.</td>
			<td style="width:119px;">EQ-CR2032-CASE</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="25">
			<td height="25" style="height:25px;">LiCoO2 electrode&#160;</td>
			<td style="width:108px;">MTI Corp.</td>
			<td style="width:119px;">EQ-CR2032</td>
			<td style="width:167px;">Cathode material</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">lithium metal&#160;</td>
			<td style="width:108px;">Alfa Aesar</td>
			<td align="right" style="width:119px;">10769</td>
			<td style="width:167px;">Anode Material</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Stainless Steel Spacer</td>
			<td style="width:108px;">MTI Corp.</td>
			<td style="width:119px;">EQ-CR20-Spacer304-02</td>
			<td style="width:167px;">15.5 mm Dia x 0.2 mm</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Wave Spring</td>
			<td style="width:108px;">MTI Corp.</td>
			<td style="width:119px;">EQ-CR20WS-Spring304</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:259px;">Electric Coin Cell Crimping Machine</td>
			<td style="width:108px;">MTI Corp.</td>
			<td style="width:119px;">MSK-160D</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:259px;">Glove box</td>
			<td style="width:108px;">Mbraun</td>
			<td style="width:119px;"></td>
			<td style="width:167px;">Water free, oxygen free operation</td>
		</tr>
	</tbody>
</table>

synthesis of ionic liquid based electrolytes, assembly of li-ion batteries, and measurements of performance at high temperature

The chemical instability of the traditional electrolyte remains a safety issue in widely used energy storage devices such as Li-ion batteries. Li-ion batteries for use in devices operating at elevated temperatures require thermally stable and non-flammable electrolytes. Ionic liquids (ILs), which are non-flammable, non-volatile, thermally stable molten salts, are an ideal replacement for flammable and low boiling point organic solvent electrolytes currently used today. We herein describe the procedures to: 1) synthesize mono- and di-phosphonium ionic liquids paired with chloride or bis(trifluoromethane)sulfonimide (TFSI) anions; 2) measure the thermal properties and stability of these ionic liquids by differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA); 3) measure the electrochemical properties of the ionic liquids by cyclic voltammetry (CV); 4) prepare electrolytes containing lithium bis(trifluoromethane)sulfonamide; 5) measure the conductivity of the electrolytes as a function of temperature; 6) assemble a coin cell battery with two of the electrolytes along with a Li metal anode and LiCoO2 cathode; and 7) evaluate battery performance at 100 &#176;C. We additionally describe the challenges in execution as well as the insights gained from performing these experiments.

The ionic liquids, mono-HexC10Cl and di-HexC10Cl, were prepared via a nucleophilic reaction, and a subsequent halide exchange reaction gave the mono-HexC10TFSI and di-HexC10TFSI ionic liquids, respectively (Figure 1A).14 All four ionic liquids were colorless and slightly viscous liquids (Figure 1B). A representative 1H NMR of the mono-HexC10TFSI ionic liquid is shown in Figure 1C, and along with mass spectrometry and...

Watch this Scientific Journal Video about Synthesis of Ionic Liquid Based Electrolytes, Assembly of Li-ion Batteries, and Measurements of Performance at High Temperature at JoVE.com

Synthesis of Ionic Liquid Based Electrolytes, Assembly of Li-ion Batteries, and Measurements of Performance at High Temperature

Here, we describe protocols to prepare phosphonium-based ionic liquid and lithium bis(trifluoromethane)sulfonimide salt electrolytes, and assemble a non-flammable and high temperature functioning lithium-ion coin cell battery.

The chemical instability of the traditional electrolyte remains a safety issue in widely used energy storage devices such as Li-ion batteries. Li-ion ...

The overall goal of this procedure is to assemble a high-temperature functioning lithium ion battery that utilizes a non-flammable, thermally stable phosphonium-based ion liquid electrolyte containing lithium bis trifluoromethane sulfonamide. This method addresses key challenges in a high temperature energy storage field, specifically the safety issues with the use of conventional electrolytes in lithium ion batteries. The main advantage of this technique is that it provides an approach to synthesize and characterize thermally stable electrolytes and to construct high temperature functioning lithium ion batteries.Though this method provides insight into rational design bionic liquid electrolytes optimized for lithium ion batteries, it can also be applied to super capacitors and other energy storage devices. Generally, individuals new to this method struggle because the measurements will be taken under inert atmosphere with extremely dry materials. Visual demonstration of this method is critical as introduction of bionic liquids in the batteries is challenging due to their high viscosities.In an argon-filled glove box, use glass pipettes to dispense 8.3 grams of trihexyl phosphene and 5.22 grams of 1-chlorodecane into an oven-dried heavy wall pressure vessel containing a stir bar. Cap the vessel with a PTFE bushing and stir the mixture under argon at 140 degrees Celsius for 24 hours. Remove volatiles under vacuum at 140 degrees to obtain crude mono-hexe-10-chloride.Extract the mono-hexe-10-chloride into DCM three times with ten milliliter portions of a one to one mixture of DCM and brine. Remove volatiles from the DCM phase to isolate the mono-hexe-10-chloride product. Next, dissolve 6.25 grams of lithium TFSI in ten milliliters of deionized water.Then, dissolve 7.75 grams of mono-hexe-10-chloride in ten milliliters of DCM. Add the TFSI solution. Cap the container and stir the mixture at room temperature for 24 hours to obtain crude mono-hexe-10-TFSI.Extract the mono-hexe-10-TFSI into 20 milliliters of DCM three times. Test for the presence of chloride by adding one to two drops of one normal silver nitrate solution to one milliliter of the DCM phase. Repeat the extraction if silver chloride is observed as a white precipitate.Then, dry the mono-hexe-10-TFSI solution with one gram of anhydrous magnesium sulfate. Decant the dried solution and remove the solvent with a rotary evaporator to isolate the product. To synthesize the di-phosphonium analogues follow this procedure using 1, 10-dichlorodecane and appropriately adjust its molar ratios.To perform viscosity measurements, set up a controlled strain rheometer in a nitrogen gas-filled glove bag. Place one milliliter of the ionic liquid onto the Peltier stage of the rheometer ensuring that the aluminium plate is fully covered. Set the gap between the sample and a parallel 20 millimeter diameter aluminium plate to be one to two millimeters in all of the test runs.Pre-shear the sample at a shear rate of 100 Hertz for ten seconds and then perform a 15 minute equilibrium step. Then, determine the linear visco-elastic region or LVR with an oscillatory strain sweep at a fixed frequency of one Hertz with a strain amplitude from 0.1 to ten percent. Select a strain within the LVR and perform an oscillatory frequency sweep from 0.1 to ten Hertz.Determine the complex viscosity at a chosen frequency and strain. Then, at that frequency and strain, perform an oscillatory temperature sweep from ten to 95 degrees Celsius at five degree increments with one minute of equilibrium at each temperature. To measure the sample conductivity, first dry the ionic liquid at 100 degrees Celsius under vacuum for 12 hours.Place about four milliliters of the ionic liquid in a test tube. Insert the conductivity probe and add more sample as needed to cover the probe sensor completely. Heat the sample to the first measurement temperature while stirring.Equilibrate the sample at that temperature for 30 minutes and then take the conductivity reading. Repeat this process for each temperature point. Next, set up a lithium-lithium platinum three electrode cyclic voltammetry assembly in the glove box.Place the ionic liquid in the CV chamber, immerse the electrodes in the liquid and ensure that the chamber is sealed. Equilibrate the sample at the first measurement temperature for 20 minutes and then sweep the potential at a rate of one millivolt per second between negative 0.2 volts and 6.5 volts. First is the lithium ion lithium reference potential.Repeat this measurement for each desired temperature. Prior to beginning the battery fabrication, dry the lithium TFSI for three days in a vacuum oven at 70 degrees Celsius. Dry the ionic liquid to be tested under high vacuum at 100 degrees Celsius for 24 hours while stirring vigorously.Bring both dry liquids and an oven-dried flask and stir bar into a glove box. Place 6.4 millimoles each of the ionic liquid and lithium TFSI in the flask. Stir the mixture overnight to obtain a homogenous mixture with a 1.6 molar electrolyte concentration.Dry the coin cell hardware components and a 12.7 millimeter diameter lithium cobalt oxide electrode at 70 degrees Celsius overnight before transferring them to the glove box. Place one spring and stainless steel disk in the coin cell bottom cap. Place the electrode in the steel disk.Heat the electrolyte mixture to 60 degrees Celsius on a hot plate and soak two polypropylene membrane separators in the mixture while stirring for 15 minutes. Cover the surface of the lithium cobalt oxide cathode with about 0.5 milliliters of the electrolyte mixture and then place both separators in the center of the coin cell. Place a few drops of the electrolyte mixture on top of the separators, ensuring that all crevices in the cell are filled.Heat the electrolyte-covered cathode to 60 degrees Celsius for 15 minutes. Cut out a 12.7 millimeter diameter piece of 0.75 millimeter thick lithium metal and place the metal onto the electrolyte-soaked separators. Cap the coin cell and seal it with a crimper.Remove the cell from the glove box and allow the cell to sit for 12 hours. To test the battery performance at high temperatures, thread cables from an electrochemical testing station to the back wall of an oven. Connect the coin cell to the testing station in the oven and leave the cell in the oven for 30 minutes to equilibrate to the oven temperature.At the testing station, select galvanostatic charge-discharge cycling and set the cycle number to 500. Set the charge and discharge parameters and rest times and then start the charge-discharge cycling to evaluate charge output over time. Four phosphonium based ionic liquids were evaluated for use in lithium ion batteries at high temperatures.Thermogravimetric analysis showed that the decomposition temperatures ranged from 340 to 385 degrees Celsius. The TFSI-based ionic liquids were less viscous making them better suited for completely filling pores and crevices in the battery components. Cyclic voltammetry measurements of mono and di-hexC10TFSI with lithium-TFSI in the presence of the lithium cobalt oxide cathode showed the expected lithium cobalt oxide redox peaks.For both liquids, the current increased significantly with temperature. The mono-hexC10TFSI mixture showed a higher current response to all temperatures. Charge-discharge cycling tests of coin cell batteries containing mono-hexC10TFSI at 100 degrees Celsius showed the battery capacity decay was rapid at low concentrations of lithium TFSI.At concentrations nearer the saturation point, the capacity decay was reduced to about ten percent after 20 cycles. An extended galvanostatic charge-discharge cycling test of a coin cell battery containing 1.6 molar TFSI and mono-hexC10TFSI was performed at 100 degrees Celsius. The battery capacity was initially about 135 milliampere hours per gram.After one month, the capacity had decreased to 70 milliampere hours per gram. While attempting this procedure, it's important to thoroughly dry all components of the battery such as the electrolyte and electrodes prior to cell assembly. Moreover, when assembling the coin cell, care must be taken to coat the cathode and separator with the electrolytes.After watching this video, you should be able to synthesize ionic liquid electrolytes and fabricate lithium ion batteries. Care must be taken when handling the ionic liquids since their high viscosities pose additional handling challenges compared to standard electrolytes.

Research

JoVE Journal

Engineering

Construction and Testing of Coin Cells of Lithium Ion Batteries

Rechargeable lithium ion batteries have wide applications in electronics, where customers always demand more capacity and longer lifetime.  Lithium ion ...

Characterization of Electrode Materials for Lithium Ion and Sodium Ion Batteries Using Synchrotron Radiation Techniques

Intercalation compounds such as transition metal oxides or phosphates are the most commonly used electrode materials in Li-ion and Na-ion batteries. ...

Synthesis and Microdiffraction at Extreme Pressures and Temperatures

High pressure compounds and polymorphs are investigated for a broad range of purposes such as determine structures and processes of deep planetary ...

Selective Area Modification of Silicon Surface Wettability by Pulsed UV Laser Irradiation in Liquid Environment

The wettability of silicon (Si) is one of the important parameters in the technology of surface functionalization of this material and fabrication of ...

Research and Development of High-performance Explosives

Developmental testing of high explosives for military applications involves small-scale formulation, safety testing, and finally detonation performance ...

Failure Analysis of Batteries Using Synchrotron-based Hard X-ray Microtomography

Imaging morphological changes that occur during the lifetime of rechargeable batteries is necessary to understand how these devices fail. Since the advent ...

A High Performance Impedance-based Platform for Evaporation Rate Detection

This paper describes the method of a novel impedance-based platform for the detection of the evaporation rate. The model compound hyaluronic acid was ...

Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way

To improve the accuracy of the chloride distribution along the depth of cement paste under cyclic wet-dry conditions, a new method is proposed to obtain a ...

Developing High Performance GaP/Si Heterojunction Solar Cells

To improve the efficiency of Si-based solar cells beyond their Shockley-Queisser limit, the optimal path is to integrate them with III-V-based solar ...

Determination of Aggregate Surface Morphology at the Interfacial Transition Zone (ITZ)

Determination of Aggregate Surface Morphology at the Interfacial Transition Zone ITZ

Here, we present a comprehensive method to illustrate the uneven distribution of the interfacial transition zone (ITZ) around the aggregate and the effect ...