Name: layer-by-layer synthesis and transfer of freestanding conjugated microporous polymer nanomembranes
Uploaded: 2015-12-15T13:00:00
Description: Watch this Scientific Journal Video about Layer-by-layer Synthesis and Transfer of Freestanding Conjugated Microporous Polymer Nanomembranes at JoVE.com

The authors have no acknowledgements.

1. Synthesis of CMP Thin Films through Sequential Addition
<ol>
	<li>Self-assembled monolayer (SAM) functionalization of gold on mica.
	<ol>
		<li>Prepare 1 mM solution of 11-thioacetyl-undecane acid-propargyl amide14 in ethanol (SAM-solution). Mix using ultrasonic bath till solution is clear. Protect the bottle from light using aluminum foil.</li>
		<li>Obtain gold coated mica wafer under argon. After withdrawal from the storage container immerse the mica wafer directly to the SAM-solution for 18 hr...

<ol>
	<li>Lindemann, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+of+Freestanding+Conjugated+Microporous+Polymer+Nanomembranes+for+Gas+Separation.">Preparation of Freestanding Conjugated Microporous Polymer Nanomembranes for Gas Separation.</a> Chemistry of Materials. 26 (24), 7193-71 (2014).</li><li>Kim, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+of+Ultrathin+Films+of+Molecular+Networks+through+Layer-by-Layer+Cross-Linking+Polymerization+of+Tetrafunctional+Monomers.">Preparation of Ultrathin Films of Molecular Networks through Layer-by-Layer Cross-Linking Polymerization of Tetrafunctional Monomers.</a> Macromolecules. 44 (18), 7092-7095 (2011).</li><li>Vonh&#246;ren, B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ultrafast+Layer-by-Layer+Assembly+of+Thin+Organic+Films+Based+on+Triazolinedione+Click+Chemistry.">Ultrafast Layer-by-Layer Assembly of Thin Organic Films Based on Triazolinedione Click Chemistry.</a> ACS Macro Letters. 4 (3), 331-334 (2015).</li><li>Shekhah, O., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Step-by-Step+Route+for+the+Synthesis+of+Metal&#8722;Organic+Frameworks.">Step-by-Step Route for the Synthesis of Metal&#8722;Organic Frameworks.</a> Journal of the American Chemical Society. 129 (49), 15118-15119 (2007).</li><li>Shekhah, O., Wang, H., Zacher, D., Fischer, R. A., W&#246;ll, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Growth+Mechanism+of+Metal&#8211;Organic+Frameworks:+Insights+into+the+Nucleation+by+Employing+a+Step-by-Step+Route.">Growth Mechanism of Metal&#8211;Organic Frameworks: Insights into the Nucleation by Employing a Step-by-Step Route.</a> Angewandte Chemie International Edition. 48 (27), 5038-5041 (2009).</li><li>Shekhah, O., Liu, J., Fischer, R. A., W&#246;ll, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=MOF+thin+films:+existing+and+future+applications.">MOF thin films: existing and future applications.</a> Chemical Society Reviews. 40 (2), 1081-1106 (2011).</li><li>Liu, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Deposition+of+Metal-Organic+Frameworks+by+Liquid-Phase+Epitaxy:+The+Influence+of+Substrate+Functional+Group+Density+on+Film+Orientation.">Deposition of Metal-Organic Frameworks by Liquid-Phase Epitaxy: The Influence of Substrate Functional Group Density on Film Orientation.</a> Materials. 5 (9), 1581-1592 (2012).</li><li>Such, G. K., Quinn, J. F., Quinn, A., Tjipto, E., Caruso, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Assembly+of+Ultrathin+Polymer+Multilayer+Films+by+Click+Chemistry.">Assembly of Ultrathin Polymer Multilayer Films by Click Chemistry.</a> Journal of the American Chemical Society. 128 (29), 9318-9319 (2006).</li><li>Ai, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+Nanomembranes+(CNMs)+Supported+by+Polymer:+Mechanics+and+Gas+Permeation.">Carbon Nanomembranes (CNMs) Supported by Polymer: Mechanics and Gas Permeation.</a> Advanced Materials. 26 (21), 3421-3426 (2014).</li><li>Jiang, J. -. X., Cooper, A. I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=in+Functional+Metal-Organic+Frameworks:+Gas+Storage,+Separation+and+Catalysis.">in Functional Metal-Organic Frameworks: Gas Storage, Separation and Catalysis.</a> Topics in Current Chemistry. (ed Martin Schr&#246;der) Ch. 293, 1-33 (2010).</li><li>Dawson, R., Cooper, A. I., Adams, D. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanoporous+organic+polymer+networks.">Nanoporous organic polymer networks.</a> Progress in Polymer Science. 37 (4), 530-563 (2012).</li><li>Muller, T., Br&#228;se, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Click+Chemistry+Finds+Its+Way+into+Covalent+Porous+Organic+Materials.">Click Chemistry Finds Its Way into Covalent Porous Organic Materials.</a> Angewandte Chemie International Edition. 50 (50), 11844-11845 (2011).</li><li>Tsotsalas, M., Addicoat, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Covalently+linked+organic+networks.">Covalently linked organic networks.</a> Frontiers in Materials. 2, (2015).</li><li>Kleinert, M., Winkler, T., Terfort, A., Lindhorst, T. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+modular+approach+for+the+construction+and+modification+of+glyco-SAMs+utilizing+1,3-dipolar+cycloaddition.">A modular approach for the construction and modification of glyco-SAMs utilizing 1,3-dipolar cycloaddition.</a> Organic &amp; Biomolecular Chemistry. 6 (12), 2118-2132 (2008).</li><li>Plietzsch, O., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Four-fold+click+reactions:+Generation+of+tetrahedral+methane-+and+adamantane-based+building+blocks+for+higher-order+molecular+assemblies.">Four-fold click reactions: Generation of tetrahedral methane- and adamantane-based building blocks for higher-order molecular assemblies.</a> Organic &amp; Biomolecular Chemistry. 7, (2009).</li><li>Greenler, R. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Infrared+Study+of+Adsorbed+Molecules+on+Metal+Surfaces+by+Reflection+Techniques.">Infrared Study of Adsorbed Molecules on Metal Surfaces by Reflection Techniques.</a> The Journal of Chemical Physics. 44 (1), (1966).</li></ol>

For the synthesis of the CMP-film the solution of the catalyst has to be fresh. A broken catalyst (i.e., oxidized) is indicated by a blue coloration of the solution. The fresh solution is colorless.
A crucial point is to cut the edges of the mica substrate after spin coating PMMA. Also defects in the substrate should be cut, i.e., each spot were the PMMA can come in contact with the mica substrate, because of a missing gold layer. Otherwise the gold layer cannot be stripped o...

The preparation of ultra-thin polymer membranes is of high interest for applications in gas separation and nanofiltration. Challenges in the synthesis are represented by (a) the control of the membrane thickness and the homogeneity and (b) transfer of such fragile membranes. To overcome challenge (a), molecular layer-by-layer synthesis1 has shown great promise in controlling the thickness and homogeneity of thin films grown at the solid-liquid interface.2,3 Controlling the number of layers linearly controls the film thickness. The l-b-l method has been successfully used to fabricate surface mounted metal organic frameworks (SURMOFs),4-7 also the synthesis of thin polymer films via l-b-l reaction of polymer chains was demonstrated.8 The challenge (b) concerns the handling of these ultra-thin membranes. To avoid rupture or wrinkling of the nanomembranes sacrificial supports of coatings have shown great promise. 9
Here we will present a detailed protocol for synthesis of conjugated microporous polymer (CMP)10-13 thin films through sequential addition of the molecular building blocks, with desired thickness and composition. The preparation of free-standing CMP nanomembranes is achieved by using a sacrificial support. To handle and transfer the CMP nanomembranes to other supports we will describe a simple protocol to protect the membranes with sacrificial coatings and their upfloating to the liquid air interface and subsequent transfer using dip-coating.

<table>
	<tbody>
		<tr>
			<td>Acetone</td>
			<td>VWR BDH Prolabo</td>
			<td>20066.330</td>
			<td>AnalR NORMAPUR</td>
		</tr>
		<tr>
			<td>Potassium iodide</td>
			<td>VWR BDH Prolabo</td>
			<td>26846.292</td>
			<td>AnalR NORMAPUR</td>
		</tr>
		<tr>
			<td>Ethyl acetate</td>
			<td>VWR BDH Prolabo</td>
			<td>23882.321</td>
			<td>AnalR NORMAPUR</td>
		</tr>
		<tr>
			<td>Tetrahydrofurane (THF)</td>
			<td>VWR BDH Prolabo</td>
			<td>28559.320</td>
			<td>HiPerSolv CHROMANORM</td>
		</tr>
		<tr>
			<td>THF waterfree</td>
			<td>Merck Millipore</td>
			<td>1.08107.1001</td>
			<td>SeccoSolv</td>
		</tr>
		<tr>
			<td>Iodine</td>
			<td>Sigma-Aldrich</td>
			<td>20,777-2</td>
			<td></td>
		</tr>
		<tr>
			<td>Tetrakis(acetonitrile)copper(I)hexafluoro-phosphate</td>
			<td>Sigma-Aldrich</td>
			<td>346276-5G</td>
			<td></td>
		</tr>
		<tr>
			<td>Poly(methyl methacrylate) 996 kDa (PMMA)</td>
			<td>Sigma-Aldrich</td>
			<td>182265-25G</td>
			<td></td>
		</tr>
		<tr>
			<td>1.1.1.1 Methanetetrayltetrakis(4-azidobenzene) (TPM-azide)</td>
			<td></td>
			<td></td>
			<td>provided by AK Prof. Br&#228;se. Institute of organic chemistry, Karlsruhe Institute of Technology. Synthesized according to9</td>
		</tr>
		<tr>
			<td>1.1.1.1 Methanetetrayltetrakis(4-ethinylenebenzene) (TPM-alkyne)</td>
			<td></td>
			<td></td>
			<td>provided by AK Prof. Br&#228;se. Institute of organic chemistry, Karlsruhe Institute of Technology. Synthesized according to9</td>
		</tr>
		<tr>
			<td>11-thioacetyl-undecaneacid propargylamide</td>
			<td></td>
			<td></td>
			<td>provided by AK Prof. Br&#228;se. Institute of organic chemistry, Karlsruhe Institute of Technology. Synthesized according to8</td>
		</tr>
		<tr>
			<td>gold/titan coated silicium-wafer</td>
			<td>Georg Albert PVD, 76857 Silz, Germany</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>gold coated mica</td>
			<td>Georg Albert PVD, 76857 Silz, Germany</td>
			<td></td>
			<td></td>
		</tr>
	</tbody>
</table>

layer-by-layer synthesis and transfer of freestanding conjugated microporous polymer nanomembranes

CMP as large surface area materials have attracted growing interest recently, due to their high variability in the incorporation of functional groups in combination with their outstanding thermal and chemical stability, and low densities. However, their insoluble nature causes problems in their processing since usually applied techniques such as spin coating are not available. Especially for membrane applications, where the processing of CMP as thin films is desirable, the processing problems have hindered their commercial application.
Here we describe the interfacial synthesis of CMP thin films on functionalized substrates via molecular layer-by-layer (l-b-l) synthesis. This process allows the preparation of films with desired thickness and composition and even desired composition gradients.
The use of sacrificial supports allows the preparation of freestanding membranes by dissolution of the support after the synthesis. To handle such ultra-thin freestanding membranes the protection with sacrificial coatings showed great promise, to avoid rupture of the nanomembranes. To transfer the nanomembranes to the desired substrate, the coated membranes are upfloated at the air-liquid interface and then transferred via dip coating.

The membranes are characterized by infrared reflection absorption spectroscopy (IRRAS).16 Figure 4 shows IRRA-spectra from a CMP-membrane transferred to a gold wafer. Typical bands from the vibrations of the aromatic backbone are at 1,605 cm-1, 1,515 cm-1 and 1,412 cm-1. Unreacted alkyne and azide groups can be observed by characteristic bands at 2,125 cm-1 and 1,227 cm-1. Figure 5 shows a scanning electron microscopy (SEM...

Watch this Scientific Journal Video about Layer-by-layer Synthesis and Transfer of Freestanding Conjugated Microporous Polymer Nanomembranes at JoVE.com

Layer-by-layer Synthesis and Transfer of Freestanding Conjugated Microporous Polymer Nanomembranes

In this paper we describe the interfacial synthesis of conjugated microporous polymers (CMP) on sacrificial substrates, and the dissolution of the substrate for the preparation of freestanding CMP nanomembranes. In addition, we will describe how the fragile nanomembranes can be transferred to other substrates.

CMP as large surface area materials have attracted growing interest recently, due to their high variability in the incorporation of functional groups in ...

Research

JoVE Journal

Chemistry

Confocal Imaging of Confined Quiescent and Flowing Colloid-polymer Mixtures

The behavior of confined colloidal suspensions with attractive interparticle interactions is critical to the rational design of materials for directed ...

Fabrication of Large-area Free-standing Ultrathin Polymer Films

This procedure describes a method for the fabrication of large-area and ultrathin free-standing polymer films.  Typically, ultrathin films are prepared ...

Preparation of Highly Porous Coordination Polymer Coatings on Macroporous Polymer Monoliths for Enhanced Enrichment of Phosphopeptides

We describe a protocol for the preparation of hybrid materials based on highly porous coordination polymer coatings on the internal surface of macroporous ...

Photodynamic Therapy with Blended Conducting Polymer/Fullerene Nanoparticle Photosensitizers

In this article a method for the fabrication and reproducible in-vitro evaluation of conducting polymer nanoparticles blended with fullerene as the next ...

The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry

A method for using Diels Alder thermo-reversible chemistry as cross-linking tool for rubber products is demonstrated. In this work, a commercial ...

Monitoring the Effects of Illumination on the Structure of Conjugated Polymer Gels Using Neutron Scattering

We demonstrate a protocol to effectively monitor the gelation process of a high concentration solution of conjugated polymer both in the presence and ...

Microfluidic Dry-spinning and Characterization of Regenerated Silk Fibroin Fibers

The protocol demonstrates a method for mimicking the spinning process of silkworm. In the native spinning process, the contracting spinning duct enables ...

Time-resolved Photophysical Characterization of Triplet-harvesting Organic Compounds at an Oxygen-free Environment Using an iCCD Camera

Here, we present a sensible method of the acquisition and analysis of time-resolved photoluminescence using an ultrafast iCCD camera. This system enables ...

Raman and IR Spectroelectrochemical Methods as Tools to Analyze Conjugated Organic Compounds

In the presented work, two spectroelectrochemical techniques are discussed as tools for the analysis of the structural changes occurring in the molecule ...