Name: preparation and testing of plant seed meal-based wood adhesives
Uploaded: 2015-03-05T15:00:00
Description: Watch this Scientific Journal Video about Preparation and Testing of Plant Seed Meal-based Wood Adhesives at JoVE.com

Data reported in this work are part of the USDA-ARS National Program 306 Project 'Values-Added Products from Cottonseed' research supported by the Agency's in-house funding. Publication of this paper is supported in part by the Journal of Visualized Experiments. Mention of trade names or commercial products in this publication is solely for the purpose of providing specific information and does not imply recommendation or endorsement by the U.S. Department of Agriculture. USDA is an equal opportunity provider and employer. We acknowledge the constructive comments from JoVE science editor and peer reviewers in the review and revision process.

1. Cottonseed and Soy Meal-based Products (Figure 1)
<ol>
	<li>Obtain the raw materials, defatted cottonseed and soy meals, from commercially available sources.</li>
	<li>Obtain the working meal by grinding the solid defatted meal in a cyclone sample mill to pass a 0.5 mm steel screen16.</li>
	<li>Prepare water washed meals from the working meals after water extraction (25 g meal:200 ml water) to separate water soluble components in the meals21.</li>
	<li>Prepare protein isolates from the working ...

<ol>
	<li>Frihart, C. R., Hunt, C. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Wood Handbook: wood as an engineering material: General technical report FPL; GTR-190. , (2010).</li><li>Lambuth, A. L., Pizza, A., Mittal, K. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Handbook of Adhesive Technology. , 457-478 (2003).</li><li>Kalapathy, U., Hettiarachchy, N. S., Myers, D., Hanna, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Modification+of+soy+proteins+and+their+adhesive+properties+on+woods.">Modification of soy proteins and their adhesive properties on woods.</a> J. Am. Oil Chem. Soc. 72 (5), 507-510 (1995).</li><li>Li, K., Peshkova, S., Geng, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Investigation+of+soy+protein-Kymene+adhesive+systems+for+wood+composites.">Investigation of soy protein-Kymene adhesive systems for wood composites.</a> J. Am. Oil Chem. Soc. 81 (5), 487-491 (2004).</li><li>Qi, G., Li, N., Wang, D., Sun, X. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adhesion+and+physicochemical+properties+of+soy+protein+modified+by+sodium+bisulfite.">Adhesion and physicochemical properties of soy protein modified by sodium bisulfite.</a> J. Am. Oil Chem. Soc. 90 (12), 1917-1926 (2013).</li><li>Cheng, H. N., Dowd, M. K., He, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Investigation+of+modified+cottonseed+protein+adhesives+for+wood+composites.">Investigation of modified cottonseed protein adhesives for wood composites.</a> Ind. Crop. Prod. 46, 399-403 (2013).</li><li>Pan, Z., Cathcart, A., Wang, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermal+and+chemical+treatments+to+improve+adhesive+property+of+rice+bran.">Thermal and chemical treatments to improve adhesive property of rice bran.</a> Ind. Crop. Prod. 22 (3), 233-240 (2005).</li><li>Nordqvist, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Wheat+gluten+fractions+as+wood+adhesives-glutenins+versus+gliadins.">Wheat gluten fractions as wood adhesives-glutenins versus gliadins.</a> J. Appl. Polymer Sci. 123 (3), 1530-1538 (2012).</li><li>Bandara, N., Chen, L., Wu, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adhesive+properties+of+modified+triticale+distillers+grain+proteins.">Adhesive properties of modified triticale distillers grain proteins.</a> Int. J. Adhes. Adhes. 44, 122-129 (2013).</li><li>Li, N., Qi, G., Sun, X. S., Stamm, M. J., Wang, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physicochemical+properties+and+adhesion+performance+of+canola+protein+modified+with+sodium+bisulfite.">Physicochemical properties and adhesion performance of canola protein modified with sodium bisulfite.</a> J. Am. Oil Chem. Soc. 89 (5), 897-908 (2012).</li><li>Wang, C., Wu, J., Bernard, G. M., Wasylishen, R. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+characterization+of+canola+protein+isolate+-poly(glycidyl+methacrylate)+conjugates:+a+bio-based+adhesive.">Preparation and characterization of canola protein isolate -poly(glycidyl methacrylate) conjugates: a bio-based adhesive.</a> Ind. Crop. Prod. 57, 124-131 (2014).</li><li>Kong, X., Liu, G., Curtis, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+of+canola+oil+based+polyurethane+wood+adhesives.">Characterization of canola oil based polyurethane wood adhesives.</a> Int. J. Adhes. Adhes. 31 (6), 559-564 (2011).</li><li>Xiao, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Utilization+of+sorghum+lignin+to+improve+adhesion+strength+of+soy+protein+adhesives+on+wood+veneer.">Utilization of sorghum lignin to improve adhesion strength of soy protein adhesives on wood veneer.</a> Ind. Crop. Prod. 50, 501-509 (2013).</li><li>Moubarik, A., Grimi, N., Boussetta, N., Pizzi, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Isolation+and+characterization+of+lignin+from+Moroccan+sugar+cane+bagasse:+Production+of+lignin-phenol-formaldehyde+wood+adhesive.">Isolation and characterization of lignin from Moroccan sugar cane bagasse: Production of lignin-phenol-formaldehyde wood adhesive.</a> Ind. Crop. Prod. 45, 296-302 (2013).</li><li>Patel, A. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Development+of+a+chitosan-based+adhesive.+Application+to+wood+bonding.">Development of a chitosan-based adhesive. Application to wood bonding.</a> J. Appl. Polymer Sci. 127 (6), 5014-5021 (2013).</li><li>He, Z., Cao, H., Cheng, H. N., Zou, H., Hunt, J. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effects+of+vigorous+blending+on+yield+and+quality+of+protein+isolates+extracted+from+cottonseed+and+soy+flours.">Effects of vigorous blending on yield and quality of protein isolates extracted from cottonseed and soy flours.</a> Modern Appl. Sci. 7 (10), 79-88 (2013).</li><li>Amico, S., Hrabalova, M., Muller, U., Berghofer, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Bonding+of+spruce+wood+with+wheat+flour+glue-Effect+of+press+temperature+on+the+adhesive+bond+strength.">Bonding of spruce wood with wheat flour glue-Effect of press temperature on the adhesive bond strength.</a> Ind. Crop. Prod. 31, 255-260 (2010).</li><li>Gao, Q., Shi, S. Q., Li, J., Liang, K., Zhang, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Soybean+meal-based+wood+adhesives+enhanced+by+modified+polyacrylic+acid+solution.">Soybean meal-based wood adhesives enhanced by modified polyacrylic acid solution.</a> BioResources. 7 (1), 946-956 (2011).</li><li>Chen, N., Lin, Q., Rao, J., Zeng, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Water+resistances+and+bonding+strengths+of+soy-based+adhesives+containing+different+carbohydrates.">Water resistances and bonding strengths of soy-based adhesives containing different carbohydrates.</a> Ind. Crop. Prod. 50, 44-49 (2013).</li><li>He, Z., Chapital, D. C., Cheng, H. N., Dowd, M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Comparison+of+adhesive+properties+of+water-+and+phosphate+buffer-washed+cottonseed+meals+with+cottonseed+protein+isolate+on+maple+and+poplar+veneers.">Comparison of adhesive properties of water- and phosphate buffer-washed cottonseed meals with cottonseed protein isolate on maple and poplar veneers.</a> Int. J. Adhes. Adhes. 50, 102-106 (2014).</li><li>He, Z., Cheng, H. N., Chapital, D. C., Dowd, M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Sequential+fractionation+of+cottonseed+meal+to+improve+its+wood+adhesive+properties.">Sequential fractionation of cottonseed meal to improve its wood adhesive properties.</a> J. Am. Oil Chem. Soc. 91 (1), 151-158 (2014).</li><li>Sun, X., Bian, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Shear+strength+and+water+resistance+of+modified+soy+protein+adhesives.">Shear strength and water resistance of modified soy protein adhesives.</a> J. Am. Oil Chem. Soc. 76 (8), 977-980 (1999).</li><li>He, Z., Chapital, D. C., Cheng, H. N., Klasson, K. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Application+of+tung+oil+to+improve+adhesion+strength+and+water+resistance+of+cottonseed+meal+and+protein+adhesives+on+maple+veneer.">Application of tung oil to improve adhesion strength and water resistance of cottonseed meal and protein adhesives on maple veneer.</a> Ind. Crop. Prod. 61, 398-402 (2014).</li><li>Hettiarachchy, N. S., Kalapathy, U., Myers, D. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Alkali-modified+soy+protein+with+improved+adhesive+and+hydrophobic+properties.">Alkali-modified soy protein with improved adhesive and hydrophobic properties.</a> J. Am. Oil Chem. Soc. 72 (12), 1461-1464 (1995).</li><li>Wang, D., Sun, X. S., Yang, G., Wang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Improved+water+resistance+of+soy+protein+adhesive+at+isoelectric+point.">Improved water resistance of soy protein adhesive at isoelectric point.</a> Trans. ASABE. 52 (1), 173-177 (2009).</li><li>Zhong, Z., Sun, X. S., Fang, X., Ratto, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adhesive+strength+of+guanidine+hydrochloride-modified+soy+protein+for+fiberboard+application.">Adhesive strength of guanidine hydrochloride-modified soy protein for fiberboard application.</a> Int. J. Adhes. Adhes. 22 (4), 267-272 (2002).</li><li>Kafkalidis, M., Thouless, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+effects+of+geometry+and+material+properties+on+the+fracture+of+single+lap-shear+joints.">The effects of geometry and material properties on the fracture of single lap-shear joints.</a> Int. J. Solids Structures. 39 (17), 4367-4383 (2002).</li><li>Tang, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamic+adhesive+wettability+of+poplar+veneer+with+cold+oxygen+plasma+treatment.">Dynamic adhesive wettability of poplar veneer with cold oxygen plasma treatment.</a> Bio Res. 7 (3), 3327-3339 (2012).</li><li>Gui, C., Liu, X., Wu, D., Zhou, T., Wang, G., Zhu, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+of+a+new+type+of+polyamidoamine+and+its+application+for+soy+flour-based+adhesives.">Preparation of a new type of polyamidoamine and its application for soy flour-based adhesives.</a> J. Am. Oil Chem. Soc. 99 (90), 265-272 (2013).</li></ol>

This paper presents a basic procedure to prepare and test plant seed-based products as wood adhesives. The adhesive slurries exampled in this protocol are simply the defatted seed meal product and water. Various adhesive formulations can be reached by addition of testing reagents (such as sodium dodecyl sulfate, sodium bisulfite or tung oil)5,6,23 and/or changes in mixing conditions (such as pH, ratio of solid and water)3,24,25. Adjustment of the adhesive formulation is also needed if the rheologica...

Adhesive bonding of wood plays an increasing role in the forest product industry and is a key factor for efficiently utilizing timber resources1. Interest in the use of natural product-based adhesives for wood increased steadily from the 1930s to reach a peak around 19602. After this period, the price of petroleum-based adhesives became so low that they displaced protein adhesives from several traditional markets. In the past two decades, this trend has reversed with renewed interest in the use of materials that are renewable, biodegradable, and more environmentally acceptable. These natural resources include, but are not limited to, soy protein3-5, cottonseed protein6, rice bran7, wheat gluten8, distillers grain protein9, canola protein and oil10-12, lignin from sorghum and sugar cane bagasse13,14, and polysaccharides derived from shrimp shells15.
Whereas seed protein isolates have been widely evaluated as potential wood adhesives, the isolation procedure involves corrosive alkaline and acidic reagents and it makes isolate-based adhesives relatively expensive and less environment-friendly16. Thus, some defatted seed meals (flours) with or without treatment have also been tested for the adhesive purpose, even though the adhesive properties of these meals do not perform as well as protein isolates17-19. We have sequentially fractionated cottonseed meal (CM) into different fractions, and examined their adhesive strength in bonding wood veneers20,21. The water-insoluble solid fraction (hereinafter washed cottonseed meal-WCM) could be used as wood adhesives, comparable to cottonseed protein isolate (CSPI), and would be less costly to prepare than CSPI.
Adhesive strength and water resistance are two critical parameters in evaluating the performance of a potential adhesive material. Here, the adhesive strength is reported as the shear strength at break of the lap bond of each wood specimen. Water resistance of the adhesive is measured by the change in lap shear strength of the bonded wood specimen at break due to water soaking. Using defatted cottonseed and soy meals as raw materials, this protocol provides a simple and straightforward way to prepare and test plant seed-based products as wood adhesives. This protocol would be helpful in facilitating the effort in seeking more economic and environment-friendly formulations of natural product-based wood adhesives.

<table border="0" cellpadding="0" cellspacing="0" width="927">
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:265px;">Material and Equipment</td>
			<td style="width:227px;">Supplier/Manufacturer</td>
			<td style="width:227px;"></td>
			<td style="width:211px;">Address</td>
		</tr>
		<tr height="22">
			<td height="22" style="height:23px;">defatted cottonseed meal</td>
			<td>Kentwood Co-op</td>
			<td></td>
			<td>Kentwood, LA, USA&#160;</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">defatted soy meal</td>
			<td>Kentwood Co-op</td>
			<td></td>
			<td>Kentwood, LA, USA</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">wood veneers</td>
			<td>Certainly Wood, Inc.</td>
			<td></td>
			<td>East Aurora, NY, USA</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">cyclone sample mill (model 3010-014)</td>
			<td>UDY Corporation</td>
			<td></td>
			<td>Fort Collins, CO, USA</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Benchtop Heated Press&#160; (Model 3856)</td>
			<td>Carver, Inc.</td>
			<td></td>
			<td>Wabash, IN. USA</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Materials Tester</td>
			<td>Zwick GmbH &#38; Co.</td>
			<td></td>
			<td>Ulm, Germany</td>
		</tr>
	</tbody>
</table>

preparation and testing of plant seed meal-based wood adhesives

Recently, the interest in plant seed meal-based products as wood adhesives has steadily increased, as these plant raw materials are considered renewable and environment-friendly. These natural products may serve as alternatives to petroleum-based adhesives to ease environmental and sustainability concerns. This work demonstrates the preparation and testing of the plant seed-based wood adhesives using cottonseed and soy meal as raw materials. In addition to untreated meals, water washed meals and protein isolates are prepared and tested. Adhesive slurries are prepared by mixing a freeze-dried meal product with deionized water (3:25 w/w) for 2 hr. Each adhesive preparation is applied to one end of 2 wood veneer strips using a brush. The tacky adhesive coated areas of the wood veneer strips are lapped and glued by hot-pressing. Adhesive strength is reported as the shear strength of the bonded wood specimen at break. Water resistance of the adhesives is measured by the change in shear strength of the bonded wood specimens at break after water soaking. This protocol allows one to assess plant seed-based agricultural products as suitable candidates for substitution of synthetic-based wood adhesives. Adjustments to the adhesive formulation with or without additives and bonding conditions could optimize their adhesive properties for various practical applications.

Each adhesive formulation&#8217;s performance is determined by the shear strength of the bonded wood specimen at break and the values vary depending on the dimensions of the wood veneer used. For example, in Table 1, the dry and soaked adhesive strength values of the bonded specimens are lower when thinner and narrower maple strips are used (see Cottonseed-1), as opposed to the thicker and wider strips of Cottonseed-2 recommended in the protocol, using the same cottonseed-based adhesive formulation. Also...

Watch this Scientific Journal Video about Preparation and Testing of Plant Seed Meal-based Wood Adhesives at JoVE.com

Preparation and Testing of Plant Seed Meal-based Wood Adhesives

To facilitate the effort in seeking more economic and environment-friendly formulations of natural product-based wood adhesives, this work demonstrates the preparation and testing of plant seed-based wood adhesives. This protocol allows one to assess plant seed-based agricultural products as suitable candidates for the substitution of synthetic-based wood adhesives.

Recently, the interest in plant seed meal-based products as wood adhesives has steadily increased, as these plant raw materials are considered renewable ...

Research

Education

JoVE Core

JoVE Journal

Civil Engineering

Environment

Unit 1

Wood

SCIENTISTS IN ACTION

A Rapid and Efficient Method for Assessing Pathogenicity of Ustilago maydis on Maize and Teosinte Lines

A Rapid and Efficient Method for Assessing Pathogenicity of Ustilago maydis on Maize and Teosinte Lines

Maize is a major cereal crop worldwide. However, susceptibility to biotrophic pathogens is the primary constraint to increasing productivity. U. maydis is ...

Transcript and Metabolite Profiling for the Evaluation of Tobacco Tree and Poplar as Feedstock for the Bio-based Industry

The global demand for food, feed, energy, and water poses extraordinary challenges for future generations. It is evident that robust platforms for the ...

A Technical Perspective in Modern Tree-ring Research - How to Overcome Dendroecological and Wood Anatomical Challenges

Dendroecological research uses information stored in tree rings to understand how single trees and even entire forest ecosystems responded to ...

Preparation and Testing of Impedance-based Fluidic Biochips with RTgill-W1 Cells for Rapid Evaluation of Drinking Water Samples for Toxicity

This manuscript describes how to prepare fluidic biochips with Rainbow trout gill epithelial (RTgill-W1) cells for use in a field portable water toxicity ...

Reliable Method for Assessing Seed Germination, Dormancy, and Mortality under Field Conditions

We describe techniques for approximating seed bank dynamics over time using Helianthus annuus as an example study species. Strips of permeable polyester ...

On the Preparation and Testing of Fuel Cell Catalysts Using the Thin Film Rotating Disk Electrode Method

We present a step-by-step tutorial to prepare proton exchange membrane fuel cell (PEMFC) catalysts, consisting of Pt nanoparticles (NPs) supported on a ...

The Plant Infection Test: Spray and Wound-Mediated Inoculation with the Plant Pathogen Magnaporthe Grisea

The Plant Infection Test: Spray and Wound-Mediated Inoculation with the Plant Pathogen Magnaporthe Grisea

Plants possess a powerful system to defend themselves against potential threats by pathogenic fungi. For agriculturally important plants, however, current ...

Xylem Water Distribution in Woody Plants Visualized with a Cryo-scanning Electron Microscope

A scanning electron microscope installed cryo-unit (cryo-SEM) allows specimen observation at subzero temperatures and has been used for exploring water ...

Sample Preparation Method of Scanning and Transmission Electron Microscope for the Appendages of Woodboring Beetle

This report described sample preparation methods that scanning and transmission electron microscope observations, demonstrated by preparing appendages of ...

The Effect of Construction and Demolition Waste Plastic Fractions on Wood-Polymer Composite Properties

Construction and demolition waste (CDW), including valuable materials such as plastics, have a remarkable influence on the waste sector. In order for ...