We are grateful to the Pacific Northwest National Laboratory (PNNL) Nuclear Process Science Initiative (NPSI)-Laboratory Directed Research and Development (LDRD) fund for support. Dr. Sayandev Chatterjee provided the synthesized boehmite particles. Instrumental access was provided through a W. R. Wiley Environmental Molecular Sciences Laboratory (EMSL) General User Proposal. EMSL is a national scientific user facility sponsored by the Office of Biological and Environmental Research (BER) at PNNL. PNNL is operated by Battelle for the DOE under Contract DE-AC05-76RL01830.

1. Prepare AlOOH Liquid Sample
NOTE: Do not touch the specimen or anything inside the SEM chamber with bare hands. Powder free gloves should be worn at all times when handling the SALVI device and mounting it onto the SEM stage in order to avoid potential contamination during surface analysis.
<ol>
	<li>Make an AlOOH stock solution (1 mg/mL)
	<ol>
		<li>Dissolve 10 mg of AlOOH powder in 10 mL DI water to make the 1 mg/mL AlOOH stock solution.</li>
		<li>Ultrasonicate the sto...

<ol>
	<li>Goldstein, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Scanning Electron Microscopy and X-Ray Microanalysis: A Text for Biologists, Materials Scientists, and Geologists. , (1992).</li><li>Donald, A. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+use+of+environmental+scanning+electron+microscopy+for+imaging+wet+and+insulating+materials.">The use of environmental scanning electron microscopy for imaging wet and insulating materials.</a> Nat Mater. 2 (8), 511-516 (2003).</li><li>Rossi, M. P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Environmental+Scanning+Electron+Microscopy+Study+of+Water+in+Carbon+Nanopipes.">Environmental Scanning Electron Microscopy Study of Water in Carbon Nanopipes.</a> Nano Lett. 4 (5), 989-993 (2004).</li><li>Nune, S. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Anomalous+water+expulsion+from+carbon-based+rods+at+high+humidity.">Anomalous water expulsion from carbon-based rods at high humidity.</a> Nat Nano. 11 (9), 791-797 (2016).</li><li>Soumya, E. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Scanning Electron Microscopy (SEM) and Environmental SEM: Suitable Tools for Study of Adhesion Stage and Biofilm Formation. , (2012).</li><li>Thiberge, S. Y., Nechushtan, A., Sprinzak, D., Moses, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scanning+electron+microscopy+of+cells+and+tissues+under+fully+hydrated+conditions.">Scanning electron microscopy of cells and tissues under fully hydrated conditions.</a> Proc Natl Acad Sci U S A. 101 (10), 3346-3351 (2004).</li><li>Thiberge, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scanning+electron+microscopy+of+cells+and+tissues+under+fully+hydrated+conditions.">Scanning electron microscopy of cells and tissues under fully hydrated conditions.</a> Proc Natl Acad Sci U S A. 101 (10), 3346-3351 (2004).</li><li>Thiberge, S., Zik, O., Moses, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+apparatus+for+imaging+liquids,+cells,+and+other+wet+samples+in+the+scanning+electron+microscopy.">An apparatus for imaging liquids, cells, and other wet samples in the scanning electron microscopy.</a> Rev Sci Instrum. 75 (7), 2280-2289 (2004).</li><li>Yu, X. -. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Systems+and+methods+for+analyzing+liquids+under+vacuum.">Systems and methods for analyzing liquids under vacuum.</a> USA patent. , (2011).</li><li>Yang, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+SEM+and+ToF-SIMS+analysis+of+IgG+conjugated+gold+nanoparticles+at+aqueous+surfaces.">In situ SEM and ToF-SIMS analysis of IgG conjugated gold nanoparticles at aqueous surfaces.</a> Surf Interface Anal. 46 (4), 224-228 (2014).</li><li>Liu, B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+chemical+probing+of+the+electrode-electrolyte+interface+by+ToF-SIMS.">In situ chemical probing of the electrode-electrolyte interface by ToF-SIMS.</a> Lab Chip. 14 (5), 855-859 (2014).</li><li>Ding, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+Molecular+Imaging+of+the+Biofilm+and+Its+Matrix.">In situ Molecular Imaging of the Biofilm and Its Matrix.</a> Anal Chem. 88 (22), 11244-11252 (2016).</li><li>Hua, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Two-dimensional+and+three-dimensional+dynamic+imaging+of+live+biofilms+in+a+microchannel+by+time-of-flight+secondary+ion+mass+spectrometry.">Two-dimensional and three-dimensional dynamic imaging of live biofilms in a microchannel by time-of-flight secondary ion mass spectrometry.</a> Biomicrofluidics. 9 (3), 031101 (2015).</li><li>Hua, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Chemical+imaging+of+molecular+changes+in+a+hydrated+single+cell+by+dynamic+secondary+ion+mass+spectrometry+and+super-resolution+microscopy.">Chemical imaging of molecular changes in a hydrated single cell by dynamic secondary ion mass spectrometry and super-resolution microscopy.</a> Integr Biol. 8 (5), 635-644 (2016).</li><li>Hua, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+molecular+imaging+of+a+hydrated+biofilm+in+a+microfluidic+reactor+by+ToF-SIMS.">In situ molecular imaging of a hydrated biofilm in a microfluidic reactor by ToF-SIMS.</a> Analyst. 139 (7), 1609-1613 (2014).</li><li>Yu, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Capturing+the+transient+species+at+the+electrode-electrolyte+interface+by+in+situ+dynamic+molecular+imaging.">Capturing the transient species at the electrode-electrolyte interface by in situ dynamic molecular imaging.</a> Chem Commun. 52 (73), 10952-10955 (2016).</li><li>Yang, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Making+a+hybrid+microfluidic+platform+compatible+for+in+situ+imaging+by+vacuum-based+techniques.">Making a hybrid microfluidic platform compatible for in situ imaging by vacuum-based techniques.</a> J Vac Sci Technol, A. 29 (6), (2011).</li><li>Yang, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Probing+liquid+surfaces+under+vacuum+using+SEM+and+ToF-SIMS.">Probing liquid surfaces under vacuum using SEM and ToF-SIMS.</a> Lab Chip. 11 (15), 2481-2484 (2011).</li><li>Yao, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Switchable+1,8-diazabicycloundec-7-ene+and+1-hexanol+ionic+liquid+analyzed+by+liquid+ToF-SIMS.">Switchable 1,8-diazabicycloundec-7-ene and 1-hexanol ionic liquid analyzed by liquid ToF-SIMS.</a> Surf Sci Spectra. 23 (1), 9-28 (2016).</li><li>Yu, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Capturing+the+transient+species+at+the+electrode-electrolyte+interface+by+in+situ+dynamic+molecular+imaging.">Capturing the transient species at the electrode-electrolyte interface by in situ dynamic molecular imaging.</a> Chem Commun. 52 (73), 10952-10955 (2016).</li><li>Clark, S. B., Buchanan, M., Wilmarth, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Basic Research Needs for Environmental Management. , (2016).</li><li>Mills, O. P., Rose, W. I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Shape+and+surface+area+measurements+using+scanning+electron+microscope+stereo-pair+images+of+volcanic+ash+particles.">Shape and surface area measurements using scanning electron microscope stereo-pair images of volcanic ash particles.</a> Geosphere. 6, 805-811 (2010).</li><li>Li, S., Jiang, F., Yin, Q., Jin, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scanning+electron+acoustic+microscopy+of+semiconductor+materials.">Scanning electron acoustic microscopy of semiconductor materials.</a> Solid State Commun. 99 (11), 853-857 (1996).</li><li>Dohnalkova, A. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Imaging+Hydrated+Microbial+Extracellular+Polymers:+Comparative+Analysis+by+Electron+Microscopy.">Imaging Hydrated Microbial Extracellular Polymers: Comparative Analysis by Electron Microscopy.</a> Appl Environ Microbiol. 77 (4), 1254-1262 (2011).</li><li>Yu, X. -. Y., Liu, B., Yang, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Imaging+liquids+using+microfluidic+cells.">Imaging liquids using microfluidic cells.</a> Microfluid Nanofluid. 15 (6), 725-744 (2013).</li><li>Barshack, I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Novel+Method+for+"Wet"+SEM.">A Novel Method for "Wet" SEM.</a> Ultrastruct Pathol. 28 (1), 29-31 (2004).</li><li>Cameron, R. E., Donald, A. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Minizing+sample+evaporation+in+the+Environmental+Scanning+Microscope.">Minizing sample evaporation in the Environmental Scanning Microscope.</a> J Microsc. (Oxford, U. K.). 173 (3), 227-237 (1994).</li><li>Danilatos, G. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=REVIEW+AND+OUTLINE+OF+ENVIRONMENTAL+SEM+AT+PRESENT.">REVIEW AND OUTLINE OF ENVIRONMENTAL SEM AT PRESENT.</a> J Microsc (Oxford, U.K.). 162 (3), 391-402 (1991).</li><li>Stokes, D. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Recent+advances+in+electron+imaging,+image+interpretation+and+applications:+environmental+scanning+electron+microscopy.">Recent advances in electron imaging, image interpretation and applications: environmental scanning electron microscopy.</a> Philos Trans R Soc, A. 361 (1813), 2771-2787 (2003).</li></ol>

SEM is a powerful technique in surface characterization of organic and inorganic materials on a nanoscale (nm) level with high resolution1. For example, it is widely used for analyzing the solid and dry samples such as geological materials26 and semiconductor27. However, it has limitations in characterizing the wet and liquid samples due to the incompatibility of liquid within the highly vacuumed environment required for electron microscopy<sup class...

Scanning Electron Microscope (SEM) has been widely applied to investigate a variety of specimens by producing high resolution imaging1. The energy dispersive x-ray spectroscopy (EDX) associated with the SEM enables the determination of elemental composition1. Traditionally, SEM is applied for imaging only dry and solid samples. In the last 30 years, Environmental SEM (ESEM) was developed for analyzing the partial hydrated samples in a vapor environment2,3,4,5. However, ESEM is unable to image the wet, fully fluid samples with desired high resolution6. Wet SEM cells were also developed to image wet specimens using SEM7,8; nevertheless, these cells were developed mainly for biological specimens and backscattered electron imaging, and are more accessible for applications with those designs9,10.
To address the challenges in analyzing various samples in their native liquid environment using SEM, we invented a vacuum compatible microfluidic device, System for Analysis at the Liquid Vacuum Interface (SALVI), to enable high spatial resolution secondary electron (SE) imaging and elemental analysis of liquid samples using the high vacuum mode in SEM. This novel technique includes the following unique features: 1) liquid is directly probed in a small aperture of 1 - 2 &#181;m in diameter; 2) liquid is held within the hole by surface tension; and 3) SALVI is portable and can be adapted to more than one analytical platform11,12,13,14,15,16,17,18.
SALVI consists of a 100 nm thick silicon nitride (SiN) membrane and a 200 &#181;m wide microchannel made of polydimethylsiloxane (PDMS) block. The SiN membrane window is applied to seal the microchannel. The fabrication details and key design considerations were detailed in previous papers and patents11,19,20. Currently, a leading manufacturer and distributor of consumable supply for microscopy has purchased the license to sell SALVI devices commercially for liquid SEM applications21,22.
The applications of SALVI in vacuum-based analytical instruments have been demonstrated using a variety of aqueous solutions and complex liquid mixtures including biofilms, mammalian cells, nanoparticles, and electrode materials12,14,17,20,23,24. However, most of the aforementioned work utilized time-of-flight secondary ion mass spectrometry (ToF-SIMS) as the key analysis tool, thus the application of liquid SEM with SALVI has not been explored fully. In this work, SALVI has been used to study larger non-spherical colloidal particles in liquid using liquid SEM imaging and EDX elemental analysis. The sample consists of AlOOH particles synthesized at our laboratory. Submicrometer-sized boehmite particles are known to exist in high-level radioactive waste at the Hanford site. They are slow to dissolve and may cause rheological problems in waste treatment. Therefore, it is important to have the capability to characterize boehmite particles in liquid25. This technical approach can be used to study boehmite in various physicochemical conditions for improved understanding of these particles and related rheological properties. These particles were utilized to demonstrate step-by-step how to apply SALVI to high vacuum SEM in order to study particles suspended in liquid. Key technical points for SALVI and SEM integration and SEM data acquisition are highlighted within the paper.
The protocol provides demonstration of the liquid sample analysis using SALVI and liquid SEM imaging, for those who are interested in utilizing this novel technique in diverse applications of liquid SEM in the future.

<table width="2033">
	<tbody>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Carbon Coater</td>
			<td style="width:311px;">Cressington</td>
			<td style="width:196px;">208 Carbon</td>
			<td style="width:1237px;">It is accompanied with thickness monitor MTM-10.</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">SEM</td>
			<td style="width:311px;">FEI</td>
			<td>Quanta 3D FEG</td>
			<td style="width:1237px;">It provides highly resolved scanning electron microscopy and elemental analysis.</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">System for Analysis at the Liquid Vacuum Interface (SALVI)</td>
			<td style="width:311px;">Pacific Northwest National Laboratory</td>
			<td>N/A</td>
			<td style="width:1237px;">SALVI is a unique, vacuum compatible microfluidic cell that enables the characterization of the liquid sample using vacuu- based scientific instrument.</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">PEEK Union</td>
			<td style="width:311px;">Valco</td>
			<td>ZU1TPK</td>
			<td>The polyether ether ketone union is used for connecting the inlet and outlet of SALVI</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Syringe</td>
			<td style="width:311px;">BD</td>
			<td>309659</td>
			<td style="width:1237px;">1 mL</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Pipette</td>
			<td style="width:311px;">Thermo Fisher Scientific</td>
			<td>21-377-821</td>
			<td style="width:1237px;">Range: 100 to 1,000 mL</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Pipette Tip 1</td>
			<td style="width:311px;">Neptune</td>
			<td>2112.96.BS</td>
			<td style="width:1237px;">1,000 &#181;L</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Pipette Tip 2</td>
			<td style="width:311px;">Rainin</td>
			<td>17001865</td>
			<td style="width:1237px;">20 &#181;L</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Syringe Pump</td>
			<td style="width:311px;">Harvard Apparatus</td>
			<td>70-2213</td>
			<td style="width:1237px;">It is used to inject the liquid sample into the SALVI device.</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">pH meter</td>
			<td style="width:311px;">Fisher Scientific/accumet</td>
			<td>13-636-AP72</td>
			<td style="width:1237px;">It is used for measuring the pH of AlOOH in DI water.</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Barnstead Ultrapure Water System, UV/UF</td>
			<td style="width:311px;">Thermo Scientific Barnstead</td>
			<td style="width:196px;">Nanopure diamond D11931</td>
			<td style="width:1237px;">It is used for producing DI water.</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Centrifuge tubes</td>
			<td style="width:311px;">Fisher scientific/Falcon</td>
			<td>15-527-90</td>
			<td style="width:1237px;">15 mL</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Bransonic ultrasonic cleaner</td>
			<td style="width:311px;">Sigma-Aldrich</td>
			<td>2510</td>
			<td style="width:1237px;">It is used to ultrasonicate the AlOOH liquid sample.</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">Balance</td>
			<td style="width:311px;">Mettler Toledo</td>
			<td>11106015</td>
			<td style="width:1237px;">XS64</td>
		</tr>
		<tr height="20">
			<td height="20" style="width:289px;height:20px;">AlOOH</td>
			<td style="width:311px;">Pacific Northwest National Laboratory</td>
			<td>N/A</td>
			<td style="width:1237px;">It is synthesized by scientists at Pacific Northwest National Laboratory.</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">xT microscope Control</td>
			<td>FEI</td>
			<td>Quanta 3D FEG</td>
			<td>Default microscope control software of SEM Quanta 3D FEG</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">EDAX Genesis software</td>
			<td style="width:311px;">EDAX</td>
			<td>N/A</td>
			<td style="width:1237px;">The software is used for collecting the EDX elemental information of the samples.</td>
		</tr>
		<tr height="21">
			<td height="21" style="width:289px;height:21px;">Teflon tubing</td>
			<td>SUPELCO</td>
			<td>58697-U</td>
			<td style="width:1237px;">It is used for introducing the sample into the microchannel and holding adequate volume of liquid.</td>
		</tr>
	</tbody>
</table>

in situ characterization of boehmite particles in water using liquid sem

In situ imaging and elemental analysis of boehmite (AlOOH) particles in water is realized using the System for Analysis at the Liquid Vacuum Interface (SALVI) and Scanning Electron Microscopy (SEM). This paper describes the method and key steps in integrating the vacuum compatible SAVLI to SEM and obtaining secondary electron (SE) images of particles in liquid in high vacuum. Energy dispersive x-ray spectroscopy (EDX) is used to obtain elemental analysis of particles in liquid and control samples including deionized (DI) water only and an empty channel as well. Synthesized boehmite (AlOOH) particles suspended in liquid are used as a model in the liquid SEM illustration. The results demonstrate that the particles can be imaged in the SE mode with good resolution (i.e., 400 nm). The AlOOH EDX spectrum shows significant signal from the aluminum (Al) when compared with the DI water and the empty channel control. In situ liquid SEM is a powerful technique to study particles in liquid with many exciting applications. This procedure aims to provide technical know-how in order to conduct liquid SEM imaging and EDX analysis using SALVI and to reduce potential pitfalls when using this approach.

The representative results are presented to show how the particles are imaged and analyzed using in situ liquid SEM imaging coupled with EDX. The results include SE images and EDX spectra. The SE images were obtained at 100,000X and 200,000X magnification levels in Figure 1. Figure 1a depicts the SE image of the AlOOH, Figure 1b DI water, and Figure 1c the hole ...

Watch this Scientific Journal Video about In Situ Characterization of Boehmite Particles in Water Using Liquid SEM at JoVE.com

In Situ Characterization of Boehmite Particles in Water Using Liquid SEM

We present a procedure for real-time imaging and elemental composition analysis of boehmite particles in deionized water by in situ liquid Scanning Electron Microscopy.

In Situ Characterization of Boehmite Particles in Water Using Liquid SEM

In situ imaging and elemental analysis of boehmite (AlOOH) particles in water is realized using the System for Analysis at the Liquid Vacuum Interface ...

The overall goal of this in situ liquid scanning electron microscopy imaging procedure is to provide technical knowhow for efficient imaging and analysis of particles in liquids in conventional high-vacuum SEM using a vacuum-compatible microfluidic module. This method can help answer key questions in the microscopy and microanalysis field such as how to characterize evolving particle size and morphology responding to the environmental changes. The main advantage of this technique is that we can directly visualize polydispersed particles in liquid without drying or freezing the sample in high-vacuum mode and also without resorting to environmental SEM.The implication of this technique extend toward the efficient analysis or the various liquid material and the biological samples using SEM because many of them only function or exist in liquid. Visual demonstration of this method is critical as simple mounting and in situ imaging steps are difficult to learn because they are different from regular solid samples. Begin this procedure with carbon coating of the system for analysis at the liquid vacuum interface, or SALVI device, as described in the tech's protocol.Mounting the microfluidic device on the SEM stage is quite critical for the success of in situ liquid SEM analysis. Make sure the device is properly grounded and is secured to minimize the charging effect before the experiment. To mount the SALVI device onto the SEM stage, first open the SEM specimen chamber door carefully once venting has completed.Select the SEM specimen holder. Fix the holder onto the center of the stage using the appropriate bolt and hex wrench. Place two strips of double sided carbon tape on the specimen holder.Then stick the SALVI device onto the carbon tape placed on the holder with the silicon nitride membrane side facing up. Securely immobilize the SALVI onto the specimen holder using an additional two strips of single sided copper tape to bind the SALVI PDMS block to the SEM specimen holder. In addition use the copper tapes to connect the silicon nitride frame and the metal specimen holder.Make sure that the tape does not completely cover the silicon nitride membrane. To pump down the specimen chamber, close the specimen chamber door, select the high vacuum mode on the SEM software GUI under the beam control page, click the pump button on the beam control page to start vacuuming. Apply pressure by hand to the chamber door until the desired vacuum is established.Next make apertures in the silicon nitride membrane using focused ion beam, or FIB, as described in the tech's protocol. Following the procedure, turn off both the electron beam and ion beam to vent the chamber by clicking beam on when the corresponding beam imaging area is activated. Click vent on the beam control page to vent the specimen chamber.Carefully open the SEM chamber door after it is fully vented leaving the SALVI device as it is on the stage. Draw one milliliter of deionized water into a sterile syringe and connect the syringe with the inlet of the microfluidic device using a polytetrafluoroethylene tubing adapter fitting. Slowly inject the liquid for three to five minutes.Repeat this process three times using one milliliter of 10 micrograms per milliliter aluminum oxyhydroxide to ensure the concentration of the sample is not diluted by the preloaded deionized water. After the injection, remove the syringe. Connect the inlet and outlet of SALVI using polyether ether ketone union.Dry any liquid outside the SALVI with lab wipes. If there are any bubbles within the tubing or microchannel, redo the sample injection until no bubbles are seen within the tubing. To take images using the ETD and secondary electron mode, first close the specimen chamber door.After establishing the desired vacuum on the chamber door as before, activate the electron beam imaging area by clicking the pause icon on the toolbar. Turn on the electron beam by clicking the beam on button on the beam control page. Select the ETD and the secondary electron mode for imaging from the detector's drop-down menu.In selecting the optimal conditions it is really important to be able to attain high-quality images. In this work, we will show you a set of conditions suitable for a secondary electron imaging of the light elements like aluminum silicon. When analyzing other elements like iron and nickel, operation conditions should be modified to optimize the secondary electron imaging.Set the accelerating voltage to eight kiloelectron-volts and the beam current to approximately 0.47 nanoamps from the corresponding list boxes displayed on the GUI toolbar at the electron beam imaging area. Set the working distance as seven millimeters by typing seven into the text box of the coordinate Z on the navigation page when the actual distance is selected. Magnify the feature to 1, 000 X and twist the contrast, brightness, coarse and fine knobs on the manual user interface to optimize the image of the particle feature.Center the first hole in the live image of the electron beam imaging area by twisting the X and Y shift knobs on the manual user interface board, enlarge the images with particles to magnification 200, 000 X by twisting the magnification knob on the manual user interface board. Select the screen resolution to 1, 024 by 884 from the list box on the tool bar. Then set the scan rate as 30 microseconds from the list box on the tool bar.Press the F4 key to take the snapshot of the current image shown in the electron beam imaging area. Press the control and S keys to save the image as a TIF file to the desired location with the defined file name including an incremental number. Zoom out by twisting the magnification knob to locate the next adjacent hole.Repeat these operations to image the aluminum oxyhydroxide particles in the rest of the holes. To conduct elemental analysis using energy-dispersive x-ray spectroscopy, or EDX, insert the energy-dispersive spectroscopy detectors into the chamber. Select the ETD on the microscope control monitor.Then select the secondary electron mode for viewing the sample on the electron beam imaging area and set the parameters as before. Enlarge the aluminum oxyhydroxide particles in each hole with a magnification of 200, 000 X by twisting the magnification knob on the manual user interface board. Next open the associated EDAC software.Click start recording new spectra in the user interface to collect the EDX spectrum. Select peak ID to choose the probable elements of the spectrum. Then type in the observed elements into the element field.Click add to apply the element to the spectrum. Click on file and then click save as. Save the spectral data in CSV format using the desired file name for plotting using a graphing software.After finishing the imaging and spectrum recording for each of the holes, turn off the electron beam by clicking the beam on button on the beam control page when the electron beam imaging area is on. Vent the SEM chamber by clicking vent on the same page. Carefully take the sample off the stage by removing all the tapes after the chamber door is open.Repeat the procedure to conduct the control experiments using deionized water and an empty microchannel. Finally plot the EDX spectrum as described in the tech's protocol. Using the SALVI microfluidic interface, the electron beam can directly bombard the small, micrometer sized aperture with liquid underneath.Boehmite particles in deionized water were compared with the deionized water control and empty channel control in their secondary electron images. This provides direct evidence of particle secondary electron imaging of Boehmite particles in the liquid. Visualization of the particle in deionized water within the one micrometer hole demonstrates the feasibility to observe particles in liquid in situ.In the Boehmite sample, a strong aluminum peak is observed. In contrast, only a strong oxygen peak is observed in the deionized sample indicating the observation of water. In the empty channel, residual of the gallium-focused ion beam is seen.The oxygen peak is quite small because there is not any water inside. Once mastered this technique can be done in a couple of hours if it is performed properly. Generally individuals new to this method will struggle because it is difficult to directly visualize liquids in high-vacuum SEM.After watching this video, you should have a good understanding of how to characterize particles in liquid using in situ liquid SEM with SALVI. While attempting this procedure it is really important to remember that the microreactor should be free of leaks before mounting to the SEM stage. Following this procedure, other methods like TOF-SIMS or NMR can be performed in order to answer additional questions like molecular composition and fluidic field mapping.After its development, this technique paved the way for researchers in the field of material sciences, chemical engineering and nuclear engineering to explore particle size and morphological changes in a caustic liquid environment. Don't forget that when working with surface analysis using SEM, gloves and goggles should be worn when performing this procedure.

Research

JoVE Journal

Chemistry

Untargeted Metabolomics from Biological Sources Using Ultraperformance Liquid Chromatography-High Resolution Mass Spectrometry (UPLC-HRMS)

Untargeted Metabolomics from Biological Sources Using Ultraperformance Liquid Chromatography-High Resolution Mass Spectrometry UPLC-HRMS

Here we present a workflow to analyze the metabolic profiles for biological samples of interest including; cells, serum, or tissue. The sample is first ...

Assessment of Boron Doped Diamond Electrode Quality and Application to In Situ Modification of Local pH by Water Electrolysis

Assessment of Boron Doped Diamond Electrode Quality and Application to In Situ Modification of Local pH by Water Electrolysis

Boron doped diamond (BDD) electrodes have shown considerable promise as an electrode material where many of their reported properties such as extended ...

Synthesis and Exfoliation of Discotic Zirconium Phosphates to Obtain Colloidal Liquid Crystals

Due to their abundance in natural clay and potential applications in advanced materials, discotic nanoparticles are of interest to scientists and ...

Radiolabeling and Quantification of Cellular Levels of Phosphoinositides by High Performance Liquid Chromatography-coupled Flow Scintillation

Phosphoinositides (PtdInsPs) are essential signaling lipids responsible for recruiting specific effectors and conferring organelles with molecular ...

In Situ Characterization of Hydrated Proteins in Water by SALVI and ToF-SIMS

In Situ Characterization of Hydrated Proteins in Water by SALVI and ToF-SIMS

This work demonstrates in situ characterization of protein biomolecules in the aqueous solution using the System for Analysis at the Liquid Vacuum ...

Sequencing of Plant Wall Heteroxylans Using Enzymic, Chemical (Methylation) and Physical (Mass Spectrometry, Nuclear Magnetic Resonance) Techniques

Sequencing of Plant Wall Heteroxylans Using Enzymic, Chemical Methylation and Physical Mass Spectrometry, Nuclear Magnetic Resonance Techniques

This protocol describes the specific techniques used for the characterization of reducing end (RE) and internal region glycosyl sequence(s) of ...

In Situ Characterization of Shewanella oneidensis MR1 Biofilms by SALVI and ToF-SIMS

In Situ Characterization of Shewanella oneidensis MR1 Biofilms by SALVI and ToF-SIMS

Bacterial biofilms are surface-associated communities that are vastly studied to understand their self-produced extracellular polymeric substances (EPS) ...

Using Graphene Liquid Cell Transmission Electron Microscopy to Study in Situ Nanocrystal Etching

Using Graphene Liquid Cell Transmission Electron Microscopy to Study in Situ Nanocrystal Etching

Graphene liquid cell electron microscopy provides the ability to observe nanoscale chemical transformations and dynamics as the reactions are occurring in ...

Preparation of Graphene-Supported Microwell Liquid Cells for In Situ Transmission Electron Microscopy

Preparation of Graphene-Supported Microwell Liquid Cells for In Situ Transmission Electron Microscopy

The fabrication and preparation of graphene-supported microwell liquid cells (GSMLCs) for in situ electron microscopy is presented in a stepwise protocol. ...

In situ FTIR Spectroscopy as a Tool for Investigation of Gas/Solid Interaction: Water-Enhanced CO2 Adsorption in UiO-66 Metal-Organic Framework

In situ FTIR Spectroscopy as a Tool for Investigation of Gas/Solid Interaction: Water-Enhanced CO2 Adsorption in UiO-66 Metal-Organic Framework

In situ infrared spectroscopy is an inexpensive, highly sensitive, and selective valuable tool to investigate the interaction of polycrystalline solids ...