The Natural Sciences and Engineering Research Council (NSERC) of Canada and the Canadian Institutes of Health Research (CIHR) have provided funding for this work. The authors would like to acknowledge Dr. Amin Rizkalla for the use of his electrospraying system, the Nanofabrication Facility at Western University for use of SEM imaging equipment, the Mount Brydges Abattoir for the provision of porcine tissue samples, and Drs. Aaron Grant, Brian Evans, and Robert Richards for their clinical collaborations in support of this research.

1. Decellularized Tissue Processing
<ol>
	<li>Decellularization and Lyophilization
	<ol>
		<li>Decellularize tissue(s) of interest following an established protocol. 
		NOTE: Scaffolds in the current study have been prepared following published decellularization protocols for human DAT28, porcine DDT8, and porcine DLV32. Commercially-available, insoluble collagen can also be used to fabricate foams and microcarriers, such as collagen sourced from bovine tendon, which has been used successfully over a concentration range of 10 - 50 mg/mL. Other insoluble collagen sources may be utilized, but may require optimization to identify the concentration range that will yield stable scaffolds.</li>
		<li>Transfer the hydrated decellularized tissue or purified collagen into a 50 mL centrifuge tube with forceps and add sufficient double distilled water (ddH2O) to submerge the tissue, to a maximum total volume of 35 mL.</li>
		<li>Freeze the sample overnight at -80 &#176;C, with the centrifuge tube positioned horizontally during freezing to maximize the surface area for sublimation during subsequent lyophilization.</li>
		<li>Remove the cap from the centrifuge tube and transfer the frozen sample into a lyophilization jar.</li>
		<li>Lyophilize the sample using a laboratory freeze dryer for 48 - 72 h or until fully dried. 
		NOTE: Drying time may vary for different lyophilizers and decellularized tissues.</li>
		<li>Finely mince the lyophilized ECM into small pieces (~ 1 - 2 mm3) using sharp surgical scissors.</li>
		<li>Store the minced ECM in a desiccator until ready for further processing. 
		NOTE: It is recommended that the minced ECM be used immediately to prevent moisture absorption from the environment.</li>
	</ol>
	</li>
	<li>Cryomilling (optional for foam fabrication)
	<ol>
		<li>Fill a 25 mL stainless steel milling chamber for a laboratory ball mill system with minced lyophilized ECM and add two 10 mm stainless steel milling balls.</li>
		<li>Close and completely submerge the loaded milling chamber in liquid nitrogen for 3 min.</li>
		<li>Mill the frozen sample for 3 min at 30 Hz (1,800 rpm).</li>
		<li>Repeat steps 1.2.2 and 1.2.3 until the ECM is milled into a fine powder. 
		NOTE: The number of times these steps should be repeated may vary between ECM sources. For example, DAT typically requires 3 milling cycles to generate a fine powder.</li>
		<li>Transfer the powder using a scoopula into a glass vial, seal tightly, and store in a desiccator.</li>
	</ol>
	</li>
	<li>ECM Suspension Preparation
	<ol>
		<li>Weigh out 250 mg of either minced (for foams) or cryomilled (for foams or microcarriers) ECM and transfer it to a 15 mL centrifuge tube. Refer to step 1.1.6 and section 1.2 for preparation of minced ECM and cryomilled ECM, respectively. 
		NOTE: This protocol is designed to prepare a 50 mg/mL ECM suspension, which is recommended for human DAT, porcine DDT, and porcine DLV. Depending on the specific ECM source, uniform suspensions may be generated at higher or lower starting concentrations.</li>
		<li>Add 5 mL of 0.22 M NaH2PO4 (pH 5.4) buffer to the centrifuge tube and mark the liquid level on the tube.</li>
		<li>Prepare an &#945;-amylase stock solution by adding 7.5 mg of &#945;-amylase to 1 mL 0.22 M NaH2PO4 (pH 5.4) buffer. Add 100 &#956;L of the &#945;-amylase stock solution (0.75 mg of &#945;-amylase; 0.3% w/w of dry tissue) to the sample. Add 0.22 M NaH2PO4 to obtain a final volume of 10 mL.</li>
		<li>Agitate the suspension continuously at 300 rpm for 72 h at room temperature.</li>
		<li>Centrifuge the suspension at 1,500 x g for 10 min. Carefully collect and discard the supernatant without disturbing the digested ECM pellet. Resuspend the pelleted material in 10 mL of 5% NaCl diluted in ddH2O.</li>
		<li>Repeat step 1.3.5 for a total of two rinses with 5% NaCl in ddH2O.</li>
		<li>Discard the supernatant and resuspend the pelleted material in 10 mL of ddH2O.</li>
		<li>Agitate the suspension continuously at 300 rpm for 10 min at RT.</li>
		<li>Centrifuge the suspension at 1,500 x g for 10 min. Carefully collect and discard the supernatant without disturbing the digested ECM pellet.</li>
		<li>Add 0.2 M acetic acid to the 5 mL mark made in step 1.3.2.</li>
		<li>Agitate the suspension continuously at 120 rpm O/N&#160;at 37 &#176;C.</li>
		<li>Homogenize the ECM suspension at room temperature in ten-second intervals using a hand-held homogenizer equipped with a saw tooth 10 mm wide probe until no visible fragments remain. Place the suspension in a beaker of cold water between the homogenization intervals to prevent overheating. 
		NOTE: Depending on the ECM source, further dilution in 0.2 M acetic acid may be required to obtain a homogeneous suspension. Excessive cooling of the ECM suspension may result in an increase in viscosity that can interfere with efficient homogenization. If an increase in viscosity is noted, the sample can be rewarmed to 37 &#176;C and subjected to further processing.</li>
		<li>Store at 4 &#176;C for up to one month prior to foam or microcarrier fabrication.</li>
	</ol>
	</li>
</ol>
2. ECM-derived Foam Fabrication
<ol>
	<li>Incubate the ECM suspension from step 1.3.13 (minced or cryomilled) at 37 &#176;C with continuous agitation at 120 rpm until the suspension is warm.</li>
	<li>Dilute the ECM suspension in 0.2 M acetic acidic to the desired concentration. 
	NOTE: Depending on the ECM source, stable foams may be prepared in the range of 10 - 100 mg/mL, with 15 - 50 mg/mL as the recommended range for DAT, DDT and DLV. Typically, foams fabricated at higher concentrations will be slightly less porous but more stable in culture and easier to handle.</li>
	<li>Using a 3 mL syringe with an 18 G needle to prevent bubble formation in the ECM suspension, fill the desired mold with the ECM suspension. To fabricate the DAT, DDT, and DLV foams, dispense 400 &#956;L of 35 mg/mL ECM suspension into a 48-well cell culture-treated plate. 
	NOTE: The shape of the selected mold and the volume of ECM suspension will determine the geometry of the resultant foam.</li>
	<li>Cover and freeze the molds overnight by placing them in a -20 &#176;C or -80 &#176;C freezer. 
	NOTE: The freezing temperature may affect the porosity of the foams. Larger pores are expected when the samples are frozen at -20 &#176;C as compared to -80 &#176;C due to the formation of larger ice crystals33. To fabricate foams with a uniform porous structure, ensure that the mold is not in contact with a conductive surface to prevent directional cooling.</li>
	<li>Place the molds containing the frozen samples into a lyophilizer flask. Connect the lyophilizer flask to the laboratory freeze dryer system and dry for 24 h. 
	NOTE: It is important that the sample remains frozen prior to lyophilization.</li>
	<li>Store the lyophilized foams in a desiccator until required.</li>
</ol>
3. ECM-derived Microcarrier Fabrication via Electrospraying
NOTE: An overview of the electrospraying set up is shown in Figure 2.
<ol>
	<li>Incubate the cryomilled ECM suspension from step 1.3.13 at 37 &#176;C with continuous agitation at 100 rpm O/N. 
	NOTE: Cryomilled ECM is used to fabricate the ECM-derived microcarriers to ensure greater uniformity in the suspension and prevent clogging during electrospraying.</li>
	<li>Load 3 mL of ECM suspension into a 3 mL Luer lock syringe and attach a winged infusion set onto the bore of the syringe. 
	NOTE: A range of needle gauges can be used, recognizing that the selection may influence the size and shape of the resultant microcarriers. To fabricate the DAT, DDT, and DLV microcarriers, use a 25 G needle.</li>
	<li>Secure the syringe within the syringe pump. Fasten the needle to a retort stand and position the needle tip vertically at a distance of 4 - 6 cm from the top of a low-form Dewar flask (250 - 500 mL size range recommended).</li>
	<li>Attach an alligator clip electrode to the tip of the needle and connect it to the positive terminal of the high-voltage power supply.</li>
	<li>Fold a strip of aluminum foil (12 x 5 cm) over the edge of the vacuum flask.</li>
	<li>Attach a second alligator clip electrode to the outer edge of the foil and connect it to the ground source terminal of the power supply.</li>
	<li>Fill the Dewar flask with liquid nitrogen to approximately 1 cm from the top, so that &#190; of the foil is submerged. 
	NOTE: It is important to keep the Dewar flask filled with liquid nitrogen. The surface of the liquid nitrogen must be no less than 2 cm from the top of the flask during the electrospraying process. Continuous refilling of the liquid nitrogen is required to maintain a constant level during electrospraying.</li>
	<li>Set the syringe pump to an infusion rate of 30 mL/h. 
	NOTE: Varying the infusion rate can alter the microcarrier shape and diameter, but the recommended range is 25 - 35 mL/h. While it is highly dependent on the viscosity of the suspension, flow rates below 25 mL/h may result in the generation of larger microcarriers. At very low flow rates, the size and shape of the microcarriers may become less homogeneous. At infusion rates above 35 mL/h, the uniformity of the droplets generated via electrospraying may be disrupted, resulting in non-spherical microcarriers with a broader size distribution34.</li>
	<li>Apply a voltage of 20 kV and turn on the syringe pump to initiate electrospraying. 
	NOTE: The voltage may be varied to tune the size of the microcarriers and tends to have a greater impact on the diameter than the infusion rate. The recommended voltage range is 15 - 25 kV. A decrease in microcarrier diameter is expected with an increase in voltage35.</li>
	<li>Once the infusion is complete, carefully pour off excess liquid nitrogen from the Dewar, leaving the microcarriers suspended in ~ 25 mL of liquid nitrogen to ensure they remain frozen.</li>
	<li>Immediately transfer the microcarriers with the liquid nitrogen into a 50 mL centrifuge tube by pouring in one smooth motion. Collect any frozen microcarriers remaining in the Dewar with a scoopula and add them to the centrifuge tube. 
	NOTE: Depending on the size of the Dewar, the microcarriers in liquid nitrogen can be initially poured into a mid-sized vessel, and then transferred immediately into the 50 mL centrifuge tube.</li>
	<li>Cover the centrifuge tube containing the microcarriers in liquid nitrogen with aluminum foil perforated with small holes in preparation for lyophilization.</li>
	<li>Place the covered centrifuge tubes into a lyophilizer flask. Immediately connect the flask to the lyophilizer and dry the samples O/N. 
	NOTE: It is very important to keep the microcarriers suspended in liquid nitrogen to ensure they do not thaw before this step, as thawing may result in collapse and/or aggregation. DAT, DDT and DLV microcarriers fabricated at a concentration of 35 mg/mL using the electrospraying conditions described above will typically have a hydrated diameter ranging between 350 - 500 &#956;m in size. The size distribution may vary depending on the ECM source.</li>
	<li>Store the lyophilized microcarriers in a desiccator until required.</li>
</ol>
<img alt="Figure 2" src="/files/ftp_upload/55436/55436fig2.jpg" /> 
Figure 2. Overview of the Electrospraying Apparatus used in Microcarrier Fabrication. A: Image showing the arrangement of the key electrospraying equipment including the syringe pump and high voltage power supply, as well as the positioning of the needle relative to the Dewar of liquid nitrogen. B: Electrospraying schematic, including the recommended ranges for the voltage, infusion rate, and distance. <a href="http://cloudfront.jove.com/files/ftp_upload/55436/55436fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
4. Preparing Foams and Microcarriers for Cell Culture
<ol>
	<li>Rehydration
	<ol>
		<li>Transfer the lyophilized foams with forceps into a 50 mL centrifuge tube containing excess absolute ethanol (~ 99.9%) (~ 5:1 ratio of ethanol to foams). Similarly, resuspend the lyophilized microcarriers in excess absolute ethanol within the original centrifuge tube used for collection. Using a serological pipette, filter the microcarriers through a stainless sieve with a defined mesh size into a new 50 mL centrifuge tube to remove any aggregates and select for desired size ranges. 
		NOTE: If the foams are fabricated within TCPS plates, they can be rehydrated directly within these vessels.</li>
		<li>Incubate at 4 &#176;C for 4 h or until the foams or microcarriers have gravity settled to the bottom of the centrifuge tube. Perform all subsequent steps in a laminar flow hood using sterile reagents and proper aseptic technique.</li>
		<li>Remove the absolute ethanol using a serological pipette and add excess (5:1 ratio) 95% ethanol diluted with sterile phosphate buffered saline (PBS) to the scaffolds. Incubate at 4 &#176;C for 4 h or until the ECM-derived scaffolds have sunk to the bottom of the rehydration vessel.</li>
		<li>Gradually rehydrate the scaffolds through an ethanol series (90, 85, 80, 75, 70, 50, 25 and&#160;0%, diluted with sterile PBS). At each step, incubate at 4 &#176;C until the scaffolds have sunk to the bottom of the vessel before changing the solution. Degas the scaffolds under light vacuum if bubble formation within the scaffolds is observed.</li>
		<li>Replace the sterile PBS for an additional two rinses to remove residual ethanol.</li>
		<li>Store in 100% sterile PBS at 4 &#176;C until ready for cell culture. Use the scaffolds within 1 - 2 weeks following rehydration.</li>
	</ol>
	</li>
	<li>Preparation for Cell Seeding
	<ol>
		<li>On the day prior to seeding, transfer the foams using forceps into cell culture treated well plates or transwell inserts and add sufficient cell culture medium (selected based on the cell type of interest) to completely submerge the scaffolds (e.g., 2.5 mL/scaffold in a 12-well plate). Similarly, allow the microcarriers to gravity settle within the centrifuge tube, carefully remove the PBS using a serological pipette without disturbing the microcarriers, and add cell culture medium to achieve a 5:1 ratio of medium to the microcarriers. 
		NOTE: For seeding human ASCs, utilize Dulbecco&#39;s Modified Eagle&#39;s medium (DMEM):Ham&#39;s F12 nutrient mixture supplemented with 10% fetal bovine serum (FBS) and 1% penicillin-streptomycin.</li>
		<li>Replace the cell culture medium for a total of one rinse.</li>
		<li>Equilibrate the scaffolds overnight in cell culture medium at 37 &#176;C. The scaffolds will be ready for cell seeding the next day. 
		NOTE: The foams can be statically seeded in cell culture inserts or tissue culture well plates29, or dynamically seeded using a laboratory shaker36. Depending on the ECM source, processing methods and suspension concentration, dynamic seeding may enhance initial cell attachment, proliferation and infiltration. The microcarriers can be seeded dynamically using a spinner culture system11.</li>
	</ol>
	</li>
</ol>

The authors have nothing to disclose.

In general, bioscaffolds derived from decellularized tissues can more closely approximate the complex 3D composition and structure of the ECM in the native cellular microenvironment as compared to synthetic scaffolds or standard culture models based on 2D TCPS. As previously discussed, cell-ECM interactions are critically important in mediating cellular behavior both in culture and in the body1. Recognizing that the biochemical, biophysical, and biomechanical properties of the ECM are unique to each tissue, there is increasing evidence to support the rationale for applying tissue-specific approaches in the design of biomaterials for tissue engineering, as well as in the development of more physiologically relevant culture models for in vitro experiments20. Utilizing decellularized tissues as a starting material, our methods can incorporate the complex composition of the tissue-specific ECM within more customizable scaffold formats. While the mechanical and enzymatic processing steps will result in a loss of the native ECM ultrastructure, previous studies with DAT have demonstrated that the instructive effects of the adipose-derived ECM are conserved in these scaffold formats, suggesting that the bioscaffold composition is a key mediator of cell function11,29. A significant advantage to using the ECM-derived foams and microcarriers as cell culture substrates as compared to the intact decellularized tissues is that they are more homogeneous, which can improve uniformity in cell distribution and cell-cell/cell-ECM interactions.
The methods described here can be utilized to generate a broad array of tissue-specific bioscaffolds for use in cell culture and tissue-engineering applications. For example, in addition to the DAT, DDT, and DLV, our lab has successfully applied these techniques to generate 3D porous foams using decellularized bone, cartilage, nucleus pulposus, and annulus fibrosis, as well as commercially-available, insoluble collagen derived from bovine tendon. From an in vitro perspective, these bioscaffolds could be used as a basis for higher-fidelity 3D culture models for investigating cellular biology, physiology or disease pathology38, as bioactive substrates in high-throughput drug screening platforms39, or as instructive matrices for stem cell differentiation40,41. DAT, DDT and DLV foams fabricated at concentrations of 25 - 50 mg/mL are stable in long-term in vitro culture (tested up to 28 days). Further, all three types of microcarriers can support cell attachment and proliferation under dynamic conditions in a low-shear spinner culture system (10 - 15 rpm) for at least 2 weeks. For in vivo applications, the biocompatible and biodegradable ECM-derived foams and microcarriers hold promise as off-the-shelf products to stimulate constructive tissue remodeling and regeneration11,29. Further, the cell-adhesive scaffolds could be used as cell therapy delivery systems42,43. As an example, DAT foams were shown to promote angiogenesis and adipogenesis when seeded with allogeneic ASCs and implanted subcutaneously in an immunocompetent rat model29. Relative to the intact DAT, the more highly processed DAT foams degraded much more rapidly, with a 50% reduction in volume noted at 3 weeks as they became integrated with the host tissues, and almost complete resorption by 12 weeks. However, the foams also induced a more potent angiogenic response, suggesting that the enzyme-digested ECM had unique pro-regenerative effects. Similarly, the ECM-derived microcarriers could be used as in vitro cell culture substrates within dynamic culture systems and as injectable cell delivery vehicles11,30,44. More specifically, the small diameter and large surface area of the microcarriers could enable the delivery of a large quantity of cells in a small volume, while providing a matrix that may help to support cell viability and increase cell retention at the site of injection30. Prior to use in any living system, it is critical to ensure that the source ECM is substantially devoid of antigenic cellular components and/or potentially cytotoxic decellularization reagents that could trigger a negative host response7.
The proteolytic enzyme pepsin is commonly used in the preparation of ECM-derived hydrogels15. Pepsin is a non-specific protease that will digest collagen and other ECM proteins into small fragments45. While hydrogels fabricated from pepsin-digested ECM have been reported to have cell-instructive effects, a limitation is that these materials tend to be extremely mechanically weak46. In our initial development of the DAT microcarriers, we utilized a composite approach in which pepsin-digested DAT was combined with alginate and added dropwise into CaCl2 to form spherical beads30. The beads were subsequently photo-crosslinked and the alginate was extracted using sodium citrate. In addition to the requirement for chemical crosslinking, a key limitation was that the microcarriers fabricated with this approach had poor stability below a size range of 900 - 950 &#181;m30. In place of pepsin, the methods presented here utilize a more mild digestion of the ECM with the glycolytic enzyme &#945;-amylase, which is postulated to cleave carbohydrate groups from the telopeptide regions of collagen, thereby increasing solubility in acetic acid37. This approach enables the isolation of highly polymerized collagen that can be used to generate pure ECM-derived foams and microcarriers without the need for chemical crosslinking or other additives. These bioscaffolds are stabilized through physical interactions and hydrogen bonding between well-preserved collagen fibrils, similar to the collagen in the native ECM microenvironment.
The foams are a highly flexible platform that can be fabricated in a wide range of geometries depending on the specific mold selected. For cell culture studies, the foams may be cast directly in TCPS well plates, to form coatings or 3D scaffolds of varying thickness. To fabricate 3D foams with very uniform surfaces, it is recommended that a custom mold is designed that can be sealed on both sides with plastic or glass slides. Either minced or cryomilled ECM can be used to synthesize the foams. In general, we have found that the cryomilled foams tend to be macroscopically softer and have a more disrupted ultrastructure at lower concentrations31,36. Depending on the tissue source, the additional mechanical processing steps may cause alterations in the ECM composition that could impact cell function. For example, in our previous work, laminin was detected in minced DLV foams, but not cryomilled DLV foams31. In contrast, collagen I, collagen IV, laminin, and fibronectin were detected in both minced and cryomilled DAT foams36. In addition to the mechanical processing steps, the porosity and pore size of the foams can be tuned to some extent by varying the ECM suspension concentration and the freezing temperature47. In general, lower concentration foams (~ 10 - 15 mg/mL) are qualitatively more porous, but may contract rapidly and have poor stability in long-term culture31,36. Similarly, a slower freezing rate, typically achieved by a higher freezing temperature, can result in larger pores in the foams due to the size of the ice crystals formed during fabrication29. All of these parameters may influence cell interactions with the materials, including attachment, infiltration, and remodeling. For example, cell growth on foams that are fabricated with higher ECM concentrations may be limited to the surface regions, particularly with minced ECM sources and under static culture conditions36.
For the microcarriers, the key parameters that can be tuned are the ECM suspension concentration, needle gauge, and applied voltage, with higher concentrations typically yielding microcarriers that are more stable under long-term dynamic culture. Following the initiation of electrospraying, the ECM suspension droplets should quickly fall into the center of the flask, towards the direction of the aluminum foil collector. To prevent aggregation, it is important that the beads contact the liquid nitrogen prior to the foil. The distance between the needle and the surface of the liquid nitrogen can be adjusted to meet these requirements. It is important to note that optimization may be required depending on the properties of each specific ECM source, in particular in selecting the concentration range that will generate stable bioscaffolds. Another key factor is the decellularization protocol that is used to generate the starting materials, as decellularization methods that degrade the ECM or the presence of residual reagents (e.g., surfactants) may negatively impact the stability of the resultant foams and microcarriers. If challenges are encountered with bioscaffold stability, options that can be investigated include using a more gradual rehydration process, increasing the ECM suspension concentration, and exploring minced versus cryomilled ECM. Should all of these options fail to resolve the issue, it may be necessary to explore alternative decellularization protocols or ECM sources.
To ensure reproducibility during scaffold production, special care must be taken at certain steps in the protocol. When cryomilling the decellularized tissues, it is recommended that milling be conducted immediately after lyophilization in a dry environment to reduce the likelihood of particle aggregation due to the absorption of moisture from the environment. During microcarrier fabrication, it is suggested that the suspension is electrosprayed in small batches, with a maximum volume of 3 mL, to avoid issues with sample cooling that can result in clogging of the needle. Further, it is essential that the microcarriers are not permitted to thaw after the electrospraying process. To maintain their spherical geometry and mechanical stability, the microcarriers should be collected from the liquid nitrogen, transported in a liquid nitrogen-filled container, and immediately lyophilized. Finally, for both the foams and microcarriers, it is critical that the rehydration steps are performed slowly over a period of multiple days. Rapid rehydration can result in structural collapse on the macro- and/or micro-scale. Further, rehydration must occur slowly to prevent the formation of small air bubbles within the scaffold, which can require a significant amount of time to degas under light vacuum.
In conclusion, the methods presented in this paper can be used to fabricate a diverse array of tissue-specific foams and microcarriers comprised of pure, non-chemically crosslinked ECM. An advantage for biological researchers is that the bioscaffolds are easy to handle and can be processed similarly to tissues when performing analyses with techniques such as histology, immunohistochemistry, or gene and protein expression assays. In addition, the ECM-derived scaffolds can be enzymatically degraded to extract seeded cell populations or can be used directly as biodegradable and biocompatible cell delivery vehicles. Overall, this flexible platform technology holds great utility for numerous applications including for 3D cell culture studies investigating cell function, as cell expansion substrates, and as pro-regenerative bioscaffolds.

The extracellular matrix (ECM) is comprised of a complex 3D network of proteins, glycoproteins, and polysaccharides1. Once regarded as a predominantly structural framework, it is now well recognized that the ECM incorporates a diverse array of bioactive molecules with important functional roles2. Cell-ECM interactions can direct cell survival, adhesion, migration, proliferation, and differentiation3. While the major classes of ECM macromolecules are generally well conserved across tissues and species, each tissue has a unique matrix composition and architecture4. Overall, the tissue-specific ECM provides an instructive microenvironment that mediates function from the subcellular to the tissue/organ scale5.
Due to the critical role of the ECM in mediating cellular function, there has been increasing interest in the development of ECM-derived bioscaffolds for applications in tissue engineering and regenerative medicine. In particular, the method of decellularization has been extensively explored as a means of obtaining ECM from a wide range of tissues for use as a scaffolding material for tissue regeneration and cell delivery5,6,7. Decellularization typically involves a series of mechanical, chemical, and/or biological treatment stages targeted at removing cells and cellular components, while ideally causing minimal alterations to the 3D structure and composition of the ECM8. Through surveying the literature, various decellularization protocols can be identified for virtually every tissue in the body7.
While decellularized tissues can be used directly as implantable scaffolds or 3D cell culture substrates, cellular infiltration may be limited in tissues with a dense ECM structure9. Further, the natural heterogeneity in the ECM may cause variability in cell attachment and distribution within the decellularized matrices, which could potentially impact the cellular response10. Overall, while promising for some applications, applying decellularized tissues in their intact form offers limited versatility in terms of tuning scaffold properties including shape, porosity, and stiffness, as well as the mode of delivery for in vivo applications.
To circumvent these limitations, numerous research groups are applying further processing methods to generate customized scaffold formats using decellularized tissues as a base material. In the simplest form, this may involve cryomilling the decellularized tissues to generate injectable tissue-specific ECM particles11. These ECM particles may be incorporated as a cell-instructive component in composite scaffolds with other biomaterials, such as in situ crosslinking hydrogels12,13,14. In addition to mechanical processing, decellularized tissues can also be subjected to enzymatic digestion with proteolytic and/or glycolytic enzymes to fabricate ECM-derived hydrogels, foams, microcarriers, and coatings15,16,17, as well as to synthesize bioinks for 3D printing18.
In addition to tissue-engineering applications, ECM-derived bioscaffolds hold great potential for the generation of higher fidelity in vitro models for biological research. There is a significant need to develop 3D cell culture systems that better recapitulate the native cellular microenvironment19. Most in vitro cell culture studies to date are conducted on tissue culture polystyrene (TCPS), which has little correlation with the biologically complex and dynamic cellular milieu found within living tissues20. While convenient for studying cellular interactions within a controlled environment, culturing cells on these simplified rigid 2D substrates alters cell attachment and morphology, as well as both cell-cell and cell-ECM interactions21,22. The cellular adaptations observed on 2D TCPS can impact intracellular signaling pathways that regulate diverse cell functions including survival, proliferation, migration, and differentiation, raising questions of the relevance of 2D studies in modelling in vivo systems23. There has been increasing recognition that cellular behavior can vary greatly in 2D versus 3D systems24, and that biochemical and biomechanical signaling with the ECM are key mediators of cell function25. Many groups have attempted to overcome the limitations of established 2D systems by coating TCPS with ECM components such as collagen, laminin, and fibronectin. While these strategies can improve cell attachment and may alter cellular responses, these models remain limited by their 2D configuration that does not mimic the complex spatial organization or biochemistry of the native ECM26,27.
Our bioengineering laboratory has been interested in the development of ECM-derived bioscaffolds as substrates for 3-D cell culture and tissue-engineering applications. In particular, we have pioneered the use of decellularized adipose tissue (DAT) as a scaffolding platform for adipose regeneration28. Moreover, we have established methods for synthesizing 3D microcarriers and porous foams using DAT digested with the proteolytic enzyme pepsin or glycolytic enzyme &#945;-amylase29,30,31. Notably, we have demonstrated across all of these scaffold formats that the adipose-derived ECM provides an inductive microenvironment for the adipogenic differentiation of human adipose-derived stem/stromal cells (ASCs) in culture. More recently, we extended our fabrication methods to generate 3D porous foams from &#945;-amylase-digested porcine decellularized left ventricle (DLV) (decellularization methods adapted from Wainwright et al.32), and showed that they provide a supportive platform for inducing early cardiomyogenic marker expression in human pericardial fat-derived ASCs31.
This article describes in detail the methods for synthesizing non-chemically crosslinked 3D porous foams and microcarriers derived purely from &#945;-amylase-digested ECM for use as biologically complex 3D in vitro cell culture substrates and as biomaterials for tissue regeneration. In theory, any ECM source containing high molecular weight collagen may be used as the starting material for these techniques. To demonstrate the flexibility of this approach, the methods have been applied to generate tissue-specific bioscaffolds using human DAT, porcine decellularized dermal tissue (DDT)8, and porcine DLV as representative examples. Figure 1 provides a visual overview of the fabrication process for the ECM-derived foams and microcarriers.
<img alt="Figure 1" src="/files/ftp_upload/55436/55436fig1.jpg" /> 
Figure 1. Overview of the Method for the Production of the Tissue-specific ECM-derived Foams and Microcarriers. 1. Decellularized tissues, prepared following established decellularization protocols, can be used for tissue-specific ECM-derived bioscaffold fabrication. Macroscopic images are shown of hydrated human DAT (prepared as described in Flynn 201028), porcine DDT (prepared as described in Reing, J. E., et al. 20108), and porcine DLV (prepared as described in Wainwright et al. 201032), as representative examples of ECM sources that can be used as starting materials. Scale bars represent 3 cm. 2. The decellularized tissues are lyophilized, and then 3. mechanically minced. Scale bars represent 1 cm. 4. The minced ECM can then be cryomilled, which is optional for foam fabrication, but required for microcarrier synthesis. Scale bar represents 3 mm. 5. The minced or cryomilled ECM is then digested with &#945;-amylase and homogenized to create a homogenous ECM suspension. Scale bar represents 1 cm. 6a) For foam fabrication, the ECM suspension is transferred into a user-defined mold, frozen, and lyophilized to generate a porous 3D scaffold with a well-defined geometry. Scale bar represents 1 cm. 6b) For microcarrier fabrication, the cryomilled ECM suspension is electrosprayed to generate discrete spherical microcarriers. Scale bar represents 2 mm. 7. The foams and microcarriers can then be gradually rehydrated and seeded with cells. Representative images are shown of human ASCs (viable cells=green) seeded on a DAT foam (left) and DAT microcarrier (right). Scale bars represent 100 &#181;m. <a href="http://cloudflare.jove.com/files/ftp_upload/55436/55436fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

<table><tbody><tr><td>Acetic acid, glacial</td><td>BioShop</td><td>ACE222.500</td><td></td></tr><tr><td>Alligator clip leads</td><td>VWR</td><td>470149-728</td><td></td></tr><tr><td>Aluminium foil</td><td>Fisher Scientific</td><td>01-213-101</td><td></td></tr><tr><td>&amp;alpha;-amylase</td><td>Sigma</td><td>101074694</td><td>from Aspergillus aryzae</td></tr><tr><td>Analytical balance</td><td>Sartorius</td><td>CPA225D</td><td></td></tr><tr><td>Centrifuge</td><td>Thermo Scientific</td><td>75004251</td><td>With swinging bucket rotor for 15 &amp;amp; 50 mL centrifuge tubes</td></tr><tr><td>Centrifuge tubes (15 mL)</td><td>Sarstedt</td><td>62.554.205</td><td></td></tr><tr><td>Centrifuge tubes (50 mL)</td><td>Sarstedt</td><td>62.547.205</td><td></td></tr><tr><td>Collagen from bovine achilles tendon (insoluble)</td><td>Sigma</td><td>C9879&amp;nbsp;</td><td>Or similar insoluble collagen source; Can be used as an alternative to decellularized tissues to fabricate the foams and microcarriers</td></tr><tr><td>Cryomilling system</td><td>Retsch</td><td>20.745.0001</td><td>MM 400</td></tr><tr><td>Dessicator</td><td>Fisher Scientific</td><td>8624426</td><td>For lyophilized ECM and bioscaffold storage</td></tr><tr><td>DMEM: F12 Hams</td><td>Sigma</td><td>D6421</td><td>Used for proliferation media</td></tr><tr><td>Dewar flask</td><td>Fisher Scientific</td><td>10-196-6</td><td>Low form; volume range of 250 - 500 mL</td></tr><tr><td>Double distilled water (ddH&lt;sub&gt;2&lt;/sub&gt;O)</td><td></td><td></td><td>From Barnstead GenPure xCAD Water Purification System</td></tr><tr><td>D-PBS (Phosphate-buffered Saline)</td><td>Wisent</td><td>311425125</td><td></td></tr><tr><td>ECM (Extracellular Matrix)</td><td></td><td></td><td>Isolated from human adipose tissue, porcine dermis or porcine myocardium, as described in Flynn &lt;em&gt;et al.&lt;/em&gt; 2010, Reing &lt;em&gt;et al.&lt;/em&gt; 2010, and Wainwright &lt;em&gt;et al.&lt;/em&gt; 2010 (ref # 28, 8, 32)</td></tr><tr><td>Ethanol</td><td>Greenfield Specialty Alcohols Inc.</td><td>P016EAAN</td><td>Absolute</td></tr><tr><td>Fetal bovine serum (FBS)</td><td>Wisent</td><td>80150</td><td>Used for proliferation media</td></tr><tr><td>Forceps</td><td>VWR</td><td>37-501-32</td><td>For transferring the foams</td></tr><tr><td>Freezer (-20 &amp;deg;C)</td><td>VWR</td><td>97043-346</td><td></td></tr><tr><td>Freezer ( -80 &amp;deg;C)</td><td>Thermo Scientific</td><td>EXF40086A</td><td></td></tr><tr><td>Glass vials</td><td>Fisher Scientific</td><td>03-339-26D</td><td>To store lyophilized cryomilled ECM</td></tr><tr><td>Hand held homogenizer</td><td>Fisher Scientific</td><td>14-359-251</td><td>Speed: 8,000 - 30,000 rpm</td></tr><tr><td>Homogenizer accessories: saw tooth bottom generator probes</td><td>Fisher Scientific</td><td>14-261-17</td><td>10 x 95 mm</td></tr><tr><td>Liquid nitrogen</td><td></td><td></td><td>For electrospraying</td></tr><tr><td>Lyophilizer</td><td>Labconco</td><td>7750021</td><td>FreeZone4.5</td></tr><tr><td>Milling chamber</td><td>Retsch</td><td>02.462.0213</td><td>25 mL volume recommended</td></tr><tr><td>Milling balls</td><td>VWR</td><td>16003-606</td><td>10 mm diameter, stainless steel recommended</td></tr><tr><td>18 G needle</td><td>VWR</td><td>C ABD305185</td><td>For dispensing ECM suspension into moulds</td></tr><tr><td>Orbital incubator shaker</td><td>SciLogex</td><td>832010089999</td><td>Temperature controlled (37 &amp;deg;C)</td></tr><tr><td>Penicillin-streptomycin</td><td>Life Technologies</td><td>15140-122</td><td>Used for proliferation media</td></tr><tr><td>Pipet-Aid XP</td><td>Mandel Scientific</td><td>DRU-4-000-101</td><td></td></tr><tr><td>Retort stand</td><td>VWR</td><td>470019-526</td><td></td></tr><tr><td>Retort stand clamp</td><td>VWR</td><td>21573-606</td><td></td></tr><tr><td>Safety-Lok Syringe</td><td>BD</td><td>309606</td><td>3 mL Luer lock syringe for microcarrier fabrication and dispensing ECM suspension</td></tr><tr><td>Serological pipettes (10&amp;nbsp;mL)</td><td>Sarstedt</td><td>86.1254.001</td><td></td></tr><tr><td>Serological pipettes (25 mL)</td><td>Sarstedt</td><td>86.1685.001</td><td></td></tr><tr><td>Sodium chloride</td><td>BioShop</td><td>7647-14-5</td><td></td></tr><tr><td>Sodium phosphate monobasic</td><td>BioShop</td><td>10049-21-5</td><td></td></tr><tr><td>Scoopula</td><td>VWR</td><td>89259-968</td><td>For collecting microcarriers</td></tr><tr><td>Surgical scissors</td><td>VWR</td><td>82027-590</td><td></td></tr><tr><td>Syringe pump</td><td>VWR</td><td>10117-490</td><td>Microprocessor controlled</td></tr><tr><td>High voltage power supply</td><td>Gamma High Voltage Research</td><td>ES30P-5W/DDPM</td><td>Capable of recommended 15 - 25 kV voltage range</td></tr><tr><td>12-well plates</td><td>Fisher Scientific</td><td>12565321</td><td>For use as molds during foam fabrication; Other sizes or user-defined molds can also be selected</td></tr><tr><td>Winged infusion set</td><td>Terumo</td><td>22258092</td><td>30 cm tubing length, 25 G 3/4&quot; recommended; Other needle gauges can be used and may influence microcarrier diameter</td></tr></tbody></table>

fabrication of extracellular matrix-derived foams and microcarriers as tissue-specific cell culture and delivery platforms

Cell function is mediated by interactions with the extracellular matrix (ECM), which has complex tissue-specific composition and architecture. The focus of this article is on the methods for fabricating ECM-derived porous foams and microcarriers for use as biologically-relevant substrates in advanced 3D in vitro cell culture models or as pro-regenerative scaffolds and cell delivery systems for tissue engineering and regenerative medicine. Using decellularized tissues or purified insoluble collagen as a starting material, the techniques can be applied to synthesize a broad array of tissue-specific bioscaffolds with customizable geometries. The approach involves mechanical processing and mild enzymatic digestion to yield an ECM suspension that is used to fabricate the three-dimensional foams or microcarriers through controlled freezing and lyophilization procedures. These pure ECM-derived scaffolds are highly porous, yet stable without the need for chemical crosslinking agents or other additives that may negatively impact cell function. The scaffold properties can be tuned to some extent by varying factors such as the ECM suspension concentration, mechanical processing methods, or synthesis conditions. In general, the scaffolds are robust and easy to handle, and can be processed as tissues for most standard biological assays, providing a versatile and user-friendly 3D cell culture platform that mimics the native ECM composition. Overall, these straightforward methods for fabricating customized ECM-derived foams and microcarriers may be of interest to both biologists and biomedical engineers as tissue-specific cell-instructive platforms for in vitro and in vivo applications.

In the current study, we have fabricated ECM-derived foams and microcarriers using human DAT, porcine DDT, and porcine DLV as representative examples demonstrating that the techniques can be applied to generate tissue-specific bioscaffolds using a variety of decellularized tissues as ECM sources (Figure 1). For both foam and microcarrier fabrication, the Nishihara technique of collagen solubilization with the glycolytic enzyme &#945;-amylase37 was adapted to generate a viscous ECM suspension from the decellularized tissue starting materials, which is used to synthesize the bioscaffolds through controlled freezing and lyophilization procedures.
To fabricate the foams, the decellularized tissues can be processed through either mechanical mincing or cryomilling to increase the surface area prior to enzymatic digestion. Following &#945;-amylase treatment and homogenization, the resultant ECM suspension is dispensed into a user-defined mold, which is then frozen and lyophilized. The scaffolds can be stored stably in a dry state for an extended period of time. Prior to use in cell culture studies, the lyophilized scaffolds must be subjected to a controlled rehydration process that yields porous and highly-hydrated homogeneous foams derived from pure ECM (Figure 3A). If the foams are rehydrated too quickly, rapid swelling may damage delicate structural features, resulting in loss of integrity and structural collapse. In general, the foams will retain the shape defined by the original mold following rehydration and are stable without the need for chemical crosslinking. Figure 3B shows representative scanning electron microscope (SEM) images of the DAT, DDT, and DLV foams fabricated with cryomilled ECM at a concentration of 35 mg/mL and a freezing temperature of -80 &#176;C.
<img alt="Figure 3" src="/files/ftp_upload/55436/55436fig3.jpg" /> 
Figure 3. Representative Images of the DAT, DDT, and DLV Foams Fabricated with Cryomilled ECM Suspensions at a Concentration of 35 mg/mL and Frozen at -80 &#176;C. A: Macroscopic view of the DAT, DDT, and DLV milled foams synthesized in a 48-well tissue culture plate mold following rehydration. Scale bars represent 1 cm. B: SEM images of the DAT, DDT, and DLV foams showing a homogeneous porous ultrastructure. Scale bars represent 100 &#181;m. <a href="http://cloudflare.jove.com/files/ftp_upload/55436/55436fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
The cryomilled ECM suspensions can also be used to generate pure ECM-derived microcarriers via electrospraying techniques (Figure 2). For each ECM source, the suspension concentration, needle gauge, infusion rate, and voltage can be tuned to generate discrete spherical microcarriers ranging from 350 - 500 &#956;m in diameter following controlled rehydration (Figure 4A). While the microcarriers can be stored in a lyophilized state, it is recommended for ease of handling that they are dispensed or sieved to a desired size range following resuspension in ethanol. SEM imaging suggests that the microcarrier ultrastructure can vary depending on the decellularized tissue source (Figure 4B).
<img alt="Figure 4" src="/files/ftp_upload/55436/55436fig4.jpg" /> 
Figure 4. Representative Images of the DAT, DDT, and DLV Microcarriers Fabricated with Cryomilled ECM Suspensions at a Concentration of 35 mg/mL, an Infusion Rate of 0.5 mL/min, and an Applied Voltage of 20 kV. A: Macroscopic view of the hydrated DAT, DDT, and DLV microcarriers. Scale bars represent 4 mm. B: SEM images of the DAT, DDT, and DLV microcarriers showing that the ultrastructure and size can vary depending on the ECM source. Scale bars represent 100 &#181;m. <a href="http://cloudflare.jove.com/files/ftp_upload/55436/55436fig4large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
The mechanical properties of the scaffolds are dependent on the ECM source, the method of processing applied (i.e. mincing versus cryomilling), the ECM suspension concentration, and the freezing temperature. In general, the scaffolds are soft and compliant, with Young&#39;s moduli in the range of 1 - 5 kPa reported for the DAT (50 &#38; 100 mg/mL)29 and DLV foams (20 - 50 mg/mL)31, and &#60; 1 kPa for the microcarriers. The cryomilled foams are typically softer than the minced foams due to their more disrupted nature. Specialized mechanical testing systems equipped with highly-sensitive load cells are needed for accurate characterization of the compressive properties. Typically, the foams and microcarriers would have lower moduli than the native decellularized tissues due to the additional processing steps involved in fabrication including enzymatic digestion and homogenization, as well as the non-covalently crosslinked nature of the scaffolds. However, this can vary depending on the tissue of interest. For example, in previous work, we found that minced DAT foams fabricated at high ECM concentrations (100 mg/mL) had similar moduli to native adipose tissue29.
The rehydrated ECM-derived foams and microcarriers can be seeded with cells under static or dynamic culture conditions to provide a cell supportive platform for in vitro cell culture studies and/or in vivo cell delivery. While the scaffolds generally support cell attachment, the seeding efficiency will depend on the ECM source, the scaffold geometry and porosity, and the cell type of interest. As such, the seeding methods and densities will require optimization depending on the user-defined conditions. For the foams described above, we recommend a starting cell concentration in the range of 0.25 - 1 x 106 cells/scaffold, with dynamic seeding on an orbital shaker to enhance cell infiltration. For the microcarriers, we suggest an initial seeding density in the range of 25,000 - 50,000 cells/mg of microcarriers, with seeding performed under dynamic conditions in a spinner culture flask11. The images shown at the bottom of Figure 1 represent human ASCs seeded on a DAT foam (left) or DAT microcarrier (right, prelabeled with an amine-reactive dye and appearing blue13), as visualized by confocal microscopy using a fluorescent cell viability stain (live cells = green, dead cells = red; Scale bars represent 100 &#181;m). Confocal microscopy can be used to visualize cells seeded on the surface of foams up to 2 mm in thickness, but visualization into the central regions of the scaffolds is limited by their opaque nature. However, the foams and microcarriers can be treated as tissues and paraffin-embedded or cryo-sectioned for histological and immunohistochemical analyses to visualize cell distribution and marker expression.

Watch this Scientific Journal Video about Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms at JoVE.com

Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms

The tissue-specific extracellular matrix (ECM) is a key mediator of cell function. This article describes methods for synthesizing pure ECM-derived foams and microcarriers that are stable in culture without the need for chemical crosslinking for applications in advanced 3D in vitro cell culture models or as pro-regenerative bioscaffolds.

Cell function is mediated by interactions with the extracellular matrix (ECM), which has complex tissue-specific composition and architecture. The focus ...

fabrication-extracellular-matrix-derived-foams-microcarriers-as

Research

JoVE Journal

Bioengineering

13.4K Views.  The University of Western Ontario.  Het weefsel-specifieke extracellulaire matrix (ECM) is een sleutelmediator van celfunctie. Dit artikel beschrijft werkwijzen voor het synthetiseren van zuiver ECM afgeleide schuimen en microdragers die stabiel in cultuur zonder de noodzaak voor chemische verknoping voor toepassingen in geavanceerde 3D in vitro celkweekmodellen of pro-regeneratieve bioscaffolds. 

Video: Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms

Microfabricated Platforms for Mechanically Dynamic Cell Culture

The ability to systematically probe in vitro cellular response to combinations of mechanobiological stimuli for tissue engineering, drug discovery or fundamental cell biology studies is limited by current bioreactor technologies, which cannot simultaneously apply a variety of mechanical stimuli to cultured cells. In order to address this issue, we have developed a series of microfabricated platforms designed to screen for the effects of mechanical stimuli in a high-throughput format. In this protocol, we demonstrate the fabrication of a microactuator array of vertically displaced posts on which the technology is based, and further demonstrate how this base technology can be modified to conduct high-throughput mechanically dynamic cell culture in both two-dimensional and three-dimensional culture paradigms.

In this protocol, we demonstrate the fabrication of a microactuator array of vertically displaced posts on which the technology is based, and how this base technology can be modified to conduct high-throughput mechanically dynamic cell culture in both two-dimensional and three-dimensional culture paradigms.

The ability to systematically probe in vitro cellular response to combinations of mechanobiological stimuli for tissue engineering, drug discovery or ...

Synthesis of Biocompatible Liquid Crystal Elastomer Foams as Cell Scaffolds for 3D Spatial Cell Cultures

Here, we present a step-by-step preparation of a 3D, biodegradable, foam-like cell scaffold. These scaffolds were prepared by cross-linking star block co-polymers featuring cholesterol units as side-chain pendant groups, resulting in smectic-A (SmA) liquid crystal elastomers (LCEs). Foam-like scaffolds, prepared using metal templates, feature interconnected microchannels, making them suitable as 3D cell culture scaffolds. The combined properties of the regular structure of the metal foam and of the elastomer result in a 3D cell scaffold that promotes not only higher cell proliferation compared to conventional porous templated films, but also better management of mass transport (i.e., nutrients, gases, waste, etc.). The nature of the metal template allows for the easy manipulation of foam shapes (i.e., rolls or films) and for the preparation of scaffolds of different pore sizes for different cell studies while preserving the interconnected porous nature of the template. The etching process does not affect the chemistry of the elastomers, preserving their biocompatible and biodegradable nature. We show that these smectic LCEs, when grown for extensive time periods, enable the study of clinically relevant and complex tissue constructs while promoting the growth and proliferation of cells.

This study presents a methodology to prepare 3D, biodegradable, foam-like cell scaffolds based on biocompatible side-chain liquid crystal elastomers (LCEs). Confocal microscopy experiments show that foam-like LCEs allow for cell attachment, proliferation, and the spontaneous alignment of C2C12s myoblasts.

Here, we present a step-by-step preparation of a 3D, biodegradable, foam-like cell scaffold. These scaffolds were prepared by cross-linking star block ...

3D Microtissues for Injectable Regenerative Therapy and High-throughput Drug Screening

To upgrade traditional 2D cell culture to 3D cell culture, we have integrated microfabrication with cryogelation technology to produce macroporous microscale cryogels (microcryogels), which can be loaded with a variety of cell types to form 3D microtissues. Herein, we present the protocol to fabricate versatile 3D microtissues and their applications in regenerative therapy and drug screening. Size and shape-controllable microcryogels can be fabricated on an array chip, which can be harvested off-chip as individual cell-loaded carriers for injectable regenerative therapy or be further assembled on-chip into 3D microtissue arrays for high-throughput drug screening. Due to the high elastic nature of these microscale cryogels, the 3D microtissues exhibit great injectability for minimally invasive cell therapy by protecting cells from mechanical shear force during injection. This ensures enhanced cell survival and therapeutic effect in the mouse limb ischemia model. Meanwhile, assembly of 3D microtissue arrays in a standard 384-multi-well format facilitates the use of common laboratory facilities and equipment, enabling high-throughput drug screening on this versatile 3D cell culture platform.

This protocol describes the fabrication of elastic 3D macroporous microcryogels by integrating microfabrication with cryogelation technology. Upon loading with cells, 3D microtissues are generated, which can be readily injected in vivo to facilitate regenerative therapy or assembled into arrays for in vitro high-throughput drug screening.

To upgrade traditional 2D cell culture to 3D cell culture, we have integrated microfabrication with cryogelation technology to produce macroporous ...

Custom Engineered Tissue Culture Molds from Laser-etched Masters

As the field of tissue engineering has continued to mature, there has been increased interest in a wide range of tissue parameters, including tissue shape. Manipulating tissue shape on the micrometer to centimeter scale can direct cell alignment, alter effective mechanical properties, and address limitations related to nutrient diffusion. In addition, the vessel in which a tissue is prepared can impart mechanical constraints on the tissue, resulting in stress fields that can further influence both the cell and matrix structure. Shaped tissues with highly reproducible dimensions also have utility for in vitro assays in which sample dimensions are critical, such as whole tissue mechanical analysis.
This manuscript describes an alternative fabrication method utilizing negative master molds prepared from laser etched acrylic: these molds perform well with polydimethylsiloxane (PDMS), permit designs with dimensions on the centimeter scale and feature sizes smaller than 25 &#181;m, and can be rapidly designed and fabricated at a low cost and with minimal expertise. The minimal time and cost requirements allow for laser etched molds to be rapidly iterated upon until an optimal design is determined, and to be easily adapted to suit any assay of interest, including those beyond the field of tissue engineering.

Herein we present a rapid, facile, and low-cost method for fabricating custom polydimethylsiloxane molds that can be used for producing hydrogel-based engineered tissues with complex geometries. We additionally describe results from mechanical and histological assessments conducted on engineered cardiac tissues produced using this technique.

As the field of tissue engineering has continued to mature, there has been increased interest in a wide range of tissue parameters, including tissue ...

Recombinant Collagen I Peptide Microcarriers for Cell Expansion and Their Potential Use As Cell Delivery System in a Bioreactor Model

Tissue engineering is a promising field, focused on developing solutions for the increasing demand on tissues and organs regarding transplantation purposes. The process to generate such tissues is complex, and includes an appropriate combination of specific cell types, scaffolds, and physical or biochemical stimuli to guide cell growth and differentiation. Microcarriers represent an appealing tool to expand cells in a three-dimensional (3D) microenvironment, since they provide higher surface-to volume ratios and mimic more closely the in vivo situation compared to traditional two-dimensional methods. The vascular system, supplying oxygen and nutrients to the cells and ensuring waste removal, constitutes an important building block when generating engineered tissues. In fact, most constructs fail after being implanted due to lacking vascular support. In this study, we present a protocol for endothelial cell expansion on recombinant collagen-based microcarriers under dynamic conditions in spinner flask and bioreactors, and we explain how to determine in this setting cell viability and functionality. In addition, we propose a method for cell delivery for vascularization purposes without additional detachment steps necessary. Furthermore, we provide a strategy to evaluate the cell vascularization potential in a perfusion bioreactor on a decellularized&#160;biological matrix. We believe that the use of the presented methods could lead to the development of new cell-based therapies for a large range of tissue engineering applications in the clinical practice.

We propose a cell expansion protocol on macroporous microcarriers and their use as delivery system in a perfusion bioreactor to seed a decellularized tissue matrix. We also include different techniques to determine cell proliferation and viability of cells cultured on microcarriers. Furthermore, we demonstrate functionality of cells after bioreactor cultures.

Tissue engineering is a promising field, focused on developing solutions for the increasing demand on tissues and organs regarding transplantation ...

Fabrication of a Multiplexed Artificial Cellular MicroEnvironment Array

Cellular microenvironments consist of a variety of cues, such as growth factors, extracellular matrices, and intercellular interactions. These cues are well orchestrated and are crucial in regulating cell functions in a living system. Although a number of researchers have attempted to investigate the correlation between environmental factors and desired cellular functions, much remains unknown. This is largely due to the lack of a proper methodology to mimic such environmental cues in vitro, and simultaneously test different environmental cues on cells. Here, we report an integrated platform of microfluidic channels and a nanofiber array, followed by high-content single-cell analysis, to examine stem cell phenotypes altered by distinct environmental factors. To demonstrate the application of this platform, this study focuses on the phenotypes of self-renewing human pluripotent stem cells (hPSCs). Here, we present the preparation procedures for a nanofiber array and the microfluidic structure in the fabrication of a Multiplexed Artificial Cellular MicroEnvironment (MACME) array. Moreover, overall steps of the single-cell profiling, cell staining with multiple fluorescent markers, multiple fluorescence imaging, and statistical analyses, are described.

This article describes the detailed methodology to prepare a Multiplexed Artificial Cellular MicroEnvironment (MACME) array for high-throughput manipulation of physical and chemical cues mimicking in vivo cellular microenvironments and to identify the optimal cellular environment for human pluripotent stem cells (hPSCs) with single-cell profiling.

Cellular microenvironments consist of a variety of cues, such as growth factors, extracellular matrices, and intercellular interactions. These cues are ...

Production of Extracellular Matrix Fibers via Sacrificial Hollow Fiber Membrane Cell Culture

Engineered scaffolds derived from extracellular matrix (ECM) have driven significant interest in medicine for their potential in expediting wound closure and healing. Extraction of extracellular matrix from fibrogenic cell cultures in vitro has potential for generation of ECM from human- and potentially patient-specific cell lines, minimizing the presence of xenogeneic epitopes which has hindered the clinical success of some existing ECM products. A significant challenge in in vitro production of ECM suitable for implantation is that ECM production by cell culture is typically of relatively low yield. In this work, protocols are described for the production of ECM by cells cultured within sacrificial hollow fiber membrane scaffolds. Hollow fiber membranes are cultured with fibroblast cell lines in a conventional cell medium and dissolved after cell culture to yield continuous threads of ECM. The resulting ECM fibers produced by this method can be decellularized and lyophilized, rendering it suitable for storage and implantation.

The goal of this protocol is production of whole extracellular matrix fibers targeted for wound repair which are suitable for preclinical evaluation as part of a regenerative scaffold implant. These fibers are produced by the culture of fibroblasts on hollow fiber membranes and extracted by dissolution of the membranes.

Engineered scaffolds derived from extracellular matrix (ECM) have driven significant interest in medicine for their potential in expediting wound closure ...

3D Printing of In Vitro Hydrogel Microcarriers by Alternating Viscous-Inertial Force Jetting

Microcarriers are beads with a diameter of 60-250 &#181;m and a large specific surface area, which are commonly used as carriers for large-scale cell cultures. Microcarrier culture technology has become one of the main techniques in cytological research and is commonly used in the field of large-scale cell expansion. Microcarriers have also been shown to play an increasingly important role in in vitro tissue engineering construction and clinical drug screening. Current methods for preparing microcarriers include microfluidic chips and inkjet printing, which often rely on complex flow channel design, an incompatible two-phase interface, and a fixed nozzle shape. These methods face the challenges of complex nozzle processing, inconvenient nozzle changes, and excessive extrusion forces when applied to multiple bioink. In this study, a 3D printing technique, called alternating viscous-inertial force jetting, was applied to enable the construction of hydrogel microcarriers with a diameter of 100-300 &#181;m. Cells were subsequently seeded on microcarriers to form tissue engineering modules. Compared to existing methods, this method offers a free nozzle tip diameter, flexible nozzle switching, free control of printing parameters, and mild printing conditions for a wide range of bioactive materials.

3D Printing of In Vitro Hydrogel Microcarriers by Alternating Viscous-Inertial Force Jetting

Presented here is a mild 3D printing technique driven by alternating viscous-inertial forces to enable the construction of hydrogel microcarriers. Homemade nozzles offer flexibility, allowing easy replacement for different materials and diameters. Cell binding microcarriers with a diameter of 50-500 &#181;m can be obtained and collected for further culturing.

Microcarriers are beads with a diameter of 60-250 &#181;m and a large specific surface area, which are commonly used as carriers for large-scale cell ...

Bioscaffold Fabrication by Electrospraying: A Technique to Generate Microcarrier Scaffolds Derived from Extracellular Matrix of Decellularized Tissue

Source: Kornmuller, A. et al. <a href="https://www.jove.com/video/55436" target="_blank">Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms.</a> J. Vis. Exp. (2017)
This video demonstrates the procedure of extracellular matrix-derived microcarrier fabrication by electrospraying. These microcarriers simulate the native tissue-specific microenvironment and are stable in long-term 3D in vitro cell culture models.

Source: Kornmuller, A. et al. Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms. ...

JoVE Encyclopedia of Experiments

Cancer Research

Head and Neck Cancer

Assays & techniques

ECM Suspension Preparation: A Technique to Obtain Homogenous Suspension from Tissue-derived Extracellular Matrix

Source: Kornmuller, A. et al. <a href="https://www.jove.com/video/55436" target="_blank">Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms.</a> J. Vis. Exp. (2017)
This video describes the preparation of a homogenized and digested extracellular matrix suspension from decellularized and lyophilized tissues. This technique helps in fabricating ECM-derived porous foams and microcarriers for use as substrates in advanced 3D cell culture models.

Fabrication of Extracellular Matrix-derived Foams and Microcarriers as Tissue-specific Cell Culture and Delivery Platforms

Samenvatting

Meer video's verkennen