This work was partially supported by the Research Corporation for Science Advancement (Grant 10626), National Science Foundation (DMR-1308084), and the San Francisco State University internal award to W. M. We thank our collaborator Paul M. Chaikin from NYU for helpful discussions in experimental design and for providing the VNA system for us to use on site at SFSU. We thank our theoretical collaborators, the inventor of the HD PBG materials, Marian Florescu, Paul M. Steinhardt, and Sal Torquato for various discussions and for providing us the design of the HD point pattern and continuous discussions.

1. Design a 2D Hyperuniform Disordered Dielectric Structure11
<ol>
	<li>Chose a subclass of 2D hyperuniform disorder point pattern (blue circles in Figure 2) and partition it (blue lines in Figure 2) using Delaunay tessellation. A 2D Delaunay tessellation is a triangulation that maximizes the minimum angle for each triangle formed and guarantees there are no other points inside the circumcircle of each triangle11.</li>
	<li>Locate the centroids of each triangle (solid black circles in Figure 2); these centroids are the locations of the dielectric rods of radius r11.</li>
	<li>Connect the centroids of the neighboring triangles (thick red lines in Figure 2) to generate cells around each point11.</li>
	<li>Create the CAD design file for the 2 cm tall HD base template with holes and slots on which the rods and walls will be assembled14. Use an HD pattern with the average inner-rod spacing of a=1.33 cm and set the hole-radius to be 2.5 mm and slot-width to be 0.38 mm. Set the depth for holes and slots to be 1 cm deep to stabilize the inserted rods and walls.</li>
	<li>Create a similar CAD design file for the crystalline base template (a square lattice) for comparison14. Use the same lattice constant as the HD structure (1.33 cm) and the same hole-radius (2.5 mm) and slot-width (0.38 mm).</li>
</ol>
2. Sample Construction and Preparation
<ol>
	<li>Fabricate the template. Manufacture the HD and Square lattice plastic bases by using a stereolithography machine that produces a solid plastic model by ultraviolet laser photo-polymerization. Use a clear resin, for example polycarbonate-like plastic. The resolution is 0.1 mm in both lateral and vertical directions. (See Figure 3, center panel).</li>
	<li>Prepare the building blocks: Order commercially available Alumina rods and thin walls cut to precise dimensions (see Figure 3, left panel). Set the height to be no less than a few wavelengths, for example 10.0 cm. The diameter of all rods is 5.0 mm. Wall thickness is always 0.38 mm and widths vary from 1.0 mm to 5.3 mm, with 0.2 mm increments. &#160;&#160;</li>
	<li>Construct the defect-free test structure for bandgap measurements. Insert rods and walls into the base for the desired structure architecture. The side view of the constructed network of both rods and walls on the polymer base is shown in Figure 3, right panel.</li>
	<li>Design a waveguide or a cavity defect: Create various waveguides through the samples by directly removing or modifying rods and walls along the designed path, as shown in Figures 9A and 9C. The modular design of the samples allows fast and easy modification of point and line or curve defects.&#160;</li>
</ol>
3. Major Instruments
<ol>
	<li>Use a synthesized sweeper (microwave generator) to provide microwaves with frequency coverage of 45 MHz to 50 GHz with precise 1 Hz frequency resolution. Connect the generator to an S-parameter test set to measure transmission parameters between the two ports (terminals). Use General Purpose Interface Bus (GPIB) links and cables for communications between the sweeper and the test-set.</li>
	<li>Use a Microwave Vector Network analyzer (VNA) to process the signal received from the S-parameter test-set and to measure the signal&#8217;s magnitude and the phase. Set the S-parameter test set to S21 mode so that the VNA outputs a data file containing the real and imaginary components of the detected E-field at port 1 with respect to the source signal from port 2 as a function of frequency</li>
</ol>
4. Instrument Setup
<ol>
	<li>Start/End Frequency.&#160; Select the appropriate start and end values of the frequency range for the measurement using the VNA user menu. The relevant frequency range associated with PBG depends on the dielectric index of lattice spacing of the samples. Use 7 GHz to 15 GHz microwaves for the Alumina samples with lattice spacing a=1.33 cm.</li>
	<li>Averaging Factor. Vector analyzer computes each data point based on the average of multiple measurements to reduce random noise. Select an averaging factor from 512 to 4,096 by inputting the desired multiple on the VNA keypad. Choose a higher averaging factor to minimize noise and chose a lower averaging factor for a quicker scan.</li>
	<li>Number of Points. For measurements in the 7 GHz to 15 GHz range, chose the maximum number of data points (801), on the VNA on-screen menu, to achieving a frequency resolution of 10 MHz.</li>
	<li>Calibration. Calibrate the system by directly measuring the relative transmission ratio, and normalize it against the transmission of a pre-calibrated setting with the same background and without the sample between the horn antennas. By doing this, all the background loss due to the cables, adaptors, waveguides, and antennas can be eliminated, and the relative transmission ratio with and without the tested sample is directly recorded.&#160;&#160;
	<ol>
		<li>For bandgap measurements, measure the microwave transmission through free space between the horns facing each other at the distance of 28a and save the results as a calibration set in the VNA. Before taking data for the actual experiment with a structure between the horns, turn on the calibration set by selecting &#8220;CALIBRATION ON&#8221; on the VNA monitor. Data calculated by the VNA will be automatically normalized against the calibration set and return the ratio of transmission power with and without the sample in place.</li>
		<li>For waveguide measurements, a meaningful calibration is not well-defined, since the transmission through the sample waveguides can easily exceed the calibrated transmission between the two horns in free space. Turn off calibration on the VNA monitor and record the raw transmission, which is the detected signal over the source signal. Place the horns right next to the waveguide channel openings to achieve the best coupling efficiency.</li>
	</ol>
	</li>
</ol>
5. Experimental Setup
<ol>
	<li>Configure the experimental setup shown in Figure 4. Use high quality semi-flexible coaxial cables to connect the S-parameter test-set ports with input/output waveguides. Connect pyramidal horn antennas with the ports through rectangular single mode waveguides and adaptors to ensure the radiation to be linearly polarized, The E-field of the radiation from the horn is parallel to the short edge of the horn.</li>
	<li>For bandgap measurements: Adhere to the following steps to measure the transmission through the defect-free samples to characterize the PBG of the defect free samples.
	<ol>
		<li>Align the horns vertically and horizontally to face each other. Arrange the horns at a far enough distance, such as 20 times of the average wavelength, so that the far-field radiation reaching the sample can be approximated to plane waves. Calibrate the transmission between the facing horns in free space without the testing sample and store it in calibration memory.</li>
		<li>Place defect-free structures made of rods and walls on the rotating stage in between the two facing horns. Turn on the calibration set recorded into VNA memory during step 5.2.1. The system is now ready to measure the relative transmission ratio through the sample normalized against the transmission power of the calibrated memory.</li>
	</ol>
	</li>
	<li>For waveguides and cavity defects measurements: Adhere to the following steps to setup the experiments:
	<ol>
		<li>Construct various waveguides and cavities by removing or replacing rods and walls in the defect-free structures, as shown in Figures 9A and 9C.&#160;&#160;&#160;&#160;</li>
		<li>Arrange the horns as close to the channel openings as possible to ensure good coupling into the channel. For curved and bent channels center the horns in the middle of the channel with the edge parallel to the opening.</li>
		<li>Turn off calibration. Now the VNA system is ready to measure and record the raw transmission ratio of the detected power at port 2 over the source power at port 1.</li>
	</ol>
	</li>
</ol>
6. Data Acquisition and Analysis
<ol>
	<li>Characterize the angular dependence of the photonic properties of the samples:
	<ol>
		<li>Place structures made of rods and walls with a nearly circular boundary on a rotating stage in between the two facing horns.</li>
		<li>Make sure that the calibration saved in the VNA memory is turned on in step 5.2.2. Zero the angle scale on the rotating stage and measure transmission through the structure. After the initial measurement at zero incident angle, rotate the sample and measure the transmission in equal angle increments, such as every 2&#176;&#160;until 180&#176;&#160;rotation is reached.</li>
	</ol>
	</li>
	<li>Characterize the polarization dependence of the photonic properties for the samples: 
	Perform all measurements described above in two different polarizations respectively, by changing the horn opening orientations. For TM polarization, set the horns&#8217; short edge (the E-field direction) perpendicular to the horizontal plane of the sample base and parallel to the rods. For TE polarization, rotate the horns 90 degrees, so that their short edges (the E-field direction) are in the horizontal plane.</li>
	<li>Characterize various waveguides channels: Make sure that the calibration is turned off in step 5.3.3. Place the horns next to the sample for best coupling. Measure the transmission through various channels constructed by removing and/or replacing rods and walls along the channel path. While monitoring the transmission signal on the VNA in real time, modify the channel path by adding and removing extra rods and walls for optimized transmission power or desired filtering bandwidth.</li>
	<li>Perform analogous measurements similar to what are described above on a square lattice photonic crystal for comparison.</li>
	<li>Data analysis. Analyze and graph the data using a computer program, such as MATLAB.&#160; Plot measured transmission as a function frequency (line plot), such as Figure 5, Figure 2, and Figure 9B and 9D to study the stopgap through the samples or transmission pass though the waveguide channels.&#160; Plot transmission as a function of frequency and angle (color contour plot) to analyze the stop bands characteristics of the structures and their angular dependence, as shown in Figure 6 and Figure 7.</li>
	<li>This protocol suggests presenting the measured transmission through the samples as a function of frequency and incident angle in polar coordinates12, in order to directly visualize the rotational symmetries and angular dependence of photonic properties. Generate the polar-coordinate plots to directly show the Brillouin zone boundaries of crystalline structures and reveal the relationship between PBG formation and Bragg scattering planes (Brillouin zone boundaries) in crystals and quasicrystals.</li>
</ol>

<ol>
	<li>Strut, J. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> The propagation of waves through a Medium Endowed with a Periodic structure. Philosophical magazine. XXIV, 145-159 (1887).</li><li>Yablonovitch, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Inhibited+spontaneous+emission+in+solid-state+physics+and+electronics.">Inhibited spontaneous emission in solid-state physics and electronics.</a> Phys. Rev. Lett. 58, 2059-2062 (1987).</li><li>Yablonovitch, E., Gmitter, T. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photonic+band+structure:+The+face-centered-cubic+case.">Photonic band structure: The face-centered-cubic case.</a> Phys. Rev. Lett. 63, 1950-1953 (1989).</li><li>Sajeev, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Strong+localization+of+photons+in+Certain+Disordered+Dielectric+super+lattices.">Strong localization of photons in Certain Disordered Dielectric super lattices.</a> Phys. Rev. Lett. 58, 2486-2489 (1987).</li><li>Joannopoulos, J., Johnson, S. G., Winn, J. N., Mead, R. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Photonic Crystals: Molding the Flow of Light. , 243-248 (2008).</li><li>Noda, S., Chutinan, A., Trappin Imada, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=emission+of+photons+by+a+single+defect+in+a+photonic+bandgap+structure.">emission of photons by a single defect in a photonic bandgap structure.</a> Nature. 407, 608-610 (2000).</li><li>Cao, H., Zhao, Y. G., Ho, S. T., Seeling, E. W., Wang, Q. H., Chang, R. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Random+laser+action+in+semiconductor+powder.">Random laser action in semiconductor powder.</a> Phys. Rev. Lett. 82, 2278-2281 (1999).</li><li>Chutinan, A., John, S., Toader, O. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Diffractionless+flow+of+light+in+all-optical+microchips.">Diffractionless flow of light in all-optical microchips.</a> Phys. Rev. Lett. 90, 123901 (2003).</li><li>Vynck, K., Burresi, M., Riboli, F., Wiersma, D. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photon+management+in+two-dimensional+disordered+media.">Photon management in two-dimensional disordered media.</a> Nature Mater. 11, 1017-1022 (2012).</li><li>Ishizaki, K., Koumura, M., Suzuki, K., Gondaira, K., Noda, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Realization+of+three-dimensional+guiding+of+photons+in+photonic+crystals.">Realization of three-dimensional guiding of photons in photonic crystals.</a> Nature Photon. 7, 133-137 (2013).</li><li>Florescu, M., Torquato, S., Steinhardt, P. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Designer+disordered+materials+with+large,+complete+PBGs.">Designer disordered materials with large, complete PBGs.</a> Proc. Natl. Acad. Sci. 106, 20658-20663 (2009).</li><li>Man, W., Megens, M., Steinhardt, P. J., Chaikin, P. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Experimental+measurement+of+the+photonic+properties+of+icosahedral+quasicrystals.">Experimental measurement of the photonic properties of icosahedral quasicrystals.</a> Nature. 436, 993-996 (2005).</li><li>Torquato, S., Stillinger, F. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Local+density+fluctuations,+hyperuniformity,+and+order+metrics.">Local density fluctuations, hyperuniformity, and order metrics.</a> Phys. Rev. E. 68, 041113 (2003).</li><li>Man, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Isotropic+band+gaps+and+freeform+waveguides+observed+in+hyperuniform+disordered+photonic+solids.">Isotropic band gaps and freeform waveguides observed in hyperuniform disordered photonic solids.</a> Proc. Natl. Acad. Sci. 110, 15886-15891 (2013).</li><li>Freeform wave-guiding and tunable frequency splitting in isotropic disordered photonic band gap materials. Frontiers in Optics 2012/Laser Science XXVIII, OSA Technical Digest (online) Available from: <a target="_blank" href="https://www.osapublishing.org/abstract.cfm?uri=FiO-2012-FTh2G.5">https://www.osapublishing.org/abstract.cfm?uri=FiO-2012-FTh2G.5</a> (2012)</li><li>Cavity Modes Study in Hyperuniform Disordered Photonic Bandgap Materials. Frontiers in Optics 2012/Laser Science XXVIII, OSA Technical Digest (online) Available from: <a target="_blank" href="https://www.osapublishing.org/abstract.cfm?uri=FiO-2012-FTh3F.4">https://www.osapublishing.org/abstract.cfm?uri=FiO-2012-FTh3F.4</a> (2012)</li><li>Man, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photonic+band+gap+in+isotropic+hyperuniform+disordered+solids+with+low+dielectric+contrast.">Photonic band gap in isotropic hyperuniform disordered solids with low dielectric contrast.</a> Opt. Express. 21, 19972-19981 (2013).</li><li>Man, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Experimental+observation+of+photonic+bandgaps+in+Hyperuniform+disordered+materials.">Experimental observation of photonic bandgaps in Hyperuniform disordered materials.</a> , (2010).</li><li>Schelew, E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+of+integrated+planar+photonic+circuits+fabricated+by+a+CMOS+foundry.">Characterization of integrated planar photonic circuits fabricated by a CMOS foundry.</a> Journal of Lightwave Technology. 31 (2), 239 (2013).</li><li>Guo, Y. B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Sensitive+molecular+binding+assay+using+a+photonic+crystal+structure+in+total+internal+reflection.">Sensitive molecular binding assay using a photonic crystal structure in total internal reflection.</a> Opt. Express. 16, 11741-11749 (2008).</li></ol>

The authors have nothing to disclose.

Starting from a hyperuniform disordered point pattern, 2D HD structures consisting rods and/or wall network can be designed to obtain a complete PBG for all polarization11. Based on the design, we constructed a template with holes and slots for assembling 2D Alumina rods and walls structures at cm-scale which could be tested with microwaves. We chose to work with microwaves, because cm-scale building blocks, such as Alumina rods and walls, are inexpensive, and easily handled. We have experimentally demonstrate...

The existence of a bandgap for photons has been the focus of many scientific works, starting from the earlier studies done by Lord Rayleigh on the one-dimensional stop-band, a range of frequencies that are forbidden from propagation through a periodic medium1. Research into electromagnetic wave (EM) propagation in periodic structures has really flourished in the last two decades after the seminal publications of E. Yablonovitch2,3 and S. John4. The term &#8220;photonic crystal&#8221; was coined by Yablonovitch to describe the periodic dielectric structures that possessed a photonic bandgap (PBG). &#160;

Photonic crystals are periodic dielectric structures possessing discrete translational symmetries, rendering them invariant under translations in directions of periodicity. When this periodicity is matched with the wavelengths of incoming electromagnetic (EM) waves, a band of frequencies becomes highly attenuated and may stop propagating. If wide enough, the ranges of the forbidden frequencies, also called stop bands, may overlap in all directions to create a PBG, forbidding the existence of photons of certain frequencies.

Conceptually, EM wave propagation in photonic crystals is similar to electron wave propagation in semiconductor materials, which have a forbidden region of electron energies, also known as a bandgap. Similar to the way engineers have employed semiconductors to control and modify the flow of electrons through semiconductors, PBG materials can be used for various applications requiring optical control. For example, PBG materials can confine light of certain frequencies in wavelength size cavities, and guide or filter light along line defects in them5. PBG materials are suggested to be used for controlling the flow of light for applications in telecommunication6, lasers7, optical circuits and optical computing8, and solar energy harvesting9.

A two-dimensional (2D) square lattice photonic crystal has 4-fold rotational symmetry. EM waves entering the crystal at different angles of incidence (for example, 0&#176; and 45&#176; with respect to the lattice planes) will face different periodicities. Bragg scattering in different directions leads to stop bands of different wavelengths that may not overlap in all directions to form a PBG, without very high refractive-index contrast of the materials. In addition, in 2D structures, two different EM wave polarizations, Transverse Electric (TE) and Transverse Magnetic (TM), often form bandgaps at differing frequencies, making it even harder to form a complete PBG in all directions for all polarizations5. In periodic structures, the limited choices of rotational symmetry lead to intrinsic anisotropy (angular dependence), which not only makes it hard to form a complete PBG, but also greatly limits the design freedom of functional defects. For example, waveguide designs are proven to be restricted along very limited choices of major symmetry directions in photonic crystals10.

Inspired to surpass these limitations due to periodicity, much research has been done in the past 20 years on unconventional PBG materials. Recently a new class of disordered materials was proposed to possess an isotropic complete PBG in the absence of periodicity or quasiperiodicity: the hyperuniform Disorder (HD) PBG structure11. The photonic bands do not have exact analytical solution in disorder structures. Theoretical study of the photonic properties of the disordered structures is limited to time&#8211;consuming numerical simulations. To calculate the bands, the simulation needs to employ a super-cell approximation method and the available computational power may limit the finite size of the super-cell. To calculate transmission through these structures, computer simulations often assume ideal conditions and thus neglect real world problems like the coupling between the source and detector, the actual incident EM wave profile, and alignment imperfections12. Furthermore, any modification (defect design) of the simulated structure would require another round of simulation. Due to the large size of the minimum meaning for super-cell, it is very tedious and impractical to systematically explore various defect design architectures for these disordered materials.

We can avert these computational problems by studying the disordered photonic structures experimentally. Through our experiments we are able to verify the existence of the complete PBG in HD structures. Using microwave experiments, we can also obtain phase information and reveal the field distribution and dispersion properties of existing photonic states in them. Using an easily modifiable and modular sample at cm-scale, we can test various waveguide and cavity (defect) designs in the disordered systems and analyze the robustness of the PBGs. This kind of analysis of complex disordered photonic structures is either impractical or impossible to obtain through numerical or theoretical studies.

The design process begins by selecting a &#8220;stealthy&#8221; hyperuniform point pattern13. Hyperuniform point patterns are systems in which the number variance of the points within a &#8220;spherical&#8221; sampling window of radius R, grows more slowly than the window volume for large R, that is, more slowly than Rd in d-dimensions. For example, in a 2D Poisson random distribution of point pattern, the variance of the number of points in domain R is proportional to R2. However, in a hyperuniform disorder point pattern, the variance of the points in a window of radius R, is proportional to R. Figure 1&#160;shows a comparison between a hyperuniform disordered point pattern and a Poisson point pattern11. We use a subclass of hyperuniform disordered point patterns called &#8220;stealthy&#8221;11.

Using the design protocol described in Florescu&#160;et al11, we construct a network of dielectric walls and rods, creating a 2D hyperuniform dielectric structure similar to a crystal, but without the limitations inherent to periodicity and isotropy. The wall networks are favorable for TE-polarization bandgap, while the rods are preferable for forming band gaps with TM-polarization.&#160; A modular design was developed, so that the samples can be easily modified for use with different polarizations and for introducing freeform waveguides and cavity defects. Due to the scale invariance of Maxwell&#8217;s equations, the electromagnetic properties observed in the microwave regime are directly applicable to the infrared and optical regimes, where the samples would be scaled to micron and submicron sizes.

<table border="0" cellpadding="0" cellspacing="0" width="599">
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">stereolithography machine</td>
			<td style="width:97px;">3D Systems</td>
			<td style="width:119px;">SLA-7000</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">resin for base</td>
			<td style="width:97px;">3D Systems</td>
			<td style="width:119px;">Accura 60</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Alumina rods</td>
			<td style="width:97px;"></td>
			<td style="width:119px;"></td>
			<td>r=2.5mm, cut to 10.0cm height</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Alumina sheets</td>
			<td style="width:97px;"></td>
			<td style="width:119px;"></td>
			<td>thickness 0.38mm, various width: from 1.0mm to 5.3mm with 0.2mm incerments</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Microwave Generator</td>
			<td style="width:97px;">Agilent/HP</td>
			<td style="width:119px;">83651B</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">S-Parameter Test set</td>
			<td style="width:97px;">Agilent/HP</td>
			<td style="width:119px;">8517B</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Microwave Vector Network Analyzer</td>
			<td style="width:97px;">Agilent/HP</td>
			<td style="width:119px;">8510C</td>
			<td></td>
		</tr>
	</tbody>
</table>

using microwave and macroscopic samples of dielectric solids to study the photonic properties of disordered photonic bandgap materials

Recently, disordered photonic materials have been suggested as an alternative to periodic crystals for the formation of a complete photonic bandgap (PBG). In this article we will describe the methods for constructing and characterizing macroscopic disordered photonic structures using microwaves. The microwave regime offers the most convenient experimental sample size to build and test PBG media. Easily manipulated dielectric lattice components extend flexibility in building various 2D structures on top of pre-printed plastic templates. Once built, the structures could be quickly modified with point and line defects to make freeform waveguides and filters. Testing is done using a widely available Vector Network Analyzer and pairs of microwave horn antennas. Due to the scale invariance property of electromagnetic fields, the results we obtained in the microwave region can be directly applied to infrared and optical regions. Our approach is simple but delivers exciting new insight into the nature of light and disordered matter interaction.

Our representative results include the first experimental demonstration of the existence of a complete and isotropic PBG in a two-dimensional (2D) hyperuniform disordered dielectric structure. Additionally we demonstrate experimentally the ability of this novel photonic structure to guide electromagnetic waves (EM) through freeform waveguides of arbitrary shape.

We have achieved the first confirmation ever of an isotropic complete PBG present in hyperuniform disorder dielectric structures. Here, we present our HD structure results and compare them to that of a periodic square lattice photonic crystal.
Figure 5 shows a semi-log plot of TE polarization transmission (dB) vs. frequency (GHz) for a hyperuniform disorder structure at one incident angle. This plot shows that the stop band region is located approximately between 8.5 and 9.5 G...

Watch this Scientific Journal Video about Using Microwave and Macroscopic Samples of Dielectric Solids to Study the Photonic Properties of Disordered Photonic Bandgap Materials at JoVE.com

Using Microwave and Macroscopic Samples of Dielectric Solids to Study the Photonic Properties of Disordered Photonic Bandgap Materials

Disordered structures offer new mechanisms for forming photonic bandgaps and unprecedented freedom in functional-defect designs. To circumvent the computational challenges of disordered systems, we construct modular macroscopic samples of the new class of PBG materials and use microwaves to characterize their scale-invariant photonic properties, in an easy and inexpensive manner.

Recently, disordered photonic materials have been suggested as an alternative to periodic crystals for the formation of a complete photonic bandgap (PBG). ...

using-microwave-macroscopic-samples-dielectric-solids-to-study

Research

JoVE Journal

Engineering

12.2K Views.  San Francisco State University. Disordered structures offer new mechanisms for forming photonic bandgaps and unprecedented freedom in functional-defect designs. To circumvent the computational challenges of disordered systems, we construct modular macroscopic samples of the new class of PBG materials and use microwaves to characterize their scale-invariant photonic properties, in an easy and inexpensive manner.