tensile property characterization of glass fiber-reinforced polymer (gfrp) composite laminates

Fabrication and Mechanical Property Assessment of Fiber Composite Laminates

Fiber reinforced polymer composite (FRP) is a type of high-strength material manufactured by mixing fiber reinforcement and polymer matrixes1,2,3. It is widely used in the aerospace4,5,6, construction7,8, automotive9, and marine10,11 industries due to its low density, high specific stiffness and strength, fatigue properties, and excellent corrosion resistance. Common synthetic fibers include carbon fibers, glass fibers, and aramid fibers12. Glass fiber was chosen for investigation in this paper. Compared to traditional steel, glass fiber reinforcement composite laminates (GFRPs) are lighter, with less than one-third of the density, but can achieve a higher specific strength than steel.
The preparation process of FRP includes vacuum-assisted resin transfer molding (VARTM)13, filament winding (FW)14, and prepreg molding, in addition to many other advanced fabrication processes15,16,17,18. Compared to other preparation processes, the wet hand lay-up/vacuum bag (WLVB) process has several advantages, including simple equipment requirements and uncomplicated process technology, and the products are not limited by size and shape. This process has a high degree of freedom and can be integrated with metal, wood, plastic, or foam.
The principle of the WLVB process is to apply greater forming pressure through vacuum bags to enhance the mechanical properties of the prepared laminates; the production technology of this process is easy to master, making it an economical and simple composite material preparation process. This process is completely manual, and it is greatly influenced by the skills of preparation personnel. Therefore, the products are prone to defects such as voids and uneven thickness, leading to unstable qualities and mechanical properties of the laminate. Hence, it is necessary to describe the WLVB process in detail, finely control steps, and quantify material proportion, in order to obtain a high stability of mechanical properties of laminates.
Most researchers have studied the quasi-static19,20,21,22,23 and dynamic behavior24,25,26,27,28, as well as the property modification29,30 of composite materials. The volume fraction ratio of fiber to matrix plays a crucial role in mechanical properties of FRP laminate. In an appropriate range, a higher volume fraction of fiber can improve the strength and stiffness of FRP laminate. Andrew et al.31 investigated the effect of fiber volume fraction on the mechanical properties of specimens prepared by the fused deposition modeling (FDM) additive manufacturing process. The results showed that when the fiber volume fraction was 22.5%, the tensile strength efficiency reached its maximum, and a slight improvement in strength was observed as the fiber volume fraction reached 33%. Khalid et al.32 studied the mechanical properties of continuous carbon fiber (CF)-reinforced 3D-printed composites with diverse fiber volume fractions, and the results showed that both tensile strength and stiffness were improved with the rise in fiber content. Uzay et al.33 investigated the effects of three fabrication methods-hand lay-up, compression molding, and vacuum bagging-on the mechanical properties of carbon fiber-reinforced polymer (CFRP). The fiber volume fraction and void of the laminates were measured, tensile and bending tests were conducted. The experiments showed that the higher the fiber volume fraction, the better the mechanical properties.
Voids are one of the most common defects in FRP laminate. Voids reduce the mechanical properties of composite materials, such as strength, stiffness, and fatigue resistance34. The stress concentration generated around the voids promotes the propagation of micro-cracks and reduces the interface strength between reinforcement and matrix. Internal voids also accelerate the moisture absorption of FRP laminate, resulting in interface debonding and performance degradation. Therefore, the existence of internal voids affects the reliability of composite and restricts their wide application. Zhu et al.35 investigated the influence of void content on the static interlaminar shear strength properties of CFRP composite laminates, and found that a 1% increase in void content ranging from 0.4% to 4.6% led to a 2.4% deterioration in interlaminar shear strength. Scott et al.36 presented the effect of voids on damage mechanism in CFRP composite laminates under hydrostatic loading using computed tomography (CT), and found that the number of voids is 2.6-5 times the number of randomly distributed cracks.
High-quality and reliable FRP laminates can be manufactured by using an autoclave. Abraham et al.37 manufactured low-porosity, high-fiber content laminates by placing a WLVB assembly in an autoclave with a pressure of 1.2 MPa for curing. Nevertheless, the autoclave is a large and expensive piece of equipment, resulting in considerable manufacturing costs. Although the vacuum-assisted resin transfer process (VARTM) has been in use for a long time, it has a limit in terms of the time cost, a more complicated preparation process, and more disposable consumables such as diversion tubes and diversion media. Compared with the WL process, the WLVB process compensates for insufficient molding pressure through a low-cost vacuum bag, absorbing excess resin from the system to increase the fiber volume fraction and reduce the internal pore content, thereby greatly improving the mechanical properties of the laminate.
This study explores the differences between the WL process and the WLVB process, and details the meticulous process of the WLVB process. The fiber volume content of laminates was calculated by the formula method, and the results showed that the fiber volume content of WL laminates was 42.04%, while that of WLVB laminates was 57.82%, increasing by 15.78%. The mechanical properties of laminates were characterized by tensile and impact tests. The experimental results revealed that with the WLVB process, the strength and modulus of the laminates were enhanced by 17.4% and 16.35%, respectively, and the specific absorbed energy was increased by 19.48%.

Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process 

Measuring the Mechanical Properties of Glass Fiber Reinforcement Polymer Composite Laminates Obtained by Different Fabrication Processes

Watch this Scientific Journal Video about Tensile Property Characterization of Glass Fiber-Reinforced Polymer GFRP Composite Laminates at JoVE.com

Tensile Property Characterization of Glass Fiber-Reinforced Polymer (GFRP) Composite Laminates  

tensile-property-characterization-glass-fiber-reinforced-polymer-gfrp

Research

Education

JoVE Journal

JoVE Core

Engineering

Mechanical Engineering

Civil Engineering

Unit 1

Elasticity, Creep, and Shrinkage in Concrete

Torsion

SCIENTISTS IN ACTION

207 visualizações.  Southern University of Science and Technology. Para iniciar o teste de tração usando uma máquina de corte de alta precisão equipada com um cortador de diamante, corte amostras de 250 milímetros por 25 milímetros do polímero reforçado com fibra de vidro ou laminados GFRP. Meça as dimensões da amostra com um paquímetro vernier. Fixe quatro abas de alumínio em ambas as extremidades da amostra usando adesivo epóxi para evitar a concentração de tensões.Borrifar uma fina camada de tinta branca na parte frontal da amostra,...

Vídeo: Tensile Property Characterization of Glass Fiber-Reinforced Polymer (GFRP) Composite Laminates  