The authors Ivo W. Rangelow and Thomas Sattel would like to acknowledge the German Federal Ministry of Education and Research (BMBF) and the German Federal Ministry of Economics Affairs and Climate Action (BMWK) for supporting parts of the presented methods by funding the projects FKZ:13N16580 &#34;Active Probes with diamond tip for quantum metrology and nanofabrication&#34; within the research line KMU-innovativ: Photonics and Quantum Technologies and KK5007912DF1 &#34;Conjungate Nano-Positioner-Scanner for fast and large metrological tasks in Atomic Force Microscopy&#34; within the funding line Central Innovation Program for small and medium sized industries (ZIM). Part of the work reported here was funded by the European Union Seventh Framework Programme FP7/2007-2013 under Grant Agreement No. 318804 &#34;Single Nanometre Manufacturing: Beyond CMOS.&#34; The authors Ivo W. Rangelow and Eberhard Manske gratefully acknowledge the support by the Deutsche Forschungsgemeinschaft (DFG) in the framework of Research Training Group &#34;Tip- and laser-based 3D-Nanofabrication in extended macroscopic working areas&#34; (GRK 2182) at the Technische Universit&#228;t Ilmenau, Germany.

1. Sample preparation for large-scale inspection
<ol>
	<li>Prepare the sample with a suitable size for the AFM (see Table of Materials). 
	NOTE: Wafer-shape samples with an in-plane diameter&#160;from 75 mm to 300 mm and an expected out-of-plane height variation below 200 &#181;m can fit on the AFM sample stage. In this study, an extreme ultraviolet (EUV) mask on a 4 inch wafer is used (see Table of Materials).</li>
	<li>Clean the sample to remove contaminants and keep the samples inside a clean room or low-dust environment, such as a vacuum chamber or a nitrogen-purged cabinet.
	<ol>
		<li>Remove large dust particles by blowing the sample with a compressed nitrogen spray gun, or rinse with deionized water if the sample does not react with water. To avoid damaging the sample, use a small flow rate below 0.1 m3/min.</li>
		<li>Optionally, apply plasma cleaning to remove organic contaminants. Place the sample into the plasma treatment machine. Close the chamber and pump down the pressure to 600 mTorr. Expose the sample to plasma for 30 s for cleaning. 
		NOTE: Step 1.3.2 is optional for contamination removal. In this study, fabrication and characterization were performed inside a clean room, so this step was not needed.</li>
	</ol>
	</li>
	<li>Identify suitable imaging strategies, including areas of interest, scanning range, spatial/pixel resolution, and scanning line speed.
	<ol>
		<li>Determine whether the sample needs an overall panorama or automated imaging of multiple smaller selected areas. 
		NOTE: For nanofabricated samples with desired structures, it is often easier to determine the key areas that are more prone to defects for inspection purposes. For other samples, taking a low spatial resolution image for a quick overview, and then zooming into the smaller area of interest for high spatial resolution imaging can be easier.</li>
		<li>Estimate the size of the features based on prior knowledge of the sample to determine the desired spatial resolution to resolve these features.</li>
		<li>Use the ratio of the imaging range and spatial resolution to determine pixel resolution.</li>
		<li>Select an initial scan line speed based on prior experience with the sample, or use the AFM system software later, based on the sample material, probe dynamics, and desired spatial resolution.</li>
	</ol>
	</li>
</ol>
2. AFM instrument calibration and experiment setup
<ol>
	<li>Select the appropriate active AFM cantilever array. 
	NOTE: The AFM active cantilever stiffness, first resonance frequency, and unused probe tip sharpness for each cantilever in the probe array are characterized from production. The data can be retrieved from the manufacturer and loaded into the software automatically before imaging. Selecting the appropriate cantilever recommended by the software based on the sample material or application is helpful to ensure successful imaging. Due to manufacturing variability, the properties of each cantilever can be different but on a similar level.</li>
	<li>Turn on the AFM by switching on the main power of the controller and wait for the system to initialize. Turn on the host computer and open the AFM system software.</li>
	<li>Perform active cantilever probe installation.
	<ol>
		<li>Raise the probe scanner up by clicking on the Active Cantilever Installation. Wait for the probe holder to be raised up from the sample stage and stop automatically.</li>
		<li>Mount and secure the AFM cantilever probe array on the probe holder. 
		NOTE: The AFM cantilever arrays are attached to a nano-SD card shape holder and can be handled directly by hand for probe installation. With the fundamental difference in sensing and actuation principles, there is no need to perform any laser alignment.</li>
		<li>Click on the Probe Auto Settings and load the probe information provided by the manufacturer (see Table of Materials). Ensure to match the serial number on the probe and in the software.</li>
		<li>Conduct a probe frequency sweep to verify the resonance of each cantilever for imaging. Click on Cantilever Tuning and click on Sweep in the pop-up window. Specify the Start Frequency and End Frequency if the range is known. If not, the software will automatically update the values using the default settings. 
		NOTE: This step is, in principle, optional for new probes as they have been calibrated after production. However, for probes that have been used previously, it is recommended to perform this sweep just in case any properties have changed during the previous operation (e.g., attachment of contaminant particles that shifts the cantilever resonance). Due to thermomechanical actuation, the heating power is proportional to the square of the driving voltage. For tapping non-contact mode operation, a second harmonic of the input voltage sine wave component is generated due to the square relation in Equation 2. This second harmonic is typically matched with the cantilever resonance during excitation, as the direct current (DC) offset signal does not affect its amplitude. Therefore, the DC components control the average cantilever deflection, and the alternating current (AC) component of the drive signal is automatically set to half of the cantilever resonance frequency for imaging.</li>
	</ol>
	</li>
	<li>Load and secure the sample in place. Ensure the bottom surface in contact with the sample is parallel to the top surface with the features to be imaged. Fine-tune the sample stage tilt using the micrometer knobs to ensure the sample is flat. Add spacers if the tilt is too large for the fine adjustment positioners to compensate for.</li>
	<li>Adjust the in-plane XY position of the sample using the micrometer on the AFM stage. Use an optical microscope image to locate the area of interest and position the relative position of the cantilever array onto the first area of interest to be imaged.</li>
	<li>Establish a global coordinate by clicking on the XYZ Zero button. 
	NOTE: For the creation of a panoramic image, this step can be conducted roughly using the optical microscope view. When imaging selected areas of a nanofabricated sample, it may be necessary to precisely align the XYZ coordinate of the fabrication equipment with the AFM coordinate. This step can be performed more precisely by performing the AFM imaging and clicking on the XYZ Zero button again.</li>
	<li>Close and seal the acoustic shield. 
	&#8203;NOTE: The acoustic shield helps reduce vibration propagation through the air. Moreover, the sealed cover can also reduce the chance of dust particles landing on the sample, since large-scale imaging can take a long time to complete. This protective cover can be optional in a clean room environment without vibration sources.</li>
</ol>
3. Topography imaging and parameter tuning
<ol>
	<li>Select the tab Imaging Parameter Setup (active cantilever eigenmode, scanning speed, set-point, etc.) and input the desired imaging parameters.
	<ol>
		<li>For a single panoramic image, enter the coordinate of the top left corner of the image and the scan size. For imaging multiple selected regions automatically, repeat this process for all the regions to be imaged. Add extra padding around the imaging area for post-processing image stitching. 
		NOTE: For the present study, the top left corner of the EUV mask was set with pre-defined features, and the system was configured to capture four images with 130 &#181;m by 130 &#181;m simultaneously using each cantilever.</li>
		<li>Enter the desired in-plane pixel resolution (typically thousands of pixels per scan line) and use the default recommended line scan speed from the software for imaging. If needed, manually adjust the line scan speed for each region to be imaged. 
		NOTE: In this study, a pixel resolution of 26,000 pixels per line, corresponding to 5 nm per pixel, was used to obtain high-resolution images.</li>
		<li>For non-contact mode, use the default drive amplitude, frequency, and setpoint in the software obtained from the cantilever characteristics, or manually input the setpoint for each cantilever on the array. Leave the PID controller settings as default.</li>
	</ol>
	</li>
	<li>Engage the active cantilever probe array with the sample.
	<ol>
		<li>Click on Initialize Cantilever to pre-bend the cantilever before imaging.</li>
		<li>Click on Start Non-Contact Drive to excite the cantilever resonance.</li>
		<li>Click on Engage to let the system automatically bring the sample and the probe into contact. Imaging will start automatically after this step is completed.</li>
	</ol>
	</li>
	<li>Adjust the PID controller parameters for each cantilever based on the scanned trace/image. Adjust the PID parameters to improve the matching between the trace and retrace lines, which helps to capture the topography changes. The imaging speed can also be adjusted correspondingly to improve the topography tracking performance.</li>
	<li>Save the current data on the screen by clicking on the Save button. The data will also be automatically saved during the scan at the end of each frame.</li>
	<li>Stop imaging by clicking on the Stop button. The system will stop imaging and automatically retract the cantilever array from the sample. The cantilever drive will also be stopped so that it will be safe to uninstall the probe.</li>
	<li>Remove the probe and the sample carefully and turn off the system.</li>
</ol>
4. Post-processing and image analysis
<ol>
	<li>Open the AFM image analysis software supplied by the vendor.
	<ol>
		<li>Click on Auto Process to apply the default post-processing sequence, including sample tilt correction, pixel level outlier removal, and scan line matching.</li>
		<li>Apply further corrections on image defects manually from observation of the images. With advanced AFM instruments, such defects are rare, but images can still be improved with these steps. 
		NOTE: For large amounts of images, it is possible to automate the process using Macro or Python scripts through batch processing with the same operation. This was not required for the present study.</li>
	</ol>
	</li>
	<li>Use the software to form a panoramic image by clicking on the Panorama Image button and selecting multiple images to be stitched. 
	NOTE: Image stitching is performed automatically by directly using the overlapping space of the adjacent images. Alternatively, image merging tries to maximize the correlation of the overlapping pixels on the edges. Various options are available in these commands and can be optimized to improve the overall merging performance.</li>
	<li>Save the data for further analysis based on the specific sample.</li>
</ol>

Parallel Active Cantilever Arrays in AFMS to Enable High-Throughput Inspections

<ol>
	<li>Ando, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-speed+atomic+force+microscopy+and+its+future+prospects.">High-speed atomic force microscopy and its future prospects.</a> Biophysical Reviews. 10 (2), 285-292 (2018).</li><li>Soltani Bozchalooi, I., Careaga Houck, A., AlGhamdi, J. M., Youcef-Toumi, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+and+control+of+multi-actuated+atomic+force+microscope+for+large-range+and+high-speed+imaging.">Design and control of multi-actuated atomic force microscope for large-range and high-speed imaging.</a> Ultramicroscopy. 160, 213-224 (2016).</li><li>Sohn, Y., Ryu, S., Yang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Semiconductor+technology+challenges+in+high+volume+manufacturing+of+semiconductors.">Semiconductor technology challenges in high volume manufacturing of semiconductors.</a> Microscopy and Microanalysis. 28, 800-801 (2022).</li><li>Ebayyeh, A. A. R. M. A., Mousavi, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+review+and+analysis+of+automatic+optical+inspection+and+quality+monitoring+methods+in+electronics+industry.">A review and analysis of automatic optical inspection and quality monitoring methods in electronics industry.</a> IEEE Access. 8, 183192-183271 (2020).</li><li>Nakamae, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electron+microscopy+in+semiconductor+inspection.">Electron microscopy in semiconductor inspection.</a> Measurement Science and Technology. 32 (5), 052003 (2021).</li><li>Nduhura-Munga, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+literature+review+on+sampling+techniques+in+semiconductor+manufacturing.">A literature review on sampling techniques in semiconductor manufacturing.</a> IEEE Transactions on Semiconductor Manufacturing. 26 (2), 188-195 (2013).</li><li>Zhang, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Correlative+AFM+and+scanning+microlens+microscopy+for+time-efficient+multiscale+imaging.">Correlative AFM and scanning microlens microscopy for time-efficient multiscale imaging.</a> Advanced Science. 9 (12), 2103902 (2022).</li><li>Holz, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Correlative+microscopy+and+nanofabrication+with+AFM+integrated+with+SEM.">Correlative microscopy and nanofabrication with AFM integrated with SEM.</a> Microscopy Today. 27 (6), 24-30 (2019).</li><li>Yang, C., Xia, F., Wang, Y., Truncale, S., Youcef-Toumi, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+and+control+of+a+multi-actuated+nanopositioning+stage+with+stacked+structure.">Design and control of a multi-actuated nanopositioning stage with stacked structure.</a> 2019 American Control Conference (ACC). , 3782-3788 (2019).</li><li>Xia, F., Truncale, S., Wang, Y., Youcef-Toumi, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+and+control+of+a+multi-actuated+high-bandwidth+and+large-range+scanner+for+atomic+force+microscopy.">Design and control of a multi-actuated high-bandwidth and large-range scanner for atomic force microscopy.</a> 2018 Annual American Control Conference (ACC). , 4330-4335 (2018).</li><li>Yong, Y. K., Moheimani, S. O. R., Kenton, B. J., Leang, K. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Invited+review+article:+high-speed+flexure-guided+nanopositioning:+mechanical+design+and+control+issues.">Invited review article: high-speed flexure-guided nanopositioning: mechanical design and control issues.</a> The Review of Scientific Instruments. 83 (12), 121101 (2012).</li><li>Wang, J. Y., Mullin, N., Hobbs, J. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-speed+large+area+atomic+force+microscopy+using+a+quartz+resonator.">High-speed large area atomic force microscopy using a quartz resonator.</a> Nanotechnology. 29 (33), 335502 (2018).</li><li>Yang, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Charge+controller+with+decoupled+and+self-compensating+configurations+for+linear+operation+of+piezoelectric+actuators+in+a+wide+bandwidth.">Charge controller with decoupled and self-compensating configurations for linear operation of piezoelectric actuators in a wide bandwidth.</a> IEEE Transactions on Industrial Electronics. 66 (7), 5392-5402 (2019).</li><li>Yang, C., Xia, F., Wang, Y., Youcef-Toumi, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Comprehensive+study+of+charge-based+motion+control+for+piezoelectric+nanopositioners:+Modeling,+instrumentation+and+controller+design.">Comprehensive study of charge-based motion control for piezoelectric nanopositioners: Modeling, instrumentation and controller design.</a> Mechanical Systems and Signal Processing. 166, 108477 (2022).</li><li>Xia, F., Yang, C., Wang, Y., Youcef-Toumi, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Bandwidth+based+repetitive+controller+design+for+a+modular+multi-actuated+AFM+scanner.">Bandwidth based repetitive controller design for a modular multi-actuated AFM scanner.</a> 2019 American Control Conference (ACC). , 3776-3781 (2019).</li><li>Ahmad, A., Schuh, A., Rangelow, I. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adaptive+AFM+scan+speed+control+for+high+aspect+ratio+fast+structure+tracking.">Adaptive AFM scan speed control for high aspect ratio fast structure tracking.</a> The Review of Scientific Instruments. 85 (10), 103706 (2014).</li><li>Coskun, M. B., Alemansour, H., Fowler, A. G., Maroufi, M., Moheimani, S. O. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Q+control+of+an+active+AFM+cantilever+with+differential+sensing+configuration.">Q control of an active AFM cantilever with differential sensing configuration.</a> IEEE Transactions on Control Systems Technology. 27 (5), 2271-2278 (2019).</li><li>Xia, F., Mayborne, M. P., Ma, Q., Youcef-Toumi, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physical+intelligence+in+the+metaverse:+mixed+reality+scale+models+for+twistronics+and+atomic+force+microscopy.">Physical intelligence in the metaverse: mixed reality scale models for twistronics and atomic force microscopy.</a> 2022 IEEE/ASME International Conference on Advanced Intelligent Mechatronics (AIM). , 1722-1729 (2022).</li><li>Xia, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+modular+low-cost+atomic+force+microscope+for+precision+mechatronics+education.">A modular low-cost atomic force microscope for precision mechatronics education.</a> Mechatronics. 76, 102550 (2021).</li><li>Minne, S. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Centimeter+scale+atomic+force+microscope+imaging+and+lithography.">Centimeter scale atomic force microscope imaging and lithography.</a> Applied Physics Letters. 73 (12), 1742-1744 (1998).</li><li>Minne, S. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Automated+parallel+high-speed+atomic+force+microscopy.">Automated parallel high-speed atomic force microscopy.</a> Applied Physics Letters. 72 (18), 2340-2342 (1998).</li><li>Ahmad, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Large+area+fast-AFM+scanning+with+active+&amp;#34;Quattro&amp;#34;+cantilever+arrays.">Large area fast-AFM scanning with active &amp;#34;Quattro&amp;#34; cantilever arrays.</a> Journal of Vacuum Science &amp; Technology B. 34 (6), (2016).</li><li>Gotszalk, T., Grabiec, P., Rangelow, I. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Piezoresistive+sensors+for+scanning+probe+microscopy.">Piezoresistive sensors for scanning probe microscopy.</a> Ultramicroscopy. 82 (1), 39-48 (2000).</li><li>Angelov, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermo-mechanical+transduction+suitable+for+high-speed+scanning+probe+imaging+and+lithography.">Thermo-mechanical transduction suitable for high-speed scanning probe imaging and lithography.</a> Microelectronic Engineering. 154, 1-7 (2016).</li><li>Rangelow, I. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Active+scanning+probes:+A+versatile+toolkit+for+fast+imaging+and+emerging+nanofabrication.">Active scanning probes: A versatile toolkit for fast imaging and emerging nanofabrication.</a> Journal of Vacuum Science &amp; Technology B. 35 (6), 101 (2017).</li><li>Marinello, F., Bariani, P., De Chiffre, L., Hansen, H. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Development+and+analysis+of+a+software+tool+for+stitching+three-dimensional+surface+topography+data+sets.">Development and analysis of a software tool for stitching three-dimensional surface topography data sets.</a> Measurement Science and Technology. 18 (5), 1404 (2007).</li><li>L&#243;pez de la Rosa, F., S&#225;nchez-Reolid, R., G&#243;mez-Sirvent, J. L., Morales, R., Fern&#225;ndez-Caballero, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+review+on+machine+and+deep+learning+for+semiconductor+defect+classification+in+scanning+electron+microscope+images.">A review on machine and deep learning for semiconductor defect classification in scanning electron microscope images.</a> Applied Sciences. 11 (20), 9508 (2021).</li><li>Holz, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High+throughput+AFM+inspection+system+with+parallel+active+cantilevers.">High throughput AFM inspection system with parallel active cantilevers.</a> In Photomask Technology 2019. 11148, 278-287 (2019).</li><li>Gotszalk, T., Ivanov, T., Rangelow, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Parallel+SPM+cantilever+arrays+for+large+area+surface+metrology+and+lithography.">Parallel SPM cantilever arrays for large area surface metrology and lithography.</a> In Metrology, Inspection, and Process Control for Microlithography XXVIII. 9050, 274-282 (2014).</li><li>Ahmad, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=13th+Intl.+Workshop+on+Nanomechanical+Sensing.">13th Intl. Workshop on Nanomechanical Sensing.</a> Quattro-Cantilever Array: Large Area and High Speed AFM Imaging and Nanolithography. , (2016).</li><li>Shearer, C. J., Slattery, A. D., Stapleton, A. J., Shapter, J. G., Gibson, C. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Accurate+thickness+measurement+of+graphene.">Accurate thickness measurement of graphene.</a> Nanotechnology. 27 (12), 125704 (2016).</li><li>Shioyama, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+interactions+of+two+chemical+species+in+the+interlayer+spacing+of+graphite.">The interactions of two chemical species in the interlayer spacing of graphite.</a> Synthetic Metals. 114 (1), 1-15 (2000).</li><li>Ivanova, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scanning+proximal+probes+for+parallel+imaging+and+lithography.">Scanning proximal probes for parallel imaging and lithography.</a> Journal of Vacuum Science &amp; Technology B. 26 (6), 2367-2373 (2008).</li><li>Garc&#237;a, R., San Paulo, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Attractive+and+repulsive+tip-sample+interaction+regimes+in+tapping-mode+atomic+force+microscopy.">Attractive and repulsive tip-sample interaction regimes in tapping-mode atomic force microscopy.</a> Physical Review B. 60 (7), 4961-4967 (1999).</li><li>Ruppert, M. G., Fowler, A. G., Maroufi, M., Moheimani, S. O. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=On-chip+dynamic+mode+atomic+force+microscopy:+a+silicon-on-insulator+MEMS+approach.">On-chip dynamic mode atomic force microscopy: a silicon-on-insulator MEMS approach.</a> Journal of Microelectromechanical Systems. 26 (1), 215-225 (2017).</li></ol>

The authors have no conflicts of interest.

As demonstrated in the representative results, an active cantilever array can be used to capture multiple images of a static sample in parallel. This scalable setup can significantly improve the imaging throughput of large-area samples, making it suitable for inspecting nanofabricated devices on semiconductor wafers. The technique is also not limited to man-made structures; as long as the topography variation within a group of active cantilevers is not too large for the cantilever array to handle, high-throughput imaging...

Atomic force microscopes (AFMs) can capture 3D topography images with nanoscale spatial resolution. Researchers have extended the capability of AFMs to create sample property maps in mechanical, electrical, magnetic, optical, and thermal domains. In the meantime, improving imaging throughput has also been the focus of research to adapt AFMs to new experimental needs. There are primarily two application domains for high-throughput AFM imaging: the first category is high-speed imaging of a small area to capture dynamic changes in the sample due to biological or chemical reactions1,2; the second category is for high-spatial resolution, large-scale imaging of static samples during an inspection, which is discussed in detail in this work. With transistor size shrinking down to the nanoscale, the semiconductor industry urgently needs high-throughput AFMs to inspect wafer-scale nanofabricated devices with nanoscale spatial resolution3.
The characterization of nanofabricated devices on a wafer can be challenging due to the vast scale difference between wafer and transistor features. Large defects can be spotted with optical microscopes automatically4. In addition, scanning electron microscopes (SEMs) are widely used for inspection down to tens of nanometers in 2D5. For 3D information and higher resolution, the AFM is a more suitable tool if its throughput can be improved.
With limited imaging throughput, one approach is to image selected wafer areas where nanofabrication defects are more likely to happen6. This would require prior knowledge of the design and fabrication process. Alternatively, combining other modalities, such as an optical microscope or SEM with an AFM for overview and zoom, is possible7,8. A wide-range, high-precision positioning system is needed to properly align the coordinate system between the fabrication and characterization tools. Moreover, an automated AFM system to image various selected areas is necessary to realize this functionality.
As an alternative, researchers have investigated different ways to increase AFM scanning speed. Since enabling high-throughput AFMs is a systematic precision instrumentation challenge, researchers have investigated various methods, including using smaller AFM probes, redesigning high-bandwidth nano-positioners9,10,11,12 and driving electronics13, optimizing modes of operation, imaging control algorithms14,15,16,17, etc. With these efforts, the effective relative tip and sample speed can be increased to a maximum of around tens of millimeters per second for commercially available single-probe AFM systems.
To further improve the imaging throughput, adding multiple probes to operate in parallel is a natural solution. However, the optical beam deflection (OBD) system utilized for cantilever deflection sensing is relatively bulky, which makes the addition of multiple probes relatively challenging. Individual cantilever deflection control can also be difficult to realize.
To overcome this limitation, embedded sensing, and actuation principles without bulky external components, are preferred. As detailed in previously published reports18,19, deflection sensing with piezoresistive, piezoelectric, and optomechanical principles can be considered embedded sensing, with the former two being more mature and easier to implement. For embedded actuation, thermomechanical with electrical heating or piezoelectric principles can both be utilized. Although piezoelectric principles can operate in a wider temperature range down to cryogenic environments, they can only support tapping mode AFM operations, since static deflection cannot be measured due to the charge leakage and static actuation suffering from hysteresis and creep. In prior work, active cantilever probe arrays using a piezoresistive sensor and the piezoelectric sensor have been developed for large-range imaging20,21, but have not been further scaled up for large-scale imaging or commercialized. In this work, the combination of piezoresistive sensing and thermomechanical actuation are selected as embedded transducers with static deflection control capability.
In this work, a novel &#34;Quattro&#34;22 parallel active cantilever array is used as the probe23 for simultaneous imaging using active cantilevers. To measure the cantilever deflection, piezoresistive sensors in a Wheatstone bridge configuration19 are nanofabricated at the base of each micro-cantilever to measure the internal stress, which is linearly proportional to the cantilever tip deflection. This compact embedded sensor can also achieve sub-nanometer resolution as the conventional OBD sensor. The governing equation of the Wheatstone bridge voltage output Uout in response to the applied force F or cantilever deflection z is shown in Equation 119 for a cantilever with length L, width W, and thickness H, piezoresistive sensor coefficient PR, and effective elastic modulus of the cantilever E bridge supply voltage Ub.
<img alt="Equation 1" src="/files/ftp_upload/65210/65210eq01.jpg" style="margin: auto;" />&#160; &#160; (1)
As dynamic tapping/non-contact mode operation is preferred for noninvasive imaging to avoid disturbing the sample, a thermomechanical actuator made of serpentine shape aluminum wires is used to heat up the bimorph cantilever made with aluminum/magnesium alloy24, silicon, and silicon oxide materials. At the microscopic scale, the time constant of thermal processes is much smaller, and the cantilever resonance at tens to hundreds of kilohertz can be excited by driving the heater with an electrical signal. The cantilever free end deflection zh controlled by the heater temperature&#160;&#916;T relative ambience is shown in Equation 219for cantilever length L with a constant K, depending on the bimorph material thermo coefficient of expansion and geometric thickness and area. It should be noted that the&#160;&#916;T&#160;is proportional to the heater power P, which is equal to the square of the applied voltage V divided by its resistance R.
<img alt="Equation 2" src="/files/ftp_upload/65210/65210eq02.jpg" style="margin: auto;" />&#160; &#160; (2)
As an added benefit, static deflection can also be controlled in addition to resonance excitation. This can be a particularly helpful capability to regulate the probe-sample interaction of each cantilever individually. Moreover, multiple cantilevers on the same base chip can be excited individually with the embedded thermomechanical actuator, which is impossible in conventional resonance excitation with piezo-generated acoustic waves.
Combining piezoresistive sensing and thermomechanical actuation, the active cantilever probe has enabled a wide range of applications, including collocated AF microscopy in SE microscopy, imaging in opaque liquid, and scanning probe lithography, with more details available in review25. For high-throughput inspection purposes, the active cantilever array is created with a representative AFM implementation example involving four parallel cantilevers, as shown in Figure 1. In the future, an industrial-scale system will be developed using eight parallel active cantilevers and tens of positioners28. To illustrate the scale using an example, with an in-plane spatial resolution of 100 nm, imaging an area of 100 mm by 100 mm would result in over 106 scan lines and 1012 pixels. With a scanning speed of 50 mm/s per cantilever, this would require a total of over 555.6 h of scanning (23+ days) for a single cantilever, which is too long to be practically useful. Using the active cantilever array technology with tens of positioners, the required imaging time can be reduced by around two orders of magnitude to 5-10 h (less than half a day) without making any compromise to the resolution, which is a reasonable time scale for industrial inspection purpose.
To capture large-area, high-resolution images, the nano-positioning system is also upgraded. For imaging wafer-scale large samples, scanning the probe instead of the sample is preferred, in order to reduce the size of the objects being moved. With the separation distance between active cantilevers at 125 &#181;m, the scanner covers an area slightly larger than this range so that images from each cantilever can be stitched together during post-processing. Upon completion of a scan, the coarse positioner automatically repositions the probe to a new adjacent area to continue the imaging process. While the embedded thermomechanical actuatorregulates the deflection of each cantilever, the averaged deflection of all parallel cantilevers is regulated with another proportional-integral-derivative (PID) controller to assist the cantilevers during topography tracking. The scanner controller also ensures that the bending of each cantilever does not exceed a maximum threshold value, which may cause other probes to lose contact with the surface if the topography variation is too large.
The level of topography variation that can be tracked for cantilevers on the same base chip should it be limited, since the static deflection control range of the cantilever is on the order of tens of microns. For semiconductor wafers, the sample topography variations are typically on the sub-micrometer scale, so they should not be much of a big problem. However, with the addition of more cantilevers, the sample plane tilt with respect to the line of cantilevers can become a problem. In practice, eight parallel cantilevers with spacings close to 1 mm would still allow 1&#176; of tilt angle, while adding more cantilevers can make the tilting control more difficult to realize. Therefore, using multiple groups of eight-cantilever probes placed on separated probe scanners is an ongoing effort to fully realize the potential of the parallel active cantilever probe principle.
After data collection, a post-processing operation is necessary to retrieve the desired information. The process generally involves removing scanning artifacts, stitching adjacent images to form an overall panorama, and optionally identifying the structure defects by comparing them to the desired geometry using suitable algorithms26. It is worth noting that the amount of data accumulated can be enormous for a large range of images, and data-driven learning algorithms are also being developed for more efficient processing27.
This article illustrates the general process of acquiring high-resolution AFM images using the parallel active cantilever array integrated into a custom AFM system. Detailed implementation of the system is available in22,28,29,30, and it is being commercialized with the model number listed in Table of Materials. All four cantilevers were operated in tapping mode excited by the embedded thermal-mechanical actuator. Representative results on calibration samples, nanofabrication masks, and highly oriented pyrolytic graphite (HOPG) samples (see Table of Materials) are provided to illustrate the effectiveness of this new AFM tool for large-area inspection.

<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Active-Cantilever&#160;</td>
			<td>nano analytik GmbH</td>
			<td>AC-10-2012</td>
			<td>AFM Probe</td>
		</tr>
		<tr>
			<td>E-Beam</td>
			<td>EBX-30, INC</td>
			<td>012323-15</td>
			<td>Mask patterning instrument</td>
		</tr>
		<tr>
			<td>Highly Oriented Pyrolytic Graphite &#8211; HOPG</td>
			<td>TED PELLA, INC</td>
			<td>626-10</td>
			<td>AFM calibration sample</td>
		</tr>
		<tr>
			<td>Mask Sample</td>
			<td>Nanda Technologies GmbH</td>
			<td>Test substrate</td>
			<td>EUV Mask Sample substrate</td>
		</tr>
		<tr>
			<td>NANO-COMPAS-PRO&#160;</td>
			<td>nano analytik GmbH</td>
			<td>23-2016</td>
			<td>AFM Software</td>
		</tr>
		<tr>
			<td>nanoMetronom 20</td>
			<td>nano analytik GmbH</td>
			<td>1-343-2020</td>
			<td>AFM Instrument</td>
		</tr>
	</tbody>
</table>

active probe atomic force microscopy with quattro-parallel cantilever arrays for high-throughput large-scale sample inspection

An Atomic Force Microscope&#160;(AFM) is&#160;a powerful and versatile tool for nanoscale surface studies to capture 3D topography images of samples. However, due to their limited imaging throughput, AFMs have not been widely adopted for large-scale inspection purposes. Researchers have developed high-speed AFM systems to record dynamic process videos in chemical and biological reactions at tens of frames per second, at the cost of a small imaging area of up to several square micrometers. In contrast, inspecting large-scale nanofabricated structures, such as semiconductor wafers, requires nanoscale spatial resolution imaging of a static sample over hundreds of square centimeters with high productivity. Conventional AFMs use a single passive cantilever probe with an optical beam deflection system, which can only collect one pixel at a time during AFM imaging, resulting in low imaging throughput. This work utilizes an array of active cantilevers with embedded piezoresistive sensors and thermomechanical actuators, which allows simultaneous multi-cantilever operation in parallel operation for increased imaging throughput. When combined with large-range nano-positioners and proper control algorithms, each cantilever can be individually controlled to capture multiple AFM images. With data-driven post-processing algorithms, the images can be stitched together, and defect detection can be performed by comparing them to the desired geometry. This paper introduces principles of the custom AFM using the active cantilever arrays, followed by a discussion on practical experiment considerations for inspection applications. Selected example images of silicon calibration grating, highly-oriented pyrolytic graphite, and extreme ultraviolet lithography masks are captured using an array of four active cantilevers (&#34;Quattro&#34;) with a 125 &#181;m tip separation distance. With more engineering integration, this high-throughput, large-scale imaging tool can provide 3D metrological data for extreme ultraviolet (EUV) masks, chemical mechanical planarization (CMP) inspection, failure analysis, displays, thin-film step measurements, roughness measurement dies, and laser-engraved dry gas seal grooves.

Author Spotlight: Introduction to Active Probe Atomic Force Microscopy with Quattro-Parallel Cantilever Arrays

Active Probe Atomic Force Microscopy with Quattro-Parallel Cantilever Arrays for High-Throughput Large-Scale Sample Inspection

Scanning probe microscopy based on novel micro electromechanical system probes are called active cantilevers. Cantilevers with integrated actuation and sensing provide several advantages over passive cantilevers, which rely on piezoelectric excitation and optical beam deflection measurement. The most recent development in this field is the realization of arrays of active cantilevers for high-throughput parallel SPM imaging.The arrays of active cantilevers use integrated piezoresistive sensors to offer sensitivity comparable to optical readout methods without diffraction limits to allow smaller, softer, and more compact AFM probes. The results of this technique paved the way for the operation and building of high-throughput atomic force microscopes using high-speed multichannel electronics. The advances in this technique can facilitate the faster and more reliable operation of massively parallel active cantilever systems in the future.

To demonstrate the effectiveness of AFM large-range imaging using parallel active cantilevers for topography imaging, the stitched images of a calibration grating, taken by four cantilevers operated in parallel, are shown in Figure 2. The silicon wafer calibration structure has 45 &#181;m long features with a height of 14 nm. Each cantilever covers an area of 125 &#181;m by 125 &#181;m, which gives a stitched panoramic image of 500 &#181;m by 125 &#181;m. The scanning speed was set to 10 lin...

Watch this Scientific Journal Video about Author Spotlight: Introduction to Active Probe Atomic Force Microscopy with Quattro-Parallel Cantilever Arrays at JoVE.com

Large-scale sample inspection with nanoscale resolution has a wide range of applications, especially for nanofabricated semiconductor wafers. Atomic force microscopes can be a great tool for this purpose, but are limited by their imaging speed. This work utilizes parallel active cantilever arrays in AFMs to enable high-throughput and large-scale inspections.

An Atomic Force Microscope&#160;(AFM) is&#160;a powerful and versatile tool for nanoscale surface studies to capture 3D topography images of samples. ...

active-probe-atomic-force-microscopy-with-quattro-parallel-cantilever

Research

JoVE Journal

Engineering

Instrument Calibration, Experimental Setup, and Parameter Tuning for Semiconductor Wafer Topography Imaging with AFM

1.0K Views.  Massachusetts Institute of Technology.  Large-scale sample inspection with nanoscale resolution has a wide range of applications, especially for nanofabricated semiconductor wafers. Atomic force microscopes can be a great tool for this purpose, but are limited by their imaging speed. This work utilizes parallel active cantilever arrays in AFMs to enable high-throughput and large-scale inspections.

Parallel Active Cantilever Arrays in AFMS to Enable High-Throughput Inspections

Özet