Name: fabricating metamaterials using the fiber drawing method
Uploaded: 2012-10-18T12:00:00
Description: Watch this Scientific Journal Video about Fabricating Metamaterials Using the Fiber Drawing Method at JoVE.com

This research was supported under Australian Research Council's Discovery Projects funding scheme (project number DP120103942). B. T. K. and A. A. are the recipients of an Australian Research Council Future Fellowship (FT0991895) and Australian Research Fellowship (DP1093789) respectively.

Overview
The composite indium/PMMA fiber (Figure 3) is produced by drawing a stack of PMMA fibers including a single indium wire (Figure 2), which themselves have to be prepared from available PMMA tubes and wires. The steps presented are:
<ol class="ualpha">
 <li>Produce a PMMA fiber that contains a single indium wire of diameter appropriate for manual stacking. For this, first prepare a PMMA tube that can accommodate a 1 mm indium wire (Section 1), then inc...

<ol>
	<li>Cai, W., Shalaev, V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Optical Metamaterials: Fundamentals and Applications. , (2010).</li><li>Pendry, J. B., Holden, A. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Extremely+Low+Frequency+Plasmons+in+Metallic+Mesostructures.">Extremely Low Frequency Plasmons in Metallic Mesostructures.</a> Phys. Rev. Lett. 76, 4773-4776 (1996).</li><li>Schurig, D., Mock, J. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metamaterial+Electromagnetic+Cloak+at+Microwave+Frequencies.">Metamaterial Electromagnetic Cloak at Microwave Frequencies.</a> Science. 314, 977-980 (2006).</li><li>Shalaev, V. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Optical+negative-index+metamaterials.">Optical negative-index metamaterials.</a> Nat. Photonics. 1, 41-48 (2007).</li><li>Liu, Z., Lee, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Far-field+optical+hyperlens+magnifying+sub-diffraction-limited+objects.">Far-field optical hyperlens magnifying sub-diffraction-limited objects.</a> Science. 315, (2007).</li><li>Boltasseva, A., Shalaev, V. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+optical+negative-index+metamaterials:+Recent+advances+and+outlook.">Fabrication of optical negative-index metamaterials: Recent advances and outlook.</a> Metamaterials. 2, 1-17 (2008).</li><li>Soukoulis, C. M., Wegener, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Past+achievements+and+future+challenges+in+the+development+of+three-dimensional+photonic+metamaterials.">Past achievements and future challenges in the development of three-dimensional photonic metamaterials.</a> Nat. Photonics. 5, 523-530 (2011).</li><li>Tuniz, A., Kuhlmey, B. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Drawn+metamaterials+with+plasmonic+response+at+terahertz+frequencies.">Drawn metamaterials with plasmonic response at terahertz frequencies.</a> Appl. Phys. Lett. 96, 191101 (2010).</li><li>Argyros, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microstructured+polymer+optical+fibers.">Microstructured polymer optical fibers.</a> J. Lightwave Technol. 27, 1571-1579 (2009).</li><li>Donald, I. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Production,+properties+and+applications+of+microwire+and+related+products.">Production, properties and applications of microwire and related products.</a> J. Mater. Sci. 22, 2661-2679 (1987).</li><li>Grischkowsky, D., Keiding, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Far-infrared+time-domain+spectroscopy+with+terahertz+beams+of+dielectrics+and+semiconductors.">Far-infrared time-domain spectroscopy with terahertz beams of dielectrics and semiconductors.</a> J. Opt. Soc. Am. B. 7, 2006-2015 (1990).</li><li>Wang, A., Tuniz, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fiber+metamaterials+with+negative+magnetic+permeability+in+the+terahertz.">Fiber metamaterials with negative magnetic permeability in the terahertz.</a> Opt. Mat. Express. 1, 115-120 (2010).</li><li>Tuniz, A., Lwin, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stacked-and-drawn+metamaterials+with+magnetic+resonances+in+the+terahertz+range.">Stacked-and-drawn metamaterials with magnetic resonances in the terahertz range.</a> Opt. Express. 19, 16480-16490 (2011).</li></ol>

The technique presented here allows the fabrication of kilometers of continuous three-dimensional metamaterials with microscale feature sizes, possessing a plasmonic response (and thus a tailored electric permittivity) in the THz range, effectively behaving as a high-pass filter. This can be experimentally characterized using terahertz time-domain spectroscopy 11. Such fiber-shaped metamaterials can be cut and stacked into bulk materials to realize a large number of devices, or woven into other structures, for...

<table border="1">
	<tbody>
		<tr>
			<td>Name of Reagent/Material</td>
			<td>Company</td>
			<td>Catalogue Number</td>
			<td>Comments</td>
		</tr>
		<tr>
			<td>Indium 99.99% Wire, 1 mm diameter</td>
			<td>AIM Specialty</td>
			<td>Available on request</td>
			<td><a href="http://www.aimspecialty.com" target="_blank">www.aimspecialty.com</a> 
			<a href="http://www.aimspecialty.com/Portals/0/Files/Indium.pdf" target="_blank">http://www.aimspecialty.com/Portals/0/Files/Indium.pdf</a></td>
		</tr>
		<tr>
			<td>2-Propanol(Isopropanol)</td>
			<td>Sigma-Aldrich</td>
			<td>Product Number 
			190764</td>
			<td><a href="http://www.sigmaaldrich.com/chemistry/solvents/products.html?TablePage=17292086" target="_blank">http://www.sigmaaldrich.com/chemistry/solvents/products.html?TablePage=17292086</a></td>
		</tr>
		<tr>
			<td>Adhesive tape</td>
			<td>Staples</td>
			<td>&nbsp;</td>
			<td>&nbsp;</td>
		</tr>
		<tr>
			<td>One Wrap PTFE Tape, 5 ml x 12 mmW x 0.2 mmT</td>
			<td>RS Components</td>
			<td>RS Stock Number 
			231-964</td>
			<td><a href="http://uk.rs-online.com/web/p/ptfe-tapes/0231964/" target="_blank">http://uk.rs-online.com/web/p/ptfe-tapes/0231964/</a></td>
		</tr>
		<tr>
			<td>50 Micron Aluminium Foil Tape</td>
			<td>Advance Adhesive Tapes</td>
			<td>AT506</td>
			<td><a href="http://www.advancetapes.com/Products/types/9/page1/81" target="_blank">http://www.advancetapes.com/Products/types/9/page1/81</a></td>
		</tr>
		<tr>
			<td>Blu-tak</td>
			<td>Bostik</td>
			<td>&nbsp;</td>
			<td><a href="http://www.blutack.com/index.html" target="_blank">http://www.blutack.com/index.html</a></td>
		</tr>
		<tr>
			<td>Araldite Quick Set</td>
			<td>Selleys</td>
			<td>&nbsp;</td>
			<td><a href="http://selleys.com.au/adhesives/household-adhesive/araldite/quick-set" target="_blank">http://selleys.com.au/adhesives/household-adhesive/araldite/quick-set</a></td>
		</tr>
		<tr>
			<td>PMMA tubes: 
			- ID 6 mm, OD 12 mm 
			- ID 9 mm, OD 12 mm</td>
			<td>B &amp; M Plastics: Plastic Fabrication</td>
			<td>Available on request</td>
			<td><a href="http://www.bmplastics.com.au/about-us.htm" target="_blank">http://www.bmplastics.com.au/about-us.htm</a></td>
		</tr>
		<tr>
			<td>&nbsp;</td>
			<td>&nbsp;</td>
			<td>&nbsp;</td>
			<td>Equipment Requirements</td>
		</tr>
		<tr>
			<td>&nbsp;</td>
			<td>&nbsp;</td>
			<td>&nbsp;</td>
			<td>
			<ul>
				<li>Fibre draw tower with furnaces of maximum temperatures of at least 200 &deg;C (Heathway Polymer Draw Tower with Preform and Fibre draw facilities). A photograph of the draw tower is shown in Figure 5.</li>
				<li>Annealing oven of maximum temperatures of at least 90 &deg;C.</li>
				<li>Optical microscope.</li>
				<li>Hot air gun.</li>
				<li>Vacuum pump.</li>
				<li>Top preform extender (metal tube of 30 cm length and 12 mm diameter).</li>
				<li>Primary draw bottom extender (metal tube of 100 cm length and 12 mm diameter).</li>
				<li>Secondary draw bottom extender (PMMA tube of 20 cm length and 12 mm diameter).</li>
			</ul>
			</td>
		</tr>
	</tbody>
</table>

fabricating metamaterials using the fiber drawing method

Metamaterials are man-made composite materials, fabricated by assembling components much smaller than the wavelength at which they operate 1. They owe their electromagnetic properties to the structure of their constituents, instead of the atoms that compose them. For example, sub-wavelength metal wires can be arranged to possess an effective electric permittivity that is either positive or negative at a given frequency, in contrast to the metals themselves 2. This unprecedented control over the behaviour of light can potentially lead to a number of novel devices, such as invisibility cloaks 3, negative refractive index materials 4, and lenses that resolve objects below the diffraction limit 5. However, metamaterials operating at optical, mid-infrared and terahertz frequencies are conventionally made using nano- and micro-fabrication techniques that are expensive and produce samples that are at most a few centimetres in size 6-7. Here we present a fabrication method to produce hundreds of meters of metal wire metamaterials in fiber form, which exhibit a terahertz plasmonic response 8. We combine the stack-and-draw technique used to produce microstructured polymer optical fiber 9 with the Taylor-wire process 10, using indium wires inside polymethylmethacrylate (PMMA) tubes. PMMA is chosen because it is an easy to handle, drawable dielectric with suitable optical properties in the terahertz region; indium because it has a melting temperature of 156.6 &deg;C which is appropriate for codrawing with PMMA. We include an indium wire of 1 mm diameter and 99.99% purity in a PMMA tube with 1 mm inner diameter (ID) and 12 mm outside diameter (OD) which is sealed at one end. The tube is evacuated and drawn down to an outer diameter of 1.2 mm. The resulting fiber is then cut into smaller pieces, and stacked into a larger PMMA tube. This stack is sealed at one end and fed into a furnace while being rapidly drawn, reducing the diameter of the structure by a factor of 10, and increasing the length by a factor of 100. Such fibers possess features on the micro- and nano- scale, are inherently flexible, mass-producible, and can be woven to exhibit electromagnetic properties that are not found in nature. They represent a promising platform for a number of novel devices from terahertz to optical frequencies, such as invisible fibers, woven negative refractive index cloths, and super-resolving lenses.

Metamaterial fibers were produced using the technique described. They was assembled from a preform of 1 mm PMMA fibers containing 100 &mu;m diameter continuous indium wires, shown in Figure 2, which in turn had themselves been drawn from a preform of 1 mm indium wires contained inside a 10 mm polymer jacket, which was produced by sleeving appropriately sized polymer tubes, as shown in the schematic of Figure 1. A microscope image of the cross section of an example of a metamaterial fiber...

Watch this Scientific Journal Video about Fabricating Metamaterials Using the Fiber Drawing Method at JoVE.com

Fabricating Metamaterials Using the Fiber Drawing Method

Metamaterials at terahertz frequencies offer unique opportunities, but are challenging to fabricate in bulk. We adapt the fabrication procedure for microstructured polymer optical fibers to inexpensively fabricate metamaterials potentially on an industrial scale. We produce polymethylmethacrylate fibers containing ~10 &mu;m diameter indium wires separated by ~100 &mu;m, which exhibit a terahertz plasmonic response.

Metamaterials are man-made composite materials, fabricated by assembling components much smaller than the wavelength at which they operate 1. They owe ...

Research

JoVE Journal

Engineering

Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics

We present a method for colloidal synthesis of silver nanocubes and the use of these in combination with a smooth gold film, to fabricate plasmonic ...

Fabrication of Nanopillar-Based Split Ring Resonators for Displacement Current Mediated Resonances in Terahertz Metamaterials

Terahertz (THz) split ring resonator (SRR) metamaterials (MMs) has been studied for gas, chemical, and biomolecular sensing applications because the SRR ...

Installation Method to Enhance Quality Control for Fiber Reinforced Polymer Spike Anchors

Fiber reinforced polymer (FRP) anchors are a promising way to enhance the performance of externally-bonded FRPs applied to existing structures, as they ...

Fabricating Reactive Surfaces with Brush-like and Crosslinked Films of Azlactone-Functionalized Block Co-Polymers

In this paper, fabrication methods that generate novel surfaces using the azlactone-based block co-polymer, poly (glycidyl methacrylate)-block-poly (vinyl ...

One-Step Approach to Fabricating Polydimethylsiloxane Microfluidic Channels of Different Geometric Sections by Sequential Wet Etching Processes

Polydimethylsiloxane (PDMS) materials are substantially exploited to fabricate microfluidic devices by using soft lithography replica molding techniques. ...

Design and Fabrication of an Optical Fiber Made of Water

In this report, an optical fiber of which the core is made solely of water, while the cladding is air, is designed and manufactured. In contrast with ...

Drawing and Hydrophobicity-patterning Long Polydimethylsiloxane Silicone Filaments

Polydimethylsiloxane (PDMS) silicone is a versatile polymer that cannot readily be formed into long filaments. Traditional spinning methods fail because ...

Fabricating van der Waals Heterostructures with Precise Rotational Alignment

In this work we describe a technique for creating new crystals (van der Waals heterostructures) by stacking distinct ultrathin layered 2D materials. We ...

Fabrication of a Fabry-P&#233;rot Etalon for Application in Trace-Gas Spectroscopy

Fabrication of a Low-Cost, Fiber-Coupled, and Air-Spaced Fabry-P&#233;rot Etalon

Author Spotlight: Fabrication of a Low-Cost, Fiber-Coupled, and Air-Spaced Fabry-P&#233;rot Etalon  

Fabry-P&#233;rot etalons (FPE) have found their way into many applications. In fields such as spectroscopy, telecommunications, and astronomy, FPEs are ...