Name: patterning via optical saturable transitions - fabrication and characterization
Uploaded: 2014-12-11T14:00:00
Description: Watch this Scientific Journal Video about Patterning via Optical Saturable Transitions - Fabrication and Characterization at JoVE.com

Thanks to Michael Knutson, Paul Hamric, Greg Scott, and Chris Landes for helpful discussions and assistance related to the custom inert atmosphere sample holder and assistance in the University of Utah student machine shop. P.C. acknowledges the NSF GRFP under Grant No. 0750758. P.C. acknowledges the University of Utah Nanotechnology Training Fellowship. R.M. acknowledges a NSF CAREER Award No. 1054899 and funding from the USTAR Initiative.

참고 : 클린 룸 클래스 100 조건 또는 더 나은 아래의 모든 다음 단계를 수행하십시오. 1. 샘플 준비 <ol><li> (: 유해 화학 물질주의) 2 분 동안 버퍼 산화물 에칭 (BOE) 솔루션 (6 부품 40 % NH 4 F 1 부 49 %의 HF)와 2 &quot;직경의 실리콘 웨이퍼를 청소합니다. 표면에있는 유기물이나 오염 물질을 제거하려면이 에칭 시간을 선택합니다. 약 5 분 동안 탈 이온수 (DI) 물에 씻어. 건조 N <...

<ol>
	<li>Brimhall, N., Andrew, T. L., Manthena, R. V., Menon, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Breaking+the+far-field+diffraction+limit+in+optical+nanopatterning+via+repeated+photochemical+and+electrochemical+transitions+in+photochromic+molecules.">Breaking the far-field diffraction limit in optical nanopatterning via repeated photochemical and electrochemical transitions in photochromic molecules.</a> Physical Review Letters. 107 (20), 205501 (2011).</li><li>Cantu, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Subwavelength+nanopatterning+of+photochromic+diaryethene+films.">Subwavelength nanopatterning of photochromic diaryethene films.</a> Applied Physics Letters. 100 (18), 183103 (2012).</li><li>Cantu, P., Andrew, T. L., Menon, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanopatterning+of+diarylethene+films+via+selective+dissolution+of+one+photoisomer.">Nanopatterning of diarylethene films via selective dissolution of one photoisomer.</a> Applied Physics Letters. 103 (17), 173112 (2013).</li><li>Abbe, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Beitr&#228;ge+zur+Theorie+des+Mikroskops+und+der+mikroskopischen+Wahrnehmung.">Beitr&#228;ge zur Theorie des Mikroskops und der mikroskopischen Wahrnehmung.</a> Archiv f&#252;r mikroskopische Anatomie. 9 (1), 413-418 (1873).</li><li>Li, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Achieving+&#955;/20+resolution+by+one-color+initiation+and+deactivation+of+polymerization.">Achieving &#955;/20 resolution by one-color initiation and deactivation of polymerization.</a> Science. 324 (5929), 910-913 (2009).</li><li>Fischer, J., von Freymann, G., Wegener, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+materials+challenge+in+diffraction-unlimited+direct-laser-writing+optical+lithography.">The materials challenge in diffraction-unlimited direct-laser-writing optical lithography.</a> Advanced Materials. 22 (32), 3578-3582 (2010).</li><li>Mirkin, C. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Beam+pen+lithography.">Beam pen lithography.</a> Nature Nanotechnology. 5, 637-640 (2010).</li><li>Xie, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Manipulating+spatial+light+fields+for+micro-+and+nano-photonics.">Manipulating spatial light fields for micro- and nano-photonics.</a> Physica E: Low-dimensional Systems and Nanostructures. 44, 1109-1126 (2012).</li><li>Leroy, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-speed+metal-insulator+transition+in+vanadium+dioxide+films+induced+by+an+electrical+pulsed+voltage+over+nano-gap+electrodes.">High-speed metal-insulator transition in vanadium dioxide films induced by an electrical pulsed voltage over nano-gap electrodes.</a> Applied Physics Letters. 100 (21), 213507 (2012).</li><li>Carr, D., Sekaric, L., Craighead, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measurement+of+nanomechanical+resonant+structures+in+single-crystal+silicon.">Measurement of nanomechanical resonant structures in single-crystal silicon.</a> Journal of Vacuum Science &amp; Technology B. 16 (6), 3821-3824 (1998).</li><li>Wilhelmi, O., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Rapid+prototyping+of+nanostructured+materials+with+a+focused+ion+beam.">Rapid prototyping of nanostructured materials with a focused ion beam.</a> Japanese Journal of Applied Physics. 47 (6), 2010-5014 (2008).</li><li>Hell, S. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Far-field+optical+nanoscopy.">Far-field optical nanoscopy.</a> Science. 316 (5828), 1153-1158 (2007).</li><li>Chou, S. Y., Krauss, P. R., Renstrom, P. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanoimprint+lithography.">Nanoimprint lithography.</a> Journal of Vacuum Science &amp; Technology B. 14, 4129 (1996).</li><li>Guillemette, M. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+topography+induces+3D+self-orientation+of+cells+and+extracellular+matrix+resulting+in+improved+tissue+function.">Surface topography induces 3D self-orientation of cells and extracellular matrix resulting in improved tissue function.</a> Integrative Biology. 1 (2), 196-204 (2009).</li></ol>

The fabrication, experimental setup and related operational procedures of Patterning via Optical Saturable Transitions (POST) have been described. By exploiting the linear switching properties of thermally stable photochromic molecules, POST offers new perspectives on circumventing the far-field diffraction limit.1-2,4
Previously long-term storage requirement of the samples was solved by storing the samples under N2, directly after the initial evaporation.2 How...

광학 리소그래피는 나노 구조 및 장치의 제조에 대단히 중요하다. 새로운 리소그래피 기술의 향상 발전은 새로운 장치의 새로운 세대를 가능하게하는 기능이있다. 8 ~ 11이 글에서 검토가 새로운 환성 분자를 사용하여 깊은 파장 이하의 해상도를 달성 광 리소그래피 기술의 클래스 표시됩니다. 이 방법은 광학 - 가포 전환 (POST)를 통해 패턴 화라고합니다. 1-3 POST 고유 즉, (1,2- 비스 (5,5&#39;- 디메틸 -2,2&#39;- bithiophen 일))의 광 변색 성 분자 천이 포화의 사상을 겸비한 신규 한 나노 기술 perfluorocyclopent -1- 엔이다. 놓고,이 화합물을 그 larg의 강력한 도구하게 간섭 리소그래피와 같은 유도 방출 핍층 (STED) 현미경 (12)에 사용되는 것과 같은 BTE,도 1이라2 및 3 차원의 잠재적 인 확장과 다양한 표면 위에 깊은 서브 파장 기능의 전자 영역 병렬 나노 패터닝. 광 변색 층은 원래 하나의 균질 한 상태입니다. 이 층은 λ (1)의 균일 한 조명에 노출되는 경우, 제 2 이성체 상태 (도 1c),도 2로 변환한다. 그 후 샘플은 제 이성체 상태로 샘플 (변환 λ (2)에 포커싱 된 노드에 노출 1O) 사방 노드의 근처 부근에서 제외. 노광량을 제어함으로써, 전환되지 않은 영역의 크기는 임의로 작게 만들어 질 수있다. 이성체 중 하나의 후속 정착 단계는 선택적으로 패턴을 비가 역적으로 잠글 (블랙) 3 차 상태 (잠금) 변환 될 수있다. 이어서, 층을 다시 원래의 상태로 락 영역을 제외한 모든 변환 한 λ, 균일 노출된다.단계들의 시퀀스는 그 간격 원방 회절 한계보다 작은 두 잠긴 영역 결과적으로 광학 샘플의 상대 변위로 반복 될 수있다. 따라서, 임의의 형상은 &quot;도트 매트릭스&quot;방식으로 패턴 화 될 수있다. 1-3

<table border="0" cellpadding="0" cellspacing="0" width="778">
	<tbody>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Name of Material/ Equipment</td>
			<td style="width:205px;">Company</td>
			<td style="width:119px;">Catalog Number</td>
			<td style="width:239px;">Comments/Description</td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">Isopropanol</td>
			<td style="width:205px;">Fisher Scientific</td>
			<td style="width:119px;">P/7500/15</td>
			<td style="width:239px;">CAUTION: flammable, use good 
			ventilation and avoid all ignition 
			sources.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Buffered Oxide Etch</td>
			<td style="width:205px;"></td>
			<td style="width:119px;"></td>
			<td></td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">Methanol</td>
			<td style="width:205px;">Ricca Chemical</td>
			<td style="width:119px;">48-293-2&#160;</td>
			<td style="width:239px;">CAUTION: flammable, use good 
			ventilation and avoid all ignition 
			sources.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Ethylene Glycol</td>
			<td style="width:205px;">Sigma-Aldrich</td>
			<td style="width:119px;">324558</td>
			<td>CAUTION: Harmful if swallowed</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Silicon wafer</td>
			<td style="width:205px;"></td>
			<td style="width:119px;"></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Diamond Scribe</td>
			<td style="width:205px;"></td>
			<td style="width:119px;"></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Glass Beakers</td>
			<td style="width:205px;"></td>
			<td style="width:119px;"></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Tweezers</td>
			<td style="width:205px;">Ted Pella</td>
			<td style="width:119px;">5226</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Reactive Ion Etching System</td>
			<td style="width:205px;">Oxford</td>
			<td style="width:119px;">Plasma Lab 80 Plus</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Inert Atmosphere Sample Holder</td>
			<td style="width:205px;">Proprietary In-house Designed</td>
			<td style="width:119px;"></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Polarizing beamsplitter cube</td>
			<td style="width:205px;">Thorlabs</td>
			<td style="width:119px;">PBS052</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">HeNe Laser</td>
			<td style="width:205px;">Melles Griot</td>
			<td style="width:119px;">25-LHP-171</td>
			<td>CAUTION: Wear safety glasses</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Half-wave plates</td>
			<td style="width:205px;">Thorlabs</td>
			<td style="width:119px;">WPH05M-633</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Thermal Evaporator</td>
			<td style="width:205px;">Proprietary In-house Designed</td>
			<td style="width:119px;"></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">TMV Super</td>
			<td style="width:205px;">TM Vacuum Products</td>
			<td style="width:119px;">TMV Super</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Voltammograph</td>
			<td style="width:205px;">Bioanalytical Systems</td>
			<td style="width:119px;">CV-37</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Shortwave UV lamp 365nm</td>
			<td style="width:205px;">UVP Analytik Jena Company</td>
			<td style="width:119px;">UVGL-25</td>
			<td>CAUTION: Wear UV safety glasses</td>
		</tr>
	</tbody>
</table>

patterning via optical saturable transitions - fabrication and characterization

This protocol describes the fabrication and characterization of nanostructures using a novel nanolithographic technique called Patterning via Optical Saturable Transitions (POST). In this technique the chemical properties of organic photochromic molecules that undergo single-photon reactions are exploited, enabling rapid top-down nanopatterning over large areas at low light intensities, thereby, allowing for the circumvention of the far-field diffraction barrier.4 Simple, cost-effective, high throughput and resolution alternatives to nanopatterning are being explored, such as, two-photon polymerization5,6, beam pen lithography (BPL)7, scanning electron beam lithography (SEBL), and focused ion beam (FIB) patterning. However, multi-photon approaches require high light intensities, which limit their potential for high throughput and offer low image contrast. Although, electron and ion beam lithographic processes offer increased resolution, the serial nature of the process is limited to slow writing speeds, which also prevents patterning of features over large areas. Beam-pen lithography is an approach towards parallel near-field optical lithography. However, the gap between the source of the beam and the surface of the photoresist needs to be controlled extremely precisely for good pattern uniformity and this is very challenging to accomplish for large arrays of beams. Patterning via Optical Saturable Transitions (POST) is an alternative optical nanopatterning technique for patterning sub-wavelength features1-3. Since this technique uses single photons instead of electrons, it is extremely fast and does not require high light intensities1-3, opening the door to massive parallelization.

제작 된 샘플 : 순환 전압 전류 측정에서 0.85 V의 산화 전압을도 3에서의 원자 힘 현미경 사진에 의해 도시 된 바와 같이, 상이한 산화 시간은 특성화 하였다. 50 nm 두께의 필름은 0.95 mW의 / ㎠의 전력 밀도에서 60 초 동안 400 nm 인 λ = 647 nm에서 정재파 노출시켰다. 산화 시간을 25 분에서 10 분으로 증가함에 1O 이루어지는 영역의 일부...

Watch this Scientific Journal Video about Patterning via Optical Saturable Transitions - Fabrication and Characterization at JoVE.com

Patterning via Optical Saturable Transitions - Fabrication and Characterization

We report that the diffraction limit of conventional optical lithography can be overcome by exploiting the transitions of organic photochromic derivatives induced by their photoisomerization at low light intensities.1-3 This paper outlines our fabrication technique and two locking mechanisms, namely: dissolution of one photoisomer and electrochemical oxidation.

광학 가포 전환을 통해 패터닝 - 제조 및 특성

This protocol describes the fabrication and characterization of nanostructures using a novel nanolithographic technique called Patterning via Optical ...

Research

JoVE Journal

Engineering

Simulation, Fabrication and Characterization of THz Metamaterial Absorbers

THz Metamaterial Absorbers 시뮬레이션, 제조 및 특성

Metamaterials (MM),  artificial materials engineered to have properties that may not be found in  nature, have been widely explored since the first ...

연구

공학

Fabrication And Characterization Of Photonic Crystal Slow Light Waveguides And Cavities

광자 크리스탈 느린 경 Waveguides 그리고 안의 공간의 제조 및 특성

Slow light has been one of the hot topics in the photonics community in the past decade, generating great interest both from a fundamental point of view ...

Design, Fabrication, and Experimental Characterization of Plasmonic Photoconductive Terahertz Emitters

Plasmonic의 광전 테라 헤르츠 터의 설계, 제작 및 실험 특성

In this video article we present a detailed demonstration of a highly efficient method for generating terahertz waves. Our technique is based on ...

Fabrication and Characterization of Disordered Polymer Optical Fibers for Transverse Anderson Localization of Light

빛의 통과 앤더슨 현지화 무질서 폴리머 광섬유의 제조 및 특성

We develop and characterize a disordered polymer optical fiber that uses transverse Anderson localization as a novel waveguiding mechanism. The developed ...

Fabrication of Uniform Nanoscale Cavities via Silicon Direct Wafer Bonding

실리콘 다이렉트 웨이퍼 본딩을 통한 균일한 나노스케일 캐비티 제조

Measurements of the heat capacity and superfluid fraction of confined 4He have been performed near the lambda transition using lithographically patterned ...

Fabrication and Operation of a Nano-Optical Conveyor Belt

나노 광학 컨베이어 벨트의 제작 및 운영

The technique of using focused laser beams to trap and exert forces on small particles has enabled many pivotal discoveries in the nanoscale biological ...

Compact Lens-less Digital Holographic Microscope for MEMS Inspection and Characterization

MEMS 검사 및 특성화를위한 소형 렌즈가없는 디지털 홀로그램 현미경

A micro-electro-mechanical-system (MEMS) is a widely used component in many industries, including energy, biotechnology, medical, communications, and ...

Printing Fabrication of Bulk Heterojunction Solar Cells and In Situ Morphology Characterization

Printing Fabrication of Bulk Heterojunction Solar Cells and In Situ Morphology Characterization

벌크 이종 접합 태양 전지의 인쇄 제작 및<em&gt; 현장에서</em&gt; 형태학 특성

Polymer-based materials hold promise as low-cost, flexible efficient photovoltaic devices. Most laboratory efforts to achieve high performance devices ...

Fabrication and Characterization of Superconducting Resonators

Superconducting microwave resonators are of interest for a wide range of applications, including for their use as microwave kinetic inductance detectors ...