Name: reverse microemulsion-mediated synthesis of monometallic and bimetallic early transition metal carbide and nitride nanoparticles
Uploaded: 2015-11-27T14:00:00
Description: Watch this Scientific Journal Video about Reverse Microemulsion-mediated Synthesis of Monometallic and Bimetallic Early Transition Metal Carbide and Nitride Nanoparticles at JoVE.com

This work was sponsored by the Chemical Sciences, Geosciences and Biosciences Division, Office of Basic Energy Sciences, Office of Science, U.S. Department of Energy, grant no. DE-FG02-12ER16352. S.T.H. thanks the National Science Foundation for financial support through the National Science Foundation Graduate Research Fellowship under Grant No. 1122374.

실리카 캡슐화 단본위제 또는 바이메탈 금속 산화물 나노 입자의 합성 (1) <ol><li> 역 마이크로 에멀젼을 준비 <ol><li> 깨끗하고 졸업 오븐 건조 실린더를 사용하여 오븐 건조 자기 교반 막대를 포함하는 바닥 플라스크 (RBF) 라운드 깨끗하고 오븐 건조 1 L에 무수 n- 헵탄 240 ML을 추가합니다. </li><li> 일정한 교반 n- 헵탄에 폴리 옥시 에틸렌 (4) 라 우릴 에테르 54 ML을 추가합니다. 참고 : 때문에 고?...

<ol>
	<li>Oyama, S. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> The Chemistry of Transition Metal Carbides and Nitrides. , (1996).</li><li>Michalsky, R., Zhang, Y. -. J., Medford, A. J., Peterson, A. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Departures+from+the+Adsorption+Energy+Scaling+Relations+for+Metal+Carbide+Catalysts.">Departures from the Adsorption Energy Scaling Relations for Metal Carbide Catalysts.</a> J. Phys. Chem. C. 118 (24), 13026-13034 (2014).</li><li>Kimmel, Y. C., Xu, X., Yu, W., Yang, X., Chen, J. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Trends+in+Electrochemical+Stability+of+Transition+Metal+Carbides+and+Their+Potential+Use+As+Supports+for+Low-Cost+Electrocatalysts.">Trends in Electrochemical Stability of Transition Metal Carbides and Their Potential Use As Supports for Low-Cost Electrocatalysts.</a> ACS Catal. 4 (5), 1558-1562 (2014).</li><li>Levy, R. B., Boudart, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Platinum-like+behavior+of+tungsten+carbide+in+surface+catalysis.">Platinum-like behavior of tungsten carbide in surface catalysis.</a> Science. 181, 547-549 (1973).</li><li>Chen, Z., Higgins, D., Yu, A., Zhang, L., Zhang, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+review+on+non-precious+metal+electrocatalysts+for+PEM+fuel+cells.">A review on non-precious metal electrocatalysts for PEM fuel cells.</a> Energy Environ. Sci. 4 (9), 3167-3192 (2011).</li><li>Esposito, D. V., Chen, J. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Monolayer+platinum+supported+on+tungsten+carbides+as+low-cost+electrocatalysts:+opportunities+and+limitations.">Monolayer platinum supported on tungsten carbides as low-cost electrocatalysts: opportunities and limitations.</a> Energy Environ. Sci. 4, 3900 (2011).</li><li>Stottlemyer, A. L., Kelly, T. G., Meng, Q., Chen, J. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reactions+of+oxygen-containing+molecules+on+transition+metal+carbides:+Surface+science+insight+into+potential+applications+in+catalysis+and+electrocatalysis.">Reactions of oxygen-containing molecules on transition metal carbides: Surface science insight into potential applications in catalysis and electrocatalysis.</a> Surf. Sci. Rep. 67, 201-232 (2012).</li><li>Bell, A. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+impact+of+nanoscience+on+heterogeneous+catalysis.">The impact of nanoscience on heterogeneous catalysis.</a> Science. 299, 1688-1691 (2003).</li><li>Kimmel, Y. C., Esposito, D. V., Birkmire, R. W., Chen, J. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+surface+carbon+on+the+hydrogen+evolution+reactivity+of+tungsten+carbide+(WC)+and+Pt-modified+WC+electrocatalysts.">Effect of surface carbon on the hydrogen evolution reactivity of tungsten carbide (WC) and Pt-modified WC electrocatalysts.</a> Int. J. Hydrogen Energy. 37, 3019-3024 (2012).</li><li>Yang, X., Kimmel, Y. C., Fu, J., Koel, B. E., Chen, J. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Activation+of+Tungsten+Carbide+Catalysts+by+Use+of+an+Oxygen+Plasma+Pretreatment.">Activation of Tungsten Carbide Catalysts by Use of an Oxygen Plasma Pretreatment.</a> ACS Catal. 2, 765-769 (2012).</li><li>Garcia-Esparza, A. T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tungsten+carbide+nanoparticles+as+efficient+cocatalysts+for+photocatalytic+overall+water+splitting.">Tungsten carbide nanoparticles as efficient cocatalysts for photocatalytic overall water splitting.</a> ChemSusChem. 6, 168-181 (2013).</li><li>Yan, Z., Cai, M., Shen, P. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanosized+tungsten+carbide+synthesized+by+a+novel+route+at+low+temperature+for+high+performance+electrocatalysis.">Nanosized tungsten carbide synthesized by a novel route at low temperature for high performance electrocatalysis.</a> Sci. Rep. 3, 1646 (2013).</li><li>Giordano, C., Erpen, C., Yao, W., Antonietti, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+Mo+and+W+carbide+and+nitride+nanoparticles+via+a+simple+'urea+glass'+route.">Synthesis of Mo and W carbide and nitride nanoparticles via a simple 'urea glass' route.</a> Nano Lett. 8, 4659-4663 (2008).</li><li>Abdullaeva, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High+temperature+stable+WC1&#8722;x@C+and+TiC@C+core&#8211;shell+nanoparticles+by+pulsed+plasma+in+liquid.">High temperature stable WC1&#8722;x@C and TiC@C core&#8211;shell nanoparticles by pulsed plasma in liquid.</a> R. Soc. Chem. Adv. 3, 513 (2013).</li><li>Vallance, S. R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Probing+the+microwave+interaction+mechanisms+and+reaction+pathways+in+the+energy-efficient,+ultra-rapid+synthesis+of+tungsten+carbide.">Probing the microwave interaction mechanisms and reaction pathways in the energy-efficient, ultra-rapid synthesis of tungsten carbide.</a> Green Chem. 14, 2184 (2012).</li><li>Shen, P. K., Yin, S., Li, Z., Chen, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+performance+of+nanosized+tungsten+carbides+for+electrocatalysis.">Preparation and performance of nanosized tungsten carbides for electrocatalysis.</a> Electrochim. Acta. 55, 7969-7974 (2010).</li><li>Nikiforov, A. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=WC+as+a+non-platinum+hydrogen+evolution+electrocatalyst+for+high+temperature+PEM+water+electrolysers.">WC as a non-platinum hydrogen evolution electrocatalyst for high temperature PEM water electrolysers.</a> Int. J. Hydrogen Energy. 37, 18591-18597 (2012).</li><li>Fang, Z. Z., Wang, X., Ryu, T., Hwang, K. S., Sohn, H. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis,+sintering,+and+mechanical+properties+of+nanocrystalline+cemented+tungsten+carbide+&#8211;+A+review.">Synthesis, sintering, and mechanical properties of nanocrystalline cemented tungsten carbide &#8211; A review.</a> Int. J. Refract. Met. Hard Mater. 27, 288-299 (2009).</li><li>Liu, Y., Kelly, T. G., Chen, J. G., Mustain, W. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Metal+Carbides+as+Alternative+Electrocatalyst+Supports.">Metal Carbides as Alternative Electrocatalyst Supports.</a> ACS Catal. 3, 1184-1194 (2013).</li><li>Nie, M., Shen, P. K., Wei, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanocrystaline+tungsten+carbide+supported+Au&#8211;Pd+electrocatalyst+for+oxygen+reduction.">Nanocrystaline tungsten carbide supported Au&#8211;Pd electrocatalyst for oxygen reduction.</a> J. Power Sources. 167 (1), 69-73 (2007).</li><li>Ham, D. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Palladium-nickel+alloys+loaded+on+tungsten+carbide+as+platinum-free+anode+electrocatalysts+for+polymer+electrolyte+membrane+fuel+cells.">Palladium-nickel alloys loaded on tungsten carbide as platinum-free anode electrocatalysts for polymer electrolyte membrane fuel cells.</a> Chem Commun (Camb). 47 (20), 5792-5794 (2011).</li><li>Yan, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Template-free+pseudomorphic+synthesis+of+tungsten+carbide+nanorods.">Template-free pseudomorphic synthesis of tungsten carbide nanorods.</a> Small. 8, 3350-3356 (2012).</li><li>Esposito, D. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Low-cost+hydrogen-evolution+catalysts+based+on+monolayer+platinum+on+tungsten+monocarbide+substrates.">Low-cost hydrogen-evolution catalysts based on monolayer platinum on tungsten monocarbide substrates.</a> Angew. Chem. Int. Ed. 49, 9859-9862 (2010).</li><li>Esposito, D. V., Hunt, S. T., Kimmel, Y. C., Chen, J. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+new+class+of+electrocatalysts+for+hydrogen+production+from+water+electrolysis:+metal+monolayers+supported+on+low-cost+transition+metal+carbides.">A new class of electrocatalysts for hydrogen production from water electrolysis: metal monolayers supported on low-cost transition metal carbides.</a> J. Am. Chem. Soc. 134, 3025-3033 (2012).</li><li>Kelly, T. G., Hunt, S. T., Esposito, D. V., Chen, J. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Monolayer+palladium+supported+on+molybdenum+and+tungsten+carbide+substrates+as+low-cost+hydrogen+evolution+reaction+(HER)+electrocatalysts.">Monolayer palladium supported on molybdenum and tungsten carbide substrates as low-cost hydrogen evolution reaction (HER) electrocatalysts.</a> Int. J. Hydrogen Energy. 38, 5638-5644 (2013).</li><li>Hunt, S. T., Nimmanwudipong, T., Roman-Leshkov, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Engineering+non-sintered,+metal-terminated+tungsten+carbide+nanoparticles+for+catalysis.">Engineering non-sintered, metal-terminated tungsten carbide nanoparticles for catalysis.</a> Angew. Chem. Int. Ed. Engl. 53 (20), 5131-5136 (2014).</li><li>Mehrota, R. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Alkoxides+and+Alkylalkoxides+of+Metals+and+Metalloids.">Alkoxides and Alkylalkoxides of Metals and Metalloids.</a> Inorg. Chim. Acta. 1, 99-112 (1967).</li><li>Munoz-Aguado, M., Gregorkiewitz, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Sol-Gel+Synthesis+of+Microporous+Amorphous+Silica+from+Purely+Inorganic+Precursors.">Sol-Gel Synthesis of Microporous Amorphous Silica from Purely Inorganic Precursors.</a> J. Colloid Interface Sci. 185, 459-465 (1997).</li></ol>

가변 크기와 구조를 갖는 비 소결 금속 말단 전이 금속 탄화물 및 질화물 나노 입자를 합성하는 방법은 여기에서 제시되는 방법은 26 긴급 단계를 포함한다 :. 희석 된 금속 알콕시 드 전구체를 함유하는 수분이없는 RBF를 이용하여, 알칼리 금속을 피 침탄 또는 질화시켜 부품 및 플루오르 화 암모늄 작업시 적절한 PPE를 사용하기 전에 적절한 누설 검사를 수행, 아세톤 또는 이소프로판올과 ...

초기 전이 금속 탄화물 (TMCS)는 저비용, 높은 열적 및 전기 화학적 안정성뿐만 아니라 고유의 촉매 활성을 나타내는 지구 풍부한 물질이다. 특히 1-3, 텅스텐 카바이드 (WC)과 탄화 몰리브덴 (Mo를 2 C)이 때문에 이러한 유리한 특성 백금족 금속 (PGM). 4,5- 그들의 촉매 유사성 광범위하게 연구되고, TMCS는 바이오 매스 변환, 연료 전지 등의 재생 에너지 기술을 신흥 비싼 PGM 촉매를 교체하기위한 후보로서 식별 된 및 전해조. 6,7 촉매 활성을 최대화하기 위해, 상용 촉매는 거의 항상 카본 블랙 등의 초소형 나노 입자의 높은 표면적 지지체 상에 분산 된 (직경 &lt;10 ㎚)로 제형 화된다. 8 그러나 TMCS의 합성 ~ 700 °의 C보다 높은 온도를 필요로한다. 이것은 nanopartic 광범위 소결 리드레 NPS (), 과량의 표면 탄소 증착 (코크스), 및 열 열화 지원. 모두 입자 소결 지원 저하 리드 재료 표면 영역이 감소한다. 도시 된 과량의 표면 불순물 증착 블록 활성 금속 부위가 크게 감소 또는 어떤 경우에는 완전히의 TMCS. 9,10와 같은 촉매 활성을 제거하기 위해, TMC 반응성 기본적인 연구는 주로 대량 미립자 또는 얇은 필름에서 수행 미세 다소 높은 표면적 TMC의 나노 물질에 비해 표면을 통제했다. 많은 방법은 TMC NPS를 합성하기 위해 개발되어 왔지만,이 방법은 촉매 활성 TMC NPS를 합성하기에 적합하지 않다. 기존의 습식 함침 기술은 높은 비 표면적 지지체 상에 함침 된 금속 염 용액을 사용한다. 가열에, 습윤 함침 방법을 지원하기 위해 분해 선도 파괴 침탄 조건 촉매 지지체를 노출 할 수있다. 또한, 소결 C은 지지체상의 금속의 낮은 중량 %의 로딩에서 완화 될 수 있으며 습식 함 침법을 사용하여 지원되지 않는 TMC의 나노 분말을 합성하는 것도 가능하지 않다. 몇몇 최신의 방법은 탄소 전구체와 금속 전구체를 혼합하고, 종래와 비 전통적인 가열 기법을 적용. 11-18 과잉 탄소 소결을 방지하기 위해 사용되지만, 광범위한 표면 탄소이 과잉 탄소 결과는, 촉매 적용에 적합하지 이들 물질을 포함한다. 때문에 이러한 합성 도전, TMCS 전통적 PGMs 대한 조 촉매 (11)로서 연구되어, 촉매 19-22 PGMs 대한 지원 또는 활성 PGM 단층에 대해 지원한다. 23-25 ​​여기에 제시된 방법은 비 소결 양쪽을 합성하는 기능을 구비 금속 NP에 TMC 말단뿐 아니라 전이 금속 질화물 (TMN) 가변 크기, 결정 단계, 및 금속 조성 된 NP.도 26은 또한,이 방법은 AB를 제공 선물했다ility은 TMC 또는 TMN nanodispersions를 획득하거나 지원함으로써 열적 열화를 완화, 상온에서 고 표면적 촉매 지지체에 TMC TMN 및 NPS를 증착하도록. 이 방법은 TMC TMN 및 NP에 고급 multimetallic TMC TMN 및 NP에, 또는 미세하게 제어 된 입자 크기 및 표면을 필요로하는 다른 애플리케이션의 개발 촉매 독립형 애플리케이션에 적합하다. 26 여기에 제시된 방법은 TMC TMN 및 NPS를 합성하는 3 단계의 프로토콜을 사용한다. 1 단계에서, 역 마이크로 에멀젼 (RME)는 실리카 나노 코트에 초기 전이 금속 산화물 (TMO) NP에 사용된다. 에멀젼은 비 이온 계면 활성제를 상업적 이용 비극성 매체에 물방울을 분산시킴으로써 제조된다. 실리카 캡슐화 TMO의 NPS는 다음 침탄 또는 질 화성 열처리 중을 실시한다. 반응성 가스는 t로 확산시키면서 여기서, 실리카는 고온에서의 입자의 소결을 방지그는 TMO NP에와 TMC 또는 TMN 된 NP로 변환. 마지막 단계에서, 실리카 셸은 카본 블랙과 같은 고 표면적 지지체 상에 분산 될 수 TMC 또는 TMN nanodispersions을 얻었다 산성 또는 알칼리 처리를 사용하여 제거된다.

<table border="0" cellpadding="0" cellspacing="0">
	<tbody>
		<tr>
			<td>n-heptane</td>
			<td>Sigma-Aldrich</td>
			<td>246654</td>
			<td></td>
		</tr>
		<tr>
			<td>polyoxyethylene (4) lauryl ether</td>
			<td>Sigma-Aldrich</td>
			<td>235989</td>
			<td>Brij&#174; L4</td>
		</tr>
		<tr>
			<td>tungsten (VI) isopropoxide</td>
			<td>Alfa Aesar</td>
			<td>40247</td>
			<td>W(VI)IPO</td>
		</tr>
		<tr>
			<td>tungsten (VI) chloride</td>
			<td>Sigma-Aldrich</td>
			<td><a href="http://www.sigmaaldrich.com/catalog/product/aldrich/241911?lang=en&amp;region=US">241911</a></td>
			<td>To prepare W(VI)IPO, homemade</td>
		</tr>
		<tr>
			<td>tungsten (IV) chloride</td>
			<td>Strem Chemicals</td>
			<td>74-2348</td>
			<td>To prepare W(IV)IPO, homemade</td>
		</tr>
		<tr>
			<td>tantalum (V) isopropoxide</td>
			<td>Alfa Aesar</td>
			<td><a href="http://www.alfa.com/en/catalog/40038">40038</a></td>
			<td>Ta(V)IPO</td>
		</tr>
		<tr>
			<td>niobium (V) isopropoxide</td>
			<td>Alfa Aesar</td>
			<td><a href="http://www.alfa.com/en/catalog/36572">36572</a></td>
			<td>Nb(V)IPO</td>
		</tr>
		<tr>
			<td>nickel (II) methoxyethoxide</td>
			<td>Alfa Aesar</td>
			<td>42377</td>
			<td>Ni(II)MEO</td>
		</tr>
		<tr>
			<td>titanium (IV) isopropoxide</td>
			<td>Sigma-Aldrich</td>
			<td><a href="http://www.sigmaaldrich.com/catalog/product/aldrich/87560?lang=en&amp;region=US">87560</a></td>
			<td>Ti(IV)IPO</td>
		</tr>
		<tr>
			<td>molybdenum (V) isopropoxide</td>
			<td>Alfa Aesar</td>
			<td><a href="http://www.alfa.com/en/catalog/39159">39159</a></td>
			<td>Mo(V)IPO</td>
		</tr>
		<tr>
			<td>molybdenum (V) chloride</td>
			<td>Sigma-Aldrich</td>
			<td><a href="http://www.sigmaaldrich.com/catalog/product/aldrich/208353?lang=en&amp;region=US">208353</a></td>
			<td>To prepare Mo(V)IPO, homemade</td>
		</tr>
		<tr>
			<td>tetraethyl orthosilicate</td>
			<td>Sigma-Aldrich</td>
			<td>333859</td>
			<td>TEOS</td>
		</tr>
		<tr>
			<td>ammonium hydroxide</td>
			<td>Sigma-Aldrich</td>
			<td>320145</td>
			<td></td>
		</tr>
		<tr>
			<td>methanol</td>
			<td>Sigma-Aldrich</td>
			<td>34860</td>
			<td></td>
		</tr>
		<tr>
			<td>anhydrous isopropanol</td>
			<td>Sigma-Aldrich</td>
			<td><a href="http://www.sigmaaldrich.com/catalog/product/sial/278475?lang=en&amp;region=US">278475</a></td>
			<td>To prepare homemade alkoxides</td>
		</tr>
		<tr>
			<td>ammonium bifluoride</td>
			<td>Sigma-Aldrich</td>
			<td>224820</td>
			<td></td>
		</tr>
		<tr>
			<td>carbon black</td>
			<td>Cabot Corp.</td>
			<td>Vulcan&#174; XC72R</td>
			<td></td>
		</tr>
		<tr>
			<td>Methane</td>
			<td>AirGas</td>
			<td>ME R300</td>
			<td></td>
		</tr>
		<tr>
			<td>Hydrogen</td>
			<td>AirGas</td>
			<td>HY UHP300</td>
			<td></td>
		</tr>
		<tr>
			<td>Ammonia</td>
			<td>AirGas</td>
			<td>AM AH80N705</td>
			<td></td>
		</tr>
		<tr>
			<td>Quartz Tube Furnace</td>
			<td>MTI Corp.</td>
			<td>OTF-1200X-S-UL</td>
			<td></td>
		</tr>
	</tbody>
</table>

reverse microemulsion-mediated synthesis of monometallic and bimetallic early transition metal carbide and nitride nanoparticles

역 마이크로 에멀젼이 미다 실리카 껍질 단본위제 또는 바이메탈 초기 전이 금속 산화물 나노 입자를 캡슐화하는데 사용된다. 실리카 담지 된 금속 산화물 나노 입자는 실리카 캡슐화 초기 전이 금속 탄화물의 나노 입자를 형성하기 위해 800 ℃ 이상 고온에서 메탄 / 수소 분위기에서 침탄 처리​​된다. 또한 과량의 탄소 표면의 침착을 방지하면서 침탄 공정 중에, 실리카 포탄 인접 카바이드 나노 입자의 소결을 방지 할 수있다. 대안으로, 실리카 - 캡슐화 된 금속 산화물 나노 입자는 실리카 캡슐화 초기 전이 금속 질화물 나노 입자를 형성하기 위해 800 ℃ 이상 온도에서 암모니아 분위기 nitridized 수있다. 역 마이크로 에멀젼 파라미터, 실리카 껍질의 두께 및 침탄 / 질화 조건을 조정함으로써, 전이 금속 탄화물 또는 질화물 나노 입자는 다양한 크기, 조성물에 동조 할 수있다차 크리스탈 단계. 또는 침탄 질화 후, 실리카 쉘은 실온 수성 플루오르 화 암모늄 용액 또는 40-60 ℃에서 0.1~0.5 M NaOH 용액을 사용하여 제거된다. 실리카 껍질은 용해되지만, 고 표면적 지지체는, 카본 블랙 등,지지 초기 전이 금속 탄화물 또는 질화물 나노 입자를 얻기 위해 이들 용액에 첨가 될 수있다. 더 높은 표면적 지지체를 첨가하지 않은 경우, 나노 입자는 나노 분산 저장 또는 나노 분말을 얻기 위해 원심 분리 할 수​​있다.

프로토콜의 제 1 단계에서, 목표는 미세 다공성 실리카 구 내의 단본위제 또는 바이메탈 전이 금속 산화물 (TMO) NPS를 캡슐화하는 것이다. (1) 전에 메탄올로 침전 후 대표적인 합성의 촬영 된 영상을 보여준다. 두 재생 가능한 형태 학적 결과는 합성에 사용 된 금속에 의존 할 것으로 보인다이 단계에서 관찰되었다 : TMO의 NP는 단독 실리카 구 (도가 2B) 또는 다수...

Watch this Scientific Journal Video about Reverse Microemulsion-mediated Synthesis of Monometallic and Bimetallic Early Transition Metal Carbide and Nitride Nanoparticles at JoVE.com

Reverse Microemulsion-mediated Synthesis of Monometallic and Bimetallic Early Transition Metal Carbide and Nitride Nanoparticles

A &#8220;removable ceramic coating method&#8221; is presented in visual format for the synthesis of non-sintered and metal-terminated monometallic and bimetallic early transition metal carbide and nitride nanoparticles with tunable sizes and crystal structures.

단본위제 및 바이메탈 조기 전이 금속 탄화물 및 질화물 나노 입자의 역 마이크로 에멀젼 매개 합성

A reverse microemulsion is used to encapsulate monometallic or bimetallic early transition metal oxide nanoparticles in microporous silica shells. The ...

Research

JoVE Journal

Chemistry

Anticancer Metal Complexes: Synthesis and Cytotoxicity Evaluation by the MTT Assay

MTT의 분석에 의해 합성 및 세포 독성 평가 : 항암 금속 합성물

Titanium (IV) and vanadium (V) complexes are highly potent anticancer agents. A challenge in their synthesis refers to their hydrolytic instability; ...

연구

화학

Synthesis and Characterization of Functionalized Metal-organic Frameworks

기능화의 합성 및 특성 금속 - 유기 프레임 워크

Metal-organic frameworks have attracted extraordinary amounts of research attention, as they are attractive candidates for numerous industrial and ...

Metal-free Synthesis of Ynones from Acyl Chlorides and Potassium Alkynyltrifluoroborate Salts

아실 염화물과 칼륨 Alkynyltrifluoroborate 소금에서 Ynones의 금속이 합성

Ynones are a valuable functional group and building block in organic synthesis. Ynones serve as a precursor to many important organic functional groups ...

Synthesis, Characterization, and Functionalization of Hybrid Au/CdS and Au/ZnS Core/Shell Nanoparticles

합성, 특성 및 하이브리드 금 / CD 및 금 /은 ZnS 코어 / 쉘 나노 입자의 작용 화

Plasmonic nanoparticles are an attractive material for light harvesting applications due to their easily modified surface, high surface area and large ...

Synthesis of Ligand-free CdS Nanoparticles within a Sulfur Copolymer Matrix

황 합체 매트릭스 내의 자유 리간드의 CDS 나노 입자의 합성

Aliphatic ligands are typically used during the synthesis of nanoparticles to help mediate their growth in addition to operating as high-temperature ...

Synthesis of a Water-soluble Metal&#8211;Organic Complex Array

Synthesis of a Water-soluble MetalÃƒÆ’Ã‚Â¢ÃƒÂ¢Ã¢â‚¬Å¡Ã‚Â¬ÃƒÂ¢Ã¢â€šÂ¬Ã…â€œOrganic Complex Array

수용성 유기 금속 복합 어레이의 합성

We demonstrate a method for the synthesis of a water-soluble multimetallic peptidic array containing a predetermined sequence of metal centers such as ...

In Situ Detection and Single Cell Quantification of Metal Oxide Nanoparticles Using Nuclear Microprobe Analysis

In Situ Detection and Single Cell Quantification of Metal Oxide Nanoparticles Using Nuclear Microprobe Analysis

제자리에서 검색 및 핵 현미경 분석을 사용 하 여 금속 산화물 나노 입자의 단일 셀 정량화

Micro-analytical techniques based on chemical element imaging enable the localization and quantification of chemical composition at the cellular level. ...

Synthesis and Performance Characterizations of Transition Metal Single Atom Catalyst for Electrochemical CO2 Reduction

Synthesis and Performance Characterizations of Transition Metal Single Atom Catalyst for Electrochemical CO2 Reduction

합성 및 전기 화학적 CO2 감소를 위한 전이 금속 단일 원자 촉매의 성능 Characterizations

This protocol presents both the synthesis method of the Ni single atom catalyst, and the electrochemical testing of its catalytic activity and selectivity ...

Ligand-Mediated Nucleation and Growth of Palladium Metal Nanoparticles

Ligand 중재 Nucleation 및 팔라듐 금속 나노 입자의 성장

The size, size distribution and stability of colloidal nanoparticles are greatly affected by the presence of capping ligands. Despite the key contribution ...

Synthesis of Bimetallic Pt/Sn-based Nanoparticles in Ionic Liquids

이온 액체의 바이메탈 Pt/Sn 기반 나노 입자의 합성

We demonstrate a method for the synthesis of bimetallic nanoparticles consisting of Pt and Sn. A synthesis strategy is used in which the particular ...