Name: colloidal synthesis of nanopatch antennas for applications in plasmonics and nanophotonics
Uploaded: 2016-05-28T15:00:00
Duration: 9 min 12 s
Description: Watch this Scientific Journal Video about Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics at JoVE.com

This work was supported by the Air Force Office of Scientific Research Young Investigator Research Program (AFOSR, Grant. No. FA9550-15-1-0301).

<ol>
	<li>Fan, J. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Self-Assembled+Plasmonic+Nanoparticle+Clusters.">Self-Assembled Plasmonic Nanoparticle Clusters.</a> Science. 328 (5982), 1135-1138 (2010).</li><li>Zhang, Q., Li, W., Wen, L. -. P., Chen, J., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+Synthesis+of+Ag+Nanocubes+of+30+to+70+in+Edge+Length+with+CF3COOAg+as+a+Precursor.">Facile Synthesis of Ag Nanocubes of 30 to 70 in Edge Length with CF3COOAg as a Precursor.</a> Chem. Eur. J. 16 (33), 10234-10239 (2010).</li><li>Sun, Y., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Shape-Controlled+Synthesis+of+Gold+and+Silver+Nanoparticles.">Shape-Controlled Synthesis of Gold and Silver Nanoparticles.</a> Science. 298 (5601), 2176-2179 (2002).</li><li>Xia, Y., Halas, N. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Shape-Controlled+Synthesis+and+Surface+Plasmonic+Properties+of+Metallic+Nanostructures.">Shape-Controlled Synthesis and Surface Plasmonic Properties of Metallic Nanostructures.</a> MRS Bull. 30 (05), 338-348 (2005).</li><li>Ciraci, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Probing+the+Ultimate+Limits+of+Plasmonic+Enhancement.">Probing the Ultimate Limits of Plasmonic Enhancement.</a> Science. 337 (6098), 1072-1074 (2012).</li><li>Chandran, S. P., Chaudhary, M., Pasricha, R., Ahmad, A., Sastry, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+Gold+Nanotriangles+and+Silver+Nanoparticles+Using+Aloevera+Plant+Extract.">Synthesis of Gold Nanotriangles and Silver Nanoparticles Using Aloevera Plant Extract.</a> Biotechnol. Prog. 22 (2), 577-583 (2006).</li><li>Perez-Juste, J., Pastoriza-Santos, I., Liz-Marz&#225;n, L. M., Mulvaney, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+nanorods:+Synthesis,+characterization+and+applications.">Gold nanorods: Synthesis, characterization and applications.</a> Coord. Chem. Rev. 249 (17-18), 1870-1901 (2005).</li><li>Nikoobakht, B., El-Sayed, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+Growth+Mechanism+of+Gold+Nanorods+(NRs)+Using+Seed-Mediated+Growth+Method.">Preparation and Growth Mechanism of Gold Nanorods (NRs) Using Seed-Mediated Growth Method.</a> Chem. Mater. 15 (10), 1957-1962 (2003).</li><li>Rycenga, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlling+the+Synthesis+and+Assembly+of+Silver+Nanostructures+for+Plasmonic+Applications.">Controlling the Synthesis and Assembly of Silver Nanostructures for Plasmonic Applications.</a> Chem. Rev. 111 (6), 3669-3712 (2011).</li><li>Cortie, M. B., McDonagh, A. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+Optical+Properties+of+Hybrid+and+Alloy+Plasmonic+Nanoparticles.">Synthesis and Optical Properties of Hybrid and Alloy Plasmonic Nanoparticles.</a> Chem. Rev. 111 (6), 3713-3735 (2011).</li><li>Halas, N. J., Lal, S., Chang, W. -. S., Link, S., Nordlander, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmons+in+Strongly+Coupled+Metallic+Nanostructures.">Plasmons in Strongly Coupled Metallic Nanostructures.</a> Chem. Rev. 111 (6), 3913-3961 (2011).</li><li>Rose, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Control+of+Radiative+Processes+Using+Tunable+Plasmonic+Nanopatch+Antennas.">Control of Radiative Processes Using Tunable Plasmonic Nanopatch Antennas.</a> Nano Lett. 14 (8), 4797-4802 (2014).</li><li>Akselrod, G. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Probing+the+mechanisms+of+large+Purcell+enhancement+in+plasmonic+nanoantennas.">Probing the mechanisms of large Purcell enhancement in plasmonic nanoantennas.</a> Nature Photon. 8 (11), 835-840 (2014).</li><li>Hoang, T. B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ultrafast+spontaneous+emission+source+using+plasmonic+nanoantennas.">Ultrafast spontaneous emission source using plasmonic nanoantennas.</a> Nat. Commun. 6, (2015).</li><li>Akselrod, G. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Leveraging+Nanocavity+Harmonics+for+Control+of+Optical+Processes+in+2D+Semiconductors.">Leveraging Nanocavity Harmonics for Control of Optical Processes in 2D Semiconductors.</a> Nano Lett. 15 (5), 3578-3584 (2015).</li><li>Mock, J. J., Hill, R. T., Tsai, Y. -. J., Chilkoti, A., Smith, D. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Probing+Dynamically+Tunable+Localized+Surface+Plasmon+Resonances+of+Film-Coupled+Nanoparticles+by+Evanescent+Wave+Excitation.">Probing Dynamically Tunable Localized Surface Plasmon Resonances of Film-Coupled Nanoparticles by Evanescent Wave Excitation.</a> Nano Lett. 12 (4), 1757-1764 (2012).</li><li>Skrabalak, S. E., Au, L., Li, X., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+synthesis+of+Ag+nanocubes+and+Au+nanocages.">Facile synthesis of Ag nanocubes and Au nanocages.</a> Nat. Protocols. 2 (9), 2182-2190 (2007).</li><li>Im, S. H., Lee, Y. T., Wiley, B., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Large-Scale+Synthesis+of+Silver+Nanocubes:+The+Role+of+HCl+in+Promoting+Cube+Perfection+and+Monodispersity.">Large-Scale Synthesis of Silver Nanocubes: The Role of HCl in Promoting Cube Perfection and Monodispersity.</a> Angew. Chem. Int. Ed. 44 (14), 2154-2157 (2005).</li><li>Moreau, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlled-reflectance+surfaces+with+film-coupled+colloidal+nanoantennas.">Controlled-reflectance surfaces with film-coupled colloidal nanoantennas.</a> Nature. 492 (7427), 86-89 (2012).</li><li>Lassiter, J. B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmonic+Waveguide+Modes+of+Film-Coupled+Metallic+Nanocubes.">Plasmonic Waveguide Modes of Film-Coupled Metallic Nanocubes.</a> Nano Lett. 13 (12), 5866-5872 (2013).</li></ol>

The authors declare that they have no competing financial interests.

Nanocubes d&#39;argent ont été chimiquement synthétisés en utilisant des conditions de réaction similaires à des synthèses précédemment rapportées. 2,12,17-20 Cette synthèse permet la fabrication de nanocubes ayant des longueurs latérales allant de 50 à 100 nm. Par exemple, une période typique de chauffage de 2,5 heures entraînera nanocubes avec des longueurs latérales de ~ 75 nm. Un temps de synthèse plus longue (&gt; 3 h) va conduire à de plus grandes nanoparticules, cependant, cela peut également entraîner des différentes formes telles que nanocubes ou octaèdres tronqués. La solution finale a été centrifugé et remis en suspension dans de l&#39; eau déminéralisée, et peut être stocké pendant au moins un mois dans un réfrigérateur à 4 ° C sans aucun changement notable dans les spectres de diffusion des résonances de plasmon. 12 La taille et la forme des nanocubes Ag du procédé présenté dans le protocole ci-dessus sont très sensibles au nettoyage du RBF, son capuchon et la barre d&#39;agitation, ainsi que la qualité de la solution EG. Nanoparticules avec différentes formes telles que des nanoparticules arrondies ou allongées est un signe qu&#39;il ya probablement un problème avec une de ces étapes de la synthèse. Il est donc conseillé que les étapes 1.1.1-1.1.4 et 1.2.1-1.2.2 sont d&#39;une importance cruciale. Sur la figure 4b , le spectre de diffusion ont été recueillies à partir d&#39; une seule antenne est représentée Nanopatch qui présente une résonance plasmonique forte à 650 nm. Une telle résonance indique un excellent confinement de mode dans la région de l&#39;écart entre le nanocube Ag et Au cinéma rendue possible par nanocubes de haute qualité. En outre, pour obtenir un tel spectre, il est également nécessaire que l&#39;échantillon est propre, les couches d&#39;espacement (couches de PE) ont une épaisseur uniforme, et que le film d&#39;Au sous-jacent est lisse. La résonance plasmonique forte est confirmée par les données présentées dans la figure 4c , où les antennes de Nanopatch individuelles peuvent être observées dans l&#39;image sombre sur le terrain et dans la figure 4d où grande fluorescenceOn observe l&#39;amélioration des molécules Cy5 situées dans la zone d&#39;intervalle. Il convient également de noter que les nanocubes Ag oxydent au cours du temps en dépit du revêtement PVP lorsqu&#39;il est exposé à l&#39;air et, par conséquent, il est recommandé que les mesures optiques doivent être effectuées le jour où l&#39;échantillon est préparé ou de 1 à 3 jours. Pour réduire au minimum l&#39;oxydation, il est recommandé que les échantillons d&#39;antenne Nanopatch être stockés sous vide ou dans l&#39;azote gazeux. La méthode présentée dans ce document permet la fabrication de nanocubes Ag et les antennes de Nanopatch plasmoniques avec des dimensions bien contrôlées en utilisant la synthèse colloïdale et un processus couche par couche de revêtement par immersion. Par rapport aux autres techniques telles que la lithographie par faisceau optique ou électronique, la technique présentée ici offre la possibilité de production à faible coût et à grande échelle, tout en produisant une étroite distribution de tailles de nanoparticules. Les antennes de Nanopatch plasmoniques présentées dans ce document tiennent aussi une grande promesse pournouveaux nanomatériaux par la conception présentant des propriétés uniques qui peuvent ne pas exister dans leurs homologues macroscopiques. En particulier, ces nanoantennas ont montré record fluorescence amélioration des molécules de colorant incorporés dépassant 30.000; 12 améliorations de taux d&#39;émission spontanée de 1000; ultra - rapide de l&#39; émission spontanée et le rendement quantique élevé 13,14 En outre., il a été montré que des émetteurs couplés à ces antennes présentent Nanopatch d&#39;émission hautement directionnel qui est essentiel pour les applications où le couplage à un détecteur externe ou d&#39;une fibre monomode est nécessaire. Les applications futures des antennes patch à l&#39; échelle nanométrique peuvent aller de dispositifs optoélectroniques ultrarapides, tels que des diodes électroluminescentes, à haute photodétecteurs d&#39;efficacité et de dispositifs photovoltaïques, de détection et de technologies quantiques de traitement de l&#39; information. 12-14

Au cours des dernières années, la synthèse colloïdale de nanoparticules et l&#39;assemblage de ceux - ci dans des structures avancées ont suscité de grands intérêts à la fois dans la recherche et le développement industriel. 1-4 synthèse colloïdal de nanoparticules présentent plusieurs avantages par rapport aux nanostructures lithographique fabriqués , y compris supérieure homogénéité de taille, à faible coût et de la possibilité de grande échelle, la production parallèle. Des nanoparticules métalliques tels que l&#39; argent (Ag) et l&#39; or (Au) peut supporter des polaritons de plasmons de surface localisés et ont la possibilité de confiner la lumière dans un volume beaucoup plus petit que la limite de diffraction. 1,3-5 L&#39;intensité de champ élevée résultante crée une améliorée locale densité d&#39;états permettant des interactions lumière-matière à être adaptée à l&#39;échelle nanométrique. Les efforts récents ont démontré des procédures pour synthétiser Ag et Au nanoparticules dans une large gamme de tailles et de formes, y compris les triangles, 4,6 cages, 3,4 et tiges4,7,8 en plus des nanocubes discutées ici. Nanostructures composés de plusieurs nanocomposants Ag ou Au ont également été fabriqués sur mesure Démonstrations de propriétés. 1,9-11 Ici, nous démontrons une procédure pour synthétiser nanocubes Ag et plus important encore, de coupler ces nanocubes Ag avec un film d&#39;Au sous-jacente pour former des antennes Nanopatch plasmoniques. La distance entre nanocubes Ag et le film Au peut être contrôlé avec une résolution ~ nm à l&#39;aide d&#39;une série de couches d&#39;espacement polyélectrolyte. Nous démontrons également comment incorporer un milieu actif, tel qu&#39;un colorant organique, dans les antennes Nanopatch plasmonique. En raison des champs électromagnétiques fortement confinés dans la région de l&#39; écart entre les nanocubes et le film Au, les antennes de Nanopatch peuvent être utilisés pour hautement amélioré la fluorescence et l&#39; émission spontanée des molécules de colorant incorporés. 12,13 Les méthodes présentées dans le présent document peuvent être généralisés pour les autres émetteurs, Such selon l&#39; état ​​solide des points quantiques colloïdaux 14 ou matériaux semi - conducteurs bidimensionnels, 15 et la résonance de plasmon peut être réglée sur une large plage spectrale en faisant varier la taille des nanocubes ou le vide.

<table>
	<tbody>
		<tr>
			<td>Reagents</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Ethylene glycol&#160;</td>
			<td>J.T. Baker</td>
			<td>9300</td>
			<td>Must be anhydrous</td>
		</tr>
		<tr>
			<td>Sodium hydrosulfide hydrate&#160;&#160;</td>
			<td>Sigma Aldrich</td>
			<td>161527</td>
			<td></td>
		</tr>
		<tr>
			<td>Poly vinylpyrrolidone&#160;</td>
			<td>Sigma Aldrich</td>
			<td>856568</td>
			<td></td>
		</tr>
		<tr>
			<td>Hydrochroric acid BDH ARISTAR PLUS</td>
			<td>VWR International</td>
			<td>7647-01-0</td>
			<td></td>
		</tr>
		<tr>
			<td>Silver trifluoroacetate&#160;</td>
			<td>Sigma Aldrich</td>
			<td>482307</td>
			<td>Store in dark place</td>
		</tr>
		<tr>
			<td>Acetone</td>
			<td>Sigma Aldrich</td>
			<td>48358</td>
			<td></td>
		</tr>
		<tr>
			<td>Nitric acid&#160;</td>
			<td>Sigma Aldrich</td>
			<td>7697-37-2</td>
			<td>&#160;concentrated (70%), for cleaning</td>
		</tr>
		<tr>
			<td>Poly(allylamine) hydrochloride (PAH)</td>
			<td>Sigma-Aldrich</td>
			<td>283215</td>
			<td></td>
		</tr>
		<tr>
			<td>Polystyrene sulfonate&#160; (PSS)</td>
			<td>Sigma-Aldrich</td>
			<td>561223</td>
			<td></td>
		</tr>
		<tr>
			<td>Sodium Chloride&#160;</td>
			<td>Macron Inc.</td>
			<td>7647</td>
			<td></td>
		</tr>
		<tr>
			<td>Sulfo-Cyanine5 carboxylic acid (Cy5)</td>
			<td>Lumiprobe</td>
			<td>13390</td>
			<td>Fluorescent dye (molecular weight: 664.76 g/mol)</td>
		</tr>
		<tr>
			<td>Equipments</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Stirring hotplate with temperature control</td>
			<td>VWR International</td>
			<td>89000-338</td>
			<td></td>
		</tr>
		<tr>
			<td>Vortex mixers</td>
			<td>VWR International</td>
			<td>10153-834</td>
			<td></td>
		</tr>
		<tr>
			<td>Microcentrifuge</td>
			<td>Thermoscientific</td>
			<td>Model 59A</td>
			<td></td>
		</tr>
		<tr>
			<td>Silicone fluid&#160;</td>
			<td>Sigma-Aldrich</td>
			<td>63148-62-9</td>
			<td></td>
		</tr>
		<tr>
			<td>Micro-scale</td>
			<td>Mettler Toledo</td>
			<td>Model ML 104/03</td>
			<td></td>
		</tr>
		<tr>
			<td>Electron-beam metal evaporator&#160;</td>
			<td>CHA Industries</td>
			<td>E-beam evaporator</td>
			<td>Located inside a clean room</td>
		</tr>
		<tr>
			<td>Pre-cleaned glass slides</td>
			<td>Schott North America, Inc.</td>
			<td>Nexterion Glass B&#160;</td>
			<td>Clean room pre-cleaned</td>
		</tr>
		<tr>
			<td>25-mL 24/40 round-bottle flask&#160;</td>
			<td>VWR International</td>
			<td>60002-290</td>
			<td></td>
		</tr>
		<tr>
			<td>Magnetic stirring bar</td>
			<td>VWR International</td>
			<td>58948-116</td>
			<td></td>
		</tr>
		<tr>
			<td>Micropipettes (1-10mL, 10&#8211;100 mL and 100&#8211;1000 mL)</td>
			<td>VWR International</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Ultrasonic cleaning bath</td>
			<td>Branson Ultrasonic</td>
			<td>Model 1510R-DTH</td>
			<td></td>
		</tr>
		<tr>
			<td>Stopwatch</td>
			<td>VWR International</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Eppendorf centrifugation tubes (1.5 mL)</td>
			<td>VWR International</td>
			<td>22364111</td>
			<td></td>
		</tr>
		<tr>
			<td>Poly(propylene) coning tubes (50 mL)</td>
			<td>VWR International</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Home built bright/darkfield microscope</td>
			<td></td>
			<td></td>
			<td>75 W Xenon white light source, Nikon BF/DF 50x ELWD 
			0.55 NA, 8.2 mm WD objective, Nikon D90 digital camera, Acton 2300i spectrometer, Photometrics CoolSnap HQ&#160; charge coupled device (CCD) camera</td>
		</tr>
		<tr>
			<td>He Ne laser (633 nm), 5 mW</td>
			<td>New Port Co.</td>
			<td>R-30990</td>
			<td></td>
		</tr>
		<tr>
			<td>Reflectance standard</td>
			<td>Lab Sphere</td>
			<td>Model SRS-99-010</td>
			<td></td>
		</tr>
		<tr>
			<td>Laser long pass filter 633 nm</td>
			<td>Semrock</td>
			<td>LP02-633RU-25</td>
			<td></td>
		</tr>
	</tbody>
</table>

colloidal synthesis of nanopatch antennas for applications in plasmonics and nanophotonics

Nous présentons un procédé de synthèse colloïdale de nanocubes d&#39;argent et l&#39;utilisation de ceux-ci en combinaison avec un film d&#39;or lisse, pour fabriquer plasmoniques antennes patch nanométrique. Cela comprend une procédure détaillée pour la fabrication de films minces d&#39;une épaisseur bien contrôlée sur des zones macroscopiques en utilisant un dépôt de couche par couche de polymères polyélectrolytes, à savoir le poly (allylamine) (PAH) et le polystyrène sulfonate (PSS). Ces couches de polyélectrolyte d&#39;écartement servent d&#39;interstice diélectrique entre nanocubes d&#39;argent et une couche d&#39;or. En contrôlant la taille des nanocubes ou l&#39;épaisseur de la fente, la résonance de plasmon peut être réglée entre environ 500 nm à 700 nm. Ensuite, nous montrons comment incorporer un acide carboxylique (Cy5) des molécules de colorant sulfo-organiques cyanine5 dans la zone d&#39;intervalle de polymère diélectrique des antennes Nanopatch. Enfin, nous montrons grandement amélioré la fluorescence des colorants Cy5 en faisant correspondre spectralement la résonance plasmonique avec l&#39;énergie d&#39;excitation et til Cy5 pic d&#39;absorption. La méthode présentée ici permet la fabrication d&#39;antennes de Nanopatch plasmoniques avec des dimensions bien contrôlées en utilisant la synthèse colloïdale et un processus couche par couche de revêtement par immersion avec le potentiel de faible coût et de production à grande échelle. Ces antennes Nanopatch sont très prometteurs pour des applications pratiques, par exemple dans la détection, des dispositifs optoélectroniques ultrarapides et photodétecteurs à haute efficacité.

Ici, nous montrons les résultats représentatifs des caractéristiques des antennes Nanopatch plasmoniques, y compris des images au MEB de la structure des échantillons, un spectre de réflexion d&#39;un ensemble d&#39;antennes Nanopatch et un spectre de diffusion à partir d&#39;une antenne unique Nanopatch. L&#39;énergie de la résonance plasmon des antennes Nanopatch dépend de la taille des nanocubes, l&#39;épaisseur de la région d&#39;espacement diélectrique, soit le nombre de couches de PE, ainsi que le matériau diélectrique. Dans le mode opératoire présenté ci-dessus, nous avons obtenu nanocubes Ag avec une longueur de côté moyenne de 75 nm et des angles légèrement arrondis (rayon de courbure ~ 10 nm) enrobé dans une couche de PVP ayant une épaisseur d&#39;environ 1 à 3 nm. En combinaison avec les 5 couches PE et un film d&#39;or, ce résultat dans une résonance plasmon centrée à ~ 650 nm avec une pleine largeur au demi-hauteur (FWHM) de ~ 50 nm. Cela a un bon chevauchement spectral avec la longueur d&#39;onde d&#39;absorption et d&#39;émission de til Cy5 molécules qui est centrée à 646 et 662 nm, respectivement. La figure 3A montre une image MEB d&#39;un échantillon avec une concentration élevée de nanocubes. Ces nanocubes ont été déposées sur le dessus d&#39;un film de Au avec 5 couches de PE. Ces images MEB sont utilisés pour vérifier la qualité globale de la synthèse de nanocube; cependant, ces exemples ne sont pas utilisées pour d&#39;autres mesures que la densité optique des nanocubes est trop élevée. En outre, en raison de la densité élevée, certains nanocubes ne mentent pas sur la surface qui est essentiel pour former la structure d&#39;antenne Nanopatch plasmonique. La figure 3B montre une image MEB d&#39;un échantillon de nanocubes fabriqué en utilisant une solution de nanocube qui ont été dilués par un facteur de 1/10. Cet échantillon est utilisé pour les mesures où la réflectivité de la lumière blanche à partir d&#39;un ensemble d&#39;antennes Nanopatch a été mesurée pour déterminer larésonance plasmonique dans son ensemble. La figure 3C montre une image MEB d&#39;un échantillon de nanocubes fabriqué en utilisant une solution de nanocube qui ont été dilués par un facteur de 1/100. Cet échantillon est utilisé pour les mesures de diffusion d&#39;une antenne de Nanopatch individuelle. En utilisant la solution de nanocube diluée permet antennes Nanopatch individuelles pour être spatialement isolé à un plan d&#39;image en utilisant un petit trou. La figure 4A montre un spectre de réflexion, après normalisation avec le fond de la lumière blanche, mesurée à partir d&#39; un échantillon similaire à celui représenté dans l&#39;image MEB de la figure 3B. La figure 4B montre un spectre de diffusion à partir d&#39; une antenne unique Nanopatch similaire à l&#39;échantillon représenté sur la image SEM de la figure 3C. La figure 4C montre une image de champ sombre d&#39;un échantillon d&#39;antenne Nanopatch (préparé par un dixième0 solution nanocube diluée dispersé sur un film d&#39;or avec 5 PE couches) prise par un appareil photo numérique Nikon D90. Les points rouges lumineux observés sont dus à la diffusion de la lumière blanche des antennes de Nanopatch individuelles. Quelques taches sont observées pour avoir des couleurs autres que le rouge, ce qui est un résultat de nanocubes avec différentes tailles plus grandes ou des nanoparticules de forme non cubique. La figure 4D montre deux spectres de fluorescence, une mesure d&#39;une antenne Nanopatch unique ( à partir d&#39; un échantillon similaire à celui représenté sur la figure 3C) et l&#39;autre à partir d&#39; un échantillon témoin constitué d&#39;une lame de verre ayant le même nombre de couches de PE et la densité de Cy5 des molécules de colorant. L&#39;intensité de fluorescence des molécules Cy5 couplées à l&#39;antenne de Nanopatch est beaucoup plus forte que sur la lame de verre. Cela résulte d&#39;un taux d&#39;excitation amélioré ainsi qu&#39;un diagramme de rayonnement modifié et une plus grande efficacité quantique des molécules de colorant. 1<html> 2 Après correction de la fluorescence de fond et de normalisation par unité de surface en divisant l&#39;aire sous la nanocube avec la taille du spot d&#39;excitation, 12 on obtient un facteur d&#39;accroissement de ~ 12.000 à partir des données présentées dans la figure 4D. Ce facteur d&#39;amélioration est plus faible par rapport à la valeur précédemment déclarée de 30.000 12 probablement en raison de l&#39;utilisation d&#39;une Au lieu d&#39; un film Ag, ce qui augmente les pertes non radiatives. <img alt="Figure 1" src="/files/ftp_upload/53876/53876fig1.jpg" /> Figure 1. Configuration de l&#39; équipement pour la synthèse de nanocube Ag. (A) Une photographie de l&#39;installation de l&#39; équipement montrant le bain de chauffage au - dessus de la plaque de cuisson en remuant avec contrôle de la température. (B) Un gros plan du ballon à fond rond (RBF) contenant la solution de nanocube lors de la synthèse. L&#39;installation est située dans une hotte avec une ventilation de l&#39;air.tp: //www.jove.com/files/ftp_upload/53876/53876fig1large.jpg &quot;target =&quot; _ blank &quot;&gt; S&#39;il vous plaît cliquer ici pour voir une version plus grande de cette figure. <img alt="Figure 2" src="/files/ftp_upload/53876/53876fig2.jpg" /> Figure 2. Images de la solution de nanocube. (A) solution Nanocube après la synthèse de 2,5 h et (B) après le transfert dans des tubes plus petits et remis en suspension dans de l&#39;eau déminéralisée. <a href="https://www.jove.com/files/ftp_upload/53876/53876fig2large.jpg" target="_blank">S&#39;il vous plaît cliquer ici pour voir une version plus grande de cette figure .</a> <img alt="Figure 3" src="/files/ftp_upload/53876/53876fig3highres.jpg" width="700" /> Figure 3. SEM caractérisations de nanocubes Ag. (A) de l&#39; image SEM d&#39;un échantillon de nanocube concentré, (B) une dilution (1/10)échantillon nanocube, et (C) une dilution (1/100) de l&#39; échantillon de nanocube. <a href="https://www.jove.com/files/ftp_upload/53876/53876fig3highres.jpg" target="_blank">S&#39;il vous plaît cliquer ici pour voir une version plus grande de cette figure.</a> <img alt="Figure 4" src="/files/ftp_upload/53876/53876fig4highres.jpg" width="700" /> Figure 4. caractérisations optiques des antennes Nanopatch. (A) du spectre de réflexion mesuré à partir Normalisée d&#39; un ensemble d&#39;antennes de Nanopatch (solution nanocube non diluée). (B) spectre de diffusion à partir d&#39; une antenne unique Nanopatch (1/100 de la solution diluée nanocube). (C) de l&#39; image sur fond noir d&#39;un échantillon d&#39;antenne Nanopatch (1/100 de la solution diluée nanocube) prises sous un éclairage de lumière blanche. Chaque point rouge vif correspond à une antenne Nanopatch plasmonique individuelle. (D) à partir de la fluorescence des molécules de colorant Cy5 intégrerded dans une antenne Nanopatch (ligne rouge solide) par rapport à celle d&#39;une lame de verre avec une concentration identique de colorants Cy5 (ligne noire en pointillés). <a href="https://www.jove.com/files/ftp_upload/53876/53876fig4highres.jpg" target="_blank">S&#39;il vous plaît cliquer ici pour voir une version plus grande de cette figure.</a>

Watch this Scientific Journal Video about Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics at JoVE.com

Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics

Un protocole pour la synthèse colloïdale de nanocubes d&#39;argent et la fabrication de plasmoniques antennes patch à l&#39;échelle nanométrique avec des sous-10 nm lacunes est présenté.

Colloïdal Synthèse de Nanopatch Antennes pour Applications dans plasmonique et nanophotonique

We present a method for colloidal synthesis of silver nanocubes and the use of these in combination with a smooth gold film, to fabricate plasmonic ...

Research

JoVE Journal

Engineering

Hyperpolarized Xenon for NMR and MRI Applications

Xénon hyperpolarisé pour la RMN et l&#39;IRM Applications

Nuclear magnetic resonance (NMR) spectroscopy and imaging (MRI) suffer from intrinsic low sensitivity because even strong external magnetic fields of ~10 ...

Recherche

Ingénierie

Solid-state Graft Copolymer Electrolytes for Lithium Battery Applications

Solid-state greffe électrolytes de copolymère pour le lithium applications de batteries

Battery safety has been a very important research area over the past decade. Commercially available lithium ion batteries employ low flash point (&lt;80 ...

Synthesis and Operation of Fluorescent-core Microcavities for Refractometric Sensing

Synthèse et exploitation des Fluorescent-core Microcavités de détection réfractométrique

This paper discusses  fluorescent core microcavity-based sensors that can operate in a microfluidic  analysis setup. These structures are based on the ...

Three-dimensional Particle Tracking Velocimetry for Turbulence Applications: Case of a Jet Flow

Trois dimensions Velocimetry de suivi des particules pour Turbulence Applications: Cas d&#39;un débit de jet

3D-PTV is a quantitative flow measurement technique that aims to track the Lagrangian paths of a set of particles in three dimensions using stereoscopic ...

Creating Sub-50 Nm Nanofluidic Junctions in PDMS Microfluidic Chip via Self-Assembly Process of Colloidal Particles

Création de sous-50 Nm nanofluidiques Jonctions en PDMS microfluidique Chip via processus d&#39;auto-assemblage des particules colloïdales

Polydimethylsiloxane (PDMS) is the prevailing building material to make microfluidic devices due to its ease of molding and bonding as well as its ...

Scanning Light Scattering Profiler (SLPS) Based Methodology to Quantitatively Evaluate Forward and Backward Light Scattering from Intraocular Lenses

Scanning Light Scattering Profiler SLPS Based Methodology to Quantitatively Evaluate Forward and Backward Light Scattering from Intraocular Lenses

Méthodologie basée sur le Profiler de diffusion de lumière de balayage (SLPS) pour évaluer quantitativement la diffusion de lumière vers l&#39;avant et vers l&#39;arrière à partir de lentilles intraoculaires

The scanning light scattering profiler (SLSP) methodology has been developed for the full-angle quantitative evaluation of forward and backward light ...

Fabrication of Polymer Microspheres for Optical Resonator and Laser Applications

Fabrication de microsphères polymères pour résonateurs optiques et applications laser

This paper describes three methods of preparing fluorescent microspheres comprising &#960;-conjugated or non-conjugated polymers: vapor diffusion, ...

Fabrication of Periodic Gold Nanocup Arrays Using Colloidal Lithography

Fabrication de tableaux de Nanocup or périodique à l’aide de lithographie colloïdale

Within recent years, the field of plasmonics has exploded as researchers have demonstrated exciting applications related to chemical and optical sensing ...

Fabrication of Superhydrophobic Metal Surfaces for Anti-Icing Applications

Fabrication de Surfaces superhydrophobes en métal pour Applications d’antigivrage

Several ways to produce superhydrophobic metal surfaces are presented in this work. Aluminum was chosen as the metal substrate due to its wide use in ...

A Modular Microfluidic Technology for Systematic Studies of Colloidal Semiconductor Nanocrystals

Une technologie Microfluidic modulaire pour l’étude systématique des nanocristaux semiconducteurs colloïdal

Colloidal semiconductor nanocrystals, known as quantum dots (QDs), are a rapidly growing class of materials in commercial electronics, such as light ...