Name: a bending test for determining the atterberg plastic limit in soils
Uploaded: 2016-06-28T15:00:00
Description: Watch this Scientific Journal Video about A Bending Test for Determining the Atterberg Plastic Limit in Soils at JoVE.com

This research has been partially funded by a grant (Beca de Investigaci&#242;n Ambiental) from the Servicio de Medio Ambiente de la Diputaci&#242;n Provincial de Toledo (gran number 133/10) and the research project PEII-2014-025-P of the Junta de Comunidades de Castilla-La Mancha.

1. איסוף, ניקוי מסננת מדגם הבדיקה <ol style=";text-align:right;direction:rtl"><li style=";text-align:right;direction:rtl"> איסוף דגימת קרקע בתחום (להשתמש את חפירה או מרית) ולאחסן אותו בשקית פוליאתילן. הערה: היקף המדגם משתנה בהתאם לסוג הקרקע: בקרקעות בסדר (חרסיות silts) בין 100 ו- G 1,000 מספיקה בדרך כלל, אבל בקרקע...

<ol>
	<li>Atterberg, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=&#220;ber+die+physikalische+Bodenuntersuchung+und+&#252;ber+die+Plastizit&#228;t+der+Tone.">&#220;ber die physikalische Bodenuntersuchung und &#252;ber die Plastizit&#228;t der Tone.</a> Internationale Mitteilungen f&#252;r Bodenkunde. 1, 10-43 (1911).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> ASTM Standard ASTM D 4318. Standard Test Methods for Liquid Limit, Plastic Limit, and Plasticity Index of Soils. , (2005).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> UNE 103-103-94. Determinaci&#242;n del l&#236;mite l&#236;quido de un suelo por el m&#233;todo del aparato de Casagrande. , (1994).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> BS 1377-2. Methods of test for soils for civil engineering purposes-Part 2: Classification tests. , (1990).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> UNE 103-104-93. Determinaci&#242;n del l&#236;mite pl&#225;stico de un suelo. , (1993).</li><li>Whyte, I. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Soil+plasticity+and+strength:+a+new+approach+using+extrusion.">Soil plasticity and strength: a new approach using extrusion.</a> Ground Eng. 15 (1), 16-24 (1982).</li><li>Temyingyong, A., Chantawaragul, K., Sudasna-na-Ayudthya, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Statistical+Analysis+of+Influenced+Factors+Affecting+the+Plastic+Limit+of+Soils.">Statistical Analysis of Influenced Factors Affecting the Plastic Limit of Soils.</a> Kasetsart J. (Nat. Sci.). 36, 98-102 (2002).</li><li>Bobrowski, L. J., Griekspoor, D. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Determination+of+the+Plastic+Limit+of+a+Soil+by+Means+of+a+Rolling+Device.">Determination of the Plastic Limit of a Soil by Means of a Rolling Device.</a> Geotech. Test. J., GTJODJ. 15 (3), 284-287 (1992).</li><li>Rashid, A. S. A., Kassim, K. A., Katimon, A., Noor, N. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Determination+of+Plastic+Limit+of+soil+using+modified+methods.">Determination of Plastic Limit of soil using modified methods.</a> MJCE. 20 (2), 295-305 (2008).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> ASTM Standard ASTM D 248. Standard Practice for Classification of Soils for Engineering Purposes (Unified Soil Classification System). , (2000).</li><li>Casagrande, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Research+on+the+Atterberg+limits+of+soils.">Research on the Atterberg limits of soils.</a> Public Roads. 13 (8), 121-136 (1932).</li><li>Casagrande, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Classification+and+Identification+of+Soils.">Classification and Identification of Soils.</a> Transactions, ASCE. 113, 901-991 (1948).</li><li>Sokurov, V. V., Ermolaeva, N., Matroshilina, T. V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plastic+limit+of+clayey+soils+and+its+subjetive+determination.">Plastic limit of clayey soils and its subjetive determination.</a> Soil Mech. Found. Eng. 48 (2), 52-57 (2011).</li><li>Andrade, F. A., Al-Qureshi, H. A., Hotza, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measuring+the+plasticity+of+clays:+A+review.">Measuring the plasticity of clays: A review.</a> Appl. Clay Sci. 51, 1-7 (2011).</li><li>Harison, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Using+the+BS+cone+penetrometer+for+the+determination+of+the+plastic+limits+of+soils.">Using the BS cone penetrometer for the determination of the plastic limits of soils.</a> G&#233;otechnique. 38 (3), 433-438 (1988).</li><li>Feng, T. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fall-cone+penetration+and+water+content+relationship+of+clays.">Fall-cone penetration and water content relationship of clays.</a> G&#233;otechnique. 50 (2), 181-187 (2000).</li><li>Feng, T. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Using+a+small+ring+and+a+fall-cone+to+determinate+the+plastic+limit.">Using a small ring and a fall-cone to determinate the plastic limit.</a> ASCE, J. Geotech. Geoenviron. Eng. 130 (6), 630-635 (2004).</li><li>Lee, L. T., Freeman, R. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dual-weight+fall+cone+method+for+simultaneous+liquid+and+plastic+determination.">Dual-weight fall cone method for simultaneous liquid and plastic determination.</a> ASCE, J. Geotech. Geoenviron. Eng. 135 (1), 158-161 (2009).</li><li>Sivakumar, V., Glynn, D., Cairns, P., Black, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+new+method+of+measuring+plastic+limit+of+fine+materials.">A new method of measuring plastic limit of fine materials.</a> G&#233;otechnique. 59 (10), 813-823 (2009).</li><li>Sivakumar, V., O'Kelly, B. C., Henderson, L., Moorhead, C., Chow, S. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measuring+the+plastic+limit+of+fine+soils:+an+experimental+study.">Measuring the plastic limit of fine soils: an experimental study.</a> P. I. Civil Eng. - Geotec. 168 (GE-1), 53-64 (2015).</li><li>Wroth, C. P., Wood, D. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+correlation+of+index+properties+with+some+basic+engineering+properties+of+soils.">The correlation of index properties with some basic engineering properties of soils.</a> Can. Geotech. J. 15 (2), 137-145 (1978).</li><li>Haigh, S. K., Vardanega, P. J., Bolton, M. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+plastic+limit+of+clays.">The plastic limit of clays.</a> G&#233;otechnique. 63 (6), 435-440 (2013).</li><li>Barnes, G. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+apparatus+for+the+plastic+limit+and+workability+of+soils.">An apparatus for the plastic limit and workability of soils.</a> P. I. Civil Eng. - Geotec. 162 (3), 175-185 (2009).</li><li>Barnes, G. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+apparatus+for+the+determination+of+the+workability+and+plastic+limit+of+clays.">An apparatus for the determination of the workability and plastic limit of clays.</a> Appl. Clay Sci. 80-81, 281-290 (2013).</li><li>Moreno-Maroto, J. M., Alonso-Azc&#225;rate, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+accurate,+quick+and+simple+method+to+determine+the+plastic+limit+and+consistency+changes+in+all+types+of+clay+and+soil:+The+thread+bending+test.">An accurate, quick and simple method to determine the plastic limit and consistency changes in all types of clay and soil: The thread bending test.</a> Appl. Clay Sci. 114, 497-508 (2015).</li><li>Bain, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+plasticity+chart+as+an+aid+to+the+identification+and+assessment+of+industrial+clays.">A plasticity chart as an aid to the identification and assessment of industrial clays.</a> Clay Miner. 9 (1), 1-17 (1971).</li></ol>

מגבלת פלסטיק Atterberg 1 היא פרמטר חשוב מאוד בקרקעות, בעיקר כי זה נעשה שימוש נרחב למטרות גיאוטכני 10,11,12. המבחן מגלגל חוט התקן לקביעת PL זכה לביקורת נרחבת בגלל זה תלוי במידה רבה על המיומנות ושיקול הדעת של המפעיל ציפי לבן, שמנהל את הבדיקה ולכן גישות חדשות כדי להשיג ...

הגבל נוזלי (LL) ופלסטיק גבול (PL) הם שני גבולות עקביויות קרקע החשובים ביותר של אלה המוגדרים על ידי Atterberg בשנת 1911 1. LL מסמן את הגבול בין מדינות נוזלות פלסטיק, ו PL בין הפלסטיק ומדינות חצי קשות. LL מתקבל ברחבי העולם על פי כמה סטנדרטים באמצעות שיטת Casagrande 2,3 או חדירת המבחן 4. שתי השיטות נערכות באופן מכני על ידי התקנים; ובכך, הפרעות מפעיל מינימאליות הן מעורבות. במקרה של PL, &quot;מבחן מגלגל חוט&quot; שנקרא השיטה הפופולרית וסטנדרטי ביותר עבור נחישותה 2,5. מבחן זה מבוסס על גלגול אדמה אל 3 אשכולות מ&quot;מ ביד עד המפעיל רואה את האדמה עד שהם מתפוררות. מסיבה זו הוא זכתה לביקורת נרחבת בגלל המיומנות ושיקול הדעת של המפעיל לשחק תפקיד קריטי התוצאה של הבדיקה. מבחן מתגלגל התקן מושפע מכך על ידי גורמים בלתי מבוקרים רבים, כגוןכמו הלחץ המופעל, הגיאומטריה קשר, החיכוך, מהירות גלגול, את גודל המדגם פי סוג הקרקע 6,7. האגודה האמריקנית לבדיקות וחומרים (ASTM) פתחה את תקן ASTM D 4318 הכולל מכשיר פשוט כדי להקטין למינימום את ההפרעה מפעיל 2,8, אולם הבדלים משמעותיים דווחו כמה קרקעות כאשר משווים את הבדיקה מתגלגל הידנית נגד הבדיקה שבוצע על ידי מכשיר D4318 ASTM 9. PL הוא פרמטר חשוב מאוד למטרות גיאוטכני, מאז אינדקס פלסטיות (PI) מתקבל ממנו (PI = LL - PL); PI משמש לסווג את הקרקע בהתאם תרשים פלסטיות שמוצג ASTM D 2487 10, המבוסס על מחקר של Casagrande 11,12. שגיאות PL משפיעים כשלעצמם על סיווג זה שלילי 13, ומסיבה זו, בדיקה חדשה לקביעת PL נדרש. פפרקורן הבדיקה, חרוט penetrometer, rheometer נימים, rheometer המומנט או בדיקות-מתח מתח כמה דוגמאות של שיטות חלופיות למדידת אדמה פלסטית 14, אבל אלה אינם מספיקים כדי להשיג את PL. עם המופע המיוחד של בדיקות קונוס בסתיו, מספר רב של חוקרים ניסה להגדיר מתודולוגיה חדשה לקביעת PL באמצעות penetrometer השונה עיצובי 15-20, אבל בלי להגיע לשום הסכמה. יתר על כן, כל זה מבוסס על ההנחה כי כוח הגזירה על PL הוא 100 פעמים ב 21 LL, וזה לא נכון 22. בארנס 23,24 פתחה מנגנון, חיקה את התנאים המתגלגלים של בלוני קרקע בניסיון נשכב קריטריון ברור לקביעת PL. אף על פי כן, כמה חסרונות מזוהים עם גישה זו, כגון המשך המורכב, הבדיקה שלה ובעיקר את האמצעים בספק חישוב PL 25. ההצלחה של המבחן הסטנדרטי מתגלגלטמון בפשטותה, ביצועים מהירים ועלות נמוכה, ולכן אין שיטה חלופית תוכל להחליף אותו, אלא אם היא עונה על שלוש הדרישות הללו אחרים, כגון הפרעה מפעיל דיוק גבוה נמוכה. במחקר קודם על ידי המחברים, גישה חדשה PL הוצעה 25: החוט המקורי כיפוף מבחן (או פשוט כיפוף בדיקה) אפשר PL שיופק מן גרף שבו הוא ייצג את היחסים בין תכולת מים דפורמציות כיפוף. המחברים השיגו זממו כמה נקודות ניסיון עבור כל קרקע (הפרוטוקול אחריו כדי לקבל נקודות אלה היו זהים לזה מצוין בעבודה הנוכחית), כך קורלציה של הנקודות ניתן להגדיר בשתי דרכים מבלי להתפשר בשום אופן את הגדרה נכונה של שביל הנקודות: כמו עקומת פרבוליות, בשם העקום הכיפוף (איור 1 א), וכן שני קווים ישרים מצטלבים עם שיפוע שונה, בשם הקו הנוקשה-פלסטיקוקו-פלסטיק רך. השורה נוקשה-פלסטיק הוא התלול אחד, ו PL חושבה ממנו כאחוז לחות המתאים נקודת החיתוך של זה עם ציר y (איור 1B). בשנת נקודת החיתוך הזה הכיפוף המיוצר הוא אפס, וזה בהתאם מושג גבול פלסטיק, כלומר., PL הוא תכולת הלחות שבו הקרקע אינה מסוגלת לעמוד בפני דפורמציות מתחת לסף זה (מצב מוצק למחצה) אך היא עושה דוב אותם מעליו (מדינת פלסטיק). למרות במחקר המקורי, PL לא ניתן היה לקבל באופן ישיר על ידי עקומת כיפוף (זה לא יחתוך את ציר ה- y), קו זה היה מאוד שימושי כי בהתחשב כי עקומת כיפוף ואת קווים מצטלבים בנתיבים דומים מאוד, כיפוף משוואה עקומה מתקבלת על פי נתוני הניסוי שמשה להשיג נקודות נוספות כדי, ראשית, תתקן חריגה, ושנית, כדי לבצע את הבדיקה עם רק כמה נקודות כפי שמוצגת באיור 1 ב. &lt;<html> / P&gt; <img alt="איור 1" src="/files/ftp_upload/54118/54118fig1.jpg" /> ייצוג גרפי איור 1. מנקודות BW באדמה נבדקה על ידי מבחן הכיפוף המקורי. (א) המתאם של הנקודות מיוצגים עקום פרבוליות, בשם עקום כיפוף המשוואה אשר כלולה. (ב) המתאם של הנקודות מוגדרות על ידי שני קווים מצטלבים ו נקודות נוספות אחרות מתווספות (הם חושבו מתוך המשוואה העקומה הכיפוף). ערכי B מתקבלים כמו B = 52.0-D (כאשר D היא המרחק הממוצע הנמדד בין טיפים בעת פיצוח מ&quot;מ) ואת PL מחושבת כתוכן מים התואם את נקודת החיתוך של קו נוקשה-פלסטיק עם ציר y. נתון זה יש הבדל בין מורנו-Maroto &amp; אלונסו-Azcárate 25.k &quot;&gt; לחץ כאן כדי לצפות בגרסה גדולה יותר של דמות זו. כל התוצאות היו בהסכמה מעולה עם אלה מושגים באמצעות שיטת מגלגל חוט המסורתית על ידי מפעיל בעל ניסיון רב. עם זאת, בדיקת הכיפוף המקורית נשארת איטית יותר מאשר מבחן מגלגל חוט הסטנדרטי. בניסיון נוסף לחסוך זמן בדיקה, גרסת נקודות הועלתה. הוא התבסס על מדרון כיפוף הממוצע (מ &#39;) שהושג ב -24 קרקעות נבדקות, אשר היה 0.108 (m הוא השיפוע עקום הכיפוף כאשר הוא מיוצג סולם לוגריתמים כפול; מ&#39; מופיע על משוואת עקומת כיפוף באיור 1A) . באמצעות משוואה גורם שם זה נכלל, הוא השורות הנוקשה-הפלסטיק רך הפלסטיק נמשכו בצורה גרפית, וכך PL נאמד. תוצאות אלו גם היו בקורלציה גבוהה עם שני במבחן כיפוף ריבוי נקודות ואת המבחן מתגלגל הסטנדרטי. למרות versio חד בנקודה זוn להיות אפילו מהר יותר מאשר הבדיקה המסורתית, חישוב PL היה מורכב יותר בגלל המזימות היו הכרחיות. מסיבה זו, על בסיס קריטריונים סטטיסטיים משוואה חדשה לחישוב PL פותחה במחקר זה, כך זוממים אינו נדרש וניתן להשיג תוצאות עם רק נקודה אחת, ואילו פרוטוקול הניסוי הוא זהה כיפוף המקורי מִבְחָן. גרסה חדשה זו עומדת בדרישות ההכרחיות כדי להחליף את השיטה מגלגל החוט המיושנת.

<table border="0" cellpadding="0" cellspacing="0" width="978">
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:244px;">Shovel</td>
			<td style="width:76px;">Any</td>
			<td style="width:117px;">NA</td>
			<td style="width:541px;">It is preferable a round point metal shovel so that it can penetrate easily in the soil.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Trowel</td>
			<td>Any</td>
			<td>NA</td>
			<td>It should be easy to handle both in field and laboratory, so approximately 500 g of soil should be the maximum of soil that could pick up.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Polyethylene bags</td>
			<td>Any</td>
			<td>NA</td>
			<td>The size of the bags depends on the collected soil volume. If we were interested in preserving the natural moisture, use sealing tape to close the bag.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Soil splitter&#160;</td>
			<td>PROETISA</td>
			<td>S0012</td>
			<td>It is not mandatory, because the quartering can be performed with the shovel, but in case of using it: it must be big enough to split several kg of sample in the cases of soils with large amounts of gravel or pebbles.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Oven</td>
			<td>SELECTA</td>
			<td>2001254</td>
			<td>The oven must be able to maintain constant temperature and should have some sort of slot or outlet opening to facilitate the release of water vapor.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Lab trays</td>
			<td>Any</td>
			<td>NA</td>
			<td>Metal trays are preferred over plastic because the first ones tolerate the oven temperatures better than the second ones.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Mortar and pestle</td>
			<td>MECACISA</td>
			<td>V112-02</td>
			<td>A ceramic mortar is valid.&#160; It is recommended to use a rubber covered pestle because if the pestle was of other different materials (like metal or a ceramic), it could break the sand particles.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">0.40 mm sieve (or 0.425 mm sieve)</td>
			<td>FILTRA</td>
			<td>0,400 (or 0,425)</td>
			<td>Make sure that the sieve mesh is in perfect conditions of use (it should not be neither broken or worn).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Brush</td>
			<td>Any</td>
			<td>NA</td>
			<td>It is useful for passing the soil during the sieving.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Wash-bottle</td>
			<td>Any</td>
			<td>NA</td>
			<td>It should have an approximate capacity of one litre and it should be easy to control the amount of water that it releases.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Distilled water</td>
			<td>Any</td>
			<td>NA</td>
			<td>Distilled water can be purchased or obtained by filtering from tap water (in this last case, a filtering system is necessary).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Nonabsorbent smooth glass plate&#160;</td>
			<td>Any</td>
			<td>NA</td>
			<td>The plate should have a minimum area of approximately 30 &#215; 30 cm.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Metal spatula</td>
			<td>Any</td>
			<td>NA</td>
			<td>The metal blade of the spatula must be flexible. Dry it with a paper after water-cleaning to prevent rusting.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Latex gloves</td>
			<td>Any</td>
			<td>NA</td>
			<td>Latex, vinyl, nitrile or other impermeable materials are valid. They should be thin enough to sense the soil with the hands.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Cling film</td>
			<td>Any</td>
			<td>NA</td>
			<td>Normal cling film is valid.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Airtight bags</td>
			<td>Any</td>
			<td>NA</td>
			<td>Remove the air before closing them.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Thread molder</td>
			<td>Any</td>
			<td>NA</td>
			<td>It is a tool designed in this experiment (drawings with dimmensions are included in this paper).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Steel pushers</td>
			<td>Any</td>
			<td>NA</td>
			<td>It is a tool designed in this experiment (drawings with dimmensions are included in this paper).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Damp cloth</td>
			<td>Any</td>
			<td>NA</td>
			<td>A normal damph cloth is valid.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Roll of paper</td>
			<td>Any</td>
			<td>NA</td>
			<td>Normall rolls of paper used to dry hands are valid.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Caliper</td>
			<td>Any</td>
			<td>NA</td>
			<td>It must have an accuracy of at least 0.1 mm.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Paper and pen</td>
			<td>Any</td>
			<td>NA</td>
			<td>Paper and pen are used to write the results.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Containers with covers</td>
			<td>Any</td>
			<td>NA</td>
			<td>Small cylindrical glass containers are valid. If they do not have covers, watch glasses can be used as covers. Covers are useful to avoid the loss of water during the test and also to prevent the dry soil absorbs moisture from the air after oven drying.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Precision or analytical balance</td>
			<td>BOECO</td>
			<td>BPS 52 PLUS</td>
			<td>It must have an accuracy of at least 0.01 g.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Protective gloves</td>
			<td>Any</td>
			<td>NA</td>
			<td>Protective gloves are used to catch the metal trays from the oven.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Tongs</td>
			<td>Any</td>
			<td>NA</td>
			<td>Tongs are used to catch the hot containers from the oven.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Desiccator</td>
			<td>MECACISA</td>
			<td>A036-01</td>
			<td>A normal glass desiccator with silica gel is valid to prevent the dry soil absorbs moisture from the air after oven drying.</td>
		</tr>
	</tbody>
</table>

a bending test for determining the atterberg plastic limit in soils

המבחן מגלגל חוט הוא השיטה הנפוצה ביותר כדי לקבוע את גבול הפלסטיק (PL) בקרקעות. זה כבר לביקורת רבה, משום שיפוט סובייקטיבי ניכר מהמפעיל שמבצע את הבדיקה מעורבת במהלך הביצועים שלו, אשר עשויים להשפיע על התוצאה הסופית באופן משמעותי. שיטות חלופיות שונות הוצעו, אבל הם לא יכולים להתחרות עם המבחן מתגלגל הסטנדרטי מהירה, פשטות ועלות. במחקר קודם על ידי המחברים, שיטה פשוטה עם מכשיר פשוט לקבוע את PL הוצגה (להלן: &quot;חוט כיפוף מבחן&quot; או פשוט &quot;כיפוף בדיקה&quot;); שיטה זו אפשרה PL שתופק עם הפרעת מפעיל מינימאלית. בעבודה הנוכחית גרסה של מבחן הכיפוף המקורי מוצגת. הבסיס הניסיון זהה במבחן הכיפוף המקורי: אשכולות אדמה שהן 3 מ&quot;מ בקוטר 52 מ&quot;מ אורך מכופפים עד שהם מתחילים לפצח, כך ששני bending הפיק תכולת לחות הקשורים אליה נחושים. עם זאת, גרסה חדשה זו מאפשרת החישוב של PL מ משוואה, כך אין צורך לתכנן כל עקומה או בקו ישר להשיג פרמטר זה, למעשה, PL ניתן להשיג עם רק נקודה אחת ניסיוני (אבל שתי נקודות ניסיון מומלץ). תוצאות PL שהושגו עם גרסה חדשה זו הן מאוד דומות לאלה שהושגו באמצעות מבחן הכיפוף המקורי ואת המבחן מתגלגל תקן ידי מפעיל בעל ניסיון רב. רק במקרים מסוימים של קרקעות מלוכדות גבוהה פלסטיות, יש הבדל גדול בתוצאה. למרות זאת, בדיקת הכיפוף עובדת טוב מאוד עבור כל סוגי הקרקע, הוא הקרקעות מלוכדות מאוד נמוכות פלסטיות, כאשר האחרונות הם קשים ביותר שיש לבדוק באמצעות שיטת מגלגל חוט הרגילה.

<html> משוואת PL לראות בשלב 6.1 של הפרוטוקול הושגה באמצעות מחקר סטטיסטי של 24 הקרקעות נבדקו במחקר קודם של מחברים 25 (הטבלה 1). המטרה היתה להכיר את המדרון כיפוף הסביר ביותר (המונח מ במשוואה עקומת כיפוף, המופיע באיור 1 א) לבין השווי ה...

Watch this Scientific Journal Video about A Bending Test for Determining the Atterberg Plastic Limit in Soils at JoVE.com

A Bending Test for Determining the Atterberg Plastic Limit in Soils

המבחן הסטנדרטי המסורתי לקביעת גבול הפלסטיק בקרקעות מבוצע ביד, והתוצאה משתנית בהתאם למפעיל. שיטה חלופית המבוססת על מדידות כיפוף מוצגת במחקר זה. זה מאפשר להגביל פלסטיק שיופק עם קריטריון ברור ואובייקטיבי.

מבחן כיפוף לקביעת מגבלת פלסטיק Atterberg בקרקעות

The thread rolling test is the most commonly used method to determine the plastic limit (PL) in soils. It has been widely criticized, because a ...

The overall goal of this new procedure is to determine the plastic limit in soils by measuring bending deformations. The traditional thread-rolling method is highly influenced by the skill of the laboratory operators, so an alternative approach is presented. This method allows the plastic limit to be obtained with a clear and objective criterion.Therefore the obtained results are highly reliable to classify and identify soils for botanical purposes. The main advantage of this technique is that it is not only quick, simple, and cheap, but also accurate and free of subjective interpretations. Beginning with a fine soil sample, dry it at 60 degrees Celsius or less, as needed.Next, disaggregate the soil manually using a mortar. Preferably, use a rubber-lined pestle to avoid breaking up the sand particles. Then, pass the sample through a 0.4 millimeter sieve and discard the soil collected in the sieve.Now, take about 20 to 40 grams of soil and wet it down on a non-absorbent glass plate. Then, knead the sample with a metal spatula until a homogeneous soil-water mixture is obtained. Wearing latex gloves, roll the mixture into a ball that is between three and five centimeters in diameter.Now, make a second ball with more or less water than the first, so the balls have different moisture content. Both soil balls must not crumble or stick when they are handled. Then, wrap each soil ball with cling film and place them in an airtight bag.Store the bag for 24 hours under hermetic conditions. After the tempering period, wearing latex gloves, flatten the soil ball on a smooth glass plate into a nearly three-millimeter thick patty. Keep the patty's surface covered with cling film to avoid moisture loss.Then, using a thread moulder, get the thickness down to precisely three millimeters. Now, cut the jagged edges of the flattened soil mass with a spatula, and make strips of soil that are at least 52 millimeters long, and three millimeters wide. Next, roll the soil strip with the thread moulder until the square section just becomes round, so it is three millimeters in diameter.If the strip is too dry and crumbly, or too sticky, repeat the test, using soil with more or less water content. Next, place the soil thread next to the front side of the thread moulder, and use the width of the thread moulder to make the cylinder exactly 52 millimeters long. Now, turn the thread moulder upside-down, and put the cylindrical piece in contact with the central part of the soil thread.Put the steel pushers in contact with the center of the soil thread. Then, carefully move the steel pushers towards the tips of the soil thread in a circular path. Repeat this motion, until the point of cracking.If the first crack appears near one of the thread tips, keep bending the other tip until the second crack appears at the opposite end. Now, remove the thread moulder and use a caliber to measure the distance between the central part of each tip to a precision of 0.1 millimeter. Now, put the soil thread into a container of known weight, and cover it to prevent moisture loss.If the bending deformations are so large that even the thread tips come into contact, remove the pushers and thread moulder, and continue bending the soil thread by hand, until the point of cracking. Then measure the distance between the thread tips, and record a negative value. From the excess soil, shape other additional threads, but do not cut their tips.Store these in the same container, and cover it again. Now, make a second soil thread that is 52 millimeters long, like the first. Repeat the bending process on the second soil thread.If the results are similar, do not bend more threads. If they differed, shape and bend at least one more soil thread, until agreeable measurements are obtained. Once a minimum of five grams of threads are obtained, record the weight of the container with the soil threads to a precision of at least 01 grams.Now, repeat the entire process for the second ball of soil. Begin with placing the two containers of soil threads uncovered in an oven at 105 degrees Celsius to dry the soil for at least 18 hours. The next day, put the containers in a desiccator.Once they have cooled to ambient temperatures, record their weights to a precision of at least 01 grams. Then, place the containers back into the same oven for at least six more hours. Again, cool them in a desiccator, and measure their weight.Continue repeating this process until two consecutive weight measurements are completely identical, which is the weight of the soil when dry. Now, for each soil ball, using the known water content, W, and its bending at cracking, B, calculate the plastic limit of each ball. Then, use the average value to characterize the soil.The number, minus 0.108, in the plastic limit equation, corresponds to the average value of ending a slope obtained in a previous study with a multiple inversion in which 24 soils were tested. The number 2.135 refers to the average bending value corresponding to the plastic limit in the bending curve for those 24 soils, in accordance with our original multi-point test. The plastic limits calculated from 30 soils with the described bending test, were compared to the original multi-point bending test, and the standard rolling test.Each test was executed by a highly experienced operator, and the results were very similar. The plastic limit results obtained through the new bending test were highly correlated with the original bending test, and the standard thread-rolling test. Most results were perfectly correlated, even with very low-plasticity soils.After watching this video, you should have a good understanding of how the plastic limit can be obtained instantly and accurately with a simple test in which the operator does not play a critical role in the final outcome. Once mastered, this technique can be done in five to ten minutes. So it can be even faster than the traditional test.In addition to its quick performance, the simplicity, low cost, and accuracy of this test, make it easily affordable for any laboratory. After its development, this technique paved the way for researchers and companies in the field of geotechnics, agriculture, ceramics, and soil science, to obtain more reliable plastic limit results.

Research

Education

JoVE Core

JoVE Journal

Mechanical Engineering

Environment

Unit 1

Bending

SCIENTISTS IN ACTION

Determination of Microbial Extracellular Enzyme Activity in Waters, Soils, and Sediments using High Throughput Microplate Assays

קביעת מיקרוביאלית התאית אנזים הפעילות במים, קרקעות, ומשקעים באמצעות מבחני Microplate תפוקה גבוהה

Much of the nutrient cycling and carbon  processing in natural environments occurs through the activity of extracellular  enzymes released by ...

Integrated Field Lysimetry and Porewater Sampling for Evaluation of Chemical Mobility in Soils and Established Vegetation

משולב שדה Lysimetry וPorewater דגימה להערכת כימית ניידות בקרקעות וצמחייה הוקמה

Potentially toxic chemicals are routinely applied to land to meet growing demands on waste management and food production, but the fate of these chemicals ...

Measurement of Greenhouse Gas Flux from Agricultural Soils Using Static Chambers

מדידה של שטף גזי חממה מקרקעות חקלאיות באמצעות לשכות סטטי

Measurement of greenhouse gas (GHG) fluxes between the soil and the atmosphere, in both managed and unmanaged ecosystems, is critical to understanding the ...

Extraction and Analysis of Microbial Phospholipid Fatty Acids in Soils

הפקה וניתוח של פוספוליפידים מיקרוביאלית חומצות שומן בקרקעות

Phospholipid fatty acids (PLFAs) are key components of microbial cell membranes. The analysis of PLFAs extracted from soils can provide information about ...

Methods of Soil Resampling to Monitor Changes in the Chemical Concentrations of Forest Soils

שיטות Resampling הקרקע לעקוב אחר שינויים בריכוזיים הכימית של קרקעות יער

Recent soils research has shown that important chemical soil characteristics can change in less than a decade, often the result of broad environmental ...

Extraction of Organochlorine Pesticides from Plastic Pellets and Plastic Type Analysis

הפקת חומרי הדברה אורגנוכלורינים מפלסטיק וגלגול סוג פלסטיק

Plastic resin pellets, categorized as microplastics (&#8804;5 mm in diameter), are small granules that can be unintentionally released to the environment ...

Optimized Procedure for Determining the Adsorption of Phosphonates onto Granular Ferric Hydroxide using a Miniaturized Phosphorus Determination Method

אופטימיזציה הליך לקביעת ספיחה של Phosphonates על גבי הידרוקסיד Ferric פרטנית באמצעות שיטה נחישות זרחן מיניאטורי

This paper introduces a procedure to investigate the adsorption of phosphonates onto iron-containing filter materials, particularly granular ferric ...

The Plant Infection Test: Spray and Wound-Mediated Inoculation with the Plant Pathogen Magnaporthe Grisea

The Plant Infection Test: Spray and Wound-Mediated Inoculation with the Plant Pathogen Magnaporthe Grisea

הבדיקה זיהום צמח: ריסוס, בתיווך הפצע חיסון עם הפתוגן של צמח Magnaporthe Grisea

Plants possess a powerful system to defend themselves against potential threats by pathogenic fungi. For agriculturally important plants, however, current ...

Sampling Soils in a Heterogeneous Research Plot

קרקעות הדגימה במחקר הטרוגנית מגרש

Soils are highly heterogeneous. In general, the number of soil samples required for soil research has always been determined arbitrarily and the ...

Combined Size and Density Fractionation of Soils for Investigations of Organo-Mineral Interactions

גודל משולב של צפיפות Fractionation של קרקעות החקירות של האינטראקציות אורגניות-מינרליים

Combined size and density fractionation (CSDF) is a method used to physically separate soil into fractions differing in particle size and mineralogy. CSDF ...