Name: a bending test for determining the atterberg plastic limit in soils
Uploaded: 2016-06-28T15:00:00
Description: Watch this Scientific Journal Video about A Bending Test for Determining the Atterberg Plastic Limit in Soils at JoVE.com

This research has been partially funded by a grant (Beca de Investigaci&#242;n Ambiental) from the Servicio de Medio Ambiente de la Diputaci&#242;n Provincial de Toledo (gran number 133/10) and the research project PEII-2014-025-P of the Junta de Comunidades de Castilla-La Mancha.

1. Recoger, seca y tamiza la muestra de prueba <ol><li> Se recoge una muestra de suelo en el campo (use una pala o una paleta) y almacenarlo en una bolsa de polietileno. Nota: El volumen de la muestra varía en función del tipo de suelo: en suelos finos (arcillas y limos) entre 100 y 1.000 g es generalmente suficiente, pero en suelos arenosos y los que contienen grava y guijarros, se pueden requerir grandes cantidades, desde unos pocos a varios kg. </li><li> Reducir la muestra por cuarteo en el laboratorio si ...

<ol>
	<li>Atterberg, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=&#220;ber+die+physikalische+Bodenuntersuchung+und+&#252;ber+die+Plastizit&#228;t+der+Tone.">&#220;ber die physikalische Bodenuntersuchung und &#252;ber die Plastizit&#228;t der Tone.</a> Internationale Mitteilungen f&#252;r Bodenkunde. 1, 10-43 (1911).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> ASTM Standard ASTM D 4318. Standard Test Methods for Liquid Limit, Plastic Limit, and Plasticity Index of Soils. , (2005).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> UNE 103-103-94. Determinaci&#242;n del l&#236;mite l&#236;quido de un suelo por el m&#233;todo del aparato de Casagrande. , (1994).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> BS 1377-2. Methods of test for soils for civil engineering purposes-Part 2: Classification tests. , (1990).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> UNE 103-104-93. Determinaci&#242;n del l&#236;mite pl&#225;stico de un suelo. , (1993).</li><li>Whyte, I. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Soil+plasticity+and+strength:+a+new+approach+using+extrusion.">Soil plasticity and strength: a new approach using extrusion.</a> Ground Eng. 15 (1), 16-24 (1982).</li><li>Temyingyong, A., Chantawaragul, K., Sudasna-na-Ayudthya, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Statistical+Analysis+of+Influenced+Factors+Affecting+the+Plastic+Limit+of+Soils.">Statistical Analysis of Influenced Factors Affecting the Plastic Limit of Soils.</a> Kasetsart J. (Nat. Sci.). 36, 98-102 (2002).</li><li>Bobrowski, L. J., Griekspoor, D. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Determination+of+the+Plastic+Limit+of+a+Soil+by+Means+of+a+Rolling+Device.">Determination of the Plastic Limit of a Soil by Means of a Rolling Device.</a> Geotech. Test. J., GTJODJ. 15 (3), 284-287 (1992).</li><li>Rashid, A. S. A., Kassim, K. A., Katimon, A., Noor, N. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Determination+of+Plastic+Limit+of+soil+using+modified+methods.">Determination of Plastic Limit of soil using modified methods.</a> MJCE. 20 (2), 295-305 (2008).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> ASTM Standard ASTM D 248. Standard Practice for Classification of Soils for Engineering Purposes (Unified Soil Classification System). , (2000).</li><li>Casagrande, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Research+on+the+Atterberg+limits+of+soils.">Research on the Atterberg limits of soils.</a> Public Roads. 13 (8), 121-136 (1932).</li><li>Casagrande, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Classification+and+Identification+of+Soils.">Classification and Identification of Soils.</a> Transactions, ASCE. 113, 901-991 (1948).</li><li>Sokurov, V. V., Ermolaeva, N., Matroshilina, T. V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plastic+limit+of+clayey+soils+and+its+subjetive+determination.">Plastic limit of clayey soils and its subjetive determination.</a> Soil Mech. Found. Eng. 48 (2), 52-57 (2011).</li><li>Andrade, F. A., Al-Qureshi, H. A., Hotza, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measuring+the+plasticity+of+clays:+A+review.">Measuring the plasticity of clays: A review.</a> Appl. Clay Sci. 51, 1-7 (2011).</li><li>Harison, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Using+the+BS+cone+penetrometer+for+the+determination+of+the+plastic+limits+of+soils.">Using the BS cone penetrometer for the determination of the plastic limits of soils.</a> G&#233;otechnique. 38 (3), 433-438 (1988).</li><li>Feng, T. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fall-cone+penetration+and+water+content+relationship+of+clays.">Fall-cone penetration and water content relationship of clays.</a> G&#233;otechnique. 50 (2), 181-187 (2000).</li><li>Feng, T. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Using+a+small+ring+and+a+fall-cone+to+determinate+the+plastic+limit.">Using a small ring and a fall-cone to determinate the plastic limit.</a> ASCE, J. Geotech. Geoenviron. Eng. 130 (6), 630-635 (2004).</li><li>Lee, L. T., Freeman, R. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dual-weight+fall+cone+method+for+simultaneous+liquid+and+plastic+determination.">Dual-weight fall cone method for simultaneous liquid and plastic determination.</a> ASCE, J. Geotech. Geoenviron. Eng. 135 (1), 158-161 (2009).</li><li>Sivakumar, V., Glynn, D., Cairns, P., Black, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+new+method+of+measuring+plastic+limit+of+fine+materials.">A new method of measuring plastic limit of fine materials.</a> G&#233;otechnique. 59 (10), 813-823 (2009).</li><li>Sivakumar, V., O'Kelly, B. C., Henderson, L., Moorhead, C., Chow, S. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Measuring+the+plastic+limit+of+fine+soils:+an+experimental+study.">Measuring the plastic limit of fine soils: an experimental study.</a> P. I. Civil Eng. - Geotec. 168 (GE-1), 53-64 (2015).</li><li>Wroth, C. P., Wood, D. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+correlation+of+index+properties+with+some+basic+engineering+properties+of+soils.">The correlation of index properties with some basic engineering properties of soils.</a> Can. Geotech. J. 15 (2), 137-145 (1978).</li><li>Haigh, S. K., Vardanega, P. J., Bolton, M. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+plastic+limit+of+clays.">The plastic limit of clays.</a> G&#233;otechnique. 63 (6), 435-440 (2013).</li><li>Barnes, G. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+apparatus+for+the+plastic+limit+and+workability+of+soils.">An apparatus for the plastic limit and workability of soils.</a> P. I. Civil Eng. - Geotec. 162 (3), 175-185 (2009).</li><li>Barnes, G. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+apparatus+for+the+determination+of+the+workability+and+plastic+limit+of+clays.">An apparatus for the determination of the workability and plastic limit of clays.</a> Appl. Clay Sci. 80-81, 281-290 (2013).</li><li>Moreno-Maroto, J. M., Alonso-Azc&#225;rate, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+accurate,+quick+and+simple+method+to+determine+the+plastic+limit+and+consistency+changes+in+all+types+of+clay+and+soil:+The+thread+bending+test.">An accurate, quick and simple method to determine the plastic limit and consistency changes in all types of clay and soil: The thread bending test.</a> Appl. Clay Sci. 114, 497-508 (2015).</li><li>Bain, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+plasticity+chart+as+an+aid+to+the+identification+and+assessment+of+industrial+clays.">A plasticity chart as an aid to the identification and assessment of industrial clays.</a> Clay Miner. 9 (1), 1-17 (1971).</li></ol>

El límite plástico Atterberg 1 es un parámetro muy importante en los suelos, principalmente debido a que se utiliza ampliamente para fines geotécnicos 10,11,12. La prueba de laminado de roscas estándar para la determinación PL ha sido ampliamente criticado porque depende de la habilidad y el juicio del operador que está llevando a cabo la prueba y por consiguiente nuevos enfoques para obtener el PL se reivindican altamente 6,7,9,13,15- 20, 23-25. Sin embargo, la simplicidad, bajo ...

Límite líquido (LL) y el límite plástico (PL) son los dos más importantes límites de consistencia del suelo de los definidos por Atterberg en 1911 1. LL marca el límite entre los estados líquido y plástico, y PL entre el plástico y los estados semisólidos. LL se obtiene en todo el mundo de acuerdo con varios estándares mediante el método de Casagrande 2,3 o el ensayo de penetración 4. Ambos métodos se llevan a cabo mecánicamente por medio de dispositivos; de ese modo, la interferencia mínima del operador está involucrado. En el caso de PL, la denominada &quot;prueba de laminado de roscas&quot; es el método más popular y estandarizado para su determinación 2,5. Esta prueba se basa en el suelo rodando en hilos 3 mm con la mano hasta que el operador considera que el suelo sea desmorona. Por esta razón, ha sido ampliamente criticado debido a que la habilidad y juicio del operador juegan un papel crítico en el resultado de la prueba. prueba de balance estándar es importante afectada por muchos factores no controlados, talestal como se aplica la presión, la geometría de contacto, la fricción, la velocidad de laminado, el tamaño de la muestra y el tipo de suelo 6,7. La Sociedad Americana para Pruebas y Materiales (ASTM) ha desarrollado el estándar ASTM D 4318, que incluye un dispositivo simple con el fin de minimizar la interferencia del operador de 2,8, sin embargo, diferencias significativas se han reportado en algunos suelos cuando se compara la prueba de balance manual de la prueba en contra realizada por el dispositivo ASTM D4318 9. PL es un parámetro muy importante para los propósitos geotécnicos, ya que el índice de plasticidad (PI) se obtiene de ella (PI = LL - PL); PI se utiliza para clasificar el suelo de acuerdo con la carta de plasticidad se muestra en la ASTM D 2487 10, con base en la investigación de Casagrande 11,12. Los errores en el PL afectan negativamente a esta clasificación 13, y por esta razón, se requiere una nueva prueba para la determinación de PL. prueba de Pfefferkorn, penetrome conopruebas Ter, reómetro capilar, reómetro de torsión o de tensión-deformación son algunos ejemplos de métodos alternativos para medir la plasticidad del suelo 14, pero estos no son adecuados para obtener el PL. Con la instancia especial de las pruebas de caída de cono, un gran número de investigadores han tratado de definir una nueva metodología para la determinación PL utilizando diferentes diseños penetrometro 15-20, pero sin llegar a ningún acuerdo real. Por otra parte, todos de la misma se basa en la suposición de que la resistencia al cizallamiento en la PL es 100 veces mayor que en la LL 21, que no es verdad 22. Barnes 23,24 desarrolló un aparato que emula las condiciones de rodadura de cilindros de suelo en un intento de establecer un criterio claro para la determinación PL. Sin embargo, algunas deficiencias se identifican con este enfoque, tal como su complejidad, duración de la prueba y principalmente los medios cuestionables del cálculo de la PL 25. El éxito de la prueba de balance estándarradica en su simplicidad, rendimiento rápido y de bajo costo, por lo que no existe un método alternativo será capaz de reemplazarlo, a menos que cumpla estos tres requisitos y otros, tales como alta precisión y baja interferencia del operador. En un estudio previo de los autores, se propuso un nuevo enfoque PL 25: el hilo original ensayo de flexión (o simplemente ensayo de flexión) permitió la PL que se obtiene a partir de un gráfico en el que se representa la relación entre el contenido de agua y deformaciones de flexión. Los autores obtuvieron y se representan varios puntos experimentales para cada suelo (el protocolo seguido para obtener estos puntos fue la misma que la indicada en el presente documento), de modo que la correlación de los puntos se puede definir de dos maneras sin comprometer en modo alguno la correcta definición de la trayectoria del: como una curva parabólica, llamado la curva de flexión (Figura 1A), y como dos rectas distintas con diferente pendiente, el nombre de la línea dura y plásticoy la línea suave y plástico. La línea de dura de plástico es la más empinada uno, y PL se calculó de la misma como el porcentaje de humedad que corresponde al punto de corte de este con el eje (Figura 1B). En este punto de corte la curvatura producida es cero, lo que está de acuerdo con el concepto de límite plástico, es decir., PL es el contenido de humedad en el que el suelo no es capaz de resistir deformaciones por debajo de este umbral (estado semisólido), pero lo hace oso ellos por encima de ella (estado plástico). Aunque en el estudio original, el PL no podría ser obtenida directamente por la curva de la flexión (esto no se cruza con el eje y), esta línea fue muy útil porque teniendo en cuenta que la curva de flexión y las líneas de intersección siguen caminos muy similares, la flexión ecuación de la curva obtenida a partir de los datos experimentales se utilizó para obtener puntos extra para, en primer lugar, corregir cualquier desviación, y, en segundo lugar, para llevar a cabo la prueba con sólo unos pocos puntos, como se muestra en la Figura 1B. &lt;<html> / P&gt; <img alt="Figura 1" src="/files/ftp_upload/54118/54118fig1.jpg" /> Figura 1. Representación gráfica de los puntos de BW en un terreno probado por la prueba de flexión inicial. (A) La correlación de los puntos se representa como una curva parabólica, llamado la curva de flexión cuya ecuación está incluido. (B) La correlación de los puntos está definida por dos líneas que se cruzan y otros puntos adicionales se añaden (que se calculan a partir de la ecuación de la curva de flexión). valores B se obtienen como B = 52.0-D (donde D es la distancia media medida entre las puntas en el momento de formación de grietas en mm) y la PL se calcula como el contenido de agua correspondiente al punto de corte de la línea de dura de plástico con el eje y. Esta cifra ha sido modificado a partir de Moreno-Maroto y Alonso-Azcárate 25.k &quot;&gt; Haga clic aquí para ver una versión más grande de esta figura. Todos los resultados están en excelente acuerdo con los obtenidos por el método tradicional de laminado de roscas por un operador muy experimentado. Sin embargo, la prueba de flexión original, se mantuvo más lento que la prueba de laminado de roscas estandarizado. En un intento por economizar aún más el tiempo de prueba, una versión de un punto fue presentada. Se basa en el promedio de flexión de la pendiente (m) obtenido en los 24 suelos probados, que era 0,108 (m es la pendiente de la curva de flexión cuando se representa en escala logarítmica doble; aparece m en la ecuación de la curva de flexión en la figura 1A) . Por medio de una ecuación en la que se incluyó este factor, las líneas tanto de la rigidez de plástico y de plástico blando se dibujan de forma gráfica, y por lo tanto se estimó la PL. Estos resultados también fueron altamente correlacionados tanto con el ensayo de flexión de múltiples puntos y la prueba de balance estándar. A pesar de ello de un punto version es incluso más rápido que la prueba tradicional, el cálculo PL era más compleja porque el trazado era necesario. Por esta razón, sobre la base de criterios estadísticos una nueva ecuación para el cálculo PL se ha desarrollado en este estudio, por lo que no se requiere que el trazado y los resultados se puede lograr con un solo punto, mientras que el protocolo experimental es el mismo que la curvatura original de prueba. Esta nueva versión cumple con los requisitos necesarios para reemplazar el método de laminado de roscas obsoleta.

<table border="0" cellpadding="0" cellspacing="0" width="978">
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:244px;">Shovel</td>
			<td style="width:76px;">Any</td>
			<td style="width:117px;">NA</td>
			<td style="width:541px;">It is preferable a round point metal shovel so that it can penetrate easily in the soil.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Trowel</td>
			<td>Any</td>
			<td>NA</td>
			<td>It should be easy to handle both in field and laboratory, so approximately 500 g of soil should be the maximum of soil that could pick up.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Polyethylene bags</td>
			<td>Any</td>
			<td>NA</td>
			<td>The size of the bags depends on the collected soil volume. If we were interested in preserving the natural moisture, use sealing tape to close the bag.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Soil splitter&#160;</td>
			<td>PROETISA</td>
			<td>S0012</td>
			<td>It is not mandatory, because the quartering can be performed with the shovel, but in case of using it: it must be big enough to split several kg of sample in the cases of soils with large amounts of gravel or pebbles.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Oven</td>
			<td>SELECTA</td>
			<td>2001254</td>
			<td>The oven must be able to maintain constant temperature and should have some sort of slot or outlet opening to facilitate the release of water vapor.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Lab trays</td>
			<td>Any</td>
			<td>NA</td>
			<td>Metal trays are preferred over plastic because the first ones tolerate the oven temperatures better than the second ones.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Mortar and pestle</td>
			<td>MECACISA</td>
			<td>V112-02</td>
			<td>A ceramic mortar is valid.&#160; It is recommended to use a rubber covered pestle because if the pestle was of other different materials (like metal or a ceramic), it could break the sand particles.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">0.40 mm sieve (or 0.425 mm sieve)</td>
			<td>FILTRA</td>
			<td>0,400 (or 0,425)</td>
			<td>Make sure that the sieve mesh is in perfect conditions of use (it should not be neither broken or worn).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Brush</td>
			<td>Any</td>
			<td>NA</td>
			<td>It is useful for passing the soil during the sieving.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Wash-bottle</td>
			<td>Any</td>
			<td>NA</td>
			<td>It should have an approximate capacity of one litre and it should be easy to control the amount of water that it releases.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Distilled water</td>
			<td>Any</td>
			<td>NA</td>
			<td>Distilled water can be purchased or obtained by filtering from tap water (in this last case, a filtering system is necessary).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Nonabsorbent smooth glass plate&#160;</td>
			<td>Any</td>
			<td>NA</td>
			<td>The plate should have a minimum area of approximately 30 &#215; 30 cm.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Metal spatula</td>
			<td>Any</td>
			<td>NA</td>
			<td>The metal blade of the spatula must be flexible. Dry it with a paper after water-cleaning to prevent rusting.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Latex gloves</td>
			<td>Any</td>
			<td>NA</td>
			<td>Latex, vinyl, nitrile or other impermeable materials are valid. They should be thin enough to sense the soil with the hands.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Cling film</td>
			<td>Any</td>
			<td>NA</td>
			<td>Normal cling film is valid.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Airtight bags</td>
			<td>Any</td>
			<td>NA</td>
			<td>Remove the air before closing them.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Thread molder</td>
			<td>Any</td>
			<td>NA</td>
			<td>It is a tool designed in this experiment (drawings with dimmensions are included in this paper).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Steel pushers</td>
			<td>Any</td>
			<td>NA</td>
			<td>It is a tool designed in this experiment (drawings with dimmensions are included in this paper).</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Damp cloth</td>
			<td>Any</td>
			<td>NA</td>
			<td>A normal damph cloth is valid.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Roll of paper</td>
			<td>Any</td>
			<td>NA</td>
			<td>Normall rolls of paper used to dry hands are valid.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Caliper</td>
			<td>Any</td>
			<td>NA</td>
			<td>It must have an accuracy of at least 0.1 mm.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Paper and pen</td>
			<td>Any</td>
			<td>NA</td>
			<td>Paper and pen are used to write the results.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Containers with covers</td>
			<td>Any</td>
			<td>NA</td>
			<td>Small cylindrical glass containers are valid. If they do not have covers, watch glasses can be used as covers. Covers are useful to avoid the loss of water during the test and also to prevent the dry soil absorbs moisture from the air after oven drying.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Precision or analytical balance</td>
			<td>BOECO</td>
			<td>BPS 52 PLUS</td>
			<td>It must have an accuracy of at least 0.01 g.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Protective gloves</td>
			<td>Any</td>
			<td>NA</td>
			<td>Protective gloves are used to catch the metal trays from the oven.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Tongs</td>
			<td>Any</td>
			<td>NA</td>
			<td>Tongs are used to catch the hot containers from the oven.</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Desiccator</td>
			<td>MECACISA</td>
			<td>A036-01</td>
			<td>A normal glass desiccator with silica gel is valid to prevent the dry soil absorbs moisture from the air after oven drying.</td>
		</tr>
	</tbody>
</table>

a bending test for determining the atterberg plastic limit in soils

La prueba de laminado de roscas es el método más comúnmente utilizado para determinar el límite plástico (PL) en los suelos. Ha sido ampliamente criticada, debido a que un considerable juicio subjetivo del operador que lleva a cabo la prueba está involucrado durante su funcionamiento, lo que puede afectar significativamente el resultado final. Diferentes métodos alternativos se han propuesto, pero no pueden competir con la prueba de balance estándar en velocidad, simplicidad y costo. En un estudio anterior de los autores, un método simple con un dispositivo simple para determinar el PL se presentó (el &quot;hilo ensayo de flexión&quot; o simplemente &quot;ensayo de flexión&quot;); este método permite la PL que se obtiene con una mínima interferencia del operador. En el presente trabajo se muestra una versión de la prueba de flexión originales. La base experimental es el mismo que la prueba de flexión original: hilos del suelo que son de 3 mm de diámetro y 52 mm de largo se doblan hasta que empiezan a romper, por lo que tanto la bending producida y su contenido de humedad relacionada se determina. Sin embargo, esta nueva versión permite el cálculo de PL a partir de una ecuación, por lo que no es necesario trazar cualquier curva o línea recta para obtener este parámetro y, de hecho, la PL se puede lograr con un solo punto experimental (pero dos puntos experimentales se recomiendan). Los resultados obtenidos PL con esta nueva versión son muy similares a los obtenidos a través de la prueba de flexión original y el ensayo de rodadura estándar por un operador muy experimentado. Sólo en casos particulares de suelos cohesivos de alta plasticidad, existe una mayor diferencia en el resultado. A pesar de esto, el ensayo de flexión funciona muy bien para todo tipo de suelos, tanto en suelos cohesivos plasticidad y muy bajas, donde estos últimos son los más difíciles de prueba por medio del método de laminado de roscas estándar.

La ecuación PL se muestra en el paso 6.1 del protocolo se logró a través de un estudio estadístico de los 24 suelos analizados en un estudio previo de los autores 25 (Tabla 1). El objetivo fue conocer la pendiente más probable flexión (el término m en la ecuación de la curva de flexión, que aparece en la Figura 1A) y el valor promedio de B en la curva de flexión en el que se obtuvo PL según la prueba de flexión original (e...

Watch this Scientific Journal Video about A Bending Test for Determining the Atterberg Plastic Limit in Soils at JoVE.com

A Bending Test for Determining the Atterberg Plastic Limit in Soils

El ensayo normalizado tradicional para la determinación del límite plástico en suelos se realiza a mano, y el resultado varía en función del operador. Un método alternativo basado en las mediciones de flexión se presenta en este estudio. Esto permite que se obtenga el límite de plástico con un criterio claro y objetivo.

Un ensayo de flexión para determinar el límite de Atterberg plástico en Suelos

The thread rolling test is the most commonly used method to determine the plastic limit (PL) in soils. It has been widely criticized, because a ...

The overall goal of this new procedure is to determine the plastic limit in soils by measuring bending deformations. The traditional thread-rolling method is highly influenced by the skill of the laboratory operators, so an alternative approach is presented. This method allows the plastic limit to be obtained with a clear and objective criterion.Therefore the obtained results are highly reliable to classify and identify soils for botanical purposes. The main advantage of this technique is that it is not only quick, simple, and cheap, but also accurate and free of subjective interpretations. Beginning with a fine soil sample, dry it at 60 degrees Celsius or less, as needed.Next, disaggregate the soil manually using a mortar. Preferably, use a rubber-lined pestle to avoid breaking up the sand particles. Then, pass the sample through a 0.4 millimeter sieve and discard the soil collected in the sieve.Now, take about 20 to 40 grams of soil and wet it down on a non-absorbent glass plate. Then, knead the sample with a metal spatula until a homogeneous soil-water mixture is obtained. Wearing latex gloves, roll the mixture into a ball that is between three and five centimeters in diameter.Now, make a second ball with more or less water than the first, so the balls have different moisture content. Both soil balls must not crumble or stick when they are handled. Then, wrap each soil ball with cling film and place them in an airtight bag.Store the bag for 24 hours under hermetic conditions. After the tempering period, wearing latex gloves, flatten the soil ball on a smooth glass plate into a nearly three-millimeter thick patty. Keep the patty's surface covered with cling film to avoid moisture loss.Then, using a thread moulder, get the thickness down to precisely three millimeters. Now, cut the jagged edges of the flattened soil mass with a spatula, and make strips of soil that are at least 52 millimeters long, and three millimeters wide. Next, roll the soil strip with the thread moulder until the square section just becomes round, so it is three millimeters in diameter.If the strip is too dry and crumbly, or too sticky, repeat the test, using soil with more or less water content. Next, place the soil thread next to the front side of the thread moulder, and use the width of the thread moulder to make the cylinder exactly 52 millimeters long. Now, turn the thread moulder upside-down, and put the cylindrical piece in contact with the central part of the soil thread.Put the steel pushers in contact with the center of the soil thread. Then, carefully move the steel pushers towards the tips of the soil thread in a circular path. Repeat this motion, until the point of cracking.If the first crack appears near one of the thread tips, keep bending the other tip until the second crack appears at the opposite end. Now, remove the thread moulder and use a caliber to measure the distance between the central part of each tip to a precision of 0.1 millimeter. Now, put the soil thread into a container of known weight, and cover it to prevent moisture loss.If the bending deformations are so large that even the thread tips come into contact, remove the pushers and thread moulder, and continue bending the soil thread by hand, until the point of cracking. Then measure the distance between the thread tips, and record a negative value. From the excess soil, shape other additional threads, but do not cut their tips.Store these in the same container, and cover it again. Now, make a second soil thread that is 52 millimeters long, like the first. Repeat the bending process on the second soil thread.If the results are similar, do not bend more threads. If they differed, shape and bend at least one more soil thread, until agreeable measurements are obtained. Once a minimum of five grams of threads are obtained, record the weight of the container with the soil threads to a precision of at least 01 grams.Now, repeat the entire process for the second ball of soil. Begin with placing the two containers of soil threads uncovered in an oven at 105 degrees Celsius to dry the soil for at least 18 hours. The next day, put the containers in a desiccator.Once they have cooled to ambient temperatures, record their weights to a precision of at least 01 grams. Then, place the containers back into the same oven for at least six more hours. Again, cool them in a desiccator, and measure their weight.Continue repeating this process until two consecutive weight measurements are completely identical, which is the weight of the soil when dry. Now, for each soil ball, using the known water content, W, and its bending at cracking, B, calculate the plastic limit of each ball. Then, use the average value to characterize the soil.The number, minus 0.108, in the plastic limit equation, corresponds to the average value of ending a slope obtained in a previous study with a multiple inversion in which 24 soils were tested. The number 2.135 refers to the average bending value corresponding to the plastic limit in the bending curve for those 24 soils, in accordance with our original multi-point test. The plastic limits calculated from 30 soils with the described bending test, were compared to the original multi-point bending test, and the standard rolling test.Each test was executed by a highly experienced operator, and the results were very similar. The plastic limit results obtained through the new bending test were highly correlated with the original bending test, and the standard thread-rolling test. Most results were perfectly correlated, even with very low-plasticity soils.After watching this video, you should have a good understanding of how the plastic limit can be obtained instantly and accurately with a simple test in which the operator does not play a critical role in the final outcome. Once mastered, this technique can be done in five to ten minutes. So it can be even faster than the traditional test.In addition to its quick performance, the simplicity, low cost, and accuracy of this test, make it easily affordable for any laboratory. After its development, this technique paved the way for researchers and companies in the field of geotechnics, agriculture, ceramics, and soil science, to obtain more reliable plastic limit results.

Research

Education

JoVE Core

JoVE Journal

Mechanical Engineering

Environment

Unit 1

Bending

SCIENTISTS IN ACTION

Determination of Microbial Extracellular Enzyme Activity in Waters, Soils, and Sediments using High Throughput Microplate Assays

Determinación de la actividad enzimática extracelular microbiana en aguas, suelos y sedimentos de los que utilizan y alto rendimiento de microplacas Ensayos

Much of the nutrient cycling and carbon  processing in natural environments occurs through the activity of extracellular  enzymes released by ...

Investigación

Medio ambiente

Integrated Field Lysimetry and Porewater Sampling for Evaluation of Chemical Mobility in Soils and Established Vegetation

Lysimetry Integrado de campo y toma de muestras de agua intersticial para la Evaluación de la Movilidad de Química en Suelos y Vegetación Establecido

Potentially toxic chemicals are routinely applied to land to meet growing demands on waste management and food production, but the fate of these chemicals ...

Measurement of Greenhouse Gas Flux from Agricultural Soils Using Static Chambers

Medición de Flujo de Gas de efecto invernadero procedentes de los suelos agrícolas Usando cámaras estáticas

Measurement of greenhouse gas (GHG) fluxes between the soil and the atmosphere, in both managed and unmanaged ecosystems, is critical to understanding the ...

Extraction and Analysis of Microbial Phospholipid Fatty Acids in Soils

Extracción y análisis de ácidos grasos de fosfolípidos microbiana en suelos

Phospholipid fatty acids (PLFAs) are key components of microbial cell membranes. The analysis of PLFAs extracted from soils can provide information about ...

Methods of Soil Resampling to Monitor Changes in the Chemical Concentrations of Forest Soils

Los métodos de remuestreo del suelo para controlar los cambios en las concentraciones químicas de los suelos forestales

Recent soils research has shown that important chemical soil characteristics can change in less than a decade, often the result of broad environmental ...

Extraction of Organochlorine Pesticides from Plastic Pellets and Plastic Type Analysis

Extracción de plaguicidas organoclorados de pellets de plástico y análisis de tipos de plástico

Plastic resin pellets, categorized as microplastics (&#8804;5 mm in diameter), are small granules that can be unintentionally released to the environment ...

Optimized Procedure for Determining the Adsorption of Phosphonates onto Granular Ferric Hydroxide using a Miniaturized Phosphorus Determination Method

Procedimiento optimizado para la determinación de la adsorción de los fosfonatos en hidróxido férrico Granular utilizando un método de determinación de fósforo miniaturizados

This paper introduces a procedure to investigate the adsorption of phosphonates onto iron-containing filter materials, particularly granular ferric ...

The Plant Infection Test: Spray and Wound-Mediated Inoculation with the Plant Pathogen Magnaporthe Grisea

The Plant Infection Test: Spray and Wound-Mediated Inoculation with the Plant Pathogen Magnaporthe Grisea

La prueba de infección de planta: Spray y mediada por la herida la inoculación con el patógeno de planta Magnaporthe Grisea

Plants possess a powerful system to defend themselves against potential threats by pathogenic fungi. For agriculturally important plants, however, current ...

Sampling Soils in a Heterogeneous Research Plot

Parcela de muestreo de suelos en una investigación heterogéneo

Soils are highly heterogeneous. In general, the number of soil samples required for soil research has always been determined arbitrarily and the ...

Combined Size and Density Fractionation of Soils for Investigations of Organo-Mineral Interactions

Tamaño combinado y fraccionamiento de densidad de los suelos para las investigaciones de interacciones de abonos minerales

Combined size and density fractionation (CSDF) is a method used to physically separate soil into fractions differing in particle size and mineralogy. CSDF ...