Name: preparation of poly(pentafluorophenyl acrylate) functionalized sio2 beads for protein purification
Uploaded: 2018-11-19T14:00:00
Description: Watch this Scientific Journal Video about Preparation of Polypentafluorophenyl acrylate Functionalized SiO2 Beads for Protein Purification at JoVE.com

This work was supported by Agency for Defense Development (Grant No. UD170039ID).

1. Preparation of Poly(PFPA) Homopolymer
<ol>
	<li>Recrystallization of AIBN
	<ol>
		<li>Combine 5 g of 2,2&#8217;-azobis(2-methylpropionitrile) (AIBN) with 25 mL of methanol in a 250 mL beaker. Immerse the beaker in a 60 &#176;C oil bath, then vigorously stir the mixture with a stir bar until AIBN is fully dissolved.</li>
		<li>Filter the warm solution through filter paper (5-8 &#956;m particle retention) and store the filtrate at 4 &#176;C to allow the crystals to form slowly.</li>
		<li>Collect the recrystallized AI...

<ol>
	<li>Johnsson, B., L&#246;f&#229;s, S., Lindquist, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Immobilization+of+proteins+to+a+carboxymethyldextran-modified+gold+surface+for+biospecific+interaction+analysis+in+surface+plasmon+resonance+sensors.">Immobilization of proteins to a carboxymethyldextran-modified gold surface for biospecific interaction analysis in surface plasmon resonance sensors.</a> Analytical Biochemistry. 198 (2), 268-277 (1991).</li><li>Kurzawa, C., Hengstenberg, A., Schuhmann, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Immobilization+method+for+the+preparation+of+biosensors+based+on+pH+shift-induced+deposition+of+biomolecule-containing+polymer+films.">Immobilization method for the preparation of biosensors based on pH shift-induced deposition of biomolecule-containing polymer films.</a> Analytical Chemistry. 74 (2), 355-361 (2002).</li><li>You, C. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Detection+and+identification+of+proteins+using+nanoparticle-fluorescent+polymer+'chemical+nose'+sensors.">Detection and identification of proteins using nanoparticle-fluorescent polymer 'chemical nose' sensors.</a> Nature Nanotechnology. 2 (5), 318-323 (2007).</li><li>Roberts, M. W., Ongkudon, C. M., Forde, G. M., Danquah, M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Versatility+of+polymethacrylate+monoliths+for+chromatographic+purification+of+biomolecules.">Versatility of polymethacrylate monoliths for chromatographic purification of biomolecules.</a> Journal of Separation Science. 32 (15-16), 2485-2494 (2009).</li><li>Sandison, M. E., Cumming, S. A., Kolch, W., Pitt, A. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=On-chip+immunoprecipitation+for+protein+purification.">On-chip immunoprecipitation for protein purification.</a> Lab on a Chip. 10 (20), 2805-2813 (2010).</li><li>Das, A., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Activated+Ester+Containing+Polymers:+Opportunities+and+Challenges+for+the+Design+of+Functional+Macromolecules.">Activated Ester Containing Polymers: Opportunities and Challenges for the Design of Functional Macromolecules.</a> Chemical Reviews. 116 (3), 1434-1495 (2016).</li><li>Choi, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Functionalization+and+patterning+of+reactive+polymer+brushes+based+on+surface+reversible+addition+and+fragmentation+chain+transfer+polymerization.">Functionalization and patterning of reactive polymer brushes based on surface reversible addition and fragmentation chain transfer polymerization.</a> Journal of Polymer Science Part A: Polymer Chemistry. 50 (19), 4010-4018 (2012).</li><li>Kessler, D., Jochum, F. D., Choi, J., Char, K., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reactive+surface+coatings+based+on+polysilsesquioxanes:+universal+method+toward+light-responsive+surfaces.">Reactive surface coatings based on polysilsesquioxanes: universal method toward light-responsive surfaces.</a> ACS Applied Materials &amp; Interfaces. 3 (2), 124-128 (2011).</li><li>Son, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Penetration+and+exchange+kinetics+of+primary+alkyl+amines+applied+to+reactive+poly(pentafluorophenyl+acrylate)+thin+films.">Penetration and exchange kinetics of primary alkyl amines applied to reactive poly(pentafluorophenyl acrylate) thin films.</a> Polymer Journal. 48 (4), 487-495 (2016).</li><li>Kessler, D., Roth, P. J., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reactive+surface+coatings+based+on+polysilsesquioxanes:+controlled+functionalization+for+specific+protein+immobilization.">Reactive surface coatings based on polysilsesquioxanes: controlled functionalization for specific protein immobilization.</a> Langmuir. 25 (17), 10068-10076 (2009).</li><li>Kessler, D., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reactive+surface+coatings+based+on+polysilsesquioxanes:+defined+adjustment+of+surface+wettability.">Reactive surface coatings based on polysilsesquioxanes: defined adjustment of surface wettability.</a> Langmuir. 25 (24), 14200-14206 (2009).</li><li>Kessler, D., Nilles, K., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Modular+approach+towards+multi-functional+surfaces+with+adjustable+and+dual-responsive+wettability+using+a+hybrid+polymer+toolbox.">Modular approach towards multi-functional surfaces with adjustable and dual-responsive wettability using a hybrid polymer toolbox.</a> Journal of Materials Chemistry. 19 (43), 8184-8189 (2009).</li><li>Eberhardt, M., Mruk, R., Zentel, R., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+pentafluorophenyl(meth)acrylate+polymers:+new+precursor+polymers+for+the+synthesis+of+multifunctional+materials.">Synthesis of pentafluorophenyl(meth)acrylate polymers: new precursor polymers for the synthesis of multifunctional materials.</a> European Polymer Journal. 41 (7), 1569-1575 (2005).</li><li>Jochum, F. D., Forst, F. R., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=PNIPAM+copolymers+containing+light-responsive+chromophores:+a+method+toward+molecular+logic+gates.">PNIPAM copolymers containing light-responsive chromophores: a method toward molecular logic gates.</a> Macromolecular Rapid Communications. 31 (16), 1456-1461 (2010).</li><li>Schattling, P., Pollmann, I., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+CO2-responsive+polymers+by+post-polymerization+modification.">Synthesis of CO2-responsive polymers by post-polymerization modification.</a> Reactive &amp; Functional Polymers. 75, 16-21 (2014).</li><li>He, L., Szameit, K., Zhao, H., Hahn, U., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Postpolymerization+modification+using+less+cytotoxic+activated+ester+polymers+for+the+synthesis+of+biological+active+polymers.">Postpolymerization modification using less cytotoxic activated ester polymers for the synthesis of biological active polymers.</a> Biomacromolecules. 15 (8), 3197-3205 (2014).</li><li>Arnold, R. M., McNitt, C. D., Popik, V. V., Locklin, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Direct+grafting+of+poly(pentafluorophenyl+acrylate)+onto+oxides:+versatile+substrates+for+reactive+microcapillary+printing+and+self-sorting+modification.">Direct grafting of poly(pentafluorophenyl acrylate) onto oxides: versatile substrates for reactive microcapillary printing and self-sorting modification.</a> Chemical Communications. 50 (40), 5307-5309 (2014).</li><li>Son, H., Ku, J., Kim, Y., Li, S., Char, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Amine-Reactive+Poly(pentafluorophenyl+acrylate)+Brush+Platforms+for+Cleaner+Protein+Purification.">Amine-Reactive Poly(pentafluorophenyl acrylate) Brush Platforms for Cleaner Protein Purification.</a> Biomacromolecules. 19 (3), 951-961 (2018).</li><li>Cullen, S. E., Schwartz, B. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+improved+method+for+isolation+of+H-2+and+Ia+alloantigens+with+immunoprecipitation+induced+by+protein+A-bearing+staphylococci.">An improved method for isolation of H-2 and Ia alloantigens with immunoprecipitation induced by protein A-bearing staphylococci.</a> The Journal of Immunology. 117 (1), 136-142 (1976).</li><li>Sisson, T. H., Castor, C. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+improved+method+for+immobilizing+IgG+antibodies+on+protein+A-agarose.">An improved method for immobilizing IgG antibodies on protein A-agarose.</a> Journal of Immunology Methods. 127 (2), 215-220 (1990).</li><li>Peritz, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Immunoprecipitation+of+mRNA-protein+complexes.">Immunoprecipitation of mRNA-protein complexes.</a> Nature Protocols. 1 (2), 577-580 (2006).</li><li>Zhang, Z., Chen, S., Jiang, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dual-functional+biomimetic+materials:+nonfouling+poly+(carboxybetaine)+with+active+functional+groups+for+protein+immobilization.">Dual-functional biomimetic materials: nonfouling poly (carboxybetaine) with active functional groups for protein immobilization.</a> Biomacromolecules. 7 (12), 3311-3315 (2006).</li><li>Yao, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=NHS-ester+functionalized+poly(PEGMA)+brushes+on+silicon+surface+for+covalent+protein+immobilization.">NHS-ester functionalized poly(PEGMA) brushes on silicon surface for covalent protein immobilization.</a> Colloids and Surfaces B: Biointerfaces. 66 (2), 233-239 (2008).</li><li>Ma, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+fabrication+of+microsphere-polymer+brush+hierarchically+three-dimensional+(3D)+substrates+for+immunoassays.">Facile fabrication of microsphere-polymer brush hierarchically three-dimensional (3D) substrates for immunoassays.</a> Chemical Communications. 51 (31), 6749-6752 (2015).</li><li>Chong, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thiocarbonylthio+compounds+[SC+(Ph)+S&#8722;+R]+in+free+radical+polymerization+with+reversible+addition-fragmentation+chain+transfer+(RAFT+Polymerization).+Role+of+the+free-radical+leaving+group+(R).">Thiocarbonylthio compounds [SC (Ph) S&#8722; R] in free radical polymerization with reversible addition-fragmentation chain transfer (RAFT Polymerization). Role of the free-radical leaving group (R).</a> Macromolecules. 36 (7), 2256-2272 (2003).</li><li>Jochum, F. D., Theato, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Temperature-+and+Light-Responsive+Polyacrylamides+Prepared+by+a+Double+Polymer+Analogous+Reaction+of+Activated+Ester+Polymers.">Temperature- and Light-Responsive Polyacrylamides Prepared by a Double Polymer Analogous Reaction of Activated Ester Polymers.</a> Macromolecules. 42 (16), 5941-5945 (2009).</li><li>JoVE Science Education Database. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Basic+Methods+in+Cellular+and+Molecular+Biology.+The+Western+Blot.">Basic Methods in Cellular and Molecular Biology. The Western Blot.</a> JoVE. , (2018).</li><li>Chua, G. B. H., Roth, P. J., Duong, H. T. T., Davis, T. P., Lowe, A. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+Thermoresponsive+Solution+Properties+of+Poly[oligo(ethylene+glycol)+(meth)acrylamide]s:+Biocompatible+PEG+Analogues.">Synthesis and Thermoresponsive Solution Properties of Poly[oligo(ethylene glycol) (meth)acrylamide]s: Biocompatible PEG Analogues.</a> Macromolecules. 45 (3), 1362-1374 (2012).</li></ol>

The synthesis of poly(PFPA) grafted SiO2 beads is illustrated in Figure 1. By employing APTMS as a linker molecule, poly(PFPA) brushes covalently grafted to SiO2 substrate can be prepared via a simple two-step process. Although some of the PFP units are sacrificed for the reaction with APTMS, a large number of the PFP units are expected to remain available for later reaction with either amino-PEG or antibodies. The PFP groups are known to form low energy surfaces so pol...

Reactive polymer brushes have received much interest in recent years. They can be used to immobilize functional molecules on organic or inorganic materials to create activated surfaces with applications in areas such as detection and separation1,2,3,4,5. Among the reactive polymers reported, those containing pentafluorophenyl ester units are particularly useful due to their high reactivity with amines and resistance toward hydrolysis6. One such polymer is poly(PFPA), and it can be readily functionalized post-polymerization with molecules containing primary or secondary amines7,8,9,10. In one example, poly(PFPA) brushes were reacted with amino-spiropyrans to create light-responsive surfaces7.
The preparation of poly(PFPA) and its applications have been described in a number of previous publications6,7,8,9,10,11,12,13,14,15,16,17. In particular, Theato and co-workers reported the synthesis of poly(PFPA) brushes via both &#34;grafting to&#34; and &#34;grafting from&#34; methods7,8,10,11,12. In the &#34;grafting to&#34; approach, a poly(methylsilsesquioxane)-poly(pentafluorophenyl acrylate) (poly(MSSQ-PFPA)) hybrid polymer was synthesized8,10,11,12. The poly(MSSQ) component was able to form strong adhesion with a number of different organic and inorganic surfaces, thus allowing the poly(PFPA) component to form a brush layer on the coated material surface. In the &#34;grafting from&#34; approach, surface initiated reversible addition and fragmentation chain transfer (SI-RAFT) polymerization was employed to prepare poly(PFPA) brushes7. In this case, a surface immobilized chain transfer agent (SI-CTA) was first covalently attached to the substrate via silica-silane reaction. The immobilized SI-CTA then participated in the SI-RAFT polymerization of PFPA monomers, generating densely packed poly(PFPA) brushes with stable covalent linkage to the substrate.
By utilizing the poly(PFPA) brushes synthesized via SI-RAFT polymerization, we recently demonstrated the immobilization of antibodies on poly(PFPA) grafted silica particles and their subsequent application in protein purification18. The use of poly(PFPA) brushes for antibody immobilization was found to resolve a number of issues associated with current protein separation through IP. Conventional IP relies on the use of Protein A/G as a linker for antibody immobilization19,20,21. Since the use of Protein A/G allows the antibodies to be attached with a specific orientation, high target antigen recovery efficiency is achieved. However, the use of Protein A/G suffers from non-specific protein interaction as well as the loss of antibodies during protein recovery, both of which contribute to a high level of background noise. To resolve these shortcomings, direct crosslinking of the antibodies to a solid support has been explored22,23,24. The efficiency of such techniques is typically low due to the random orientation of the crosslinked antibodies. For the poly(PFPA) grafted substrate, the immobilization of antibodies is permanent, achieved through exchange reaction between PFP units and amine functionalities on antibodies. Although the antibody orientation is still random, the system benefits from having many reactive PFP sites, controllable by the degree of polymerization. Furthermore, we showed that by partial substitution of PFP units with amino-PEG, surface hydrophilicity can be tuned, further improving the protein recovery efficiency of the system18. Overall, the poly(PFPA) grafted silica particles were shown to be an effective alternative to traditional IP with reasonable efficiency as well as much cleaner background.
In this contribution, we report an alternative method to prepare poly(PFPA) grafted surface for antibody immobilization and IP application. In a simple two-step process, as illustrated in Figure 1, an APTMS linker molecule is first deposited onto the silica surface, then the poly(PFPA) polymer is covalently attached to the linker molecule through the reaction between the PFP units on the polymer and the amine functions on APTMS. This preparation method allows for the permanent crosslinking of poly(PFPA) to a substrate surface, but avoids the many complications associated with SI-CTA synthesis and SI-RAFT polymerization of poly(PFPA) brushes. Partial substitution of the PFP units with amino-PEG can still be performed, allowing fine-tuning of the polymer brush surface properties. We show the poly(PFPA) grafted silica beads thus prepared can be immobilized with antibodies and used for protein enrichment via IP. The detailed bead preparation procedure, antibody immobilization, and IP testing are documented in this article, for readers interested in seeking an alternative to conventional Protein A/G based IP.

<table>
	<tbody>
		<tr>
			<td>2,2-Azobisisobutyronitrile, 99%</td>
			<td>Daejung Chemicals</td>
			<td>1102-4405</td>
			<td></td>
		</tr>
		<tr>
			<td>Methyl alcohol for HPLC, 99.9%</td>
			<td>Duksan Pure Chemicals</td>
			<td>d62</td>
			<td></td>
		</tr>
		<tr>
			<td>Phenylmagnesium bromide solution 1.0&#160;M in THF</td>
			<td>Sigma-Aldrich</td>
			<td>331376</td>
			<td></td>
		</tr>
		<tr>
			<td>Carbon disulfide anhydrous, &#8805;99%</td>
			<td>Sigma-Aldrich</td>
			<td>335266</td>
			<td></td>
		</tr>
		<tr>
			<td>Benzyl bromide, 98%</td>
			<td>Sigma-Aldrich</td>
			<td>B17905</td>
			<td></td>
		</tr>
		<tr>
			<td>Petroleum ether, 90%</td>
			<td>Samchun Chemicals</td>
			<td>P0220</td>
			<td></td>
		</tr>
		<tr>
			<td>Ethyl ether, 99%</td>
			<td>Daejung Chemicals</td>
			<td>4025-4404</td>
			<td></td>
		</tr>
		<tr>
			<td>Magnesium sulfate anhydrous, powder,&#160;99%</td>
			<td>Daejung Chemicals</td>
			<td>5514-4405</td>
			<td></td>
		</tr>
		<tr>
			<td>Pentafluorophenyl acrylate</td>
			<td>Santa Cruz Biotechnology</td>
			<td>sc-264001</td>
			<td>contains inhibitor</td>
		</tr>
		<tr>
			<td>Aluminium oxide, activated, basic, Brockmann I</td>
			<td>Sigma-Aldrich</td>
			<td>199443</td>
			<td></td>
		</tr>
		<tr>
			<td>Sodium Chloride (NaCl)</td>
			<td>Daejung Chemicals</td>
			<td>7548-4400</td>
			<td></td>
		</tr>
		<tr>
			<td>Anisole anhydrous, 99.7%</td>
			<td>Sigma-Aldrich</td>
			<td>296295</td>
			<td></td>
		</tr>
		<tr>
			<td>Silica nanoparticle</td>
			<td>Microparticles GmbH</td>
			<td>SiO2-R-0.7</td>
			<td>5% w/v aqueous suspension</td>
		</tr>
		<tr>
			<td>3-Aminopropyltrimethoxysilane, &#62;96.0%</td>
			<td>Tokyo Chemical Industry</td>
			<td>T1255</td>
			<td></td>
		</tr>
		<tr>
			<td>Dimethyl sulfoxide for HPLC, &#8805;99.7%</td>
			<td>Sigma-Aldrich</td>
			<td>34869</td>
			<td></td>
		</tr>
		<tr>
			<td>Amino-terminated poly(ethylene glycol) methyl ether</td>
			<td>Polymer Source</td>
			<td>P16082-EGOCH3NH2</td>
			<td></td>
		</tr>
		<tr>
			<td>Phosphate buffered saline tablet</td>
			<td>Takara</td>
			<td>T9181</td>
			<td></td>
		</tr>
		<tr>
			<td>Tween-20</td>
			<td>Calbiochem</td>
			<td>9480</td>
			<td></td>
		</tr>
		<tr>
			<td>Tris-HCl (pH 8.0)</td>
			<td>Invitrogen</td>
			<td>AM9855G</td>
			<td></td>
		</tr>
		<tr>
			<td>KCl</td>
			<td>Invitrogen</td>
			<td>AM9640G</td>
			<td></td>
		</tr>
		<tr>
			<td>NP-40</td>
			<td>VWR</td>
			<td>E109-50ML</td>
			<td></td>
		</tr>
		<tr>
			<td>Glycerol</td>
			<td>Invitrogen</td>
			<td>15514-011</td>
			<td></td>
		</tr>
		<tr>
			<td>Dithiothreitol</td>
			<td>Biosesang</td>
			<td>D1037</td>
			<td></td>
		</tr>
		<tr>
			<td>Protease inhibitor</td>
			<td>Merck</td>
			<td>535140-1MLCN</td>
			<td></td>
		</tr>
		<tr>
			<td>Bromo phenol blue</td>
			<td>Sigma-Aldrich</td>
			<td>B5525-5G</td>
			<td></td>
		</tr>
		<tr>
			<td>Tris-HCl (pH 6.8)</td>
			<td>Biosolution</td>
			<td>BT033</td>
			<td></td>
		</tr>
		<tr>
			<td>Sodium dodecyl sulfate</td>
			<td>Biosolution</td>
			<td>BS003</td>
			<td></td>
		</tr>
		<tr>
			<td>2-Mercaptoethanol</td>
			<td>Gibco</td>
			<td>21985-023</td>
			<td></td>
		</tr>
		<tr>
			<td>PKR Antibody</td>
			<td>Cell Signaling Technology</td>
			<td>12297S</td>
			<td></td>
		</tr>
		<tr>
			<td>GAPDH Antibody</td>
			<td>Santa Cruz Biotechnology</td>
			<td>sc-32233</td>
			<td></td>
		</tr>
		<tr>
			<td>Normal Rabbit IgG</td>
			<td>Cell Signaling Technology</td>
			<td>2729S</td>
			<td></td>
		</tr>
		<tr>
			<td>HeLa</td>
			<td>Korea Cell Line Bank</td>
			<td>10002</td>
			<td></td>
		</tr>
		<tr>
			<td>Sonicator</td>
			<td>DAIHAN Scientific</td>
			<td>WUC-D10H</td>
			<td></td>
		</tr>
		<tr>
			<td>Ultrasonicator</td>
			<td>BMBio</td>
			<td>BR2006A</td>
			<td></td>
		</tr>
		<tr>
			<td>Centrifuge I</td>
			<td>Eppendorf</td>
			<td>5424 R</td>
			<td></td>
		</tr>
		<tr>
			<td>Centrifuge II</td>
			<td>LABOGENE</td>
			<td>1736R</td>
			<td></td>
		</tr>
		<tr>
			<td>Rotator</td>
			<td>FINEPCR</td>
			<td>ROTATOR/AG</td>
			<td></td>
		</tr>
		<tr>
			<td>Vacuum oven</td>
			<td>DAIHAN Scientific</td>
			<td>ThermoStable OV-30</td>
			<td></td>
		</tr>
		<tr>
			<td>Gel permeation chromatography (THF)</td>
			<td>Agilent Technologies</td>
			<td>1260 Infinity II</td>
			<td></td>
		</tr>
		<tr>
			<td>X-ray photoelectron spectrometer</td>
			<td>Thermo VG Scientific</td>
			<td>Sigma Probe</td>
			<td></td>
		</tr>
		<tr>
			<td>Dynamic light scattering</td>
			<td>Malvern Instruments</td>
			<td>ZEN 3690</td>
			<td></td>
		</tr>
	</tbody>
</table>

preparation of poly(pentafluorophenyl acrylate) functionalized sio2 beads for protein purification

We demonstrate a simple method to prepare poly(pentafluorophenyl acrylate) (poly(PFPA)) grafted silica beads for antibody immobilization and subsequent immunoprecipitation (IP) application. The poly(PFPA) grafted surface is prepared via a simple two-step process. In the first step, 3-aminopropyltrimethoxysilane (APTMS) is deposited as a linker molecule onto the silica surface. In the second step, poly(PFPA) homopolymer, synthesized via the reversible addition and fragmentation chain transfer (RAFT) polymerization, is grafted to the linker molecule through the exchange reaction between the pentafluorophenyl (PFP) units on the polymer and the amine groups on APTMS. The deposition of APTMS and poly(PFPA) on the silica particles are confirmed by X-ray photoelectron spectroscopy (XPS), as well as monitored by the particle size change measured via dynamic light scattering (DLS). To improve the surface hydrophilicity of the beads, partial substitution of poly(PFPA) with amine-functionalized poly(ethylene glycol) (amino-PEG) is also performed. The PEG-substituted poly(PFPA) grafted silica beads are then immobilized with antibodies for IP application. For demonstration, an antibody against protein kinase RNA-activated (PKR) is employed, and IP efficiency is determined by Western blotting. The analysis results show that the antibody immobilized beads can indeed be used to enrich PKR while non-specific protein interactions are minimal.

A schematic for the preparation of poly(PFPA) grafted SiO2 beads, with or without PEG substitution is shown in Figure 1. To monitor the APTMS and poly(PFPA) grafting process, bare SiO2 beads, APTMS functionalized SiO2 beads, and poly(PFPA) grafted SiO2 beads are characterized by both DLS (Figure 2) and XPS (Figure 3). IP efficiencies of the beads are determ...

Watch this Scientific Journal Video about Preparation of Polypentafluorophenyl acrylate Functionalized SiO2 Beads for Protein Purification at JoVE.com

Preparation of Polypentafluorophenyl acrylate Functionalized SiO2 Beads for Protein Purification

A protocol for the preparation of poly(pentafluorophenyl acrylate) (poly(PFPA)) grafted silica beads is presented. The poly(PFPA) functionalized surface is then immobilized with antibodies and used successfully for the protein separation through immunoprecipitation.

Preparation of Poly(pentafluorophenyl acrylate) Functionalized SiO2 Beads for Protein Purification

We demonstrate a simple method to prepare poly(pentafluorophenyl acrylate) (poly(PFPA)) grafted silica beads for antibody immobilization and subsequent ...

Research

JoVE Journal

Chemistry

Synthesis and Characterization of Functionalized Metal-organic Frameworks

功能化的合成与表征金属 - 有机骨架

Metal-organic frameworks have attracted extraordinary amounts of research attention, as they are attractive candidates for numerous industrial and ...

科研

化学

Microbubble Fabrication of Concave-porosity PDMS Beads

的凹孔隙PDMS珠微泡制作

Microbubble fabrication (by use of a fine emulsion) provides a means of increasing the surface-area-to-volume (SAV) ratio of polymer materials, which is ...

Immobilization of Multi-biocatalysts in Alginate Beads for Cofactor Regeneration and Improved Reusability

藻酸盐珠多生物催化剂辅因子再生和可重用性改进的固定化

We have recently developed a simple, reusable and coupled whole-cell biocatalytic system with the capability of cofactor regeneration and biocatalyst ...

Preparation of a Corannulene-functionalized Hexahelicene by Copper(I)-catalyzed Alkyne-azide Cycloaddition of Nonplanar Polyaromatic Units

Preparation of a Corannulene-functionalized Hexahelicene by CopperI-catalyzed Alkyne-azide Cycloaddition of Nonplanar Polyaromatic Units

一个碗烯官能Hexahelicene的铜（Ⅰ）制备催化的非平面多环芳烃单位炔叠氮化物环加成

The main purpose of this video is to show 6 reaction steps of a convergent synthesis and prepare a complex molecule containing up to three nonplanar ...

The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance

The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance

界面化学键合在TiO中的作用<sub&gt; 2</sub&gt; -SiO<sub&gt; 2</sub&gt;复合材料对其光催化NOx消除性能的影响

The chemical bonding of particulate photocatalysts to supporting material surfaces is of great importance in engineering more efficient and practical ...

Methionine Functionalized Biocompatible Block Copolymers for Targeted Plasmid DNA Delivery

用于靶向质粒DNA输送的美聚氨酸功能化生物相容性块共聚物

Reversible addition-fragmentation chain transfer (RAFT) polymerization integrates the advantages of radical polymerization and living polymerization. This ...

Efficient Synthesis of All-Carbon Quaternary Centers via the Conjugate Addition of Functionalized Monoorganozinc Bromides

功能化单有机硼化合物共轭法高效合成全碳第四纪中心

The conjugate addition of organometallic reagents to &#945;,&#946;-unsaturated carbonyls represents an important method to generate C&#8211;C bonds in the ...

Organic Solvent-Based Protein Precipitation for Robust Proteome Purification Ahead of Mass Spectrometry

有机溶剂基蛋白质沉淀，在质谱分析之前实现强大的蛋白质组纯化

While multiple advances in mass spectrometry (MS) instruments have improved qualitative and quantitative proteome analysis, more reliable front-end ...

Porphyrin-Modified Beads in Flow Cytometry

Porphyrin-Modified Beads for Use as Compensation Controls in Flow Cytometry

Porphyrin-Modified Beads for Use as Compensation Controls in Flow Cytometry (Video) | JoVE 

卟啉修饰微球用作流式细胞术补偿质控

Flow cytometry can rapidly characterize and quantify diverse cell populations based on fluorescence measurements. The cells are first stained with one or ...