Name: synthesis of graphene nanofluids with controllable flake size distributions
Uploaded: 2019-07-17T13:00:00
Description: Watch this Scientific Journal Video about Synthesis of Graphene Nanofluids with Controllable Flake Size Distributions at JoVE.com

Dette arbejde blev støttet af national Nature Science Foundation i Kina (Grant No. 21776095), Guangzhou videnskab og teknologi Key program (Grant No. 201804020048), og Guangdong Key Laboratory af Clean Energy Technology (Grant No. 2008A060301002). Vi takker LetPub (www.letpub.com) for sin sproglige bistand under forberedelsen af dette manuskript.

1. eksfoliering af grafit i en flydende fase
<ol><li>Klargøring af reagenser<ol>
<li>I en tør, ren flad bund kolbe tilsættes 20 g polyvinylchlorid alkohol (PVA), hvorefter der tilsættes 1.000 mL destilleret vand. Bemærk: hvis suspensionen ikke blev behandlet tilfredsstillende, kunne trinnet gentages for at opnå en yderligere suspension.</li>
		<li>Stryg forsigtigt kolben, indtil PVA opløses helt. Forsigtig: PVA er skadeligt for mennesker; således bør beskyttende handsker og kirurgiske masker anvendes.</l...

<ol>
	<li>Sadeghinezhad, E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+comprehensive+review+on+graphene+nanofluids:+Recent+research,+development+and+applications.">A comprehensive review on graphene nanofluids: Recent research, development and applications.</a> Energy Conversion and Management. 111, 466-487 (2016).</li><li>Wang, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+Efficient+Production+of+Graphene+by+an+Ultrasound+Coupled+with+a+Shear+Mixer+in+Supercritical+CO2.">Highly Efficient Production of Graphene by an Ultrasound Coupled with a Shear Mixer in Supercritical CO2.</a> Industrial &amp; Engineering Chemistry Research. 57 (49), 16701-16708 (2018).</li><li>Cao, H. Y., Guo, Z. X., Xiang, H., Gong, X. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Layer+and+size+dependence+of+thermal+conductivity+in+multilayer+graphene+nanoribbons.">Layer and size dependence of thermal conductivity in multilayer graphene nanoribbons.</a> Physics Letters A. 376 (4), 525-528 (2012).</li><li>Yang, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+and+adjustment+of+the+graphene+work+function+via+size,+modification,+defects,+and+doping:+a+first-principle+theory+study.">Design and adjustment of the graphene work function via size, modification, defects, and doping: a first-principle theory study.</a> Nanoscale Research Letters. 12, (2017).</li><li>Khan, U., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+selection+of+dispersed,+exfoliated+graphene+flakes+by+controlled+centrifugation.">Size selection of dispersed, exfoliated graphene flakes by controlled centrifugation.</a> Carbon. 50 (2), 470-475 (2012).</li><li>Smith, R. J., King, P. J., Wirtz, C., Duesberg, G. S., Coleman, J. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lateral+size+selection+of+surfactant-stabilised+graphene+flakes+using+size+exclusion+chromatography.">Lateral size selection of surfactant-stabilised graphene flakes using size exclusion chromatography.</a> Chemical Physics Letters. 531, 169-172 (2012).</li><li>Galvin, K. P., Pratten, S. J., Nicol, S. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dense+medium+separation+using+a+teetered+bed+separator.">Dense medium separation using a teetered bed separator.</a> Minerals Engineering. 12 (9), 1059-1081 (1999).</li><li>Cai, C. J., Sang, N. N., Shen, Z. G., Zhao, X. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+and+size-controllable+preparation+of+graphene+oxide+nanosheets+using+high+shear+method+and+ultrasonic+method.">Facile and size-controllable preparation of graphene oxide nanosheets using high shear method and ultrasonic method.</a> Journal of Experimental Nanoscience. 12 (1), 247-262 (2017).</li><li>Chen, L. X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Oriented+graphene+nanoribbons+embedded+in+hexagonal+boron+nitride+trenches.">Oriented graphene nanoribbons embedded in hexagonal boron nitride trenches.</a> Nature Communications. 8, (2017).</li><li>Fan, T. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controllable+size-selective+method+to+prepare+graphene+quantum+dots+from+graphene+oxide.">Controllable size-selective method to prepare graphene quantum dots from graphene oxide.</a> Nanoscale Research Letters. 10, 1-8 (2015).</li><li>Oikonomou, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scalable+bottom-up+assembly+of+suspended+carbon+nanotube+and+graphene+devices+by+dielectrophoresis.">Scalable bottom-up assembly of suspended carbon nanotube and graphene devices by dielectrophoresis.</a> Physica Status Solidi-Rapid Research Letters. 9 (9), 539-543 (2015).</li><li>Liu, Y., Zhang, D., Pang, S. W., Liu, Y. Y., Shang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+separation+of+graphene+oxide+using+preparative+free-flow+electrophoresis.">Size separation of graphene oxide using preparative free-flow electrophoresis.</a> Journal of Separation Science. 38 (1), 157-163 (2015).</li><li>Cui, C. N., Huang, J. T., Huang, J. H., Chen, G. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+separation+of+mechanically+exfoliated+graphene+sheets+by+electrophoresis.">Size separation of mechanically exfoliated graphene sheets by electrophoresis.</a> Electrochimica Acta. 258, 793-799 (2017).</li><li>Sun, Z. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-yield+exfoliation+of+graphite+in+acrylate+polymers:+A+stable+few-layer+graphene+nanofluid+with+enhanced+thermal+conductivity.">High-yield exfoliation of graphite in acrylate polymers: A stable few-layer graphene nanofluid with enhanced thermal conductivity.</a> Carbon. 64, 288-294 (2013).</li><li>Sun, Z. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Amine-based+solvents+for+exfoliating+graphite+to+graphene+outperform+the+dispersing+capacity+of+N-methyl-pyrrolidone+and+surfactants.">Amine-based solvents for exfoliating graphite to graphene outperform the dispersing capacity of N-methyl-pyrrolidone and surfactants.</a> Chemical Communications. 50 (72), 10382-10385 (2014).</li><li>Du, B. L., Jian, Q. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+controllable+synthesis+of+graphene+water+nanofluid+with+enhanced+stability.">Size controllable synthesis of graphene water nanofluid with enhanced stability.</a> Fullerenes Nanotubes and Carbon Nanostructures. 27 (1), 87-96 (2019).</li><li>Tao, H. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scalable+exfoliation+and+dispersion+of+two-dimensional+materials+-+an+update.">Scalable exfoliation and dispersion of two-dimensional materials - an update.</a> Physical Chemistry Chemical Physics. 19 (2), 921-960 (2017).</li><li>Phiri, J., Gane, P., Maloney, T. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-concentration+shear-exfoliated+colloidal+dispersion+of+surfactant-polymer-stabilized+few-layer+graphene+sheets.">High-concentration shear-exfoliated colloidal dispersion of surfactant-polymer-stabilized few-layer graphene sheets.</a> Journal of Materials Science. 52 (13), 8321-8337 (2017).</li></ol>

Vi har foreslået en metode til syntese af Graphene nanofluider med kontrollerbar flake størrelsesfordelinger. Metoden kombinerer to procedurer: eksfoliering og centrifugering. Eksfoliering kontrollerer nanopartiklenes nedre størrelsesgrænse, og Centrifugerings kontrol styrer nanopartiklenes øvre størrelsesgrænse.
Selv om vi beskæftigede flydende fase eksfoliering af grafit til fremstilling af Graphene nanopartikler, bør følgende ændringer af protokollen overvejes. Yderligere eksfota...

Traditionelle metoder, der anvendes til at syntetisere Graphene nanofluider bruger ofte sonikering til at sprede Graphene pulver1 i væsker, og sonikering har vist sig at ændre størrelsesfordelingen af Graphene nanopartikler2. Da den termiske ledningsevne Graphene afhænger af flake længde3,4, syntesen af Graphene nanofluider med kontrollerbar flake størrelsesfordelinger er afgørende for varmeoverførsel applikationer. Kontrolleret centrifugering er blevet anvendt med succes på flydende eksfolierede Graphene dispersioner for at adskille suspensioner i fraktioner med forskellige gennemsnitlige flake størrelser5,6. Forskellige Terminal hastigheder, der anvendes ved centrifugering, fører til forskellige kritiske partikelstørrelser7. Den terminale hastighed kan anvendes til at eliminere store Graphene nanopartikler8.
For nylig er der indført størrelses kontrollerbare metoder til at syntetisere Graphene via flydende fase eksfoliering for at overvinde de grundlæggende problemer, som konventionelle metoder9,10,11, 12,13. Flydende fase eksfoliering af grafit har vist sig at være en effektiv måde at producere Graphene suspensioner14,15,16, og den underliggende mekanisme viser, at procesparametrene er relateret til nedre grænser for Graphene nanopartikler størrelsesfordelinger. Graphene nanofluider blev syntetiseret af den flydende eksfoliering af grafit ved hjælp af overfladeaktive stoffer17. Mens de nedre grænser for Graphene nanopartikel størrelsesfordeling kunne styres ved at justere parametrene under eksfoliering, mindre opmærksomhed er betalt til de øvre grænser for Graphene nanopartikel størrelsesfordeling.
Målet med dette arbejde er at udvikle en protokol, der kan bruges til at syntetisere Graphene nanofluider med kontrollerbar flake størrelsesfordelinger. Da eksfoliering kun er ansvarlig for den nedre grænse for den resulterende Graphene nanoflakes, introduceres yderligere centrifugering for at kontrollere den øvre størrelsesgrænse for den resulterende Graphene nanoflakes. Den foreslåede metode er imidlertid ikke specifik for Graphene og kan være hensigtsmæssig for andre lagdelte forbindelser, der ikke kan syntetiseres ved hjælp af traditionelle metoder.

<table>
	<tbody>
		<tr>
			<td>Beaker</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>500 mL</td>
			<td></td>
		</tr>
		<tr>
			<td>Beaker</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>5000 mL</td>
			<td></td>
		</tr>
		<tr>
			<td>Deionized water</td>
			<td>Guangzhou Yafei Water Treatment Equipment Co., Ltd.</td>
			<td></td>
			<td>analytical grade</td>
		</tr>
		<tr>
			<td>Electronic balance</td>
			<td>Shanghai Puchun Co., Ltd.</td>
			<td>JEa10001</td>
			<td></td>
		</tr>
		<tr>
			<td>Filter membrane</td>
			<td>China Tianjin Jinteng Experiment Equipments Co., Ltd.</td>
			<td>0.2 micron</td>
			<td></td>
		</tr>
		<tr>
			<td>Graphite powder</td>
			<td>Tianjin Dengke chemical reagent Co., Ltd.</td>
			<td></td>
			<td>analytical grade</td>
		</tr>
		<tr>
			<td>Hand gloves</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Laboratory shear mixer</td>
			<td>Shanghai Specimen and Model Factory</td>
			<td>jrj-300</td>
			<td></td>
		</tr>
		<tr>
			<td>Long neck flat bottom flask</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>1000 ml</td>
			<td></td>
		</tr>
		<tr>
			<td>Nanoparticle analyzer</td>
			<td>HORIBA, Ltd.</td>
			<td>SZ-100Z</td>
			<td></td>
		</tr>
		<tr>
			<td>PVA</td>
			<td>Shanghai Yingjia Industrial Development Co., Ltd.</td>
			<td>1788</td>
			<td>analytical grade</td>
		</tr>
		<tr>
			<td>Raman spectrophotometer</td>
			<td>HORIBA, Ltd.</td>
			<td>Horiba LabRam 2</td>
			<td></td>
		</tr>
		<tr>
			<td>Scanning electron microscope</td>
			<td>Zeiss Co., Ltd.</td>
			<td>LEO1530VP</td>
			<td>SEM</td>
		</tr>
		<tr>
			<td>Surgical mask</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>for one-time use</td>
			<td></td>
		</tr>
		<tr>
			<td>Thermal Gravimetric Analyzer</td>
			<td>German NETZSCH Co., Ltd.</td>
			<td>NETZSCH TG 209 F1 Libra</td>
			<td>TGA analysis</td>
		</tr>
		<tr>
			<td>Transmission electron microscope</td>
			<td>Japan Electron Optics Laboratory Co., Ltd.</td>
			<td>JEM-1400plus</td>
			<td>TEM</td>
		</tr>
		<tr>
			<td>UV-Vis spectrophotometer</td>
			<td>Agilent Technologies, Inc.+BB2:B18</td>
			<td>Varian Cary 60</td>
			<td></td>
		</tr>
	</tbody>
</table>
Try the professional online HTML editor

synthesis of graphene nanofluids with controllable flake size distributions

En metode til syntese Graphene nanofluider med kontrollerbar flake størrelsesfordelinger er præsenteret. Graphene nanoflakes kan opnås ved eksfoliering af grafit i den flydende fase, og eksfoliering tid bruges til at styre de nedre grænser for Graphene nanoflake størrelsesfordelinger. Centrifugering bruges med succes til at styre de øvre grænser for nanoparti størrelsesfordelinger. Formålet med dette arbejde er at kombinere eksfoliering og centrifugering til at kontrollere Graphene nanoflake størrelsesfordelinger i de resulterende suspensioner.

Forekomsten af Graphene nanosheets kan valideres af forskellige karakteristiske teknikker. Figur 1 viser resultaterne af UV-Vis-målingen for de forskellige størrelsesfordelinger af flake, der er fremstillet ved ovennævnte protokol. Spektra absorbans peak opnået ved en bølgelængde på 270 nm er tegn på Graphene flager. Forskellige abscisse svarer til forskellige koncentrationer. Den observerede laveste absorbans svarer til den højeste centrifugeringshastighed. Spektrene bekræfter kra...

Watch this Scientific Journal Video about Synthesis of Graphene Nanofluids with Controllable Flake Size Distributions at JoVE.com

Synthesis of Graphene Nanofluids with Controllable Flake Size Distributions

En metode til syntese Graphene nanofluider med kontrollerbar flake størrelsesfordelinger er præsenteret.

Syntese af Graphene Nanofluids med kontrollerbar flake Størrelsesfordelinger

A method for synthesizing graphene nanofluids with controllable flake size distributions is presented. Graphene nanoflakes can be obtained by the ...

Den foreslåede metode anvender eksfolieringsproces og centrifugeringsproces til at kontrollere de nedre grænser og de øvre grænser for størrelsesfordelinger af grafinatsuspensionen separat. Den største fordel ved den foreslåede metode er, at den endelige størrelsesfordeling kan styres ved at justere procesparametrene for eksfolieringstrinnet og centrifugeringstrinnet. I en tør, ren, flad bundkolbe tilsættes 20 gram PVA, og derefter tilsættes 1000 milliliter destilleret vand.Svir forsigtigt kolben, indtil PVA er helt opløst. Derefter tilsættes 50 gram grafitpulver til den flade bundkolbe, og kolben hvirvles forsigtigt rundt, indtil grafitpulveret er helt spredt i suspensionen. 500 milliliter af den resulterende suspension overføres til et bægerglas med 500 milliliter.Anlækkeren placeres under en forskydningsblander, hvor bægerglasset placeres nær midten af blandebeholderen for at forhindre dannelsen af en vortex. Sænk blandehovedet til sin laveste position, 30 millimeter fra basisplanet. Derefter forberede et vandbad ved at fylde en 5000-milliliter bægerglas med stuetemperatur vand, og placere 500-milliliter bægerglas i badet.Start mixeren, og forøg hastigheden gradvist til 4.500 omdr./min. Bland ved denne hastighed i 120 minutter. Skift vand hvert 30.Udfør dette eksfolieringstrin fem gange mere med forskellig varighed. Blandingstiden bestemmer den lavere laterale størrelsesgrænse for grafennnanofnnerne. Saml de 500 millilitergenererede suspensioner efter hvert eksfolieringstrin.Mærke hver suspension med eksfolationstid, og centrifuge den indsamlede suspension ved 140 gange g i 45 minutter. For at fjerne den uudsolierede grafit, skal du bruge en pipette til at indsamle de øverste 80% af supernatanten fra hvert centrifugerør for yderligere centrifugering. Centrifuge supernatant suspension fra sidste centrifugering trin på 8, 951 gange g i 45 minutter.Den øverste 50% af supernatanten opsamres i centrifugerøret, og afmærkning prøven med et tal. Derefter, at genbruge sedimentet på bunden af centrifugerøret, tilsæt 50 milliliter af den tidligere forberedte PVA vand reagens til sedimentet, og ryst røret kraftigt i hånden, indtil sedimentet er godt dispergeret i suspensionen. Centrifuge suspensionen ved 8, 951 gange g i 45 minutter.Opsaml de øverste 80 % for yderligere målinger. Gentag centrifugeringstrinnet for pellet fire gange mere med fire forskellige centrifugeringshastigheder. Centrifugeringshastigheden bestemmer grafennnanofnnens øvre laterale størrelsesgrænse.Nu forberede ultraviolet synlige spektroskopi. Med den tidligere forberedte PVA-vandopløsning i en tør, ren prøvecelle kalibreres det ultraviolette synlige spektrometer, hvor PVA-vandkoncentrationerne indstilles til 0%Derefter tilsættes PVA-vandrepensionen efter centrifugering til en tør, ren prøvecelle med en stilængde på 10 millimeter, og der skal opnås en udlæsning ved hjælp af producentens software. Klik på knappen Hent for at hente grafen for måleresultater og gemme resultaterne.Dernæst for at bestemme grafen vægt, vakuum filtrere prøve suspensionen ved hjælp af en nylon membran med en pore størrelse på 0,2 mikron. Membranfilmen, og vask med ca. 200 milliliter vand i et bægerglas. Vasken gentages tre gange, indtil alle faste stoffer vaskes væk fra membranen.Bestem den vaskede vandmasse med en højpræcisionsmikrobalance for at opnå vægten af faste stofferne. Igen, vakuum filtrere vand suspensioner ved hjælp af en nylon membran med en pore størrelse på 0,2 mikron. Få membranen, og tør det ved stuetemperatur i over 12 timer.Skyl efterfølgende filmen med 200 milliliter deioniseret vand i et bægerglas. Hvis den ønskede koncentration er mindre end produktionshastigheden med et milligram pr. milliliter, tilsættes den forberedte PVA-vandopløsning for at opnå den ønskede koncentration. Hvis den ønskede koncentration er højere end 1%tør det deioniserede vand under vakuum i tørretumbleren i 24 timer for at opnå grafen nanosheets.I denne protokol viser den ultraviolette synlige måling af de forskellige flagestørrelsesfordelinger den spektraabsorberende toppe, der opnås ved en bølgelængde på 270 nanometer, hvilket indikerer tegn på grafenflager. Suspension med forskellig koncentration har forskellige 660-nanometer absorption. D-båndet og 2D-båndet af Raman-spektroskopien bestemmer flageftykkelsen af grafennnanofnlakes.D-båndet af Raman spektrum, som er relateret til graphene sp3 kulstofatomer, skelner mellem den oprindelige grafit og grafen nanoflakes. Lav D-båndintensitet indikerer de defekte grafennanosheets. Der blev observeret en karakteristisk størrelsesfordeling for den resulterende suspension, der blev fremstillet ved hjælp af forskellige centrifugeringshastigheder.Både transmissionselektrekroskopien og scanningselelektronmikroskopien viser, at grafen blev produceret, og eksfolieringen var vellykket. Centrifugeringstrinnet virkede dog kun på nanopartikler med gennemsnitsdiametre på over 1000 nanometer. Forholdet mellem de øvre grænser for størrelsesfordelinger med centrifugeringshastigheden skal bestemmes på forhånd.Da størrelsen ikke påvirker med den foreslåede metode, varmeoverførsel effektivitet er muligt at blive manipuleret under forhold som nogle tilslutningsmuligheder, konvektion, og overføre applikationer i centrum. PVA-polymeren er skadelig for mennesker. Der skal anvendes ansigtsmaske og handsker til at beskytte operatøren.

Research

JoVE Journal

Chemistry

Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance

Skabelon Instrueret Syntese af plasmoniske Guld Nanorør med Justerbar IR Absorbans

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) ...

A Simple Method for the Size Controlled Synthesis of Stable Oligomeric Clusters of Gold Nanoparticles under Ambient Conditions

En simpel metode til størrelse Kontrolleret Syntese af stabile Oligomere Klynger af guld nanopartikler under omgivende betingelser

Reducing dilute aqueous HAuCl4 with sodium thiocyanate (NaSCN) under alkaline conditions produces 2 to 3 nm diameter nanoparticles. Stable grape-like ...

Synthesis and Characterization of Fe-doped Aluminosilicate Nanotubes with Enhanced Electron Conductive Properties

Syntese og karakterisering af Fe-doteret aluminiumsilicat nanorør med Enhanced Electron ledende egenskaber

The goal of the protocol is to synthesize Fe-doped aluminosilicate nanotubes of the imogolite type with the formula (OH)3Al2-xFexO3SiOH. Doping with Fe ...

Nanosponge Tunability in Size and Crosslinking Density

Nanosponge Tunability i størrelse og Crosslinking tæthed

We describe a protocol for the synthesis of linear polyesters containing pendant epoxide functionality and their incorporation into a nanosponge with ...

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area

Kemisk udfældning metode til syntese af Nb2O5 ændret Bulk nikkel katalysatorer med høje specifikke overfladeareal

We demonstrate a method for the synthesis of NixNb1-xO catalysts with sponge-like and fold-like nanostructures. By varying the Nb:Ni ratio, a series of ...

Preparation and Characterization of C60/Graphene Hybrid Nanostructures

Preparation and Characterization of C60/Graphene Hybrid Nanostructures

Forberedelse og karakterisering af C60/Graphene Hybrid nanostrukturer

Physical thermal deposition in a high vacuum environment is a clean and controllable method for fabricating novel molecular nanostructures on graphene. We ...

Synthesis of Substrate-Bound Au Nanowires Via an Active Surface Growth Mechanism

Syntese af substrat-bundet Au Nanowires Via en aktiv overflade vækst mekanisme

Advancing synthetic capabilities is important for the development of nanoscience and nanotechnology. The synthesis of nanowires has always been a ...

Synthesis and Structure Determination of &#181;-Conotoxin PIIIA Isomers with Different Disulfide Connectivities

Syntese og struktur bestemmelse af µ-Conotoxin PIIIA isomerer med forskellige disulfid Connectivities

Peptides with a high number of cysteines are usually influenced regarding the three-dimensional structure by their disulfide connectivity. It is thus ...

Preparation of Graphene-Supported Microwell Liquid Cells for In Situ Transmission Electron Microscopy

Preparation of Graphene-Supported Microwell Liquid Cells for In Situ Transmission Electron Microscopy

Fremstilling af Graphene-understøttede Microwell Liquid-celler til in situ -Transmissionselektronmikroskopi

The fabrication and preparation of graphene-supported microwell liquid cells (GSMLCs) for in situ electron microscopy is presented in a stepwise protocol. ...

Synthesis of Aptamer-PEI-g-PEG Modified Gold Nanoparticles Loaded with Doxorubicin for Targeted Drug Delivery

Syntese af Aptamer-PEI-g-PEG Modificeret Guld Nanopartikler Fyldt med Doxorubicin for målrettet drug delivery

Due to drug resistance and toxicity in healthy cells, use of doxorubicin (DOX) has been limited in clinical cancer therapy. This protocol describes the ...