Name: synthesis of graphene nanofluids with controllable flake size distributions
Uploaded: 2019-07-17T13:00:00
Description: Watch this Scientific Journal Video about Synthesis of Graphene Nanofluids with Controllable Flake Size Distributions at JoVE.com

Dette arbeidet ble støttet av National Nature Science Foundation i Kina (Grant no. 21776095), Guangzhou Science and Technology Key program (Grant no. 201804020048), og Guangdong nøkkel laboratorium for Clean Energy Technology (Grant no. 2008A060301002). Vi takker LetPub (www.letpub.com) for sin språklige assistanse under utarbeidelsen av dette manuskriptet.

1. peeling av grafitt i en flytende fase
<ol><li>Tilberedning av reagenser<ol>
<li>I en tørr ren flat-Bottom kolbe, tilsett 20 g polyvinylklorid (PVA), og deretter legge til 1 000 mL destillert vann. Merk: Hvis suspensjonen ikke ble behandlet til tilfredshet, kan trinnet gjentas for å få en ekstra suspensjon.</li>
		<li>Forsiktig virvel flasken til PVA helt oppløses. FORSIKTIG: PVA er skadelig for mennesker; vernehansker og kirurgiske masker skal derfor brukes.</li>
		<li>Tilsett 50 g av grafitt pulver til fl...

<ol>
	<li>Sadeghinezhad, E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+comprehensive+review+on+graphene+nanofluids:+Recent+research,+development+and+applications.">A comprehensive review on graphene nanofluids: Recent research, development and applications.</a> Energy Conversion and Management. 111, 466-487 (2016).</li><li>Wang, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+Efficient+Production+of+Graphene+by+an+Ultrasound+Coupled+with+a+Shear+Mixer+in+Supercritical+CO2.">Highly Efficient Production of Graphene by an Ultrasound Coupled with a Shear Mixer in Supercritical CO2.</a> Industrial &amp; Engineering Chemistry Research. 57 (49), 16701-16708 (2018).</li><li>Cao, H. Y., Guo, Z. X., Xiang, H., Gong, X. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Layer+and+size+dependence+of+thermal+conductivity+in+multilayer+graphene+nanoribbons.">Layer and size dependence of thermal conductivity in multilayer graphene nanoribbons.</a> Physics Letters A. 376 (4), 525-528 (2012).</li><li>Yang, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+and+adjustment+of+the+graphene+work+function+via+size,+modification,+defects,+and+doping:+a+first-principle+theory+study.">Design and adjustment of the graphene work function via size, modification, defects, and doping: a first-principle theory study.</a> Nanoscale Research Letters. 12, (2017).</li><li>Khan, U., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+selection+of+dispersed,+exfoliated+graphene+flakes+by+controlled+centrifugation.">Size selection of dispersed, exfoliated graphene flakes by controlled centrifugation.</a> Carbon. 50 (2), 470-475 (2012).</li><li>Smith, R. J., King, P. J., Wirtz, C., Duesberg, G. S., Coleman, J. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lateral+size+selection+of+surfactant-stabilised+graphene+flakes+using+size+exclusion+chromatography.">Lateral size selection of surfactant-stabilised graphene flakes using size exclusion chromatography.</a> Chemical Physics Letters. 531, 169-172 (2012).</li><li>Galvin, K. P., Pratten, S. J., Nicol, S. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dense+medium+separation+using+a+teetered+bed+separator.">Dense medium separation using a teetered bed separator.</a> Minerals Engineering. 12 (9), 1059-1081 (1999).</li><li>Cai, C. J., Sang, N. N., Shen, Z. G., Zhao, X. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+and+size-controllable+preparation+of+graphene+oxide+nanosheets+using+high+shear+method+and+ultrasonic+method.">Facile and size-controllable preparation of graphene oxide nanosheets using high shear method and ultrasonic method.</a> Journal of Experimental Nanoscience. 12 (1), 247-262 (2017).</li><li>Chen, L. X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Oriented+graphene+nanoribbons+embedded+in+hexagonal+boron+nitride+trenches.">Oriented graphene nanoribbons embedded in hexagonal boron nitride trenches.</a> Nature Communications. 8, (2017).</li><li>Fan, T. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controllable+size-selective+method+to+prepare+graphene+quantum+dots+from+graphene+oxide.">Controllable size-selective method to prepare graphene quantum dots from graphene oxide.</a> Nanoscale Research Letters. 10, 1-8 (2015).</li><li>Oikonomou, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scalable+bottom-up+assembly+of+suspended+carbon+nanotube+and+graphene+devices+by+dielectrophoresis.">Scalable bottom-up assembly of suspended carbon nanotube and graphene devices by dielectrophoresis.</a> Physica Status Solidi-Rapid Research Letters. 9 (9), 539-543 (2015).</li><li>Liu, Y., Zhang, D., Pang, S. W., Liu, Y. Y., Shang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+separation+of+graphene+oxide+using+preparative+free-flow+electrophoresis.">Size separation of graphene oxide using preparative free-flow electrophoresis.</a> Journal of Separation Science. 38 (1), 157-163 (2015).</li><li>Cui, C. N., Huang, J. T., Huang, J. H., Chen, G. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+separation+of+mechanically+exfoliated+graphene+sheets+by+electrophoresis.">Size separation of mechanically exfoliated graphene sheets by electrophoresis.</a> Electrochimica Acta. 258, 793-799 (2017).</li><li>Sun, Z. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-yield+exfoliation+of+graphite+in+acrylate+polymers:+A+stable+few-layer+graphene+nanofluid+with+enhanced+thermal+conductivity.">High-yield exfoliation of graphite in acrylate polymers: A stable few-layer graphene nanofluid with enhanced thermal conductivity.</a> Carbon. 64, 288-294 (2013).</li><li>Sun, Z. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Amine-based+solvents+for+exfoliating+graphite+to+graphene+outperform+the+dispersing+capacity+of+N-methyl-pyrrolidone+and+surfactants.">Amine-based solvents for exfoliating graphite to graphene outperform the dispersing capacity of N-methyl-pyrrolidone and surfactants.</a> Chemical Communications. 50 (72), 10382-10385 (2014).</li><li>Du, B. L., Jian, Q. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+controllable+synthesis+of+graphene+water+nanofluid+with+enhanced+stability.">Size controllable synthesis of graphene water nanofluid with enhanced stability.</a> Fullerenes Nanotubes and Carbon Nanostructures. 27 (1), 87-96 (2019).</li><li>Tao, H. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scalable+exfoliation+and+dispersion+of+two-dimensional+materials+-+an+update.">Scalable exfoliation and dispersion of two-dimensional materials - an update.</a> Physical Chemistry Chemical Physics. 19 (2), 921-960 (2017).</li><li>Phiri, J., Gane, P., Maloney, T. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-concentration+shear-exfoliated+colloidal+dispersion+of+surfactant-polymer-stabilized+few-layer+graphene+sheets.">High-concentration shear-exfoliated colloidal dispersion of surfactant-polymer-stabilized few-layer graphene sheets.</a> Journal of Materials Science. 52 (13), 8321-8337 (2017).</li></ol>

Vi har foreslått en metodikk for syntetisere grafen nanofluider med kontrollerbar størrelse distribusjoner. Metoden kombinerer to prosedyrer: peeling og sentrifugering. Peeling styrer den nedre størrelsesgrensen av nanopartikler, og sentrifugering styrer den øvre størrelsesgrensen av nanopartikler.
Selv om vi brukte væske-fase peeling av grafitt å produsere grafen nanopartikler, bør følgende endringer i protokollen vurderes. Ytterligere peeling parametre (for eksempel rotor hastighet,...

Tradisjonelle metoder som brukes til å syntetisere grafen nanofluider ofte bruker sonikering til å spre grafen pulver1 i væsker, og sonikering har vist seg å endre størrelsesfordelingen av grafen nanopartikler2. Siden varmeledningsevne av grafen avhenger av flak lengde3,4, syntesen av grafen nanofluider med kontrollerbar flak størrelse distribusjoner er avgjørende for varmeoverføring programmer. Kontrollert sentrifugering har blitt brukt på flytende ekspandert grafen dispersjoner for å skille suspensjoner til fraksjoner med forskjellige gjennomsnitts flak størrelser5,6. Ulike Terminal hastigheter som brukes i sentrifugering føre til ulike kritiske settling partikkelstørrelser7. Terminalen hastighet kan brukes til å eliminere store grafen nanopartikler8.
Nylig har størrelse-kontrollerbar metoder som brukes til å syntetisere grafen via væske-fase peeling er innført for å overvinne de grunnleggende problemene som oppdages av konvensjonelle metoder9,10,11, 12,13. Væskefase peeling av grafitt har vist seg å være en effektiv måte å produsere grafen suspensjoner14,15,16, og den underliggende mekanismen viser at prosessparametrene er knyttet til nedre grenser for grafen nanopartikler størrelses fordelinger. Grafen nanofluider ble syntetisert ved flytende peeling av grafitt ved hjelp av overflateaktive midler17. Mens de nedre grensene for grafen nanopartikkel størrelsesfordelingen kan styres ved å justere parametrene under peeling, blir mindre oppmerksomhet til de øvre grensene av grafen nanopartikkel størrelsesfordelingen.
Målet med dette arbeidet er å utvikle en protokoll som kan brukes til å syntetisere grafen nanofluider med kontrollerbar størrelse distribusjoner. Fordi peeling er ansvarlig bare for den nedre størrelsesgrensen av den resulterende grafen nanoflakes, er ytterligere sentrifugering innført for å kontrollere den øvre størrelsesgrensen av den resulterende grafen nanoflakes. Den foreslåtte metoden er imidlertid ikke spesifikk for grafen og kan være hensiktsmessig for andre lagdelte forbindelser som ikke kan syntetisert ved hjelp av tradisjonelle metoder.

<table>
	<tbody>
		<tr>
			<td>Beaker</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>500 mL</td>
			<td></td>
		</tr>
		<tr>
			<td>Beaker</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>5000 mL</td>
			<td></td>
		</tr>
		<tr>
			<td>Deionized water</td>
			<td>Guangzhou Yafei Water Treatment Equipment Co., Ltd.</td>
			<td></td>
			<td>analytical grade</td>
		</tr>
		<tr>
			<td>Electronic balance</td>
			<td>Shanghai Puchun Co., Ltd.</td>
			<td>JEa10001</td>
			<td></td>
		</tr>
		<tr>
			<td>Filter membrane</td>
			<td>China Tianjin Jinteng Experiment Equipments Co., Ltd.</td>
			<td>0.2 micron</td>
			<td></td>
		</tr>
		<tr>
			<td>Graphite powder</td>
			<td>Tianjin Dengke chemical reagent Co., Ltd.</td>
			<td></td>
			<td>analytical grade</td>
		</tr>
		<tr>
			<td>Hand gloves</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Laboratory shear mixer</td>
			<td>Shanghai Specimen and Model Factory</td>
			<td>jrj-300</td>
			<td></td>
		</tr>
		<tr>
			<td>Long neck flat bottom flask</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>1000 ml</td>
			<td></td>
		</tr>
		<tr>
			<td>Nanoparticle analyzer</td>
			<td>HORIBA, Ltd.</td>
			<td>SZ-100Z</td>
			<td></td>
		</tr>
		<tr>
			<td>PVA</td>
			<td>Shanghai Yingjia Industrial Development Co., Ltd.</td>
			<td>1788</td>
			<td>analytical grade</td>
		</tr>
		<tr>
			<td>Raman spectrophotometer</td>
			<td>HORIBA, Ltd.</td>
			<td>Horiba LabRam 2</td>
			<td></td>
		</tr>
		<tr>
			<td>Scanning electron microscope</td>
			<td>Zeiss Co., Ltd.</td>
			<td>LEO1530VP</td>
			<td>SEM</td>
		</tr>
		<tr>
			<td>Surgical mask</td>
			<td>China Jiangsu Mingtai Education Equipments Co., Ltd.</td>
			<td>for one-time use</td>
			<td></td>
		</tr>
		<tr>
			<td>Thermal Gravimetric Analyzer</td>
			<td>German NETZSCH Co., Ltd.</td>
			<td>NETZSCH TG 209 F1 Libra</td>
			<td>TGA analysis</td>
		</tr>
		<tr>
			<td>Transmission electron microscope</td>
			<td>Japan Electron Optics Laboratory Co., Ltd.</td>
			<td>JEM-1400plus</td>
			<td>TEM</td>
		</tr>
		<tr>
			<td>UV-Vis spectrophotometer</td>
			<td>Agilent Technologies, Inc.+BB2:B18</td>
			<td>Varian Cary 60</td>
			<td></td>
		</tr>
	</tbody>
</table>
Try the professional online HTML editor

synthesis of graphene nanofluids with controllable flake size distributions

En metode for syntetisere grafen nanofluider med kontrollerbar flak størrelse distribusjoner er presentert. Grafen nanoflakes kan fås ved peeling av grafitt i væskefasen, og peeling tid brukes til å kontrollere de nedre grensene av grafen nanoflake størrelse distribusjoner. Sentrifugering brukes med hell til å kontrollere de øvre grensene for nanopartikkel størrelses distribusjoner. Målet med dette arbeidet er å kombinere peeling og sentrifugering for å kontrollere grafen nanoflake størrelses distribusjoner i de resulterende suspensjoner.

Eksistensen av grafen nanosheets kan valideres av ulike karakteristiske teknikker. Figur 1 viser resultatet av UV-Vis målingen for de forskjellige flak størrelses distribusjonene som produseres av ovennevnte-protokollen. Den Spectra absorbansen peak oppnådd i en bølgelengde på 270 NM er bevis på grafen flak. Ulike absorbances tilsvarer ulike konsentrasjoner. Den laveste absorbansen som er observert, tilsvarer den høyeste sentrifugering hastigheten. Spectra bekrefter sterkt at grafen e...

Watch this Scientific Journal Video about Synthesis of Graphene Nanofluids with Controllable Flake Size Distributions at JoVE.com

Synthesis of Graphene Nanofluids with Controllable Flake Size Distributions

En metode for syntetisere grafen nanofluider med kontrollerbar flak størrelse distribusjoner er presentert.

Syntese av grafen Nanofluider med kontrollerbar flak størrelse distribusjoner

A method for synthesizing graphene nanofluids with controllable flake size distributions is presented. Graphene nanoflakes can be obtained by the ...

Den foreslåtte metoden benytter eksfolieringsprosess og sentrifugeringsprosess for å kontrollere de nedre grensene og de øvre grensene for størrelsesfordelinger av resulterende grafinsuspensjon separat. Den største fordelen med den foreslåtte metoden er at den endelige størrelsesfordelingen kan kontrolleres ved å justere prosessparametrene for eksfolieringstrinnet og sentrifugeringstrinnet. I en tørr, ren, flat bunnkolbe, tilsett 20 gram PVA, og tilsett deretter 1000 milliliter destillert vann.Virvle forsiktig kolben til PVA oppløses helt. Tilsett deretter 50 gram grafittpulver til den flate bunnkolben og virvle forsiktig kolben til grafittpulveret sprer seg fullt ut i suspensjonen. Overfør 500 milliliter av den resulterende suspensjonen til et 500-milliliter beger.Plasser begeret under en skjærblander, plasser begeret nær midten av blandebeholderen for å forhindre dannelse av en virvel. Senk blandehodet til sin laveste posisjon, 30 millimeter fra baseplanet. Deretter forbereder du et vannbad ved å fylle et 5000-milliliter beger med romtemperaturvann, og plasser det 500 milliliter begeret i badekaret.Start mikseren, og øk hastigheten gradvis til 4, 500 rpm. Bland med denne hastigheten i 120 minutter. Bytt vannet hvert 30.Utfør dette eksfolieringstrinnet fem ganger til med forskjellig varighet. Blandetiden bestemmer den nedre sidestørrelsesgrensen for grafennanoflakene. Samle 500-milliliter generert suspensjoner etter hvert eksfoliering trinn.Merk hver suspensjon med eksfolasjonstiden, og sentrifuger den oppsamlede suspensjonen ved 140 ganger g i 45 minutter. For å fjerne den ueksfolierte grafitten, bruk en pipette til å samle de øverste 80% av supernatanten fra hvert sentrifugerør for ytterligere sentrifugering. Sentrifuger den overnaturlige suspensjonen fra siste sentrifugeringstrinn på 8, 951 ganger g i 45 minutter.Samle de øvre 50% av supernatant i sentrifugerøret, og merk prøven med et tall. Deretter, for å resirkulere sedimentet på bunnen av sentrifugerøret, tilsett 50 milliliter av den tidligere tilberedte PVA vannreagensen til sedimentet, og rist røret kraftig for hånd til sedimentet er godt dispergert i suspensjonen. Sentrifuger suspensjonen ved 8, 951 ganger g i 45 minutter.Samle de øvre 80%for ytterligere målinger. Gjenta sentrifugeringstrinnet for pelleten fire ganger til med fire forskjellige sentrifugeringshastigheter. Sentrifugeringshastigheten bestemmer den øvre sidestørrelsesgrensen for grafennanoflakene.Nå, forberede ultrafiolett synlig spektroskopi. Med den tidligere tilberedte PVA-vannløsningen i en tørr, ren prøvecelle, kalibrer det ultrafiolette synlige spektrometeret, sett PVA-vannkonsentrasjonen til 0%Deretter legger du til PVA-vannrefusjonen etter sentrifugering til en tørr, ren prøvecelle, med en banelengde på 10 millimeter, og få en avlesning ved hjelp av produsentens programvare. Klikk på Hent-knappen for å få grafen for måleresultater, og lagre resultatene.Deretter, for å bestemme grafenvekten, støvsug prøvens suspensjon ved hjelp av en nylonmembran med en porestørrelse på 0,2 mikrometer. Få membranen film, og vask med ca 200 milliliter vann i et beger. Gjenta vasken tre ganger, til alle faste stoffer vaskes bort fra membranen.Bestem den vasket vannmassen med en høypresisjons mikrobalanse for å oppnå vekten av faste stoffer. Igjen, vakuum filtrere vann suspensjoner ved hjelp av en nylon membran med en pore størrelse på 0,2 mikrometer. Få membranen, og tørk den ved romtemperatur i over 12 timer.Skyll deretter filmen med 200 milliliter av deionisert vann i et beger. Hvis ønsket konsentrasjon er mindre enn produksjonshastigheten på ett mg per milliliter, tilsett den tilberedte PVA-vannløsningen for å oppnå ønsket konsentrasjon. Hvis ønsket konsentrasjon er høyere enn 1% tørke det avioniserte vannet under vakuum i tørketrommelen i 24 timer for å oppnå grafen nanoark.I denne protokollen viser den ultrafiolette synlige målingen av de ulike flakstørrelsesfordelene spektraabsorbanstoppen oppnådd ved en bølgelengde på 270 nanometer, noe som indikerer beviset på grafenflakene. Suspensjon med forskjellig konsentrasjon har forskjellig 660 nanometer absorpsjon. D-båndet og 2D-båndet i Raman-spektroskopien bestemmer flaktykkelsen på grafennanoflakene.D-båndet i Raman-spekteret, som er relatert til grafen sp3 karbonatomer, skiller mellom den opprinnelige grafitten og grafennanoflakene. Lav D-båndintensitet indikerer de defektfrie grafennanoarkene. Særskilt størrelsesfordeling ble observert for den resulterende suspensjonen, tilberedt ved hjelp av forskjellige sentrifugeringshastigheter.Både transmisjonselektronmikroskopien og skanneelektronmikroskopien viser at grafen ble produsert, og eksfolieringen var vellykket. Sentrifugeringstrinnet fungerte imidlertid bare på nanopartikler med gjennomsnittlig diameter større enn 1000 nanometer. Forholdet mellom de øvre grensene for størrelsesfordelinger med sentrifugeringshastighet bør forhåndsbest.Siden størrelsen ikke påvirker med den foreslåtte metoden, er varmeoverføringseffektiviteten mulig å bli manipulert under forhold som noen tilkoblings-, konveksjons- og overføringsapplikasjoner i sentrum. PVA-polymeren er skadelig for mennesker. Ansiktsmaske og hansker skal brukes til å beskytte operatøren.

Research

JoVE Journal

Chemistry

Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance

Mal Regissert Syntese av Plasmonic Gold Nanorør med Fleksibel IR Absorbans

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) ...

A Simple Method for the Size Controlled Synthesis of Stable Oligomeric Clusters of Gold Nanoparticles under Ambient Conditions

En enkel metode for størrelsen Kontrollert Syntese av Stabile Oligomere Klynger av gull nanopartikler under omgivelses

Reducing dilute aqueous HAuCl4 with sodium thiocyanate (NaSCN) under alkaline conditions produces 2 to 3 nm diameter nanoparticles. Stable grape-like ...

Synthesis and Characterization of Fe-doped Aluminosilicate Nanotubes with Enhanced Electron Conductive Properties

Syntese og karakterisering av Fe-dopet Aluminosilicate nanorør med Enhanced Electron ledende egenskaper

The goal of the protocol is to synthesize Fe-doped aluminosilicate nanotubes of the imogolite type with the formula (OH)3Al2-xFexO3SiOH. Doping with Fe ...

Nanosponge Tunability in Size and Crosslinking Density

Nanosponge Tunability i størrelse og Crosslinking tetthet

We describe a protocol for the synthesis of linear polyesters containing pendant epoxide functionality and their incorporation into a nanosponge with ...

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area

Kjemisk nedbør metoden for syntese av Nb2O5 endret Bulk nikkel katalysatorer med høy bestemt areal

We demonstrate a method for the synthesis of NixNb1-xO catalysts with sponge-like and fold-like nanostructures. By varying the Nb:Ni ratio, a series of ...

Preparation and Characterization of C60/Graphene Hybrid Nanostructures

Preparation and Characterization of C60/Graphene Hybrid Nanostructures

Forberedelse og karakterisering av C60/Graphene Hybrid nanostrukturer

Physical thermal deposition in a high vacuum environment is a clean and controllable method for fabricating novel molecular nanostructures on graphene. We ...

Synthesis of Substrate-Bound Au Nanowires Via an Active Surface Growth Mechanism

Syntese av underlaget-bundet Au Nanowires Via en aktiv overflate vekst mekanisme

Advancing synthetic capabilities is important for the development of nanoscience and nanotechnology. The synthesis of nanowires has always been a ...

Synthesis and Structure Determination of &#181;-Conotoxin PIIIA Isomers with Different Disulfide Connectivities

Syntese og proteinstrukturer av μ-Conotoxin PIIIA isomerene med forskjellige Disulfide Connectivities

Peptides with a high number of cysteines are usually influenced regarding the three-dimensional structure by their disulfide connectivity. It is thus ...

Preparation of Graphene-Supported Microwell Liquid Cells for In Situ Transmission Electron Microscopy

Preparation of Graphene-Supported Microwell Liquid Cells for In Situ Transmission Electron Microscopy

Utarbeidelse av grafen-støttede Mikrotiterplateleser væske celler for in situ Transmission Electron mikroskopi

The fabrication and preparation of graphene-supported microwell liquid cells (GSMLCs) for in situ electron microscopy is presented in a stepwise protocol. ...

Synthesis of Aptamer-PEI-g-PEG Modified Gold Nanoparticles Loaded with Doxorubicin for Targeted Drug Delivery

Syntese av Aptamer-PEI-g-PEG Modifisert Gull Nanopartikler Lastet med Doxorubicin for målrettet legemiddellevering

Due to drug resistance and toxicity in healthy cells, use of doxorubicin (DOX) has been limited in clinical cancer therapy. This protocol describes the ...