Electrospray Deposition of Uniform Thickness Ge23Sb7S70 and As40S60 Chalcogenide Glass Films

Solution-based electrospray film deposition, which is compatible with continuous, roll-to-roll processing, is applied to chalcogenide glasses. Two ...

Clemson University

Thin films of lithium niobate are wafer bonded onto silicon substrates and rib-loaded with a chalcogenide glass, Ge(23)Sb(7)S(70), to demonstrate strongly confined single-mode submicron waveguides, microring modulators, and Mach-Zehnder modulators in the telecom C band. The 200 μm radii microring modulators present 1.2 dB/cm waveguide propagation loss, 1.2 × 10(5) quality factor, 0.4 GHz/V tuning rate, and 13 dB extinction ratio. The 6 mm long Mach-Zehnder modulators have a half-wave voltage-length product of 3.8 V.cm and an extinction ratio of 15 dB. The demonstrated work is a key step towards enabling wafer scale dense on-chip integration of high performance lithium niobate electro-optical devices on silicon for short reach optical interconnects and higher order advanced modulation schemes.

Heterogeneous microring and Mach-Zehnder modulators based on lithium niobate and chalcogenide glasses on silicon.

Low-loss waveguides constitute an important building block for integrated photonic systems. In this work, we investigated low-loss photonic device fabrication in Ge23Sb7S70 chalcogenide glass using electron beam lithography followed by plasma dry etching. High-index-contrast waveguides with a low propagation loss of 0.5 dB/cm and microdisk resonators with an intrinsic quality factor (Q-factor) of 1.2×106 were demonstrated. Both figures represent, to the best of our knowledge, the best low-loss results reported thus far in submicrometer single-mode chalcogenide glass devices.

Spencer Novak

Department of Materials Science and Engineering

Clemson University

Electrospray Deposition of Uniform Thickness Ge₂₃Sb₇S₇₀ and As₄₀S₆₀ Chalcogenide Glass Films