A Facile and Eco-friendly Route to Fabricate Poly(Lactic Acid) Scaffolds with Graded Pore Size

Over the recent years, functionally graded scaffolds (FGS) gaineda crucial role for manufacturing of devices for tissue engineering. The importance of ...

University of Palermo

The actinomycetes, Gram-positive filamentous bacteria, are the most prolific source of natural occurring antibiotics. At an industrial level, antibiotics from actinomycete strains are produced by means of submerged fermentations, where one of the major factors negatively affecting bioproductivity is the pellet-shaped biomass growth. The immobilization of microorganisms on properly chosen supports prevents cell-cell aggregation resulting in improving the biosynthetic capability. Thus, novel porous biopolymer-based devices are developed by combining melt mixing and particulate leaching. In particular, polycaprolactone (PCL), polyethylene glycol (PEG), and sodium chloride (NaCl) with different grain sizes are used to prepare PCL/PEG/NaCl blends in the melt. These blends are then leached to obtain PCL-based porous membranes that are used as solid support for the growth of Streptomyces coelicolor, a model streptomycete used to produce various antibiotics including the blue colored actinorhodin (ACT). Thereafter, the effect of the devices' characteristics on the bacterial growth and on the production ACT is evaluated. The results showed that ACT production is strongly dependent on the pore size distribution of the device. Moreover, membranes with pores ranging from 90 to 110 μm are able to offer a potential improvement in volumetric productivity of ACT if compared to conventional submerged liquid culture.

Effect of PCL/PEG-Based Membranes on Actinorhodin Production in Streptomyces coelicolor Cultivations.

A novel bi-layered multiphasic scaffold (BLS) have been fabricated for the first time by combining melt mixing, compression molding and particulate leaching. One layer has been composed by polylactic acid (PLA) presenting pore size in the range of 90-110µm while the other layer has been made of polycaprolactone (PCL) with pores ranging from 5 to 40µm. The different chemo-physical properties of the two biopolymers combined with the tunable pore architecture permitted to realize monolithic functionally graded scaffolds engineered to be potentially used for interface tissues regenerations. BLS have been characterized from a morphological and a mechanical point of view. In particular, mechanical tests have been carried out both in air and immersing the specimens in phosphate buffered saline (PBS) solution at 37°C, in order to evaluate the elastic modulus and the interlayer adhesion strength. Fibroblasts and osteoblasts have been cultured and co-cultured in order to investigate the cells permeation trough the different layers. The results indicate that the presented method is appropriate for the preparation of multiphasic porous scaffolds with tunable morphological and mechanical characteristics. Furthermore, the cells seeded were found to grow with a different trend trough the different layers thus demonstrating that the presented device has good potential to be used in interface tissue regeneration applications.

Francesco Lopresti

Department of Civil,
environmental,
Aerospace,
and materials engineering (DICAM),
RU INSTM,
Department of civil, environmental, aerospace, and materials engineering (DICAM), RU INSTM

University of Palermo

A Facile and Eco-friendly Route to Fabricate Poly(Lactic Acid) Scaffolds with Graded Pore Size

Francesco Lopresti

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Department of Civil,environmental,Aerospace,and materials engineering (DICAM),RU INSTM,Department of civil, environmental, aerospace, and materials engineering (DICAM), RU INSTM

University of Palermo

A Facile and Eco-friendly Route to Fabricate Poly(Lactic Acid) Scaffolds with Graded Pore Size

Department of Civil,
environmental,
Aerospace,
and materials engineering (DICAM),
RU INSTM,
Department of civil, environmental, aerospace, and materials engineering (DICAM), RU INSTM