fabrication of square pyramidal microwells for tumor spheroid fabrication

Fabrication Followed by 3D Encapsulation of Tumor Spheroids in PEG Hydrogels

Tumor spheroids have emerged as useful in vitro tools in studying cancer etiology, pathology, and drug responsiveness1. Traditionally, spheroids have been cultured in conditions such as low adhesion plates or bioreactors, where cell-cell adhesion is favored over cell-surface adhesion2. However, it is now recognized that to recapitulate the tumor microenvironment more faithfully, in vitro spheroid models should capture both cell-cell and cell-matrix interactions. This has prompted multiple groups to design scaffolds, such as hydrogels, where spheroids can be encapsulated3,4. Such hydrogel-based spheroid models enable the elucidation of cell-cell and cell-matrix interactions on various cell behaviors, such as viability, proliferation, stemness, or therapy responsiveness3.
Here, we describe a protocol for the encapsulation of glioblastoma spheroids in polyethylene glycol (PEG) hydrogels. There are multiple literature reports of glioblastoma cell spheroid encapsulation in hydrogels. For example, spheroids were formed by encapsulating U87 cells in PEG hydrogels decorated with an RGDS adhesive ligand and crosslinked with an enzymatically cleavable peptide to determine the effect of hydrogel stiffness on cell behavior5. U87 cells have also been formed in other PEG-based or hyaluronic acid-based hydrogels to expand the cancer stem cell population6 or to explore matrix-mediated mechanisms of chemotherapy resistance7,8,9. Glioblastoma spheroids have also been encapsulated in gelatin hydrogels to study the crosstalk between microglia and cancer cells and its effect on cell invasion10. Overall, such studies have demonstrated the utility of hydrogel-based in vitro models in understanding glioblastoma pathology and devising treatments.
Further, there are different methods for tumor spheroid fabrication and hydrogel encapsulation11. For example, dispersed cells could be seeded in hydrogels and allowed to form spheroids over time5,12. One drawback of such a method is the polydispersity of the formed spheroids, which could lead to differential cell responses. To produce uniform spheroids, cells could be encapsulated in microgels and cultured for extended periods until they invade and remodel the gel13, or cells could be deposited in templated gels with spherical &#39;holes&#39; and allowed to aggregate14. The drawback of these methods is their relative complexity, the need for a droplet generator or other means to form microgels or the &#39;holes&#39; in the gel, and the time it takes for spheroids to grow and mature. Alternatively, spheroids could be pre-formed in microwells9,15,16 or in hanging-drop plates17,18 and then encapsulated in a hydrogel, similar to the technique described here. These methods are simpler and can be done in a higher throughput fashion. Interestingly, it has been shown that the method of spheroid formation can affect spheroid cell behaviors, such as gene expression, cell proliferation, or drug responsiveness19,20.
Here, we focus on glioblastoma since it is a solid tumor whose native environment is the soft, nanoporous brain matrix21, which can be mimicked by a soft, nanoporous hydrogel. Glioblastoma is also the deadliest brain cancer for which there is no available cure22. However, the protocol described here can be used for the encapsulation of spheroids representing any solid tumor. We chose to use PEG hydrogels that are formed through a Michael-type addition reaction23. PEG is a synthetic, non-degradable, and biocompatible hydrogel that is inert and serves as scaffolding and physical cell support but does not support cell attachment23. Cell adhesiveness can be added separately via tethering of whole proteins or adhesive ligands24, and degradability can be added via chemical modifications of the PEG polymer chain or hydrolytically or enzymatically degradable crosslinkers25,26. This allows for biochemical properties to be tuned independently of mechanical or physical hydrogel properties, which could be advantageous in studying cell-matrix interactions. The Michael-type gelation chemistry is selective and happens at physiological conditions; hence, it allows for spheroid encapsulation by simply mixing the spheroids with the hydrogel precursor solution.
Overall, the methodology presented here has several notable characteristics. First, fabricating tumor spheroids in a multiwell assembly is efficient, quick, and the cost of the required materials is low. Second, the spheroids are produced in large batches in a variety of sizes with low polydispersity. Finally, only commercially available materials are required. The utility of the methodology is illustrated by exploring the effect of substrate properties on spheroid cell viability, circularity, and cell stemness.

Author Spotlight: In Vitro Hydrogel Model for Glioblastoma Microenvironment Study

Tumor Spheroid Fabrication and Encapsulation in Polyethylene Glycol Hydrogels for Studying Spheroid-Matrix Interactions

Our lab focuses on designing in vitro hydrogel models for glioblastoma steroid encapsulation to mimic the tumor extracellular microenvironment. The effective substrate, mechanical and biochemical properties on steroid cell viability, circularity, stemness, and spreading are investigated with such models. Current experimental challenges in tumor module development revolve around a desire for complexity to mimic all aspects of the tumor microenvironment for physiological relevance, and also a desire for simplicity to make the model accessible, robust, low cost, and easy to use, and compatible with multiplex screening approaches.We present a protocol that enables fast, robust, and low-cost fabrication of tumor steroids and encapsulation in hydrogels made to mimic the tumor microenvironment. The model does not require any specialized equipment. It will be particularly useful for exploring steroid matrix interactions in building in vitro tissue physiology or pathology models.Understanding the interactions between glioblastoma cancer cells and their microenvironment can encourage development of new therapies to better treat this cancer. Furthermore, development of an in vitro model for glioblastoma cancer can enhance development of this model for other cancer diseases.

Fabrication of Square Pyramidal Microwells for Tumor Spheroid Fabrication

To begin pour two grams or about one milliliter of negative PDMS precursor solution onto one well of a six well square parametal master mold. After covering the master mold with PDMS, place the plate in a vacuum desiccate to degas the solution. Next, place the plate in an oven at 60 degrees Celsius for 24 hours to cure the PDMS.Once PDMS cures but is still warm, use a spatula to carefully remove the PDMS mold from the master mold. Then with a biopsy punch, cut it into a 35 millimeter diameter slab. Place the properly cut PDMS mold in a Petri dish and cover it with the lid to continue curing it at room temperature for an additional 24 hours.To prepare the positive PDMS mold place a 35 millimeter slab of the negative PDMS mold in a 35 millimeter Petri dish with the textured micro wells facing up. Pour 2.5 grams or about 1.2 milliliters of positive PDMS precursor solution onto the negative mold in the Petri dish. Degas the precursor solution for 30 minutes before placing it into the oven at 60 degrees Celsius for three to four hours.After curing, remove the molds from the Petri dish. Immediately peel the positive mold from the negative mold. Use a 10 millimeter biopsy punch to cut the positive molds into slabs.Next, use tweezers to gently dip the flat side of each 10 millimeter positive mold into the pre-prepared PDMS glue precursor solution. Carefully place one mold per well in a well of a 48 well plate. Gently press each mold to glue it to the well bottom.Incubate the assembled plate at 60 degrees Celsius for four to 24 hours to cure the glue.

fabrication-square-pyramidal-microwells-for-tumor-spheroid

Research

JoVE Journal

Bioengineering

64 次观看.  Saint Louis University. 首先，将两克或约一毫升的负性PDMS前驱体溶液倒入六孔方形顺金属母模的一个孔中。用PDMS覆盖母模后，将板置于真空干燥中以使溶液脱气。接下来，将板放入 60 摄氏度的烤箱中 24 小时以固化 PDMS。一旦PDMS固化但仍然温暖，用刮刀小心地从主模具中取出PDMS模具。然后用活检冲床将其切成直径为 35 毫米的板。将正确切割的PDMS模具放入培养皿中，并用盖子盖住，以继续在...