Material Formation of Recombinant Spider Silks through Aqueous Solvation using Heat and Pressure

Many spiders produce seven types of silks. Six of the silks are fiber in form when produced by the spiders. These fibers are not water soluble. In order ...

Utah State University

Spider silks have unique mechanical properties but current efforts to duplicate those properties with recombinant proteins have been unsuccessful. This study was designed to develop a single process to spin fibers with excellent and consistent mechanical properties. As-spun fibers produced were brittle, but by stretching the fibers the mechanical properties were greatly improved. A water-dip or water-stretch further increased the strength and elongation of the synthetic spider silk fibers. Given the promising results of the water stretch, a mechanical double-stretch system was developed. Both a methanol/water mixture and an isopropanol/water mixture were independently used to stretch the fibers with this system. It was found that the methanol mixture produced fibers with high tensile strength while the isopropanol mixture produced fibers with high elongation.

Development of a Process for the Spinning of Synthetic Spider Silk.

The production of recombinant spider silk proteins continues to be a key area of interest for a number of research groups. Several key obstacles exist in their production as well as in their formulation into useable products. The original reported method to solubilize recombinant spider silk proteins (rSSp) in an aqueous solution involved using microwaves to quickly generate heat and pressure inside of a sealed vial containing rSSp and water. Fibers produced from this system are remarkable in their mechanical ability and demonstrate the ability to be stretched and recover 100 times. The microwave method dissolves the rSSPs with dissolution time increasing with higher molecular weight constructs, increasing concentration of rSSPs, protein type, and salt concentration. It has proven successful in solvating a number of different rSSPs including native-like sequences (MaSp1, MaSp2, piriform, and aggregate) as well as chimeric sequences (FlAS) in varied concentrations that have been spun into fibers and formed into films, foams, sponges, gels, coatings, macro and micro spheres and adhesives. The system is effective but inherently unpredictable and difficult to control. Provided that the materials that can be generated from this method of dissolution are impressive, an alternative means of applying heat and pressure that is controllable and predictable has been developed. Results indicate that there are combinations of heat and pressure (135 °C and 140 psi) that result in maximal dissolution without degrading the recombinant MaSp2 protein tested, and that heat and pressure are the key elements to the method of dissolution.

Brianne E. Bell

Department of Biology

Utah State University

Material Formation of Recombinant Spider Silks through Aqueous Solvation using Heat and Pressure

Brianne E. Bell

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Department of Biology

Utah State University

Material Formation of Recombinant Spider Silks through Aqueous Solvation using Heat and Pressure

Department of Biology