Towards Biomimicking Wood: Fabricated Free-standing Films of Nanocellulose, Lignin, and a Synthetic Polycation

Woody materials are comprised of plant cell walls that contain a layered secondary cell wall composed of structural polymers of polysaccharides and ...

Virginia Tech

A biomimetic approach was taken for studying the adsorption of a model copolymer (pullulan abietate, DS 0.027), representing the lignin-carbohydrate complex, to a model surface for cellulose fibers (Langmuir-Blodgett thin films of regenerated cellulose). Adsorption results were assayed using surface plasmon resonance spectroscopy (SPR) and atomic force microscopy (AFM). Rapid, spontaneous, and desorption-resistant surface modification resulted. This effort is viewed as a critical first step towards the permanent surface modification of cellulose fibers with a layer of molecules amenable to either enzymatic crosslinking for improved wood composites or thermoplastic consolidation.

Surface modification of cellulose fibers: towards wood composites by biomimetics.

The assembly of dissolved technical lignins in aqueous and organic medium has been studied at the solid-liquid interface. Adsorption of alkali lignin onto gold coated crystals treated with a cationic polymer was determined using a quartz crystal microbalance with dissipation monitoring. Complete coverage of the cationic surface with alkali lignin occurred at low solution concentration, revealing a high affinity coefficient under both alkali and neutral conditions. With additional adsorption studies from organosolv lignin in organic solvent and spectroscopic analysis of mixtures of cationic polymer and alkali lignin, a noncovalent interaction between lignin's aromatic rings and the cation of the quaternary ammonium group was shown to exist. The work underscores how polyphenolic biopolymers can strongly interact with cations through noncovalent interactions to control molecular architecture.

Cation-pi interactions as a mechanism in technical lignin adsorption to cationic surfaces.

Surface chemistry of wood is based on the exposed surface that is the combination of the intact and cut cellular wall material. It is inherently complex and changes with processing history. Modification of wood surfaces through noncovalent attachment of amine containing water soluble polyelectrolytes provides a path to create functional surfaces in a controlled manner. Adsorption of polyethylenimine (PEI) and polydiallydimethylammonium chloride (PDDA) to wood was quantified as a function of solution conditions (pH and ionic strength). Polycation adsorption was maximized under basic pH without the addition of electrolyte. Added salt either had marginal influence or decreased adsorption of polycation, indicating interactions are strongly influenced by Coulombic forces. PEI adsorption could be modeled by both a Langmuir and Freundlich equations, although the wood surface is known to be heterogeneous. After adsorption of polycations, layer-by-layer assembled films were created on the wood surface. Layered films masked ultrastructural features of the cell wall, while leaving the microscale features of wood (cut lumen walls and openings) evident. These findings revealed for the first time that nanoscale films on wood can be deposited without changing the microscopic and macroscopic texture. Functionalized wood surfaces created by nanoscale films may have a future role in adhesives systems for wood composites, wood protection, and creating new functional features on wood.

Nanoscale coatings on wood: polyelectrolyte adsorption and layer-by-layer assembled film formation.

Unusual fractions of cellulose microfibrils from woody material with dimensions of hundreds of nanometers in length and single digit angstrom thickness were obtained by intensive sonication of TEMPO-oxidized cellulose fibers. These cellulose microfibril fragments, composed of many mono- and bilayer molecular sheets, were analyzed with scattering and spectroscopy techniques to understand the structural changes at the supramolecular level. XRD data indicated that sonication breaks the cellulose microfibrils along its (200) planes, yet some form of the Iβ crystalline structure is still retained with reduced crystallinity. The Raman and FTIR analysis indicated structural changes to the cellulose microfibrils do not occur until after sonication; furthermore, AFM observation indicates that the structural changes began to occur within 5 min of sonication. An altered supramolecular structure is evident after sonication: major features from cellulose I are preserved, although certain spectral features similar to mercerized and ball milled cellulose appeared in its FTIR and Raman spectra. These spectral differences are traced to changes in the methine environment, hydroxymethyl conformations, and skeletal vibrations. By integrating the present findings and previous research, a cellulose molecular sheet delamination scheme is proposed to describe this microfibril fragmentation along its (200) plane.

Supramolecular structure characterization of molecularly thin cellulose I nanoparticles.

Novel cellulose based-scaffolds were studied for their ability to nucleate bioactive calcium phosphate crystals for future bone healing applications. Cellulose-based scaffolds were produced by electrospinning cellulose acetate (CA) dissolved in a mixture of acetone/dimethylacetamide (DMAc). The resulting nonwoven CA mats containing fibrils with diameters in the range of 200 nm to 1.5 μm were saponified by NaOH/ethanol for varying times to produce regenerated cellulose scaffolds. Biomimetic crystal growth nucleated from the fiber surface was studied as a function of surface chemistry. Regenerated cellulose scaffolds of varying treatments were soaked in simulated body fluid (SBF) solution. Scaffolds that were treated with CaCl(2), a mixture of carboxymethyl cellulose (CMC) and CaCl(2), and NaOH and CaCl(2), were analyzed using X-ray photoelectron spectroscopy, X-ray powder diffraction, and scanning electron microscopy to understand the growth of bioactive calcium phosphate (Ca-P) crystals as a function of surface treatment. The crystal structure of the nucleated Ca-P crystals had a diffraction pattern similar to that of hydroxyapatite, the mineralized component of bone. The study shows that the scaffold surface chemistry can be manipulated, providing numerous routes to engineer cellulosic substrates for the requirements of scaffolding.

Biomimetic calcium phosphate crystal mineralization on electrospun cellulose-based scaffolds.

Alkali metal counter-cations alter the electron density of phenolates in solution by electrostatic interactions. This change in electron density affects their reactivity toward formaldehyde, hydroxymethylphenols, and isocyanates during polymerization. The electronic perturbation of phenolic model compounds in the presence of alkali metal hydroxides was investigated with (13)C and (1)H nuclear magnetic resonance in polar solvents relative to non-ionic controls, altering the chemical shifts of the model compounds, thus indicating changes in electron density using the chemical shift as a proxy. These shifts were attributed to Coulombic electrostatic interactions of the counter-cation with the phenolate anion that correlated to hydrated ionic radius and solvent dielectric constants. The predicted relative reaction rates for formaldehyde addition based on electron density ranking from (13)C nuclear magnetic resonance of the phenolic models was compared with the literature values. Predictions for condensation reactions of 2- and 4-hydroxymethylphenol from chemical shifts were consistent with published results. The results permit predictions for the reaction of phenolic compounds for the formation of thermosetting polymeric materials.

Chemical shifts of phenolic monomers in solution and implications for addition and self-condensation.

Introducing porosity in electrospun scaffolds is critical to improve cell penetration and nutrient diffusion for tissue engineering. Nanofibrous cellulose scaffolds were prepared by electrospinning cellulose acetate (CA) followed by saponification to regenerate cellulose. Using a computer-assisted design approach, scaffolds underwent laser ablation resulting in pores with diameters between 50 and 300 μm without damaging or modifying the surrounding scaffold area. A new mineralization method was employed in conjunction with microablation using commercial phosphate buffered saline (PBS) to soak carboxymethylcellulose surface-modified electrospun scaffolds. The resulting crystals within the scaffold on the interior of the pore had a calcium to phosphate ratio of 1.56, similar to hydroxyapatite. It was observed that porosity of the cellulose scaffolds enhanced osteoblast cell attachment at the edge of the pores, while mineralization enhanced overall cell density.

Electrospun nanofibrous cellulose scaffolds with controlled microarchitecture.

This study focused on the assembly characteristics of debranched xylan onto cellulose surfaces. A rye arabinoxylan polymer with an initial arabinose/xylose ratio of 0.53 was debranched with an oxalic acid treatment as a function of time. The resulting samples contained reduced arabinose/xylose ratios significantly affecting the molecular architecture and solution behavior of the biopolymer. With this treatment, an almost linear xylan with arabinose DS of only 0.04 was obtained. The removal of arabinose units resulted in the self-assembly of the debranched polymer in water into stable nanoparticle aggregates with a size around 300 nm with a gradual increase in crystallinity of the isolated xylan. Using quartz crystal microbalance with dissipation monitoring, the adsorption of xylan onto model cellulose surfaces was quantified. Compared to the nonmodified xylan, the adsorption of debranched xylan increased from 0.6 to 5.5 mg m(-2). Additionally, adsorption kinetics suggest that the nanoparticles rapidly adsorbed to the cellulose surfaces compared to the arabinoxylan. In summary, a control of the molecular structure of xylan influences its ability to form a new class of polysaccharide nanoparticles in aqueous suspensions and its interaction with nanocellulose surfaces.

Assembly of debranched xylan from solution and on nanocellulosic surfaces.

The in-depth understanding of the enzymatic hydrolysis of cellulose with heterogeneous morphology (that is, crystalline versus amorphous) may help develop better cellulase cocktail mixtures and biomass pretreatment, wherein cost-effective release of soluble sugars from solid cellulosic materials remains the largest obstacle to the economic viability of second generation biorefineries.

New insights into enzymatic hydrolysis of heterogeneous cellulose by using carbohydrate-binding module 3 containing GFP and carbohydrate-binding module 17 containing CFP.

Scott Renneckar

Institute for Critical Technology and Applied Science,
Macromolecules and Interfaces Institute,
Department of Sustainable Biomaterials,
Sustainable Nanotechnology Interdisciplinary Graduate Education Program

Virginia Tech

Towards Biomimicking Wood: Fabricated Free-standing Films of Nanocellulose, Lignin, and a Synthetic Polycation

Scott Renneckar

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Institute for Critical Technology and Applied Science,Macromolecules and Interfaces Institute,Department of Sustainable Biomaterials,Sustainable Nanotechnology Interdisciplinary Graduate Education Program

Virginia Tech

Towards Biomimicking Wood: Fabricated Free-standing Films of Nanocellulose, Lignin, and a Synthetic Polycation

Institute for Critical Technology and Applied Science,
Macromolecules and Interfaces Institute,
Department of Sustainable Biomaterials,
Sustainable Nanotechnology Interdisciplinary Graduate Education Program