Implantation of Electrospun Vascular Grafts with Optimized Structure in a Rat Model

Here, we present a protocol to fabricate macroporous PCL vascular graft and describe an evaluation protocol by using a rat model of abdominal aorta ...

Nankai University

The vascular grafts prepared by electrospinning often have relatively small pores, which limit cell infiltration into the grafts and hinder the regeneration and remodeling of the grafts into neoarteries. To overcome this problem, macroporous electrospun polycaprolactone (PCL) scaffolds with thicker fibers (5-6 μm) and larger pores (∼30 μm) were fabricated in the present study. In vitro cell culture indicated that macrophages cultured on thicker-fiber scaffolds tended to polarize into the immunomodulatory and tissue remodeling (M2) phenotype, while those cultured on thinner-fiber scaffolds expressed proinflammatory (M1) phenotype. In vivo implantation by replacing rat abdominal aorta was performed and followed up for 7, 14, 28 and 100 d. The results demonstrated that the macroporous grafts markedly enhanced cell infiltration and extracellular matrix (ECM) secretion. All grafts showed satisfactory patency for up to 100 days. At day 100, the endothelium coverage was complete, and the regenerated smooth muscle layer was correctly organized with abundant ECM similar to those in the native arteries. More importantly, the regenerated arteries demonstrated contractile response to adrenaline and acetylcholine-induced relaxation. Analysis of the cellularization process revealed that the thicker-fiber scaffolds induced a large number of M2 macrophages to infiltrate into the graft wall. These macrophages further promoted cellular infiltration and vascularization. In conclusion, the present study confirmed that the scaffold structure can regulate macrophage phenotype. Our thicker-fiber electrospun PCL vascular grafts could enhance the vascular regeneration and remodeling process by mediating macrophage polarization into M2 phenotype, suggesting that our constructs may be a promising cell-free vascular graft candidate and are worthy for further in vivo evaluation. 

The effect of thick fibers and large pores of electrospun poly(ε-caprolactone) vascular grafts on macrophage polarization and arterial regeneration.

Nitric oxide (NO) is an important signaling molecule in cardiovascular system, and the sustained release of NO by endothelial cells plays a vital role in maintaining patency and homeostasis. In contrast, lack of endogenous NO in artificial blood vessel is believed to be the main cause of thrombus formation. In this study, enzyme prodrug therapy (EPT) technique was employed to construct a functional vascular graft by immobilization of galactosidase on the graft surface. The enzyme-functionalized grafts exhibited excellent catalytic property in decomposition of the exogenously administrated NO prodrug. Localized and on-demand release of NO was demonstrated by in vitro release assay and fluorescent probe tracing in an ex vivo model. The immobilized enzyme retained catalytic property even after subcutaneous implantation of the grafts for one month. The functional vascular grafts were implanted into the rat abdominal aorta with a 1-month monitoring period. Results showed effective inhibition of thrombus formation in vivo and enhancement of vascular tissue regeneration and remodeling on the grafts. Thus, we create an enzyme-functionalized vascular graft that can catalyze prodrug to release NO locally and sustainably, indicating that this approach may be useful to develop new cell-free vascular grafts for treatment of vascular diseases. 

Enzyme-functionalized vascular grafts catalyze in-situ release of nitric oxide from exogenous NO prodrug.

Current in vitro models fail in predicting the degradation rate and mode of magnesium (Mg) stents in vivo. To overcome this, the microenvironment of the stent is simulated here in an ex vivo bioreactor with porcine aorta and circulating medium, and compared with standard static in vitro immersion and with in vivo rat aorta models. In ex vivo and in vivo conditions, pure Mg wires were exposed to the aortic lumen and inserted into the aortic wall to mimic early- and long-term implantation, respectively. Results showed that: 1) Degradation rates of Mg were similar for all the fluid diffusion conditions (in vitro static, aortic wall ex vivo and in vivo); however, Mg degradation under flow condition (i.e. in the lumen) in vivo was slower than ex vivo; 2) The corrosion mode in the samples can be mainly described as localized (in vitro), mixed localized and uniform (ex vivo), and uniform (in vivo); 3) Abundant degradation products (MgO/Mg(OH) and Ca/P) with gas bubbles accumulated around the localized degradation regions ex vivo, but a uniform and thin degradation product layer was found in vivo. It is concluded that the ex vivo vascular bioreactor provides an improved test setting for magnesium degradation between static immersion and animal experiments and highlights its promising role in bridging degradation behavior and biological response for vascular stent research.

Ex vivo blood vessel bioreactor for analysis of the biodegradation of magnesium stent models with and without vessel wall integration.

Wound healing dressings are increasingly needed clinically due to the large number of skin damage annually. Nitric oxide (NO) plays a key role in promoting wound healing, thus biomaterials with NO-releasing property receive increasing attention as ideal wound dressing. In present study, we prepared a novel functional wound dressing by combining electrospun poly(ε-caprolactone) (PCL) nonwoven mat with chitosan-based NO-releasing biomaterials (CS-NO). As-prepared PCL/CS-NO dressing released NO sustainably under the physiological conditions, which was controlled by the catalysis of β-galactosidase. In vivo wound healing characteristics were further evaluated on full-thickness cutaneous wounds in mice. Results showed that PCL/CS-NO wound dressings remarkably accelerated wound healing process through enhancing re-epithelialization and granulation formation and effectively improved the organization of regenerated tissues including epidermal-dermal junction, which could be ascribed to the pro-angiogenesis, immunomodulation, and enhanced collagen synthesis provided by the sustained release of NO. Therefore, PCL/CS-NO may be a promising candidate for wound dressings, especially for the chronic wound caused by the ischemia.

Functional poly(ε-caprolactone)/chitosan dressings with nitric oxide-releasing property improve wound healing.

Rapid endothelialization is a key factor that determines the success of small-diameter vascular grafts as an artery substitute in the treatment of cardiovascular diseases. Aimed to facilitate vascular regeneration, we developed a vascular scaffold loaded with resveratrol, which is a natural compound extracted from plants and showed multifaceted effects in cardiovascular protection. The tubular poly(ε-caprolactone) (PCL) scaffold was prepared by electrospinning with resveratrol in the PCL solution. In vitro assay demonstrated that resveratrol could be released from the scaffolds in a sustained and controlled manner. Cell culture results indicated that the migration of endothelial cells (ECs), nitric oxide production, and the ability of tube formation increased in the resveratrol-containing PCL scaffold groups compared with the PCL control. Meanwhile, the level of tumor necrosis factor (TNF)-α, the main proinflammatory factor secreted from macrophages, was reduced, and the messenger RNA expressions of the M2 macrophage-related genes were increased in the resveratrol-containing group. Further, in vivo implantation was performed by replacing rat abdominal aorta. We observed fast endothelialization and enhanced vascular regeneration in rats with resveratrol-containing scaffolds. The presence of resveratrol also induced a large number of M2 macrophages to infiltrate into the graft wall. Taken together, the incorporation of resveratrol into the PCL grafts enhanced the vascular regeneration by modulation of ECs and macrophages.

Effect of Resveratrol on Modulation of Endothelial Cells and Macrophages for Rapid Vascular Regeneration from Electrospun Poly(ε-caprolactone) Scaffolds.

Long-term evaluation of vascular grafts is an essential step to facilitate clinical translation. In this study, we investigate the long-term performance of a macro-porous poly(ɛ-caprolactone) (PCL) electrospun vascular graft using the rat abdominal artery replacement model. Long-term patency, endothelialization, and smooth muscle cell regeneration were evaluated, as well as calcification and degradation. The data showed that all the grafts remained open and unobstructed. There was no evidence of aneurysm, stenosis, or calcification one year after implantation. Importantly, neo-vessel was regenerated on the luminal surface of the graft, and was composed of a complete endothelial layer and several layers of smooth muscle cells. The neo-vessel showed vascular physiological function, although not as good as that in native blood vessels, likely due to the remaining scaffold fibers. These data indicated that the PCL macro-porous electrospun vascular graft has potential to be an artery substitute for long-term implantation. Also, this work indicates that continued efforts are needed to develop advanced vascular grafts that exhibit the appropriate balance between the regeneration of the neo-vessel and the complete degradation of the graft materials. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1618-1627, 2018.

The regeneration of macro-porous electrospun poly(ɛ-caprolactone) vascular graft during long-term in situ implantation.

In the present study, pure zinc stents were implanted into the abdominal aorta of rabbits for 12 months. Multiscale analysis including micro-CT, scanning electron microscopy (SEM), scanning transmission electron microscopy (STEM) and histological stainings was performed to reveal the fundamental degradation mechanism of the pure zinc stent and its biocompatibility. The pure zinc stent was able to maintain mechanical integrity for 6 months and degraded 41.75 ± 29.72% of stent volume after 12 months implantation. No severe inflammation, platelet aggregation, thrombosis formation or obvious intimal hyperplasia was observed at all time points after implantation. The degradation of the zinc stent played a beneficial role in the artery remodeling and healing process. The evolution of the degradation mechanism of pure zinc stents with time was revealed as follows: Before endothelialization, dynamic blood flow dominated the degradation of pure zinc stent, creating a uniform corrosion mode; After endothelialization, the degradation of pure zinc stent depended on the diffusion of water molecules, hydrophilic solutes and ions which led to localized corrosion. Zinc phosphate generated in blood flow transformed into zinc oxide and small amounts of calcium phosphate during the conversion of degradation microenvironment. The favorable physiological degradation behavior makes zinc a promising candidate for future stent applications.

Evolution of the degradation mechanism of pure zinc stent in the one-year study of rabbit abdominal aorta model.

Long-term results of implants in small animal models can be used to optimize the design of grafts to further promote tissue regeneration. In previous study, we fabricated a poly(ɛ-caprolactone) (PCL) bi-layered vascular graft consisting of an internal layer with circumferentially aligned microfibers and an external layer with random nanofibers. The circumferentially oriented vascular smooth muscle cells (VSMCs) were successfully regenerated after the grafts were implanted in rat abdominal aorta for 3 months. Here we investigated the long-term (18 months) performance of the bi-layered grafts in the same model. All the grafts were patent. No thrombosis, aneurysm, or stenosis occurred. The endothelium maintained complete. However, most of circumferentially oriented VSMCs migrated to luminal surface of the grafts to form a neointima with uniform thickness. Accordingly, extracellular matrix including collagen, elastin, and glycosaminoglycan displayed high density in neointima layer while with low density in the grafts wall because of the incomplete degradation of PCL. A small amounts of calcification occurred in the grafts. The contraction and relaxation function of regenerated neoartery almost disappeared. These data indicated that based on the structure design, many other factors of grafts should be considered to achieve the regenerated neoartery similar to the native vessels after long-term implantation. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2018.

Yifan Wu

State Key Laboratory of Medicinal Chemical Biology,
Key Laboratory of Bioactive Materials (Ministry of Education),
College of Life Sciences,
State Key Laboratory of Medicinal Chemical Biology, Key Laboratory of Bioactive Materials (Ministry of Education), College of Life Sciences

Nankai University

Implantation of Electrospun Vascular Grafts with Optimized Structure in a Rat Model