High-resolution Thermal Micro-imaging Using Europium Chelate Luminescent Coatings

Micro-electronic devices often undergo significant self-heating when biased to their typical operating conditions. This paper describes a convenient ...

University of Northern Iowa

Two new Raman modes below 100 cm(-1) are observed in twisted bilayer graphene grown by chemical vapor deposition. The two modes are observed in a small range of twisting angle at which the intensity of the G Raman peak is strongly enhanced, indicating that these low energy modes and the G Raman mode share the same resonance enhancement mechanism, as a function of twisting angle. The ~94 cm(-1) mode (measured with a 532 nm laser excitation) is assigned to the fundamental layer breathing vibration (ZO' mode) mediated by the twisted bilayer graphene lattice, which lacks long-range translational symmetry. The dependence of this mode's frequency and line width on the rotational angle can be explained by the double resonance Raman process that is different from the previously identified Raman processes activated by twisted bilayer graphene superlattice. The dependence also reveals the strong impact of electronic-band overlaps of the two graphene layers. Another new mode at ~52 cm(-1), not observed previously in the bilayer graphene system, is tentatively attributed to a torsion mode in which the bottom and top graphene layers rotate out-of-phase in the plane.

Observation of low energy Raman modes in twisted bilayer graphene.

We investigated the low-frequency Raman spectra of freestanding few-layer graphene (FLG) at varying temperatures (400-900 K) controlled by laser heating. At high temperature, we observed the fundamental Raman mode for the lowest-frequency branch of rigid-plane layer-breathing mode (LBM) vibration. The mode frequency redshifts dramatically from 81 cm(-1) for bilayer to 23 cm(-1) for 8-layer. The thickness dependence is well described by a simple model of coupled oscillators. Notably, the LBM Raman response is unobservable at room temperature, and it is turned on at higher temperature (>600 K) with a steep increase of Raman intensity. The observation suggests that the LBM vibration is strongly suppressed by molecules adsorbed on the graphene surface but is activated as desorption occurs at high temperature.

Courtney Keiser

Department of Physics

University of Northern Iowa

High-resolution Thermal Micro-imaging Using Europium Chelate Luminescent Coatings

Courtney Keiser

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Department of Physics

University of Northern Iowa

High-resolution Thermal Micro-imaging Using Europium Chelate Luminescent Coatings

Department of Physics