Preparation of Biomass-based Mesoporous Carbon with Higher Nitrogen-/Oxygen-chelating Adsorption for Cu(II) Through Microwave Pre-Pyrolysis

An environment-friendly technique for synthesizing biomass-based mesoporous activated carbon with high nitrogen-/oxygen-chelating adsorption for Cu(II) is ...

Nanjing Agricultural University

A convenient effective microwave pre-pyrolysis treatment to synthesize biomass-based mesoporous carbon with higher nitrogen/oxygen-chelating adsorption for Cu(II) is reported here, in which phosphoric acid impregnated bagasse was used as a microwave absorber and porogen. For comparison, conventional electric-heating pyrolyzed carbon was prepared and doped with nitrogen/oxygen groups. Nitrogen adsorption, scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy (XPS) and batch adsorption were employed to investigate the effects of the two pre-pyrolysis modes on the sample physicochemical and Cu(II) adsorptive properties. The 22-min-microwave-pyrolyzed bagasse mesoporous activated carbon (MBAC, 85.32% mesoporosity) contained 10.52% O, which is 3.94% more than electric-heating pyrolyzed mesoporous activated carbon (89.52% mesoporosity). After electrophilic aromatic substitutions of N/O doping, the former possessed more N (5.83%) and more O (21.40%), confirming that time-saving energy-efficient microwave pyrolysis favors the formation of defective C/O atoms in or at the edges of the graphite layer of MBAC, which are highly active and tend to act as preferred reactive positions for the doping of N/O-containing groups simultaneously compared with conventional electric-heating pyrolysis. These N and O species existed mainly as COOH, OH, NH and NH functional groups, and were confirmed by XPS to be active sites for metal binding via electrostatic attraction, hydrogen bonding, a chelate effect and complexation, resulting in the great enhancement of Cu(II) adsorption. Langmuir isotherm and pseudo-second-order kinetic fitting further proved that Cu(II) adsorption by N/O-doped MBAC is ascribed mainly to chemisorption. Therefore, rapid microwave pre-pyrolysis provides a promising route to prepare excellent-performance N/O-doped carbon adsorbents.

Effect of pre-pyrolysis mode on simultaneous introduction of nitrogen/oxygen-containing functional groups into the structure of bagasse-based mesoporous carbon and its influence on Cu(II) adsorption.

Pure N mono- and N/P dual-doped cotton-stalk-derived activated carbon fibers (CSCFs) were synthesized by steam, HNO(CSCF-N), NH(CSCF-A), and (NH)PO(CSCF-N/P) treatments. This study investigated how three different N/P modifiers affected the pore structure, chemical property, HO generation ability, and electrocatalytic activity of methylene blue (MB) degradation of CSCFs in an electric-Fenton system. Results confirmed that the three employed treatments effectively doped N/P in the carbon lattice and slightly changed the pore structures. NH and (NH)PO were the most effective modifiers for the N mono-doping and N/P dual-doping of CSCFs, respectively. Among the fabricated CSCFs, the N/P dual-doped CSCF-N/P demonstrated the highest electrochemical activity in an electro-Fenton system, followed by the N mono-doped CSCF-A, the CSCF-N, and the raw CSCF. In contrast to the CSCF electrode, the CSCF-N/P electrode exhibited enhanced HO, OH generation, and MB degradation efficiency by 42%, 41%, and 35%, respectively. Under optimum conditions, the electrochemical decolorization efficiency of MB (initial concentration, 100 mg L) of the CSCF-N/P reached 93% after 150 min and was 24.1% higher than that of the CSCF. By the tenth cycle, 82.2% of the MB could still be decomposed, suggesting the excellent stability and reusability of the N/P co-doped CSCF electrode. The outstanding electrocatalytic performance of the CSCF-N/P electrode is primarily due to the simultaneous doping of active N/P sites with low activation energy and introduction of mesopores with strong trapping forces for MB. The MB reduction catalyzed by CSCF electrodes followed pseudo-first-order kinetics, and the reaction rate depended on the modifiers.

Zeqing Wan

College of Engineering

Nanjing Agricultural University

Preparation of Biomass-based Mesoporous Carbon with Higher Nitrogen-/Oxygen-chelating Adsorption for Cu(II) Through Microwave Pre-Pyrolysis

Zeqing Wan

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}College of Engineering

Nanjing Agricultural University

Preparation of Biomass-based Mesoporous Carbon with Higher Nitrogen-/Oxygen-chelating Adsorption for Cu(II) Through Microwave Pre-Pyrolysis

College of Engineering