micromechanical-tension-testing-additively-manufactured-17-4-ph

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

This study presents a methodology for the rapid fabrication and micro-tensile testing of additively manufactured (AM) 17-4PH stainless steels by combining ...

University of Arkansas

Six types of diamond-like carbon (DLC) coatings with zirconium (Zr)-containing interlayers on titanium alloy (Ti-6Al-4V) were investigated for improving the biotribological performance of orthopedic implants. The coatings consist of three layers: above the substrate a layer stack of 32 alternating Zr and ZrN sublayers (Zr:ZrN), followed by a layer comprised of Zr and DLC (Zr:DLC), and finally a N-doped DLC layer. The Zr:ZrN layer is designed for increasing load carrying capacity and corrosion resistance; the Zr:DLC layer is for gradual transition of stress, thus enhancing layer adhesion; and the N-doped DLC layer is for decreasing friction, squeaking noises and wear. Biotribological experiments were performed in simulated body fluid employing a ball-on-disc contact with a SiN ball and a rotational oscillating motion to mimic hip motion in terms of gait angle, dynamic contact pressures, speed and body temperature. The results showed that the Zr:DLC layer has a substantial influence on eliminating delamination of the DLC from the substrates. The DLC/SiN pairs significantly reduced friction coefficient, squeaking noise and wear of both the SiN balls and the discs compared to those of the Ti-6Al-4V/SiN pair after testing for a duration that is equivalent to one year of hip motion in vivo.

Diamond-like carbon coatings with zirconium-containing interlayers for orthopedic implants.

The number of revision joint replacements has been increasing substantially over the last few years. Understanding their failure mechanism is extremely important for improving the design and material selection of current implants. This study includes ten retrieved and four new mildly cross-linked ultra-high molecular weight polyethylene (UHMWPE) acetabular liners. Among them, most of the prostheses (n = 5) were reported to be revised and replaced due to aseptic loosening, followed by painful joint (n = 2), dislocation (n = 1), intra articular ossification (n = 1), combination of wear (liner) and osteolysis (stem) (n=1). Surface deviations (wear, material inflation and roughness), oxidative degradation and change of material properties were measured using micro-computed tomography (micro-CT) scan, 3D laser scanning microscopy, raman spectroscopy and nanoindentation, respectively. Prostheses having eccentric worn areas had much higher linear wear rates (228.01 ± 35.51µm/year) compared to that of centrically worn prostheses (96.71 ± 10.83µm/year). Oxidation index (OI) showed similar trends to the surface penetration depth. Among them, sample 10 exhibited the highest OI across the contact area and the rim of the cup liner. It also had the lowest hardness/elasticity ratio. Overall, wear and creep, oxidative degradation and reduced hardness/elasticity ratio all contributed to the premature failure of the UHMWPE acetabular cup liners.

Josh Goss

Department of Mechanical Engineering

University of Arkansas

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

Josh Goss

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Department of Mechanical Engineering

University of Arkansas

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

Department of Mechanical Engineering