The skeletal structure of polymers synthesized via radical polymerization is always branched. For example, the polymerization of ethylene by radical polymerization results in a low-density grade of polyethylene with a heavily branched skeletal structure. Here, the radical site abstracts hydrogen from the growing chain, and the radical site shifts from the end (a primary carbon center) to anywhere within the growing chain (a secondary carbon center). Consequently, the part of the chain from the abstraction site to the end of the chain becomes a branch.

In intermolecular hydrogen abstraction, the radical site abstracts hydrogen from another growing polymer chain and terminates its chain growth. A new branch grows in the other chain where the hydrogen was removed. Figure 1 demonstrates the intermolecular hydrogen abstraction and the consequent chain growth from the middle of the polymer chain.

Figure1

Figure 1: The intermolecular hydrogen abstraction (top) and the subsequent addition of the newly formed radical site to a monomer (bottom).

The radical site abstracts hydrogen from the same growing chain in intramolecular hydrogen abstraction. The length of the branch depends on the distance between the radical site and the abstraction site. Intramolecular 1,5-hydrogen abstraction frequently occurs due to the relatively stable six-membered transition state, resembling the chair conformation of cyclohexane. The resultant butyl branches are commonly found in branched polymers. Figure 2 shows the intramolecular hydrogen abstraction and the formation of the butyl branch.

Figure2

Figure 2: The intramolecular hydrogen abstraction (top) and subsequent addition of the newly formed radical site on a monomer (bottom).

In general, intramolecular hydrogen abstraction is more probable than intermolecular hydrogen abstraction. Also, short-chain branching is more common than long-chain branching, as the ends of the chains are more accessible.

Tagi
Radical PolymerizationChain BranchingLow density PolyethyleneHydrogen AbstractionIntermolecular Hydrogen AbstractionIntramolecular Hydrogen AbstractionPolymer ChainsSkeletal StructureButyl BranchesTransition StateCyclohexaneShort chain BranchingLong chain Branching

Z rozdziału 21:

article

Now Playing

21.10 : Radical Chain-Growth Polymerization: Chain Branching

Synthetic Polymers

1.8K Wyświetleń

article

21.1 : Charakterystyka i nomenklatura homopolimerów

Synthetic Polymers

2.8K Wyświetleń

article

21.2 : Charakterystyka i nomenklatura kopolimerów

Synthetic Polymers

2.3K Wyświetleń

article

21.3 : Polimery: definiowanie masy cząsteczkowej

Synthetic Polymers

2.6K Wyświetleń

article

21.4 : Polimery: rozkład masy cząsteczkowej

Synthetic Polymers

3.0K Wyświetleń

article

21.5 : Klasyfikacja polimerów: Architektura

Synthetic Polymers

2.5K Wyświetleń

article

21.6 : Klasyfikacja polimerów: Krystaliczność

Synthetic Polymers

2.7K Wyświetleń

article

21.7 : Klasyfikacja polimerów: Stereospecyficzność

Synthetic Polymers

2.3K Wyświetleń

article

21.8 : Polimeryzacja radykalnego wzrostu łańcucha: przegląd

Synthetic Polymers

2.2K Wyświetleń

article

21.9 : Polimeryzacja wzrostu łańcucha rodnikowego: mechanizm

Synthetic Polymers

2.3K Wyświetleń

article

21.11 : Polimeryzacja anionowa ze wzrostem łańcucha: przegląd

Synthetic Polymers

2.0K Wyświetleń

article

21.12 : Polimeryzacja wzrostu łańcucha anionowego: mechanizm

Synthetic Polymers

1.9K Wyświetleń

article

21.13 : Polimeryzacja wzrostu łańcucha kationowego: mechanizm

Synthetic Polymers

2.1K Wyświetleń

article

21.14 : Polimeryzacja wzrostu łańcucha Zieglera-Natty: przegląd

Synthetic Polymers

3.1K Wyświetleń

article

21.15 : Polimeryzacja krokowa: przegląd

Synthetic Polymers

3.3K Wyświetleń

See More

JoVE Logo

Prywatność

Warunki Korzystania

Zasady

Badania

Edukacja

O JoVE

Copyright © 2025 MyJoVE Corporation. Wszelkie prawa zastrzeżone