We acknowledge the Virginia Military Institute (VMI) Department of Chemistry for support of electrochemical experiments and instrumentation (L.S.C. and J.T.H.). The VMI Office of the Dean of Faculty supported production fees associated with JoVE publications. We acknowledge the UNC EFRC: Center for Solar Fuels, an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences under Award Number DE-SC0001011, for support of compound synthesis and materials characterization (D.P.H).

1. Synthesize 1
Synthesize&#160;1 (PhTpy is 4&#39;-phenyl-2,2&#39;:6&#39;,2&#39;&#39;-terpyridine; 5,5&#8217;-dvbpy is 5,5&#39;-divinyl-2,2&#39;-bipyridine; Figure 4) according to the procedure outlined previously.18
2. Prepare 1.3 mM Monomer Solution of 1 in an Electrolyte Solution
<ol>
	<li>Prepare a 0.1 M stock electrolyte solution of tetra-n-butylammonium hexafluorophosphate, TBAPF6, in acetonitrile, MeCN.
	<ol>
		<li>Place MeCN over activated 3 &#197; molecular sieves, or K2CO3, for 24 hr to remove adventitious H2O.</li>
		<li>Place TBAPF6 (0.969 g, 2.50 mmol) in a 25.00 ml flame dried volumetric flask.</li>
		<li>Filter the molecular sieve or K2CO3 particulates from the dried MeCN and bring the 25.00 ml volumetric flask containing TBAPF6 to volume.</li>
	</ol>
	</li>
	<li>Place 1 (0.0049 g, 5.2 x 10-6 mol) in and dry 4 dram vial or a 10 ml round bottom flask and add 4.00 ml of the stock solution of 0.1 M TBAPF6 in MeCN.</li>
	<li>Transfer 3.5-4.0 ml of the red-orange colored electrolytic solution of 1 into the central compartment of a 3-compartment cell, with each compartment separated by a medium porosity glass frit.</li>
	<li>Quickly fill the outer compartments of the 3-compartment cell to an equal height as the central compartment stock solution, with some of the remaining dry 0.1 M TBAPF6 in MeCN to prevent leakage to the outer compartments. Note: Time is an important factor because solutions in the different compartments will slowly mix and significantly change the concentration of the main compartment if the solvent heights are not the same.</li>
</ol>
3. Electropolymerize 1 on a 3 mm Diameter Glassy Carbon Electrode or a 1.0 cm2 FTO Electrode
<ol>
	<li>Prepare septa for nitrogen/argon degassing tubes and for electrodes.
	<ol>
		<li>Cut a slit into each of the 3 rubber septa and guide a thin polytetrafluoroethylene, PTFE, tube through the slit.</li>
		<li>Slide the Ag/AgNO3 reference electrode through one of the septa, place the reference electrode/PTFE tube/septum in one of the outer compartments, and seal the compartment with the septum.</li>
		<li>Guide the platinum wire/gauze counter electrode through a different septum place the platinum wire/PTFE tube/septum in one of the outer compartments, and seal the compartment with the septum. If the slit is not sufficiently large or wire sufficiently stiff to prevent bending the wire, use a wide bore needle to guide the platinum wire counter electrode through the septum.</li>
		<li>Guide a freshly polished 3 mm glassy carbon electrode through the remaining septum and place it such that the electrode is suspended in the solution or, for an FTO slide, guide a wire connected to an alligator clip through the septum, then clamp the FTO slide with the alligator clip and make sure that the conductive side of the slide is perpendicular to the counter electrode when submerged.
		<ol>
			<li>Prior to inserting the glassy carbon electrode: polish the glassy carbon by placing alumina (0.5 &#956;m) on a wetted polishing pad, then, move the electrode in a figure-8 motion for 30 sec while holding the electrode perpendicular to the pad &#8212; to polish all sides of the electrode evenly &#8212; and rinse any remaining alumina off with a H2O water squirt bottle followed by an MeCN squirt bottle rinse.</li>
			<li>Prior to clamping the FTO slide: wrap several layers of non-conductive Kapton tape around the center part of a 30 x 10 mm FTO slide such that a 10 x 10 mm portion of the slide is exposed.</li>
			<li>Collect a UV-Vis spectrum of the FTO slide by placing/holding the FTO slide in a position in the beam path of the spectrometer that has been predetermined to ensure consistency.</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>De-aerate the solutions in the 3-compartment electrochemical cell.
	<ol>
		<li>Connect one end of Tygon tubing to the nitrogen/argon supply and connect the other end to a gas washer containing MeCN.</li>
		<li>Cut another piece of Tygon tubing, connect one end to the outflowing MeCN washed nitrogen/argon, and connect the other end to a 4 way splitter.</li>
		<li>Connect the PTFE tubes to the 3 remaining connections of the 4 way splitter.</li>
		<li>Submerge the PTFE tubes into the solutions in each of the compartments and turn on the flow of nitrogen/argon such that a rapid bubbling of the solution commences.</li>
		<li>Continue de-aerating the solution for 5-10 min, then pull the PTFE tubes just above the surface of the solution, leaving the flow of nitrogen/argon on in order to keep a positive pressure of inert gas on the system and to prevent solution convection caused by bubbling.</li>
	</ol>
	</li>
	<li>Perform electrochemical experiments.
	<ol>
		<li>Connect electrodes from the potentiostat to the appropriate electrodes in the 3&#8209;compartment cell.</li>
		<li>Perform a cyclic voltammetry, CV, experiment with the following parameters: switching potentials = 0 V and -1.81 V; scan/sweep rate = 100 mV/sec; number of cycles = 5.</li>
		<li>When the CV experiment is complete, remove the working (glassy carbon or FTO) electrode from the polymerization solution and gently rinse the surface of the electrode with MeCN from a pipette or a squirt bottle to remove any remaining monomer solution.</li>
	</ol>
	</li>
</ol>
4. Surface Coverage Determination
<ol>
	<li>Place the rinsed working electrode in a freshly prepared solution of 0.1 M TBAPF6/MeCN in an electrochemical cell containing a counter electrode and a reference electrode (preferably the same reference electrode used in the electropolymerization).</li>
	<li>Perform a cyclic voltammetry, CV, experiment with the following parameters: switching potentials = 0 and +1.5 V; scan/sweep rate = 100 mV/sec; number of cycles = 15.</li>
	<li>Integrate the charge under the anodic and cathodic peaks for the adsorbed electropolymer Ru(III/II) couple, average the charge under the anodic and cathodic peaks, and using Equation 1 determine the surface coverage.</li>
	<li>For the FTO slide: place/hold the FTO slide in the predetermined position in front of the UV-Vis sample holder such that the beam-path passes through the colored film. The FTO slide can be wet or dry but make comparisons under the same conditions as the blank spectra was collected under.</li>
	<li>Subtract the spectrum obtained for the FTO spectrum that was collected for that particular slide prior to electropolymerization from the spectrum of the film-on-FTO in order to produce an absorption spectrum for the film itself.</li>
</ol>

<ol>
	<li>Abru&#241;a, H. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Coordination+chemistry+in+two+dimensions:+chemically+modified+electrodes.">Coordination chemistry in two dimensions: chemically modified electrodes.</a> Coordination Chemistry Reviews. 86, 135-189 (1988).</li><li>Waltman, R. J., Bargon, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrically+conducting+polymers:+a+review+of+the+electropolymerization+reaction,+of+the+effects+of+chemical+structure+on+polymer+film+properties,+and+of+applications+towards+technology.">Electrically conducting polymers: a review of the electropolymerization reaction, of the effects of chemical structure on polymer film properties, and of applications towards technology.</a> Canadian Journal of Chemistry. 64, 76-95 (1986).</li><li>Zhong, Y. -. W., Yao, C. -. J., Nie, H. -. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electropolymerized+films+of+vinyl-substituted+polypyridine+complexes:+Synthesis,+characterization,+and+applications.">Electropolymerized films of vinyl-substituted polypyridine complexes: Synthesis, characterization, and applications.</a> Coordination Chemistry Reviews. 257, 1357-1372 (2013).</li><li>Bard, A. J., Faulkner, L. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Electrochemical Methods Fundamentals and Applications. , (1980).</li><li>Ramos Sende, J. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrocatalysis+of+CO2+Reduction+in+Aqueous+Media+at+Electrodes+Modified+with+Electropolymerized+Films+of+Vinylterpyridine+Complexes+of+Transition+Metals.">Electrocatalysis of CO2 Reduction in Aqueous Media at Electrodes Modified with Electropolymerized Films of Vinylterpyridine Complexes of Transition Metals.</a> Inorganic Chemistry. 34, 3339-3348 (1995).</li><li>Cosnier, S., Deronzier, A., Moutet, J. -. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+coating+of+a+platinum+electrode+by+a+poly(pyrrole)+film+containing+the+fac-Re(2,2'-bipyridine)(CO)3Cl+system+application+to+electrocatalytic+reduction+of+CO2.">Electrochemical coating of a platinum electrode by a poly(pyrrole) film containing the fac-Re(2,2'-bipyridine)(CO)3Cl system application to electrocatalytic reduction of CO2.</a> Journal of Electroanalytical Chemistry and Interfacial Electrochemistry. 207, 315-321 (1986).</li><li>Cosnier, S., Deronzier, A., Moutet, J. -. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrocatalytic+reduction+of+CO2+on+electrodes+modified+by+fac-Re(2,2'-bipyridine)(CO)3Cl+complexes+bonded+to+polypyrrole+films.">Electrocatalytic reduction of CO2 on electrodes modified by fac-Re(2,2'-bipyridine)(CO)3Cl complexes bonded to polypyrrole films.</a> Journal of Molecular Catalysis. 45, 381-391 (1988).</li><li>Toole, T. R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrocatalytic+reduction+of+CO2+at+a+chemically+modified+electrode.">Electrocatalytic reduction of CO2 at a chemically modified electrode.</a> Journal of the Chemical Society, Chemical Communications. 20, 1416-1417 (1985).</li><li>Cheung, K. -. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ruthenium+Terpyridine+Complexes+Containing+a+Pyrrole-Tagged+2,2&#8242;-Dipyridylamine+Ligand&#8212;Synthesis.">Ruthenium Terpyridine Complexes Containing a Pyrrole-Tagged 2,2&#8242;-Dipyridylamine Ligand&#8212;Synthesis.</a> Crystal Structure, and Electrochemistry. Inorganic Chemistry. 51, 6468-6475 (2012).</li><li>Ashford, D. L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Water+Oxidation+by+an+Electropolymerized+Catalyst+on+Derivatized+Mesoporous+Metal+Oxide+Electrodes.">Water Oxidation by an Electropolymerized Catalyst on Derivatized Mesoporous Metal Oxide Electrodes.</a> Journal of the American Chemical Society. 136, 6578-6581 (2014).</li><li>Abru&#241;a, H. D., Denisevich, P., Umana, M., Meyer, T. J., Murray, R. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Rectifying+interfaces+using+two-layer+films+of+electrochemically+polymerized+vinylpyridine+and+vinylbipyridine+complexes+of+ruthenium+and+iron+on+electrodes.">Rectifying interfaces using two-layer films of electrochemically polymerized vinylpyridine and vinylbipyridine complexes of ruthenium and iron on electrodes.</a> Journal of the American Chemical Society. 103, 1-5 (1981).</li><li>Gould, S., Gray, K. H., Linton, R. W., Meyer, T. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microstructures+in+thin+polymeric+films.+Photochemically+produced+molecular+voids.">Microstructures in thin polymeric films. Photochemically produced molecular voids.</a> Inorganic Chemistry. 31, 5521-5525 (1992).</li><li>Devenney, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Excited+State+Interactions+in+Electropolymerized+Thin+Films+of+Ru(II).">Excited State Interactions in Electropolymerized Thin Films of Ru(II).</a> Os(II), and Zn(II) Polypyridyl Complexes. The Journal of Physical Chemistry A. 101, 4535-4540 (1997).</li><li>Moss, J. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Sensitization+and+Stabilization+of+TiO2+Photoanodes+with+Electropolymerized+Overlayer+Films+of+Ruthenium+and+Zinc+Polypyridyl+Complexes:+A+Stable+Aqueous+Photoelectrochemical+Cell.">Sensitization and Stabilization of TiO2 Photoanodes with Electropolymerized Overlayer Films of Ruthenium and Zinc Polypyridyl Complexes: A Stable Aqueous Photoelectrochemical Cell.</a> Inorganic Chemistry. 43, 1784-1792 (2004).</li><li>Yang, J., Sykora, M., Meyer, T. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Electropolymerization of Vinylbipyridine Complexes of Ruthenium(II) and Osmium(II) in SiO2 Sol&#8722;Gel Films. Inorganic Chemistry. 44, 3396-3404 (2005).</li><li>Nie, H. -. J., Shao, J. -. Y., Wu, J., Yao, J., Zhong, Y. -. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+Reductive+Electropolymerization+of+Metal+Complexes+with+5,5&#8242;-Divinyl-2,2&#8242;-Bipyridine.">Synthesis and Reductive Electropolymerization of Metal Complexes with 5,5&#8242;-Divinyl-2,2&#8242;-Bipyridine.</a> Organometallics. 31, 6952-6959 (2012).</li><li>Yao, C. -. J., Zhong, Y. -. W., Nie, H. -. J., Abru&#241;a, H. D., Yao, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Near-IR+Electrochromism+in+Electropolymerized+Films+of+a+Biscyclometalated+Ruthenium+Complex+Bridged+by+1,2,4,5-Tetra(2-pyridyl)benzene.">Near-IR Electrochromism in Electropolymerized Films of a Biscyclometalated Ruthenium Complex Bridged by 1,2,4,5-Tetra(2-pyridyl)benzene.</a> Journal of the American Chemical Society. 133, 20720-20723 (2011).</li><li>Harrison, D. P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Coordination+Chemistry+of+Single-Site+Catalyst+Precursors+in+Reductively+Electropolymerized+Vinylbipyridine+Films.">Coordination Chemistry of Single-Site Catalyst Precursors in Reductively Electropolymerized Vinylbipyridine Films.</a> Inorganic Chemistry. 52, 4747-4749 (2013).</li><li>Calvert, J. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthetic+and+mechanistic+investigations+of+the+reductive+electrochemical+polymerization+of+vinyl-containing+complexes+of+iron(II),+ruthenium(II),+and+osmium(II).">Synthetic and mechanistic investigations of the reductive electrochemical polymerization of vinyl-containing complexes of iron(II), ruthenium(II), and osmium(II).</a> Inorganic Chemistry. 22, 2151-2162 (1983).</li><li>Moss, J. A., Argazzi, R., Bignozzi, C. A., Meyer, T. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electropolymerization+of+Molecular+Assemblies.">Electropolymerization of Molecular Assemblies.</a> Inorganic Chemistry. 36, 762-763 (1997).</li><li>Deronzier, A., Eloy, D., Jardon, P., Martre, A., Moutet, J. -. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electroreductive+coating+of+electrodes+from+soluble+polypyrrole-ruthenium+(II)+complexes:+ion+modulation+effects+on+their+electroactivity.">Electroreductive coating of electrodes from soluble polypyrrole-ruthenium (II) complexes: ion modulation effects on their electroactivity.</a> Journal of Electroanalytical Chemistry. 453, 179-185 (1998).</li><li>Mola, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ru-Hbpp-Based+Water-Oxidation+Catalysts+Anchored+on+Conducting+Solid+Supports.">Ru-Hbpp-Based Water-Oxidation Catalysts Anchored on Conducting Solid Supports.</a> Angewandte Chemie International Edition. 47, 5830-5832 (2008).</li><li>Deronzier, A., Moutet, J. -. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polypyrrole+films+containing+metal+complexes:+syntheses+and+applications.">Polypyrrole films containing metal complexes: syntheses and applications.</a> Coordination Chemistry Reviews. 147, 339-371 (1996).</li><li>Sabouraud, G., Sadki, S., Brodie, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+mechanisms+of+pyrrole+electropolymerization.">The mechanisms of pyrrole electropolymerization.</a> Chemical Society Review. 29, 283-293 (2000).</li><li>Denisevich, P., Abru&#241;a, H. D., Leidner, C. R., Meyer, T. J., Murray, R. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electropolymerization+of+vinylpyridine+and+vinylbipyridine+complexes+of+iron+and+ruthenium:+homopolymers,+copolymers,+reactive+polymers.">Electropolymerization of vinylpyridine and vinylbipyridine complexes of iron and ruthenium: homopolymers, copolymers, reactive polymers.</a> Inorganic Chemistry. 21, 2153-2161 (1982).</li><li>Younathan, J. N., Wood, K. S., Meyer, T. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrocatalytic+reduction+of+nitrite+and+nitrosyl+by+iron(III)+protoporphyrin+IX+dimethyl+ester+immobilized+in+an+electropolymerized+film.">Electrocatalytic reduction of nitrite and nitrosyl by iron(III) protoporphyrin IX dimethyl ester immobilized in an electropolymerized film.</a> Inorganic Chemistry. 31, 3280-3285 (1992).</li><li>Ikeda, T., Schmehl, R., Denisevich, P., Willman, K., Murray, R. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Permeation+of+electroactive+solutes+through+ultrathin+polymeric+films+on+electrode+surfaces.">Permeation of electroactive solutes through ultrathin polymeric films on electrode surfaces.</a> Journal of the American Chemical Society. 104, 2683-2691 (1982).</li><li>Concepcion, J. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Making+Oxygen+with+Ruthenium+Complexes.">Making Oxygen with Ruthenium Complexes.</a> Accounts of Chemical Research. 42, 1954-1965 (2009).</li><li>Chen, Z., Concepcion, J. J., Jurss, J. W., Meyer, T. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Single-Site,+Catalytic+Water+Oxidation+on+Oxide+Surfaces.">Single-Site, Catalytic Water Oxidation on Oxide Surfaces.</a> Journal of the American Chemical Society. 131, 15580-15581 (2009).</li><li>Lapides, A. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stabilization+of+a+Ruthenium(II)+Polypyridyl+Dye+on+Nanocrystalline+TiO2+by+an+Electropolymerized+Overlayer.">Stabilization of a Ruthenium(II) Polypyridyl Dye on Nanocrystalline TiO2 by an Electropolymerized Overlayer.</a> Journal of the American Chemical Society. 135, 15450-15458 (2013).</li><li>Paulson, S. C., Sapp, S. A., Elliott, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+and+Spectroelectrochemical+Investigations+into+the+Nature+of+Charge-Trapping+in+Electrochemically-Generated+Homopolymer+Films+of+Tris(4-vinyl-4&#8216;-methyl-2,2&#8216;-bipyridine)ruthenium(II).">Electrochemical and Spectroelectrochemical Investigations into the Nature of Charge-Trapping in Electrochemically-Generated Homopolymer Films of Tris(4-vinyl-4&#8216;-methyl-2,2&#8216;-bipyridine)ruthenium(II).</a> The Journal of Physical Chemistry B. 105, 8718-8724 (2001).</li><li>Laviron, E., Roullier, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=General+expression+of+the+linear+potential+sweep+voltammogram+for+a+surface+redox+reaction+with+interactions+between+the+adsorbed+molecules:+Applications+to+modified+electrodes.">General expression of the linear potential sweep voltammogram for a surface redox reaction with interactions between the adsorbed molecules: Applications to modified electrodes.</a> J. Electroanal. Chem. Interfacial Electrochem. 115, 65-74 (1980).</li><li>Laviron, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=General+expression+of+the+linear+potential+sweep+voltammogram+in+the+case+of+diffusionless+electrochemical+systems.">General expression of the linear potential sweep voltammogram in the case of diffusionless electrochemical systems.</a> J. Electroanal. Chem. 101, 19-28 (1979).</li><li>Ratcliff, E. L., Jenkins, J. L., Nebesny, K., Armstrong, N. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrodeposited,+&#34;Textured&#34;+Poly(3-hexyl-thiophene)+(e-P3HT)+Films+for+Photovoltaic+Applications.">Electrodeposited, &#34;Textured&#34; Poly(3-hexyl-thiophene) (e-P3HT) Films for Photovoltaic Applications.</a> Chemistry of Materials. 20, 5796-5806 (2008).</li></ol>

No conflicts of interest declared.

Electropolymerization offers a large range of controllable variables that are not common to other techniques. In addition to standard reaction variables like reagent (monomer) concentration, temperature, solvent, etc., electropolymerization can be additionally controlled by electrochemical experiment parameters common to electrochemical methods. CV scan rates, switching potentials, and number of cycles affect the deposition of electropolymers. For example, as the number of cycles through the ligand reduction wav...

Electropolymerization is a polymerization technique that utilizes an applied potential to initiate the polymerization of monomeric precursors directly at the surface of an electrode and has been exploited to produce thin electroactive and/or photochemically active polypyridyl films on electrode and semiconductor surfaces.1-4 Electrocatalysis,5-10 electron transfer,11,12 photochemistry,13-16 electrochromism,17 and coordination chemistry18 have been investigated in electropolymerized films. This technique was first developed at the University of North Carolina in a Meyer-Murray collaboration for the electropolymerization of vinyl3,5,7,8,11-15,19,20 and pyrrole6,9,21-24 derivatized metal complexes on a variety of conducting substrates. Figure 1 presents a number of common pyridyl based ligands that, when coordinated to metal complexes, have produced electropolymers. In reductive electropolymerization, electropolymerization of vinyl containing compounds occurs upon the reduction of pyridyl ligands conjugated to vinyl groups, while with pyrrole-functionalized ligands, electropolymerization is initiated by oxidation of the pyrrole moieties, resulting in oxidative electropolymerization (Figure 2). Electropolymerization technology was developed with the goal of providing a generalized methodology for directly attaching virtually any transition metal complex to any electrode. The versatility of the method opens the door to numerous investigations of electropolymer modified electrodes.
In contrast to other attachment strategies, which involve direct bonding to the electrode, electropolymerization offers the advantage of not requiring electrode surface pre-modification. Therefore it can be applied to any number of conducting substrates, regardless of surface composition or morphology.4,10,25,26 This versatility is a result of changing physical properties as the polymer length grows; the monomers are soluble in the electrolytic solution but as polymerization occurs and cross-linking rigidifies the film, precipitation and physical adsorption the electrode surface occurs (Figure 3).27
Compared to oxide surface-bound carboxylate, which are unstable on oxide surfaces in water, or phosphonate-derivatized complexes, which are unstable at elevated pH&#39;s, commonly used in solar fuels research, these interfacial electrode-polymer film structures offer the added benefit of stability in a variety of media including organic solvents and water over a large pH range (0-14).28-30 Electropolymerization can also deposit films with large ranges of apparent surface coverages, from sub-monolayer to dozens or hundreds of equivalents monolayer, whereas carboxylate or phosphonate-derivatized complexes-interface structures are limited to monolayer surface coverages.
Although any number of vinyl or pyrrole containing pyridyl and polypyridyl compounds are capable of polymerization, [RuII(PhTpy)(5,5&#8217;-dvbpy)(MeCN)](PF6)2, (1; PhTpy is 4&#39;-phenyl-2,2&#39;:6&#39;,2&#39;&#39;-terpyridine; 5,5&#8217;-dvbpy is 5,5&#39;-divinyl-2,2&#39;-bipyridine; Figure 4) will be utilized as a model complex to demonstrate reductive electropolymerization on glassy carbon and fluorine-doped tin oxide, FTO, electrodes in this report. 1 is an example of a modern electropolymer precursor that has potential electrocatalytic applications and, due to its metal-to-ligand charge transfer, MLCT, absorption spectrum lying in the visible region of the light spectrum, can be investigated with UV-Vis spectroscopy.18,30 Please note that some results presented here for 1 have already been published in a slightly modified form.18

<table border="0" cellpadding="0" cellspacing="0" width="652">
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:384px;">Name of Reagent/ Equipment</td>
			<td style="width:108px;">Company</td>
			<td style="width:160px;">Catalog Number</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">Tetrabutylammonium hexafluorophosphate for electrochemical analysis, &#8805;99.0%,&#160;</td>
			<td>Sigma-Aldrich</td>
			<td>86879-25G</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;width:384px;">Acetonitrile&#160;(Optima LC/MS), Fisher Chemical</td>
			<td>Fisher Scientific</td>
			<td>A955-4</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">3 mm dia. Glassy Carbon Working Electrode</td>
			<td>CH Instruments</td>
			<td>CH104</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">Non-Aqueous Ag/Ag+ Reference Electrode w/ porous Teflon Tip</td>
			<td>CH Instruments</td>
			<td>CHI112</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">Platinum&#160;gauze</td>
			<td>Alfa Aesar</td>
			<td>AA10282FF&#160;</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">Electrode Polishing Kit</td>
			<td>CH Instruments</td>
			<td>CHI120</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;width:384px;">Cole-Parmer KAPTON TAPE&#160;1/2IN X 36 YD</td>
			<td>Fisher Scientific</td>
			<td>NC0099200</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;width:384px;">Fisherbrand Polypropylene Tubing&#160;4-Way&#160;Connectors</td>
			<td>Fisher Scientific</td>
			<td>15-315-32B</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">500mL Bottle, Gas Washing, Tall Form, Coarse Frit</td>
			<td>Chemglass</td>
			<td>CG-1114-15</td>
		</tr>
		<tr height="20">
			<td height="20" style="height:20px;">3 compartment H-Cell for electrochemistry</td>
			<td colspan="2">Custom made H-cell with 3 compartments</td>
		</tr>
	</tbody>
</table>

reductive electropolymerization of a vinyl-containing poly-pyridyl complex on glassy carbon and fluorine-doped tin oxide electrodes

Controllable electrode surface modification is important in a number of fields, especially those with solar fuels applications. Electropolymerization is one surface modification technique that electrodeposits a polymeric film at the surface of an electrode by utilizing an applied potential to initiate the polymerization of substrates in the Helmholtz layer. This useful technique was first established by a Murray-Meyer collaboration at the University of North Carolina at Chapel Hill in the early 1980s and utilized to study numerous physical phenomena of films containing inorganic complexes as the monomeric substrate. Here, we highlight a procedure for coating electrodes with an inorganic complex by performing reductive electropolymerization of the vinyl-containing poly-pyridyl complex onto glassy carbon and fluorine doped tin oxide coated electrodes. Recommendations on electrochemical cell configurations and troubleshooting procedures are included. Although not explicitly described here, oxidative electropolymerization of pyrrole-containing compounds follows similar procedures to vinyl-based reductive electropolymerization but are far less sensitive to oxygen and water.

Electropolymer growth is most easily recognized when observing the progress of the prescribed CV experiment (Protocol Text STEP 3.3.2). Figure 5 exemplifies electropolymer growth on a 0.071 cm2 (3 mm diameter) glassy carbon electrode with 1. The first cycle of the experiment produces a voltammogram roughly resembling that which is expected for a ruthenium solution of similar concentration (Figure 5, black trace) but upon successive cycles, through the 1st...

Watch this Scientific Journal Video about Reductive Electropolymerization of a Vinyl-containing Poly-pyridyl Complex on Glassy Carbon and Fluorine-doped Tin Oxide Electrodes at JoVE.com

Reductive Electropolymerization of a Vinyl-containing Poly-pyridyl Complex on Glassy Carbon and Fluorine-doped Tin Oxide Electrodes

A procedure for performing reductive electropolymerization of vinyl-containing compounds onto glassy carbon and fluorine doped tin-oxide coated electrodes is presented. Recommendations on electrochemical cell configurations and troubleshooting procedures are included. Although not explicitly described here, oxidative electropolymerization of pyrrole-containing compounds follows similar procedures to vinyl-based reductive electropolymerization.

Controllable electrode surface modification is important in a number of fields, especially those with solar fuels applications. Electropolymerization is ...

reductive-electropolymerization-vinyl-containing-poly-pyridyl-complex

Research

JoVE Journal

Chemistry

11.8K Views.  Virginia Military Institute. A procedure for performing reductive electropolymerization of vinyl-containing compounds onto glassy carbon and fluorine doped tin-oxide coated electrodes is presented. Recommendations on electrochemical cell configurations and troubleshooting procedures are included. Although not explicitly described here, oxidative electropolymerization of pyrrole-containing compounds follows similar procedures to vinyl-based reductive electropolymerization. 

Video: Reductive Electropolymerization of a Vinyl-containing Poly-pyridyl Complex on Glassy Carbon and Fluorine-doped Tin Oxide Electrodes

Improved In-gel Reductive &#946;-Elimination for Comprehensive O-linked and Sulfo-glycomics by Mass Spectrometry

Separation of proteins by SDS-PAGE followed by in-gel proteolytic digestion of resolved protein bands has produced high-resolution proteomic analysis of biological samples. Similar approaches, that would allow in-depth analysis of the glycans carried by glycoproteins resolved by SDS-PAGE, require special considerations in order to maximize recovery and sensitivity when using mass spectrometry (MS) as the detection method. A major hurdle to be overcome in achieving high-quality data is the removal of gel-derived contaminants that interfere with MS analysis. The sample workflow presented here is robust, efficient, and eliminates the need for in-line HPLC clean-up prior to MS. Gel pieces containing target proteins are washed in acetonitrile, water, and ethyl acetate to remove contaminants, including polymeric acrylamide fragments. O-linked glycans are released from target proteins by in-gel reductive &#946;-elimination and recovered through robust, simple clean-up procedures. An advantage of this workflow is that it improves sensitivity for detecting and characterizing sulfated glycans. These procedures produce an efficient separation of sulfated permethylated glycans from non-sulfated (sialylated and neutral) permethylated glycans by a rapid phase-partition prior to MS analysis, and thereby enhance glycomic and sulfoglycomic analyses of glycoproteins resolved by SDS-PAGE.

In order to comprehensively explore the diversity of O-linked glycans, a new procedure for in-gel reductive &#946;-elimination, combined with permethylation and a rapid phase-partition method, is applied to the analysis of O-linked glycans directly released from glycoproteins resolved by SDS-PAGE and amenable to subsequent glycomic analysis by mass spectrometry.

Separation of proteins by SDS-PAGE followed by in-gel proteolytic digestion of resolved protein bands has produced high-resolution proteomic analysis of ...

Atomically Defined Templates for Epitaxial Growth of Complex Oxide Thin Films

Atomically defined substrate surfaces are prerequisite for the epitaxial growth of complex oxide thin films. In this protocol, two approaches to obtain such surfaces are described. The first approach is the preparation of single terminated perovskite SrTiO3 (001) and DyScO3 (110) substrates. Wet etching was used to selectively remove one of the two possible surface terminations, while an annealing step was used to increase the smoothness of the surface. The resulting single terminated surfaces allow for the heteroepitaxial growth of perovskite oxide thin films with high crystalline quality and well-defined interfaces between substrate and film. In the second approach, seed layers for epitaxial film growth on arbitrary substrates were created by Langmuir-Blodgett (LB) deposition of nanosheets. As model system Ca2Nb3O10- nanosheets were used, prepared by delamination of their layered parent compound HCa2Nb3O10. A key advantage of creating seed layers with nanosheets is that relatively expensive and size-limited single crystalline substrates can be replaced by virtually any substrate material.

Various procedures are outlined to prepare atomically defined templates for epitaxial growth of complex oxide thin films. Chemical treatments of single crystalline SrTiO3 (001) and DyScO3 (110) substrates were performed to obtain atomically smooth, single terminated surfaces. Ca2 Nb3 O10- nanosheets were used to create atomically defined templates on arbitrary substrates.

Atomically defined substrate surfaces are prerequisite for the epitaxial growth of complex oxide thin films. In this protocol, two approaches to obtain ...

Transport of Surface-modified Carbon Nanotubes through a Soil Column

Carbon nanotubes (CNTs) are widely manufactured nanoparticles, which are being utilized in a number of consumer products, such as sporting goods, electronics and biomedical applications. Due to their accelerating production and use, CNTs constitute a potential environmental risk if they are released to soil and groundwater systems. It is therefore essential to improve the current understanding of environmental fate and transport of CNTs. The transport and retention of CNTs in both natural and artificial media have been reported in literature, but the findings widely vary and are thus not conclusive. There are a number of physical and chemical parameters responsible for variation in retention and transport. In this study, a complete procedure of selected multiwalled carbon nanotubes (MWCNTs) is presented starting from their surface modification to a complete set of laboratory column experiments at critical physical and chemical scenarios. Results indicate that the stability of the commercially available MWCNTs are critical with their attached surface functional group which can also influence the transport and retention of MWCNT through the surrounding medium.

Surface properties of a nanoparticle are important for their interaction with the surrounding medium. Therefore the surface modification of carbon nanotubes can be critical for their transport and retention through porous media. Here, lab scale column experiments are used to understand the possible transport and retention of these nanoparticles.

Carbon nanotubes (CNTs) are widely manufactured nanoparticles, which are being utilized in a number of consumer products, such as sporting goods, ...

Preparation of Carbon Nanosheets at Room Temperature

Amphiphilic molecules equipped with a reactive, carbon-rich "oligoyne" segment consisting of conjugated carbon-carbon triple bonds self-assemble into defined aggregates in aqueous media and at the air-water interface. In the aggregated state, the oligoynes can then be carbonized under mild conditions while preserving the morphology and the embedded chemical functionalization. This novel approach provides direct access to functionalized carbon nanomaterials. In this article, we present a synthetic approach that allows us to prepare hexayne carboxylate amphiphiles as carbon-rich siblings of typical fatty acid esters through a series of repeated bromination and Negishi-type cross-coupling reactions. The obtained compounds are designed to self-assemble into monolayers at the air-water interface, and we show how this can be achieved in a Langmuir trough. Thus, compression of the molecules at the air-water interface triggers the film formation and leads to a densely packed layer of the molecules. The complete carbonization of the films at the air-water interface is then accomplished by cross-linking of the hexayne layer at room temperature, using UV irradiation as a mild external stimulus. The changes in the layer during this process can be monitored with the help of infrared reflection-absorption spectroscopy and Brewster angle microscopy. Moreover, a transfer of the carbonized films onto solid substrates by the Langmuir-Blodgett technique has enabled us to prove that they were carbon nanosheets with lateral dimensions on the order of centimeters.

We present the synthesis of an amphiphilic hexayne and its use in the preparation of carbon nanosheets at the air-water interface from a self-assembled monolayer of these reactive, carbon-rich molecular precursors.

Amphiphilic molecules equipped with a reactive, carbon-rich "oligoyne" segment consisting of conjugated carbon-carbon triple bonds self-assemble into ...

Photochemical Oxidative Growth of Iridium Oxide Nanoparticles on CdSe@CdS Nanorods

We demonstrate a procedure for the photochemical oxidative growth of iridium oxide catalysts on the surface of seeded cadmium selenide-cadmium sulfide (CdSe@CdS) nanorod photocatalysts. Seeded rods are grown using a colloidal hot-injection method and then moved to an aqueous medium by ligand exchange. CdSe@CdS nanorods, an iridium precursor and other salts are mixed and illuminated. The deposition process is initiated by absorption of photons by the semiconductor particle, which results with formation of charge carriers that are used to promote redox reactions. To insure photochemical oxidative growth we used an electron scavenger. The photogenerated holes oxidize the iridium precursor, apparently in a mediated oxidative pathway. This results in the growth of high quality crystalline iridium oxide particles, ranging from 0.5 nm to about 3 nm, along the surface of the rod. Iridium oxide grown on CdSe@CdS heterostructures was studied by a variety of characterization methods, in order to evaluate its characteristics and quality. We explored means for control over particle size, crystallinity, deposition location on the CdS rod, and composition. Illumination time and excitation wavelength were found to be key parameters for such control. The influence of different growth conditions and the characterization of these heterostructures are described alongside a detailed description of their synthesis. Of significance is the fact that the addition of iridium oxide afforded the rods astounding photochemical stability under prolonged illumination in pure water (alleviating the requirement for hole scavengers).

A protocol for the photochemical oxidative growth of small crystalline iridium oxide nanoparticles on the surface of CdSe@CdS seeded rod nanoparticles is presented.

We demonstrate a procedure for the photochemical oxidative growth of iridium oxide catalysts on the surface of seeded cadmium selenide-cadmium sulfide ...

On-line Analysis of Nitrogen Containing Compounds in Complex Hydrocarbon Matrixes

The shift to heavy crude oils and the use of alternative fossil resources such as shale oil are a challenge for the petrochemical industry. The composition of heavy crude oils and shale oils varies substantially depending on the origin of the mixture. In particular they contain an increased amount of nitrogen containing compounds compared to the conventionally used sweet crude oils. As nitrogen compounds have an influence on the operation of thermal processes occurring in coker units and steam crackers, and as some species are considered as environmentally hazardous, a detailed analysis of the reactions involving nitrogen containing compounds under pyrolysis conditions provides valuable information. Therefore a novel method has been developed and validated with a feedstock containing a high nitrogen content, i.e., a shale oil. First, the feed was characterized offline by comprehensive two-dimensional gas chromatography (GC &#215; GC) coupled with a nitrogen chemiluminescence detector (NCD). In a second step the on-line analysis method was developed and tested on a steam cracking pilot plant by feeding pyridine dissolved in heptane. The former being a representative compound for one of the most abundant classes of compounds present in shale oil. The composition of the reactor effluent was determined via an in-house developed automated sampling system followed by immediate injection of the sample on a GC &#215; GC coupled with a time-of-flight mass spectrometer (TOF-MS), flame ionization detector (FID) and NCD. A novel method for quantitative analysis of nitrogen containing compounds using NCD and 2-chloropyridine as an internal standard has been developed and demonstrated.

A method combining comprehensive two-dimensional gas chromatography with nitrogen chemiluminescence detection has been developed and applied to on-line analysis of nitrogen containing compounds in a complex hydrocarbon matrix.

The shift to heavy crude oils and the use of alternative fossil resources such as shale oil are a challenge for the petrochemical industry. The ...

Investigations on the Ga(III) Complex of EOB-DTPA and Its 68Ga Radiolabeled Analogue

We demonstrate a method for the isolation of EOB-DTPA (3,6,9-triaza-3,6,9-tris(carboxymethyl)-4-(ethoxybenzyl)-undecanedioic acid) from its Gd(III) complex and protocols for the preparation of its novel non-radioactive, i.e., natural Ga(III) as well as radioactive 68Ga complex. The ligand as well as the Ga(III) complex were characterized by nuclear magnetic resonance (NMR) spectroscopy, mass spectrometry and elemental analysis. 68Ga was obtained by a standard elution method from a 68Ge/68Ga generator. Experiments to evaluate the 68Ga-labeling efficiency of EOB-DTPA at pH 3.8&#8211;4.0 were performed. Established analysis techniques radio TLC (thin layer chromatography) and radio HPLC (high performance liquid chromatography) were used to determine the radiochemical purity of the tracer. As a first investigation of the 68Ga tracers&#39; lipophilicity the n-octanol/water distribution coefficient of 68Ga species present in a pH 7.4 solution was determined by an extraction method. In vitro stability measurements of the tracer in various media at physiological pH were performed, revealing different rates of decomposition.

Investigations on the GaIII Complex of EOB-DTPA and Its 68Ga Radiolabeled Analogue

A procedure for the isolation of EOB-DTPA and subsequent complexation with natural Ga(III) and 68Ga is presented herein, as well as a thorough analysis of all compounds and investigations on labeling efficiency, in vitro stability and the n-octanol/water distribution coefficient of the radiolabeled complex.

We demonstrate a method for the isolation of EOB-DTPA (3,6,9-triaza-3,6,9-tris(carboxymethyl)-4-(ethoxybenzyl)-undecanedioic acid) from its Gd(III) ...

Grafting Multiwalled Carbon Nanotubes with Polystyrene to Enable Self-Assembly and Anisotropic Patchiness

We demonstrate a straightforward protocol to graft pristine multiwalled carbon nanotubes (MWCNTs) with polystyrene (PS) chains at the sidewalls through a free-radical polymerization strategy to enable the modulation of the nanotube surface properties and produce supramolecular self-assembly of the nanostructures. First, a selective hydroxylation of the pristine nanotubes through a biphasic catalytically mediated oxidation reaction creates superficially distributed reactive sites at the sidewalls. The latter reactive sites are subsequently modified with methacrylic moieties using a silylated methacrylic precursor to create polymerizable sites. Those polymerizable groups can address further polymerization of styrene to produce a hybrid nanomaterial containing PS chains grafted to the nanotube sidewalls. The polymer-graft content, amount of silylated methacrylic moieties introduced and hydroxylation modification of the nanotubes are identified and quantified by Thermogravimetric Analysis (TGA). The presence of reactive functional groups hydroxyl and silylated methacrylate are confirmed by Fourier Transform Infrared Spectroscopy (FT-IR). Polystyrene-grafted carbon nanotube solutions in tetrahydrofuran (THF) provide wall-to-wall collinearly self-assembled nanotubes when cast samples are analyzed by transmission electron microscopy (TEM). Those self-assemblies are not obtained when suitable blanks are similarly cast from analogous solutions containing non-grafted counterparts. Therefore, this method enables the modification of the nanotube anisotropic patchiness at the sidewalls which results into spontaneous auto-organization at the nanoscale.

A procedure for the synthesis of polystyrene-grafted multiwalled carbon nanotubes using successive chemical modification steps to selectively introduce the polymer chains to the sidewalls and their self-assembly via anisotropic patchiness is presented.

We demonstrate a straightforward protocol to graft pristine multiwalled carbon nanotubes (MWCNTs) with polystyrene (PS) chains at the sidewalls through a ...

Electrochemical Impedance Spectroscopy as a Tool for Electrochemical Rate Constant Estimation

Electrochemical impedance spectroscopy (EIS) was used for advanced characterization of organic electroactive compounds along with cyclic voltammetry (CV). In the case of fast reversible electrochemical processes, current is predominantly affected by the rate of diffusion, which is the slowest and limiting stage. EIS is a powerful technique that allows separate analysis of stages of charge transfer that have different AC frequency response. The capability of the method was used to extract the value of charge transfer resistance, which characterizes the rate of charge exchange on the electrode-solution interface. The application of this technique is broad, from biochemistry up to organic electronics. In this work, we are presenting the method of analysis of organic compounds for optoelectronic applications.

Electrochemical impedance spectroscopy (EIS) of species that undergo reversible oxidation or reduction in solution was used for determination of rate constants of oxidation or reduction.

Electrochemical impedance spectroscopy (EIS) was used for advanced characterization of organic electroactive compounds along with cyclic voltammetry (CV). ...

Solvothermal Synthesis of MIL-96 and UiO-66-NH2 on Atomic Layer Deposited Metal Oxide Coatings on Fiber Mats

Metal-organic frameworks (MOFs), which contain reactive metal clusters and organic ligands allowing for large porosities and surface areas, have proven effective in gas adsorption, separations, and catalysis. MOFs are most commonly synthesized as bulk powder, requiring additional processes to adhere them to functional devices and fabrics that risk decreasing the powder porosity and adsorption capacity. Here, we demonstrate a method of first coating fabrics with metal oxide films using atomic layer deposition (ALD). This process creates conformal films of controllable thickness on each fiber, while providing a more reactive surface for MOF nucleation. By submerging the ALD coated fabric in solution during solvothermal MOF synthesis, the MOFs create a conformal, well-adhered coating on the fibers, resulting in a MOF-functionalized fabric, without additional adhesion materials that may block MOF pores and functional sites. Here we demonstrate two solvothermal synthesis methods. First, we form a MIL-96(Al) layer on polypropylene fibers using synthetic conditions that convert the metal oxide to MOF. Using initial inorganic films of varying thicknesses, diffusion of the organic linker into the inorganic allows us to control the extent of MOF loading on the fabric. Second, we perform a solvothermal synthesis of UiO-66-NH2 in which the MOF nucleates on the conformal metal oxide coating on polyamide-6 (PA-6) fibers, thereby producing a uniform and conformal thin film of MOF on the fabric. The resulting materials can be directly incorporated into filter devices or protective clothing and eliminate the maladroit qualities of loose powder.

Solvothermal Synthesis of MIL-96 and UiO-66-NH2 on Atomic Layer Deposited Metal Oxide Coatings on Fiber Mats

Metal-organic frameworks are effective in gas storage and heterogeneous catalysis, but typical synthesis methods result in loose powders that are difficult to incorporate into smart materials. We demonstrate a method of first coating fabrics with ALD metal oxides, resulting in conformal films of MOF on the fabrics during solvothermal synthesis.

Metal-organic frameworks (MOFs), which contain reactive metal clusters and organic ligands allowing for large porosities and surface areas, have proven ...

Reductive Electropolymerization of a Vinyl-containing Poly-pyridyl Complex on Glassy Carbon and Fluorine-doped Tin Oxide Electrodes

Podsumowanie

Przeglądaj więcej filmów

Rozdziały w tym wideo

Improved In-gel Reductive β-Elimination for Comprehensive O-linked and Sulfo-glycomics by Mass Spectrometry