Development of Whispering Gallery Mode Polymeric Micro-optical Electric Field Sensors

Summary

A high-sensitivity photonic micro sensor was developed for electric field detection. The sensor exploits the optical modes of a dielectric sphere. Changes in the external electric field perturb the sphere morphology leading to shifts in its optical modes. The electric field strength is measured by monitoring these optical shifts.

Abstract

Optical modes of dielectric micro-cavities have received significant attention in recent years for their potential in a broad range of applications. The optical modes are frequently referred to as "whispering gallery modes" (WGM) or "morphology dependent resonances" (MDR) and exhibit high optical quality factors. Some proposed applications of micro-cavity optical resonators are in spectroscopy¹, micro-cavity laser technology², optical communications^3-6 as well as sensor technology. The WGM-based sensor applications include those in biology⁷, trace gas detection⁸, and impurity detection in liquids⁹. Mechanical sensors based on microsphere resonators have also been proposed, including those for force^10,11, pressure¹², acceleration¹³ and wall shear stress¹⁴. In the present, we demonstrate a WGM-based electric field sensor, which builds on our previous studies^15,16. A candidate application of this sensor is in the detection of neuronal action potential.

The electric field sensor is based on polymeric multi-layered dielectric microspheres. The external electric field induces surface and body forces on the spheres (electrostriction effect) leading to elastic deformation. This change in the morphology of the spheres, leads to shifts in the WGM. The electric field-induced WGM shifts are interrogated by exciting the optical modes of the spheres by laser light. Light from a distributed feedback (DFB) laser (nominal wavelength of ~ 1.3 μm) is side-coupled into the microspheres using a tapered section of a single mode optical fiber. The base material of the spheres is polydimethylsiloxane (PDMS). Three microsphere geometries are used: (1) PDMS sphere with a 60:1 volumetric ratio of base-to-curing agent mixture, (2) multi layer sphere with 60:1 PDMS core, in order to increase the dielectric constant of the sphere, a middle layer of 60:1 PDMS that is mixed with varying amounts (2% to 10% by volume) of barium titanate and an outer layer of 60:1 PDMS and (3) solid silica sphere coated with a thin layer of uncured PDMS base. In each type of sensor, laser light from the tapered fiber is coupled into the outermost layer that provides high optical quality factor WGM (Q ~ 10⁶). The microspheres are poled for several hours at electric fields of ~ 1 MV/m to increase their sensitivity to electric field.

Protocol

1. PDMS Microsphere Preparation (Sphere I)

1. Polydimethylsiloxane (PDMS) base and the curing agent are mixed with a volume ratio of 60:1.
2. A strand of silica optical fiber, about 2 cm long, is first stripped of its plastic cladding using an optical stripper.
3. One end of the fiber is heated and stretched to provide a stem end that is ~25-50 μm in diameter at the tip.
4. The stretched end of the fiber is submerged into the PDMS mixture by a length of approximately 2-4 mm and then is pulled out.
5. Surface tension and weight of the PDMS mixture allow for the formation of a sphere at the tip of the silica fiber. The size of the sphere is controlled by the dipping length and extraction velocity. By varying these two parameters, sphere diameters in the range 100 μm - 1,000 μm can be obtained.
6. The microsphere/stem assembly is then placed in an oven at ~90 °C for 4 hr to allow for proper curing of the polymer material (to form cross-linked chains). Figure 1a is a schematic of Sphere I.

2. PDMS-based Triple Layer Sphere Preparation (Sphere II)

1. A 60:1 PDMS microsphere is used as the inner core. The same steps described in 1) above is followed for this process.
2. A mixture of barium titanate (BaTiO₃) nano-particles and 60:1 PDMS is used as the middle layer. The PDMS mixture, prepared in the same way described in 1.1) above, is mixed with barium titanate nano-particles.
3. The PDMS microsphere core described in 2.1) is then dipped into the PDMS- barium titanate mixture to coat it (with a layer nominal thickness of ~ 10 μm).
4. Next, the two-layer sphere is placed in an oven at ~ 90 °C for 4 hr to allow for proper curing of the second layer.
5. Once the two layer sphere is cured, it is again immersed in a mixture of 60:1 PDMS to provide an outer coating (third layer). This outermost layer serves as spherical optical guide (~10 μm thickness). Figure 1b is a schematic of Sphere II.

3. Silica/PDMS Microsphere Preparation (Sphere III)

1. A ~ 3 cm long section of a silica single mode optical fiber is first stripped of its buffer (plastic) coating and then its tip is melted using a micro-torch (together with the cladding and core). Surface tension and gravity work together to shape the melted tip into a sphere. Spheres with diameters ranging from 200 to 500 μm can be obtained with this process.
2. The silica microsphere is then immersed in a bath of PDMS base (without the curing agent) to cover it with a coat of ~ 50 μm. This outer layer stays as a highly-viscous Bingham (yield-stress) fluid. Figure 1c is a schematic of Sphere III.

4. Optical Fiber Preparation

1. A section of a single mode optical fiber is stripped of its plastic cladding using an optical stripper. Using a micro-torch the striped section of the fiber is heated until it is molten (both the cladding and fiber core).
2. While the middle section is molten, one end of the optical fiber is pulled along its axis to form a tapered section of the fiber that is about 1 cm long. The duration of heating, the pulling speed and distance determine the diameter of the tapered section that ranges between 10 and 20 μm. The light from the DFB laser is coupled into the sphere through the tapered section of the fiber. Figure 2 shows the sphere-fiber coupling.

5. Optoelectronic Setup

1. The output of a tunable DFB laser is coupled into a single mode optical fiber on one end and terminated at a fast photodiode on the other end as shown in Figure 3.
2. The photodiode output is digitized using an analog-to-digital converter (A/D) and stored on a personal computer (PC).
3. Using a micro-translation stage the microsphere (Type I, II or III) is brought in contact with the tapered section of the optical fiber (Figures 2 and 3) to provide optical coupling between the two elements.
4. The DFB laser is tuned by a laser controller. The laser controller, in turn is driven by a function generator which provides a saw-tooth voltage input.

6. Electric Field Generation

1. Two square brass plates (2 x 2 cm) with thickness of 1 mm are used to generate the uniform electric field. The plates are connected to a voltage supply and the sphere sensors are placed in the gap between the two plates (Figure 4).
2. In order to increase the measurement sensitivity, the spheres are first poled in an electric field of 1 MV/m for 2 hr.

Results

An optical mode (WGM) of the sphere is excited by the laser light when optical path length traveled by the light is a multiple integer of the laser wavelength. For the arrangement shown in Figure 3, the optical path length is 2πrn, where n and r are the refractive index and radius of the sphere, respectively. Using geometric optics approximation, a WGM condition is satisfied when 2πrn = lλ wherel is an integer and λ is the laser's ...

Discussion

The spheres are initially poled by connecting the electrodes to a DC high voltage supply. At the end of the poling duration, the electrode leads are disconnected from the DC voltage supply and connected to a function generator as indicated in Figure 4. The results presented in Figures 5 through 8 show that positive and negative electric fields (relative to direction of poling) lead to sphere elongation and compression, respectively. Sphere I, which is a single layer 60:1...

Materials

Name	Company	Catalog Number	Comments
PDMS	Dow Corning	Sylgard 184
Silica fiber	Fiber Instrument Sales	E-37AP15-FIS
Barium Titanate (BaTiO3) nanoparticles	Sigma Aldrich	467634-100G
Laser Controller	ILX Lightwave	LDC-3724B
DFB Laser	Agere	Agere 2300	1.310 μm central wavelength
Photodiode	Thorlabs	PDA10CS
A/D Card	National Instruments	PXI 6115