Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display significant necking. Necking is the local reduction in cross-sectional area under stress. An interesting aspect of most brittle materials is their higher ultimate strength in compression than in tension, primarily due to microscopic defects like cracks or cavities that can weaken the material under tensile stress but have minimal impact on its compressive strength.

Concrete, a common brittle material, behaves differently under tension and compression. The stress-strain diagram under tension reveals a linear elastic range up to the yield point, followed by a rapid increase in strain until rupture. In contrast, concrete shows a larger linear elastic range under compression, and rupture does not occur even at peak stress. Instead, stress decreases as strain increases until rupture. Importantly, the modulus of elasticity, indicated in the stress-strain curve by the slope of the linear section, remains consistent in both tension and compression for most brittle materials.

Etiketler
Brittle MaterialsStress strain DiagramFracture CharacteristicsElongation RateBreaking StrengthUltimate StrengthNormal StressesRuptureNeckingCompressive StrengthTensile StressConcrete BehaviorLinear Elastic RangeModulus Of Elasticity

Bölümden 18:

article

Now Playing

18.4 : Stress-Strain Diagram - Brittle Materials

Gerilim ve Zorlanma - Eksenel Yükleme

598 Görüntüleme Sayısı

article

18.1 : Eksenel Yükleme Altında Normal Gerinim

Gerilim ve Zorlanma - Eksenel Yükleme

326 Görüntüleme Sayısı

article

18.2 : Gerilim-Gerinim Diyagramı

Gerilim ve Zorlanma - Eksenel Yükleme

364 Görüntüleme Sayısı

article

18.3 : Gerilme-Gerinim Diyagramı - Sünek Malzemeler

Gerilim ve Zorlanma - Eksenel Yükleme

365 Görüntüleme Sayısı

article

18.5 : Gerçek Gerilme ve Gerçek Gerinim

Gerilim ve Zorlanma - Eksenel Yükleme

202 Görüntüleme Sayısı

article

18.6 : Hooke Yasası

Gerilim ve Zorlanma - Eksenel Yükleme

263 Görüntüleme Sayısı

article

18.7 : Plastik Davranış

Gerilim ve Zorlanma - Eksenel Yükleme

137 Görüntüleme Sayısı

article

18.8 : Yorgunluk

Gerilim ve Zorlanma - Eksenel Yükleme

134 Görüntüleme Sayısı

article

18.9 : Elemanın Çoklu Yüklemeler Altında Deformasyonu

Gerilim ve Zorlanma - Eksenel Yükleme

93 Görüntüleme Sayısı

article

18.10 : Statik Olarak Belirsiz Problem Çözme

Gerilim ve Zorlanma - Eksenel Yükleme

273 Görüntüleme Sayısı

article

18.11 : Termal Gerinim

Gerilim ve Zorlanma - Eksenel Yükleme

273 Görüntüleme Sayısı

article

18.12 : Sıcaklığa Bağlı Deformasyon

Gerilim ve Zorlanma - Eksenel Yükleme

98 Görüntüleme Sayısı

article

18.13 : Poisson Oranı

Gerilim ve Zorlanma - Eksenel Yükleme

251 Görüntüleme Sayısı

article

18.14 : Genelleştirilmiş Hooke Yasası

Gerilim ve Zorlanma - Eksenel Yükleme

588 Görüntüleme Sayısı

article

18.15 : Yığın Modülü

Gerilim ve Zorlanma - Eksenel Yükleme

195 Görüntüleme Sayısı

See More

JoVE Logo

Gizlilik

Kullanım Şartları

İlkeler

Araştırma

Eğitim

JoVE Hakkında

Telif Hakkı © 2020 MyJove Corporation. Tüm hakları saklıdır