Name: the evolution of silica nanoparticle-polyester coatings on surfaces exposed to sunlight
Uploaded: 2016-10-11T14:00:00
Description: Watch this Scientific Journal Video about The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight at JoVE.com

Funding from the Australian Research Council Industrial Transformation Research Hubs Scheme (Project Number IH130100017) is gratefully acknowledged. Authors gratefully acknowledge the RMIT Microscopy and Microanalysis Facility (RMMF) for providing access to the characterisation instruments. This research was also undertaken on the Infrared Microscopectroscopy beamline at the Australian Synchrotron, Victoria, Australia.

<html> 1. As amostras de aço <ol><li> Obtenção de amostras de aço de 1 mm de espessura a partir de um fornecedor comercial. NOTA: As amostras foram revestidas com qualquer poliéster ou de poliéster revestido com nanopartículas de sílica. </li><li> Expor amostras à luz solar em Rockhampton, Queensland, Austrália: recolher amostras após intervalos de um ano e cinco anos ao longo de um período total de 5 anos. Cortar painéis de exemplo para discos redondos de diâmetro de 1 cm, utiliza...

<ol>
	<li>Fathima Sabirneeza, A. A., Geethanjali, R., Subhashini, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polymeric+corrosion+inhibitors+for+iron+and+its+alloys:+A+review.">Polymeric corrosion inhibitors for iron and its alloys: A review.</a> Chem. Eng. Commun. 202 (2), 232-244 (2015).</li><li>Gupta, R. K., Birbilis, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+influence+of+nanocrystalline+structure+and+processing+route+on+corrosion+of+stainless+steel:+A+review.">The influence of nanocrystalline structure and processing route on corrosion of stainless steel: A review.</a> Corros. Sci. 92, 1-15 (2015).</li><li>Lee, H. S., Ismail, M. A., Choe, H. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Arc+thermal+metal+spray+for+the+protection+of+steel+structures:+An+overview.">Arc thermal metal spray for the protection of steel structures: An overview.</a> Corros. Rev. 33 (1-2), 31-61 (2015).</li><li>Moore, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Corrosion challenges - urban water industry. , (2010).</li><li>Hays, G. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> World Corrosion Organization. , (2013).</li><li>Koch, G. H., Brongers, M. P. H., Thompson, N. G., Virmani, P. Y., Payer, J. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion+cost+and+preventive+strategies+in+the+United+States.">Corrosion cost and preventive strategies in the United States.</a> CC Technologies Laboratories, Incorporated; NACE International; Federal Highway Administration, NACE International. , (2002).</li><li>Pojtanabuntoeng, T., Singer, M., Nesic, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Corrosion 2011. , (2011).</li><li>Jas&#776;niok, T., Jas&#776;niok, M., Tracz, T., Hager, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> 7th Scientific-Technical Conference on Material Problems in Civil Engineering, MATBUD 2015. , 316-323 (2015).</li><li>Cambier, S. M., Posner, R., Frankel, G. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Coating+and+interface+degradation+of+coated+steel,+Part+1:+Field+exposure.">Coating and interface degradation of coated steel, Part 1: Field exposure.</a> Electrochim. Acta. 133, 30-39 (2014).</li><li>Barletta, M., Gisario, A., Puopolo, M., Vesco, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scratch,+wear+and+corrosion+resistant+organic+inorganic+hybrid+materials+for+metals+protection+and+barrier.">Scratch, wear and corrosion resistant organic inorganic hybrid materials for metals protection and barrier.</a> Mater. Des. 69, 130-140 (2015).</li><li>Fu, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Experimental+and+theoretical+study+on+the+inhibition+performances+of+quinoxaline+and+its+derivatives+for+the+corrosion+of+mild+steel+in+hydrochloric+acid.">Experimental and theoretical study on the inhibition performances of quinoxaline and its derivatives for the corrosion of mild steel in hydrochloric acid.</a> Ind. Eng. Chem. Res. 51 (18), 6377-6386 (2012).</li><li>Hattori, M., Nishikata, A., Tsuru, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=EIS+study+on+degradation+of+polymer-coated+steel+under+ultraviolet+radiation.">EIS study on degradation of polymer-coated steel under ultraviolet radiation.</a> Corros. Sci. 52 (6), 2080-2087 (2010).</li><li>Yang, X. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Weathering+degradation+of+a+polyurethane+coating.">Weathering degradation of a polyurethane coating.</a> Polym. Degrad. Stab. 74 (2), 341-351 (2001).</li><li>Armstrong, R. D., Jenkins, A. T. A., Johnson, B. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+investigation+into+the+uv+breakdown+of+thermoset+polyester+coatings+using+impedance+spectroscopy.">An investigation into the uv breakdown of thermoset polyester coatings using impedance spectroscopy.</a> Corros. Sci. 37 (10), 1615-1625 (1995).</li><li>Zhou, W., Liu, M., Chen, N., Sun, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion+properties+of+sol-gel+silica+coatings+on+phosphated+carbon+steel+in+sodium+chloride+solution.">Corrosion properties of sol-gel silica coatings on phosphated carbon steel in sodium chloride solution.</a> J. Sol. Gel. Sci. Technol. 76 (2), 358-371 (2015).</li><li>Hollamby, M. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hybrid+polyester+coating+incorporating+functionalized+mesoporous+carriers+for+the+holistic+protection+of+steel+surfaces.">Hybrid polyester coating incorporating functionalized mesoporous carriers for the holistic protection of steel surfaces.</a> Adv. Mater. 23 (11), 1361-1365 (2011).</li><li>Borisova, D., M&#246;hwald, H., Shchukin, D. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mesoporous+silica+nanoparticles+for+active+corrosion+protection.">Mesoporous silica nanoparticles for active corrosion protection.</a> ACS Nano. 5 (3), 1939-1946 (2011).</li><li>Wang, M., Liu, M., Fu, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+intelligent+anticorrosion+coating+based+on+pH-responsive+smart+nanocontainers+fabricated+via+a+facile+method+for+protection+of+carbon+steel.">An intelligent anticorrosion coating based on pH-responsive smart nanocontainers fabricated via a facile method for protection of carbon steel.</a> J. Mater. Chem. A. 3 (12), 6423-6431 (2015).</li><li>Truong, V. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+influence+of+nano-scale+surface+roughness+on+bacterial+adhesion+to+ultrafine-grained+titanium.">The influence of nano-scale surface roughness on bacterial adhesion to ultrafine-grained titanium.</a> Biomaterials. 31 (13), 3674-3683 (2010).</li><li>Ne&#269;as, D., Klapetek, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gwyddion:+An+open-source+software+for+SPM+data+analysis.">Gwyddion: An open-source software for SPM data analysis.</a> Cent. Eur. J. Phys. 10 (1), 181-188 (2012).</li><li>Crawford, R. J., Webb, H. K., Truong, V. K., Hasan, J., Ivanova, E. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+topographical+factors+influencing+bacterial+attachment.">Surface topographical factors influencing bacterial attachment.</a> Adv. Colloid Interface Sci. 179-182, 142-149 (2012).</li><li>Allen, N. S., Edge, M., Mohammadian, M., Jones, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Physicochemical+aspects+of+the+environmental+degradation+of+poly(ethylene+terephthalate).">Physicochemical aspects of the environmental degradation of poly(ethylene terephthalate).</a> Polym. Degrad. Stab. 43 (2), 229-237 (1994).</li><li>Newman, C. R., Forciniti, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Modeling+the+ultraviolet+photodegradation+of+rigid+polyurethane+foams.">Modeling the ultraviolet photodegradation of rigid polyurethane foams.</a> Ind. Eng. Chem. Res. 40 (15), 3346-3352 (2001).</li><li>Ivanova, E. P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Vibrio+fischeri+and+Escherichia+coli+adhesion+tendencies+towards+photolithographically+modified+nanosmooth+poly+(tert-butyl+methacrylate)+polymer+surfaces.">Vibrio fischeri and Escherichia coli adhesion tendencies towards photolithographically modified nanosmooth poly (tert-butyl methacrylate) polymer surfaces.</a> Nanotechnol. Sci. Appl. 1, 33-44 (2008).</li><li>Biggs, S., Lukey, C. A., Spinks, G. M., Yau, S. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+atomic+force+microscopy+study+of+weathering+of+polyester/melamine+paint+surfaces.">An atomic force microscopy study of weathering of polyester/melamine paint surfaces.</a> Prog. Org. Coat. 42 (1-2), 49-58 (2001).</li><li>Signor, A. W., VanLandingham, M. R., Chin, J. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effects+of+ultraviolet+radiation+exposure+on+vinyl+ester+resins:+Characterization+of+chemical,+physical+and+mechanical+damage.">Effects of ultraviolet radiation exposure on vinyl ester resins: Characterization of chemical, physical and mechanical damage.</a> Polym. Degrad. Stab. 79 (2), 359-368 (2003).</li><li>Wang, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion-resistance,+robust+and+wear-durable+highly+amphiphobic+polymer+based+composite+coating+via+a+simple+spraying+approach.">Corrosion-resistance, robust and wear-durable highly amphiphobic polymer based composite coating via a simple spraying approach.</a> Prog. Org. Coat. 82, 74-80 (2015).</li><li>Liszka, B. M., Lenferink, A. T. M., Witkamp, G. J., Otto, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Raman+micro-spectroscopy+for+quantitative+thickness+measurement+of+nanometer+thin+polymer+films.">Raman micro-spectroscopy for quantitative thickness measurement of nanometer thin polymer films.</a> J. Raman Spectrosc. 46 (12), 1230-1234 (2015).</li><li>Alghunaim, A., Kirdponpattara, S., Newby, B. M. Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Techniques+for+determining+contact+angle+and+wettability+of+powders.">Techniques for determining contact angle and wettability of powders.</a> Powder Technol. 287, 201-215 (2016).</li><li>Trevi&#241;o, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Erosive+wear+of+plasma+electrolytic+oxidation+layers+on+aluminium+alloy+6061.">Erosive wear of plasma electrolytic oxidation layers on aluminium alloy 6061.</a> Wear. 301 (1-2), 434-441 (2013).</li></ol>

Os revestimentos de poliéster têm sido amplamente utilizados para proteger substratos de aço a partir da corrosão que ocorreria numa superfície não revestidas devido à acumulação de poluentes e de humidade. A aplicação de revestimentos de poliéster pode proteger o aço contra a corrosão; No entanto, a eficácia a longo prazo destes revestimentos é comprometida se eles estão expostos a altos níveis de luz ultravioleta sob condições húmidas, como ocorre em climas tropicais. nanopartículas de sílica po...

Environmental corrosion of metals in the environment is both prevalent and costly1-3. A recent study conducted by the Australasian Corrosion Association (ACA) reported that corrosion of metals resulted in a yearly cost of $982 million, which was directly associated with the degradation of assets and infrastructure through metallic corrosion within the water industry4. From an international perspective, the World Corrosion Organization estimated that metallic corrosion was responsible for a direct cost of $3.3 trillion, over 3% of the world's GDP5. The process of galvanizing as a corrosion preventative method has been widely used to increase the lifespan of steel material6. In humid and subtropical climates, however, water tends to condense into small pockets or grooves within the surface of the galvanized steel, leading to the acceleration of corrosion rates through pit corrosion7,8. Thermosetting polymer coatings based on polyesters have been developed to coat the galvanized steel substrata increasing their ability to withstand humid weathering conditions for items such as satellite dishes, garden furniture, air-conditioning units or agricultural construction equipment9-11. Unfortunately polymer coatings on steel surfaces have been found to be considerably adversely affected by the presence of high levels of ultraviolet (uv) radiation12-14. Coatings comprised of silica nanoparticles (SiO2) spread over a polymer layer have been widely used with a view to increasing their corrosion-, wear-, tear- and degradation-resistance15,16. The tendency of the protective polymeric coatings to form pores and cracks can be reduced by incorporating nanoparticles (NPs), which contribute to the passive obstruction of corrosion initiation17,18. Also, the mechanical stability of the protective polymeric layer can be improved by NPs inclusion. However, these coatings act as passive physical barriers and, in comparison to the galvanization approach, cannot inhibit corrosion propagation actively.
An in-depth understanding of the effect that high-levels of ultraviolet light exposure under humid conditions upon these metal coatings is yet to be obtained. In this paper, a wide range of surface analytical techniques, including X-ray photoelectron spectroscopy (XPS), attenuated total reflection infrared micro-spectroscopy (ATR IR), contact angle goniometry, optical profiling and atomic force microscopy (AFM) will be employed to examine the changes in the surface of steel coatings prepared from polyester- and silica nanoparticle-coated polyester (silica nanoparticles/polyester) after exposure to sunlight. Furthermore, the aim of this work is to give a concise, practical overview of the overall characterization techniques to examine weathered samples.

<table border="0" cellpadding="0" cellspacing="0" width="1044">
	<colgroup>
		<col />
		<col />
		<col />
		<col />
	</colgroup>
	<tbody>
		<tr height="41">
			<td height="41" style="height:41px;width:263px;">polyester-coated steel 
			silica nanoparticle-polyester coated steel substrata</td>
			<td style="width:231px;">BlueScope Steel</td>
			<td style="width:163px;"></td>
			<td style="width:387px;">Samples provided by company</td>
		</tr>
		<tr height="26">
			<td height="26" style="height:26px;width:263px;">Millipore PetriSlideTM&#160;</td>
			<td style="width:231px;">Fisher Scientific</td>
			<td style="width:163px;">PDMA04700</td>
			<td>Storing samples</td>
		</tr>
		<tr height="49">
			<td height="49" style="height:49px;width:263px;">Thermo ScientificTM K-alpha 
			X-ray Photoelectron Spectrometer</td>
			<td>Thermo Fisher Scientific, Inc.</td>
			<td>IQLAADGAAFFACVMAHV</td>
			<td>Acquire XPS spectra</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:263px;">Avantage Data System</td>
			<td>Thermo Fisher Scientific, Inc.</td>
			<td>IQLAADGACKFAKRMAVI</td>
			<td>Analyse XPS spectra</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">A Bruker Hyperion 2000 microscope&#160;</td>
			<td style="width:231px;">Bruker Corporation</td>
			<td style="width:163px;"></td>
			<td>Synchrotron integrated instrument</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Bruker Opus v. 7.2</td>
			<td style="width:231px;">Bruker Corporation</td>
			<td style="width:163px;"></td>
			<td>ATR-IR analysis software</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:263px;">Contact angle goniometer, FTA1000c</td>
			<td>First Ten &#197;ngstroms Inc., VA, USA</td>
			<td style="width:163px;"></td>
			<td>Measuring the wettability of surfaces</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:263px;">FTA v. 2.0</td>
			<td>First Ten &#197;ngstroms Inc., VA, USA</td>
			<td style="width:163px;"></td>
			<td>Anaylyzing water contact angle</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Optical profiler, Wyko NT1100&#160;</td>
			<td>Bruker Corporation</td>
			<td style="width:163px;"></td>
			<td>Measure surface topography</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Innova atomic force microscope&#160;</td>
			<td>Bruker Corporation</td>
			<td style="width:163px;"></td>
			<td>Measure surface topography</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:263px;">Phosphorus doped silicon probes, MPP-31120-10</td>
			<td>Bruker Corporation</td>
			<td style="width:163px;"></td>
			<td>AFM probes</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;">Gwyddion software</td>
			<td style="width:231px;">http://gwyddion.net/</td>
			<td style="width:163px;"></td>
			<td>Software used to measure optical profiling and AFM data</td>
		</tr>
	</tbody>
</table>

the evolution of silica nanoparticle-polyester coatings on surfaces exposed to sunlight

Corrosão de superfícies metálicas é prevalente no ambiente e é de grande preocupação em muitas áreas, incluindo as indústrias militares, transporte, aviação, construção e alimentos, entre outros. Poliéster e revestimentos que contêm poliéster e nanopartículas de sílica (SiO 2 NPS) têm sido amplamente utilizados para proteger substratos de aço contra a corrosão. Neste estudo, utilizou raios-X espectroscopia de fotoelétrons, reflexão total atenuada infravermelho micro-espectroscopia, medidas de ângulo de contato com água, profiling óptica e microscopia de força atômica para fornecer uma visão sobre como a exposição ao sol pode causar alterações na micro e nanoescala integridade dos revestimentos. Nenhuma mudança significativa na superfície micro-topografia foi detectada utilizando perfilometria óptica, no entanto, alterações estatisticamente significativas em nanoescala à superfície foi detectado usando microscopia de força atómica. Análise da espectroscopia de fotoelétrons de raios-X e infravermelho micro reflexão total atenuadaespectroscopia de dados revelou que a degradação dos grupos éster tinha ocorrido através da exposição à luz ultravioleta para formar COO ·, -H 2, -O C · · ·, -CO radicais. Durante o processo de degradação, CO e CO2 foram também produzidos.

<html> As amostras de aço revestidas que tinham sido sujeitos à exposição à luz solar para qualquer um ou cinco anos foram recolhidos, e de contacto da água medidas do ângulo foram realizados para determinar se a exposição resultou numa mudança na hidrofobicidade de superfície da superfície (Figura 2 ). <img alt="Figura 2" src="/files/ftp_upload/54309/54309fig2.jpg" /> Figura 2. variação molhabilidade das superfície...

Watch this Scientific Journal Video about The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight at JoVE.com

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight

Dois tipos de superfícies, de aço e poliéster revestidos por poliéster revestido com uma camada de nanopartículas de sílica, foram estudados. Ambas as superfícies foram expostas à luz solar, o que se verificou causar alterações substanciais na química e nanoescala topografia da superfície.

A evolução de sílica Coatings nanopartículas-poliéster em superfícies expostas à luz solar

Corrosion of metallic surfaces is prevalent in the environment and is of great concern in many areas, including the military, transport, aviation, ...

Research

JoVE Journal

Engineering

Investigation of Early Plasma Evolution Induced by Ultrashort Laser Pulses

Investigação da Evolução Plasma Precoce Induzida por Pulsos ultracurtos de laser

Early plasma is generated owing to high intensity laser irradiation of target and the subsequent target material ionization. Its dynamics plays a ...

Engenharia

Fabrication of Silica Ultra High Quality Factor Microresonators

Fabricação de Sílica Ultra microresonators alto fator de qualidade

Whispering gallery resonant cavities confine light in circular orbits at their periphery.1-2 The photon storage lifetime in the cavity, quantified by the ...

Probing and Mapping Electrode Surfaces in Solid Oxide Fuel Cells

Sondagem e Mapeamento superfície do eletrodo em células a combustível de óxido sólido

Solid oxide fuel cells (SOFCs) are potentially the most efficient and cost-effective solution to utilization of a wide variety of fuels beyond hydrogen ...

Fabrication of Nano-engineered Transparent Conducting Oxides by Pulsed Laser Deposition

Fabricação de Nano-engenharia transparentes Óxidos Realização por deposição por laser pulsado

Nanosecond Pulsed  Laser Deposition (PLD) in the presence of a background gas allows the deposition  of metal oxides with tunable morphology, structure, ...

High-speed Particle Image Velocimetry Near Surfaces

Alta velocidade da partícula Velocimetry Imagem perto de superfícies

Multi-dimensional and transient flows play a key role in many areas of science, engineering, and health sciences but are often not well understood. The ...

Monolayer Contact Doping of Silicon Surfaces and Nanowires Using Organophosphorus Compounds

Monolayer Contact Doping (MLCD) is a simple method for doping of surfaces and nanostructures1. MLCD results in the formation of highly controlled, ultra ...

High-resolution Thermal Micro-imaging Using Europium Chelate Luminescent Coatings

High-resolution Micro-imagem térmica Usando európio quelato luminescentes Coatings

Micro-electronic devices often undergo significant self-heating when biased to their typical operating conditions. This paper describes a convenient ...

Evanescent Field Based Photoacoustics: Optical Property Evaluation at Surfaces

Evanescente Campo photoacoustics Baseado: Avaliação da Propriedade óptica a Surfaces

Here, we present a protocol to estimate material and surface optical properties using the photoacoustic effect combined with total internal reflection. ...

Pool-Boiling Heat-Transfer Enhancement on Cylindrical Surfaces with Hybrid Wettable Patterns

Enhancement Pool-ebulição de transferência de calor em cilíndricos Superfícies com padrões molháveis ​​híbridos

In this study, pool-boiling heat-transfer experiments were performed to investigate the effect of the number of interlines and the orientation of the ...

Fabrication of Superhydrophobic Metal Surfaces for Anti-Icing Applications

Fabricação de superfícies de Metal Superhydrophobic para aplicações antigelo

Several ways to produce superhydrophobic metal surfaces are presented in this work. Aluminum was chosen as the metal substrate due to its wide use in ...