Name: in situ synthesis of gold nanoparticles without aggregation in the interlayer space of layered titanate transparent films
Uploaded: 2017-01-17T14:00:00
Description: Watch this Scientific Journal Video about In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films at JoVE.com

This work was partly supported by Nippon Sheet Glass Foundation for Materials Science and Engineering and JSPS KAKENHI (Grant-in-Aid for Challenging Exploratory Research, #50362281).

Precaución: Siempre tenga cuidado cuando se trabaja con productos químicos y soluciones. Siga las prácticas de seguridad apropiadas y usar guantes, gafas y una bata de laboratorio en todo momento. Tenga en cuenta que los nanomateriales pueden tener riesgos adicionales en comparación con su contraparte mayor. 1. Preparación de Regentes <ol><li> Preparar la solución de metil viológeno acuosa mediante la disolución de 0,0012 g de dicloruro de 1,1&#39;-dimetil-4,4&#39;-bipiridinio (metil viológeno; MV <su...

Este manuscrito proporciona un protocolo detallado para la síntesis in situ de nanopartículas de oro (AuNPs) dentro del espacio entre capas de las películas de TNS. Este es el primer informe de la síntesis in situ de AuNPs dentro del espacio entre capas de TNS. Por otra parte, se encontró que la 2-AET + funciona como un reactivo de protección eficaz para AuNPs dentro de la capa intermedia de TNS. Estos métodos se hibridan AuNPs y TNS películas transparentes. TNS películas con buena ...

Varios nanopartículas de metales nobles (MNPS) presentan colores o tonos característicos debido a su resonancia de plasmones superficiales (localizada) LSPR propiedades; Por lo tanto, MNPs pueden ser utilizados en diversas aplicaciones / fotoquímicos ópticos y o 1-4. Recientemente, combinaciones de semiconductor de óxido metálico (MOS) fotocatalizadores, tales como óxido de titanio (TiO 2) y MNPs, se han investigado a fondo como nuevos tipos de fotocatalizadores 5-14. Sin embargo, en muchos casos, cantidades muy pequeñas de MNPs existir en la superficie MOS, porque la mayoría de las partículas de MOS tienen áreas superficiales relativamente bajas. Por otro lado, en capas de semiconductores de óxido de metal (LMOSs) exhiben propiedades fotocatalíticas y tienen un área superficial grande, típicamente de varios cientos de metros cuadrados por unidad g de un OVM 15-17. Además, varios LMOSs tienen propiedades de intercalación (es decir, varias especies químicas se pueden acomodar dentro de sus espacios entre capas expandibles y grandes) 15-20. Por lo tanto, con una combinación de MNPs y LMOSs, se espera que cantidades relativamente grandes de MNPs se hibridan con los fotocatalizadores semiconductores. Nos han informado de la primera síntesis in situ de nanopartículas de cobre (21) CuNPs dentro del espacio de capa intermedia de OVM (óxido de titanio nanosheet; TNS 16-30) películas transparentes a través de pasos muy sencillos. Sin embargo, aún no se ha informado de los detalles de los procedimientos de síntesis y la caracterización de los otros híbridos MNPs y TNS nobles. Por otra parte, los CuNPs dentro de las capas de TNS se oxidaron fácilmente y se decolora en condiciones ambientales 21. Como tal, nos centramos en las nanopartículas de oro (AuNPs), porque AuNPs son ampliamente utilizados para diversos óptica, fotoquímico, y aplicaciones catalíticas, y se espera que sean relativamente estable frente a la oxidación 3-5,7,8,10-14 , 28,31,32. Aquí, se presenta la síntesis de AuNPs dentro del espacio de capa intermedia de TNS y mostrar tha2 t-ammoniumethanethiol (2-AET +; Figura 1 recuadro) funciona efectivamente como un reactivo de protección para AuNPs dentro de la capa intermedia de TNS.

<table border="0" cellpadding="0" cellspacing="0" width="979">
	<colgroup>
		<col />
		<col />
		<col />
		<col />
	</colgroup>
	<tbody>
		<tr height="22">
			<td height="22" style="height:22px;width:295px;">Methyl viologen dichloride</td>
			<td style="width:173px;">Aldrich Chemical&#160; Co., Inc.</td>
			<td style="width:124px;">1910-42-5</td>
			<td style="width:388px;"></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">Tetrabutylammonium hydroxide</td>
			<td>TCI</td>
			<td>T1685</td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">cesium carbonate</td>
			<td>Kanto Chemical Co., Inc.</td>
			<td>07184-33</td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">anatase titanium dixoide</td>
			<td>Ishihara Sangyo Ltd.</td>
			<td>ST-01</td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">hydrochloric acid</td>
			<td>Junsei Chemical Co., Ltd.</td>
			<td>20010-0350</td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">sodium hydroxide</td>
			<td>Junsei Chemical Co., Ltd.</td>
			<td>195-13775</td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">Tetrachloroauric(III) acid trihydrate</td>
			<td>Kanto Chemical Co., Inc.</td>
			<td>17044-60</td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">sodium tetrahydroborate</td>
			<td>Junsei Chemical Co., Ltd.</td>
			<td>39245-1210</td>
			<td></td>
		</tr>
		<tr height="22">
			<td height="22" style="height:22px;">2-ammoniumethanethiol hydrochloride</td>
			<td>TCI</td>
			<td>A0296</td>
			<td></td>
		</tr>
		<tr height="24">
			<td height="24" style="height:24px;">Ultrapure water (0.056 &#181;S/cm)</td>
			<td></td>
			<td></td>
			<td>Milli-Q water purification system (Direct-Q&#174; 3UV, Millipore)</td>
		</tr>
		<tr height="22">
			<td>Microscope slide (Thickness : 1.0&#8764;1.2 mm)</td>
			<td>Matsunami glass Co., Ltd.</td>
			<td></td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;"></td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
	</tbody>
</table>

in situ synthesis of gold nanoparticles without aggregation in the interlayer space of layered titanate transparent films

Combinations of metal oxide semiconductors and gold nanoparticles (AuNPs) have been investigated as new types of materials. The in situ synthesis of AuNPs within the interlayer space of semiconducting layered titania nanosheet (TNS) films was investigated here. Two types of intermediate films (i.e., TNS films containing methyl viologen (TNS/MV2+) and 2-ammoniumethanethiol (TNS/2-AET+)) were prepared. The two intermediate films were soaked in an aqueous tetrachloroauric(III) acid (HAuCl4) solution, whereby considerable amounts of Au(III) species were accommodated within the interlayer spaces of the TNS films. The two types of obtained films were then soaked in an aqueous sodium tetrahydroborate (NaBH4) solution, whereupon the color of the films immediately changed from colorless to purple, suggesting the formation of AuNPs within the TNS interlayer. When only TNS/MV2+ was used as the intermediate film, the color of the film gradually changed from metallic purple to dusty purple within 30 min, suggesting that aggregation of AuNPs had occurred. In contrast, this color change was suppressed by using the TNS/2-AET+ intermediate film, and the AuNPs were stabilized for over 4 months, as evidenced by the characteristic extinction (absorption and scattering) band from the AuNPs.

Se utilizaron dos tipos de películas precursoras en este estudio (es decir, con y sin el reactivo de protección (2-AET +) dentro de la capa intermedia de TNS). En ausencia de 2-AET +, 1,1&#39;-bipiridinio-dimetil-4,4&#39; dicloruro de (viológeno de metilo; MV 2 +) se usó como un expansor del espacio entre capas, porque MV 2 + que contienen LMOSs haber sido se utiliza con frecuencia como intermedios en el método de intercambio de i...

Watch this Scientific Journal Video about In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films at JoVE.com

In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films

A continuación, se presenta un protocolo para la síntesis in situ de nanopartículas de oro (AuNPs) dentro del espacio de capa intermedia de películas titanato estratificado sin la agregación de AuNPs. No se observó cambio espectral incluso después de 4 meses. El material sintetizado se espera que las aplicaciones en catálisis, fotocatálisis, y el desarrollo de dispositivos plasmónicas rentables.

In Situ Síntesis de nanopartículas de oro sin agregación en el espacio entre capas de Capas de titanato películas transparentes

Combinations of metal oxide semiconductors and gold nanoparticles (AuNPs) have been investigated as new types of materials. The in situ synthesis of AuNPs ...

Research

JoVE Journal

Engineering

In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films

Synthesis and Functionalization of Nitrogen-doped Carbon Nanotube Cups with Gold Nanoparticles as Cork Stoppers

Síntesis y funcionalización de nitrógeno dopados Copas de nanotubos de carbono con nanopartículas de oro como tapones de corcho

Nitrogen-doped carbon  nanotubes consist of many cup-shaped graphitic compartments termed as  nitrogen-doped carbon nanotube cups (NCNCs).  These ...

Investigación

Ingeniería

Detection and Recovery of Palladium, Gold and Cobalt Metals from the Urban Mine Using Novel Sensors/Adsorbents Designated with Nanoscale Wagon-wheel-shaped Pores

Detección y recuperación de paladio, oro y cobalto Metales de la Mina Urbana utilizando sensores Novela / adsorbentes designados con nanoescala Los poros en forma de rueda-Wagon

Developing low-cost, efficient processes for recovering and recycling palladium, gold and cobalt metals from urban mine remains a significant challenge in ...

Fabrication and Characterization of Superconducting Resonators

Fabricación y caracterización de resonadores superconductores

Superconducting microwave resonators are of interest for a wide range of applications, including for their use as microwave kinetic inductance detectors ...

Electrospray Deposition of Uniform Thickness Ge23Sb7S70 and As40S60 Chalcogenide Glass Films

Electrospray Deposition of Uniform Thickness Ge23Sb7S70 and As40S60 Chalcogenide Glass Films

Electropulverización La deposición de espesor uniforme Ge<sub&gt; 23</sub&gt; Sb<sub&gt; 7</sub&gt; S<sub&gt; 70</sub&gt; Y As<sub&gt; 40</sub&gt; S<sub&gt; 60</sub&gt; calcogenura las películas de cristal

Solution-based electrospray film deposition, which is compatible with continuous, roll-to-roll processing, is applied to chalcogenide glasses. Two ...

Spark Plasma Sintering Apparatus Used for the Formation of Strontium Titanate Bicrystals

Spark aparato de plasma sinterización usado para la formación de titanato de estroncio Bicrystals

A spark plasma sintering apparatus was used as a novel method for diffusion bonding of two single crystals of strontium titanate to form bicrystals with ...

Fabrication of Ultra-thin Color Films with Highly Absorbing Media Using Oblique Angle Deposition

Fabricación de películas ultra delgadas Color con altamente absorbente de los medios de comunicación mediante deposición oblicua

Ultra-thin film structures have been studied extensively for use as optical coatings, but performance and fabrication challenges remain.&#160; We present ...

Methods of Ex Situ and In Situ Investigations of Structural Transformations: The Case of Crystallization of Metallic Glasses

Methods of Ex Situ and In Situ Investigations of Structural Transformations: The Case of Crystallization of Metallic Glasses

Métodos Ex Situ e In Situ las investigaciones de las transformaciones estructurales: el caso de la cristalización de vidrios metálicos

We demonstrate the use of two nuclear-based analytical methods that can follow the modifications of microstructural arrangement of iron-based metallic ...

Controllable Nucleation of Cavitation from Plasmonic Gold Nanoparticles for Enhancing High Intensity Focused Ultrasound Applications

Nucleación controlable de la cavitación de la plasmónica nanopartículas de oro para aumentar la intensidad alta enfocada ultrasonido aplicaciones

In this study, plasmonic gold nanoparticles were simultaneously exposed to pulsed near-infrared laser light and high intensity focused ultrasound (HIFU) ...

Radio Frequency Magnetron Sputtering of GdBa2Cu3O7&#8722;&#948;/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 (STO) Single-crystal Substrates

Radio Frequency Magnetron Sputtering of GdBa2Cu3O7ÃƒÆ’Ã‚Â¢Ãƒâ€¹Ã¢â‚¬Â 'ÃƒÆ’Ã…Â½Ãƒâ€šÃ‚Â´/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 STO Single-crystal Substrates

Radio frecuencia de magnetrón Sputtering de GdBa2Cu3O7−δ/ La0.67Films Sr0.33MnO3 cuasi-bicapa sobre sustratos de monocristal SrTiO3 (STO)

Here, we demonstrate a method of coating ferromagnetic La0.67Sr0.33MnO3 (LSMO) nanoparticles on (001) SrTiO3 (STO) single-crystal substrates by radio ...

Large Area Substrate-Based Nanofabrication of Controllable and Customizable Gold Nanoparticles Via Capped Dewetting

Área base de sustrato nanofabricación de nanopartículas de oro personalizables y controlables Via Dewetting tapado

Recent scientific advances in the utilization of metallic nanoparticle for enhanced energy conversion efficiency, improved optical device performance, and ...