Name: synthesis of hydrogels with antifouling properties as membranes for water purification
Uploaded: 2017-04-07T14:00:00
Description: Watch this Scientific Journal Video about Synthesis of Hydrogels with Antifouling Properties As Membranes for Water Purification at JoVE.com

We gratefully acknowledge the financial support of this work by the Korean Carbon Capture and Sequestration R&amp;D Center (KCRC).

プレポリマー溶液の調製<ol><li> 調製溶媒として水を使用して <ol><li>磁気撹拌棒をガラスボトルに脱イオン（DI）水の10.00グラムを追加します。 </li><li> SBMAの2.00グラムを測定し、水を含むガラスびんに移します。 SBMAが完全に溶解するまで、30分間溶液を撹拌しました。 </li><li>別個の瓶に、（M、N = 700グラム/モル）PEGDAの20.00グラムを加えます。 </li><li> PEGDA溶液に、1-ヒド?...

<ol>
	<li>Qasim, M., Darwish, N. A., Sarp, S., Hilal, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Water+desalination+by+forward+(direct)+osmosis+phenomenon:+A+comprehensive+review.">Water desalination by forward (direct) osmosis phenomenon: A comprehensive review.</a> Desalination. , 47-69 (2015).</li><li>Geise, G. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Water+purification+by+membranes:+The+role+of+polymer+science.">Water purification by membranes: The role of polymer science.</a> J. Polym. Sci. Part B Polym. Phys. 48 (15), 1685-1718 (2010).</li><li>Miller, D. J., Dreyer, D., Bielawski, C., Paul, D. R., Freeman, B. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+modification+of+water+purification+membranes:+A+review.">Surface modification of water purification membranes: A review.</a> Angew Chem Int Ed Engl. , (2016).</li><li>Zhao, S. Z., Huang, K. P., Lin, H. Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Impregnated+Membranes+for+Water+Purification+Using+Forward+Osmosis.">Impregnated Membranes for Water Purification Using Forward Osmosis.</a> Ind. Eng. Chem. Res. 54 (49), 12354-12366 (2015).</li><li>Ostuni, E., Chapman, R. G., Holmlin, R. E., Takayama, S., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+survey+of+structure-property+relationships+of+surfaces+that+resist+the+adsorption+of+protein.">A survey of structure-property relationships of surfaces that resist the adsorption of protein.</a> Langmuir. 17 (18), 5605-5620 (2001).</li><li>Jiang, S., Cao, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ultralow-fouling,+functionalizable,+and+hydrolyzable+zwitterionic+materials+and+their+derivatives+for+biological+applications.">Ultralow-fouling, functionalizable, and hydrolyzable zwitterionic materials and their derivatives for biological applications.</a> Adv Mat. 22 (9), 920-932 (2010).</li><li>Shah, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Transport+properties+of+small+molecules+in+zwitterionic+polymers.">Transport properties of small molecules in zwitterionic polymers.</a> J. Polym. Sci. Part B Polym. Phys. 54 (19), 1924-1934 (2016).</li><li>Shao, Q., Jiang, S. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Molecular+Understanding+and+Design+of+Zwitterionic+Materials.">Molecular Understanding and Design of Zwitterionic Materials.</a> Adv Mat. 27 (1), 15-26 (2015).</li><li>Zhang, Z., Chao, T., Chen, S., Jiang, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Superlow+Fouling+Sulfobetaine+and+Carboxybetaine+Polymers+on+Glass+Slides.">Superlow Fouling Sulfobetaine and Carboxybetaine Polymers on Glass Slides.</a> Langmuir. 22 (24), 10072-10077 (2006).</li><li>Chen, S., Li, L., Zhao, C., Zheng, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+hydration:+principles+and+applications+toward+low-fouling/nonfouling+biomaterials.">Surface hydration: principles and applications toward low-fouling/nonfouling biomaterials.</a> Polymer. 51 (23), 5283-5293 (2010).</li><li>Bengani, P., Kou, Y. M., Asatekin, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Zwitterionic+copolymer+self-assembly+for+fouling+resistant,+high+flux+membranes+with+size-based+small+molecule+selectivity.">Zwitterionic copolymer self-assembly for fouling resistant, high flux membranes with size-based small molecule selectivity.</a> J Membr Sci. 493, 755-765 (2015).</li><li>Chiang, Y. C., Chang, Y., Chuang, C. J., Ruaan, R. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+facile+zwitterionization+in+the+interfacial+modification+of+low+bio-fouling+nanofiltration+membranes.">A facile zwitterionization in the interfacial modification of low bio-fouling nanofiltration membranes.</a> J Membr Sci. 389, 76-82 (2012).</li><li>Mi, Y. F., Zhao, Q., Ji, Y. L., An, Q. F., Gao, C. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+novel+route+for+surface+zwitterionic+functionalization+of+polyamide+nanofiltration+membranes+with+improved+performance.">A novel route for surface zwitterionic functionalization of polyamide nanofiltration membranes with improved performance.</a> J Membr Sci. 490, 311-320 (2015).</li><li>Shafi, H. Z., Khan, Z., Yang, R., Gleason, K. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+modification+of+reverse+osmosis+membranes+with+zwitterionic+coating+for+improved+resistance+to+fouling.">Surface modification of reverse osmosis membranes with zwitterionic coating for improved resistance to fouling.</a> Desalination. 362, 93-103 (2015).</li><li>Yang, R., Goktekin, E., Gleason, K. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Zwitterionic+Antifouling+Coatings+for+the+Purification+of+High-Salinity+Shale+Gas+Produced+Water.">Zwitterionic Antifouling Coatings for the Purification of High-Salinity Shale Gas Produced Water.</a> Langmuir. 31 (43), 11895-11903 (2015).</li><li>Yang, R., Jang, H., Stocker, R., Gleason, K. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synergistic+Prevention+of+Biofouling+in+Seawater+Desalination+by+Zwitterionic+Surfaces+and+Low-Level+Chlorination.">Synergistic Prevention of Biofouling in Seawater Desalination by Zwitterionic Surfaces and Low-Level Chlorination.</a> Adv Mat. 26 (11), 1711-1718 (2014).</li><li>Azari, S., Zou, L. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Using+zwitterionic+amino+acid+L-DOPA+to+modify+the+surface+of+thin+film+composite+polyamide+reverse+osmosis+membranes+to+increase+their+fouling+resistance.">Using zwitterionic amino acid L-DOPA to modify the surface of thin film composite polyamide reverse osmosis membranes to increase their fouling resistance.</a> J Membr Sci. 401, 68-75 (2012).</li><li>Chang, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Underwater+Superoleophobic+Surfaces+Prepared+from+Polymer+Zwitterion/Dopamine+Composite+Coatings.">Underwater Superoleophobic Surfaces Prepared from Polymer Zwitterion/Dopamine Composite Coatings.</a> Adv Mater Inter. , (2016).</li><li>Lin, H., Kai, T., Freeman, B. D., Kalakkunnath, S., Kalika, D. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Effect+of+Cross-Linking+on+Gas+Permeability+in+Cross-Linked+Poly(Ethylene+Glycol+Diacrylate).">The Effect of Cross-Linking on Gas Permeability in Cross-Linked Poly(Ethylene Glycol Diacrylate).</a> Macromolecules. 38 (20), 8381-8393 (2005).</li><li>Sagle, A. C., Ju, H., Freeman, B. D., Sharma, M. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=PEG-based+hydrogel+membrane+coatings.">PEG-based hydrogel membrane coatings.</a> Polymer. 50 (3), 756-766 (2009).</li><li>Wu, Y. -. H., Park, H. B., Kai, T., Freeman, B. D., Kalika, D. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Water+uptake,+transport+and+structure+characterization+in+poly(ethylene+glycol)+diacrylate+hydrogels.">Water uptake, transport and structure characterization in poly(ethylene glycol) diacrylate hydrogels.</a> J Membr Sci. 347 (1-2), 197-208 (2010).</li><li>Rahimpour, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Novel+functionalized+carbon+nanotubes+for+improving+the+surface+properties+and+performance+of+polyethersulfone+(PES)+membrane.">Novel functionalized carbon nanotubes for improving the surface properties and performance of polyethersulfone (PES) membrane.</a> Desalination. 286, 99-107 (2012).</li><li>Gulmine, J. V., Janissek, P. R., Heise, H. M., Akcelrud, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polyethylene+characterization+by+FTIR.">Polyethylene characterization by FTIR.</a> Polym Testing. 21 (5), 557-563 (2002).</li><li>Ara&#250;jo, J. R., Waldman, W. R., De Paoli, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermal+properties+of+high+density+polyethylene+composites+with+natural+fibres:+Coupling+agent+effect.">Thermal properties of high density polyethylene composites with natural fibres: Coupling agent effect.</a> Polym. Degrad. Stab. 93 (10), 1770-1775 (2008).</li><li>McCloskey, B. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+polydopamine+deposition+conditions+on+pure+water+flux+and+foulant+adhesion+resistance+of+reverse+osmosis,+ultrafiltration,+and+microfiltration+membranes.">Influence of polydopamine deposition conditions on pure water flux and foulant adhesion resistance of reverse osmosis, ultrafiltration, and microfiltration membranes.</a> Polymer. 51 (15), 3472-3485 (2010).</li></ol>

我々は、自立フィルムおよび両性イオン性ヒドロゲルに基づいた含浸膜を調製する容易な方法を実証しました。 3（メタ）アクリレートの特徴的なピーク（ すなわち 、810、1,190、及び1410センチメートル-1）得られたポリマーフィルムのIRスペクトルでの消失、膜を含浸させた（ 図2）は 、モノマーおよび架橋剤4の良好な変換を示し<sup class...

増大する需要を満たすためにきれいな水を生成するために、低コストかつエネルギー効率の高い技術を開発する大きな必要性があります。ポリマー膜は、動作1におけるそれらの高いエネルギー効率、低コスト、および単純として、それらの固有の利点に水浄化のための主要な技術として浮上しています。膜は、純水を透過して汚染物質を拒否することができます。しかしながら、膜は、しばしば、それらの有利な相互作用2、3から膜表面に吸着することができる給水中の汚染物質により汚染にさらされます。ファウリングは劇的に必要な膜面積及び水の浄化のコストを増加させる、膜を通して水の流量を減少させることができます。 ファウリングを軽減する効果的なアプローチは、親水性を増加させ、従って良好でを減少させるために、膜表面を改質することです膜表面と汚染物質との間のteractions。一つの方法は、超親水3つのヒドロゲルで薄膜コーティングを使用することです。ヒドロゲルは、多くの場合、高い透水性を持っています。従って、薄膜コーティングは、膜全体を横切るわずかに増加輸送抵抗にもかかわらず、原因緩和ファウリングに膜を通して長期水透過性を増加させることができます。ヒドロゲルはまた、直接浸透アプリケーション4に水浄化用含浸膜に製造することができます。 双性イオン性材料は、正味中性の電荷の両方正と負に帯電した官能基を含有し、静電誘導される水素結合5、6、7、8、9を介して強い表面の水和を有します。強固に結合した水和層は、物理として機能しますエネルギー障壁は、表面に付着する汚染物質を防止する優れた防汚特性10を示します。増加する両性イオン性ポリ（スルホベタインメタクリレート）などのポリマー、（PSBMA）およびポリ（カルボキシベタインメタクリレート）（のpCBMA）11を塗布して膜表面を修飾するために使用されてきた、12、13、14、15、16、17、18表面親水性、したがって防汚性。 ここでは、機械的強度を向上させるために、ポリ（エチレングリコール）ジアクリレート（PEGDA、M N = 700グラム/モル）を使用して架橋される重合を介して、スルホベタインメタクリレート（SBMA）を使用して双性イオン性ヒドロゲルを調製する容易な方法を実証します。我々はまた、提示光重合前に高度に多孔質の疎水性支持体にモノマーと架橋剤を含浸させて堅牢な膜を構築する手順。自立フィルムおよび含浸膜の物理的及び水輸送特性を徹底的に水の浄化のための構造/特性関係を解明することを特徴とします。調製したヒドロゲルは膜の分離特性を向上させるために表面コーティングとして用いることができます。架橋密度を調整することにより、または疎水性多孔質支持体に含浸させることによって、これらの材料はまた、正浸透又は圧力遅延浸透4として浸透プロセスのための十分な機械的強度を有する薄膜を形成することができます。

<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Poly(ethylene glycol) diacrylate&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160; Mn = 700 (PEGDA)</td>
			<td>Sigma Aldrich</td>
			<td>455008</td>
			<td></td>
		</tr>
		<tr>
			<td>1-Hydroxycyclohexyl phenyl ketone, 99% (HCPK)</td>
			<td>Sigma Aldrich</td>
			<td>405612</td>
			<td></td>
		</tr>
		<tr>
			<td>[2-(Methacrloyloxy)ethyl dimethyl-(3-sulfopropyl) ammonium hydroxide, 97%</td>
			<td>Sigma Aldrich</td>
			<td>537284</td>
			<td>Acutely Toxic</td>
		</tr>
		<tr>
			<td>Ethanol, 95%</td>
			<td>Koptec, VWR International</td>
			<td>V1101</td>
			<td>Flamable</td>
		</tr>
		<tr>
			<td>Decane, anhydrous, 99%</td>
			<td>Sigma Aldrich</td>
			<td>457116</td>
			<td></td>
		</tr>
		<tr>
			<td>Solupor Membrane</td>
			<td>Lydall</td>
			<td>7PO7D</td>
			<td></td>
		</tr>
		<tr>
			<td>Micrometer&#160;</td>
			<td>Starrett</td>
			<td>2900-6</td>
			<td></td>
		</tr>
		<tr>
			<td>ATR-FTIR</td>
			<td>Vertex 70</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>DSC: TA Q2000</td>
			<td>TA Instruments</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Rame&#8217;-hart Goniometer: Model 190</td>
			<td>Rame&#8217;-hart Instruments</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Ultraviolet Crosslinker: CX-2000</td>
			<td>Ultra-Violet Products</td>
			<td></td>
			<td>UV radiation&#160;</td>
		</tr>
		<tr>
			<td>Permeation Cell: Model UHP-43</td>
			<td>Advantec MFS</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Deionized Water: Milli-Q Water</td>
			<td>EMD Millipore</td>
			<td></td>
			<td></td>
		</tr>
	</tbody>
</table>

synthesis of hydrogels with antifouling properties as membranes for water purification

ヒドロゲルは広く防汚性を増加させ、したがって、経時膜を通して安定した水透過性を達成する、浄水のための膜の表面の親水性を高めるために利用されてきました。ここでは、膜用途のための両性イオンに基づくヒドロゲルを製造するための容易な方法を報告しています。自立フィルムは、光重合を介してポリ架橋剤（エチレングリコール）ジアクリレート（PEGDA）とスルホベタインメタクリレート（SBMA）から調製することができます。ヒドロゲルはまた、機械的強度を高めるために、疎水性の多孔性支持体に含浸させることにより調製することができます。これらのフィルムは、ポリマー鎖のダイナミクスのための親水性および示差走査熱量測定（DSC）のためのゴニオメータを用いて、（メタ）アクリレート基の転化の程度を決定するための赤外分光法（ATR-FTIR）を形質転換減衰全反射フーリエ変換によって特徴付けることができます。また、デッドエンドFILTRAに透水性を決定するためのプロトコルを報告しますンシステム及び膜性能に対する汚染物質の影響（ウシ血清アルブミン、BSA）。

ステップ1.1と1.2で指定されたプレポリマー溶液を用いて調製した自立膜は、それぞれ、S50とS30と呼ばれます。詳細情報は、表1に示されています。ステップ1.2で指定されたプレポリマー溶液はまた、IMS30として示される含浸膜を作製しました。多孔性支持体を疎水性ポリエチレンで作られているので、エタノールを含?...

Watch this Scientific Journal Video about Synthesis of Hydrogels with Antifouling Properties As Membranes for Water Purification at JoVE.com

Synthesis of Hydrogels with Antifouling Properties As Membranes for Water Purification

This paper reports practical methods to prepare hydrogels in freestanding films and impregnated membranes and to characterize their physical properties, including water transport properties.

水質浄化のための膜のような防汚特性を持つハイドロゲルの合成

Hydrogels have been widely utilized to enhance the surface hydrophilicity of membranes for water purification, increasing the antifouling properties and ...

Research

JoVE Journal

Bioengineering

Quantifying the Mechanical Properties of the Endothelial Glycocalyx with Atomic Force Microscopy

原子間力顕微鏡と内皮グリコカリックスの機械的性質の定量化

Our  understanding of the interaction of leukocytes and the vessel wall during  leukocyte capture is limited by an incomplete understanding of the ...

Preparation of Light-responsive Membranes by a Combined Surface Grafting and Postmodification Process

複合表面グラフトと後置修飾法による光応答膜の調製

In order to modify the surface tension of commercial available track-edged polymer membranes, a procedure of surface-initiated polymerization is ...

Combination of Microstereolithography and Electrospinning to Produce Membranes Equipped with Niches for Corneal Regeneration

角膜再生のためのニッチを装備膜を製造するためのマイクロ光とエレクトロスピニングの組み合わせ

Corneal problems affect millions of people worldwide reducing their quality of life significantly. Corneal disease can be caused by illnesses such as ...

Three-Dimensionally Printed Microfluidic Cross-flow System for Ultrafiltration/Nanofiltration Membrane Performance Testing

限外濾過/ナノ濾過膜性能試験のための三次元プリントマイクロ流体クロスフローシステム

Minimization and management of membrane fouling is a formidable challenge in diverse industrial processes and other practices that utilize membrane ...

Transport Properties of Ibuprofen Encapsulated in Cyclodextrin Nanosponge Hydrogels: A Proton HR-MAS NMR Spectroscopy Study

シクロデキストリンNanospongeヒドロゲル中のイブプロフェンカプセル化の輸送特性：プロトンHR-MAS NMR分光研究

The chemical cross-linking of &#946;-cyclodextrin (&#946;-CD) with ethylenediaminetetraacetic dianhydride (EDTA) led to branched polymers referred to as ...

The Synthesis of RGD-functionalized Hydrogels as a Tool for Therapeutic Applications

治療用途のためのツールとしてのRGD官能ヒドロゲルの合成

The use of polymers as biomaterials has provided significant advantages in therapeutic applications. In particular, the possibility to modify and ...

Synthesis of Biocompatible Liquid Crystal Elastomer Foams as Cell Scaffolds for 3D Spatial Cell Cultures

3D空間の細胞培養のための細胞骨格などの生体適合性液晶エラストマー発泡体の合成

Here, we present a step-by-step preparation of a 3D, biodegradable, foam-like cell scaffold. These scaffolds were prepared by cross-linking star block ...

Ultrathin Porated Elastic Hydrogels As a Biomimetic Basement Membrane for Dual Cell Culture

デュアルのバイオミメティック基底膜として極薄 Porated 弾性ゲルの細胞培養

The basement membrane is a critical component of cellular bilayers that can vary in stiffness, composition, architecture, and porosity. In vitro studies ...

Synthesis of Multi-walled Carbon Nanotubes Modified with Silver Nanoparticles and Evaluation of Their Antibacterial Activities and Cytotoxic Properties

銀ナノ粒子とその抗菌活性と細胞毒性の評価変更多層カーボンナノ チューブの合成

In this study, multi-walled carbon nanotubes (MWCNTs) were treated with an aqueous sulfuric acid solution to form an oxygen-based functional group. Silver ...

Immobilization of Live Caenorhabditis elegans Individuals Using an Ultra-thin Polydimethylsiloxane Microfluidic Chip with Water Retention

Immobilization of Live Caenorhabditis elegans Individuals Using an Ultra-thin Polydimethylsiloxane Microfluidic Chip with Water Retention

極薄ポリジメチルシロキサン マイクロ流体チップを用いた保水ライブ線虫個人の固定化

Radiation is widely used for biological applications and for ion-beam breeding, and among these methods, microbeam irradiation represents a powerful means ...