Name: mimicking and measuring occlusal erosive tooth wear with the "rub&amp;roll" and non-contact profilometry
Uploaded: 2018-02-02T12:30:00
Description: Watch this Scientific Journal Video about Mimicking and Measuring Occlusal Erosive Tooth Wear with the "Rub&Roll" and Non-contact Profilometry at JoVE.com

लेखकों को कोई पावती नहीं है ।

इस प्रयोग में प्रयुक्त दांतों का संग्रह क्षेत्रीय चिकित्सा आचार समिति के दिशानिर्देशों के अनुसार किया गया था ।
1. नमूना संग्रह और नमूना तैयारी
<ol><li>दंत व्यवहार से 24 ध्वनि निकाले मानव (पूर्व) द?...

<ol>
	<li>Anderson, K., Throckmorton, G. S., Buschang, P. H., Hayasaki, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+effects+of+bolus+hardness+on+masticatory+kinematics.">The effects of bolus hardness on masticatory kinematics.</a> J Oral Rehabil. 29, 689-696 (2002).</li><li>Koolstra, J. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamics+of+the+human+masticatory+system.">Dynamics of the human masticatory system.</a> Crit Rev Oral Biol M. 13 (4), 366-376 (2002).</li><li>Lepley, C. R., Throckmorton, G. S., Ceen, R. F., Buschang, P. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Relative+contributions+of+occlusion,+maximum+bite+force,+and+chewing+cycle+kinematics+to+masticatory+performance.">Relative contributions of occlusion, maximum bite force, and chewing cycle kinematics to masticatory performance.</a> Am J Orthod Dentofac. 13, 606-613 (2011).</li><li>Lee, A., He, H., Lyons, K., Swain, M. V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tooth+wear+and+wear+investigations+in+dentistry.">Tooth wear and wear investigations in dentistry.</a> J Oral Rehabil. 39, 217-225 (2012).</li><li>Lussi, A., Megert, B., Shellis, R. P., Wang, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Analysis+of+the+erosive+effect+of+different+dietary+substances+and+medications.">Analysis of the erosive effect of different dietary substances and medications.</a> Br J Nutr. 107, 252-262 (2012).</li><li>Vieira, A., Overweg, E., Ruben, J. L., Huysmans, M. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Toothbrush+abrasion,+simulated+tongue+friction+and+attrition+of+eroded+bovine+enamel+in+vitro.">Toothbrush abrasion, simulated tongue friction and attrition of eroded bovine enamel in vitro.</a> J Dent. 34 (5), 336-342 (2006).</li><li>Heintze, S. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=How+to+qualify+and+validate+wear+simulation+devices+and+methods.">How to qualify and validate wear simulation devices and methods.</a> Dent Mater. 22, 712-734 (2006).</li><li>Lambrechts, P., Dibbles, E., van Landuyt, K., Peumans, M., van Meerbeek, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=How+to+simulate+wear?+Overview+of+existing+methods.">How to simulate wear? Overview of existing methods.</a> Dent Mater. 22, 693-701 (2006).</li><li>Ruben, J. L., Roeters, F. J. M., Montagner, A. F., Huysmans, M. C. D. N. J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+multifunctional+device+to+simulate+oral+ageing:+the+"Rub&amp;Roll".">A multifunctional device to simulate oral ageing: the "Rub&amp;Roll".</a> J Mech Behav Biomed Mater. 30, 75-82 (2014).</li><li>Xu, W. L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Review+of+the+human+masticatory+system+and+masticatory+robotics.">Review of the human masticatory system and masticatory robotics.</a> Mech Mach Theory. 43, 1353-1375 (2008).</li><li>Abrahamsen, T. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+worn+dentition+pathognomonic+patterns+of+abrasion+and+erosion.">The worn dentition pathognomonic patterns of abrasion and erosion.</a> Int Dent J. 55, 268-276 (2005).</li><li>Khan, F., Young, W. G., Law, V., Priest, J., Daley, D. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cupped+lesions+of+early+onset+dental+erosion+in+young+southeast+Queensland+adults.">Cupped lesions of early onset dental erosion in young southeast Queensland adults.</a> Aust Dent J. 46, 100-107 (2001).</li><li>Montagner, A. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Bonding+Efficacy+and+Fracture+Pattern+of+Adhesives+Submitted+to+Mechanical+Aging+with+the+Rub&amp;Roll+Device.">Bonding Efficacy and Fracture Pattern of Adhesives Submitted to Mechanical Aging with the Rub&amp;Roll Device.</a> J Adhes Dent. 19, 59-68 (2017).</li><li>Martinez Choy, S. E., Lenz, J., Schweizerhof, K., Schmitter, M., Schindler, H. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Realistic+kinetic+loading+of+the+jaw+system+during+single+chewing+cycles:+a+finite+element+study.">Realistic kinetic loading of the jaw system during single chewing cycles: a finite element study.</a> J Oral Rehabil. 44, 375-384 (2017).</li></ol>

यहां प्रस्तुत आवेदन रगड़ और रोल के नैदानिक प्रासंगिकता का एक अच्छा प्रभाव देता है । उच्चतम लोड हो रहा है स्तर के साथ प्रयोग में बनाया गया था कि occlusal आकृति विज्ञान कटाव दांत पहनने की नैदानिक प्रस्तुति के ?...

मौखिक गुहा एक कठोर वातावरण माना जा सकता है: आर्द्रता, तापमान गर्म और ठंडे भोजन के सेवन के कारण परिवर्तन, और मानव शरीर में सबसे मजबूत मांसपेशियों में से कुछ के साथ यांत्रिक लोड हो रहा है । दांत, तथापि, इन चुनौतियों का सामना करने के लिए खासे सुसज्जित हैं । तामचीनी बहुत कठिन है, और नीचे दंतधातु fracturing से अपेक्षाकृत भंगुर तामचीनी रोकता है । दोनों सामग्री के खनिज घटक, hydroxyapatite बहुत कम घुलनशीलता की है और supersaturated लार के साथ संतुलन में । चबाने, पीने, और सामयिक दांत पीसने एक जीवनकाल1,2,3के दौरान शारीरिक दांत पहनने में परिणाम होगा । ऐसे बुक्सिज्म या अभ्यस्त विदेशी वस्तुओं पर चबाने के रूप में चरम चुनौतियों, अत्यधिक पहनने के लिए नेतृत्व कर सकते हैं । हाल ही में मैकेनिकल टूथ वियर को तेज करने में कटाव की भूमिका को मान्यता मिली है । दांत कटाव गया है बड़े पैमाने पर इन विट्रो मेंअध्ययन किया है, लेकिन इस्तेमाल किया मॉडल आम तौर पर सरल किया गया है, और यांत्रिक कारकों काफी हद तक नजरअंदाज कर दिया गया है । रासायनिक और यांत्रिक पहनने प्रक्रियाओं के बीच नैदानिक खेल इसलिए4पूरी तरह से समझ नहीं है ।
इन विट्रो कटाव और क्षरण पहनने के अध्ययन में कई फ्लैट पॉलिश तामचीनी या dentine नमूनों की सरल एसिड विसर्जन का उपयोग किया है, कठोरता हानि या माप दृष्टिकोण5के रूप में profilometry का उपयोग कर । एक घर्षण घटक की शुरूआत आम तौर पर शामिल किया गया है टूथ ब्रशिंग कार्रवाई, या कई बार जीभ या तामचीनी cusp फिसलने संपर्क6। इस तरह के अध्ययनों से पता चला है कि एक नरम सतह परत में तामचीनी कटाव परिणाम है, जो आसानी से abraded है । यांत्रिक लोडिंग डिवाइस असमान सतहों को हैंडल नहीं कर सकते, और असमान सतहों के लिए मापने तकनीक भी अधिक जटिल हैं क्योंकि फ्लैट सतहों आम तौर पर की जरूरत है । हालांकि, किशोरों में सबसे कटाव दांत पहनने occlusal cusps पर देखा जाता है, और भोजन चबाने से घर्षण occlusal कटाव पहनने में सबसे अधिक प्रासंगिक यांत्रिक कारक होने की उंमीद है । आदर्श मौखिक पहनने की मशीन है कि सभी विवरण में मौखिक वातावरण नकल मौजूद नहीं है, और सबसे इन विट्रो मॉडल के लिए अनुमति नहीं देगा दांतों की प्राकृतिक occlusal सतहों के लिए या तो उजागर या7मापा,8।
हमारी प्रयोगशाला ने हाल ही में एक उपंयास डिवाइस है, जो Heintze के7 विनिर्देशों और मौखिक पहनने सिमुलेशन मॉडल की सहनशीलता के कई अनुरूप है, और है कि उपयोगकर्ता के लिए सक्षम बनाता है पहनते है और लोड हो रहा है या अलग से अध्ययन में एक साथ पेश कटाव और/या घर्षण पर्यावरण । नई डिवाइस (रगड़ और रोल) एक सरगर्मी मशीन और एक कंटेनर (चित्र 1a) के होतेहैं । कंटेनर में, नमूनों के साथ एक सिलेंडर घुड़सवार किया जा सकता है । सिलेंडर के बीच और कंटेनर की भीतरी दीवार के बीच एक और छड़ रखा (आंकड़ा 1b) रहे हैं । सरगर्मी मोटर शुरू करके, रॉड सिलेंडर में नमूनों (चित्रा 1c) के ऊपर घूमता है । परत का प्रयोग, विभिंन बलों के नमूनों पर लागू किया जा सकता है । डिजाइन, निर्माण, आपरेशन तंत्र, और डिवाइस की सुविधाओं का एक व्यापक विवरण के लिए कागज शुरू करने और डिवाइस पर चर्चा करने के लिए देखें9. डिवाइस मजबूत है, तकनीकी रूप से मांग नहीं है, और एक साथ ३२ नमूनों के लिए लोड लागू कर सकते हैं । विरोधी बल नमूना सतह पर चलती है, जबकि चिकनी, सतत संपर्क है, जो सामांय चबाने10के बराबर है बनाए रखने । यहां हम occlusal प्राकृतिक दांत की सतहों के मॉडल कटाव पहनने के लिए एक आवेदन पेश करते हैं, और हम नैदानिक प्रासंगिकता और विधि की बहुमुखी प्रतिभा का प्रदर्शन ।

<table>
	<tbody>
		<tr>
			<td>Low speed handpiece</td>
			<td>KAVO, Leutkirch imm Allgau, Germany</td>
			<td></td>
			<td>Dental equipment</td>
		</tr>
		<tr>
			<td>Brush for handpiece</td>
			<td>KAVO, Leutkirch imm Allgau, Germany</td>
			<td></td>
			<td>Dental equipment</td>
		</tr>
		<tr>
			<td>Pumish</td>
			<td></td>
			<td></td>
			<td>Dental equipment</td>
		</tr>
		<tr>
			<td>Human third molars</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Impression compound green</td>
			<td>Kerr, Bioggio, Switzerland</td>
			<td>Art.nr. 00444</td>
			<td></td>
		</tr>
		<tr>
			<td>Microscope slide</td>
			<td>Menzel, Braunschweig, Germany</td>
			<td></td>
			<td>76 x 26 mm</td>
		</tr>
		<tr>
			<td>Autoplast Cold curing denture base material</td>
			<td>Candulor, Wangen, Switzerland</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Silicone mold with inside dimensions of 12 x 15 x 27.5</td>
			<td>3M Espe Neuss, Germany</td>
			<td>Express STD</td>
			<td></td>
		</tr>
		<tr>
			<td>Pressure vessel</td>
			<td>Al Dente, Meckenbeuren, Germany</td>
			<td>581-009-024/25</td>
			<td></td>
		</tr>
		<tr>
			<td>Milling cutter &#248;16mm</td>
			<td>Format, Germany</td>
			<td>HSSCo8 nr. 21691600</td>
			<td></td>
		</tr>
		<tr>
			<td>Milling machine</td>
			<td>Weiss Machine Tools</td>
			<td>WMD 20 LV</td>
			<td></td>
		</tr>
		<tr>
			<td>Rub&#38;Roll</td>
			<td>UMCN , Nijmegen The Netherlands</td>
			<td></td>
			<td>Technical workshop</td>
		</tr>
		<tr>
			<td>Rub&#38;Roll container</td>
			<td>UMCN , Nijmegen The Netherlands</td>
			<td></td>
			<td>Technical workshop</td>
		</tr>
		<tr>
			<td>Rub&#38;Roll cylinder sample holder</td>
			<td>UMCN , Nijmegen The Netherlands</td>
			<td></td>
			<td>Technical workshop</td>
		</tr>
		<tr>
			<td>Rub&#38;Roll motor</td>
			<td>UMCN , Nijmegen The Netherlands</td>
			<td></td>
			<td>Technical workshop</td>
		</tr>
		<tr>
			<td>Shim: Silicone plate massive 1 mm/ 1,5mm, 60 &#177; 5&#176; Shore A, red</td>
			<td>Peter van den Berg afdichtingstechniek, Barendrecht</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Lactid acid extra pure 88%</td>
			<td>Boom, The Netherlands</td>
			<td>CAS nummer: 79-33-4</td>
			<td></td>
		</tr>
		<tr>
			<td>Calcium Chloride dihydrate CaCL2 .2H2O</td>
			<td>Merck, Darmstadt, Germany</td>
			<td>CAS nummer: 10043-52-4</td>
			<td></td>
		</tr>
		<tr>
			<td>Pottassium dihydrogen Phosphate KH2PO4</td>
			<td>Merck, Darmstadt, Germany</td>
			<td>CAS nummer: 7778-77-0</td>
			<td></td>
		</tr>
		<tr>
			<td>Chloramine T (sodium salt) trihydrate for synthesis CH3C6H4SO2NClNa&#183;3H2O</td>
			<td>Merck, Darmstadt, Germany</td>
			<td>CAS nummer: 7080-50-4</td>
			<td></td>
		</tr>
		<tr>
			<td>Natriumfluoride standard solution 1000mg/L F Certipur</td>
			<td>Merck, Darmstadt, Germany</td>
			<td>CAS nummer: 7681-49-4</td>
			<td></td>
		</tr>
		<tr>
			<td>Deionized water</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Kaliumhydroxide, pellets EMSURE analytical reagent KOH</td>
			<td>Merck, Darmstadt, Germany</td>
			<td>CAS nummer: 1310-58-3</td>
			<td></td>
		</tr>
		<tr>
			<td>PVC tube(Hardness73 Shore A)outer diameter 14mm inner diameter 10mm</td>
			<td>DEUTSCH &#38; NEUMANN, Germany</td>
			<td>Art.nr. 3501014</td>
			<td></td>
		</tr>
		<tr>
			<td>Insert of a stainless steel 316 (Hardness 130&#8211;150 HB) diameter 9mm</td>
			<td>UMCN , Nijmegen The Netherlands</td>
			<td></td>
			<td>Technical workshop</td>
		</tr>
		<tr>
			<td>pH glass electrode</td>
			<td>WTW, Weilheim, Germany</td>
			<td>Sentix 61 103640</td>
			<td></td>
		</tr>
		<tr>
			<td>Non contact Profilometer Proscan 2100</td>
			<td>Scantron Industrial Products Ltd, Taunton, UK</td>
			<td></td>
			<td>http://www.scantronltd.co.uk</td>
		</tr>
		<tr>
			<td>Software version Proscan 2100 2.1.1.15A+ Sensor S29 / 10-10000 microns</td>
			<td>Scantron Industrial Products Ltd, Taunton, UK</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Software version Proform</td>
			<td>Scantron Industrial Products Ltd, Taunton, UK</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Stereomicroscope Leica</td>
			<td>www.leica-microsystems.com</td>
			<td>M50</td>
			<td></td>
		</tr>
		<tr>
			<td>Photocamera Canon</td>
			<td>Canon Japan</td>
			<td>EOS 50D</td>
			<td></td>
		</tr>
		<tr>
			<td>Syringe</td>
			<td>BD Plastipak, Spain</td>
			<td>20 ml.</td>
			<td></td>
		</tr>
		<tr>
			<td>Hotplate</td>
			<td>Schott instruments Mainz</td>
			<td>SLK1</td>
			<td></td>
		</tr>
		<tr>
			<td>Silone impression material (Vinyl Polysiloxane Expres)</td>
			<td>3M Espe , USA</td>
			<td>Regular</td>
			<td></td>
		</tr>
		<tr>
			<td>Stirring Plate</td>
			<td>IKA Werke, Germany</td>
			<td>KMO2 Basic</td>
			<td></td>
		</tr>
	</tbody>
</table>

mimicking and measuring occlusal erosive tooth wear with the "rub&amp;roll" and non-contact profilometry

चबाने, पीने, और सामयिक दांत पीसने एक जीवन भर के दौरान शारीरिक दांत पहनने में परिणाम होगा । ऐसे बुक्सिज्म या अभ्यस्त विदेशी वस्तुओं पर चबाने के रूप में चरम चुनौतियों, अत्यधिक पहनने के लिए नेतृत्व कर सकते हैं । हाल ही में मैकेनिकल टूथ वियर को तेज करने में कटाव की भूमिका को मान्यता मिली है, लेकिन केमिकल और मैकेनिकल वियर प्रक्रियाओं के बीच अंतर का बड़े पैमाने पर अध्ययन नहीं किया गया है । हमारी प्रयोगशाला ने हाल ही में एक उपंयास मौखिक पहनने सिमुलेशन उपकरण, रगड़ और रोल, कि उपयोगकर्ता के लिए सक्षम बनाता है पहनते है और लोड हो रहा है या अलग से अध्ययन एक साथ एक कटाव और/ इस पांडुलिपि डिवाइस के एक आवेदन का वर्णन: संयुक्त यांत्रिक और कटाव लोडिंग निकाली मानव (पूर्व) के एक नकली चबाने आंदोलन में दाढ़, बल, वेग, द्रव, और समय के एक नियंत्रित आवेदन के साथ, और के आवेदन गैर संपर्क visualizing और परिणामस्वरूप पहनने के पैटर्न को मापने में profilometry । सबसे अधिक लदान स्तर के साथ प्रयोग में बनाया गया था कि occlusal आकृति विज्ञान कटाव पहनने के नैदानिक प्रस्तुति के लिए बहुत समान है ।

हम मानव दाढ़ दांत उजागर (n = प्रति समूह 8) रगड़ और रोल में पीएच ४.८ में एक अंलीय जलीय समाधान के लिए, 3 महीने के लिए । यह लगभग 6 वर्षों के एक नैदानिक कार्य समय से मेल खाती है । लागू किया गया यांत्रिक लो...

Watch this Scientific Journal Video about Mimicking and Measuring Occlusal Erosive Tooth Wear with the "Rub&Roll" and Non-contact Profilometry at JoVE.com

Mimicking and Measuring Occlusal Erosive Tooth Wear with the "Rub&Roll" and Non-contact Profilometry

रगड़ और रोल चबाने चक्र की नकल कर सकते हैं, चबाने बल के परिवर्तन की अनुमति, दूरी फिसलने, वेग चबाने, चक्र की संख्या, और आवृत्ति, और कटाव और घर्षण चुनौतियों का एक संयोजन के साथ मौखिक उंर बढ़ने के एक जटिल अनुकरण में परिणाम कर सकते हैं ।

नकल उतार और "रगड़ और रोल" और गैर संपर्क Profilometry के साथ Occlusal कटाव दांत पहनने को मापने

Chewing, drinking, and occasional tooth grinding will result in physiological tooth wear during a lifetime. Extreme challenges, such as bruxism or ...

The overall goals of this experiment are to apply mechanical loading in an erosive environment to mimic the clinical dental wear process and to use non-contact profilometry for visualization and measurement of the resulting wear pattern. This method can help answering key questions about etiology in erosive tooth wear, such as which factors influence erosive tooth wear and how do they interact? The main advantage of this technique is that it facilitates a simulation of the clinical interplay between chemical and mechanical wear processes.Though this method can provide insight in etiology and pathogenesis of tooth wear, it can also be applied to other system, such as cyclic loading to mimic fatigue and to test the amount of wear of dental restorations. Begin by using a low-speed hand piece to brush 24 sound extracted human molars with pumice until no debris or gingival remnants remain. When all of the teeth have a smooth surface, rinse each specimen for 15 seconds under running tap water.Next, melt one 113 gram stick of impression compound on a 50 degree Celsius hot plate for approximately 10 minutes. And dip the occlusal end of the first molar into the molten substance until the entire occlusal surface is covered. Place the molar upside down on a glass microscope slide and press down until all of the cup tips touch the glass.When all of the molars have been set, use a syringe to dispense 10 milliliters of polymethylmethacrylate, or PMAA mixture, until one 12 x 15 x 27.5 millimeter silicon mold per tooth, and suspend each molar upside down in the PMAA, pressing the slides down until they touch the molds. When all of the samples have been immersed, allow the PMAA to set at room temperature and 1, 000 hectopascals. After 20 minutes, remove the teeth from the molds and use a milling machine equipped with a 16 millimeter milling cutter to adjust the height of each sample to exactly 27.3 millimeters.To scan the specimens, turn on the profilometer equipment and secure the appropriate sensor with a thumb screw. Carefully insert the optical fiber in the sensor controller and select the correct sensor on the sensor controller. Press F4 twice to display the confocal sensor menu, then press F3 and scroll to 2 to 10, 000 micrometers.Select 10 millimeters and press F4.Press F1 and select F4 to save the settings to memory, then select LED intensity and adjust the position to plus or minus 9-o'clock. Press F4 then F2 then F4 again to obtain a dark reference of the sensor. Next, open the software and connect to the device.The measuring table will automatically move to the home position search. Under the tools menu, click sensor selection. Then set sensor S29 to 10 to 10, 000 micrometers.Set the sample rate 300 Hertz. And the speed sensor to 0 to 100%Under scan, select key move stage and select the yellow area in the middle of the screen to move the measuring table to the center of the viewing area. Place the sensor above the area of interest on the specimen and adjust the distance of the sensor until the complete sample area to be scanned is located within the focus range of the sensor.When the height is within the range of the sensor, the sensor controller will display a green area in the live data height. Set the average to 2 to ensure that each recorded data point is the average of two measurements. Click OK to return to the main scanning setup and position the sensor beam on the upper left corner of the specimen.Set the total scan area to 15 x 12 millimeters with the step size of 40 micrometers in the X and Y directions and click scan to begin the scanning, saving the file when the scan is over. To analyze the scanned files, under the warpage menu, apply a warpage filter of 1 to eliminate the noise of the scanning table and sensor, and select the highest point menu to find the highest point on the molar. Under tools, select option scale for the scan configuration and set the offset in millimeters as calculated by the Z value of the highest point minus 3, 500.Set the range from 0 to 3.6 millimeters and click OK.Then open the load area menu bar to reset the scale and save the file. When all of the molars have been scanned, remove the cylinder from the Rub&Roll machine container and place the molars into the cylinder recesses. To adjust the loading force, place a 1 millimeter shim in the recess underneath eight specimens and a 1.5 millimeter shim under a second set of eight specimens, leaving the last set of eight specimens load free.Next, mount the two halves of the cylinder, then secure the cylinder with an M6 bolt. Place the cylinder back into the container and fill the container with 500 millimeters of demineralization solution. Insert the loading rod and set the rotation speed to 20 RPM to simulate a relevant clinical chewing frequency.Without interrupting the rotation, replace the demineralization solution and loading tube and use a calibrated glass electrode to check the pH twice a week. After three months, disconnect the cylinder from the container and disassemble the cylinder to remove the samples. Then scan the specimens as just demonstrated and store them in the ionized water.For profilometric subtraction of the scanned data, open the original and modified scan files and select manual leveling for the original scanned file and offset for the modified scan file. Under the window menu, select Create View and Cross Section. Select the modified scan file surface and use the control and arrow keys to move the modified file surface over the surface of the original file until the subtracted volume and height appear in the difference view and are as low as possible.Light microscopy reveals the presence of saucer-shaped lesions on the occlusal cusped tips of molars exposed to three moths of acidic aqueous solution under mechanical loading conditions in the rub and roll, as just demonstrated. This cupping closely resembles the clinical phenomenon associated with erosive tooth wear and is further apparent by color mapping after scanning with a non-contact profilometer, as just demonstrated. Indeed, profilometric scanning before and after exposure allows comparison of the differences in molar cusp tip erosion over time as well as the quantification of the mean occlusal surface height loss for each sample under various mechanical load pressure conditions.Following this procedure, other processes may be investigated, such as aging of dental restorations, or the development of carious lesions in mechanically loaded teeth. After watching this video, you should have a good understanding how to use the Rub&Roll for mechanical and chemical loading in simulated chewing movements under controlled force, velocity, fluids and time conditions.

Research

JoVE Journal

Bioengineering

Mimicking and Measuring Occlusal Erosive Tooth Wear with the "Rub&amp;Roll" and Non-contact Profilometry

Gold Nanostar Synthesis with a Silver Seed Mediated Growth Method

गोल्ड एक रजत बीज मध्यस्थता ग्रोथ विधि के साथ nanostar संश्लेषण

The physical, chemical and optical properties of nano-scale colloids depend on their material composition, size and shape 1-5. There is a great interest ...

Measuring Left Ventricular Pressure in Late Embryonic and Neonatal Mice

मापने देर भ्रूण और नवजात चूहे में छोड़ दिया ventricular दबाव

Blood pressure increases significantly during embryonic and postnatal development in vertebrate animals. In the mouse, blood flow is first detectable ...

Non-contact, Label-free Monitoring of Cells and Extracellular Matrix using Raman Spectroscopy

गैर संपर्क, सेल और बाह्य मैट्रिक्स का उपयोग करते हुए रमन स्पेक्ट्रोस्कोपी का लेबल मुक्त निगरानी

Non-destructive, non-contact and label-free technologies to monitor cell and tissue cultures are needed in the field of biomedical research.1-5 However, ...

Creating Adhesive and Soluble Gradients for Imaging Cell Migration with Fluorescence Microscopy

प्रतिदीप्ति माइक्रोस्कोपी के साथ इमेजिंग सेल प्रवासन के लिए चिपकने वाला और घुलनशील Gradients बनाना

Cells can sense and migrate towards higher concentrations of adhesive cues such as the glycoproteins of the extracellular matrix and soluble cues such as ...

In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint

In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint

सीटू Compressive लोड हो रहा है और हड्डी periodontal बंधन टूथ तंतु संधि के correlative noninvasive इमेजिंग में

This study demonstrates a novel biomechanics testing protocol. The advantage of this protocol includes the use of an in situ loading device coupled to a ...

Microfluidic Platform for Measuring Neutrophil Chemotaxis from Unprocessed Whole Blood

Unprocessed पूरे रक्त से न्युट्रोफिल Chemotaxis मापने के लिए मंच microfluidic

Neutrophils play an essential role in protection against infections and their numbers in the blood are frequently measured in the clinic. Higher ...

Measuring and Modeling Contractile Drying in Human Stratum Corneum

मापने और मानव परत corneum में मॉडलिंग सिकुड़ा सुखाने

Stratum corneum (SC) is the most superficial skin layer. Its contact with the external environment means that this tissue layer is subjected to both ...

Preparation and Characterization of Novel HDL-mimicking Nanoparticles for Nerve Growth Factor Encapsulation

नेवल ग्रोथ फैक्टर इनकैप्सुलेशन के लिए उपन्यास एचडीएल-एमएममिटिंग नैनोपार्टिक्स की तैयारी और विशेषता

The objective of this article is to introduce preparation and characterization methods for nerve growth factor (NGF)-loaded, high-density, lipoprotein ...

Agarose-based Tissue Mimicking Optical Phantoms for Diffuse Reflectance Spectroscopy

Agarose आधारित फैलाना चिंतनशील स्पेक्ट्रोस्कोपी के लिए ऑप्टिकल प्रेतों नकल उतार ऊतक

This protocol describes how to make agarose-based tissue-mimicking phantoms and demonstrates how to determine their optical properties using a ...

Manufacturing Abdominal Aorta Hydrogel Tissue-Mimicking Phantoms for Ultrasound Elastography Validation

अल्ट्रासाउंड Elastography सत्यापन के लिए उदर महाधमनी Hydrogel ऊतक-नकल उतारने प्रेतों विनिर्माण

Ultrasound (US) elastography, or elasticity imaging, is an adjunct imaging technique that utilizes sequential US images of soft tissues to measure the ...