Name: intermediate strain rate material characterization with digital image correlation
Uploaded: 2019-03-01T14:00:00
Description: Watch this Scientific Journal Video about Intermediate Strain Rate Material Characterization with Digital Image Correlation at JoVE.com

The authors acknowledge the great assistance from Dmitrii Klishch, Michel Delannoy, Tyler Musclow, Fraser Kirby, Joshua Ilse and Alex Naftel. Financial support by the National Research Council Canada (NRC) through the Security Materials Technology (SMT) Program is also appreciated.

1. Specimen preparation
<ol>
	<li>Prepare dog bone shaped tensile specimens according to ISO standard6 in advance. 
	NOTE: Similar specimens are also used4.</li>
	<li>Install strain gauges on the tab section (mandatory for load measurement) and on the gauge section (optional for strain measurement) of the tensile specimen.
	<ol>
		<li>Select the proper model of strain gauge based on the size, maximum extension, testing temperature, electrical resistance, etc.<sup cla...

<ol>
	<li>Xiao, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamic+tensile+testing+of+plastic+materials.">Dynamic tensile testing of plastic materials.</a> Polymer Testing. 27 (2), 164-178 (2008).</li><li>Nemat-Nasser, S., Isaacs, J. B., Starrett, J. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hopkinson+techniques+for+dynamic+recovery+experiments.">Hopkinson techniques for dynamic recovery experiments.</a> Proceedings of Royal Society of London A Mathematical Physical and Engineering Sciences. 435 (1894), 371-391 (1991).</li><li>Bruce, D., Matlock, D., Speer, J., De, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Assessment+of+the+strain-rate+dependent+tensile+properties+of+automotive+sheet+steels.">Assessment of the strain-rate dependent tensile properties of automotive sheet steels.</a> SAE World Congress. , (2004).</li><li>Rahmat, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamic+mechanical+characterization+of+aluminum:+analysis+of+strain-rate-dependent+behavior.">Dynamic mechanical characterization of aluminum: analysis of strain-rate-dependent behavior.</a> Mechanics Time-Dependent Materials. , (2018).</li><li>Gray, G., Blumenthal, W. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Split-Hopkinson pressure bar testing of soft materials. 8, 1093-1114 (2000).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> ISO 26203-2:2011; Metallic materials-Tensile testing at high strain rates-Part 2: Servo-hydraulic and other test systems. , 15 (2011).</li><li>Rahmat, M., Naftel, A., Ashrafi, B., Jakubinek, M. B., Martinez-Rubi, Y., Simard, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamic+Mechanical+Characterization+of+Boron+Nitride+Nanotube+-+Epoxy+Nanocomposites.">Dynamic Mechanical Characterization of Boron Nitride Nanotube - Epoxy Nanocomposites.</a> Polymer Composites. , (2018).</li><li>. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=SAE,+High+strain+rate+testing+of+polymers.">SAE, High strain rate testing of polymers.</a> SAE International. , 27 (2008).</li><li>Wang, Y., Xu, H., Erdman, D. L., Starbuck, M. J., Simunovic, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+of+high-strain+rate+mechanical+behavior+of+AZ31+magnesium+alloy+using+3D+digital+image+correlation.">Characterization of high-strain rate mechanical behavior of AZ31 magnesium alloy using 3D digital image correlation.</a> Advanced Engineering Materials. 13 (10), 943-948 (2011).</li><li>Mansilla, R. A., Garc&#237;a, D., Negro, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamic+tensile+testing+for+determining+the+stress-strain+curve+at+different+strain+rate.">Dynamic tensile testing for determining the stress-strain curve at different strain rate.</a> 6th International Conference on Mechanical and Physical Behaviour of Materials Under Dynamic Loading. 10 (9), 695-700 (2000).</li><li>Zhu, D., Mobasher, B., Rajan, S. D., Peralta, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+of+Dynamic+Tensile+Testing+Using+Aluminum+Alloy+6061-T6+at+Intermediate+Strain+Rates.">Characterization of Dynamic Tensile Testing Using Aluminum Alloy 6061-T6 at Intermediate Strain Rates.</a> Journal of Engineering Mechanics. 137 (10), 669-679 (2011).</li><li>Schossig, M., Bieroegel, C., Grellmann, W., Bardenheier, R., Mecklenburg, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+strain+rate+on+mechanical+properties+of+reinforced+polyolefins.">Effect of strain rate on mechanical properties of reinforced polyolefins.</a> 16th European Conference of Fracture. , 507-508 (2006).</li><li>Xia, Y., Zhu, J., Wang, K., Zhou, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+and+verification+of+a+strain+gauge-based+load+sensor+for+medium-speed+dynamic+tests+with+a+hydraulic+test+machine.">Design and verification of a strain gauge-based load sensor for medium-speed dynamic tests with a hydraulic test machine.</a> International Journal of Impact Engineering. 88, 139-152 (2016).</li><li>Yang, X., Hector, L. G., Wang, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Combined+Theoretical/Experimental+Approach+for+Reducing+Ringing+Artifacts+in+Low+Dynamic+Testing+with+Servo-hydraulic+Load+Frames.">A Combined Theoretical/Experimental Approach for Reducing Ringing Artifacts in Low Dynamic Testing with Servo-hydraulic Load Frames.</a> Experimental Mechanics. 54 (5), 775-789 (2014).</li><li>Xia, Y., Zhu, J., Zhou, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Verification+of+a+multiple-machine+program+for+material+testing+from+quasi-static+to+high+strain-rate.">Verification of a multiple-machine program for material testing from quasi-static to high strain-rate.</a> International Journal of Impact Engineering. 86, 284-294 (2015).</li><li>Yan, B., Kuriyama, Y., Uenishi, A., Cornette, D., Borsutzki, M., Wong, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Recommended+Practice+for+Dynamic+Testing+for+Sheet+Steels+-+Development+and+Round+Robin+Tests.">Recommended Practice for Dynamic Testing for Sheet Steels - Development and Round Robin Tests.</a> SAE International. , (2006).</li><li>Borsutzki, M., Cornette, D., Kuriyama, Y., Uenishi, A., Yan, B., Opbroek, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Recommendations+for+Dynamic+Tensile+Testing+of+Sheet+Steels.">Recommendations for Dynamic Tensile Testing of Sheet Steels.</a> International Iron and Steel Institute. , (2005).</li><li>Rusinek, A., Cheriguene, R., B&#228;umer, A., Klepaczko, J. R., Larour, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Dynamic+behaviour+of+high-strength+sheet+steel+in+dynamic+tension:+Experimental+and+numerical+analyses.">Dynamic behaviour of high-strength sheet steel in dynamic tension: Experimental and numerical analyses.</a> The Journal of Strain Analysis for Engineering Design. 43 (1), 37-53 (2008).</li><li>Diot, S., Guines, D., Gavrus, A., Ragneau, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Two-step+procedure+for+identification+of+metal+behavior+from+dynamic+compression+tests.">Two-step procedure for identification of metal behavior from dynamic compression tests.</a> International Journal of Impact Engineering. 34 (7), 1163-1184 (2007).</li><li>LeBlanc, M. M., Lassila, D. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+hybrid+Technique+for+compression+testing+at+intermediate+strain+rates.">A hybrid Technique for compression testing at intermediate strain rates.</a> Experimental Techniques. 20 (5), 21-24 (1996).</li><li>Xiao, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Analysis+of+dynamic+tensile+testing.">Analysis of dynamic tensile testing.</a> 11th International Congress and Exhibition on Experimental and Applied Mechanics. , (2008).</li><li>Othman, R., Gu&#233;gan, P., Challita, G., Pasco, F., LeBreton, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+modified+servo-hydraulic+machine+for+testing+at+intermediate+strain+rates.">A modified servo-hydraulic machine for testing at intermediate strain rates.</a> International Journal of Impact Engineering. 36 (3), 460-467 (2009).</li><li>Kwon, J. B., Huh, H., Ahn, C. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+improved+technique+for+reducing+the+load+ringing+phenomenon+in+tensile+tests+at+high+strain+rates.">An improved technique for reducing the load ringing phenomenon in tensile tests at high strain rates.</a> Annual Conference and Exposition on Experimental and Applied Mechanics. Costa Mesa, United States. , (2016).</li><li>Pan, W., Schmidt, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Strain+rate+effect+in+material+testing+of+bulk+adhesive.">Strain rate effect in material testing of bulk adhesive.</a> 9th International Conference on Structures Under Shock and Impact. 87, 107-116 (2006).</li><li>Zhang, D. N., Shangguan, Q. Q., Xie, C. J., Liu, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+modified+Johnson-Cook+model+of+dynamic+tensile+behaviors+for+7075-T6+aluminum+alloy.">A modified Johnson-Cook model of dynamic tensile behaviors for 7075-T6 aluminum alloy.</a> Journal of Alloys and Compounds. 619, 186-194 (2015).</li><li>Fitoussi, J., Meraghni, F., Jendli, Z., Hug, G., Baptiste, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Experimental+methodology+for+high+strain-rates+tensile+behaviour+analysis+of+polymer+matrix+composites.">Experimental methodology for high strain-rates tensile behaviour analysis of polymer matrix composites.</a> Composites Science and Technology. 65 (14), 2174-2188 (2005).</li></ol>

The raw data obtained from the experiment is influenced by the specimen geometry and strain gauges location on the specimen. The load data in low strain rate dynamic tests acquired by a piezo-electric load washer incorporated into the load frame at higher strain rates (Bruce et al.3 suggested &#62; 10/s, while for Wang et al.9 reported this limit to be 100/s) typically suffer from large amplitude oscillations due to dynamic waves associated with the loadin...

Most materials demonstrate some degree of strain rate dependency in their mechanical behavior1 and, therefore, mechanical testing conducted only at quasistatic strain rates is not suitable to determine the material properties for dynamic applications. The strain rate dependency of materials is typically investigated using five types of mechanical testing systems: conventional screw drive load frames, servo-hydraulic systems, high-rate servo-hydraulic systems, impact testers, and Hopkinson bar systems1. Split Hopkinson bars have been a common facility for the dynamic characterization of materials for the past 50 years2. There have also been efforts to modify Hopkinson bars to test at intermediate and lower strain rates. However, these facilities are typically more suitable for the high strain rate characterizations of the material (i.e., usually greater than 200/s). There is a gap in the literature on the strain rate characterization of material properties at intermediate strain rates in the range of 10&#8722;200/s (i.e., between quasistatic and high strain rate results obtained from split Hopkinson bars3), which is due to the limited access to facilities and a lack of reliable procedures of intermediate strain rate material testing.
A high-speed servo-hydraulic load frame applies load to the specimen at a constant and predefined velocity. These load frames benefit from a slack adaptor, which, in tensile tests, allows the crosshead to reach the desired velocity before the loading starts. The slack adaptor allows the head to travel a certain distance (e.g., 0.1 m) to reach the target velocity and then starts applying the load to the specimen. High-speed servo-hydraulic load frames typically perform tests under displacement control mode and maintain a constant actuator velocity to produce constant engineering strain rates3.
Techniques for measuring specimen elongation are generally classified as either contact or noncontact techniques4. Contact techniques include the use of instruments such as clip-on extensometers, while laser extensometers are employed for noncontact measurements. Since contact extensometers are prone to inertia influences, they are not suitable for dynamic tests; noncontact extensometers do not suffer from this problem.
Digital image correlation (DIC) is an optical, non-contact, full-field strain measurement technique, which is an alternative approach to strain gauging to measure strain/load and overcome some of the challenges (e.g., the ringing phenomenon) associated with dynamic material characterization5. Resistance strain gauges can suffer from limitations such as a limited area of measurement, a limited range of elongation, and limited mounting methods, whereas DIC is always capable of providing a full-field strain measurement from the specimen surface during the experiment.
The presented procedure describes the use of a high-speed servo-hydraulic load frame along with DIC and can be used as a complementary document to the recently developed standard guidelines6 to clarify the details of the experimental procedure. The section on the servo-hydraulic load frame can be followed for a variety of test setups (e.g., tensile, compressive, and shear) and even with common quasistatic load frames as well, and, therefore, covers a vast range of facilities. Furthermore, the DIC section may be applied separately to any type of mechanical or thermal tests, with minor modifications.

<table border="0" cellpadding="0" cellspacing="0" style="width:804px;" width="803">
	<colgroup>
		<col />
		<col />
		<col />
		<col />
	</colgroup>
	<tbody>
		<tr height="21">
			<td height="21" style="height:21px;width:280px;">Camera Lens</td>
			<td style="width:183px;">Opto Engineering</td>
			<td style="width:175px;"></td>
			<td style="width:167px;">Telecentric lens 23-64</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:280px;">High Speed Camera&#160;</td>
			<td style="width:183px;">SAX Photron Fastcam&#160;</td>
			<td style="width:175px;"></td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:280px;">High Speed DAQ&#160;</td>
			<td style="width:183px;">National Instruments</td>
			<td style="width:175px;">USB-6259</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:280px;">High Speed Servo-Hydraulic Load Frame</td>
			<td style="width:183px;">MTS Systems Corporation</td>
			<td style="width:175px;">Custom Built</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:280px;">Jab Bullet Light with diffuser&#160;</td>
			<td style="width:183px;">AADyn JAB BULLET&#160;</td>
			<td style="width:175px;"></td>
			<td style="width:167px;">&#160;15&#176; diffusers&#160;</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:280px;">Strain gauge</td>
			<td style="width:183px;">Micro-Measurements</td>
			<td style="width:175px;">Model EA-13-062AQ-350</td>
			<td style="width:167px;"></td>
		</tr>
	</tbody>
</table>

intermediate strain rate material characterization with digital image correlation

The mechanical response of a material under dynamic load is typically different than its behavior under static conditions; therefore, the common quasistatic equipment and procedures used for material characterization are not applicable for materials under dynamic loads. The dynamic response of a material depends on its deformation rate and is broadly categorized into high (i.e., greater than 200/s), intermediate (i.e., 10&#8722;200/s) and low strain rate regimes (i.e., below 10/s). Each of these regimes calls for specific facilities and testing protocols to ensure the reliability of the acquired data. Due to the limited access to high-speed servo-hydraulic facilities and validated testing protocols, there is a noticeable gap in the results at the intermediate strain rate. The current manuscript presents a validated protocol for the characterization of different materials at these intermediate strain rates. Strain gauge instrumentation and digital image correlation protocols are also included as complimentary modules to extract the utmost level of detailed data from every single test. Examples of raw data, obtained from a variety of materials and test setups (e.g., tensile and shear) is presented and the analysis procedure used to process the output data is described. Finally, the challenges of dynamic characterization using the current protocol, along with the limitations of the facility and methods of overcoming potential problems are discussed.

The duration of a dynamic test is typically comparable to the time required for the stress waves to travel a round trip over the length of the load train (i.e. grips, specimen, and loading) system1. A dynamic test is valid if the number and amplitude of stress waves during a dynamic test is controlled so that a dynamic equilibrium is achieved, and the specimen experiences a homogeneous deformation at an almost constant strain rate. The Society of Automotive Enginee...

Watch this Scientific Journal Video about Intermediate Strain Rate Material Characterization with Digital Image Correlation at JoVE.com

Intermediate Strain Rate Material Characterization with Digital Image Correlation

Here we present a methodology for the dynamic characterization of tensile specimens at intermediate strain rates using a high-speed servo-hydraulic load frame. Procedures for strain gauge instrumentation and analysis, as well as for digital image correlation strain measurements on the specimens, are also defined.

The mechanical response of a material under dynamic load is typically different than its behavior under static conditions; therefore, the common ...

Research

Education

JoVE Core

JoVE Journal

Mechanical Engineering

Engineering

Unit 1

Stress and Strain - Axial Loading

SCIENTISTS IN ACTION

Echo Particle Image Velocimetry

입자 이미지 Velocimetry 에코

The transport of mass, momentum, and energy in fluid flows is ultimately determined by spatiotemporal distributions of the fluid velocity field.1 ...

연구

공학

High-resolution, High-speed, Three-dimensional Video Imaging with Digital Fringe Projection Techniques

Digital fringe projection (DFP) techniques provide dense 3D measurements of dynamically changing surfaces.&#160;Like the human eyes and brain, DFP uses ...

Characterization of Full Set Material Constants and Their Temperature Dependence for Piezoelectric Materials Using Resonant Ultrasound Spectroscopy

풀 세트 재질 상수의 특성 및 공명 초음파​​ 분광법을 사용하여 압전 재료에 대한 그들의 온도 의존성

During the operation of high power electromechanical devices, a temperature rise is unavoidable due to mechanical and electrical losses, causing the ...

Experimental Methods for Investigation of Shape Memory Based Elastocaloric Cooling Processes and Model Validation

형상 기억의 조사를 기반으로 Elastocaloric 냉각 프로세스 및 모델 검증을위한 실험 방법

Shape Memory Alloys (SMA) using elastocaloric cooling processes have the potential to be an environmentally friendly alternative to the conventional vapor ...

Compact Lens-less Digital Holographic Microscope for MEMS Inspection and Characterization

MEMS 검사 및 특성화를위한 소형 렌즈가없는 디지털 홀로그램 현미경

A micro-electro-mechanical-system (MEMS) is a widely used component in many industries, including energy, biotechnology, medical, communications, and ...

Emission Spectroscopic Boundary Layer Investigation during Ablative Material Testing in Plasmatron

Plasmatron에서 절제 재료 시험 중에 방출 분광 경계 계층 조사

Ablative Thermal Protection Systems (TPS) allowed the first humans to safely return to Earth from the moon and are still considered as the only solution ...

Strain Sensing Based on Multiscale Composite Materials Reinforced with Graphene Nanoplatelets

The electrical response of NH2-functionalized graphene nanoplatelets composite materials under strain was studied. Two different manufacturing methods are ...

Carrier Lifetime Measurements in Semiconductors through the Microwave Photoconductivity Decay Method

전자 레인지 Photoconductivity 감퇴 메서드를 통해 반도체 캐리어 수명 측정

This work presents a protocol employing the microwave photoconductivity decay (&#956;-PCD) for measurement of the carrier lifetime in semiconductor ...

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

A novel measurement approach is used to reveal the cumulative deformation field at a sub-grain level and to study the influence of microstructure on the ...

Production of a Strain-Measuring Device with an Improved 3D Printer

A traditional strain measurement sensor needs to be electrified and is susceptible to electromagnetic interference. In order to solve the fluctuations in ...