Photochemical Oxidative Growth of Iridium Oxide Nanoparticles on CdSe@CdS Nanorods

We demonstrate a procedure for the photochemical oxidative growth of iridium oxide catalysts on the surface of seeded cadmium selenide-cadmium sulfide ...

Technion – Israel Institute of Technology

We present a spray based-method for the formation and production of semiconductor nanocrystals that provides an attractive alternative to the commonly used epitaxial and colloidal procedures. According to this spray-based method, mainly thermospray, solutions of semiconductor salts are first sprayed into monodispersed droplets, which subsequently become solid nanocrystals by solvent evaporation. A semiconductor nanocrystal is produced from a single spray droplet upon the full vaporization of the solvent. The average diameter and size distribution of the final nanocrystals are controlled and determined by the solute concentration of the sprayed solution and by the droplet size, hence by the spray production parameters. The spray-produced nanocrystals are collected on any selected solid support. Representative results, shown in this letter, reveal the formation of CdS nanocrystals in the size range of 3 to 6 nanometers and with a size distribution of as low as five percent. A further structural analysis of these nanocrystals showed that they were formed in the zinc blend phase with a high degree of crystallinity.

A spray-based method for the production of semiconductor nanocrystals.

This paper focuses on the interactions between cysteamine-stabilized CdTe nanocrystals [CdTe(CA) NCs] and thioglycolic-acid-stabilized CdTe nanocrystals [CdTe(TGA) NCs]. These interactions were examined by the absorption, continuous, and time-resolved photoluminescence (PL) spectra of the electrostatically mixed and the covalently linked NCs assemblies comprised of the oppositely surface charged CdTe(CA) and CdTe(TGA) NCs and by a comparison with those of the corresponding pristine NCs. The CdTe(CA)-CdTe(TGA) coupling is dictated by the surfactant spacer, ranging between 0.93 and 1.14 nm and by electrostatic and covalent interactions, enabling a Förster resonance energy transfer (FRET) process among the NCs. The results revealed an excellent spectral overlap between the emission of the CdTe(TGA) NCs and the absorption of the CdTe(CA) NCs as well as a PL spectral red shift on the formation of electrostatic and covalent interactions. Furthermore, the measurements showed a lifetime ranging between 1.2 and 3 ns for the electrostatically mixed and the covalently linked assemblies, shorter than those of the pristine CdTe(CA) NCs and CdTe(TGA) NCs, both of which measured as approximately 5.5 ns. When CdTe(TGA) NCs performed as the most efficient donors, FRET rates of 10(10)-10(11) s(-1) were calculated for the electrostatically mixed NCs or covalently linked NCs.

Electrostatic and covalent interactions in CdTe nanocrystalline assemblies.

A novel spray-based technique enables the production of high-quality, free, uncoated semiconductor nanocrystals. Their collection, following spray droplet desolvation during flight, could result in unusual structures. We report on spray-produced ordered clusters (approximately 50 nm diameter) of MnS nanocrystals with grain size range of 1-2 nm and their assembly into micron-sized coral-shaped fractal aggregates. Ballistic cluster-particle aggregation, with the introduction of physical interaction between particles, is suggested as a model for the assemblies' growth.

Spray-produced coral-shaped assemblies of MnS nanocrystal clusters.

In ionic nanocrystals the cationic sublattice can be replaced with a different metal ion via a fast, simple, and reversible place exchange, allowing postsynthetic modification of the composition of the nanocrystal, while preserving its size and shape. Here, we demonstrate that, during such an exchange, the anionic framework of the crystal is preserved. When applied to nanoheterostructures, this phenomenon ensures that compositional interfaces within the heterostructure are conserved throughout the transformation. For instance, a morphology composed of a CdSe nanocrystal embedded in a CdS rod (CdSe/CdS) was exchanged to a PbSe/PbS nanorod via a Cu(2)Se/Cu(2)S structure. During every exchange cycle, the seed size and position within the nanorod were preserved, as evident by excitonic features, Z-contrast imaging, and elemental line scans. Anionic framework conservation extends the domain of cation exchange to the design of more complex and unique nanostructures.

Nanoheterostructure cation exchange: anionic framework conservation.

&#x7ED3;&#x6784;&#x548C;&#x7535;&#x5B50;&#x7684;&#x91CF;&#x5B50;&#x63A7;&#x5236;&#x5149;&#x654F;&#x5242;&#x5BF9;&#x975E;&#x6676; MoS3-&#x5236;&#x6C22;&#x50AC;&#x5316;&#x5242;&#x7684;&#x7814;&#x7A76;&#x3002;

Structural and electronic study of an amorphous MoS3 hydrogen-generation catalyst on a quantum-controlled photosensitizer.

&Eacute;tude structurale et &eacute;lectronique d&#39;un catalyseur de g&eacute;n&eacute;ration d&#39;hydrog&egrave;ne MoS3 amorphe sur un photosensibilisateur quantique-contr&ocirc;l&eacute;e.

Strukturelle und elektronische Studie &uuml;ber ein amorphes MoS3 Wasserstoff-Erzeugung Katalysator auf ein Photosensibilisator Quanten-gesteuert.

Studio strutturale ed elettronica di un catalizzatore di generazione di idrogeno MoS3 amorfo su un fotosensibilizzatore quantico controllata.

&#x91CF;&#x5B50;&#x5236;&#x5FA1;&#x306E;&#x5149;&#x7DDA;&#x306B;&#x975E;&#x6676;&#x8CEA; MoS3 &#x306B;&#x3088;&#x308B;&#x6C34;&#x7D20;&#x751F;&#x6210;&#x89E6;&#x5A92;&#x306E;&#x69CB;&#x9020;&#x3068;&#x96FB;&#x5B50;&#x306E;&#x7814;&#x7A76;&#x3002;

&#xC591;&#xC790; &#xC81C;&#xC5B4; photosensitizer&#xC5D0; &#xBE44;&#xC815; &#xC9C8; MoS3 &#xC218;&#xC18C; &#xBC1C;&#xC0DD; &#xCD09;&#xB9E4;&#xC758; &#xAD6C;&#xC870; &#xBC0F; &#xC804;&#xC790; &#xC5F0;&#xAD6C;.

Estudio estructural y electr&oacute;nica de un catalizador de generaci&oacute;n de hidr&oacute;geno MoS3 amorfo en un fotosensibilizador cu&aacute;ntica-controlado.

Using far-field optical microscopy we report the first measurements of photoluminescence from single nanoparticle photocatalysts. Fluence-dependent luminescence is investigated from metal-semiconductor heterojunction quantum dot catalysts exposed to a variety of environments, ranging from gaseous argon to liquid water containing a selection of hole scavengers. The catalysts each exhibit characteristic nonlinear fluence dependence. From these structurally and environmentally sensitive trends, we disentangle the separate rate-determining steps in each particle across the very wide range of time scales, which follow the initial light absorption process. This information will significantly benefit the design of effective artificial photocatalytic systems for renewable direct solar-to-fuel energy conversion.

Luminescence studies of individual quantum dot photocatalysts.

A spray-based technique, originally developed for the production of semiconductor nanocrystals, is utilized for the preparation of high-quality nanocrystalline thin films, as demonstrated with manganese sulfide. The films are formed by the use of pneumatic-assisted thermospray or pneumatic nebulizers. Our simple, low-cost, and low-temperature process results in a dense and phase-pure grain structure. The concepts and benefits of this technique are described and discussed. The film characteristics show dependence on the experimental parameters, in particular the rate of solvent vaporization. Three alternative film formation mechanisms are suggested for cases with varied experimental conditions.

A spray-based technique for the production of MnS thin films.

Reported is the design and modular synthesis of a dual metal-dual semiconductor heterostructure with control over the dimensions and placement of its individual components. Analogous to molecular synthesis, colloidal synthesis is now evolving into a series of sequential synthetic procedures with separately optimized steps. We detail the challenges and parameters that must be considered when assembling such a multicomponent nanoparticle, and their solutions. This multicomponent nanosystem, Ru-CdSe@CdS-Pt, was designed to achieve charge carrier separation and directional transfer across different interfaces toward two separate redox catalysts. This heterostructure may potentially serve as a nanometric closed circuit photoelectrochemical cell.

Modular synthesis of a dual metal-dual semiconductor nano-heterostructure.

We provide evidence that for a multielectron reaction such as hydrogen reduction, the photocatalyst design should include only a single cocatalytic site per each segment of the semiconductor capable of light excitation. This is to ensure that intermediates are formed at close proximity. These findings are demonstrated by evaluating the efficiency for hydrogen production over a nanoparticle-based photocatalyst consisting of Pt-decorated CdSe@CdS rods. Rods decorated with a single Pt catalyst were found to be the most active for hydrogen production, with QE of 27%, while rods having two reduction sites reached QE of only 18% and rods with multiple sites showed very low activity. The advantage of using a single catalytic site became negligible when the rods were employed in catalyzing a single electron reaction. We believe the implications of this finding are of significance for the proper design of photocatalysts aimed at solar-to-fuel energy conversion.

Less Is More: The Case of Metal Cocatalysts.

The enhanced catalytic properties of bimetallic particles has made them the focus of extensive research. We compare the photocatalytic activity for hydrogen production of core-shell structures of Au@Pd and Au@(Au/Pd alloy) on seeded rods of CdSe@CdS and show that Au@alloy was superior toward hydrogen production. Our finding reveals that the promotion effects of Au in Pd originate both from the alteration of the electronic structure by the Au core as well as by the atomic rearrangement of the surface. Long-term monitoring of the activity of the photocatalysts offered insights into the dynamic processes during the illumination showing that the tip morphology influenced the stability of the hybrid structures. The Au core served as a physical barrier, protecting the CdS rod against cation exchange reactions with the Pd. The coupling of these factors to achieve synergistic effects is therefore a prime aspect in the rational design of efficient cocatalysts.

Designing Bimetallic Co-Catalysts: A Party of Two.

We report a record 100% photon-to-hydrogen production efficiency, under visible light illumination, for the photocatalytic water-splitting reduction half-reaction. This result was accomplished by utilization of nanoparticle-based photocatalysts, composed of Pt-tipped CdSe@CdS rods, with a hydroxyl anion-radical redox couple operating as a shuttle to relay the holes. The implications of such record efficiency for the prospects of realizing practical over all water splitting and solar-to-fuel energy conversion are discussed.

Lilac Amirav

Schulich Faculty of Chemistry,
The Russell Berrie Nanotechnology Institute,
The Nancy and Stephen Grand Technion Energy Program,
Schulich Faculty of Chemistry, The Russell Berrie Nanotechnology Institute, The Nancy and Stephen Grand Technion Energy Program

Technion – Israel Institute of Technology

Photochemical Oxidative Growth of Iridium Oxide Nanoparticles on CdSe@CdS Nanorods