Preparation of Thermoresponsive Nanostructured Surfaces for Tissue Engineering

Thermoresponsive poly(N-isopropylacrylamide) (PIPAAm)-immobilized surfaces for controlling cell adhesion and detachment were fabricated by the ...

Tokyo University of Science

Tokyo University of science

This study used Langmuir-Schaefer (LS) method to produce thermo-responsive poly(N-isopropylacrylamide) (PIPAAm) modified surface. Dodecyl terminated-PIPAAm (PIPAAm-C12) was synthesized by reversible addition-fragmentation chain transfer radical polymerization. PIPAAm-C12 was dropped on an air-water interface and formed Langmuir film by compressing. A surface pressure measurement revealed that PIPAAm-C12 was floated and Langmuir films were formed on the interface. And the Langmuir film was transferred on a hydrophobic substrate to produce PIPAAm-C12 transferred surface (PIPAAm-LS surface). In the results of atomic force microscope, attenuated total reflection Fourier transform infrared spectroscope, and X-ray photoelectron spectroscope measurement, the transference of Langmuir films was demonstrated and densities could be precisely controlled. Ellipsometric measurements of PIPAAm-LS surfaces showed that the thicknesses of the surfaces were less than 10 nm. Cell adhesion and detachment were observed on the PIPAAm-LS surfaces. The amount of adhered cells on all LS surfaces was found to be similar on the control hydrophobic substrate at 37 °C. In regard to cell detachment, adhering cells rapidly detached themselves with higher densities and shorter PIPAAm-C12 molecules. In this method, the effect of densities and molecular weights on cell adhesion and detachment were observed. Our method should be proved novel insights for investigating cell adhesion and detachment on thermo-responsive surfaces.

Control of cell adhesion and detachment on Langmuir-Schaefer surface composed of dodecyl-terminated thermo-responsive polymers.

Thermoresponsive poly(N-isopropylacrylamide) (PIPAAm)-immobilized surfaces for controlling cell adhesion and detachment were fabricated by the Langmuir-Schaefer method. Block copolymers composed of polystyrene and PIPAAm (St-IPAAms) having various chain lengths and compositions were synthesized by reversible addition-fragmentation chain transfer radical polymerization. The St-IPAAm Langmuir film at an air-water interface was horizontally transferred onto a hydrophobically modified glass substrate while regulating its density. Atomic force microscopy images clearly visualized nanoscaled sea-island structures on the surface. By adjusting both the composition of St-IPAAms and the density of immobilized PIPAAms, a series of thermoresponsive surfaces was prepared to control the strength, rate, and quality of cell adhesion and detachment through changes in temperature across the lower critical solution temperature range of PIPAAm molecules. In addition, a two-dimensional cell structure (cell sheet) was more rapidly recovered on the optimized surfaces than on conventional PIPAAm surfaces. These unique PIPAAm surfaces are suggested to be useful for controlling the strength of cell adhesion and detachment.

Morito Sakuma

Department of Physics

Tokyo University of Science

Preparation of Thermoresponsive Nanostructured Surfaces for Tissue Engineering

Morito Sakuma

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Department of Physics

Tokyo University of Science

Preparation of Thermoresponsive Nanostructured Surfaces for Tissue Engineering

Department of Physics