Name: synthesis of near-infrared emitting gold nanoclusters for biological applications
Uploaded: 2020-03-22T13:00:00
Description: Watch this Scientific Journal Video about Synthesis of Near-Infrared Emitting Gold Nanoclusters for Biological Applications at JoVE.com

The authors are grateful to Alzbeta Magdolenova for her help with flow cytometry. The authors acknowledge the financial support from GACR project Nr. 18-12533S. Microscopy was performed in the Laboratory of Confocal and Fluorescence Microscopy co-financed by the European Regional Development Fund and the state budget of the Czech Republic, projects no. CZ.1.05/4.1.00/16.0347 and CZ.2.16/3.1.00/21515, and supported by the Czech-BioImaging large RI project LM2015062.

1. Preparation of near-infrared emitting AuNCs (1)
<ol>
	<li>Add 7.8 mg (37.8 &#956;mol) thioctic acid (TA) and 60 &#956;L of 2 M NaOH to 23.4 mL of ultrapure water (resistivity 18.2 M&#937;.cm at 25 &#176;C) and stir (at least 1,000 rpm) until it dissolves completely (~15-20 min). For faster dissolution of TA, sonicate the mixture. For the synthesis, freshly prepared TA solution is recommended.</li>
	<li>Add 10.2&#160;&#956;L of HAuCl4&#183;3H2O (470 mg/mL) of aqueous solution to the solution.</l...

NIR-emitting AuNCs were synthesized using a bottom-up approach in which the gold precursor solution (HAuCl4) was treated with suitable thiol ligands, followed by reduction of Au3+. Reduction of metal ions in aqueous solution tend to aggregate and results in large nanoparticles rather than ultrasmall NCs21. To prepare ultrasmall (&#8804;2 nm) PL AuNCs, the synthetic conditions were adjusted to prevent formation of large particles and promote formation of ultrasmall clusters. T...

In the past decade, ultrasmall (&#8804; 2 nm) photoluminescent gold nanoclusters (PL AuNCs) have emerged as promising probes for both fundamental research and practical applications1,2,3,4,5,6,7,8,9,10. Their many desirable characteristics include high photostability, tunable emission maxima, long emission lifetimes, large Stokes shifts, low toxicity, good biocompatibility, renal clearance and facile bioconjugation. PL AuNCs can provide photoluminescence from the blue to the near-infrared (NIR) spectral region, depending on the number of atoms within the cluster11 and the nature of the surface ligand12. NIR (650-900 nm) emitting AuNCs are particularly promising for long-term in vitro and in vivo imaging of cells and tissues, as they offer high signal-to-noise ratio due to minimum overlap with intrinsic autofluorescence, weaker scattering and absorption, and high tissue penetration of NIR light13,14.
In recent years, various approaches that take advantage of Au-S covalent interactions have been developed to prepare NIR-PL AuNCs capped with a variety of thiol-containing ligands13,15,16,17. For biomedical applications, AuNCs must be functionalized with a biological component to facilitate binding interactions. Thus, AuNCs with high colloidal stability that are easily functionalizable in aqueous solvent are highly desirable. The overall goal of the current protocol is to describe a previously reported18 preparation of AuNCs with a functionalizable carboxylic acid group on the surface by employing thioctic acid and polyethylene glycol (PEG) in an aqueous environment in detail and their conjugation with molecules bearing a primary amine following the acid-amine coupling method. Because of the ease of synthesis and high reproducibility, this protocol can be used and adapted by researchers from non-chemistry backgrounds.
One of the key requisites for applications of AuNCs in biomedical research is the ability to observe and measure AuNCs inside cells. Among the methods available to monitor nanoparticle uptake by cells, flow cytometry (FCM) and confocal laser scanning microscopy (CLSM) offer robust, high-throughput methods which allow fast measurements of internalization of fluorescent nanomaterials in large number of cells19. Here, FCM and CLSM method for direct measurement and analysis of PL AuNCs inside cells, without the need for additional dyes, have also been presented.

<table>
	<tbody>
		<tr>
			<td>1-(3-Dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride</td>
			<td>TCI Chemicals</td>
			<td>D1601</td>
			<td>https://www.tcichemicals.com/eshop/en/eu/commodity/D1601/;jsessionid=3AD046E5389206AAE33C8AAB5036CDD6?gclid=CjwKCAjwiZnnBRBQEiwAcWKfYrO69K6Np3tYeSsAouqGndUvzzsy1hStBPuHG-X3cpTIsAqq9z0cDBoC76MQAvD_BwE</td>
		</tr>
		<tr>
			<td>Bovine serum albumin</td>
			<td>Sigma-Aldrich</td>
			<td>A4161</td>
			<td>https://www.sigmaaldrich.com/catalog/product/sigma/a4161?lang=en&#38;region=CZ</td>
		</tr>
		<tr>
			<td>Disodium hydrogen phosphate dihydrate</td>
			<td>PENTA s.r.o.</td>
			<td>15130-31000</td>
			<td>https://www.pentachemicals.eu/soubory/specifikace/specifikace_281.pdf</td>
		</tr>
		<tr>
			<td>DL-Thioctic acid, 98%</td>
			<td>Alfa Aesar</td>
			<td>L04711</td>
			<td>https://www.alfa.com/en/catalog/L04711/</td>
		</tr>
		<tr>
			<td>Hydrochloric acid 35%</td>
			<td>PENTA s.r.o.</td>
			<td>19350-11000</td>
			<td>https://www.pentachemicals.eu/soubory/specifikace/specifikace_512.pdf</td>
		</tr>
		<tr>
			<td>Hydrogen tetrachloroaurate(III) trihydrate, ACS, 99.99% (metals basis), Au 49.0% min</td>
			<td>Alfa Aesar</td>
			<td>36400</td>
			<td>https://www.alfa.com/en/catalog/036400/</td>
		</tr>
		<tr>
			<td>O-(2-Mercaptoethyl)-O&#8242;-methylpolyethylene glycol 2000</td>
			<td>Sigma-Aldrich</td>
			<td>743127</td>
			<td>https://www.sigmaaldrich.com/catalog/product/aldrich/743127?lang=en&#38;region=CZ</td>
		</tr>
		<tr>
			<td>Potassium chloride</td>
			<td>PENTA s.r.o.</td>
			<td>16200-31000</td>
			<td>https://www.pentachemicals.eu/soubory/specifikace/specifikace_346.pdf</td>
		</tr>
		<tr>
			<td>Sodium borohydride</td>
			<td>Sigma-Aldrich</td>
			<td>452882</td>
			<td>https://www.sigmaaldrich.com/catalog/product/aldrich/452882?lang=en&#38;region=CZ&#38;gclid=CjwKCAjwiZnnBRBQEiwAcWKfYuoZKvdK_fH24F1gGugG4pamF2FFZLd36YyZmRTdGgkbm5SbyGP0jBoCoo0QAvD_BwE</td>
		</tr>
		<tr>
			<td>Sodium chloride</td>
			<td>PENTA s.r.o.</td>
			<td>16610-31000</td>
			<td>https://www.pentachemicals.eu/soubory/specifikace/specifikace_376.pdf</td>
		</tr>
		<tr>
			<td>Sodium dihydrogenphosphate dihydrate</td>
			<td>PENTA s.r.o.</td>
			<td>12330-31000</td>
			<td>https://www.pentachemicals.eu/soubory/specifikace/specifikace_124.pdf</td>
		</tr>
		<tr>
			<td>Sodium hydroxide pellets</td>
			<td>PENTA s.r.o.</td>
			<td>15740-31000</td>
			<td>https://www.pentachemicals.eu/soubory/specifikace/specifikace_307.pdf</td>
		</tr>
		<tr>
			<td>XTT (sodium 2, 3-bis (2-methoxy-4-nitro-5-sulfophenyl)-5-[(phenylamino)-carbonyl]-2H-tetrazolium inner salt)</td>
			<td>Thermo Fisher Scientific</td>
			<td>X12223</td>
			<td>https://www.thermofisher.com/order/catalog/product/X12223#/X12223</td>
		</tr>
	</tbody>
</table>

synthesis of near-infrared emitting gold nanoclusters for biological applications

Over the past decade, fluorescent gold nanoclusters (AuNCs) have witnessed growing popularity in biological applications and enormous efforts have been devoted to their development. In this protocol, a recently developed, facile method for preparation of water soluble, biocompatible, and colloidally stable near-infrared emitting AuNCs have been described in detail. This room-temperature, bottom-up chemical synthesis provides easily functionalizable AuNCs capped with thioctic acid and thiol-modified polyethylene glycol in aqueous solution. The synthetic approach requires neither organic solvents or additional ligand exchange nor extensive knowledge of synthetic chemistry to reproduce. The resulting AuNCs offer free surface carboxylic acids, which can be functionalized with various biological molecules bearing a free amine group without adversely affecting the photoluminescent properties of the AuNCs. A quick, reliable procedure for flow cytometric quantification and confocal microscopic imaging of AuNC uptake by HeLa cells also been described. Due to the large Stokes shift, proper setting of filters in flow cytometry and confocal microscopy is necessary for efficient detection of near-infrared photoluminescence of AuNCs.

NIR PL AuNCs were prepared from Au3+ in the presence of TA, and then thiol-terminated PEG (MW 2,000) was bound on the AuNC surface to obtain 1 following the workflow shown in Figure 1. Amidic coupling between 1 and 3-(aminopropyl) triphenylphosphonium (TPP) bromide provided 2. As expected, absorption spectra (Figure 2a) indicated that AuNCs 1 and 2 do not have a chara...

Watch this Scientific Journal Video about Synthesis of Near-Infrared Emitting Gold Nanoclusters for Biological Applications at JoVE.com

Synthesis of Near-Infrared Emitting Gold Nanoclusters for Biological Applications

A reliable and easily reproducible method for preparation of functionalizable, near-infrared emitting photoluminescent gold nanoclusters and their direct detection inside HeLa cells by flow cytometry and confocal laser scanning microscopy is described.

Over the past decade, fluorescent gold nanoclusters (AuNCs) have witnessed growing popularity in biological applications and enormous efforts have been ...

Research

JoVE Journal

Bioengineering

Synthesis, Assembly, and Characterization of Monolayer Protected Gold Nanoparticle Films for Protein Monolayer Electrochemistry

Colloidal gold nanoparticles protected with alkanethiolate ligands called monolayer protected gold clusters (MPCs) are synthesized and subsequently ...

Gold Nanostar Synthesis with a Silver Seed Mediated Growth Method

The physical, chemical and optical properties of nano-scale colloids depend on their material composition, size and shape 1-5. There is a great interest ...

Wideband Optical Detector of Ultrasound for Medical Imaging Applications

Optical sensors of ultrasound are a promising alternative to piezoelectric techniques, as has been recently demonstrated in the field of optoacoustic ...

In situ TEM of Biological Assemblies in Liquid

In situ TEM of Biological Assemblies in Liquid

Researchers regularly use Transmission Electron Microscopes (TEMs) to examine biological entities and to assess new materials. Here, we describe an ...

Fluorescence-quenching of a Liposomal-encapsulated Near-infrared Fluorophore as a Tool for In Vivo Optical Imaging

Fluorescence-quenching of a Liposomal-encapsulated Near-infrared Fluorophore as a Tool for In Vivo Optical Imaging

Optical imaging offers a wide range of diagnostic modalities and has attracted a lot of interest as a tool for biomedical imaging. Despite the enormous ...

Synthesis of Keratin-based Nanofiber for Biomedical Engineering

Electrospinning, due to its versatility and potential for applications in various fields, is being frequently used to fabricate nanofibers. Production of ...

Synthesis of Gold Nanoparticle Integrated Photo-responsive Liposomes and Measurement of Their Microbubble Cavitation upon Pulse Laser Excitation

Photo-responsive nanoparticles (NPs) have received considerable attention because of their potential in providing spatial, temporal, and dosage control ...

Selective Cell Elimination from Mixed 3D Culture Using a Near Infrared Photoimmunotherapy Technique

Recent developments in tissue engineering offer innovative solutions for many diseases. For example, tissue engineering using induced pluripotent stem ...

Preparation of Silicon Nanowire Field-effect Transistor for Chemical and Biosensing Applications

Surveillance using biomarkers is critical for the early detection, rapid intervention, and reduction in the incidence of diseases. In this study, we ...