laser-heating-radiance-spectrometry-for-study-nuclear-materials

Laser-heating and Radiance Spectrometry for the Study of Nuclear Materials in Conditions Simulating a Nuclear Power Plant Accident

Major and severe accidents have occurred three times in nuclear power plants (NPPs), at Three Mile Island (USA, 1979), Chernobyl (former USSR, 1986) and ...

a-novel-technique-for-raman-analysis-highly-radioactive-samples-using

A Novel Technique for Raman Analysis of Highly Radioactive Samples Using Any Standard Micro-Raman Spectrometer

A novel approach for the Raman measurement of nuclear materials is reported in this paper. It consists of the enclosure of the radioactive sample in a ...

European Commission, Joint Research Centre

Joint Research Centre (JRC)

Analysis of X-ray absorption fine structure spectra of UO(2+x) for x = 0-0.20 (UO(2)--U(4)O(9)) reveals that the adventitious O atoms are incorporated as oxo groups with U--O distances of 1.74 A, most likely associated with U(VI), that occur in clusters so that the UO(2) fraction of the material largely remains intact. In addition to the formation of some additional longer U--O bonds, the U sublattice consists of an ordered portion that displays the original U--U distance and a spectroscopically silent, glassy part. This is very different from previous models derived from neutron diffraction that maintained long U--O distances and high U--O coordination numbers. UO(2+x) also differs from PuO(2+x) in its substantially shorter An-oxo distances and no sign of stable coordination with H(2)O and its hydrolysis products.

Local structure and charge distribution in the UO(2)-U(4)O(9) system.

Apart from its technological importance, plutonium (Pu) is also one of the most intriguing elements because of its non-conventional physical properties and fascinating chemistry. Those fundamental aspects are particularly interesting when dealing with the challenging study of plutonium-based nanomaterials. Here we show that ultra-small (3.2±0.9 nm) and highly crystalline plutonium oxide (PuO2 ) nanocrystals (NCs) can be synthesized by the thermal decomposition of plutonyl nitrate ([PuO2 (NO3 )2 ]⋅3 H2 O) in a highly coordinating organic medium. This is the first example reporting on the preparation of significant quantities (several tens of milligrams) of PuO2 NCs, in a controllable and reproducible manner. The structure and magnetic properties of PuO2 NCs have been characterized by a wide variety of techniques (powder X-ray diffraction (PXRD), X-ray absorption fine structure (XAFS), X-ray absorption near edge structure (XANES), TEM, IR, Raman, UV/Vis spectroscopies, and superconducting quantum interference device (SQUID) magnetometry). The current PuO2 NCs constitute an innovative material for the study of challenging problems as diverse as the transport behavior of plutonium in the environment or size and shape effects on the physics of transuranium elements.

Ultra-small plutonium oxide nanocrystals: an innovative material in plutonium science.

Cubic fluorite-type phases have been reported in the U(IV)O2-Bi2O3 system for the entire compositional range, but an unusual non-linear variation of the lattice parameter with uranium substitution has been observed. In the current extensive investigation of the uranium(iv) oxide-bismuth(iii) oxide system, this behaviour of the lattice parameter evolution with composition has been confirmed and its origin identified. Even under inert atmosphere at 800 °C, U(IV) oxidises to U(V)/U(VI) as a function of the substitution degree. Thus, using a combination of three methods (XRD, XANES and Raman) we have identified the formation of the BiU(V)O4 and Bi2U(VI)O6 compounds, within this series. Moreover, we present here the Rietveld refinement of BiU(V)O4 at room temperature and we report the thermal expansion of both BiU(V)O4 and Bi2U(VI)O6 compounds.

Further insights into the chemistry of the Bi-U-O system.

TaC, HfC and their solid solutions are promising candidate materials for thermal protection structures in hypersonic vehicles because of their very high melting temperatures (>4000 K) among other properties. The melting temperatures of slightly hypostoichiometric TaC, HfC and three solid solution compositions (Ta1-xHfxC, with x = 0.8, 0.5 and 0.2) have long been identified as the highest known. In the current research, they were reassessed, for the first time in the last fifty years, using a laser heating technique. They were found to melt in the range of 4041-4232 K, with HfC having the highest and TaC the lowest. Spectral radiance of the hot samples was measured in situ, showing that the optical emissivity of these compounds plays a fundamental role in their heat balance. Independently, the results show that the melting point for HfC0.98, (4232 ± 84) K, is the highest recorded for any compound studied until now.

Dario Manara

European Commission, Joint Research Centre

Laser-heating and Radiance Spectrometry for the Study of Nuclear Materials in Conditions Simulating a Nuclear Power Plant Accident

A Novel Technique for Raman Analysis of Highly Radioactive Samples Using Any Standard Micro-Raman Spectrometer