This work was performed in part at the Analytical Instrumentation Facility (AIF) at North Carolina State University, which is supported by the State of North Carolina and the National Science Foundation (award number ECCS-2025064). The AIF is a member of the North Carolina Research Triangle Nanotechnology Network (RTNN), a site in the National Nanotechnology Coordinated Infrastructure (NNCI). The authors would like to thank Damien Alloyeau, CNRS Research Director at the University Paris Cit&#233;, for providing the 200 kV CFEG zeolite dose threshold study results.

1. Method 1: Dose calibration of the transmission electron microscope for TEM and scanning TEM (STEM) imaging modes
<ol>
	<li>Turn on the picoammeter and allow it to warm up for a minimum of 30 min before starting a dose calibration. Load the dose calibration holder into the TEM and connect the calibration holder to the picoammeter using the quick-connect cable.</li>
	<li>With the microscope in TEM mode, open the column valves and locate the 35 &#181;m fiducial hole on the dose holder (Figure 2). Launch the MVS software application and select Dose (Calibration Automation)&#160;from the experiment options. 
	NOTE: The fiducial hole location is saved by the software after the initial calibration, enabling the software to automatically locate its position for future calibrations.</li>
	<li>Click on the Connect&#160;icon (Figure 1A) and select the microscope to activate the connection between the TEM and the MVS software. Once connected, the images from the camera/detector will be visible in the image viewer of the software. 
	NOTE: It is not necessary to optimize the eucentric height, and the edge of the fiducial hole may appear blurry due to the thickness of the tip. This will not affect the current measurements.</li>
	<li>Navigate to the Dose tab and then to Dose Calibration. Select Dose Area Calibration process, follow the software prompts, and enter the requested user-configurable values (such as the aperture and monochromator settings). After the Dose Area Calibration is complete, select the Dose Current Calibration process and follow the software prompts.</li>
	<li>Repeat the calibration process (step 1.4) for each spot size, aperture, or monochromator setting that may be utilized during the experiment.</li>
	<li>When the calibration process for TEM mode is finished, calibrate the electron dose for STEM mode by repeating step 1.4. 
	NOTE: STEM mode does not require the Dose Area Calibration to be performed.</li>
	<li>When all desired calibrations are finished, click on Close Session, remove the dose calibration holder, and return to the start screen of the MVS software.</li>
</ol>
2. Method 2: Determination of dose threshold using the MVS and dose software
<ol>
	<li>Load a standard TEM grid with a sample (commercially available ZSM-5 zeolite nanoparticles were used in this example) into a standard TEM holder. Insert the holder into the TEM and locate a region of interest (crystalline zeolite nanoparticles).</li>
	<li>Open the MVS software application and select Other. 
	NOTE: Additional information about the sample (e.g. sample identifier and description, the operator name, and experiment notes) can be added to the experimental parameters field.</li>
	<li>Repeat step 1.3 to connect to the MVS software and navigate to the image metadata tab in the MVS software interface to select the following metadata to overlay on the image stream shown in the live display: Magnification, Max Dose, and Dose Rate. Other metadata may be included if the user desires. A screenshot of the MVS software interface showing the dose management controls is provided in Supplementary File 1.</li>
	<li>Open the Dose tab and select Dose Management and Enable Dose Monitoring to activate automated electron dose tracking. Select Show Dose Layer to display the dose color overlay.</li>
	<li>Set the values for the high dose level and the high dose rate and press on Save (in this example, values of 60,000 e-/&#197;2 and&#160;500 e-/&#197;2&#183;s, respectively, were used).</li>
	<li>Navigate to the Settings tab, select Dose, and set the Dose Navigation Map Opacity and Dose Image Overlay Opacity values (in this example, values of 0.50 and 0.30, respectively, were used).</li>
	<li>In the Live Image Viewer window, activate drift correction by clicking on Drift Correct.</li>
	<li>Navigate to the Data View tab and plot the metadata values Defocus and Focus Quotient on the Y axis. 
	NOTE: Any of the available metadata values can be plotted in real time during the experiment from the data view table.</li>
	<li>Activate Focus Assist, and then select Calibrate Focus to run the automated focus assist calibration. Once the Calibrate Focus routine is complete, close the Data View tab.</li>
	<li>Open the Image Analysis tab in the MVS software and activate the Live FFT and Quadrants 1 &#38; 2 options.</li>
	<li>Using the microscope&#39;s software controls, adjust the beam conditions so that the electron flux is ~500 e-/&#197;2&#183;s. and move to a new region in the sample and center the sample ROI in the live view of the MVS software. 
	NOTE: When making large stage movements, drift control and focus assist will automatically de-activate, and must be re-engaged once the new ROI is selected.</li>
	<li>Make a note of the dose conditions in the software using the Tag function. Highlight the Tag icon and enter the desired text to denote a specific series of images within the timeline. Images will be tagged with this text until the Tag icon is deselected.</li>
	<li>Maintain a constant dose rate while continuously imaging the same ROI until the peaks corresponding to the atomic structure in the FFT plot have disappeared.</li>
	<li>Reduce the magnification, open the Dose Management tab, and activate Show Dose Layer to overlay a color-coded dose map. 
	NOTE: This feature provides a visual reference of the areas of the sample that have been exposed to the electron beam and their relative dose exposure. Highlighting these areas in individual images with the cursor will indicate their respective dose values.</li>
	<li>Disconnect and end the session by deselecting Connect, then select Close Session. Save a copy of the session data to an external source to prevent the data saved in the MVS software from being overwritten during subsequent experiments (Supplementary File 2).</li>
</ol>
3. Method 3: Metadata and trend analysis and data export using the analysis software
<ol>
	<li>Launch the analysis software (the offline software for viewing the fully synchronized datasets) and open the experiment session file by selecting it from the file library. 
	NOTE: Users can also access the analysis software through the Review Session icon in the MVS software during an experiment.</li>
	<li>Display the drift corrected images by activating the DC tab below the Image View Port and select the desired data overlays by checking their respective Overlay Data boxes in the Image Metadata tab (in this example Microscope, Date/Time, Dose Rate, Max Dose, and Magnification&#160;were used). Other metadata may be plotted as the user desires.</li>
	<li>Check the Timeline box for Max Dose and Dose Rate to add a graphical plot of these values to the timeline. Highlight or scroll through these graphical plots to update the image displayed in the viewport. Access a variety of tools through the Notes, Image Analysis, Toolbox, and Data View tabs.
	<ol>
		<li>Access the FFT for each image through the Image Analysis tab and click on Live FFT to update the FFT while scrolling through images.</li>
		<li>Use the fading of the FFT peaks to determine the time point at which the zeolite structure loses crystallinity. Record the max dose value recorded with that image.</li>
	</ol>
	</li>
	<li>Use the Filter option to filter large datasets easily into smaller, sharable datasets without losing their associated metadata. Open the filter panel and adjust the sliders so that only data with a dose rate equal to or above ~500 e-/&#197;2&#183;s is selected, and save the new collection using the name Dose Threshold Study. 
	NOTE: Filters may be applied for any of the associated metadata types.</li>
	<li>Export the images and metadata from the session into other file types enriched with scale bars and metadata overlays.
	<ol>
		<li>Highlight the collection in the library pane and select Publish by right-clicking the selection. From the Publish window, select the desired options for the file type export.</li>
		<li>Select the drift corrected data tab and apply overlays of any desired metadata and the FFT (position the FFT overlay as desired; examples of images exported with the FFT are shown in Figure 3).</li>
	</ol>
	</li>
	<li>Export the image series as a movie file using the same Publish option. Select the images by highlighting them in the timeline, using the filter options or exporting the full database file. Select the desired movie format, frame rate, and file location. A movie of the zeolite degradation experiment obtained using a 200 kV TEM is provided in Supplementary File 3.</li>
	<li>Export the metadata separately from the acquired images as a CSV file by selecting the Metadata (CSV) option while publishing. 
	&#8203;NOTE: Raw and drift corrected images are exported as separate CSVs (Supplementary File 4 and Supplementary File 5).</li>
</ol>
4. Method 4: In situ heating study of gold on iron oxide nanoparticles
<ol>
	<li>Dropcast a nanocatalyst (Au/FeOx) suspended in ethanol onto an in situ heater E-chip, a mico-electrochmechanical (MEM) sample support, and allow it to air-dry. Mount the sample in the in situ heating holder, insert the holder with the sample into the TEM, and connect the holder to the power supply using the supplied cable. Locate a sample ROI using the TEM controls. 
	NOTE: This experiment used a heating holder which is fully integrated with the MVS software, enabling temperature metadata to be embedded with the images.</li>
	<li>Select the appropriate workflow option from the MVS software (in this example, the Fusion Workflow was used, but other manufacturer heating holders can be used by selecting Other).</li>
	<li>Follow the workflow prompts to confirm the electrical connection between the holder and the heating E-chip by loading the calibration file and performing a device check. </li>
	<li>Connect the microscope to the MVS software, as shown earlier in steps 2.3-2.10 (in this example, the metadata values for dose rate, max dose, match correlation, drift rate, and channel A temperature were selected), and center the sample ROI in the field of view.</li>
	<li>Open the Fusion AX tab and set up and apply a temperature.</li>
	<li>Click the Channel A Setup button to access the temperature control settings. Select the Temperature&#160;function and Manual control mode.</li>
	<li>Click the Experiment button to access the experimental controls. Set the Ramp Rate to 10 &#176;C/s and the Target to 600 &#176;C. Click on Apply to start the experiment. 
	NOTE: The experiment can be paused or stopped at any time using the quick access buttons in the bottom right corner of the MVS software, without opening the Fusion AX tab.</li>
	<li>After the set temperature of 600 &#176;C is reached, open the Fusion AX tab and select Experiment. Change the Ramp Rate to 2 &#176;C and the Target to 800 &#176;C. Click on Apply to start the experiment. 
	NOTE: The procedure for applying a heating ramp is dependent on the in situ heating system that is used. The steps highlighted above to apply the temperature ramp apply to the system used in this example.</li>
	<li>Highlight any events or points of interest during the experiment using the tagging feature, as shown in step 2.10. Continue to image the sample and adjust the temperature profile as desired. When finished, click on End Session and save the data file using the analysis software (a portion of the database file discussed in the representative results is supplied as Supplementary File 6).</li>
	<li>Open the analysis software to review the session. Plot the temperature, template morphing factor, dose rate, and cumulative dose in the timeline. Export images and movies as desired using the steps outlined in step 3.6 and 3.7. Images and movies may be exported with or without the dose map overlays (Figure 4).</li>
</ol>

TEM Workflows, Results Analysis, and Data Management Using a Machine-Vision Approach

<ol>
	<li>Thomas, J. M., Leary, R. K., Eggeman, A. S., Midgley, P. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+rapidly+changing+face+of+electron+microscopy.">The rapidly changing face of electron microscopy.</a> Chemical Physics Letters. 631, 103-113 (2015).</li><li>Spurgeon, S. R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Towards+data-driven+next-generation+transmission+electron+microscopy.">Towards data-driven next-generation transmission electron microscopy.</a> Nature Materials. 20 (3), 274-279 (2021).</li><li>Gai, P. L., Boyes, E. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+visualisation+and+analysis+of+dynamic+single+atom+processes+in+heterogeneous+catalysts.">In situ visualisation and analysis of dynamic single atom processes in heterogeneous catalysts.</a> Journal of Materials Chemistry A. 10 (11), 5850-5862 (2022).</li><li>Zheng, H., Lu, X., He, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+transmission+electron+microscopy+and+artificial+intelligence+enabled+data+analytics+for+energy+materials.">In situ transmission electron microscopy and artificial intelligence enabled data analytics for energy materials.</a> Journal of Energy Chemistry. 68, 454-493 (2022).</li><li>Tops&#248;e, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Developments+in+operando+studies+and+in+situ+characterization+of+heterogeneous+catalysts.">Developments in operando studies and in situ characterization of heterogeneous catalysts.</a> Journal of Catalysis. 216 (1), 155-164 (2003).</li><li>Wilkinson, M. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+FAIR+Guiding+Principles+for+scientific+data+management+and+stewardship.">The FAIR Guiding Principles for scientific data management and stewardship.</a> Scientific Data. 3 (1), 160018 (2016).</li><li>FAIR Principles. Go Fair Available from: <a target="_blank" href="https://www.go-fair.org/fair-principles/">https://www.go-fair.org/fair-principles/</a> (2023)</li><li>Draxl, C., Scheffler, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=NOMAD:+The+FAIR+concept+for+big+data-driven+materials+science.">NOMAD: The FAIR concept for big data-driven materials science.</a> MRS Bulletin. 43 (9), 676-682 (2018).</li><li>Kelly, D. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Liquid-EM+goes+viral-visualizing+structure+and+dynamics.">Liquid-EM goes viral-visualizing structure and dynamics.</a> Current Opinion in Structural Biology. 75, 102426 (2022).</li><li>AXON Studio Software Download. Protochips, Inc Available from: <a target="_blank" href="https://success.protochips.com/s/?language=en_US">https://success.protochips.com/s/?language=en_US</a> (2023)</li><li>Egerton, R. F., Li, P., Malac, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Radiation+damage+in+the+TEM+and+SEM.">Radiation damage in the TEM and SEM.</a> Micron. 35 (6), 399-409 (2004).</li><li>Grubb, D. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Radiation+damage+and+electron+microscopy+of+organic+polymers.">Radiation damage and electron microscopy of organic polymers.</a> Journal of Materials Science. 9 (10), 1715-1736 (1974).</li><li>Buban, J. P., Ramasse, Q., Gipson, B., Browning, N. D., Stahlberg, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-resolution+low-dose+scanning+transmission+electron+microscopy.">High-resolution low-dose scanning transmission electron microscopy.</a> Journal of Electron Microscopy. 59 (2), 103-112 (2010).</li><li>Chen, Q., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Imaging+beam-sensitive+materials+by+electron+microscopy.">Imaging beam-sensitive materials by electron microscopy.</a> Advanced Materials. 32 (16), 1907619 (2020).</li><li>Krause, F. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Precise+measurement+of+the+electron+beam+current+in+a+TEM.">Precise measurement of the electron beam current in a TEM.</a> Ultramicroscopy. 223, 113221 (2021).</li><li>&#379;ak, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Guide+to+controlling+the+electron+dose+to+improve+low-dose+imaging+of+sensitive+samples.">Guide to controlling the electron dose to improve low-dose imaging of sensitive samples.</a> Micron. 145, 103058 (2021).</li><li>Damiano, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=AXON+dose:+A+solution+for+measuring+and+managing+electron+dose+in+the+TEM.">AXON dose: A solution for measuring and managing electron dose in the TEM.</a> Microscopy Today. 30 (4), 22-25 (2022).</li><li>Allard, L. F., Flytzani-Stephanopoulos, M., Overbury, S. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Behavior+of+Au+species+in+Au/Fe2O3+catalysts+characterized+by+novel+in+situ+heating+techniques+and+aberration-corrected+STEM+imaging.">Behavior of Au species in Au/Fe2O3 catalysts characterized by novel in situ heating techniques and aberration-corrected STEM imaging.</a> Microscopy and Microanalysis. 16 (4), 375-385 (2010).</li><li>Sze, C., Gulari, E., Demczyk, B. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structure+of+coprecipitated+gold-iron+oxide+catalyst+materials.">Structure of coprecipitated gold-iron oxide catalyst materials.</a> Materials Letters. 36 (1-4), 11-16 (1998).</li><li>DiCecco, L. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Advancing+high-resolution+imaging+of+virus+assemblies+in+liquid+and+ice.">Advancing high-resolution imaging of virus assemblies in liquid and ice.</a> Journal of Visualized Experiments. (185), e63856 (2022).</li><li>Dukes, M. J., Gilmore, B. L., Tanner, J. R., McDonald, S. M., Kelly, D. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+situ+TEM+of+biological+assemblies+in+liquid.">In situ TEM of biological assemblies in liquid.</a> Journal of Visualized Experiments. (82), e50936 (2013).</li><li>Scheutz, G. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Probing+thermoresponsive+polymerization-induced+self-assembly+with+variable-temperature+liquid-cell+transmission+electron+microscopy.">Probing thermoresponsive polymerization-induced self-assembly with variable-temperature liquid-cell transmission electron microscopy.</a> Matter. 4 (2), 722-736 (2020).</li><li>Howe, J. Y., Allard, L. F., Bigelow, W. C., Demers, H., Overbury, S. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Understanding+catalyst+behavior+during+in+situ+heating+through+simultaneous+secondary+and+transmitted+electron+imaging.">Understanding catalyst behavior during in situ heating through simultaneous secondary and transmitted electron imaging.</a> Nanoscale Research Letters. 9 (1), 614 (2014).</li><li>Egerton, R. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mechanisms+of+radiation+damage+in+beam-sensitive+specimens,+for+TEM+accelerating+voltages+between+10+and+300+kV.">Mechanisms of radiation damage in beam-sensitive specimens, for TEM accelerating voltages between 10 and 300 kV.</a> Microscopy Research and Technique. 75 (11), 1550-1556 (2012).</li><li>Yoshida, K., Sasaki, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Optimal+accelerating+voltage+for+HRTEM+imaging+of+zeolite.">Optimal accelerating voltage for HRTEM imaging of zeolite.</a> Microscopy. 62 (3), 369-375 (2013).</li><li>Yoshida, K., Sasaki, Y., Kurata, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-resolution+imaging+of+zeolite+with+aberration-corrected+transmission+electron+microscopy.">High-resolution imaging of zeolite with aberration-corrected transmission electron microscopy.</a> AIP Advances. 3 (4), 042113 (2013).</li><li>Lee, J., Nicholls, D., Browning, N. D., Mehdi, B. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlling+radiolysis+chemistry+on+the+nanoscale+in+liquid+cell+scanning+transmission+electron+microscopy.">Controlling radiolysis chemistry on the nanoscale in liquid cell scanning transmission electron microscopy.</a> Physical Chemistry Chemical Physics. 23 (33), 17766-17773 (2021).</li><li>Schneider, N. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electron-water+interactions+and+implications+for+liquid+cell+electron+microscopy.">Electron-water interactions and implications for liquid cell electron microscopy.</a> The Journal of Physical Chemistry C. 118 (38), 22373-22382 (2014).</li><li>Fritsch, B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Radiolysis-driven+evolution+of+gold+nanostructures+-+model+verification+by+scale+bridging+in+situ+liquid-phase+transmission+electron+microscopy+and+x-ray+diffraction.">Radiolysis-driven evolution of gold nanostructures - model verification by scale bridging in situ liquid-phase transmission electron microscopy and x-ray diffraction.</a> Advanced Science. 9 (25), e2202803 (2022).</li><li>Alloyeau, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Unravelling+kinetic+and+thermodynamic+effects+on+the+growth+of+gold+nanoplates+by+liquid+transmission+electron+microscopy.">Unravelling kinetic and thermodynamic effects on the growth of gold nanoplates by liquid transmission electron microscopy.</a> Nano Letters. 15 (4), 2574-2581 (2015).</li><li>Ahmad, N., Le Bouar, Y., Ricolleau, C., Alloyeau, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Growth+of+dendritic+nanostructures+by+liquid-cell+transmission+electron+microscopy:+a+reflection+of+the+electron-irradiation+history.">Growth of dendritic nanostructures by liquid-cell transmission electron microscopy: a reflection of the electron-irradiation history.</a> Advanced Structural and Chemical Imaging. 2 (1), 9 (2016).</li><li>Zhang, Y., Keller, D., Rossell, M. D., Erni, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Formation+of+Au+nanoparticles+in+liquid+cell+transmission+electron+microscopy:+From+a+systematic+study+to+engineered+nanostructures.">Formation of Au nanoparticles in liquid cell transmission electron microscopy: From a systematic study to engineered nanostructures.</a> Chemistry of Materials. 29 (24), 10518-10525 (2017).</li></ol>

All authors are employees of Protochips, Inc.

The interpretation of TEM experimental results is often contingent on many inter-connected experimental parameters, such as microscope settings, imaging conditions, and in the case of operando or in situ experiments, changes to the environment or stimuli1,23. Accurate analysis of large TEM datasets, over which these parameters may be continuously modified, requires significant attention from the operator to accurately record each condition and setting for each image in a lab journal or other external documentation source. As TEM datasets grow in size and complexity, manual recordkeeping becomes unmanageable, and key information may be missed or inaccurately recorded. The MVS software described here consolidates the metadata generated during an experiment from the microscope, the detector/camera, and other systems (such as in situ sample holders) and aligns them with their respective images.
In addition to metadata consolidation, the software applies machine-vision algorithms to track and stabilize the field of view through a combination of spatial, beam, and digital corrections using its Drift Correct and Focus Assist functions. When the Drift Correct function is engaged, a cross-correlation &#39;template&#39; image is generated using the first image pulled into the MVS software. The template is then compared to incoming images to calculate the direction and magnitude of the sample drift or movement. With this information, the MVS software automatically applies the necessary corrections to keep the image features in the same place by adjusting at least one of three parameters: stage location, beam or image shift, and digital image correction. The Focus Assist function utilizes a combination of algorithms to assign a focus value, called the focus score to each image, and those scores are compared to determine the magnitude and direction of defocus adjustment to apply to keep the sample in focus. In STEM imaging mode, the MVS software attempts to maximize contrast through a proprietary version of normalized variance to assign the focus score. In TEM mode, a radial sum of intensity is calculated in the FFT and used to calculate the focus score. Limitations to the MVS software&#39;s ability to optimize the focus occur when it cannot accurately calculate the correct focus score for an image. This typically occurs when the microscope is misaligned or the sample is significantly out of focus during calibration, preventing the software from correctly calculating the correct starting focus score value. The MVS software can have difficulty calculating the focus score for samples with well-defined lattice fringes, as the lattice fringes in the FFT can &#39;overwhelm&#39; the focus scoring algorithm; thus, if a sample moves out of focus, the focus score may not accurately reflect the change in focus. Conversely, working at low magnifications or with a sample that has a low FFT signal can also make it challenging to calculate a good focus score. To mitigate these difficulties, the MVS software contains a number of additional algorithms that can be selected by the user for calculating the focus score if the default settings are unsuitable for the sample. These must be tested and applied on a case-by-case basis to determine the best algorithms for a given experiment.
Morphological changes in the sample structure over time are accounted for using a template morphing factor. This filter is tunable by the operator, so that registration algorithms account for morphological changes over time. Additionally, the software monitors the continuous image, microscope settings, and camera or detector settings to automatically update the template when triggered by changes in sample structure and after any operator-induced changes to the microscope, camera, or detector parameters. As shown in Figure 4, Figure 5, Supplementary File 7, and Supplementary File 8, the MVS software provides effective, immediate stabilization, allowing high resolution imaging of dynamically moving or changing samples. Although the software is capable of controlling very high rates of drift or sample movement, such as those that occur when applying a heating ramp during an in situ experiment, there are limitations to the maximum stage corrections or beam shifts that the software can control if the sample is moving or drifting very rapidly. This limit is a function of the image update rate, field of view size, and drift rate. For a given field of view and image update rate, there is a maximum drift rate that can be corrected, and if the physical movements cannot keep up, then the process may end or become unstable. From the registration templates generated when features such as Drift Correct are applied, additional calculated metadata can be generated. For instance, Match Correlation is a numerical record of the extent of change between templates in a series and is used to identify points in an experimental timeline in which the sample changed. A high match correlation value corresponds to a sample that has undergone changes to its morphology, and a low match correlation value corresponds to a sample whose structure remains relatively static. Match correlation is particularly valuable for in situ studies as it can be plotted graphically, enabling the user to quickly pinpoint images in the series corresponding to significant sample change. It is important, however, to understand that high match correlations values can also correspond to changes in imaging conditions, such as moving the stage or changing the magnification, if these actions are performed while the Drift Correction function remains active.
The calibration workflow presented here utilizes a unique calibration holder and a semi-automated calibration routine to accurately calibrate the beam under a variety of lens conditions with minimal operator intervention. The dose calibration routine is accessed through the MVS software installed on the TEM. The MVS software automatically reads the relevant microscope settings to save all measurements to reference for later experiments. On some TEMs, it is not possible to read the aperture or monochromator settings, and these must be entered into the MVS software settings by the operator during calibrations and during use. There are reminders built into the software to help keep these operator input settings updated by following the program prompts. The development of a holder with a built-in current collector, rather than relying on one integrated elsewhere in the microscope column, is a deliberate design choice. This enables the current collector to be positioned at the same plane as a sample, eliminating errors in the current measurement caused by beam deflection or differences in the absorption of electrons by apertures at different beam positions. The MVS software follows an automated routine to measure the beam current and area for any combination of lens conditions. The software can then correlate these measured calibrations with the camera or screen current and extrapolate any changes in magnification etc. to the beam area during the experiment. Once generated, these calibration files can be used immediately and are automatically saved for later use if the software detects the same settings being used during a future session. Although the longevity of the calibration file varies from microscope to microscope, the authors have found that they are able to use the same calibration files for several months without observing substantial changes to the current values. There are built-in routines monitoring the emission profile of guns to help keep these calibrations relevant, especially on cold FEG emission guns.
Normalization of dose measurements between microscopes and automated tracking of a sample&#39;s beam exposure are critical functions of the MVS software, as they allow quantitative comparisons of dose conditions between experiments to be performed on different microscope systems. Dose induced degradation of a zeolite sample (ZSM-5), obtained during identical experiments using different microscopes, results in complete disappearance of the FFT spots after a maximum cumulative or threshold electron dose (~60.000 e-/&#197;2 when applying a dose rate of ~500 e-/&#197;2&#183;s) for both setups. These comparative results demonstrate that the dose software facilitates reproducible, quantitative dose measurements. The small difference in the cumulative dose at which full FFT spot disappearance is observed for each experiment is likely a result of the different acceleration voltages employed by the two microscopes, with lower acceleration voltages resulting in more radiation damage pathways, and higher acceleration voltages typically resulting in more knock-on damage24. Literature results for the critical dose of ZSM-5 nanoparticles range from 9,000-14,000 e-/&#197;2 using the first FFT spot disappearances, rather than the complete disappearance of all the FFT spots25,26. In our results, the first FFT spot disappearance corresponds to a cumulative dose of around 25,000 e-/&#197;2. Previous studies relied on current measurements obtained using a phosphor screen, which is well documented to underestimate beam current measurements when compared to a Faraday cup15. The determined critical dose can vary by a factor of two or more, depending on which FFT peak is used to track the dose. This indicates that the higher spatial frequencies degrade first, and can result in different values depending on the zone access used during the measurements (our results focused on FFT spots from the entire zeolite crystal, rather than specific structural features)25,26. These differences in techniques and current calibration account for the difference in values between the two experiments reported in our results and previous literature studies.
Although the electron dose interactions are a significant factor in many TEM experiments, in situ and specifically liquid-EM studies are particularly sensitive to its effects. Radiolysis of liquids by the electron beam results in a cascade of chemically reactive species which can interact with the sample, complicating the analysis. Both the dose rate or fluence used during a liquid-EM experiment and the cumulative dose can have an influence on the concentration of radical species generated due to liquid radiolysis27,28. Thus, collecting and recording both cumulative dose and dose rate metadata throughout an experiment allows direct correlation between images and a sample&#39;s dose history, and is a more accurate way to elucidate and control the impact of the electron beam in these experiments. Although not covered in this protocol, an example of the utility of the dose management features for liquid-EM is shown in Figure 6.
<img alt="Figure 6" class="xfigimg" src="/files/ftp_upload/65446/65446fig06.jpg" /> 
Figure 6: Beam-induced growth of gold nanoparticles during an in situ liquid-EM experiment. (A) Low-magnification STEM overview of the resulting particle growth with a color overlay of the cumulative dose map across the region. Red areas in the overlay indicate regions of high cumulative dose exposure and yellow areas indicate regions of lower exposure. Highlighting an individual pixel with the cursor or drawing a box over an area using the included drawing tools indicates the cumulative dose for that pixel or area. The scale bar is 2 &#181;m. (B,C) Higher magnification STEM images of the areas indicated by the orange boxes (b,c) in A. Area b, exposed to a higher cumulative dose (10.811 e-/&#197;2) contains larger particles than those found in area c, which was exposed to a lower cumulative dose (0.032 e-/&#197;2). <a href="https://www.jove.com/files/ftp_upload/65446/65446fig06large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
The enriched dose rate and cumulative dose metadata simplifies the analysis of dose-dependent nanomaterial growth and degradation pathways. Figure 6 shows the beam-induced reduction of a solution of gold auric chloride (HAuCl3) ions in water during liquid-EM experiments. From the color dose map overlay in Figure 6A, it is easy to visualize that the cumulative electron dose influences the resulting size and shape of the nanoparticles29,30,31,32. The low magnification STEM overview shows regions exposed to a high (red) and low (yellow) cumulative dose. The particles in the region exposed to higher doses are larger than those in the regions exposed to lower cumulative doses. Because the dose metadata is directly embedded in each image at the pixel level, the complex effects of electron dose in liquid-EM experiments can now be systematically analyzed in a way that was never-before achievable.
In this protocol, we have demonstrated that MVS software provides a comprehensive solution for calibrating, monitoring, and tracking both the electron dose and the total dose delivered to a sample on a pixel-by-pixel basis. This ability unlocks a new paradigm for imaging dose-sensitive samples and understanding the electron beam interactions. It is particularly exciting for liquid-EM experiments, as it will allow for a more effective interrogation into the role that electron dose plays and improve experimental reproducibility. It is our hope that this new framework will allow the accurate collection of dose rate and accumulated dose information, facilitate sharing this data with the community for a more accurate interpretation of TEM results, and advance scientific collaboration and data sharing by enabling FAIR principal reporting and analysis.

Transmission electron microscopes (TEMs) and their capabilities have benefited enormously from advances in cameras, detectors, sample holders, and computing technologies. However, these advances are hampered by disconnected data streams, limitations of human operation, and cumbersome data analysis1,2. Moreover, in situ and operando experiments adapt TEMs into real-time nanoscale laboratories, enabling samples to be studied in gas or liquid environments while simultaneously applying a range of external stimuli3,4,5. The adoption of such complex workflows have only magnified these limitations, and the resulting increase of the size and complexity of these data streams is an area of growing concern. Thus, there is a growing emphasis on utilizing machine-actionability to find, access, interoperate, and reuse data, a practice known as the FAIR principles6. Publishing research data in accordance with the FAIR principles concept has received favorable attention from governmental agencies around the world7,8, and application of the FAIR principles using machine-vision software is a key step in their adoption.
A machine-vision synchronization (MVS) software platform has been developed in response to the specific pain points inherent to performing and analyzing complex, metadata-heavy TEM experiments (particularly in situ and operando experiments)9. Once installed on the TEM, the MVS software connects, integrates, and communicates with the microscope column, detectors, and integrated in situ systems. This enables it to continuously collect images and align those images with their experimental metadata, forming a comprehensive searchable database, a timeline of the experiment from start to finish (Figure 1). This connectivity allows the MVS software to apply algorithms that intelligently track and stabilize a region of interest (ROI), even when samples are undergoing morphological changes. The software applies adjustments to stage, beam, and digital corrections as necessary to stabilize the ROI through its Drift Control and Focus Assist functions. In addition to enriching the images with the raw metadata produced from the different experimental systems, the software can produce new, computational metadata using image analysis algorithms to calculate variables between images, which allow it to automatically correct for sample drift or changes in focus.
TEM images, and their associated metadata collected through the MVS software, are organized as an experimental timeline which can be opened and viewed by anyone via the free, offline version of the analysis software, Studio (hereafter referred to as the analysis software)10. During an experiment, the MVS software syncs and records three types of images from the microscope&#39;s camera or detector, which are displayed at the top of the timeline below the image viewer: single acquisition (individual single aquisition images acquired directly from the TEM software), raw&#160;(images from the detector/camera live stream that have not had any digital drift corrections applied; these images may have been physically corrected via stage movement or beam shift), and drift corrected (images from the detector/camera live stream that have been digitally drift). Data collected during an experiment or session can be further refined into smaller sections or snippets of data, known as collections, with no loss of embedded metadata. From the analysis software, images, image stacks, and metadata can be directly exported into a variety of open format images and spreadsheet types for analysis using other tools and programs.
The framework of microscope control, stabilization, and metadata integration enabled by the MVS software also allows the implementation of additional machine-vision programs or modules, designed to alleviate limitations in current TEM workflows. One of the first modules developed to take advantage of this synchronization platform is electron dose calibration and spatial tracking of beam exposed areas within the sample. All TEM images are formed from the interaction between the sample and the electron beam. However, these interactions can also result in negative, inescapable impacts on the sample, such as radiolysis and knock-on damage11,12, and require a careful balance between applying a high enough electron dose to generate the image and minimizing the resulting beam damage13,14.
Although many users rely on screen current measurements to estimate the electron dose, this method has been shown to widely underestimate the actual beam current15. Qualitative dose values can be obtained via the screen current on the same microscope with the same settings, but reproducing these dose conditions using different microscopes or settings is highly subjective. Additionally, any imaging parameter adjustments made by the user during the experiment, such as spot size, aperture, magnification, or intensity, require a separate measurement of the screen current to calculate the resulting dose. Users must either rigorously limit the imaging conditions used during a given experiment or meticulously measure and record each lens condition used, significantly complicating and extending the experiment beyond what is feasible for normal operation of the microscope16,17.
Dose, referred to as dose software for this protocol, is a dose calibration software module that utilizes a dedicated calibration holder designed to enable automated current measurements. A Faraday cup, the gold standard for accurate beam current calibration15, is integrated into the tip of the calibration holder. The MVS software performs a series of beam current and beam area calibrations for each lens condition and embeds those values on the images at the pixel level.
In this video article, MVS software protocols designed to enhance all areas of the TEM workflow are presented using representative nanomaterial samples. A beam sensitive zeolite nanoparticle sample14 is used to demonstrate the calibration and dose management workflows. We perform a representative in situ heating experiment using an Au/FeOx nanocatalyst18,19 sample that undergoes significant morphological changes when heated. This in situ experiment highlights the software&#39;s stabilization algorithms and its ability to collate multiple streams of metadata, which is an inherent challenge for in situ and operando studies. Although not described in the protocol, because of its unique electron dose sensitivity, we discuss representative examples of the software&#39;s utility for liquid-EM studies (protocols for which have been previously reported in the literature20,21,22), and how these techniques can be applied to improve the understanding of the effect of dose on liquid-EM experiments. Finally, we show how data analysis is streamlined using the offline analysis software to visualize, filter, and export a variety of image, video, and data files into other accessible formats.
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/65446/65446fig01.jpg" /> 
Figure 1: User interface examples for MVS and analysis software. (A) The synchronization software image viewing pane and control panel. A connection between the TEM and the synchronization software is established by activating the Connect button, which streams the images and metadata from the microscope into the synchronization software. From the image viewer, the operator can perform a variety of machine-vision assisted operations, such as Drift Correct and Focus Assist. It also provides the ability to apply Tag Images and Review Session without disrupting data collection. (B) Screenshot of the image analysis software highlighting the location of the Image View Port, Timeline, and the Metadata and Analysis panel. The analysis software can be accessed at any point during an experiment to review the images acquired up to that time point using the Review Session button. <a href="https://www.jove.com/files/ftp_upload/65446/65446fig01large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>ARM200F CFEG</td>
			<td>JEOL</td>
			<td></td>
			<td>Transmission Electron Microscope (200 kV)</td>
		</tr>
		<tr>
			<td>AXON DOSE Calibration Holder</td>
			<td>Protochips, Inc.</td>
			<td>AXA-FC-TFS</td>
			<td>Dose calibration and management hardware package for ThermoFisher ScientificTEM</td>
		</tr>
		<tr>
			<td>AXON DOSE Software:&#160; Version 10.6.5.3</td>
			<td>Protochips, Inc.</td>
			<td>AX-MOD-DOSE-01-1YR</td>
			<td>Dose calibration and management software</td>
		</tr>
		<tr>
			<td>AXON Studio Software: Version 10.6.5.3</td>
			<td>Protochips, Inc.</td>
			<td>No Part Number. 
			Available to download at&#160; success.protochips.com</td>
			<td>Offline analysis software for AXON datasets.&#160; A free copy of the AXON Studio software is available for down load at:&#160; success.protochips.com</td>
		</tr>
		<tr>
			<td>AXON Synchronicity Core</td>
			<td>Protochips, Inc.</td>
			<td>AXON-CORE</td>
			<td>Hardware component of the synchronization software.</td>
		</tr>
		<tr>
			<td>AXON Synchronicity Software:&#160; Version 10.6.5.3</td>
			<td>Protochips, Inc.</td>
			<td>AX-MOD-SYNCPRO-01-1YR</td>
			<td>Synchronization software</td>
		</tr>
		<tr>
			<td>Fusion In-Situ Heating E-chip</td>
			<td>Protochips, Inc.</td>
			<td>E-FHDC-VO-10</td>
			<td>Sample Support E-chip with carbon film.&#160; Used with in situ heating system</td>
		</tr>
		<tr>
			<td>Fusion Select In Situ Heating System</td>
			<td>Protochips, Inc.</td>
			<td>FFAD-6200-EXP</td>
			<td>In-situ MEMs heating system for ThermoFisher Scientific TEM.</td>
		</tr>
		<tr>
			<td>Gold(III) chloride (50% gold basis) hydrate 50790</td>
			<td>Sigma Aldrich</td>
			<td>27988-77-8</td>
			<td>Used to prepare Au/FeOx nanocatalyst.&#160; Coprecipitation synthesis procedure followed in C. Sze et al. Materials Letters. 36 (1&#8211;4), 11&#8211;16 (1998)</td>
		</tr>
		<tr>
			<td>Iron (III) Oxide 310050 (Fe2O3)</td>
			<td>Sigma Aldrich</td>
			<td>1309-37-1</td>
			<td>Used to prepare Au/FeOx nanocatalyst.&#160; Coprecipitation synthesis procedure followed in C. Sze et al. Materials Letters. 36 (1&#8211;4), 11&#8211;16 (1998)</td>
		</tr>
		<tr>
			<td>Titan ChemiSTEM</td>
			<td>ThermoFisher Scientific</td>
			<td></td>
			<td>Transmission Electron Microscope (300 kV)</td>
		</tr>
		<tr>
			<td>Zeolite ZSM-5</td>
			<td>Zeolyst</td>
			<td>CBV 8014</td>
			<td>&#160;Nanocatalyst sample:&#160; 80 SiO2/Al2O3 Mole Ratio</td>
		</tr>
	</tbody>
</table>

a machine-vision approach to transmission electron microscopy workflows, results analysis and data management

Transmission electron microscopy (TEM) enables users to study materials at their fundamental, atomic scale. Complex experiments routinely generate thousands of images with numerous parameters that require time-consuming and complicated analysis. AXON synchronicity is a machine-vision synchronization (MVS) software solution designed to address the pain points inherent to TEM studies. Once installed on the microscope, it enables the continuous synchronization of images and metadata generated by the microscope, detector, and in situ systems during an experiment. This connectivity enables the application of machine-vision algorithms that apply a combination of spatial, beam, and digital corrections to center and track a region of interest within the field of view and provide immediate image stabilization. In addition to the substantial improvement in resolution afforded by such stabilization, metadata synchronization enables the application of computational and image analysis algorithms that calculate&#8239;variables between images. This calculated metadata can be used to analyze trends or identify key areas of interest within a dataset, leading to new insights and the development of more sophisticated machine-vision capabilities in the future. One such module that builds on this calculated metadata is dose calibration and management. The dose module provides state-of-the-art calibration, tracking, and management of both the electron fluence (e-/&#197;2&#183;s-1) and cumulative dose (e-/&#197;2) that is delivered to specific areas of the sample on a pixel-by-pixel basis. This enables a comprehensive overview of the interaction between the electron beam and the sample. Experiment analysis is streamlined through a dedicated analysis software in which datasets consisting of images and corresponding metadata are easily visualized, sorted, filtered, and exported. Combined, these tools facilitate efficient collaborations and experimental analysis, encourage data mining and enhance the microscopy experience.

Author Spotlight: A Machine-Vision Approach to Transmission Electron Microscopy Workflows, Results Analysis and Data Management  

A Machine-Vision Approach to Transmission Electron Microscopy Workflows, Results Analysis and Data Management

This technology was developed to make high-performance TEM studies accessible to users of all skill levels. Furthermore, scientific advancements require the collaborative efforts of multiple investigators, so an efficient platform to share and analyze large, complex data sets is essential for successful research Operando and in situ studies transform a TEM into a real-time nanolaboratory, allowing researchers to explore the dynamic nano-scale processes that control materials'growth properties. One of the greatest challenges for in-situ TEM studies is isolating the beam irradiation effects from the intrinsic behavior of the sample.Accurate electron dose measurement and tracking is essential, but without dose management software, one can only measure electron dose rate rather than the total or critical dose Complex TEM workflows generate large data sets which must be manually aligned and indexed to their respective images. In this time-consuming process, the key information, such as adjustments to imaging conditions or samples environment, may be lost, complicating analysis and reproducibility. We have developed a machine-vision workflow to collect and index the images and metadata produced during an experiment into a data-enriched, searchable timeline.Computational and image analysis algorithms can calculate variables between images, apply corrections, and identify hidden trends. By calculating, synchronizing, and indexing new metadata into each image, multimodal analysis is suddenly a new possibility. For example, accurate accumulated dose and dose rate information in the zeolite images allows quantitative assessment of sample damage across thousands of images.We will continue to push the capabilities of in-situ TEM by making results accessible and interpretable and improving experimental reproducibility. This software is a platform to develop workflow-driven modules that target specific, historically difficult applications to make in-situ TEM experiments easier and more information rich.

This work highlights the utility of data acquisition using MVS software for TEM imaging and in situ experiments. Microscope alignment and condition setup were performed and selected through the TEM manufacturer&#39;s default controls. After initial setup, the protocols presented in this video article were conducted through the MVS software. A 300 kV TEM was used for all experiments presented in the video protocol and representative data, except for the comparison zeolite data which was acquired using a 200 kV cold FEG (Figure 3D-F and Table 1). All metadata was collected and aligned to its respective images automatically by the MVS software.
After launching the software and selecting the appropriate workflow from the menu, a connection to the microscope is established by activating the Connect button in the toolbar in the far left of the image viewer, as shown in Figure 1A. When the Connect button is highlighted, images and associated metadata from the microscope are automatically streamed into the MVS software and appear in the image view pane. These images and their associated metadata are saved chronologically in a timeline that can be opened, reviewed, and analyzed without interrupting the recording of new data into the timeline (Figure 1B). Streaming can be interrupted by the user at any time by deactivating the Connect icon.
Once the connection is activated, other workflows that are dependent on the MVS software framework can be accessed. In the examples shown in this video protocol, a dose calibration must be performed before utilizing the other functions of the MVS software. Dose calibration is an automated process controlled by the MVS software; it uses a dedicated Faraday cup dose calibration holder to measure the beam&#39;s current and area for the combination of parameters. The Faraday cup calibration holder, shown in Figure 2, connects to an external picoammeter, which precisely measures the beam current. Once inserted in the microscope, the fiducial alignment hole is centered and the desired beam conditions to be calibrated (spot sizes, apertures, and magnifications) are entered in the software. The software performs a series of calibration steps for each combination of the selected conditions. During dose calibration, the holder automatically moves between the integrated Faraday current collector cup and the through-hole. The current measurement for each combination of lens conditions is measured on the Faraday cup by the picoammeter. Then, the software translates the stage to center the beam in the through-hole and the beam area is determined through machine-vision algorithms. This series of measurements builds a profile of the the relationship between the intensity/brightness and the beam area. This enables the software to extrapolate the beam area as the intensity/brightness setting is adjusted during an experiment regardless of the field of view. Values for cumulative dose and dose rate are calculated using these beam current and beam area measurements and a dose calibration file is generated. This process essentially defines a dose &#34;fingerprint&#34; for the TEM and its individual lens conditions. Once the dose is calibrated for the TEM, the user is able to operate normally and freely adjust the magnification and intensity with no loss of dose information or manual note taking17. After calibration is complete, the dose calibration holder is removed, allowing the sample to be inserted as normal. The calibration process for both the TEM and STEM modes normally takes less than 10 min.
After calibrating the dose conditions, a commercially purchased zeolite nanoparticle (ZSM-5) sample was imaged under high dose rate conditions to determine the threshold (cumulative) dose at which the sample is too damaged to provide structural information. The ZSM-5 nanoparticles were suspended in ethanol and dropcast on a conventional copper TEM grid. They were imaged continuously at 300 kV in TEM mode using a spot size of 3 and a 100 &#181;m condenser aperture. The dose rate read by the MVS software under high dose rate conditions was 519 e-/&#197;2&#183;s. Nanoparticles in the field of view were imaged continously until the peaks in the FFT disappeared, indicating degradation of the crystalline structure, as shown in Figure 3A-C and Supplementary File 3. Overlays (which can be added during a live experiment or afterward in the analysis software) were applied to the TEM images to show the date and time, dose rate, maximum (cumulative) dose, and magnification. The dose rate was kept constant during experiments, with the cumulative dose (max dose) increasing as a function of time. The FFT peaks began to disappear after 42 s of continuous imaging (Figure 3B). At 1 min and 20 s and a cumulative dose of ~60,000 e-/&#197;2, the FFT peaks had completely disappeared (Figure 3C).
To show that this calibration method generates quantitative dose measurements that can be applied to other microscopes operating under different settings, the same calibration process and zeolite degradation experiment was conducted using a 200 kV cold field emission gun (FEG) TEM and a spot size of 1. This microscope was calibrated using the same procedure described in Method 1, and the same experiment described in Method 2 was performed using the new spot size and aperture settings. The beam settings were adjusted so that the difference in the applied dose rate between the two experiments was negligible (499 e-/&#197;2&#183;s vs. 519 e-/&#197;2&#183;s). As shown in Figure 3D-F and summarized in Table 1, the FFT spots fully disappear after 1 min and 50 s of continuous imaging and a cumulative dose of 58,230 e-/&#197;2, which aligns with the values obtained in the first experiment.
An example of how the MVS software can benefit in situ experiments was shown by performing a heating experiment. A representative nanocatalyst sample, Au/FeOx (synthesized following a published procedure19), was selected as an example system because it undergoes dynamic morphological and structural changes at high temperatures. This temperature-induced mobility makes it challenging to keep the ROI centered within the field of view due to the sample&#39;s own movement and thermal expansion of the sample suport itself during temperature changes18. With the Drift Correct and Focus Assist features enabled, the sample was imaged over a period of ~30 s at 800 &#176;C. At elevated temperatures, the gold nanoparticles within the Au/FeOx migrated along the surface of the iron oxide support and sintered to form larger particles, as shown in Figure 4 and as a movie in Supplementary File 7. Figure 5 shows a series of TEM snapshots (Figure 5A-F) of a porous region within an Au/FeOx nanocatalyst, recorded at various time points (Figure 5G) during an in situ heating experiment. The coordinated drift value of the ROI was automatically calculated by the software. The coordinated drift and temperature values of the images over the course of the series is shown graphically in Figure 5G. As expected, the coordinated drift of the sample increases as the temperature profile increases, from a rate of ~9 nm/min to ~62 nm/min, and begins to decrease toward leveling off as the temperature is held constant. Despite this high rate of drift, and changes to the sample&#39;s morphology, high resolution images are easily obtained during temperature ramping, revealing movement within the porous region, as shown in Supplementary File 8. Refer to Supplementary File 9 for download instructions and computer specifications.
<img alt="Figure 2" class="xfigimg" src="/files/ftp_upload/65446/65446fig02.jpg" /> 
Figure 2: Electron dose calibration and tracking. (A) Dose is calibrated using a dedicated sample holder that contains a current collector positioned at the sample plane for beam current measurements. (B) Illustration of the features of the tip design: Left: Faraday cup; Middle: fiducial hole; Right: through hole (C). The applied electron dose can be visualized in the software using color-coded maps to denote different dose exposures within an image. <a href="https://www.jove.com/files/ftp_upload/65446/65446fig02large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" class="xfigimg" src="/files/ftp_upload/65446/65446fig03.jpg" /> 
Figure 3: Electron dose induced degradation of zeolite (ZSM-5) nanoparticles. (A-C) Snapshots taken over a 1 min and 20 s period showing degradation data obtained with a 300 kV FEG and a measured dose rate of 519 e-/&#197;2&#183;s; the zeolite degrades within 1 min and 20 s. (D-E) Snapshots taken over a 1 min and 50 s time period showing degradation data obtained with a 200 kV cold FEG TEM and an electron dose rate of 499 e-/&#197;2&#183;s; the insets show the FFT spot fading over time. The scale bar is 60 nm. <a href="https://www.jove.com/files/ftp_upload/65446/65446fig03large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 4" class="xfigimg" src="/files/ftp_upload/65446/65446fig04.jpg" /> 
Figure 4: AXON synchronicity applies machine-vision algorithms to track and stabilize dynamically evolving samples. Metadata generated during the experiment can be plotted along the timeline, allowing the user to quickly pair an image with its associated metadata as they scroll through the image series generated during the experiment. (A-H) Images of a nanocatalyst sample (Au/FeOx) at 800 &#176;C recorded over a period of 28 s both with (A-D) and without (E-H) the dose map overlay. Red areas in the overlay indicate regions of high cumulative dose exposure, and yellow areas indicate regions of lower exposure. Highlighting an individual pixel indicates the cumulative dose for that pixel. White arrows in panels E-H indicate two particles that merge during the experiment, and the orange arrow indicates the trajectory of a moving gold particle. (I) The experiment timeline generated by the analysis software for the image series shown in A-H. The orange dots at the top of the timeline denote raw (non-digitally corrected) images and the blue dots denote drift corrected images. The orange vertical bars indicate the points on the timeline corresponding to the images shown panels A-H. The scale bar is 40 nm. <a href="https://www.jove.com/files/ftp_upload/65446/65446fig04large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 5" class="xfigimg" src="/files/ftp_upload/65446/65446fig05.jpg" /> 
Figure 5: TEM snapshots of a porous region within an Au/FeOx nanocatalyst at various time points. The MVS software stabilizes and centers the sample even during high drift rates, such as those that occur during a temperature ramp through the application of stage, beam shift, and digital corrections, as indicated by machine-vision algorithms. (A-F) TEM snapshots of a porous region within an Au/FeOx nanocatalyst, recorded at various (G) time points during an in situ heating experiment. The drift rate of the ROI is automatically calculated and recorded during an experiment by the MVS software. As plotted in (G), as the temperature profile is changed (the blue line), the drift rate (orange line) increases as the temperature increases and decreases as the temperature is held constant. <a href="https://www.jove.com/files/ftp_upload/65446/65446fig05large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Microscope Type</td>
			<td>300 kV FEG TEM</td>
			<td>200 kV Cold FEG TEM</td>
		</tr>
		<tr>
			<td>Spot Size/Condenser 2 Aperture</td>
			<td>3/100 &#181;m</td>
			<td>1/100 &#181;m</td>
		</tr>
		<tr>
			<td>Dose Rate</td>
			<td>519 e-/A2&#8226;s1</td>
			<td>499 e-/A2&#8226;s1</td>
		</tr>
		<tr>
			<td>Loss of Structure Measured by FFT 
			(Accumulated Dose)</td>
			<td>60,270 e-/A2 </td>
			<td>58,230 e-/A2 </td>
		</tr>
	</tbody>
</table>
Table 1: Summary comparison of zeolite degradation results obtained from different microscopes.
Supplementary File 1: Screenshot of the MVS software interface with the dose management tab open. <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 1 - User Interface.pdf" target="_blank">Please click here to download this File.</a>
Supplementary File 2: MVS software database file of the beam-induced zeolite degradation experiment. This viewing/analysis software is available to download for free. Please see Supplementary File 9 for download instructions and computer specifications. <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental_File_2-Data_High_Dose_Zeolite_Degradation_TFS_compressed.zip" target="_blank">Please click here to download this File.</a>
Supplementary File 3: Movie of the beam induced zeolite degradation. <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 3 - Zeolite Degradation TFS.mp4" target="_blank">Please click here to download this File.</a>
Supplementary File 4: CSV file 1 (zeolite degradation: raw data [mechanical correction only]) <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 4 - Zeolite CSV Raw.csv" target="_blank">Please click here to download this File.</a>
Supplementary File 5: CSV file (zeolite degradation: drift corrected [mechanical + digital correction]) <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 5 - Zeolite CSV Drift Corrected.csv" target="_blank">Please click here to download this File.</a>
Supplementary File 6: MVS software database file nanocatalyst in situ heating experiment. <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 6 - AuFeOx 800C Madeline Dressel Dukes.zip" target="_blank">Please click here to download this File.</a>
Supplementary File 7: Movie of the nanocatalyst at 800 &#176;C with dose overlays. <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 7 - AuFeOx Dose Map 800.mp4" target="_blank">Please click here to download this File.</a>
Supplementary File 8: Movie of the nanocatalyst during a temperature ramp with coordinated drift values. <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 8 - AuFeOx Temperature Ramp.mp4" target="_blank">Please click here to download this File.</a>
Supplementary File 9: Instructions for downloading the free analysis software. <a href="https://www.jove.com/files/ftp_upload/65446/Supplemental File 9 - Download Instructions.pdf" target="_blank">Please click here to download this File.</a>

Watch this Scientific Journal Video about A Machine-Vision Approach to Transmission Electron Microscopy Workflows, Results Analysis and Data Management at JoVE.com

Here, we present a protocol to utilize machine-vision software to stabilize dynamic processes during TEM imaging, while concurrently indexing multiple streams of metadata to each image into a navigable timeline. We demonstrate how this platform enables automated calibration and mapping of the electron dose over the course of an experiment.

Transmission electron microscopy (TEM) enables users to study materials at their fundamental, atomic scale. Complex experiments routinely generate ...

a-machine-vision-approach-to-transmission-electron-microscopy

Research

JoVE Journal

Biology

Dose Calibration of the Transmission Electron Microscope for TEM and Scanning TEM (STEM) Imaging Modes Using a Machine-Vision Approach

Begin the dose calibration by clicking the Connect icon in the MVS software installed on TAEM. Select the microscope and activate the connection between the TEM and the MVS software to visualize the images from the camera or detector in the image viewer. Navigate to the Dose tab and click on Start Dose Area Calibration.Click OK to confirm the calibration hardware and follow the software prompts to enter the requested user configurable values. Then click Start Dose Current Calibration. Follow the software prompts and enter the requested user configurable values to complete the calibration.

Determination of Dose Threshold Using the Machine-Vision Synchronization (MVS) and Dose Software

Begin by opening the MVS software application on the TEM instrument and selecting other. Connect the microscope to the MVS software. Navigate to the image metadata tab and select magnification, max dose and dose rate to overlay on the image stream seen in the live display.Other metadata may be included if the user desires. Open the dose tab. Select dose management and enable dose monitoring.Then select show dose layer and show position uncertainty to activate automated electron dose tracking and display the dose color overlay. Set the values for the low dose level and high dose level before pressing save. Then navigate to the settings tab.Select dose and set the dose navigation map opacity and dose image overlay opacity values. Activate drift correction in the live image viewer window by clicking on drift correct. Next, navigate to the data view tab and plot the metadata values defocus and focus quotient on the y axis.Activate focus assist then select calibrate focus to run the calibration of the automated focus assist. Once the calibrate focus routine is complete close the data view tab. In the MVS software, open the image analysis tab and activate the live FFT and quadrants one and two options.Using the microscope software controls adjust the beam conditions so that the electron flux is approximately 600 angstrom square per second. Move to a new region in the sample and center the sample ROI in the live view of the MVS software. Maintain a constant dose rate while continuously imaging the same ROI until the spots corresponding to the atomic structure and the FFT have disappeared.

Metadata and Trend Analysis and Data Export Using the Analysis Software

Launch the offline analysis software to view the fully synchronized datasets and open the experiment session file by selecting it from the library. Display the drift corrected images by activating the DC tab below the image viewport before selecting the desired data overlays by checking their respective overlay data boxes in the image metadata tab. Other metadata may be plotted as the user desires.Highlight or scroll through these graphical plots to update the image displayed in the viewport. Access various tools through the image analysis toolbox and data view tabs. Access the FFT for each image through the image analysis to plot live FFT to update it while scrolling through images.Use the fading of the FFT peaks to determine the time point at which the zeolite nanoparticle structure loses crystallinity. Note the dose conditions in the software using the tag function. Highlight the tag icon and enter the desired tags to denote a specific series of images within the timeline.Images will be tagged with this text until the tag icon is deselected. To easily filter large data datasets into smaller shareable ones without losing their associated metadata, open the filter panel and adjust the sliders to select only a dose rate equal to or above 500 square angstroms per second. Save the new collection using the name 500 dose rate and above.Select the images by highlighting them in the timeline or using the filter options. Then export the metadata as a CSV file and the image series as a movie file using the same publish option. The zeolite nanoparticle ZSM5 imaged to determine the threshold dose showed that the dose rate read by the MVS software under high dose rate conditions was 519 electrons per square angstrom per second.Nanoparticles in the field of view were imaged continuously until the FFT peaks disappeared, indicating crystalline structure degradation. The FFT peaks began disappearing after 42 seconds of continuous imaging. The FFT peaks had completely disappeared at one minute and 20 seconds and a cumulative dose of approximately 60, 000 electrons per square angstrom.The same process was repeated with a different microscope. The FFT spots fully disappeared after one minute and 50 seconds of continuous imaging and a cumulative dose of 58, 230 electrons per square angstrom.

In Situ Heating Study of Gold on Iron Oxide Nanoparticles

To begin, select the appropriate workflow option from the MVS software. Follow the workflow prompts to confirm the electrical connection between the holder and the heating e-chip by loading the calibration file and performing a device check. After connecting the microscope to the MVS software, center the sample ROI in the field of view.Access the Temperature Control Settings by clicking the Experiment button and Manual Control mode. Then, set the ramp rate to 25 degrees Celsius per second and the target to 200 degrees Celsius. Click on Apply to start the experiment.After reaching 200 degrees Celsius, set the ramp rate to 10 degrees Celsius per second. Adjust the target to 600 degrees Celsius and click Apply. After the set temperature of 600 degrees Celsius is reached, change the ramp rate to 2 degrees Celsius and the target to 800 degrees Celsius.Click on Apply to start the experiment. Once done, open the Analysis Software to review the session. In the timeline, plot the temperature, template morphing factor, dose rate, and cumulative dose.Export images and movies using the Publish option with or without the dose map overlays. The heating experiment performed using a representative nanocatalyst sample gold on iron oxide showed that at elevated temperatures, the gold nanoparticles within the gold on iron oxide migrated along the surface of the iron oxide support and centered to form larger particles. An in-situ heating experiment recorded a series of TEM snapshots of a porous region within a gold on iron oxide nanocatalyst at various time points.The coordinated drift of the sample increased with the increased temperature from a rate of 9 to 62 nanometers per minute, and began to decrease towards leveling off with the constant temperature. The MVS software stabilized the particle in the field of view throughout the entire temperature ramp profile, enabling high resolution imaging.

1.1K Views.  Protochips, Inc..  Here, we present a protocol to utilize machine-vision software to stabilize dynamic processes during TEM imaging, while concurrently indexing multiple streams of metadata to each image into a navigable timeline. We demonstrate how this platform enables automated calibration and mapping of the electron dose over the course of an experiment.