Name: determining the chemical composition of corrosion inhibitor/metal interfaces with xps: minimizing post immersion oxidation
Uploaded: 2017-03-15T13:00:00.000+00:00
Duration: 7 min 44 s
Description: Watch this Scientific Journal Video about Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation at JoVE.com

The work was supported by AkzoNobel through a collaboration agreement with The University of Manchester. PMG is grateful to the Fondo Sectorial CONACYT - SENER Hidrocarburos and the Instituto Mexicano de Peter&#243;leo for financial support. TB thanks Mellitah Oil &#38; Gas Companyfor funding her studentship. KK acknowledges financial support from the EPSRC (EP/L01680X/1) through the Materials for Demanding Environments Centre for Doctoral Training.&#34; PAL thanks CONACYT for financially supporting her stay in Manchester. Finally, all of the authors acknowledge Ben Spencer for his technical support and advice.

1. Substrate/Solution Preparation
<ol>
	<li>Preparation of carbon-steel substrate
	<ol>
		<li>Cut an approximately 2 - 3 mm thick disc from a cylindrical carbon-steel rod (10 &#177; 2 mm diameter), using a precision cutting machine. Employ cooling fluid during the cutting procedure to minimize mechanical damage.</li>
		<li>Grind both circular faces, and the edge of the disc-shaped sample with a series of SiC papers, i.e. 600 grit, 800 grit, 1,200 grit, 2,400 grit, and 4,000 grit.</li>
		<li>Polish both circular faces, and the edge of the disc-shaped sample with either diamond paste or alumina powder (3 &#956;m and/or 1 &#956;m) until a mirror finish is obtained.</li>
		<li>Sonicate the sample at room temperature for approximately 10 minutes in each of the following: deionized water, acetone, ethanol, and finally deionized water again.</li>
		<li>Dry all surfaces of the sample under a flow of air.</li>
		<li>Store the sample in either a desiccator or vacuum desiccator until required. Ideally, finish preparing the carbon-steel substrate just prior to solution immersion.</li>
	</ol>
	</li>
	<li>Preparation of inhibited 1 M HCl solution
	<ol>
		<li>Add 10.2 M HCl to deionized water to produce a 1 M HCl solution. CAUTION: HCl is harmful and corrosive. Undertake this step in a fume hood, wearing suitable personal protection equipment.</li>
		<li>Dissolve x g of selected organic-CI (e.g. x = 0.300 g of 2-mercaptobenzimidazole) in 1 M HCl solution to produce a 1 M HCl solution containing x mM organic-CI (e.g. x = 2 mM 2-mercaptobenzimidazole).</li>
	</ol>
	</li>
</ol>
2. Substrate Immersion in Inhibited Acid Solution
<ol>
	<li>Pour a small volume (typically 25 - 50 mL) of the 1 M HCl + x mM (e.g. x = 2 mM 2-mercaptobenzimidazole) organic-CI solution into a small glass beaker.</li>
	<li>Pick up the disc-shaped carbon-steel sample with either ceramic or plastic tweezers that are resistant to 1 M HCl. Only touch the edge of the sample with the tweezers.</li>
	<li>Introduce the sample into the glass beaker containing the 1 M HCl + x mM organic-CI solution. Orient the sample so that cylindrical faces are in the vertical plane. Deposit the sample either directly onto the bottom of the beaker, or atop the open end of a short glass tube. Ensure that the sample is fully submerged.</li>
</ol>
3. Sample Transfer
<ol>
	<li>Glove box preparation
	<ol>
		<li>Locate the circular sample-transfer opening in the base of the glove box onto the XPS load-lock flange mounting. Ensure that the seal between glove box and load-lock flange is formed correctly.</li>
		<li>Connect the glove box to an inert gas cylinder (either N2 or Ar).</li>
		<li>Adhere a small square of double-sided carbon (conductive) tape onto the XPS sample bar.</li>
		<li>Insert hardware required for sample transfer into XPS instrument through an open port on the glove box, i.e. sample bar with carbon tape attached, plastic/ceramic tweezers, nitrile gloves, laboratory tissues, plastic paraffin film, empty/dry wash bottle with spout, and glass beaker containing ~ 200 g of Na2CO3 powder.</li>
		<li>Place glass beaker containing carbon-steel sample in 1 M HCl + x mM (e.g. x = 2 mM 2-mercaptobenzimidazole) organic-CI solution inside glove box. Ensure that sample is always fully immersed during this step.</li>
		<li>Seal all ports/entry points on the glove box and begin to purge with N2 (or Ar).</li>
		<li>Continuously purge the glove box until the sample transfer is complete.</li>
	</ol>
	</li>
	<li>From solution to XPS analysis chamber
	<ol>
		<li>Allow the sample to remain submerged in the 1 M HCl + x mM organic-CI solution for the desired immersion period, e.g. 4 h, as employed for the XPS data presented below.</li>
		<li>Check that the relative humidity within the glove box is minimized, which is typically achieved after 60 - 90 min of initiating purging. A value of 8% relative humidity is required before proceeding with sample transfer; value prior to purging is typically 35 - 40%. 
		NOTE: Normally, there is no dedicated O2 sensor within the glove box, but trial measurements with such a device indicate that the purging procedure leads to a reduction in O2 concentration by a factor of ~ 1,000.</li>
		<li>Introduce hands into glove box gloves, and then cover gloved hands with nitrile gloves located within the glove box. This step reduces the possibility of contamination during sample handling, as well as increases the ease of sample manipulation.</li>
		<li>Remove the carbon-steel sample from the 1 M HCl + x mM (e.g. x = 2 mM 2-mercaptobenzimidazole) organic-CI solution, using the ceramic/plastic tweezers. Only touch the edge of the sample with the tweezers.</li>
		<li>Immediately after emersion, blow the sample dry by directing a stream of inert gas, produced by repeatedly squeezing empty/dry wash bottle located inside glove box, onto sample surfaces. 
		NOTE: Rinsing with solvents at this stage is not undertaken to minimize the potential of damaging the inhibited interface, e.g. inhibitor removal or interface oxidation.</li>
		<li>Cover beaker containing 1 M HCl + x mM organic-CI solution with plastic paraffin film.</li>
		<li>Affix the sample to the small square of double-sided carbon (conductive) tape attached to XPS sample bar. Do not touch the surface to be probed by XPS.</li>
		<li>Vent the XPS load-lock chamber to N2/Ar. Ensure that the associated turbo/rotary pump combination is switched off before performing this action.</li>
		<li>Open the load lock flange.</li>
		<li>Transfer the sample bar into the load-lock chamber and slide it onto sample holding prong.</li>
		<li>Close the load-lock flange.</li>
		<li>Switch on turbo/rotary pump combination to pump down load-lock chamber.</li>
		<li>Once pressure in load-lock chamber reaches at least ~ 5 x 10-7 mbar, manually transfer sample to intermediate chamber using transfer arm.</li>
		<li>Wait until pressure in intermediate chamber reaches ~ 1 x 10-8 mbar, and then use second transfer arm to manually transfer sample onto the sample manipulator in the analysis chamber.</li>
	</ol>
	</li>
</ol>
4. Acquisition of XPS Data
<ol>
	<li>Orient angle of sample, using keypad to drive sample manipulator motors, to desired photoelectron emission angle, e.g. 0&#176; (emission along the surface normal), as employed for the XPS data presented below.</li>
	<li>Open XPS data acquisition software by clicking on the icon located on the desktop. Open Instrument Manual Control window.</li>
	<li>Input 10 mA and 15 kV as the values for the anode emission and anode HT parameters, respectively. Then, click the &#8220;ON&#8221; button in the &#8220;X-ray Gun&#8221; section to power up the monochromated Al K&#945; X-ray source. After this, click the &#8220;ON&#8221; button in the &#8220;Neutralizer&#8221; section to turn on the charge neutralizer.</li>
	<li>Select electron analyzer &#39;Spectrum/Hybrid&#39; measurement mode from the &#39;Mode&#39; and &#39;Lens&#39; drop down menus in the &#39;Analyzer&#39; section.</li>
	<li>Input desired kinetic/binding energy ranges, pass energy(ies), step size(s), and dwell time(s) into &#39;Acquisition/Scan Control&#39; section. Example input parameter values: 1,200 - 0 eV binding energy range, 80 eV pass energy, 0.5 eV step size, and 0.1 s dwell time to acquire overview spectra.</li>
	<li>Optimize sample position by adjusting position of sample manipulator, using keypad to drive sample manipulator motors, to maximize signal from selected core level, e.g. C 1s or Fe 2p.</li>
	<li>Acquire XPS spectra by initiating data collection in XPS data acquisition software.</li>
</ol>

<ol>
	<li>Sastri, V. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Corrosion Inhibitors: Principles and Applications. , (1998).</li><li>Lindsay, R., Lyon, S. B., Cottis, R. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Introduction+to+Control+of+Corrosion+by+Environmental+Control.">Introduction to Control of Corrosion by Environmental Control.</a> In: Shreir's Corrosion, Vol. 4, Management and Control of Corrosion. , 2891-2899 (2010).</li><li>Oguzie, E. E., Li, Y., Wang, S. G., Wang, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Understanding+corrosion+inhibition+mechanisms+-+Experimental+and+theoretical+approach.">Understanding corrosion inhibition mechanisms - Experimental and theoretical approach.</a> RSC Advances. 1 (5), 866-873 (2011).</li><li>Kokalj, A., Peljhan, S., Fin&#353;gar, M., Milo&#353;ev, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=What+determines+the+inhibition+effectiveness+of+ATA,+BTAH,+and+BTAOH+corrosion+inhibitors+on+copper?.">What determines the inhibition effectiveness of ATA, BTAH, and BTAOH corrosion inhibitors on copper?.</a> Journal of the American Chemical Society. 132 (46), 16657-16668 (2010).</li><li>Kokalj, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Formation+and+structure+of+inhibitive+molecular+film+of+imidazole+on+iron+surface.">Formation and structure of inhibitive molecular film of imidazole on iron surface.</a> Corrosion Science. 68, 195-203 (2013).</li><li>Briggs, D., Seah, M. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> Practical surface analysis: by auger and x-ray photo-electron spectroscopy. 1, (1996).</li><li>Fin&#353;gar, M., Jackson, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Application+of+corrosion+inhibitors+for+steels+in+acidic+media+for+the+oil+and+gas+industry:+A+review.">Application of corrosion inhibitors for steels in acidic media for the oil and gas industry: A review.</a> Corrosion Science. 86, 17-41 (2014).</li><li>Fin&#353;gar, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=2-Mercaptobenzimidazole+as+a+copper+corrosion+inhibitor:+Part+II.+Surface+analysis+using+X-ray+photoelectron+spectroscopy.">2-Mercaptobenzimidazole as a copper corrosion inhibitor: Part II. Surface analysis using X-ray photoelectron spectroscopy.</a> Corrosion Science. 72, 90-98 (2013).</li><li>Morales-Gil, P., Walczak, M. S., Cottis, R. A., Romero, J. M., Lindsay, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion+inhibitor+binding+in+an+acidic+medium:+Interaction+of+2-mercaptobenizmidazole+with+carbon-steel+in+hydrochloric+acid.">Corrosion inhibitor binding in an acidic medium: Interaction of 2-mercaptobenizmidazole with carbon-steel in hydrochloric acid.</a> Corrosion Science. 85, 109-114 (2014).</li><li>Olivares-Xometl, O., Likhanova, N. V., Mart&#237;nez-Palou, R., Dom&#237;nguez-Aguilar, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemistry+and+XPS+study+of+an+imidazoline+as+corrosion+inhibitor+of+mild+steel+in+an+acidic+environment.">Electrochemistry and XPS study of an imidazoline as corrosion inhibitor of mild steel in an acidic environment.</a> Materials and Corrosion. 60 (1), 14-21 (2009).</li><li>Flores, E. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Sodium+phthalamates+as+corrosion+inhibitors+for+carbon+steel+in+aqueous+hydrochloric+acid+solution.">Sodium phthalamates as corrosion inhibitors for carbon steel in aqueous hydrochloric acid solution.</a> Corrosion Science. 53 (12), 3899-3913 (2011).</li><li>Zarrok, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion+control+of+carbon+steel+in+phosphoric+acid+by+purpald+-+Weight+loss,+electrochemical+and+XPS+studies.">Corrosion control of carbon steel in phosphoric acid by purpald - Weight loss, electrochemical and XPS studies.</a> Corrosion Science. 64, 243-252 (2012).</li><li>Morales-Gil, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion+inhibition+of+carbon-steel+with+2-mercaptobenzimidazole+in+hydrochloric+acid.">Corrosion inhibition of carbon-steel with 2-mercaptobenzimidazole in hydrochloric acid.</a> Corrosion Science. 101, 47-55 (2015).</li><li>Popova, A., Christov, M., Raicheva, S., Sokolova, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adsorption+and+inhibitive+properties+of+benzimidazole+derivatives+in+acid+mild+steel+corrosion.">Adsorption and inhibitive properties of benzimidazole derivatives in acid mild steel corrosion.</a> Corrosion Science. 46 (6), 1333-1350 (2004).</li><li>Gupta, R. P., Sen, S. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Calculation+of+multiplet+structure+of+core+p+-vacancy+levels+II.">Calculation of multiplet structure of core p -vacancy levels II.</a> Physical Review B. 12 (1), 15-19 (1975).</li><li>Shirley, D. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-resolution+x-ray+photoemission+spectrum+of+the+valence+bands+of+gold.">High-resolution x-ray photoemission spectrum of the valence bands of gold.</a> Physical Review B. 5 (12), 4709-4714 (1972).</li><li>Al-Refaie, A. A., Walton, J., Cottis, R. A., Lindsay, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Photoelectron+spectroscopy+study+of+the+inhibition+of+mild+steel+corrosion+by+molybdate+and+nitrite+anions.">Photoelectron spectroscopy study of the inhibition of mild steel corrosion by molybdate and nitrite anions.</a> Corrosion Science. 52 (2), 422-428 (2010).</li><li>Liu, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+study+of+self-assembled+films+of+triazole+on+iron+electrodes+using+electrochemical+methods,+XPS,+SEM+and+molecular+simulation.">The study of self-assembled films of triazole on iron electrodes using electrochemical methods, XPS, SEM and molecular simulation.</a> Electrochemistry Communications. 9 (4), 813-819 (2007).</li><li>Zhang, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Corrosion+inhibition+of+mild+steel+in+hydrochloric+acid+solution+by+quaternary+ammonium+salt+derivatives+of+corn+stalk+polysaccharide+(QAPS).">Corrosion inhibition of mild steel in hydrochloric acid solution by quaternary ammonium salt derivatives of corn stalk polysaccharide (QAPS).</a> Desalination. 372, 57-66 (2015).</li></ol>

The authors declare that they have no competing financial interests.

XPS spectra displayed in Figures 1 and 2 clearly demonstrate that the inert atmosphere employed during sample transfer is essential to avoid post immersion oxidation of these carbon-steel/organic-CI interfaces. On this basis, results from other similar XPS studies (e.g. 18,19), which involved exposure of the inhibited substrate to the ambient laboratory atmosphere, should be critically re-evaluated, as the interface chemistry may have been modified through oxidation. It should be noted that that there is no reason to assume that all organic-CIs adsorb onto oxide/hydroxide free surfaces in acidic solution. In some cases, such phases may indeed facilitate the organic-CI surface binding. Distinguishing this scenario from post immersion oxidation is not so straightforward. One possible solution is to acquire XPS data from a reference inhibited interface (e.g. 1 M HCl + 2 mM MBI) in tandem with the sample of interest to check that post immersion oxidation is not an issue.
To ensure a successful outcome to the sample transfer procedure, it is essential that the glove box is fully purged with inert gas (N2/Ar) i.e. the O2 concentration in the glove box is minimized. Care should be taken to verify that all seals on the glove box ports/entry points are correctly formed, including the seal between the glove box and XPS load-lock flange. Ideally, an in situ sensor should be used to directly monitor the O2 concentration, although it is not essential, as demonstrated by our own work. As indicated in step 3.3.2, we normally use a relative humidity sensor as a guide for when to undertake a sample transfer.
One further potential issue with the glove box environment is the presence of volatile solution components, which can contaminate the sample surface following removal from solution and prior to insertion into the load-lock. For example, the presence of 1 M HCl solution in the glove box leads to evolution of HCl vapor, which can react with carbon-steel samples leading to adventitious Cl signal in the XPS data. To minimize the likelihood of such contamination being significant, small volumes of HCl solution should be employed and sample transfer should be completed as quickly as possible. On this basis, as indicated in the Protocol, typically only one beaker/sample is inserted into the glove box for sample transfer at any one time. In addition, one should minimize the surface area of the HCl solution, as well cover the beaker following sample emersion. Na2CO3 powder (step 3.1.4) is inserted into the glove box in an attempt to control the amount of HCl vapor. In addition, it can be used to clean up any acidic solution spillages.
Besides careful control of the glove box environment, sample handling is also critical to the integrity of acquired XPS spectra. One should not acquire XPS data from any surface that has come into contact with any solid object, e.g. tweezers or glove. Furthermore, upon removal of a sample from solution, it should be immediately blown dry with inert gas (step 3.2.5). This procedure is undertaken to prevent evaporation and subsequent physical deposition of solution components onto the sample surface, which may lead to misinterpretation of data. As an additional precaution, one can also consider replacing the nitrile gloves (step 3.2.3) with a fresh pair for transferring the sample bar to the load-lock chamber, i.e. prior to step 3.1.10.
Finally, given the effectiveness of the approach outlined here, we expect it to be applied to other topics in corrosion (i.e. in addition to corrosion inhibition), where acquisition of XPS data from air-sensitive interfaces would add to understanding. Moreover, such an approach should be considered in other fields where XPS measurements are undertaken from air-sensitive interfaces formed in a fluid environment. Clearly, this procedure is not restricted to XPS, but could also be applied to any other UHV-based measurement from a surface that has previously been immersed in a liquid, e.g. scanning probe microscopy.

Corrosion inhibitors (CIs) are substances that, when introduced into an aggressive environment, reduce the corrosion rate of a metallic material by inducing a change at the solid/liquid interface1,2,3,4,5. This approach to corrosion control is widely used in industry, with high performance CIs having been successfully developed for a variety of applications. There remains, however, a considerable lack of fundamental understanding of CI performance, hindering knowledge-based optimization. For example, the precise nature of interfaces formed by organic-CIs in corrosive acidic solutions is still unclear.
Given the assumption that organic-CIs inhibit acidic corrosion through formation of an adsorbed 2-D layer2, a surface sensitive technique is required to characterize these interfaces. Consequently, X-ray photoelectron spectroscopy (XPS)6 has emerged as a technique of choice to probe the elemental/chemical composition of these interfaces ex situ7,8,9; XPS measurements are typically performed in, or close to, ultra-high vacuum (UHV). Various insights have been claimed, including that a surface oxide or hydroxide is present to facilitate organic-CI binding to the metallic substrate10,11,12. The validity of this interface description, however, is questionable as the XPS data were acquired from samples that had been exposed to the laboratory atmosphere in between removal from inhibited solution and introduction into the UHV-XPS spectrometer. Such a procedure may result in interface oxidation, undermining conclusions about interface chemical composition. An alternative approach is required, which minimizes the potential for post immersion oxidation.
In this paper, we detail a methodology designed to allow one to acquire XPS data from organic-CI/metal interfaces that have not undergone oxidation following emersion from acidic solution. A glove box, purged with inert gas, which is attached directly to the vacuum load-lock of the UHV-XPS instrument is employed. The utility of our approach is verified through presentation of XPS data from two organic-CI/carbon-steel interfaces formed following addition of sufficient CI to significantly reduce the substrate corrosion rate in aqueous 1 M hydrochloric acid (HCl) solution.

<table><tbody><tr><td>Mild steel C1010</td><td>RCSL, BAC Corrosion Control Ltd.</td><td>n/a</td><td></td></tr><tr><td>Polycrystallline iron 99.99+%</td><td>Goodfellow Cambridge Ltd.</td><td>FE007948</td><td></td></tr><tr><td>Silicon Carbide Grinding papers</td><td>Spectrographic Limited</td><td>T13316, T13317, T13318, T13156, T13153</td><td></td></tr><tr><td>Polishing Cloth</td><td>Spectrographic Limited</td><td></td><td></td></tr><tr><td>Monocrystalline Diamond compound</td><td>Spectrographic Limited</td><td>G22003</td><td></td></tr><tr><td>OmegaPol TWIN 250 mm Metallurgical Polisher</td><td>Spectrographic Limited</td><td>n/a</td><td></td></tr><tr><td>BRILLANT 220 - Wet Abrasive Cut-Off Machine</td><td>ATM GmbH Advanced Materialography</td><td>n/a</td><td></td></tr><tr><td>Ultrasonic Bath</td><td>NICKEL-ELECTRO LTD.</td><td>SW3H</td><td></td></tr><tr><td>Heat gun, D100/200 Mfg</td><td>Mar Equipment Ltd</td><td>n/a</td><td></td></tr><tr><td>Vacuum Desiccator</td><td>DURAN</td><td>24 782 57</td><td></td></tr><tr><td>Low form beaker 25 mL</td><td>Fisher Scientific</td><td>FB33170</td><td></td></tr><tr><td>Regulator for N&lt;sub&gt;2&lt;/sub&gt; gas cylinders</td><td>Freshford Ltd.</td><td>MS-10B-N2</td><td></td></tr><tr><td>Nitrogen Purge Glove Box</td><td>Terra Universal, Inc</td><td>n/a</td><td></td></tr><tr><td>Dual Purge System</td><td>Terra Universal, Inc</td><td>1606-61</td><td></td></tr><tr><td>NitroWatch System with sensor</td><td>Terra Universal, Inc</td><td>9500-00A, 9500-02A</td><td></td></tr><tr><td>SEFRAM LOG 1620 Data Logger, 50000</td><td>SEFRAM</td><td>2475144 from Farnell Element14</td><td></td></tr><tr><td>Big Digit Hygro-Thermometer</td><td>FLIR Commercial Systems, Inc. Extech Instruments Division</td><td>445703</td><td></td></tr><tr><td>Kratos Axis Ultra</td><td>Kratos Analytical Ltd</td><td>n/a</td><td></td></tr></tbody></table>

determining the chemical composition of corrosion inhibitor/metal interfaces with xps: minimizing post immersion oxidation

An approach for acquiring more reliable X-ray photoelectron spectroscopy data from corrosion inhibitor/metal interfaces is described. More specifically, the focus is on metallic substrates immersed in acidic solutions containing organic corrosion inhibitors, as these systems can be particularly sensitive to oxidation following removal from solution. To minimize the likelihood of such degradation, samples are removed from solution within a glove box purged with inert gas, either N2 or Ar. The glove box is directly attached to the load-lock of the ultra-high vacuum X-ray photoelectron spectroscopy instrument, avoiding any exposure to the ambient laboratory atmosphere, and thus reducing the possibility of post immersion substrate oxidation. On this basis, one can be more certain that the X-ray photoelectron spectroscopy features observed are likely to be representative of the in situ submerged scenario, e.g. the oxidation state of the metal is not modified.

Figure 1 shows overview, O 1s, and Fe 2p XPS data acquired from carbon-steel samples that have been immersed for 4 h in one of two different 1 M HCl + x mM organic-CI solutions, and transferred for XPS measurement as detailed above. Analogous data from a polished sample are also displayed. The carbon-steel possessed a nominal weight% composition of C (0.08-0.13), Mn (0.30-0.50), P (0.04), S(0.05), and Fe (balance). The two organic-CIs studied are: 2-mercaptobenzimidazole (MBI) and (Z)-2-2(2-(octadec-9-en-1-yl)-4,5-dihydro-1H-imidazole-1-yl)ethanamine (OMID). At the concentrations employed (MBI: 2 mM; OMID: 1 mM) corrosion rate measurements13,14 indicate that all of the species significantly inhibit the corrosion of carbon-steel, i.e. inhibition efficiencies (η%)2&gt; 90%. Best fits to the O 1s and Fe 2p spectral profiles are also displayed. Photoelectron peaks were modeled with Gaussian-Lorentzian (GL) line shape functions (30 % Lorentzian), with the exception of the Fe 2p level of metallic iron, where a Lorentzian asymmetric line shape with tail damping (LF) was used. The cationic Fex+ states were modeled with multiplet envelopes consisting of 3 and 4 GL functions for Fe2+ and Fe3+, respectively15. A Shirley-type function16 was used to describe the background of inelastically scattered electrons.
Focusing on the overview XPS data (Figure 1 (a)), the spectrum acquired from the polished sample exhibits three prominent peaks, i.e. Fe 2p, O 1s, and C 1s. These features can be assigned as follows: Fe 2p arises from the carbon-steel, O 1s derives from both an surface oxidic film and adsorbates, and the C 1s signal is due to adventitious carbon. Submersion in any of the 1 M HCl + x mM organic-CI solutions results in significant changes to the corresponding overview spectrum. A feature assigned to the N 1s core level appears, which is consistent with surface adsorption of the inhibitors; MBI and OMID both contain N. Moreover, the O1s core level signal is significantly diminished.
As regards O 1s data from the polished substrate (Figure 1 (b)), the profile can be fitted with four components. The two components at lower binding energies (BE), ~ 530.0 eV and ~ 531.3 eV, can be assigned to iron oxide (O2-) and hydroxide (OH-) phases, respectively. The two higher binding energy components, labeled O1 (BE ~ 532.2 eV) and O2 (BE ~ 533.3 eV), are likely associated with adsorbed OH (O1) and adventitious carbon species (O1 and O2)17. Immersion in either of the 1 M HCl + x mM organic-CI solutions leads to the complete quenching of the O2- and OH- components. On this basis, it can be concluded that the corrosion inhibitors are adsorbed on oxide/hydroxide free surfaces. The Fe 2p spectra in Figure 1 (c) are consistent with this result, as only a metallic Fe (Fe0) peak is apparent on the inhibited substrates. Fe2+ and Fe3+ features are present on the polished sample, due to the surface oxide/hydroxide.
O 1s and Fe 2p core level XPS spectra from two carbon-steel samples immersed in 1 M HCl + 2 mM MBI are compared in Figure 2. One sample was transferred using a fully N2-purged glove box, whilst the other was removed from solution into a partially N2-purged glove box, i.e. O2 concentration was significantly higher than target value. For the latter sample, it is apparent that post immersion oxidation has occurred, i.e. Fe2+/3+ and O2-/OH- features are present.
<img alt="XPS spectra for Pol., MBI, OMID samples; Fe 2p, O 1s binding energies; analysis of oxidation states." src="/files/ftp_upload/55163/55163fig1.jpg" data-altupdatedat="1747911167000" data-alt="Figure 1"> 
Figure 1. XPS spectra from polished and inhibited carbon-steel samples. (a) Overview, (b) O 1s, and (c) Fe 2p XPS spectra. Data presented in each panel were acquired from carbon-steel samples that had been immersed for 4 h in one of two different 1 M HCl + x mM organic-CI solutions, i.e. 2 mM MBI, and 1 mM OMID. Spectra were all acquired at a photoelectron emission angle (θE) of 0° (emission along the surface normal). For (b) and (c) the best fits (light blue markers) to the experimental data (solid black lines) are also displayed, achieved with a combination of GL (broken red lines), LF (broken red lines), and Shirley-type (broken grey lines) functions. Peak labels are explained in the main text. <a href="http://cloudflare.jove.com/files/ftp_upload/55163/55163fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="XPS spectra of O 1s and Fe 2p, diagram showing N2-purged effects on oxidation states." src="/files/ftp_upload/55163/55163fig2.jpg" data-altupdatedat="1747911167000" data-alt="Figure 2"> 
Figure 2. Impact of post immersion oxidation on XPS spectra. (a) O 1s and (b) Fe 2p XPS spectra. Data were acquired from carbon steel samples that had been immersed in 1 M HCl + 2 mM MBI solutions (η% = 99%) for 4 h. Spectra were acquired at θE = 0°. In each panel, the lower (upper) spectrum is from a sample transferred through a fully (partially) N2-purged glove box. Peak labels are explained in the main text. (Modified version of Fig. 5 in Ref. 9.) <a href="http://cloudflare.jove.com/files/ftp_upload/55163/55163fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

Watch this Scientific Journal Video about Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation at JoVE.com

Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation

A protocol to avoid the oxidation of metallic substrates during sample transfer from an inhibited acidic solution to an X-ray photoelectron spectrometer is presented.

An approach for acquiring more reliable X-ray photoelectron spectroscopy data from corrosion inhibitor/metal interfaces is described. More specifically, ...

determining-chemical-composition-corrosion-inhibitormetal-interfaces

Research

JoVE Journal

Chemistry

15.7K Views.  The University of Manchester. A protocol to avoid the oxidation of metallic substrates during sample transfer from an inhibited acidic solution to an X-ray photoelectron spectrometer is presented. 

Video: Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation

Analysis of Volatile and Oxidation Sensitive Compounds Using a Cold Inlet System and Electron Impact Mass Spectrometry

This video presents a protocol for the mass spectrometrical analysis of volatile and oxidation sensitive compounds using electron impact ionization. The analysis of volatile and oxidation sensitive compounds by mass spectrometry is not easily achieved, as all state-of-the-art mass spectrometric methods require at least one sample preparation step, e.g., dissolution and dilution of the analyte (electrospray ionization), co-crystallization of the analyte with a matrix compound (matrix-assisted laser desorption/ionization), or transfer of the prepared samples into the ionization source of the mass spectrometer, to be conducted under atmospheric conditions. Here, the use of a sample inlet system is described which enables the analysis of volatile metal organyls, silanes, and phosphanes using a sector field mass spectrometer equipped with an electron impact ionization source. All sample preparation steps and the sample introduction into the ion source of the mass spectrometer take place either under air-free conditions or under vacuum, enabling the analysis of compounds highly susceptible to oxidation. The presented technique is especially of interest for inorganic chemists, working with metal organyls, silanes, or phosphanes, which have to be handled using inert conditions, such as the Schlenk technique. The principle of operation is presented in this video.

This video presents a protocol for the mass spectrometrical analysis of volatile and oxidation sensitive compounds using electron impact ionization. The presented technique is especially of interest for inorganic chemists, working with metal organyls, silanes, or phosphanes which have to be handled using inert conditions, such as the Schlenk technique.

This video presents a protocol for the mass spectrometrical analysis of volatile and oxidation sensitive compounds using electron impact ionization. The ...

Potentiodynamic Corrosion Testing

Different metallic materials have different polarization characteristics as dictated by the open circuit potential, breakdown potential, and passivation potential of the material. The detection of these electrochemical parameters identifies the corrosion factors of a material. A reliable and well-functioning corrosion system is required to achieve this.
Corrosion of the samples was achieved via a potentiodynamic polarization technique employing a three-electrode configuration, consisting of reference, counter, and working electrodes. Prior to commencement a baseline potential is obtained. Following the stabilization of the corrosion potential (Ecorr), the applied potential is ramped at a slow rate in the positive direction relative to the reference electrode. The working electrode was a stainless steel screw. The reference electrode was a standard Ag/AgCl. The counter electrode used was a platinum mesh. Having a reliable and well-functioning in vitro corrosion system to test biomaterials provides an in-expensive technique that allows for the systematic characterization of the material by determining the breakdown potential, to further understand the material's response to corrosion. The goal of the protocol is to set up and run an in vitro potentiodynamic corrosion system to analyze pitting corrosion for small metallic medical devices.

Here, we present a protocol to set up and run an in vitro potentiodynamic corrosion system to analyze pitting corrosion for small metallic medical devices.

Different metallic materials have different polarization characteristics as dictated by the open circuit potential, breakdown potential, and passivation ...

Environment

Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media

Material corrosion can be a limiting factor for different materials in many applications. Thus, it is necessary to better understand corrosion processes, prevent them and minimize the damages associated with them. One of the most important characteristics of corrosion processes is the corrosion rate. The measurement of corrosion rates is often very difficult or even impossible especially in less conductive, non-aqueous environments such as biofuels. Here, we present five different methods for the determination of corrosion rates and the efficiency of anti-corrosion protection in biofuels: (i) a static test, (ii) a dynamic test, (iii) a static test with a reflux cooler and electrochemical measurements (iv) in a two-electrode arrangement and (v) in a three-electrode arrangement. The static test is advantageous due to its low demands on material and instrumental equipment. The dynamic test allows for the testing of corrosion rates of metallic materials at more severe conditions. The static test with a reflux cooler allows for the testing in environments with higher viscosity (e.g., engine oils) at higher temperatures in the presence of oxidation or an inert atmosphere. The electrochemical measurements provide a more comprehensive view on corrosion processes. The presented cell geometries and arrangements (the two-electrode and three-electrode systems) make it possible to perform measurements in biofuel environments without base electrolytes that could have a negative impact on the results and load them with measurement errors. The presented methods make it possible to study the corrosion aggressiveness of an environment, the corrosion resistance of metallic materials, and the efficiency of corrosion inhibitors with representative and reproducible results. The results obtained using these methods can help to understand corrosion processes in more detail to minimize the damages caused by corrosion.

The testing of processes associated with material corrosion can often be difficult especially in non-aqueous environments. Here, we present different methods for short-term and long-term testing of corrosion behavior of non-aqueous environments such as biofuels, especially those containing bioethanol.

Material corrosion can be a limiting factor for different materials in many applications. Thus, it is necessary to better understand corrosion processes, ...

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight

Corrosion of metallic surfaces is prevalent in the environment and is of great concern in many areas, including the military, transport, aviation, building and food industries, amongst others. Polyester and coatings containing both polyester and silica nanoparticles (SiO2NPs) have been widely used to protect steel substrata from corrosion. In this study, we utilized X-ray photoelectron spectroscopy, attenuated total reflection infrared micro-spectroscopy, water contact angle measurements, optical profiling and atomic force microscopy to provide an insight into how exposure to sunlight can cause changes in the micro- and nanoscale integrity of the coatings. No significant change in surface micro-topography was detected using optical profilometry, however, statistically significant nanoscale changes to the surface were detected using atomic force microscopy. Analysis of the X-ray photoelectron spectroscopy and attenuated total reflection infrared micro-spectroscopy data revealed that degradation of the ester groups had occurred through exposure to ultraviolet light to form COO&#903;, -H2C&#903;, -O&#903;, -CO&#903; radicals. During the degradation process, CO and CO2 were also produced.

Two types of surfaces, polyester-coated steel and polyester coated with a layer of silica nanoparticles, were studied. Both surfaces were exposed to sunlight, which was found to cause substantial changes in the chemistry and nanoscale topography of the surface.

Corrosion of metallic surfaces is prevalent in the environment and is of great concern in many areas, including the military, transport, aviation, ...

Engineering

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys

The increasing complexity and severity of service conditions in areas, such as aerospace and marine industries, nuclear systems, microelectronics, batteries, and biomedical devices, etc., impose great challenges on the reliable performance of alloys exposed to extreme conditions where mechanical and electrochemical attack co-exist. Finding ways for alloys to mitigate the combined attack of wear and corrosion (i.e., tribocorrosion) under such extreme conditions is thus highly critical for improving their reliability and service lifetime when used in such conditions. The challenge lies in the fact that wear and corrosion are not independent of each other, but rather work synergistically to accelerate the total material loss. Thus, a reliable method to evaluate the tribocorrosion resistance of metals and alloys is needed. Here, a protocol for measuring the tribocorrosion rate and wear-corrosion synergy of Al-based bulk and thin film samples in a corrosive environment under room temperature is presented.

Here, we present a protocol to measure the tribocorrosion rate and wear-corrosion synergy of thin film and bulk Al alloys in simulated sea water at room temperature.

The increasing complexity and severity of service conditions in areas, such as aerospace and marine industries, nuclear systems, microelectronics, ...

A Continuous-flow Photocatalytic Reactor for the Precisely Controlled Deposition of Metallic Nanoparticles

In this work, a novel photocatalytic reactor for the pulsed and controlled excitation of the photocatalyst and the precise deposition of metallic nanoparticles is developed. Guidelines for the replication of the reactor and its operation are provided in detail. Three different composite systems (Pt/graphene, Pt/TiO2, and Au/TiO2) with monodisperse and uniformly distributed particles are produced by this reactor, and the photodeposition mechanism, as well as the synthesis optimization strategy, are discussed. The synthesis methods and their technical aspects are described comprehensively. The role of the ultraviolet (UV) dose (in each excitation pulse) on the photodeposition process is investigated and the optimum values for each composite system are provided.

For a continuous and scalable synthesis of noble-metal-based nanocomposites, a novel photocatalytic reactor is developed and its structure, operation principles, and product quality optimization strategies are described.

In this work, a novel photocatalytic reactor for the pulsed and controlled excitation of the photocatalyst and the precise deposition of metallic ...

Imaging Corrosion at the Metal-Paint Interface Using Time-of-Flight Secondary Ion Mass Spectrometry

Corrosion developed at the paint and aluminum (Al) metal-paint interface of an aluminum alloy is analyzed using time-of-flight secondary ion mass spectrometry (ToF-SIMS), illustrating that SIMS is a suitable technique to study the chemical distribution at a metal-paint interface. The painted Al alloy coupons are immersed in a salt solution or exposed to air only. SIMS provides chemical mapping and 2D molecular imaging of the interface, allowing direct visualization of the morphology of the corrosion products formed at the metal-paint interface and mapping of the chemical after corrosion occurs. The experimental procedure of this method is presented to provide technical details to facilitate similar research and highlight pitfalls that may be encountered during such experiments.

Time-of-flight secondary ion mass spectrometry is applied to demonstrate the chemical mapping and corrosion morphology at the metal-paint interface of an aluminum alloy after being exposed to a salt solution compared with a specimen exposed to air.

Corrosion developed at the paint and aluminum (Al) metal-paint interface of an aluminum alloy is analyzed using time-of-flight secondary ion mass ...

Nanoscale Characterization of Liquid-Solid Interfaces by Coupling Cryo-Focused Ion Beam Milling with Scanning Electron Microscopy and Spectroscopy

Physical and chemical processes at solid-liquid interfaces play a crucial role in many natural and technological phenomena, including catalysis, solar energy and fuel generation, and electrochemical energy storage. Nanoscale characterization of such interfaces has recently been achieved using cryogenic electron microscopy, thereby providing a new path to advancing our fundamental understanding of interface processes.
This contribution provides a practical guide to mapping the structure and chemistry of solid-liquid interfaces in materials and devices using an integrated cryogenic electron microscopy approach. In this approach, we pair cryogenic sample preparation which allows stabilization of solid-liquid interfaces with cryogenic focused ion beam (cryo-FIB) milling to create cross-sections through these complex buried structures. Cryogenic scanning electron microscopy (cryo-SEM) techniques performed in a dual-beam FIB/SEM enable direct imaging as well as chemical mapping at the nanoscale. We discuss practical challenges, strategies to overcome them, as well as protocols for obtaining optimal results. While we focus in our discussion on interfaces in energy storage devices, the methods outlined are broadly applicable to a range of fields where solid-liquid interface play a key role.

Cryogenic Focused Ion Beam (FIB) and Scanning Electron Microscopy (SEM) techniques can provide key insights into the chemistry and morphology of intact solid-liquid interfaces. Methods for preparing high quality Energy Dispersive X-ray (EDX) spectroscopic maps of such interfaces are detailed, with a focus on energy storage devices.

Physical and chemical processes at solid-liquid interfaces play a crucial role in many natural and technological phenomena, including catalysis, solar ...

Preparation of Nanoparticles for ToF-SIMS and XPS Analysis

Nanoparticles have gained increasing attention in recent years due to their potential and application in different fields including medicine, cosmetics, chemistry, and their potential to enable advanced materials. To effectively understand and regulate the physico-chemical properties and potential adverse effects of nanoparticles, validated measurement procedures for the various properties of nanoparticles need to be developed. While procedures for measuring nanoparticle size and size distribution are already established, standardized methods for analysis of their surface chemistry are not yet in place, although the influence of the surface chemistry on nanoparticle properties is undisputed. In particular, storage and preparation of nanoparticles for surface analysis strongly influences the analytical results from various methods, and in order to obtain consistent results, sample preparation must be both optimized and standardized. In this contribution, we present, in detail, some standard procedures for preparing nanoparticles for surface analytics. In principle, nanoparticles can be deposited on a suitable substrate from suspension or as a powder. Silicon (Si) wafers are commonly used as substrate, however, their cleaning is critical to the process. For sample preparation from suspension, we will discuss drop-casting and spin-coating, where not only the cleanliness of the substrate and purity of the suspension but also its concentration play important roles for the success of the preparation methodology. For nanoparticles with sensitive ligand shells or coatings, deposition as powders is more suitable, although this method requires particular care in fixing the sample.

A number of different procedures for preparing nanoparticles for surface analysis are presented (drop casting, spin coating, deposition from powders, and cryofixation). We discuss the challenges, opportunities, and possible applications of each method, particularly regarding the changes in the surface properties caused by the different preparation methods.

Nanoparticles have gained increasing attention in recent years due to their potential and application in different fields including medicine, cosmetics, ...

Co-localizing Kelvin Probe Force Microscopy with Other Microscopies and Spectroscopies: Selected Applications in Corrosion Characterization of Alloys

Kelvin probe force microscopy (KPFM), sometimes referred to as surface potential microscopy, is the nanoscale version of the venerable scanning Kelvin probe, both of which measure the Volta potential difference (VPD) between an oscillating probe tip and a sample surface by applying a nulling voltage equal in magnitude but opposite in sign to the tip-sample potential difference. By scanning a conductive KPFM probe over a sample surface, nanoscale variations in surface topography and potential can be mapped, identifying likely anodic and cathodic regions, as well as quantifying the inherent material driving force for galvanic corrosion.
Subsequent co-localization of KPFM Volta potential maps with advanced scanning electron microscopy (SEM) techniques, including back scattered electron (BSE) images, energy dispersive spectroscopy (EDS) elemental composition maps, and electron backscattered diffraction (EBSD) inverse pole figures can provide further insight into structure-property-performance relationships. Here, the results of several studies co-localizing KPFM with SEM on a wide variety of alloys of technological interest are presented, demonstrating the utility of combining these techniques at the nanoscale to elucidate corrosion initiation and propagation.
Important points to consider and potential pitfalls to avoid in such investigations are also highlighted: in particular, probe calibration and the potential confounding effects on the measured VPDs of the testing environment and sample surface, including ambient humidity (i.e., adsorbed water), surface reactions/oxidation, and polishing debris or other contaminants. Additionally, an example is provided of co-localizing a third technique, scanning confocal Raman microscopy, to demonstrate the general applicability and utility of the co-localization method to provide further structural insight beyond that afforded by electron microscopy-based techniques.

Kelvin probe force microscopy (KPFM) measures surface topography and differences in surface potential, while scanning electron microscopy (SEM) and associated spectroscopies can elucidate surface morphology, composition, crystallinity, and crystallographic orientation. Accordingly, the co-localization of SEM with KPFM can provide insight into the effects of nanoscale composition and surface structure on corrosion.

Kelvin probe force microscopy (KPFM), sometimes referred to as surface potential microscopy, is the nanoscale version of the venerable scanning Kelvin ...

Determining the Chemical Composition of Corrosion Inhibitor/Metal Interfaces with XPS: Minimizing Post Immersion Oxidation