This work was sponsored by the Army Research Laboratory and was accomplished under USARL Cooperative Agreement Number W911NF&#8208;17&#8208;2&#8208;0057 awarded to G.T.F. The views and conclusions contained in this document are those of the authors and should not be interpreted as representing official policies, either expressed or implied, of the Army Research Laboratory or the U.S. Government. The U.S. Government is authorized to reproduce and distribute reprints for Government purposes notwithstanding any copyright notation herein.

1. Allocation of Au nanorods
NOTE: Cetyltrimethylammonium bromide (CTAB)-covered AuNR may be synthesized by wet-chemistry (step 1.1) or purchased commercially (step 1.2) according to the reader&#8217;s preference, with each yielding similar results. Results in this work were based on commercially-sourced, AuNR with penta-twinned crystal structure. Impact of AuNR seed crystal structure (i.e., monocrystalline vs. penta-twinned) on ultimate morphology of the secondary metal shell remains unclear within the scope of plasmonic photodeposition, but has been of keen interest in both wet-14,15 and similar photo-chemical12 syntheses. Alternative surfactants to CTAB may be employed so long as Zeta-potential is positive, although final Pd morphology could change.
<ol>
	<li>Synthesis Techniques: Synthesize aqueously-dispersed AuNR at 0.5 mM Au using the silver-assisted method by Nikoobakht et al.16,17 (yielding monocrystalline structure) or the surfactant-assisted method by Murphy et al.18,19 (yielding penta-twinned crystal structure). Wash the AuNR via centrifugation20,21 to remove excess, free CTAB to a final concentration of 1-10 mM.</li>
	<li>Commercial Sources: Purchase aqueous AuNR dispersions at 0.5 mM Au with the following specifications: 40 nm diameter, 808 nm LSPR, and CTAB ligand (5 mM concentration) in DI water. Wash the AuNR via centrifugation20,21 to remove excess, free CTAB if the CTAB concentration exceeds 1-10 mM upon receipt. 
	NOTE: Aqueous AuNR dispersions with CTAB surfactant at a variety of sizes, aspect ratios, and particle number densities may be purchased from many commercial vendors and used successfully in this protocol.</li>
</ol>
2. Plasmonic photodeposition of Pd onto Au nanorods
<ol>
	<li>Preparation of Pd precursor
	<ol>
		<li>Prepare a 20 mM HCl solution. First, make 0.1 M HCl by diluting 830 &#956;L of stock concentrated HCl (37%, 12 M) with water to 100 mL. Second, make 0.02 M HCl by diluting 4 mL of 0.1 M HCl with water to 20 mL.</li>
		<li>Pipette 10 mL of 20 mM HCl into appropriate glassware and place in a bath sonicator (no sonication) with water temperature set to 60 &#176;C.</li>
		<li>Add 0.0177 g of PdCl2 into the 10 mL of 20 mM HCl and mix via sonication until all PdCl2 is dissolved. The resultant 10 mM H2PdCl4 solution should exhibit a dark orange color.</li>
	</ol>
	</li>
	<li>Preparation of photodeposition reaction mixture 
	NOTE: The procedure described assumes a 3 mL total volume for use in a cuvette to allow real-time feedback into plasmonic photodeposition process. The cited masses/volumes were selected for compatibility with typical chemicals/materials/reagents while allowing facile washing/recovery of the Pd-decorated AuNR. It is anticipated that similar results may be achieved if scaled to other volumes and/or alternative reaction vessels are used (e.g., glass beaker).
	<ol>
		<li>Degas stock AuNR solution and methanol (MeOH) in a bath sonicator for 30 min.</li>
		<li>Pipette 2.5 mL of aqueously-suspended AuNR (from step 2.2.1) into a 1 cm path length, macrovolume cuvette with a magnetic stir bar. Place the cuvette on a stir plate. 
		NOTE: Typical volume of a macrovolume cuvette is 3.5 mL. Quartz may be substituted with UV-transparent plastics.</li>
		<li>Pipette 475 &#956;L of degassed MeOH (from step 2.2.1) into the cuvette while gently stirring for approximately 15-30 min. Periodically remove any bubbles by gently tapping the bottom of the cuvette against a rigid surface as needed; removing solvated gasses can prolong the stability of the metal halide salt.</li>
		<li>Pipette 5 &#956;L of stock concentrated HCl (37%, 12 M) into the cuvette and let mix for 15 min. 
		NOTE: Tuning concentration of HCl support could influence final morphology/rate of Pd deposition, but concentrations less than 20 mM in the reaction mixture will allow H2PdCl4 to progressively hydrolyze and oxolate, leading to eventual PdOx formation after ~3 h.</li>
	</ol>
	</li>
	<li>Plasmonic photoreduction of [PdCl4]2- onto AuNR1,13
	<ol>
		<li>Inject 25 &#956;L of 10 mM H2PdCl4 into the reaction mixture for a 1:5 Pd:Au atomic ratio. Let the solution complex in dark for 1 h while stirring. 
		NOTE: This quantity may be adjusted according the desired Pd:Au ratio as the expense of altering the final molarities of Au, [PdCl4]2-, HCl, and MeOH of the reaction mixture. Reference22 illustrates example Pt-AuNR morphologies at different Pt:Au ratios- similar results can be expected with Pd.</li>
		<li>Irradiate the reaction mixture with an un-polarized, 715 nm long-pass filtered tungsten-halogen lamp at 35 mW/cm2 intensity for 24 h. 
		NOTE: Different light filters (or sources, e.g., laser) may be chosen according to unique LSPR wavelength for different Au nanostructure seeds. For example, a 420 nm long-pass filter may be used for plasmonic seed structures exhibiting LSPR at 450 nm. Light intensity may be decreased with neutral density filtration at the expense of a slower [PdCl4]2- reduction rate, leading to a longer total reaction time. Light intensity may be increased to reduce reaction time at the expense of potential for thermal reduction of [PdCl4]2- (onset is ~360 &#176;C via Reference23). An appropriate intensity can be calculated a priori to mitigate thermal reduction via calculation of nanoparticle surface temperature in isolation and/or collective ensembles24. Effects on ultimate Pd-AuNR morphology from varying irradiation intensity have not been explored.</li>
		<li>Wash the residual chemicals/reagents from the Pd-AuNR two times, each by: centrifugation at 9,000 x g, removing the supernatant with a pipette, re-suspending the Pd-AuNR pellet in water, and immersing the vial into a bath sonicator for 1-2 min to disperse20,21.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Forcherio, G. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Targeted+deposition+of+platinum+onto+gold+nanorods+by+plasmonic+hot+electrons.">Targeted deposition of platinum onto gold nanorods by plasmonic hot electrons.</a> Journal of Physical Chemistry C. 122 (50), 28901-28909 (2018).</li><li>Langille, M. R., Personick, M. L., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmon-Mediated+Syntheses+of+Metallic+Nanostructures.">Plasmon-Mediated Syntheses of Metallic Nanostructures.</a> Angewandte Chemie International Edition. 52 (52), 13910-13940 (2013).</li><li>Qiu, J., Wei, W. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+Plasmon-Mediated+Photothermal+Chemistry.">Surface Plasmon-Mediated Photothermal Chemistry.</a> The Journal of Physical Chemistry C. 118 (36), 20735-20749 (2014).</li><li>Zhang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface-Plasmon-Driven+Hot+Electron+Photochemistry.">Surface-Plasmon-Driven Hot Electron Photochemistry.</a> Chemical Reviews. 118 (6), 2927-2954 (2018).</li><li>Qiu, J., Wu, Y. C., Wang, Y. C., Engelhard, M. H., McElwee-White, L., Wei, W. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+Plasmon+Mediated+Chemical+Solution+Deposition+of+Gold+Nanoparticles+on+a+Nanostructured+Silver+Surface+at+Room+Temperature.">Surface Plasmon Mediated Chemical Solution Deposition of Gold Nanoparticles on a Nanostructured Silver Surface at Room Temperature.</a> Journal of the American Chemical Society. 135 (1), 38-41 (2013).</li><li>Qiu, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+Plasmon-Mediated+Chemical+Solution+Deposition+of+Cu+Nanoparticle+Films.">Surface Plasmon-Mediated Chemical Solution Deposition of Cu Nanoparticle Films.</a> The Journal of Physical Chemistry C. 120 (37), 20775-20780 (2016).</li><li>Boyd, D. A., Greengard, L., Brongersma, M., El-Naggar, M. Y., Goodwin, D. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmon-Assisted+Chemical+Vapor+Deposition.">Plasmon-Assisted Chemical Vapor Deposition.</a> Nano Letters. 6 (11), 2592-2597 (2006).</li><li>Di Martino, G., Michaelis, F. B., Salmon, A. R., Hofmann, S., Baumberg, J. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlling+Nanowire+Growth+by+Light.">Controlling Nanowire Growth by Light.</a> Nano Letters. 15 (11), 7452-7457 (2015).</li><li>Di Martino, G., Turek, V. A., Braeuninger-Weimer, P., Hofmann, S., Baumberg, J. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Laser-induced+reduction+and+in-situ+optical+spectroscopy+of+individual+plasmonic+copper+nanoparticles+for+catalytic+reactions.">Laser-induced reduction and in-situ optical spectroscopy of individual plasmonic copper nanoparticles for catalytic reactions.</a> Applied Physics Letters. 110 (7), 071111 (2017).</li><li>Xue, C., Millstone, J. E., Li, S., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmon-Driven+Synthesis+of+Triangular+Core&#8211;Shell+Nanoprisms+from+Gold+Seeds.">Plasmon-Driven Synthesis of Triangular Core&#8211;Shell Nanoprisms from Gold Seeds.</a> Angewandte Chemie International Edition. 46 (44), 8436-8439 (2007).</li><li>Langille, M. R., Zhang, J., Mirkin, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmon-Mediated+Synthesis+of+Heterometallic+Nanorods+and+Icosahedra.">Plasmon-Mediated Synthesis of Heterometallic Nanorods and Icosahedra.</a> Angewandte Chemie International Edition. 50 (15), 3543-3547 (2011).</li><li>Zhai, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Polyvinylpyrrolidone-induced+anisotropic+growth+of+gold+nanoprisms+in+plasmon-driven+synthesis.">Polyvinylpyrrolidone-induced anisotropic growth of gold nanoprisms in plasmon-driven synthesis.</a> Nature Materials. 15 (8), 889-895 (2016).</li><li>Forcherio, G. T., Baker, D. R., Boltersdorf, J., McClure, J. P., Leff, A. C., Lundgren, C. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Directed+assembly+of+bimetallic+nanoarchitectures+by+interfacial+photocatalysis+with+plasmonic+hot+electrons.">Directed assembly of bimetallic nanoarchitectures by interfacial photocatalysis with plasmonic hot electrons.</a> Nanophotonic Materials XV. 10720, 107200K (2018).</li><li>Tebbe, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Silver-Overgrowth-Induced+Changes+in+Intrinsic+Optical+Properties+of+Gold+Nanorods:+From+Noninvasive+Monitoring+of+Growth+Kinetics+to+Tailoring+Internal+Mirror+Charges.">Silver-Overgrowth-Induced Changes in Intrinsic Optical Properties of Gold Nanorods: From Noninvasive Monitoring of Growth Kinetics to Tailoring Internal Mirror Charges.</a> The Journal of Physical Chemistry C. 119 (17), 9513-9523 (2015).</li><li>Mayer, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlled+Living+Nanowire+Growth:+Precise+Control+over+the+Morphology+and+Optical+Properties+of+AgAuAg+Bimetallic+Nanowires.">Controlled Living Nanowire Growth: Precise Control over the Morphology and Optical Properties of AgAuAg Bimetallic Nanowires.</a> Nano Letters. 15 (8), 5427-5437 (2015).</li><li>Nikoobakht, B., El-Sayed, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+and+Growth+Mechanism+of+Gold+Nanorods+(NRs)+Using+Seed-Mediated+Growth+Method.">Preparation and Growth Mechanism of Gold Nanorods (NRs) Using Seed-Mediated Growth Method.</a> Chemistry of Materials. 15 (10), 1957-1962 (2003).</li><li>Burrows, N. D., Harvey, S., Idesis, F. A., Murphy, C. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Understanding+the+Seed-Mediated+Growth+of+Gold+Nanorods+through+a+Fractional+Factorial+Design+of+Experiments.">Understanding the Seed-Mediated Growth of Gold Nanorods through a Fractional Factorial Design of Experiments.</a> Langmuir. 33 (8), 1891-1907 (2017).</li><li>Jana, N. R., Gearheart, L., Murphy, C. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Seed-Mediated+Growth+Approach+for+Shape-Controlled+Synthesis+of+Spheroidal+and+Rod-like+Gold+Nanoparticles+Using+a+Surfactant+Template.">Seed-Mediated Growth Approach for Shape-Controlled Synthesis of Spheroidal and Rod-like Gold Nanoparticles Using a Surfactant Template.</a> Advanced Materials. 13, 1389-1393 (2001).</li><li>Kumar, D., Lee, A. R., Kaur, S., Lim, D. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Visible-light+Induced+Reduction+of+Graphene+Oxide+Using+Plasmonic+Nanoparticle.">Visible-light Induced Reduction of Graphene Oxide Using Plasmonic Nanoparticle.</a> Journal of Visualized Experiments. 103, e53108 (2015).</li><li>Paviolo, C., McArthur, S. L., Stoddart, P. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+Nanorod-assisted+Optical+Stimulation+of+Neuronal+Cells.">Gold Nanorod-assisted Optical Stimulation of Neuronal Cells.</a> Journal of Visualized Experiments. (98), e52566 (2015).</li><li>Hoang, T. B., Huang, J., Mikkelsen, M. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Colloidal+Synthesis+of+Nanopatch+Antennas+for+Applications+in+Plasmonics+and+Nanophotonics.">Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics.</a> Journal of Visualized Experiments. (111), e53876 (2016).</li><li>Ortiz, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Harnessing+Hot+Electrons+from+Near+IR+Light+for+Hydrogen+Production+Using+Pt-End-Capped-AuNRs.">Harnessing Hot Electrons from Near IR Light for Hydrogen Production Using Pt-End-Capped-AuNRs.</a> ACS Applied Materials &amp; Interfaces. 9 (31), 25962-25969 (2017).</li><li>Schiavo, L., Aversa, L., Tatti, R., Verucchi, R., Carotenuto, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structural+Characterizations+of+Palladium+Clusters+Prepared+by+Polyol+Reduction+of+[PdCl4]2&#8722;+Ions.">Structural Characterizations of Palladium Clusters Prepared by Polyol Reduction of [PdCl4]2&#8722; Ions.</a> Journal of Analytical Methods in Chemistry. 2016, 9073594 (2016).</li><li>Baffou, G., Quidant, R., Garc&#237;a de Abajo, F. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanoscale+Control+of+Optical+Heating+in+Complex+Plasmonic+Systems.">Nanoscale Control of Optical Heating in Complex Plasmonic Systems.</a> ACS Nano. 4 (2), 709-716 (2010).</li><li>Mulvaney, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+Plasmon+Spectroscopy+of+Nanosized+Metal+Particles.">Surface Plasmon Spectroscopy of Nanosized Metal Particles.</a> Langmuir. 12 (3), 788-800 (1996).</li><li>Elding, L. I., Olsson, L. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electronic+absorption+spectra+of+square-planar+chloro-aqua+and+bromo-aqua+complexes+of+palladium(II)+and+platinum(II).">Electronic absorption spectra of square-planar chloro-aqua and bromo-aqua complexes of palladium(II) and platinum(II).</a> The Journal of Physical Chemistry. 82 (1), 69-74 (1978).</li><li>Swihart, D. L., Mason, W. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electronic+spectra+of+octahedral+platinum+(IV)+complexes.">Electronic spectra of octahedral platinum (IV) complexes.</a> Inorganic Chemistry. 9 (7), 1749-1757 (1970).</li><li>Forcherio, G. T., Dunklin, J. R., Backes, C., Vaynzof, Y., Benamara, M., Roper, D. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+nanoparticles+physicochemically+bonded+onto+tungsten+disulfide+nanosheet+edges+exhibit+augmented+plasmon+damping.">Gold nanoparticles physicochemically bonded onto tungsten disulfide nanosheet edges exhibit augmented plasmon damping.</a> AIP Advances. 7 (7), 075103 (2017).</li><li>Boltersdorf, J., Forcherio, G. T., McClure, J. P., Baker, D. R., Leff, A. C., Lundgren, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Visible+Light-Promoted+Plasmon+Resonance+to+Induce+&#8220;Hot&#8221;+Hole+Transfer+and+Photothermal+Conversion+for+Catalytic+Oxidation.">Visible Light-Promoted Plasmon Resonance to Induce &#8220;Hot&#8221; Hole Transfer and Photothermal Conversion for Catalytic Oxidation.</a> The Journal of Physical Chemistry C. 122 (50), 28934-28948 (2018).</li><li>da Silva, J. A., Meneghetti, R. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=New+Aspects+of+the+Gold+Nanorod+Formation+Mechanism+via+Seed-Mediated+Methods+Revealed+by+Molecular+Dynamics+Simulations.">New Aspects of the Gold Nanorod Formation Mechanism via Seed-Mediated Methods Revealed by Molecular Dynamics Simulations.</a> Langmuir. 34 (1), 366-375 (2018).</li><li>Teranishi, T., Miyake, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Size+Control+of+Palladium+Nanoparticles+and+Their+Crystal+Structures.">Size Control of Palladium Nanoparticles and Their Crystal Structures.</a> Chemistry of Materials. 10 (2), 594-600 (1998).</li><li>Straney, P. J., Marbella, L. E., Andolina, C. M., Nuhfer, N. T., Millstone, J. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Decoupling+Mechanisms+of+Platinum+Deposition+on+Colloidal+Gold+Nanoparticle+Substrates.">Decoupling Mechanisms of Platinum Deposition on Colloidal Gold Nanoparticle Substrates.</a> Journal of the American Chemical Society. 136 (22), 7873-7876 (2014).</li><li>Cheng, N., Lv, H., Wang, W., Mu, S., Pan, M., Marken, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=An+ambient+aqueous+synthesis+for+highly+dispersed+and+active+Pd/C+catalyst+for+formic+acid+electro-oxidation.">An ambient aqueous synthesis for highly dispersed and active Pd/C catalyst for formic acid electro-oxidation.</a> Journal of Power Sources. 195 (21), 7246-7249 (2010).</li><li>Grzelczak, M., Perez-Juste, J., Garcia de Abajo, F. J., Liz-Marzan, L. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Optical+Properties+of+Platinum-Coated+Gold+Nanorods.">Optical Properties of Platinum-Coated Gold Nanorods.</a> The Journal of Physical Chemistry C. 111 (17), 6183-6188 (2007).</li><li>Zheng, Z., Tachikawa, T., Majima, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Single-Particle+Study+of+Pt-Modified+Au+Nanorods+for+Plasmon-Enhanced+Hydrogen+Generation+in+Visible+to+Near-Infrared+Region.">Single-Particle Study of Pt-Modified Au Nanorods for Plasmon-Enhanced Hydrogen Generation in Visible to Near-Infrared Region.</a> Journal of the American Chemical Society. 136 (19), 6870-6873 (2014).</li><li>Zheng, Z., Tachikawa, T., Majima, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Plasmon-Enhanced+Formic+Acid+Dehydrogenation+Using+Anisotropic+Pd&#8211;Au+Nanorods+Studied+at+the+Single-Particle+Level.">Plasmon-Enhanced Formic Acid Dehydrogenation Using Anisotropic Pd&#8211;Au Nanorods Studied at the Single-Particle Level.</a> Journal of the American Chemical Society. 137 (2), 948-957 (2015).</li><li>Grzelczak, M., P&#233;rez-Juste, J., Rodr&#237;guez-Gonz&#225;lez, B., Liz-Marz&#225;n, L. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+silver+ions+on+the+growth+mode+of+platinum+on+gold+nanorods.">Influence of silver ions on the growth mode of platinum on gold nanorods.</a> Journal of Materials Chemistry. 16 (40), 3946-3951 (2006).</li><li>Joplin, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Correlated+Absorption+and+Scattering+Spectroscopy+of+Individual+Platinum-Decorated+Gold+Nanorods+Reveals+Strong+Excitation+Enhancement+in+the+Nonplasmonic+Metal.">Correlated Absorption and Scattering Spectroscopy of Individual Platinum-Decorated Gold Nanorods Reveals Strong Excitation Enhancement in the Nonplasmonic Metal.</a> ACS Nano. 11 (12), 12346-12357 (2017).</li><li>Sutter, P., Li, Y., Argyropoulos, C., Sutter, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+Situ+Electron+Microscopy+of+Plasmon-Mediated+Nanocrystal+Synthesis.">In Situ Electron Microscopy of Plasmon-Mediated Nanocrystal Synthesis.</a> Journal of the American Chemical Society. 139 (19), 6771-6776 (2017).</li></ol>

The authors have nothing to disclose.

Monitoring changes in optical absorbance using transmission UV-vis spectroscopy is useful to assess status of the photocatalytic reaction, with particular attention to the LMCT features of H2PdCl4. Wavelength maxima of LMCT features after injection of H2PdCl4 at step 2.3.1 (going from solid black to solid blue in Figure 1) provide insights into the local &#8220;environment&#8221; of the [PdCl4]2- molecules1</...

Guiding metal deposition onto plasmonic substrates via plasmonic hot carriers generated from a resonant external field could support 2-step formation of heterometallic, anisotropic nanostructures at ambient conditions with new degrees-of-freedom1,2,3. Conventional redox chemistry, vapor deposition, and/or electrodeposition approaches are ill-suited for high-volume processing. This is primarily due to excess/sacrificial reagent waste, low throughput 5+ step lithography processes, and energy intensive environments (0.01-10 Torr and/or 400-1000 &#176;C temperatures) with little or no direct control over resultant material characteristics. Immersion of a plasmonic substrate (e.g., Au nanoparticle/seed) into a precursor environment (e.g., aqueous Pd salt solution) under illumination at the localized surface plasmon resonance (SPR) initiates externally-tunable (i.e., field polarization and intensity) photochemical deposition of the precursor via plasmonic hot electrons and/or photothermal gradients3,4. For example, protocol parameters/requirements for plasmonically-driven photothermal decomposition of Au, Cu, Pb, and Ti organometallics and Ge hydrides onto nanostructured Ag and Au substrates have been detailed5,6,7,8,9. However, utilization of femtosecond plasmonic hot electrons to directly photoreduce metal salts at a metal-solution interface remains largely undeveloped, absent processes employing citrate or poly(vinylpyrrolidone) ligands acting as intermediary charge relays to direct nucleation/growth of the secondary metal2,10,11,12. Anisotropic Pt-decoration of Au nanorods (AuNR) under longitudinal SPR (LSPR) excitation was recently reported1,13 where the Pt distribution coincided with the dipole polarity (i.e., the assumed spatial distribution of hot carriers).
The protocol herein expands upon recent Pt-AuNR work to include Pd and highlights key synthesis metrics that can be observed in real-time, showing the reductive plasmonic photodeposition technique is applicable toward other metal halide salts (Ag, Ni, Ir, etc.).

<table><tbody><tr><td>Aspheric Condenser Lens w/ Diffuser</td><td>Thorlabs</td><td>ACL5040U-DG15</td><td>f=40 mm, NA=0.60, 1500 grit, uncoated</td></tr><tr><td>Deuterium + Tungsten-Halogen Lightsource</td><td>StellarNet</td><td>SL5</td><td></td></tr><tr><td>Gold Nanorods, AuNR</td><td>NanoPartz</td><td>A12-40-808-CTAB</td><td>CTAB surfactant, 808 nm LSPR, 40 nm diameter</td></tr><tr><td>Ground Glass Diffuser</td><td>Thorlabs</td><td>DG20-1500</td><td>1500 grit, N-BK7</td></tr><tr><td>Hydrochloric acid, HCl</td><td>J.T. Baker</td><td>9539-03</td><td>concentrated, 37%</td></tr><tr><td>Low Profile Magnetic Stirrer</td><td>VWR</td><td>10153-690</td><td></td></tr><tr><td>Macro Disposable Cuvettes, UV Plastic</td><td>FireFlySci</td><td>1PUV</td><td>10 mm path length</td></tr><tr><td>Methanol, MeOH</td><td>J.T. Baker</td><td>9073-05</td><td>&amp;ge;99.9%</td></tr><tr><td>Palladium (II) chloride, PdCl2</td><td>Sigma Aldrich</td><td>520659</td><td>&amp;ge;99.9%</td></tr><tr><td>Plano-Convex Lens</td><td>Thorlabs</td><td>LA1145</td><td>f=75 mm, N-BK7, uncoated</td></tr><tr><td>Quartz Tungsten-Halogen Lamp</td><td>Thorlabs</td><td>QTH10</td><td></td></tr><tr><td>UV-vis Spectrometer</td><td>Avantes</td><td>ULS2048L-USB2-UA-RS</td><td>AvaSpec-ULS2048L</td></tr></tbody></table>

photodeposition of pd onto colloidal au nanorods by surface plasmon excitation

A protocol is described to photocatalytically guide Pd deposition onto Au nanorods (AuNR) using surface plasmon resonance (SPR). Excited plasmonic hot electrons upon SPR irradiation drive reductive deposition of Pd on colloidal AuNR in the presence of [PdCl4]2-. Plasmon-driven reduction of secondary metals potentiates covalent, sub-wavelength deposition at targeted locations coinciding with electric field &#8220;hot-spots&#8221; of the plasmonic substrate using an external field (e.g., laser). The process described herein details a solution-phase deposition of a catalytically-active noble metal (Pd) from a transition metal halide salt (H2PdCl4) onto aqueously-suspended, anisotropic plasmonic structures (AuNR). The solution-phase process is amenable to making other bimetallic architectures. Transmission UV-vis monitoring of the photochemical reaction, coupled with ex situ XPS and statistical TEM analysis, provide immediate experimental feedback to evaluate properties of the bimetallic structures as they evolve during the photocatalytic reaction. Resonant plasmon irradiation of AuNR in the presence of [PdCl4]2- creates a thin, covalently-bound Pd0 shell without any significant dampening effect on its plasmonic behavior in this representative experiment/batch. Overall, plasmonic photodeposition offers an alternative route for high-volume, economical synthesis of optoelectronic materials with sub-5 nm features (e.g., heterometallic photocatalysts or optoelectronic interconnects).

Transmission UV-vis spectra, X-ray photoelectron spectroscopy (XPS) data, and transmission electron microscopy (TEM) images were acquired for the CTAB-covered AuNR in the presence/absence of H2PdCl4 in dark and under resonant irradiation at their longitudinal SPR (LSPR) to catalyze nucleation/growth of Pd. Transmission UV-vis spectra in Figure 1 and Figure 2 provide insights into the reaction dynamics according to changes in: (a) precursor ...

Watch this Scientific Journal Video about Photodeposition of Pd onto Colloidal Au Nanorods by Surface Plasmon Excitation at JoVE.com

Photodeposition of Pd onto Colloidal Au Nanorods by Surface Plasmon Excitation

A protocol for anisotropic photodeposition of Pd onto aqueously-suspended Au nanorods via localized surface plasmon excitation is presented.

A protocol is described to photocatalytically guide Pd deposition onto Au nanorods (AuNR) using surface plasmon resonance (SPR). Excited plasmonic hot ...

photodeposition-pd-onto-colloidal-au-nanorods-surface-plasmon

Research

JoVE Journal

Chemistry

7.4K Views.  U.S. Army Research Laboratory. Een reductief plasmonisch fotodepositieprotocol versterkt de mogelijkheid om sub-vijf nanometer covalente metaalassemblage te begeleiden op gerichte locaties met optimale interfaciale kenmerken bij omgevingsverwerkingsomstandigheden. Het belangrijkste voordeel van deze techniek is de mogelijkheid om een extern veld te gebruiken, zoals een laser om de dikte en locatie van epitaxiale metaalgroei te controleren. We hebben al aangetoond plasmonische fotodepositie van metallic platina en zilver, e...

Video: Photodeposition of Pd onto Colloidal Au Nanorods by Surface Plasmon Excitation

Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) membranes have been under development since the 1990's and have become a common method to template the synthesis of high aspect ratio nanostructures, mostly by electrochemical growth or pore-wetting. Recently, these membranes have become commercially available in a wide range of pore sizes and densities, leading to an extensive library of functional nanostructures being synthesized from AAO membranes. These include composite nanorods, nanowires and nanotubes made of metals, inorganic materials or polymers 3-10. Nanoporous membranes have been used to synthesize nanoparticle and nanotube arrays that perform well as refractive index sensors, plasmonic biosensors, or surface enhanced Raman spectroscopy (SERS) substrates 11-16, as well as a wide range of other fields such as photo-thermal heating 17, permselective transport 18, 19, catalysis 20, microfluidics 21, and electrochemical sensing 22, 23. Here, we report a novel procedure to prepare gold nanotubes in AAO membranes. Hollow nanostructures have potential application in plasmonic and SERS sensing, and we anticipate these gold nanotubes will allow for high sensitivity and strong plasmon signals, arising from decreased material dampening 15.

Solution-suspendable gold nanotubes with controlled dimensions can be synthesized by electrochemical deposition in porous anodic aluminum oxide (AAO) membranes using a hydrophobic polymer core. Gold nanotubes and nanotube arrays hold promise for applications in plasmonic biosensing, surface-enhanced Raman spectroscopy, photo-thermal heating, ionic and molecular transport, microfluidics, catalysis and electrochemical sensing.

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments1, 2. Applications of anodic aluminum oxide (AAO) ...

Synthesis, Characterization, and Functionalization of Hybrid Au/CdS and Au/ZnS Core/Shell Nanoparticles

Plasmonic nanoparticles are an attractive material for light harvesting applications due to their easily modified surface, high surface area and large extinction coefficients which can be tuned across the visible spectrum. Research into the plasmonic enhancement of optical transitions has become popular, due to the possibility of altering and in some cases improving photo-absorption or emission properties of nearby chromophores such as molecular dyes or quantum dots. The electric field of the plasmon can couple with the excitation dipole of a chromophore, perturbing the electronic states involved in the transition and leading to increased absorption and emission rates. These enhancements can also be negated at close distances by energy transfer mechanism, making the spatial arrangement of the two species critical. Ultimately, enhancement of light harvesting efficiency in plasmonic solar cells could lead to thinner and, therefore, lower cost devices. The development of hybrid core/shell particles could offer a solution to this issue. The addition of a dielectric spacer between a gold nanoparticles and a chromophore is the proposed method to control the exciton plasmon coupling strength and thereby balance losses with the plasmonic gains. A detailed procedure for the coating of gold nanoparticles with CdS and ZnS semiconductor shells is presented. The nanoparticles show high uniformity with size control in both the core gold particles and shell species allowing for a more accurate investigation into the plasmonic enhancement of external chromophores.

The synthesis of uniform gold nanoparticles coated with semiconductor shells of CdS or ZnS is performed. The semiconductor coating is conducted by first depositing a silver sulfide shell and exchanging the silver cations for zinc or cadmium cations.

Plasmonic nanoparticles are an attractive material for light harvesting applications due to their easily modified surface, high surface area and large ...

Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics

We present a method for colloidal synthesis of silver nanocubes and the use of these in combination with a smooth gold film, to fabricate plasmonic nanoscale patch antennas. This includes a detailed procedure for the fabrication of thin films with a well-controlled thickness over macroscopic areas using layer-by-layer deposition of polyelectrolyte polymers, namely poly(allylamine) hydrochloride (PAH) and polystyrene sulfonate (PSS). These polyelectrolyte spacer layers serve as a dielectric gap in between silver nanocubes and a gold film. By controlling the size of the nanocubes or the gap thickness, the plasmon resonance can be tuned from about 500 nm to 700 nm. Next, we demonstrate how to incorporate organic sulfo-cyanine5 carboxylic acid (Cy5) dye molecules into the dielectric polymer gap region of the nanopatch antennas. Finally, we show greatly enhanced fluorescence of the Cy5 dyes by spectrally matching the plasmon resonance with the excitation energy and the Cy5 absorption peak. The method presented here enables the fabrication of plasmonic nanopatch antennas with well-controlled dimensions utilizing colloidal synthesis and a layer-by-layer dip-coating process with the potential for low cost and large-scale production. These nanopatch antennas hold great promise for practical applications, for example in sensing, ultrafast optoelectronic devices and for high-efficiency photodetectors.

A protocol for the colloidal synthesis of silver nanocubes and fabrication of plasmonic nanoscale patch antennas with sub-10 nm gaps is presented.

We present a method for colloidal synthesis of silver nanocubes and the use of these in combination with a smooth gold film, to fabricate plasmonic ...

Engineering

In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films

Combinations of metal oxide semiconductors and gold nanoparticles (AuNPs) have been investigated as new types of materials. The in situ synthesis of AuNPs within the interlayer space of semiconducting layered titania nanosheet (TNS) films was investigated here. Two types of intermediate films (i.e., TNS films containing methyl viologen (TNS/MV2+) and 2-ammoniumethanethiol (TNS/2-AET+)) were prepared. The two intermediate films were soaked in an aqueous tetrachloroauric(III) acid (HAuCl4) solution, whereby considerable amounts of Au(III) species were accommodated within the interlayer spaces of the TNS films. The two types of obtained films were then soaked in an aqueous sodium tetrahydroborate (NaBH4) solution, whereupon the color of the films immediately changed from colorless to purple, suggesting the formation of AuNPs within the TNS interlayer. When only TNS/MV2+ was used as the intermediate film, the color of the film gradually changed from metallic purple to dusty purple within 30 min, suggesting that aggregation of AuNPs had occurred. In contrast, this color change was suppressed by using the TNS/2-AET+ intermediate film, and the AuNPs were stabilized for over 4 months, as evidenced by the characteristic extinction (absorption and scattering) band from the AuNPs.

In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films

Here, we present a protocol for the in situ synthesis of gold nanoparticles (AuNPs) within the interlayer space of layered titanate films without the aggregation of AuNPs. No spectral change was observed even after 4 months. The synthesized material has expected applications in catalysis, photo-catalysis, and the development of cost-effective plasmonic devices.

Combinations of metal oxide semiconductors and gold nanoparticles (AuNPs) have been investigated as new types of materials. The in situ synthesis of AuNPs ...

Fabrication of Periodic Gold Nanocup Arrays Using Colloidal Lithography

Within recent years, the field of plasmonics has exploded as researchers have demonstrated exciting applications related to chemical and optical sensing in combination with new nanofabrication techniques. A plasmon is a quantum of charge density oscillation that lends nanoscale metals such as gold and silver unique optical properties. In particular, gold and silver nanoparticles exhibit localized surface plasmon resonances-collective charge density oscillations on the surface of the nanoparticle-in the visible spectrum. Here, we focus on the fabrication of periodic arrays of anisotropic plasmonic nanostructures. These half-shell (or nanocup) structures can exhibit additional unique light-bending and polarization-dependent optical properties that simple isotropic nanostructures cannot. Researchers are interested in the fabrication of periodic arrays of nanocups for a wide variety of applications such as low-cost optical devices, surface-enhanced Raman scattering, and tamper indication. We present a scalable technique based on colloidal lithography in which it is possible to easily fabricate large periodic arrays of nanocups using spin-coating and self-assembled commercially available polymeric nanospheres. Electron microscopy and optical spectroscopy from the visible to near-infrared (near-IR) was performed to confirm successful nanocup fabrication. We conclude with a demonstration of the transfer of nanocups to a flexible, conformal adhesive film.

We demonstrate the fabrication of periodic gold nanocup arrays using colloidal lithographic techniques and discuss the importance of nanoplasmonic films.

Within recent years, the field of plasmonics has exploded as researchers have demonstrated exciting applications related to chemical and optical sensing ...

Rapid Nanoprobe Signal Enhancement by In Situ Gold Nanoparticle Synthesis

The use of nanoprobes such as gold, silver, silica or iron-oxide nanoparticles as detection reagents in bioanalytical assays can enable high sensitivity and convenient colorimetric readout. However, high densities of nanoparticles are typically needed for detection. The available synthesis-based enhancement protocols are either limited to gold and silver nanoparticles or rely on precise enzymatic control and optimization. Here, we present a protocol to enhance the colorimetric readout of gold, silver, silica, and iron oxide nanoprobes. It was observed that the colorimetric signal can be improved by up to a 10000-fold factor. The basis for such signal enhancement strategies is the chemical reduction of Au3+ to Au0. There are several chemical reactions that enable the reduction of Au3+ to Au0. In the protocol, Good&#39;s buffers and H2O2 are used and it is possible to favor the deposition of Au0 onto the surface of existing nanoprobes, in detriment of the formation of new gold nanoparticles. The protocol consists of the incubation of the microarray with a solution consisting of chloroauric acid and H2O2 in 2-(N-morpholino)ethanesulfonic acid pH 6 buffer following the nanoprobe-based detection assay. The enhancement solution can be applied to paper and glass-based sensors. Moreover, it can be used in commercially available immunoassays as demonstrated by the application of the method to a commercial allergen microarray. The signal development requires less than 5 min of incubation with the enhancement solution and the readout can be assessed by naked eye or low-end image acquisition devices such as a table-top scanner or a digital camera.

Rapid Nanoprobe Signal Enhancement by In Situ Gold Nanoparticle Synthesis

In this work, a protocol for signal enhancement of nanoprobe-based biosensing is presented. The protocol is based on the reduction of chloroauric acid onto the surface of existing nanoprobes that consist of gold, silver, silica or iron-oxide nanoparticles.

The use of nanoprobes such as gold, silver, silica or iron-oxide nanoparticles as detection reagents in bioanalytical assays can enable high sensitivity ...

Ligand-Mediated Nucleation and Growth of Palladium Metal Nanoparticles

The size, size distribution and stability of colloidal nanoparticles are greatly affected by the presence of capping ligands. Despite the key contribution of capping ligands during the synthesis reaction, their role in regulating the nucleation and growth rates of colloidal nanoparticles is not well understood. In this work, we demonstrate a mechanistic investigation of the role of trioctylphosphine (TOP) in Pd nanoparticles in different solvents (toluene and pyridine) using in situ SAXS and ligand-based kinetic modeling. Our results under different synthetic conditions reveal the overlap of nucleation and growth of Pd nanoparticles during the reaction, which contradicts the LaMer-type nucleation and growth model. The model accounts for the kinetics of Pd-TOP binding for both, the precursor and the particle surface, which is essential to capture the size evolution as well as the concentration of particles in situ. In addition, we illustrate the predictive power of our ligand-based model through designing the synthetic conditions to obtain nanoparticles with desired sizes. The proposed methodology can be applied to other synthesis systems and therefore serves as an effective strategy for predictive synthesis of colloidal nanoparticles.

The main goal of this work is to elucidate the role of capping agents in regulating the size of palladium nanoparticles by combining in situ small angle x-ray scattering (SAXS) and ligand-based kinetic modeling.

The size, size distribution and stability of colloidal nanoparticles are greatly affected by the presence of capping ligands. Despite the key contribution ...

A Continuous-flow Photocatalytic Reactor for the Precisely Controlled Deposition of Metallic Nanoparticles

In this work, a novel photocatalytic reactor for the pulsed and controlled excitation of the photocatalyst and the precise deposition of metallic nanoparticles is developed. Guidelines for the replication of the reactor and its operation are provided in detail. Three different composite systems (Pt/graphene, Pt/TiO2, and Au/TiO2) with monodisperse and uniformly distributed particles are produced by this reactor, and the photodeposition mechanism, as well as the synthesis optimization strategy, are discussed. The synthesis methods and their technical aspects are described comprehensively. The role of the ultraviolet (UV) dose (in each excitation pulse) on the photodeposition process is investigated and the optimum values for each composite system are provided.

For a continuous and scalable synthesis of noble-metal-based nanocomposites, a novel photocatalytic reactor is developed and its structure, operation principles, and product quality optimization strategies are described.

In this work, a novel photocatalytic reactor for the pulsed and controlled excitation of the photocatalyst and the precise deposition of metallic ...

Preparation and Photoacoustic Analysis of Cellular Vehicles Containing Gold Nanorods

Gold nanorods are attractive for a range of biomedical applications, such as the photothermal ablation and the photoacoustic imaging of cancer, thanks to their intense optical absorbance in the near-infrared window, low cytotoxicity and potential to home into tumors. However, their delivery to tumors still remains an issue. An innovative approach consists of the exploitation of the tropism of tumor-associated macrophages that may be loaded with gold nanorods in vitro. Here, we describe the preparation and the photoacoustic inspection of cellular vehicles containing gold nanorods. PEGylated gold nanorods are modified with quaternary ammonium compounds, in order to achieve a cationic profile. On contact with murine macrophages in ordinary Petri dishes, these particles are found to undergo massive uptake into endocytic vesicles. Then these cells are embedded in biopolymeric hydrogels, which are used to verify that the stability of photoacoustic conversion of the particles is retained in their inclusion into cellular vehicles. We are confident that these results may provide new inspiration for the development of novel strategies to deliver plasmonic particles to tumors.

We show the preparation and address the feasibility of cellular vehicles containing gold nanorods for the photoacoustic imaging of cancer.

Gold nanorods are attractive for a range of biomedical applications, such as the photothermal ablation and the photoacoustic imaging of cancer, thanks to ...

Bioengineering

Preparation of Silver-Palladium Alloyed Nanoparticles for Plasmonic Catalysis under Visible-Light Illumination

Localized surface plasmon resonance (LSPR) in plasmonic nanoparticles (NPs) can accelerate and control the selectivity of a variety of molecular transformations. This opens possibilities for the use of visible or near-IR light as a sustainable input to drive and control reactions when plasmonic nanoparticles supporting LSPR excitation in these ranges are employed as catalysts. Unfortunately, this is not the case for several catalytic metals such as palladium (Pd). One strategy to overcome this limitation is to employ bimetallic NPs containing plasmonic and catalytic metals. In this case, the LSPR excitation in the plasmonic metal can contribute to accelerate and control transformations driven by the catalytic component. The method reported herein focuses on the synthesis of bimetallic silver-palladium (Ag-Pd) NPs supported on ZrO2 (Ag-Pd/ZrO2) that acts as a plasmonic-catalytic system. The NPs were prepared by co-impregnation of corresponding metal precursors on the ZrO2 support followed by simultaneous reduction leading to the formation of bimetallic NPs directly on the ZrO2 support. The Ag-Pd/ZrO2 NPs were then used as plasmonic catalysts for the reduction of nitrobenzene under 425 nm illumination by LED lamps. Using gas chromatography (GC), the conversion and selectivity of the reduction reaction under the dark and light irradiation conditions can be monitored, demonstrating the enhanced catalytic performance and control over selectivity under LSPR excitation after alloying non-plasmonic Pd with plasmonic metal Ag. This technique can be adapted to a wide range of molecular transformations and NPs compositions, making it useful for the characterization of the plasmonic catalytic activity of different types of catalysis in terms of conversion and selectivity.

Presented here is a protocol for the synthesis of silver-palladium (Ag-Pd) alloy nanoparticles (NPs) supported on ZrO2 (Ag-Pd/ZrO2). This system allows for harvesting energy from visible light irradiation to accelerate and control molecular transformations. This is illustrated by nitrobenzene reduction under light irradiation catalyzed by Ag-Pd/ZrO2 NPs.

Photodeposition of Pd onto Colloidal Au Nanorods by Surface Plasmon Excitation

Samenvatting

Meer video's verkennen