We would like to express our sincere gratitude to Bogazici University for providing the laboratory facilities and technical support necessary for this research. We also thank Dr. Demet Sezgin Mansuroglu, Dr. Eda Karadogan, and Dr. Mustafa Enes Ozden for their valuable assistance in data collection and analysis. The research was funded by the authors. No external financial support was obtained.

1. Sample procurement
<ol>
	<li>Procure 80 acrylic blocks with an internal diameter of 1.5 mm, a radius of curvature of 5 mm, a 55&#176; curvature, and a working length of 16 mm.</li>
</ol>
2. Cleaning and shaping procedure
<ol>
	<li>Set the endomotor to a torque of 2.0 Ncm and a speed of 300 rpm.
	<ol>
		<li>Attach a 10/.04 taper file to the motor and use it in a back-and-forth motion until the working length (16 mm) is reached, ensuring that it does not bind.</li>
		<li>Irrigate the canals with 5.25% NaOCl.</li>
		<li>Attach a 15/.04 tapered file to the motor and use it in a back-and-forth motion until the working length (16 mm) is reached, ensuring that it does not bind.</li>
		<li>Repeat steps 2.1.2 and 2.1.3 with 20/.04, 25/.04, 30/.04, and 35/.04 taper files, used sequentially at the working length (16 mm).</li>
		<li>Dry the canals with paper points.</li>
	</ol>
	</li>
</ol>
3. Obturation
<ol>
	<li>Check the fit of a guttapercha cone to the canal.</li>
	<li>Inject the bioceramic canal sealer into the canal and fill it with bioceramic sealer.</li>
	<li>Insert the appropriate gutta-percha cone into the sealer-filled canal. Cut the gutta-percha 2 mm below the canal orifice using a heat tool.</li>
	<li>Take a periapical radiograph to verify the canal fillings (see Figure 1).</li>
	<li>Store the specimens in an incubator at 37 &#176;C and 100% humidity for 2 weeks.</li>
</ol>
4. Retreatment procedure
NOTE: A total of 24 new Remover files (23 mm) were used in the present study. The files were randomized into three groups of eight samples each. In determining the number of samples and files used in this research, the quota sampling method was used, considering the budget and the sample sizes of other reports in the literature27.
<ol>
	<li>Operate the files at 600 rpm and 2.5 Ncm torque according to the manufacturer&#39;s instructions. Use the files with a back-and-forth motion without applying apical pressure until they are 3 mm short of the working length.</li>
	<li>Remove the file from the canal when resistance is felt and irrigate with 5.25% NaOCl solution.</li>
	<li>Repeat steps 4.1 and 4.2 until the desired length is reached.</li>
	<li>Clean and sterilize the instruments in an autoclave for 18 min at 134 &#176;C before shaping the specimen. 
	NOTE: The files in the first group were used for retreatment in eight curved canals. The files in the second group were used for retreatment 3x each, and the files in the third group were used for retreatment 6x each. The procedures were repeated in group 2 and group 3 according to the number of uses.</li>
</ol>
5. SEM analysis
<ol>
	<li>Sample preparation and loading 
	NOTE: Take the necessary precautions to avoid contamination when handling the sample (e.g., wear gloves). Do not place the sample in a gold sputtering system as the surface is nickel-titanium.
	<ol>
		<li>Mount the sample on an SEM stub using conductive double-sided carbon tape.</li>
		<li>Attach the stub to the stage and tighten the side screw (see Figure 2).</li>
	</ol>
	</li>
	<li>SEM operation
	<ol>
		<li>Open the SEM sample chamber and remove the stage.</li>
		<li>Place the sample stub on the stage and secure it in place.</li>
		<li>Insert the sample stage into the sample chamber and close the chamber.</li>
		<li>Switch on the pumps and wait for the system notification of the vacuum.</li>
		<li>Open the SEM software and select the required operating voltage between 1 kV and 30 kV.</li>
	</ol>
	</li>
	<li>Image analysis
	<ol>
		<li>Have a trained investigator take images of the 4 mm distal end, which is the active part (area of interest), at standard magnifications of 100x, 250x, and 500x. Use an unused Remover file as a reference to evaluate the surface characteristics of the samples (see Figure 3).</li>
		<li>To commence the Auto Focus function, select the key icon within the SEM software. The resulting focused image of the sample is the desired endpoint.</li>
		<li>Set the magnification to the minimum zoom level of 50x.</li>
		<li>Enable the fast scan mode for efficient image acquisition.</li>
		<li>Adjust the focus using the coarse focus mode until a preliminary focus is achieved.</li>
		<li>Gradually increase the magnification to observe the desired feature. Use the coarse focus knob to achieve a rough focus, followed by the fine focus knob for precise focusing. Repeat this step for each magnification increase.</li>
		<li>Increase the magnification until the desired feature is observed. Adjust the coarse focus knob to roughly focus the image at this magnification. Then, use the fine focusing knob to improve the focus to obtain a focused image at the desired magnification. Repeat this step each time the magnification level is increased.</li>
		<li>Once the desired magnification is reached, refine the focus using the fine focus knob for optimal clarity.</li>
		<li>For enhanced image clarity, further increase the magnification to a near-maximum level and adjust the focus using the fine focus knob. If clarity is still not sufficient, adjust the stigmation in both the x and y axes. Continue fine-tuning the focus and stigmation until the clearest image is obtained at the higher magnification.</li>
		<li>After achieving a high-quality image of the sample, return to the desired magnification level. Capture the image by pressing the photo button. Choose either slow photo mode for higher quality and resolution, or fast photo mode for quicker capture.</li>
		<li>Repeat these steps for each sample.</li>
		<li>Download the images to the computer.</li>
		<li>Have two calibrated examiners analyze all SEM images by reviewing the images on a computer screen and recording the presence and type of deformations that occur in the files. The deformations include tip deformation, microcracks, fracture, unwinding, surface pitting, and blade disruption (Figure 4, Figure 5, Figure 6, Figure 7, and Figure 8).</li>
		<li>Have the same examiners analyze the collected data twice at 1 week intervals. 
		NOTE: Differences of opinion in the interpretation of SEM images of the samples between the observers are to be discussed until a consensus is reached.</li>
	</ol>
	</li>
</ol>
6. Statistical analysis
<ol>
	<li>Present descriptive statistics as counts and percentages.</li>
	<li>Perform analyses using statistical analysis software. Evaluate the differences between groups using the Fisher-Freeman-Halton Exact test. Set a type 1 error rate of 0.05 (two-tailed), and consider p &#60; 0.005 statistically significant.</li>
</ol>

Surface Defects in NiTi Files After Single and Multiple Uses in Endodontic Retreatment

The authors have no conflicts of interest to disclose.

This study evaluated the presence and types of microscopic defects on the external surfaces of Remover files after single, triple, and six-times use in acrylic blocks simulating curved canals. Ideally, human teeth are recommended for use in studies evaluating the fracture resistance of files to better simulate clinical use28. In their study, Peters and Barbakow29 found an increase in fracture initiation and propagation rates in instruments used in blocks compared to extract...

Endodontic retreatment is a procedure performed when a previously treated tooth fails to heal or develops new pathologies, such as persistent infection, reinfection, or missed anatomy. The procedure involves the removal of the existing root canal filling material, thorough cleaning and disinfection of the canal system and subsequent refilling1,2.
Nickel-titanium (NiTi) instruments are of great importance in improving and facilitating endodontic procedures due to their flexibility and high cutting efficiency3,4. The superelasticity of NiTi instruments permits them to better adapt to canal curvature, exhibit less wear, and have a higher resistance to fracture5,6. However, one of the major concerns with NiTi files is that they can fracture without visible deformation3.
The most common cause of fracture in NiTi rotary instruments is cyclic fatigue7. Cyclic fatigue occurs due to alternating tensile and compressive stresses on opposing surfaces of the instrument as it rotates continuously in a curved root canal without binding8,9. Fracture due to cyclic fatigue results from metal exhaustion10. Several factors influence the occurrence of fracture due to cyclic fatigue, including the physical properties of the instrument11,12, the root canal morphology13, repeated clinical use, and the sterilization process14,15. Therefore, to improve the fatigue resistance of NiTi rotary files, various modifications in the manufacturing method and core diameter, as well as changes in the cutting-edge and cross-sectional designs, have been attempted16. The Remover file is a new generation file produced by thermal treatment and a special electropolishing process called C-wire. Its design features are claimed to increase fatigue resistance. The file has a 30/100 mm non-cutting (inactive) tip and a minimally invasive core diameter. It is manufactured with a variable triple helix cross section that is symmetrical for the first 3 mm and then becomes asymmetrical towards the shaft. In addition, it is designed to preserve periradicular dentin by having a 7% taper in the first 10 mm, followed by a 0% taper towards the shaft17.
Cyclic fatigue fractures in NiTi rotary files typically occur without any visible plastic deformation18,19,20. As a result, these fractures cannot be evaluated clinically, and structural changes must be examined under high magnification using tools such as a stereomicroscope or scanning electron microscope (SEM)21. Due to the impracticality of performing such examinations on a routine basis, manufacturers recommend that files be used only once22,23. However, due to the high cost of NiTi files, many clinicians choose to reuse them24. Therefore, it is important to investigate the effects of clinical reuse on these files. One clinical study showed that rotary instruments can be safely reused up to 4x25. However, other studies have evaluated much higher reuse rates and there is no consensus on how many times a file can be safely reused24,26.
In previous studies that have evaluated the reuse of NiTi files, the primary focus has been on the effects of root canal widening and shaping on the fracture resistance of the files. A review of the literature, therefore, reveals that there is only one study that specifically evaluates the repeated use of retreatment file systems27. The aim of this study is to evaluate the impact of repeated use on the surface characteristics of the Remover file using scanning electron microscopy (SEM). It is hypothesized that increased clinical use will result in an increase in surface defects, thereby elevating the risk of fatigue fractures. The specific objective is to analyze the changes in surface defects of the Remover file after single and multiple uses, and to discuss the implications of these changes for clinical practice.

<table><tbody><tr><td>Acrylic block</td><td>ArdaDent Medical,Ankara,Turkey</td><td></td><td>for obturation</td></tr><tr><td>DiaRoot Biosealer</td><td>DiaDent, South Korea</td><td>BS23101161</td><td>for obturation</td></tr><tr><td>DualMove Endomotor</td><td>MicroMega, Coltene, France</td><td>52002023</td><td>for preparation</td></tr><tr><td>&amp;nbsp;EndoArt&amp;nbsp; Smart Gold&amp;nbsp;</td><td>EndoArt, Inci Dental, Turkey</td><td>SGK10114</td><td>&amp;nbsp;for initial preparation</td></tr><tr><td>&amp;nbsp;Gutta Percha</td><td>EndoArt, Inci Dental, Turkey</td><td>GD23080701</td><td>for obturation</td></tr><tr><td>Quattro ESEM&amp;nbsp;</td><td>Thermo Fisher Scientific, USA</td><td></td><td>SEM analysis</td></tr><tr><td>Paper Points</td><td>Dentsply Maillefer, Ballaigues, Switzerland&amp;nbsp;</td><td>1I0305</td><td>for dry to root canal</td></tr><tr><td>Remover File</td><td>MicroMega, Besan&amp;ccedil;on, France</td><td>891144/873757/</td><td>for retreatment procedure</td></tr><tr><td>Sodium Hypochlorite&amp;nbsp;</td><td>Saba Chemical&amp;amp;Medical, Turkey</td><td>3010225</td><td>for irrigation</td></tr><tr><td>SPSS v29&amp;nbsp;</td><td>IBM SPSS Corp, Armonk, New York, USA</td><td></td><td>Statistical analysis</td></tr></tbody></table>

scanning electron microscopic evaluation of surface defects of remover retreatment file after single and multiple uses

This study aimed to evaluate surface defects of Remover rotary Nickel-Titanium (NiTi) files after single and multiple uses in conventional endodontic retreatment procedures using scanning electron microscopy (SEM). Eighty acrylic blocks, simulating root canals with a 1.5 mm internal diameter, a 5 mm radius of curvature, and a 55&#176; curvature, were utilized. After chemomechanical preparation and obturation, 24 new Remover files (N30, 7%, L23) were randomly assigned to three groups: single use, triple use, and six uses. The files were operated at 600 rpm with a torque of 2.5 Ncm, cleaned, and sterilized after each use.
SEM analysis at magnifications of 100x, 250x, and 500x revealed surface defects, including tip deformation, microcracks, fracture, unwinding, surface pitting, and blade disruption. Deformation was observed in 75% of the files after a single use and in 100% of the files after three and six uses. Microcracks were absent after single use but appeared in 25% and 87.5% of files after three and six uses, respectively, showing a statistically significant increase (p &#60; 0.001). Surface pitting also significantly increased among groups (p = 0.004).
No fractures were observed in any group. The most common defects were tip deformation (91.7%) and surface pitting (70.8%). The findings suggest that repeated use of NiTi files significantly increases surface defects, elevating the risk of fatigue fractures. Thus, the results recommend limiting the reuse of Remover files to a maximum of 3x. Further research is needed to correlate defect types with anatomical factors and to assess file effectiveness in retreatment scenarios.

Deformation was observed in 75% of files after single use and in 100% of files after three and six uses, but the differences between the groups were not statistically significant (Table 1). The evaluation of deformation types among groups is shown in Table 2. When the types of deformation were evaluated separately, no microcracks were observed after a single use, while microcracks were observed in 25% of the files after three uses and in 87.5% of the files after six uses; this difference...

Scanning Electron Microscopic Evaluation of Surface Defects of Remover Retreatment File After Single and Multiple Uses

Here, we present a protocol for evaluating the surface characteristics of endodontic retreatment files after repeated use in retreatment procedures, utilizing scanning electron microscopy to identify and analyze potential surface defects.

This study aimed to evaluate surface defects of Remover rotary Nickel-Titanium (NiTi) files after single and multiple uses in conventional endodontic ...

scanning-electron-microscopic-evaluation-surface-defects-remover

Research

JoVE Journal

Medicine

413 Views.  Marmara University. Het doel van onze zoektocht is om de impact van herhaald gebruik van een verwijderbestand op de oppervlaktekarakteristiek te onderzoeken, met een bijzondere focus op het aantal gebruikers. Het doel is om het aantal keren te bepalen dat het product veilig kan worden gebruikt zonder de integriteit van het oppervlak in gevaar te brengen. Onze belangrijke bevindingen geven aan dat het behandelingsdossier voor de verwijderaar veilig kan worden gebruikt voor maxima...

Video: Scanning Electron Microscopische Evaluatie van Oppervlaktedefecten van Remover Herbehandelingsbestand na eenmalig en meervoudig gebruik

Characterization of Surface Modifications by White Light Interferometry: Applications in Ion Sputtering, Laser Ablation, and Tribology Experiments

In materials science and engineering it is often necessary to obtain quantitative measurements of surface topography with micrometer lateral resolution. From the measured surface, 3D topographic maps can be subsequently analyzed using a variety of software packages to extract the information that is needed.
In this article we describe how white light interferometry, and optical profilometry (OP) in general, combined with generic surface analysis software, can be used for materials science and engineering tasks. In this article, a number of applications of white light interferometry for investigation of surface modifications in mass spectrometry, and wear phenomena in tribology and lubrication are demonstrated. We characterize the products of the interaction of semiconductors and metals with energetic ions (sputtering), and laser irradiation (ablation), as well as ex situ measurements of wear of tribological test specimens.
Specifically, we will discuss:
<ol class="lroman">
	<li>Aspects of traditional ion sputtering-based mass spectrometry such as sputtering rates/yields measurements on Si and Cu and subsequent time-to-depth conversion.</li>
	<li>Results of quantitative characterization of the interaction of femtosecond laser irradiation with a semiconductor surface. These results are important for applications such as ablation mass spectrometry, where the quantities of evaporated material can be studied and controlled via pulse duration and energy per pulse. Thus, by determining the crater geometry one can define depth and lateral resolution versus experimental setup conditions.</li>
	<li>Measurements of surface roughness parameters in two dimensions, and quantitative measurements of the surface wear that occur as a result of friction and wear tests.</li>
</ol>
Some inherent drawbacks, possible artifacts, and uncertainty assessments of the white light interferometry approach will be discussed and explained.

White light microscope interferometry is an optical, noncontact and quick method for measuring the topography of surfaces. It is shown how the method can be applied toward mechanical wear analysis, where wear scars on tribological test samples are analyzed; and in materials science to determine ion beam sputtering or laser ablation volumes and depths.

In materials science and engineering it is often necessary to obtain quantitative measurements of surface topography with micrometer lateral resolution. ...

Engineering

Comprehensive Characterization of Extended Defects in Semiconductor Materials by a Scanning Electron Microscope

Extended defects such as dislocations and grain boundaries have a strong influence on the performance of microelectronic devices and on other applications of semiconductor materials. However, it is still under debate how the defect structure determines the band structure, and therefore, the recombination behavior of electron-hole pairs responsible for the optical and electrical properties of the extended defects. The present paper is a survey of procedures for the spatially resolved investigation of structural and of physical properties of extended defects in semiconductor materials with a scanning electron microscope (SEM). Representative examples are given for crystalline silicon. The luminescence behavior of extended defects can be investigated by cathodoluminescence (CL) measurements. They are particularly valuable because spectrally and spatially resolved information can be obtained simultaneously. For silicon, with an indirect electronic band structure, CL measurements should be carried out at low temperatures down to 5 K due to the low fraction of radiative recombination processes in comparison to non-radiative transitions at room temperature. For the study of the electrical properties of extended defects, the electron beam induced current (EBIC) technique can be applied. The EBIC image reflects the local distribution of defects due to the increased charge-carrier recombination in their vicinity. The procedure for EBIC investigations is described for measurements at room temperature and at low temperatures. Internal strain fields arising from extended defects can be determined quantitatively by cross-correlation electron backscatter diffraction (ccEBSD). This method is challenging because of the necessary preparation of the sample surface and because of the quality of the diffraction patterns which are recorded during the mapping of the sample. The spatial resolution of the three experimental techniques is compared.

The optical, electrical, and structural properties of dislocations and of grain boundaries in semiconductor materials can be determined by experiments performed in a scanning electron microscope. Electron microscopy has been used to investigate cathodoluminescence, electron beam induced current, and diffraction of backscattered electrons.

Extended defects such as dislocations and grain boundaries have a strong influence on the performance of microelectronic devices and on other applications ...

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight

Corrosion of metallic surfaces is prevalent in the environment and is of great concern in many areas, including the military, transport, aviation, building and food industries, amongst others. Polyester and coatings containing both polyester and silica nanoparticles (SiO2NPs) have been widely used to protect steel substrata from corrosion. In this study, we utilized X-ray photoelectron spectroscopy, attenuated total reflection infrared micro-spectroscopy, water contact angle measurements, optical profiling and atomic force microscopy to provide an insight into how exposure to sunlight can cause changes in the micro- and nanoscale integrity of the coatings. No significant change in surface micro-topography was detected using optical profilometry, however, statistically significant nanoscale changes to the surface were detected using atomic force microscopy. Analysis of the X-ray photoelectron spectroscopy and attenuated total reflection infrared micro-spectroscopy data revealed that degradation of the ester groups had occurred through exposure to ultraviolet light to form COO&#903;, -H2C&#903;, -O&#903;, -CO&#903; radicals. During the degradation process, CO and CO2 were also produced.

Two types of surfaces, polyester-coated steel and polyester coated with a layer of silica nanoparticles, were studied. Both surfaces were exposed to sunlight, which was found to cause substantial changes in the chemistry and nanoscale topography of the surface.

Corrosion of metallic surfaces is prevalent in the environment and is of great concern in many areas, including the military, transport, aviation, ...

Characterization of Ultra-fine Grained and Nanocrystalline Materials Using Transmission Kikuchi Diffraction

One of the challenges in microstructure analysis nowadays resides in the reliable and accurate characterization of ultra-fine grained (UFG) and nanocrystalline materials. The traditional techniques associated with scanning electron microscopy (SEM), such as electron backscatter diffraction (EBSD), do not possess the required spatial resolution due to the large interaction volume between the electrons from the beam and the atoms of the material. Transmission electron microscopy (TEM) has the required spatial resolution. However, due to a lack of automation in the analysis system, the rate of data acquisition is slow which limits the area of the specimen that can be characterized. This paper presents a new characterization technique, Transmission Kikuchi Diffraction (TKD), which enables the analysis of the microstructure of UFG and nanocrystalline materials using an SEM equipped with a standard EBSD system. The spatial resolution of this technique can reach 2 nm. This technique can be applied to a large range of materials that would be difficult to analyze using traditional EBSD. After presenting the experimental set up and describing the different steps necessary to realize a TKD analysis, examples of its use on metal alloys and minerals are shown to illustrate the resolution of the technique and its flexibility in term of material to be characterized.

This paper provides a detailed method to characterize the microstructure of ultra-fine grained and nanocrystalline materials using a scanning electron microscope equipped with a standard electron backscatter diffraction system. Metal alloys and minerals presenting refined microstructures are analyzed using this technique, showing the diversity of its possible applications.

One of the challenges in microstructure analysis nowadays resides in the reliable and accurate characterization of ultra-fine grained (UFG) and ...

Characterization Of Multi-layered Fish Scales (Atractosteus spatula) Using Nanoindentation, X-ray CT, FTIR, and SEM

The hierarchical architecture of protective biological materials such as mineralized fish scales, gastropod shells, ram&#8217;s horn, antlers, and turtle shells provides unique design principles with potentials for guiding the design of protective materials and systems in the future. Understanding the structure-property relationships for these material systems at the microscale and nanoscale where failure initiates is essential. Currently, experimental techniques such as nanoindentation, X-ray CT, and SEM provide researchers with a way to correlate the mechanical behavior with hierarchical microstructures of these material systems1-6. However, a well-defined standard procedure for specimen preparation of mineralized biomaterials is not currently available. In this study, the methods for probing spatially correlated chemical, structural, and mechanical properties of the multilayered scale of A. spatula using nanoindentation, FTIR, SEM, with energy-dispersive X-ray (EDX) microanalysis, and X-ray CT are presented.

Characterization Of Multi-layered Fish Scales Atractosteus spatula Using Nanoindentation, X-ray CT, FTIR, and SEM

This paper presents the methods used for probing spatially correlated chemical, structural, and mechanical properties of the multilayered scale of Atractosteus spatula (A. spatula) using nanoindentation, Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and X-ray computed tomography (X-ray CT). The experimental results have been used to investigate the design principles of protective biological materials.

The hierarchical architecture of protective biological materials such as mineralized fish scales, gastropod shells, ram&#8217;s horn, antlers, and turtle ...

Bioengineering

Single-Digit Nanometer Electron-Beam Lithography with an Aberration-Corrected Scanning Transmission Electron Microscope

We demonstrate extension of electron-beam lithography using conventional resists and pattern transfer processes to single-digit nanometer dimensions by employing an aberration-corrected scanning transmission electron microscope as the exposure tool. Here, we present results of single-digit nanometer patterning of two widely used electron-beam resists: poly (methyl methacrylate) and hydrogen silsesquioxane. The method achieves sub-5 nanometer features in poly (methyl methacrylate) and sub-10 nanometer resolution in hydrogen silsesquioxane. High-fidelity transfer of these patterns into target materials of choice can be performed using metal lift-off, plasma etch, and resist infiltration with organometallics.

We use an aberration-corrected scanning transmission electron microscope to define single-digit nanometer patterns in two widely-used electron-beam resists: poly (methyl methacrylate) and hydrogen silsesquioxane. Resist patterns can be replicated in target materials of choice with single-digit nanometer fidelity using liftoff, plasma etching, and resist infiltration by organometallics.

We demonstrate extension of electron-beam lithography using conventional resists and pattern transfer processes to single-digit nanometer dimensions by ...

A Virtual Simulation Experiment of Mechanics: Material Deformation and Failure Based on Scanning Electron Microscopy

This work presents a set of comprehensive virtual experiments to detect material deformation and failure. The most commonly used pieces of equipment in mechanics and material disciplines, such as a metallographic cutting machine and a high-temperature universal creep testing machine, are integrated into a web-based system to provide different experimental services to users in an immersive and interactive learning environment. The protocol in this work is divided into five subsections, namely, the preparation of the materials, molding the specimen, specimen characterization, specimen loading, nanoindenter installation, and SEM in situ experiments, and this protocol aims to provide an opportunity for users regarding the recognition of different equipment and the corresponding operations, as well as the enhancement of laboratory awareness, etc., using a virtual simulation approach. To provide clear guidance for the experiment, the system highlights the equipment/specimen to be used in the next step and marks the pathway that leads to the equipment with a conspicuous arrow. To mimic the hands-on experiment as closely as possible, we designed and developed a three-dimensional laboratory room, equipment, operations, and experimental procedures. Moreover, the virtual system also considers interactive exercises and registration before using chemicals during the experiment. Incorrect operations are also allowed, resulting in a warning message informing the user. The system can provide interactive and visualized experiments to users at different levels.

This work presents a three-dimensional virtual simulation experiment for material deformation and failure that provides visualized experimental processes. Through a set of experiments, users can become familiar with the equipment and learn the operations in an immersive and interactive learning environment.

This work presents a set of comprehensive virtual experiments to detect material deformation and failure. The most commonly used pieces of equipment in ...

Experimental Multiscale Methodology for Predicting Material Fouling Resistance

The buildup of fouling deposits in energy systems degrades their ability to transfer heat, reducing efficiency and causing operational issues such as localized corrosion. Each application presents its own challenges. In nuclear power generation, the buildup of CRUD (Chalk River Unidentified Deposits) induces unique, negative effects ranging from reduced heat transfer, to axial power shifting, to CRUD-induced localized corrosion (CILC), the last of which can cause sudden fuel failure. Knowledge of why CRUD forms and how to prevent its adhesion to nuclear fuel rods represents a major step towards eliminating it. This paper demonstrates a methodology to ascertain which materials may resist CRUD adhesion, thereby preventing its initiation and growth. It presents experiments targeted at multiple length scales: pool boiling (macroscale), which simulates CRUD initiation processes in a nuclear reactor, and atomic force microscope (AFM) force spectroscopy (microscale), which yields quantitative measurements of the adhesion between CRUD constituents and candidate CRUD-resistant materials. Early data from both sets of experiments show some correlation, suggesting that AFM force spectroscopy (AFM-FS) may be used to pre-screen materials for fouling resistance. So far, it appears that CRUD constituents adhere well to oxides, while carbides show both greatly reduced adhesion and no adherent CRUD in pool boiling experiments. The relationship between the AFM-FS measurements and the growth of CRUD in the pool boiling experiments may provide insight into the possible factors affecting fouling in nuclear reactors, eventually leading to its elimination.

Fouling, or corrosion product deposition, plagues numerous fields of energy production. At its core is adhesion between dissimilar materials. Understanding and controlling adhesion could reduce or eliminate fouling. This paper demonstrates pool boiling experiments (macroscale) and atomic force microscope force-spectroscopy measurements (microscale), which when in agreement, indicate fouling-resistance.

The buildup of fouling deposits in energy systems degrades their ability to transfer heat, reducing efficiency and causing operational issues such as ...

Biology

Targeted Studies Using Serial Block Face and Focused Ion Beam Scan Electron Microscopy

This protocol allows for the efficient and effective imaging of cell or tissue samples in three dimensions at the resolution level of electron microscopy. For many years electron microscopy (EM) has remained an inherently two-dimensional technique. With the advent of serial scanning electron microscope imaging techniques (volume EM), using either an integrated microtome or focused ion beam to slice then view embedded tissues, the third dimension becomes easily accessible. Serial block face scanning electron microscopy (SBF-SEM) uses an ultramicrotome enclosed in the SEM chamber. It has the capability to handle large specimens (1,000 &#181;m x 1,000 &#181;m) and image large fields of view at small X,Y pixel size, but is limited in the Z dimension by the diamond knife. Focused ion beam SEM (FIB-SEM) is not limited in 3D resolution, (isotropic voxels of &#8804;5 nm are achievable), but the field of view is much more limited. This protocol demonstrates a workflow for combining the two techniques to allow for finding individual regions of interest (ROIs) in a large field and then imaging the subsequent targeted volume at high isotropic voxel resolution. Preparing fixed cells or tissues is more demanding for volume EM techniques due to the extra contrasting needed for efficient signal generation in SEM imaging. Such protocols are time consuming and labor intensive. This protocol also incorporates microwave assisted tissue processing facilitating the penetration of reagents, which reduces the time needed for the processing protocol from days to hours.

Here, we present a protocol for efficiently combining serial block face and focused ion beam scanning electron microscopy to target an area of interest. This allows for efficient searching, in three dimensions, and locating rare events in a large field of view.

This protocol allows for the efficient and effective imaging of cell or tissue samples in three dimensions at the resolution level of electron microscopy. ...

Effects of Mechanical Methods Used in Peri-implantitis Treatment on Implant Surface Decontamination and Roughness

Various mechanical methods have been proposed for decontaminating dental implant surfaces with varying success. This in vitro study evaluated the decontamination efficiency of an air abrasion (AA) system with erythritol powder, a polyether-ether-ketone (PEEK) ultrasonic tip, and titanium curettes (TIT) and their effects on implant surface topography using scanning electron microscopy (SEM). A total of 60 implants were stained with permanent red ink and placed in 3D-printed Class 1A and Class 1B peri-implantitis defects, forming six groups (n=10 per group) based on defect type and treatment protocol. Additionally, one positive and one negative control implant was used. Erythritol powder, PEEK ultrasonic tips, and titanium curettes were applied for 2 min in Class 1A defects and 3 minutes in Class 1B defects. Residual red ink areas were quantified with digital software, and implant surface changes were analyzed using SEM and EDS. None of the methods achieved complete decontamination. However, erythritol powder was significantly the most effective, leaving a residual ink rate of 24% &#177; 6% (p &#60; 0.001). PEEK ultrasonic tips resulted in 41% &#177; 4% residual ink, while titanium curettes left 55% &#177; 3%. Significant differences were observed among all methods. No significant difference in decontamination efficacy was found between Class 1A and Class 1B defects. SEM analysis showed minimal surface damage with erythritol powder and PEEK tips, whereas titanium curettes caused moderate to severe damage. Based on both decontamination efficiency and surface preservation, erythritol powder and PEEK tips are safe and effective options for peri-implantitis treatment, while titanium curettes are less effective and cause considerable surface damage. These findings may assist clinicians in peri-implantitis treatment planning.

The present protocol describes an experimental model based on ink-staining which can be used for in vitro implant surface decontamination and roughness research to contribute to clinical decision-making.

Scanning Electron Microscopic Evaluation of Surface Defects of Remover Retreatment File After Single and Multiple Uses

Samenvatting

Meer video's verkennen