We thank the MIT Department of Chemistry and the MIT Lincoln Labs Advanced Concepts Committee for support of this work.

We first describe the synthesis and purification of PEG-MM B from 3 kDa O-(2-aminoethyl)polyethylene glycol (PEG-NH2) and norbornene-N-hydroxysuccinimidyl (NHS) ester. The former compound can be purchased from Sigma Aldrich Inc., or prepared via anionic polymerization according to literature procedures22,23. The latter compound can be prepared in two steps according to a published procedure21. Next we describe a synthesis of catalyst A from commercially available Grubbs 2nd generation catalyst. We then demonstrate the use of this complex for brush-first BASP synthesis. This experiment details the procedure for making BASPs with N = 10, 15, and 20 from a BI with DP = 10. All reactions were performed in a fume hood using standard scintillation vials.
CAUTION: Always wear gloves, a lab-coat, and lab glasses, and follow common laboratory safety practices when working with hazardous chemicals. Any organic solvent must be handled in a fume hood. Solids can be weighed out on a balance outside the fume hood. Chemicals should not come into contact with skin, eyes, or mouth. It is strongly recommended to read the MSDS for every solvent and solid used in this procedure before beginning.
1. Preparation of PEG-MM B
<ol>
	<li>Add PEG-NH2 (300 mg, 0.0001 mol, 1.0 eq) to a 40 ml scintillation vial equipped with a stir bar.</li>
	<li>Dissolve the PEG-NH2 in 3 ml of anhydrous N,N-dimethylformamide (DMF).</li>
	<li>Add 36 mg of norbornene-NHS ester (0.000105 mol, 1.05 eq)21.</li>
	<li>Cap the vial and stir the reaction mixture overnight at room temperature.</li>
	<li>Remove the stir bar and add diethyl ether to the reaction solution to precipitate the PEG-MM B.</li>
	<li>Filter the white fluffy precipitate and wash extensively with diethyl ether. Alternatively, transfer the suspension to a 50 m centrifuge tube, centrifuge at 4,000 rpm for 5 min at room temperature, and then decant the supernatant. Add fresh diethyl ether, centrifuge, and decant again. We recommend repeating this procedure 3x for a total of 5x.</li>
	<li>Dry the precipitate under vacuum for 24 hr to remove residual diethyl ether.</li>
</ol>
2. Purification of PEG-MM
In our previous report, the PEG-MM B was prepared from commercially available PEG-NH2 and was used for BASP synthesis without further purification after drying (i.e., after step 1.7). In this study, we vary the PEG-NH2 source (commercial versus homemade), and we compare BASP formation results before and after more rigorous preparative high performance liquid chromatography (prep-HPLC) MM purification. In the remainder of this study, the dried MM obtained after step 1.7 is referred to as B1. Prep-HPLC was used to purify B1 to give B2. An analogous prep-HPLC purified MM synthesized in our laboratory via anionic polymerization is referred to as B3. Prep-HPLC was performed using a Beckmann Coulter HPLC (127p solvent module and 166p detector module) with a 1-ml sample loop and an Agilent Zorbax 300SB-C18 PrepHT reverse-phase column at room temperature.
<ol>
	<li>Set-up HPLC with solvent A: deionized water (Millipore purification system, 18.2 &#937;) with 1% acetic acid; solvent B: acetonitrile.</li>
	<li>Prime pumps and equilibrate column with 95% A and 5% B.</li>
	<li>Dissolve PEG-MM in acetonitrile or MeOH (150 mg/ml).</li>
	<li>Filter through a 13 mm 0.45 &#181;m Nylon syringe filter.</li>
	<li>Set HPLC method: 
	- Flow rate: 20 ml/min 
	- 0-1 min: linear gradient to 10% B and 90%A 
	- 1-10 min: linear gradient to 90% B and 10% A 
	- 10-13 min: switch to initial conditions (5% B and 95%) and re-equilibrate column 
	- Set UV detector to detect absorbance at 256 nm</li>
	<li>Load 0.8 ml of sample onto the sample loop.</li>
	<li>Inject sample.</li>
	<li>Collect the major absorbance peak (under the conditions specified, the product elutes between 5-7 min).</li>
	<li>Repeat as necessary. Combine pure fractions together in a round-bottom flask.</li>
	<li>Remove all solvent via rotary evaporation.</li>
	<li>Redissolve the product in dichloromethane and add sodium sulfate. Gently shake or stir the flask periodically for &#8773; 1 hr.</li>
	<li>Filter the mixture using a fritted glass filter.</li>
	<li>Concentrate via rotary evaporation. Dry under vacuum overnight.</li>
	<li>The PEG-MM can be characterized by 1H-NMR in CD2Cl2 (15-20 mg/0.7 ml CD2Cl2, 500 MHz or higher is recommended with over 128 scans and relaxation delay, d1 = 2.0 sec), and MALDI-TOF using positive ionization mode and 2-(4-hydroxyphenylazo)benzoic acid as the MALDI matrix.</li>
	<li>The PEG-MM can be stored for months in a scintillation vial at 4 &#176;C.</li>
</ol>
3. Preparation of Catalyst A
<ol>
	<li>Add Grubbs 2nd generation catalyst (500 mg, 0.589 mmol) to a 20 ml vial equipped with a stir bar.</li>
	<li>Add pyridine (approximately 0.474 ml, 5.89 mmol, 10 eq) to the vial. The solution color should immediately change from red to green. Allow the reaction to stir until all of the red color has disappeared and the solution has become viscous (15-30 min).</li>
	<li>Fill the reaction vial with cold pentane to precipitate complex A.</li>
	<li>Filter the suspension to collect the green precipitate (catalyst A). Wash 4x with 15 ml of cold pentane.</li>
	<li>Dry the green solid under vacuum overnight.</li>
	<li>Complex A can be stored for months at room temperature in a benchtop desiccator without significant loss of activity. For extra precaution, we typically store the complex in a -20 &#176;C freezer inside a glovebox. For convenience, we pre-weigh known amounts of A into 4 ml scintillation vials immediately after drying (step 3.5). We then store these vials in the glovebox freezer. When ready to run a ROMP reaction, we simply take one vial out of the glovebox and use as described below (step 4.4).</li>
</ol>
4. Preparation of Stock Solution of Living Brush Polymer (BI) with DP = 10
<ol>
	<li>In a 3 ml vial with a gas-tight screw cap equipped with a stir bar, weigh out 65 mg (0.020 mmol, 10 eq) of MM B. This amount corresponds to 20 mg of MM for each of the 3 different sizes of BASPs, and 5 mg leftover for GPC analysis of the BI. Use a spatula to add the MM directly to the bottom of the vial. Try to prevent material from adhering to the sides of the vial as this scenario could lead to MM contamination in the final BASP product.</li>
	<li>Dissolve the MM B in 158 &#181;l of THF. Immediately cap the vial after adding THF to avoid solvent evaporation. Note: The final concentration of MM during the polymerization should be 0.05 M. If 158 &#181;l of THF is added here, then 243 &#181;l of catalyst solution, step 4.4, will be added to give 401 &#181;l of THF total, which corresponds to [MM] = 0.05 M. The amount of solvent during this step can be varied, as long as the amount of solvent during step 4.4 is also varied to give [MM] 0.05. We have found that polymerizations carried out with [MM] &#60; 0.05 sometimes do not proceed to complete conversion.</li>
	<li>Let the solution stir until all of the MM is dissolved. Heat lightly if necessary. Avoid splattering the viscous solution onto the sides or the cap of the vial.</li>
	<li>Next, add a known amount (2.8 mg for this example) of catalyst A to a 3 ml vial (or obtain a vial with pre-weighed catalyst A). Add anhydrous THF (466 &#181;l in this example) to give a 6 mg/ml catalyst solution. Cap the vial immediately. Allow the catalyst to completely dissolve; gently shake the vial if needed. This catalyst solution should be used immediately for ROMP. Note 1: The catalyst solution should be a forest green color. If it is black, or greenish-brown, then it has likely decomposed, and it will probably not yield satisfactory ROMP results. If decomposition occurs, we suggest preparing fresh catalyst (according to section 3 above), or using freshly distilled THF. Note 2: The amount of THF added to A is chosen to ensure that the final [MM] is ~0.05. This amount can be adjusted, as long as compensatory adjustments are made to the MM solution in step 4.2.</li>
	<li>Add 243 &#181;l (1.46 mg; 1 eq to B) of the catalyst solution quickly (not dropwise) to the stirring MM solution. Try to keep the needle tip just above the MM solution when adding to the vial. Avoid splashing the reaction mixture onto the sides and cap of the vial, as splashing can lead to residual MM and BI impurity in the final BASP.</li>
	<li>Cap the vial immediately and let the reaction mixture stir for 15 min to form the brush macroinitiator (BI).</li>
</ol>
5. Formation of BASPs
<ol>
	<li>Add 3.6&#177;0.1 mg (6.18 &#181;mol, 10 eq to the amount of BI to be transferred in step 5.2), 5.5 &#177; 0.1 mg (9.28&#181;mol,15 eq to the amount of BI to be transferred in step 5.2), and 7.3&#177;0.1 mg (12.4&#181;mol,20 eq to the amount of BI to be transferred in step 5.2) of crosslinker C to three separate 3 ml vials equipped with stir bars. Try to weigh the crosslinker directly onto the bottom of the vial to prevent material from adhering to the sides of the vial. Note: Crosslinker C is not highly soluble in THF. For this reason, the solid is used directly in this step. In cases where the crosslinker is soluble, then a concentrated stock solution of crosslinker can be made and various amounts of this solution can be transferred to vials. Again, the concentration of the final polymerizations should be &#62;0.05 M; if solvent is added to the crosslinker then a compensatory reduction of solvent should be made elsewhere.</li>
	<li>Add 123 &#181;l (0.618 &#181;mol) of the BI solution to each of the three vials containing C. Try to keep the needle tip just above the solid crosslinker when adding to the vial. Add the BI solution all at once rather than dropwise.</li>
	<li>Cap the vials and stir the reactions at RT for until completion. With this specific MM and crosslinker combination, the reaction is complete in ~4 hr; continued stirring for up to 24 hr has no discernible effect on BASP growth. Monitor by GPC to ensure complete conversion of BI.</li>
	<li>Quench the reactions by adding one drop of ethyl vinyl ether to the remaining BI solution and each of the N = 10, 15, and 20 BASP reaction mixtures. Stir for 10 min to ensure complete quenching.</li>
</ol>
6. GPC Sample Preparation
The GPC-MALLS results were obtained on an Agilent 1260 LC system equipped with a Shodex GPC KD-806M column, a Wyatt Dawn Heleos-II MALLS detector, and a Wyatt Optilab t-rEX refractive index detector at room temperature. DMF with 0.025 M LiBr at a flow rate of 1.0 ml/min was used as the eluent. Results were analyzed using Astra 6 software provided by Wyatt.
<ol>
	<li>Using a new glass pipette for each reaction vial, dip the pipette tip into the reaction solution to draw up a small sample of the reaction. Wash down the inside of the pipette with 250 &#181;l of 0.025 M LiBr in DMF to give a final concentration of roughly 3 mg/ml.</li>
	<li>Filter the diluted sample through a 0.45 &#181;m polytetrafluoroethylene filter before depositing the sample into a GPC vial.</li>
	<li>Set-up GPC-MALLS runs and analyze the results once the runs are completed.</li>
</ol>
List of Abbreviations:
A: Grubbs 3rd generation bis-pyridine catalyst
B: poly(ethylene glycol) (PEG) macromonomer (MM)
B1: PEG MM prepared using commercially available (Aldrich) PEG-NH2 and used without HPLC purification.
B2: PEG MM prepared using commercially available (Aldrich) PEG-NH2 and used after HPLC purification.
B3: PEG MM prepared using newly synthesized PEG-NH2 and used after HPLC purification.
BASP: brush-arm star polymer
BI: living brush initiator
C: photodegradable crosslinker
&#208;: molar mass dispersity index
DMF: N,N-dimethylformamide
DP: number average degree polymerization
GPC: gel permeation chromatography
Prep-HPLC: preparative high performance liquid chromatography
MALLS: multi-angle laser light scattering
MM: macromonomer
MW: molecular weight
Mw: weight average molar mass
N: number of crosslinker equivalents (ratio of C to A)
NHS: N-hydroxysuccinimidyl
PEG: polyethylene glycol
PEG-MM: norbornene-PEG macromonomer (also referred to as compound B)
ROMP: ring-opening metathesis polymerization
THF: tetrahydrofuran

<ol>
	<li>Bielawski, C. W., Grubbs, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Living+ring-opening+metathesis+polymerization.">Living ring-opening metathesis polymerization.</a> Prog. Polym. Sci. 32, 1-29 (2007).</li><li>Hawker, C. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+Convergence+of+Synthetic+Organic+and+Polymer+Chemistries.">The Convergence of Synthetic Organic and Polymer Chemistries.</a> Science. 309, 1200-1205 (2005).</li><li>Peer, D., Karp, J. M., Hong, S., Farokhzad, O. C., Margalit, R., Langer, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanocarriers+as+an+emerging+platform+for+cancer+therapy.">Nanocarriers as an emerging platform for cancer therapy.</a> Nat. Nano. 2, 751-760 (2007).</li><li>Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nanoscience,+Nanotechnology,+and+Chemistry.">Nanoscience, Nanotechnology, and Chemistry.</a> Small. 1, 172-179 (2005).</li><li>Leitgeb, A., Wappel, J., Slugovc, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+ROMP+toolbox+upgraded.">The ROMP toolbox upgraded.</a> Polymer. 51, 2927-2946 (2010).</li><li>Johnson, J. A., Lu, Y. Y., Burts, A. O., Lim, Y. -. H., Finn, M. G., Koberstein, J. T., Turro, N. J., Tirrell, D. A., Grubbs, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Core-Clickable+PEG-Branch-Azide+Bivalent-Bottle-Brush+Polymers+by+ROMP:+Grafting-Through+and+Clicking-To.">Core-Clickable PEG-Branch-Azide Bivalent-Bottle-Brush Polymers by ROMP: Grafting-Through and Clicking-To.</a> J. Am. Chem. Soc. 133, 559-566 (2010).</li><li>Bielawski, C. W., Grubbs, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Highly+Efficient+Ring-Opening+Metathesis+Polymerization+(ROMP)+Using+New+Ruthenium+Catalysts+Containing+N-Heterocyclic+Carbene+Ligands.">Highly Efficient Ring-Opening Metathesis Polymerization (ROMP) Using New Ruthenium Catalysts Containing N-Heterocyclic Carbene Ligands.</a> Angew. Chem. Int. Ed. 39, 2903-2906 (2000).</li><li>Love, J. A., Morgan, J. P., Trnka, T. M., Grubbs, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Practical+and+Highly+Active+Ruthenium-Based+Catalyst+that+Effects+the+Cross+Metathesis+of+Acrylonitrile.">A Practical and Highly Active Ruthenium-Based Catalyst that Effects the Cross Metathesis of Acrylonitrile.</a> Angew. Chem. Int. Ed. 41, 4035-4037 (2002).</li><li>Lu, J. A., Johnson, Y. Y., Burts, A. O., Xia, Y., Durrell, A. C., Tirrell, D. A., Grubbs, R. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Drug-Loaded,+Bivalent-Bottle-Brush+Polymers+by+Graft-through+ROMP.">Drug-Loaded, Bivalent-Bottle-Brush Polymers by Graft-through ROMP.</a> Macromolecules. 43, 10326-10335 (2010).</li><li>Burts, A. O., Li, Y. J., Zhukhovitskiy, A. V., Patel, P. R., Grubbs, R. H., Ottaviani, M. F., Turro, N. J., Johnson, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Using+EPR+To+Compare+PEG-branch-nitroxide+"Bivalent-Brush+Polymers"+and+Traditional+PEG+Bottle-Brush+Polymers:+Branching+Makes+a+Difference.">Using EPR To Compare PEG-branch-nitroxide "Bivalent-Brush Polymers" and Traditional PEG Bottle-Brush Polymers: Branching Makes a Difference.</a> Macromolecules. 45, 8310-8318 (2012).</li><li>Bazan, G. C., Schrock, R. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+star+block+copolymers+by+controlled+ring-opening+metathesis+polymerization.">Synthesis of star block copolymers by controlled ring-opening metathesis polymerization.</a> Macromolecules. 24, 817-823 (1991).</li><li>Saunders, R. S., Cohen, R. E., Wong, S. J., Schrock, R. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+amphiphilic+star+block+copolymers+using+ring-opening+metathesis+polymerization.">Synthesis of amphiphilic star block copolymers using ring-opening metathesis polymerization.</a> Macromolecules. 25, 2055-2057 (1992).</li><li>Buchmeiser, M. R., Wurst, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Access+to+Well-Defined+Heterogeneous+Catalytic+Systems+via+Ring-Opening+Metathesis+Polymerization+(ROMP):+Applications+in+Palladium(II)-Mediated+Coupling+Reactions.">Access to Well-Defined Heterogeneous Catalytic Systems via Ring-Opening Metathesis Polymerization (ROMP): Applications in Palladium(II)-Mediated Coupling Reactions.</a> J. Am. Chem. Soc. 121, 11101-11107 (1999).</li><li>Weichelt, F., Frerich, B., Lenz, S., Tiede, S., Buchmeiser, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ring-Opening+Metathesis+Polymerization-Based+Synthesis+of+CaCO3+Nanoparticle-Reinforced+Polymeric+Monoliths+for+Tissue+Engineering.">Ring-Opening Metathesis Polymerization-Based Synthesis of CaCO3 Nanoparticle-Reinforced Polymeric Monoliths for Tissue Engineering.</a> Macromol. Rapid Comm. 31, 1540-1545 (2010).</li><li>Weichelt, F., Lenz, S., Tiede, S., Reinhardt, I., Frerich, B., Buchmeiser, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=ROMP-Derived+cyclooctene-based+monolithic+polymeric+materials+reinforced+with+inorganic+nanoparticles+for+applications+in+tissue+engineering.">ROMP-Derived cyclooctene-based monolithic polymeric materials reinforced with inorganic nanoparticles for applications in tissue engineering.</a> Beilstein J. Org. Chem. 6, 1199-1205 (2010).</li><li>Mayr, M., Mayr, B., Buchmeiser, M. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Monolithic+Materials:+New+High-Performance+Supports+for+Permanently+Immobilized+Metathesis+Catalysts.">Monolithic Materials: New High-Performance Supports for Permanently Immobilized Metathesis Catalysts.</a> Angew. Chem. Int. Ed. 40, 3839-3842 (2001).</li><li>Mayr, B. H., &#246;lzl, G., Eder, K., Buchmeiser, M. R., Huber, C. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Hydrophobic,+Pellicular,+Monolithic+Capillary+Columns+Based+on+Cross-Linked+Polynorbornene+for+Biopolymer+Separations.">Hydrophobic, Pellicular, Monolithic Capillary Columns Based on Cross-Linked Polynorbornene for Biopolymer Separations.</a> Anal. Chem. 74, 6080-6087 (2002).</li><li>Otani, H., Fujita, S., Watanabe, Y., Fujiki, M., Nomura, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+Facile,+Controlled+Synthesis+of+Soluble+Star+Polymers+Containing+a+Sugar+Residue+by+Ring-Opening+Metathesis+Polymerization+(ROMP).">A Facile, Controlled Synthesis of Soluble Star Polymers Containing a Sugar Residue by Ring-Opening Metathesis Polymerization (ROMP).</a> Macromol. Symp. 293, 53-57 (2010).</li><li>Nomura, K., Watanabe, Y., Fujita, S., Fujiki, M., Otani, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Facile+Controlled+Synthesis+of+Soluble+Star+Shape+Polymers+by+Ring-Opening+Metathesis+Polymerization+(ROMP).">Facile Controlled Synthesis of Soluble Star Shape Polymers by Ring-Opening Metathesis Polymerization (ROMP).</a> Macromolecules. 42, 899-901 (2009).</li><li>Gao, H., Ohno, S., Matyjaszewski, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Low+Polydispersity+Star+Polymers+via+Cross-Linking+Macromonomers+by+ATRP.">Low Polydispersity Star Polymers via Cross-Linking Macromonomers by ATRP.</a> J. Am. Chem. Soc. 128, 15111-15113 (2006).</li><li>Liu, J., Burts, A. O., Li, Y., Zhukhovitskiy, A. V., Ottaviani, M. F., Turro, N. J., Johnson, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term="Brush-First"+Method+for+the+Parallel+Synthesis+of+Photocleavable,+Nitroxide-Labeled+Poly(ethylene+glycol)+Star+Polymers.">"Brush-First" Method for the Parallel Synthesis of Photocleavable, Nitroxide-Labeled Poly(ethylene glycol) Star Polymers.</a> J. Am. Chem. Soc. 134, 16337-16344 (2012).</li><li>Studer, P., Larras, V., Riess, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Amino+end-functionalized+poly(ethylene+oxide)-block-poly(methylidene+malonate+2.1.2)+block+copolymers:+synthesis,+characterization,+and+chemical+modification+for+targeting+purposes.">Amino end-functionalized poly(ethylene oxide)-block-poly(methylidene malonate 2.1.2) block copolymers: synthesis, characterization, and chemical modification for targeting purposes.</a> Eur. Polym. J. 44, 1714-1721 (2008).</li><li>Mosquet, M., Chevalier, Y., Le Perchec, P., Guicquero, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+of+poly+(ethylene+oxide)+with+a+terminal+amino+group+by+anionic+polymerization+of+ethylene+oxide+initiated+by+aminoalcoholates.">Synthesis of poly (ethylene oxide) with a terminal amino group by anionic polymerization of ethylene oxide initiated by aminoalcoholates.</a> Macromol. Chem. Phys. 198, 2457-2474 (1997).</li><li>Burchard, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Solution+properties+of+branched+macromolecules.">Solution properties of branched macromolecules.</a> Adv. Polym. Sci. 143, 113-194 (1999).</li><li>Gao, H. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Development+of+Star+Polymers+as+Unimolecular+Containers+for+Nanomaterials.">Development of Star Polymers as Unimolecular Containers for Nanomaterials.</a> Macromol. Rapid Comm. , 722-734 (2012).</li><li>Blencowe, A., Tan, J. F., Goh, T. K., Qiao, G. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Core+cross-linked+star+polymers+via+controlled+radical+polymerisation.">Core cross-linked star polymers via controlled radical polymerisation.</a> Polymer. 50, 5-32 (2009).</li><li>Burts, A. O., Liao, L., Lu, Y. Y., Tirrell, D. A., Johnson, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Brush-first+and+Click:+Efficient+Synthesis+of+Nanoparticles+that+Degrade+and+Release+Doxorubicin+in+Response+to+Light.">Brush-first and Click: Efficient Synthesis of Nanoparticles that Degrade and Release Doxorubicin in Response to Light.</a> Photochem. Photobiol. , (2013).</li></ol>

The authors have nothing to disclose.

The key advantage of brush-first BASP synthesis is the unique ability to rapidly synthesize nanostructures of diverse size and composition in parallel without need for specialized equipment. In this study, we demonstrate the brush-first synthetic method using a norbornene functionalized PEG macromonomer (B, Figure 1) and a bis-norbornene nitrobenzyl ester crosslinker (C, Figure 1). The PEG chains from B impart ...

Polymeric nanoparticles have been widely studied for their potential use as platforms for drug delivery, supported catalysis, biological imaging, and self-assembly1-3. Modern applications require that nanoparticle syntheses be facile, reproducible, compatible with chemical functionalities, and amenable to diversification4,5. Ring-opening metathesis polymerization (ROMP) of strained olefins is a powerful methodology for the synthesis of functional polymeric nanostructures with controlled sizes and narrow mass distributions1,6-8. For example, norbornene-functionalized poly(ethylene glycol) (PEG) macromonomers (MMs) can be efficiently polymerized via ROMP to generate water soluble bottle-brush polymers. Using this approach, nanostructures that carry multiple releasable drug molecules, fluorophores, and spin-contrast agents can be prepared rapidly and in parallel6,9,10.
ROMP has also been used for the &#34;arm-first&#34; synthesis of star polymers. In the arm-first method, linear polymers are crosslinked with a multi-functional crosslinker to give spherical nanostructures with polymeric arms. Schrock and co-workers reported the first arm-first ROMP synthesis of star polymers via crosslinking of norbornene, dicarbomethoxynorbornadiene, and trimethylsilyl protected dicarboxynorbornene linear polymers with a bifunctional norbornene crosslinker.11,12 Buchmeiser has extended this methodology for the synthesis of materials with a range of applications that include supported catalysis, tissue-engineering, and chromatography13-17. Otani and coworkers have made star polymer nanoparticles with functional surfaces via a related &#34;in-out&#34; polymerization strategy18,19.
Most arm-first polymerizations involve a complex interplay of monomer, polymer, and star coupling reactions. The latter proceeds via a step-growth mechanism that typically leads to broad molecular weight (MW) distributions. To overcome this limitation in related arm-first atom transfer radical polymerization reactions, Matyjaszewski and coworkers performed arm-first crosslinking of preformed polymeric MMs to provide star polymers with very narrow MW distributions20. In this case, the steric bulk of the MMs, and the increased ratio of star arms to initiation sites, inhibited poorly controlled star+star coupling processes, and led to a living, chain growth mechanism.
When we attempted the same strategy in the context of ROMP with a norbornene-terminated PEG-MM and a bis-norbornene crosslinker, star polymers with very broad, multi-modal MW distributions were obtained. This result suggested that in this system the MM alone was not sufficiently bulky to inhibit star+star coupling. To increase the steric bulk of the star arms, and potentially limit this uncontrolled coupling, we attempted to first polymerize the MM to form bottle-brush polymers in the absence of crosslinker and then add the crosslinker. We were pleased to find that under certain conditions, this &#34;brush-first&#34; method provided straightforward access to &#34;brush-arm star polymers&#34; (BASPs) with narrow MW distributions and tunable core and corona functionalities.
We recently reported the brush-first ROMP synthesis of PEG BASPs using Grubbs 3rd generation catalyst A (Figure 1)21. In this work, exposure of PEG-MM B to catalyst A generated a living brush macroinitiator with defined backbone length (B1, Figure 1). Transfer of aliquots of the B1&#160;to vials that contained different amounts of crosslinker C initiated BASP formation. The MW, and therefore the size, of the BASPs increased geometrically with the amount of C added. We provided a mechanistic hypothesis for this geometric growth process and demonstrated that functional, nitroxide core- and corona-labeled BASPs could be readily prepared without the need for post-polymerization modification steps or sequential monomer additions. However, in all of the reported examples, we were concerned about catalyst deactivation; we carried out all reactions under N2 atmosphere inside a glovebox.
Since our initial report, we have found that the brush-first method is very effective for the formation of BASPs from a wide range of norbornene-terminated MMs and functional crosslinkers. We have also discovered that the method can be performed on the benchtop with no special precautions to remove air or moisture.
Herein, a series of three BASPs of differing MWs will be synthesized by the brush-first method under ambient conditions. In brief, 10 equivalents of B will be exposed to 1.0 equivalents of catalyst A (Figure 1a) for 15 min to yield a BI with an average degree of polymerization (DP) of 10. Three aliquots of this batch of BI will be transferred to separate vials that contain 10, 15, and 20 equivalents (N, Figure 1b) of C. After 4 hr, the polymerizations will be quenched via addition of ethyl vinyl ether. The star polymer MWs and MW distributions will be characterized using a gel permeation chromatography instrument equipped with a multi-angle laser light scattering detector (GPC-MALLS).

<table border="0" cellpadding="0" cellspacing="0" width="592">
	<colgroup>
		<col />
		<col />
		<col />
		<col />
	</colgroup>
	<tbody>
		<tr height="42">
			<td height="84" rowspan="2" style="height:84px;width:216px;">Grubbs Second Generation Catalyst</td>
			<td rowspan="2" style="width:91px;">Materia (or Sigma Aldrich)</td>
			<td rowspan="2" style="width:119px;">C848 (Sigma Aldrich: 569747)</td>
			<td style="width:167px;">
			Used as purchased from manufacturer. 
 *Provided as a generous gift.
			</td>
		</tr>
		<tr height="42">
			<td></td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Pyridine</td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">270970</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">O-(2-aminoethyl)polyethylene glycol 3000</td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">07969</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">PEG-MM</td>
			<td style="width:91px;">N/A</td>
			<td style="width:119px;">N/A</td>
			<td style="width:167px;">Synthesized following reported procedures (Ref. 21, protocol 1)</td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">norbornene-N-hydroxysuccinimidyl (NHS) ester</td>
			<td style="width:91px;">N/A</td>
			<td style="width:119px;">N/A</td>
			<td style="width:167px;">Synthesized following reported procedures (Ref. 21)</td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">Bis-norb-NBOC Crosslinker</td>
			<td style="width:91px;">N/A</td>
			<td style="width:119px;">N/A</td>
			<td style="width:167px;">Synthesized following reported procedures (Ref. 21)</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Pentane</td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">158941</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">Tetrahydrofuran (HPLC grade)</td>
			<td style="width:91px;">Sigma Aldrich </td>
			<td style="width:119px;">34865</td>
			<td style="width:167px;">Dried and purified over a solvent purification columns </td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Dichloromethane</td>
			<td style="width:91px;">VWR </td>
			<td>BDH1113-4LG</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Acetonitrile (HPLC grade)</td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">34998</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Acetic Acid </td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">A6283</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Sodium sulfate </td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td>239313</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Diethyl ether</td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">673811</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Dimethylformamide (HPLC grade) </td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">270547</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Lithium Bromide</td>
			<td style="width:91px;">Sigma Aldrich</td>
			<td style="width:119px;">213225</td>
			<td style="width:167px;">Used as purchased from manufacturer</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">MillQ Biocel A10</td>
			<td style="width:91px;">Millipore</td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Beckmann Coulter HPLC (127p solvent module, 166p detector)</td>
			<td style="width:91px;">Beckmann Coulter</td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Zorbax 300SB-C18 PrepHT reverse phase column </td>
			<td style="width:91px;">Agilent</td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">1260 Infinity Liquid Chromatography </td>
			<td style="width:91px;">Agilent</td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">GPC KD-806M column</td>
			<td style="width:91px;">Shodex</td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Dawn Heleos II Light Scatterer</td>
			<td style="width:91px;">Wyatt</td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Optilab T-rEX Refractive Index Detector</td>
			<td style="width:91px;">Wyatt</td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Glass Scintillation Vials - 40 ml</td>
			<td style="width:91px;">Chemglass</td>
			<td>CG-4909-05</td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Glass Scintillation Vials - 4 ml </td>
			<td style="width:91px;">Chemglass</td>
			<td style="width:119px;">CG-4904-06</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Glass Scintillation Vials (PTFE-lined cap) - 2 ml </td>
			<td style="width:91px;">Agilent</td>
			<td>5183-4518</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Stir-bars</td>
			<td style="width:91px;">VWR</td>
			<td style="width:119px;">5894x</td>
			<td style="width:167px;">various sizes </td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">13 mm 0.45 &#181;m Nylon Syringe filter</td>
			<td style="width:91px;">PerkinElmer</td>
			<td>02542903</td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">13 mm 0.45 &#181;m polytetrafluoroethylene syringe filter</td>
			<td style="width:91px;">PerkinElmer</td>
			<td>02542909</td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">1 ml disposable syringes </td>
			<td style="width:91px;">VWR</td>
			<td style="width:119px;">53548-001</td>
			<td></td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">Swing bucket centrifuge or similar</td>
			<td style="width:91px;"> </td>
			<td style="width:119px;"> </td>
			<td style="width:167px;">Should be able to reach approximately 4,000 rpm</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Round bottom flask</td>
			<td style="width:91px;"> </td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Fritted glass filter assembly </td>
			<td style="width:91px;"> </td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Rotary Evaporator </td>
			<td style="width:91px;"> </td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Balance </td>
			<td style="width:91px;"> </td>
			<td style="width:119px;"> </td>
			<td style="width:167px;"> </td>
		</tr>
	</tbody>
</table>

particles without a box: brush-first synthesis of photodegradable peg star polymers under ambient conditions

Convenient methods for the rapid, parallel synthesis of diversely functionalized nanoparticles will enable discovery of novel formulations for drug delivery, biological imaging, and supported catalysis. In this report, we demonstrate parallel synthesis of brush-arm star polymer (BASP) nanoparticles by the &#34;brush-first&#34; method. In this method, a norbornene-terminated poly(ethylene glycol) (PEG) macromonomer (PEG-MM) is first polymerized via ring-opening metathesis polymerization (ROMP) to generate a living brush macroinitiator. Aliquots of this initiator stock solution are added to vials that contain varied amounts of a photodegradable bis-norbornene crosslinker. Exposure to crosslinker initiates a series of kinetically-controlled brush+brush and star+star coupling reactions that ultimately yields BASPs with cores comprised of the crosslinker and coronas comprised of PEG. The final BASP size depends on the amount of crosslinker added. We carry out the synthesis of three BASPs on the benchtop with no special precautions to remove air and moisture. The samples are characterized by gel permeation chromatography (GPC); results agreed closely with our previous report that utilized inert (glovebox) conditions. Key practical features, advantages, and potential disadvantages of the brush-first method are discussed.

Figure 2 shows GPC traces for a variety of BASPs prepared from B1, B2, and B3. In all cases, the data illustrate that increasing the equivalents of crosslinker (N) leads to an increase in the size of the BASP. As was observed in our previous report, 10 equivalents of crosslinker is not sufficient to achieve uniform BASPs; the N = 10 sample shows a clearly multi-modal GPC trace with a large amount of residual b...

Watch this Scientific Journal Video about Particles without a Box: Brush-first Synthesis of Photodegradable PEG Star Polymers under Ambient Conditions at JoVE.com

Particles without a Box: Brush-first Synthesis of Photodegradable PEG Star Polymers under Ambient Conditions

Poly(ethylene glycol) (PEG) brush-arm star polymers (BASPs) with narrow mass distributions and tunable nanoscopic sizes are synthesized in via ring opening metathesis polymerization (ROMP) of a PEG-norbornene macromonomer followed by transfer of portions of the resulting living brush initiator to vials containing varied amounts of a rigid, photo-cleavable bis-norbornene crosslinker.

Convenient methods for the rapid, parallel synthesis of diversely functionalized nanoparticles will enable discovery of novel formulations for drug ...

particles-without-box-brush-first-synthesis-photodegradable-peg-star

Research

JoVE Journal

Chemistry

39.6K Views.  Massachusetts Institute of Technology. Poly(ethylene glycol) (PEG) brush-arm star polymers (BASPs) with narrow mass distributions and tunable nanoscopic sizes are synthesized in via ring opening metathesis polymerization (ROMP) of a PEG-norbornene macromonomer followed by transfer of portions of the resulting living brush initiator to vials containing varied amounts of a rigid, photo-cleavable bis-norbornene crosslinker.