Name: easy manipulation of architectures in protein-based hydrogels for cell culture applications
Uploaded: 2017-08-04T11:00:00.000+00:00
Duration: 8 min 50 s
Description: Watch this Scientific Journal Video about Easy Manipulation of Architectures in Protein-based Hydrogels for Cell Culture Applications at JoVE.com

The authors would like to thank Baden-W&#252;rttemberg Stiftung for their financial support in the "Bioinspired Material Synthesis" framework (BioMatS-14).

1. Hydrogel Preparation
<ol>
	<li>Mix 200 mg of BSA with 1 mL of deionized H2O to create 20% (w/v) BSA stock (stock solution A).</li>
	<li>Mix 165 &#181;L of THPC solution (134 mg/mL) with 4.835 mL of deionized water to create THPC stock solution (stock solution B).</li>
	<li>Weigh 1 mg of KCSSGKSRGDS (1,111.1 g/mol) peptide (or an equivalent cell-adhesive peptide) and dilute it in 100 &#181;L of sterile H2O to obtain a 10 mg/mL solution (stock solution C). 
	NOTE: This step is optional and only needs to be included if the hydrogel is meant for cell culture application.</li>
	<li>Remove the bottom of a 96-well plate and replace it with removable plastic wrap. 
	NOTE: For the plates used here, the bottom can easily be removed by applying pressure to the bottom of each well; the thin plastic bottom will simply fall out.</li>
	<li>Mix 100 &#181;L of BSA stock solution (A) and 100 &#181;L of THPC stock solution (B) (optional: 4 &#181;L of stock solution C for functionalized, cell-adhesive hydrogels) in the 96-well plate to obtain 200 &#181;L of hydrogel. Mix the components by pipetting up and down at least 5 times to guarantee a uniform hydrogel after polymerization.</li>
	<li>Place the 96-well plate at room temperature (RT) for about 10 min until all hydrogels are properly polymerized.</li>
	<li>Carefully and slowly remove the plastic wrap from the bottom of the plate.</li>
	<li>Press the hydrogels out of the 96-well plate using a small stamp and transfer them to 1.5 mL tubes with sterile PBS, pH 7.4. 
	NOTE: The hydrogels have a cylindrical shape, with a diameter of approximately 4 mm and a height of 8 mm.</li>
	<li>Store the hydrogels in phosphate-buffered saline (PBS) at 4 &#176;C for up to several months.</li>
</ol>
2. Freeze-drying the Hydrogels
<ol>
	<li>Fill 1.5 mL tubes with 500 &#181;L of sterile deionized H2O and remove the cap. Transfer the hydrogels to the 1.5 mL reaction tubes using a spatula.</li>
	<li>Wrap the 1.5 mL tubes tightly with paraffin film-at least three layers for each vial. Use a needle to pierce small holes in the film to enable gas release from the tube.</li>
	<li>Proceed to one of the following steps:
	<ol>
		<li>Transfer the vial to liquid nitrogen solution for 5 min to guarantee that the water and hydrogel completely freeze. Immediately after removal from the liquid nitrogen, transfer the vials to the freeze dryer to prevent the material from thawing. 
		NOTE: This procedure results in pores about 10-15 &#181;m in radius.</li>
		<li>Keep the vials at -20 &#176;C overnight to slowly freeze the hydrogels. Immediately after removal from -20 &#176;C, transfer the vials to the freeze dryer to prevent the material from thawing. 
		NOTE: This procedure results in pores about 50-60 &#181;m in radius.</li>
	</ol>
	</li>
	<li>After 24 h (and the complete evaporation of the water in and around the hydrogel), thaw the material by removing it from the freeze dryer. 
	NOTE: The pore sizes can be analyzed with confocal laser scanning microscopy (step 5, &#34;Hydrogel Visualization&#34;).</li>
</ol>
3. Particle Leaching
<ol>
	<li>Prepare the hydrogel as described in steps 1.1-1.5.</li>
	<li>Directly after mixing the components, add NaCl until saturation occurs (36 mg/mL). Add salt until a salt crystal can be seen in the solution as a white precipitate.</li>
	<li>Transfer the 96-well plate to a shaker and shake until polymerization takes place (about 10 min). Remove the hydrogels from the plate, as described in steps 1.7-1.8.</li>
	<li>Incubate the hydrogels for at least 24 h at RT in sterile water on a shaker (20 rpm) to elute all salt from the hydrogel template. Store the hydrogels at 4 &#176;C in PBS for up to several months.</li>
</ol>
4. Channel Formation
<ol>
	<li>Prepare hydrogels as described in step 1. Remove a hydrogel from solution using a pincer, remove the excess water with highly absorbent paper, and place it on top of a block of dry ice.</li>
	<li>Freeze the hydrogel for 30 s and carefully remove it from the block. Do not damage the hydrogel; carefully use a spatula to scrape it off the block. Transfer the hydrogel to a 1.5 mL tube and dry it overnight at 37 &#176;C.</li>
</ol>
5. Hydrogel Visualization
<ol>
	<li>Prepare a rhodamine B stock solution by diluting 1 mg of rhodamine B in 10 mL of PBS. Prepare a serial dilution by diluting the rhodamine stock solution in PBS until a concentration of 0.001 mg/mL is reached (dilution factor: 100)</li>
	<li>Remove the hydrogel from the storage solution (e.g., from step 2.4.) and transfer it to a 1.5 mL tube with 1 mL of 0.01 mg/mL rhodamine B solution. Stain the hydrogel overnight in rhodamine B solution at RT.</li>
	<li>The next day, transfer the hydrogel that is to be visualized to 10 mL of PBS (pH 7.4) and wash for at least 3 h.</li>
	<li>Transfer the hydrogel onto a &#181;-slide 8 well and cover it with PBS.</li>
	<li>Cut small slices out of the hydrogel (about 0.5 mm in height) using a blade.</li>
	<li>Using a confocal laser scanning microscope, visualize the hydrogel at a wavelength of 514 nm (objective: EC Plan-Neofluar 40x/1.30 Oil DIC M27, plane scan mode: 514 nm, and zoom: 1X).</li>
</ol>
6. Cell Culture Feasibility
<ol>
	<li>Sterile-filter all stock solutions (A, B, and C) with a 0.45 &#181;m filter.</li>
	<li>Prepare the hydrogel as described in steps 1.1-1.4, including the cell-adhesive peptide prior to hydrogel polymerization.</li>
	<li>After mixing the components, immediately pipette the mixture into a &#181;-slide 8 well until the bottom is completely covered. 
	NOTE: This step must be performed quickly and directly after mixing the components, as polymerization takes place within minutes in the slide.</li>
	<li>Culture adhesion cells and passage to obtain a single-cell suspension using standard cell culture techniques. Transfer the cells into pre-warmed, sterile DMEM cell culture medium supplemented with fetal bovine serum (FBS, 10% (w/v)), penicillin-streptomycin (1% (w/v)), and nonessential amino acid solution (MEM, 1% (w/v)).</li>
	<li>Count the cells with a Neubauer counting chamber and carefully pipette 200 &#181;L of the desired number of cells (2 x 105 cells/cm2) onto the hydrogel surface.</li>
	<li>Cover the &#181;-slide 8 well with the lid and transfer it to an incubator (37 &#176;C, 5% CO2). Incubate for at least 4 h at 37 &#176;C.</li>
	<li>After at least 4 h of cellular attachment, wash the cells twice with 200 &#181;L of sterile cell culture PBS.</li>
	<li>Fix the cells with 200 &#181;L of 3.7% (v/v) formaldehyde for 10 min at RT and wash twice with PBS (~200 &#181;L). 
	NOTE: Wear appropriate personal protective equipment when handling formaldehyde.</li>
	<li>Permeabilize the cells with 200 &#181;L of 0.1 % Triton X for 5 min. Wash twice with PBS.</li>
	<li>Stain the cells with phalloidin-rhodamine by mixing 5 &#181;L of methanolic stock with 195 &#181;L of PBS and adding it to the cells at RT. Stain the cells for 20 min in the dark. Wash twice with PBS.</li>
	<li>Investigate the cell adhesion properties using a confocal microscope at 514 nm (objective: EC Plan-Neofluar 40x/1.30 Oil DIC M27, plane scan mode: 514 nm, and zoom: 1X). Analyze the images using appropriate software (see the Table of Materials).</li>
</ol>
7. Hydrogel Properties
<ol>
	<li>Swelling ratio.
	<ol>
		<li>Completely dry the hydrogels at 37 &#176;C for at least one day.</li>
		<li>Weigh each hydrogel and note the exact weight.</li>
		<li>Fill a 2 mL reaction tube with 1.5 mL of PBS.</li>
		<li>Transfer the hydrogel into this 2 mL reaction tube and completely immerse it in PBS.</li>
		<li>Leave the hydrogel for at least two days in PBS at RT to reach equilibrium with the PBS.</li>
		<li>After three days, remove the hydrogel from the solution and dry it with a paper tissue to remove excess water from the hydrogel surface.</li>
		<li>Weigh the hydrogel.</li>
		<li>Calculate the swelling ratio using the following formula: 
		<img alt="Equation" src="/files/ftp_upload/55813/55813eq1.jpg" /> 
		where Wd is the weight of the dried gel (step 7.1.2.) and Ws is the weight of the wet gel (step 7.1.7). Multiply with 100 to get the swelling ratio percent.</li>
	</ol>
	</li>
	<li>pH and temperature stability.
	<ol>
		<li>Transfer 5 mL of PBS to a 15-mL reaction tube.</li>
		<li>Adjust the solution to the appropriate pH (e.g., pH 2, 7, or 10) with NaOH and HCl. Bring the solution to the appropriate temperature (e.g., RT, 37 &#176;C, or 80 &#176;C).</li>
		<li>Transfer the hydrogel that is to be investigated for its stability into the appropriate solution. Readjust the pH if necessary. 
		NOTE: All hydrogels should be completely swollen at this point (see the swelling ratio) to prevent the incorrect interpretation of the weight due to the swelling of the material.</li>
		<li>After certain time intervals, remove the hydrogel from the solution (e.g., each hour for up to 2 days), dry it with a highly absorbent paper tissue to remove excess water, and weigh it.</li>
	</ol>
	</li>
	<li>Enzymatic degradation.
	<ol>
		<li>Prepare a stock enzyme solution of 300 U trypsin and pepsin, as per the manufacturer&#39;s instructions.</li>
		<li>Transfer the hydrogel (e.g., from step 1.8) to the appropriate solution. 
		NOTE: All hydrogels should be completely swollen at this point to prevent the incorrect interpretation of the weight.</li>
		<li>After certain time intervals, remove the hydrogel from the solution (e.g., each hour), dry it with a highly absorbent paper tissue to remove excess water, and weigh it.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Geckil, H., Xu, F., Zhang, X., Moon, S., Demirki, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Engineering+hydrogels+as+extracellular+matrix+mimics.">Engineering hydrogels as extracellular matrix mimics.</a> Nanomedicine. 5 (3), 469-484 (2011).</li><li>Liu, Y., Chan-Park, M. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+biomimetic+hydrogel+based+on+methacrylated+dextran-graft-lysine+and+gelatin+for+3D+smooth+muscle+cell+culture.">A biomimetic hydrogel based on methacrylated dextran-graft-lysine and gelatin for 3D smooth muscle cell culture.</a> Biomaterials. 31 (6), 1158-1170 (2010).</li><li>Raic, A., R&#246;dling, L., Kalbacher, H., Lee-Thedieck, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Biomimetic+macroporous+PEG+hydrogels+as+3D+scaffolds+for+the+multiplication+of+human+hematopoietic+stem+and+progenitor+cells.">Biomimetic macroporous PEG hydrogels as 3D scaffolds for the multiplication of human hematopoietic stem and progenitor cells.</a> Biomaterials. 35 (3), 929-940 (2014).</li><li>Wong Po Foo, C. T. S., Lee, J. S., Mulyasasmita, W., Parisi-Amon, A., Heilshorn, S. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Two-component+protein-engineered+physical+hydrogels+for+cell+encapsulation.">Two-component protein-engineered physical hydrogels for cell encapsulation.</a> Proc Nat Acad Sci USA. 106 (52), 22067-22072 (2009).</li><li>Zhu, J., Marchant, R. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Design+properties+of+hydrogel+tissue-engineering+scaffolds.">Design properties of hydrogel tissue-engineering scaffolds.</a> Expert Rev Med Devic. 8 (5), 607-626 (2011).</li><li>Samaryk, V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Versatile+Approach+to+Develop+Porous+Hydrogels+with+a+Regular+Pore+Distribution+and+Investigation+of+their+Physicomechanical+Properties.">Versatile Approach to Develop Porous Hydrogels with a Regular Pore Distribution and Investigation of their Physicomechanical Properties.</a> J Appl Polym Sci. 114 (4), 2204-2212 (2009).</li><li>Li, X. J., Valadez, A. V., Zuo, P., Nie, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microfluidic+3D+cell+culture:+potential+application+for+tissue-based+bioassays.">Microfluidic 3D cell culture: potential application for tissue-based bioassays.</a> Bioanalysis. 4 (12), 1509-1525 (2012).</li><li>Park, H., Guo, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+Swelling+Ratio+of+Injectable+Hydrogel+Composites+on+Chondrogenic+Differentiation+of+Encapsulated+Rabbit+Marrow+Mesenchymal+Stem+Cells+In+Vitro.">Effect of Swelling Ratio of Injectable Hydrogel Composites on Chondrogenic Differentiation of Encapsulated Rabbit Marrow Mesenchymal Stem Cells In Vitro.</a> Biomacromolecules. 10 (3), 541-546 (2010).</li><li>Stokols, S., Tuszynski, M. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+fabrication+and+characterization+of+linearly+oriented+nerve+guidance+scaffolds+for+spinal+cord+injury.">The fabrication and characterization of linearly oriented nerve guidance scaffolds for spinal cord injury.</a> Biomaterials. 25 (27), 5839-5846 (2004).</li><li>Sung, K. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Understanding+the+Impact+of+2D+and+3D+Fibroblast+Cultures+on+In+Vitro+Breast+Cancer+Models.">Understanding the Impact of 2D and 3D Fibroblast Cultures on In Vitro Breast Cancer Models.</a> PLoS One. 8 (10), 1-13 (2013).</li><li>Tsai, E. C., Dalton, P. D., Shoichet, M. S., Tator, C. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthetic+hydrogel+guidance+channels+facilitate+regeneration+of+adult+rat+brainstem+motor+axons+after+complete+spinal+cord+transection.">Synthetic hydrogel guidance channels facilitate regeneration of adult rat brainstem motor axons after complete spinal cord transection.</a> J Neurotrauma. 21 (6), 789-804 (2004).</li><li>Shoichet, M. S., Li, R. H., White, M. L., Winn, S. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Stability+of+hydrogels+used+in+cell+encapsulation:+An+in+vitro+comparison+of+alginate+and+agarose.">Stability of hydrogels used in cell encapsulation: An in vitro comparison of alginate and agarose.</a> Biotechnol Bioeng. 50 (4), 374-381 (1996).</li><li>Chiu, Y. -. C., Kocag&#246;z, S., Larson, J. C., Brey, E. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Evaluation+of+physical+and+mechanical+properties+of+porous+poly+(ethylene+glycol)-co-(L-lactic+acid)+hydrogels+during+degradation.">Evaluation of physical and mechanical properties of porous poly (ethylene glycol)-co-(L-lactic acid) hydrogels during degradation.</a> PloS One. 8 (4), e60728 (2013).</li><li>Jonker, A. M., L&#246;wik, D. W. P. M., van Hest, J. C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Peptide-+and+Protein-Based+Hydrogels.">Peptide- and Protein-Based Hydrogels.</a> Chem Mater. 24 (5), 759-766 (2012).</li><li>Bodenberger, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Beyond+bread+and+beer:+whole+cell+protein+extracts+from+baker's+yeast+as+a+bulk+source+for+3D+cell+culture+matrices.">Beyond bread and beer: whole cell protein extracts from baker's yeast as a bulk source for 3D cell culture matrices.</a> Appl Microbiol Biot. 101 (5), 1-11 (2016).</li><li>Bodenberger, N., Paul, P., Kubiczek, D., Walther, P., Gottschalk, K. E., Rosenau, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+novel+cheap+and+easy+to+handle+protein+hydrogel+for+3D+cell+culture+applications+a+high+stability+matrix+with+tunable+elasticity+and+cell+adhesion+properties.">A novel cheap and easy to handle protein hydrogel for 3D cell culture applications a high stability matrix with tunable elasticity and cell adhesion properties.</a> Chem Sel. 1 (7), 1353-1360 (2016).</li><li>Agarwal, S., Wendorff, J. H., Greiner, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Use+of+electrospinning+technique+for+biomedical+applications.">Use of electrospinning technique for biomedical applications.</a> Polymer. 49 (26), 5603-5621 (2008).</li><li>Hong, J., deMello, A. J., Jayasinghe, S. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Bio-electrospraying+and+droplet-based+microfluidics:+control+of+cell+numbers+within+living+residues.">Bio-electrospraying and droplet-based microfluidics: control of cell numbers within living residues.</a> Biome Mater. 5 (2), 21001 (2010).</li><li>Jayasinghe, S. N., Irvine, S., McEwan, J. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cell+electrospinning+highly+concentrated+cellular+suspensions+containing+primary+living+organisms+into+cell-bearing+threads+and+scaffolds.">Cell electrospinning highly concentrated cellular suspensions containing primary living organisms into cell-bearing threads and scaffolds.</a> Nanomedicine. 2 (4), 555-567 (2007).</li><li>Selimovi&#263;, &. #. 3. 5. 2. ;., Oh, J., Bae, H., Dokmeci, M., Khademhosseini, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microscale+strategies+for+generating+cell-encapsulating+hydrogels.">Microscale strategies for generating cell-encapsulating hydrogels.</a> Polymers. 4 (3), 1554-1579 (2012).</li><li>Annabi, N., Nichol, J. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Controlling+the+porosity+and+microarchitecture+of+hydrogels+for+tissue+engineering.">Controlling the porosity and microarchitecture of hydrogels for tissue engineering.</a> Tissue Eng Part B Rev. 16 (4), 371-383 (2010).</li><li>Lee, J., Cuddihy, M. J., Kotov, N. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Three-dimensional+cell+culture+matrices:+state+of+the+art.">Three-dimensional cell culture matrices: state of the art.</a> Tissue Eng Part B Rev. 14 (1), 61-86 (2008).</li><li>Bodenberger, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Evaluation+of+methods+for+pore+generation+and+their+influence+on+physio-chemical+properties+of+a+protein+based+hydroge.">Evaluation of methods for pore generation and their influence on physio-chemical properties of a protein based hydroge.</a> Biotech Rep. 12, 6-12 (2016).</li><li>Raja, S. T. K., Thiruselvi, T., Mandal, A. B., Gnanamani, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=pH+and+redox+sensitive+albumin+hydrogel:+A+self-derived+biomaterial.">pH and redox sensitive albumin hydrogel: A self-derived biomaterial.</a> Sci Rep. 5, 15977 (2015).</li><li>Hennink, W. E., van Nostrum, C. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Novel+crosslinking+methods+to+design+hydrogels.">Novel crosslinking methods to design hydrogels.</a> Adv Drug Deliver Rev. 64, 223-236 (2012).</li><li>Chung, C., Lampe, K. J., Heilshorn, S. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tetrakis(hydroxymethyl)+phosphonium+chloride+as+a+covalent+cross-linking+agent+for+cell+encapsulation+within+protein-based+hydrogels.">Tetrakis(hydroxymethyl) phosphonium chloride as a covalent cross-linking agent for cell encapsulation within protein-based hydrogels.</a> Biomacromolecules. 13 (12), 3912-3916 (2008).</li><li>Cal&#243;, E., Khutoryanskiy, V. V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Biomedical+applications+of+hydrogels:+A+review+of+patents+and+commercial+products.">Biomedical applications of hydrogels: A review of patents and commercial products.</a> Eur Polym J. 65, 252-267 (2015).</li><li>Huang, H., Herrera, A. I., Luo, Z., Prakash, O., Sun, X. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Structural+transformation+and+physical+properties+of+a+hydrogel-forming+peptide+studied+by+NMR,+transmission+electron+microscopy,+and+dynamic+rheometer.">Structural transformation and physical properties of a hydrogel-forming peptide studied by NMR, transmission electron microscopy, and dynamic rheometer.</a> Biophys J. 103 (5), 979-988 (2012).</li><li>Draghi, L., Resta, S., Pirozzolo, M. G., Tanzi, M. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microspheres+leaching+for+scaffold+porosity+control.">Microspheres leaching for scaffold porosity control.</a> J Mater Sci. 16 (12), 1093-1097 (2005).</li><li>Whang, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Engineering+Bone+Regeneration+with+Bioabsorbable+Scaffolds+with+Novel+Microarchitecture.">Engineering Bone Regeneration with Bioabsorbable Scaffolds with Novel Microarchitecture.</a> Tissue Eng. 5 (1), 35-51 (1999).</li><li>Ziv, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+tunable+silk-alginate+hydrogel+scaffold+for+stem+cell+culture+and+transplantation.">A tunable silk-alginate hydrogel scaffold for stem cell culture and transplantation.</a> Biomaterials. 35 (12), 3736-3743 (2014).</li><li>Butruk-Raszeja, B. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Athrombogenic+hydrogel+coatings+for+medical+devices--Examination+of+biological+properties.">Athrombogenic hydrogel coatings for medical devices--Examination of biological properties.</a> Colloid Surface B. 130, 192-198 (2015).</li><li>L&#252;, S., Li, B., Ni, B., Sun, Z., Liu, M., Wang, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Thermoresponsive+injectable+hydrogel+for+three-dimensional+cell+culture:+chondroitin+sulfate+bioconjugated+with+poly(N-isopropylacrylamide)+synthesized+by+RAFT+polymerization.">Thermoresponsive injectable hydrogel for three-dimensional cell culture: chondroitin sulfate bioconjugated with poly(N-isopropylacrylamide) synthesized by RAFT polymerization.</a> Soft Matter. 7 (22), 10763 (2011).</li><li>Ruoslahti, E., Pierschbacher, M. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=New+perspectives+in+cell+adhesion:+RGD+and+integrins.">New perspectives in cell adhesion: RGD and integrins.</a> Science. 238 (4826), 491-497 (1987).</li></ol>

The authors declare that they have no competing financial interests.

The production of macroporous matrices can be beneficial to many different fields. It has high technical and economic potential due to the defined structure of the hydrogel and the ability to control and tune specific material properties. However, the introduction of supramolecular structural elements, such as pores or channels, to a 3D template might influence the overall properties of a material, such as the swelling ratio or the stiffness. This can result in the undesired decomposition, degradation, or breakdown of th...

Hydrogels are materials that form insoluble 3D networks capable of binding large amounts of water. Such materials can provide excellent environmental conditions for living cells. Currently, there is increasing interest in the generation of three-dimensional hydrogel structures and in the development of processes to tailor their chemical and physical properties. Once this is achieved, a template for the growth of cells and the manipulation of cellular behavior can be generated1,2,3,4. These 3D structures not only create a more natural and realistic environment than conventional two-dimensional approaches, but they also reveal new possibilities for the growth of stem cells or tumor models5. Different materials possess a range of characteristics that mainly depend upon the pore size of the gel6. The pores play a crucial role in cell culture applications, tissue engineering, and the directed growth of stem cells. For example, oxygen and nutrients diffuse through the matrix, and adequate amounts must be able to reach the cells7. On the other hand, harmful metabolites must be removed as quickly as possible, and sufficient space for cell growth must be available7. Consequently, the properties of the material, and thus the pore size, severely influence the potential benefit and possible applications of the matrix. Depending upon the properties of the material, different cell-growth processes can occur in 3D cell culture, including the formation of neuronal structures; the growth and differentiation of skin or bone cells; and the directed growth of special stem cell lines, like hepatocytes or fibroblasts2,3,8,9,10,11. Another crucial point influencing the possible application of a material is its stability towards external stimuli12. For example, the hydrogel must maintain its mechanical integrity in cell culture media or the human body.
In recent years, research on 3D cell culture hydrogels intensified, and many studies were carried out to resolve the 3D architectures of the systems13. Hydrogels composed of chemically synthesized components are most commonly investigated because they can be easily synthesized and chemically modified and they exhibit high stability (see Zhu et al., 2011 for a review)5. However, proteins have many beneficial properties: as so-called &#34;precision polymers,&#34; they are biocompatible; they have a defined length; they are relatively easy to modify; and they have a large number of target sites14,15. In this regard, highly specific, innovative structures can be generated for application in many fields. In this study, a protein-based hydrogel16 was used to demonstrate the ability of well-established methods to influence the 3D architecture of the material. Furthermore, the capability of and applicability to pore generation was also investigated.
Many different techniques are available to modify 3D structures, including both simple methods and sophisticated, highly specialized techniques from different fields of material science. A widespread technique is the use of electrospinning to generate well-defined structures17. Charged fibers are pulled from a solution by an electric field and then solidify upon exposure to oxygen. In this way, fibers in the range of several nanometers up to several microns can be produced. Additional techniques to tune the size, structure, and distribution of the pores within the matrix are soft lithography, photolithography, hydrodynamic focusing, electro-spraying, and bio-printing18,19,20. A significant drawback of these techniques is their dependency upon specific, expensive equipment and special chemicals or materials. Furthermore, experience with these techniques is often not directly transferrable to protein-based materials, and many of the chemicals and methods are not cell compatible.
On the other hand, many techniques do not rely upon special equipment, making them easier and cheaper to apply and to reproduce. A widespread method for structure manipulation is solvent casting21,22,23. Particles are added prior to the polymerization reaction and are distributed homogenously to saturate the solution. After the polymerization, a change of conditions, such as a dilution or a pH change, leads to the solvation of the particles, while the pores remain within the material. The chemicals used in these techniques, such as salt, sugar, paraffin, gelatin, and chalk, are cheap and readily available. In freeze-drying, swollen hydrogels are frozen. The subsequent sublimation of the liquid phases under a vacuum is then performed23,24,25. Water sublimation from the network is gentle enough to maintain the specific 3D structures of the material. In gas foaming, a solution is streamed with a gas while the polymerization takes place, leaving pores within the gel21. The size and distribution of the pores can be adjusted depending upon the gas stream.
To form the protein hydrogel, BSA is reacted with tetrakis (hydroxymethyl) phosphonium chloride (THPC) in a Mannich-type reaction to allow for the formation of covalent bonds between primary amines and the hydroxy groups of the four-armed linker molecule26. Possible harmful intermediates are removed by excessive washing of the material after the reaction occurs.
This study demonstrates the possibility of treating a BSA-based material with different techniques to manipulate and tailor the size of the pores. Each of the techniques can be used in any laboratory worldwide, as no special equipment is necessary. In addition, different parameters, such as swelling ratio, enzymatic degradability, pH stability, and temperature sensitivity, were examined and compared to each other, especially respect to the influence of the different techniques on the generation of 3D architectures. Finally, the materials were functionalized with cell-adhesive peptides to investigate the possible application of the materials to cell culture. Two different model cell lines were used: A549 and MCF7.

<table><tbody><tr><td>Phosphate Buffered Saline (PBS)</td><td>Thermo Fisher Scientific</td><td>10010023</td><td></td></tr><tr><td>Dulbecco&amp;rsquo;s modified Eagle&amp;rsquo;s medium (high glucose)</td><td>Life Technologies / Thermo Fisher&amp;nbsp;</td><td>11140-050</td><td></td></tr><tr><td>Fetal Bovine Serum (FBS)</td><td>Life Technologies / Thermo Fisher&amp;nbsp;</td><td>10270-106</td><td></td></tr><tr><td>Penicillin-Streptomycin</td><td>Life Technologies / Thermo Fisher&amp;nbsp;</td><td>15140122</td><td></td></tr><tr><td>MEM Nonessential Amino Acid Solution</td><td>Sigma Aldrich</td><td>M7145-100ML</td><td></td></tr><tr><td>Trypsin EDTA 0.05% Phenol Red</td><td>Thermo Fisher Scientific</td><td>25300062</td><td></td></tr><tr><td>Ethanol 99.8%, verg&amp;auml;llt</td><td>&amp;Ouml;lfabrik Schmidt</td><td>2133</td><td></td></tr><tr><td>NaCl&amp;nbsp;</td><td>Carl Roth&amp;nbsp;</td><td>9265.1</td><td></td></tr><tr><td>Albumin Fraction V</td><td>Carl Roth&amp;nbsp;</td><td>3854.2</td><td></td></tr><tr><td>THPC</td><td>Sigma Aldrich</td><td>404861-100ML</td><td>Toxic</td></tr><tr><td>0.1% Triton X-100</td><td>Sigma Aldrich</td><td>X100-100ML</td><td>Slightly toxic</td></tr><tr><td>Phalloidin-rhodamine&amp;nbsp;</td><td>Life Technologies / Thermo Fisher&amp;nbsp;</td><td>R415</td><td></td></tr><tr><td>3.7% Formaldehyde&amp;nbsp;</td><td>Life Technologies / Thermo Fisher&amp;nbsp;</td><td>F8775-25ML</td><td>Toxic</td></tr><tr><td>Rhodamine B</td><td>Sigma Aldrich</td><td>81-88-9</td><td></td></tr><tr><td>Filtropur S 0.2&amp;nbsp;</td><td>Sarsted Ag und Co.</td><td>2 83.1826.001&amp;nbsp;&amp;nbsp;&amp;nbsp;</td><td></td></tr><tr><td>&amp;micro; slide 8 well</td><td>Ibidi GmbH</td><td>80826</td><td></td></tr><tr><td>KCSSGKSRGDS peptide</td><td>UPEP Ulm</td><td>Custom sysnthesis</td><td></td></tr><tr><td>Ethanol 99.8%, verg&amp;auml;llt</td><td>Carl Roth&amp;nbsp;</td><td>K928.5</td><td></td></tr><tr><td>Falcon 5 ml Polysterene Round-Bottom Tube&amp;nbsp;</td><td>Sarsted Ag und Co.</td><td>62.547.254&amp;nbsp; &amp;nbsp;&amp;nbsp;</td><td></td></tr><tr><td>Tubes 50 ml&amp;nbsp;</td><td>Sarsted Ag und Co.</td><td>62.547.254&amp;nbsp; &amp;nbsp;&amp;nbsp;</td><td></td></tr><tr><td>Tubes 1.5 ml&amp;nbsp;&amp;nbsp;</td><td>Sarsted Ag und Co.</td><td>72,690,001</td><td></td></tr><tr><td>Tubes 2 ml&amp;nbsp;&amp;nbsp;</td><td>Sarsted Ag und Co.</td><td>72,691</td><td></td></tr><tr><td>CELL CULTURE MICROPLATE, 96 WELL, PS, F-BOTTOM</td><td>Greiner</td><td>655073</td><td></td></tr><tr><td>FreezeDryer Epsilon 1-6D,&amp;nbsp;</td><td>Christ, Osterode am Harz, Germany</td><td></td><td></td></tr><tr><td>Confocal Laser Scanning Microscope&amp;nbsp;</td><td>Carl Zeiss AG, Oberkochen, Germany</td><td></td><td></td></tr><tr><td>Zen Software Version 2012 Sp1, black edition, 407 version 8,1,0,484</td><td>Carl Zeiss AG, Oberkochen, Germany</td><td></td><td></td></tr><tr><td>GSA Imaga Analyzer Software, GSA Image Analyzer, GSA, Version 419 3.8.7</td><td>GSA GmbH</td><td></td><td></td></tr></tbody></table>

easy manipulation of architectures in protein-based hydrogels for cell culture applications

Hydrogels are recognized as promising materials for cell culture applications due to their ability to provide highly hydrated cell environments. The field of 3D templates is rising due to the potential resemblance of those materials to the natural extracellular matrix. Protein-based hydrogels are particularly promising because they can easily be functionalized and can achieve defined structures with adjustable physicochemical properties. However, the production of macroporous 3D templates for cell culture applications using natural materials is often limited by their weaker mechanical properties compared to those of synthetic materials. Here, different methods were evaluated to produce macroporous bovine serum albumin (BSA)-based hydrogel systems, with adjustable pore sizes in the range of 10 to 70 &#181;m in radius. Furthermore, a method to generate channels in this protein-based material that are several hundred microns long was established. The different methods to produce pores, as well as the influence of pore size on material properties such as swelling ratio, pH, temperature stability, and enzymatic degradation behavior, were analyzed. Pore sizes were investigated in the native, swollen state of the hydrogels using confocal laser scanning microscopy. The feasibility for cell culture applications was evaluated using a cell-adhesive RGD peptide modification of the protein system and two model cell lines: human breast cancer cells (A549) and adenocarcinomic human alveolar basal epithelial cells (MCF7).

Hydrogel development has become one of the most prominent fields in material research-related biological studies, with thousands of entries indexed in scientific research archives. Although the behavior of many systems is well studied, the manipulation of 3D networks, especially of sensitive protein-based materials, is often a major issue in material science. Another commonly underestimated challenge is the correct measurement of the native structure of a material using cryo electron micr...

Watch this Scientific Journal Video about Easy Manipulation of Architectures in Protein-based Hydrogels for Cell Culture Applications at JoVE.com

Easy Manipulation of Architectures in Protein-based Hydrogels for Cell Culture Applications

Different methods to manipulate three-dimensional architecture in protein-based hydrogels are evaluated here with respect to material properties. The macroporous networks are functionalized with a cell-adhesive peptide, and their feasibility in cell culture is evaluated using two different model cell lines.

Hydrogels are recognized as promising materials for cell culture applications due to their ability to provide highly hydrated cell environments. The field ...

easy-manipulation-architectures-protein-based-hydrogels-for-cell

Research

JoVE Journal

Biochemistry

6.7K Views.  Ulm University. Different methods to manipulate three-dimensional architecture in protein-based hydrogels are evaluated here with respect to material properties. The macroporous networks are functionalized with a cell-adhesive peptide, and their feasibility in cell culture is evaluated using two different model cell lines.

Video: Easy Manipulation of Architectures in Protein-based Hydrogels for Cell Culture Applications

Microfabricated Platforms for Mechanically Dynamic Cell Culture

The ability to systematically probe in vitro cellular response to combinations of mechanobiological stimuli for tissue engineering, drug discovery or fundamental cell biology studies is limited by current bioreactor technologies, which cannot simultaneously apply a variety of mechanical stimuli to cultured cells. In order to address this issue, we have developed a series of microfabricated platforms designed to screen for the effects of mechanical stimuli in a high-throughput format. In this protocol, we demonstrate the fabrication of a microactuator array of vertically displaced posts on which the technology is based, and further demonstrate how this base technology can be modified to conduct high-throughput mechanically dynamic cell culture in both two-dimensional and three-dimensional culture paradigms.

In this protocol, we demonstrate the fabrication of a microactuator array of vertically displaced posts on which the technology is based, and how this base technology can be modified to conduct high-throughput mechanically dynamic cell culture in both two-dimensional and three-dimensional culture paradigms.

The ability to systematically probe in vitro cellular response to combinations of mechanobiological stimuli for tissue engineering, drug discovery or ...

Bioengineering

Fabrication of Micropatterned Hydrogels for Neural Culture Systems using Dynamic Mask Projection Photolithography

Increasingly, patterned cell culture environments are becoming a relevant technique to study cellular characteristics, and many researchers believe in the need for 3D environments to represent in vitro experiments which better mimic in vivo qualities 1-3. Studies in fields such as cancer research 4, neural engineering 5, cardiac physiology 6, and cell-matrix interaction7,8have shown cell behavior differs substantially between traditional monolayer cultures and 3D constructs.
Hydrogels are used as 3D environments because of their variety, versatility and ability to tailor molecular composition through functionalization 9-12. Numerous techniques exist for creation of constructs as cell-supportive matrices, including electrospinning13, elastomer stamps14, inkjet printing15, additive photopatterning16, static photomask projection-lithography17, and dynamic mask microstereolithography18. Unfortunately, these methods involve multiple production steps and/or equipment not readily adaptable to conventional cell and tissue culture methods. The technique employed in this protocol adapts the latter two methods, using a digital micromirror device (DMD) to create dynamic photomasks for crosslinking geometrically specific poly-(ethylene glycol) (PEG) hydrogels, induced through UV initiated free radical polymerization. The resulting "2.5D" structures provide a constrained 3D environment for neural growth. We employ a dual-hydrogel approach, where PEG serves as a cell-restrictive region supplying structure to an otherwise shapeless but cell-permissive self-assembling gel made from either Puramatrix or agarose. The process is a quick simple one step fabrication which is highly reproducible and easily adapted for use with conventional cell culture methods and substrates.
Whole tissue explants, such as embryonic dorsal root ganglia (DRG), can be incorporated into the dual hydrogel constructs for experimental assays such as neurite outgrowth. Additionally, dissociated cells can be encapsulated in the photocrosslinkable or self polymerizing hydrogel, or selectively adhered to the permeable support membrane using cell-restrictive photopatterning. Using the DMD, we created hydrogel constructs up to ~1mm thick, but thin film (&lt;200 &mu;m) PEG structures were limited by oxygen quenching of the free radical polymerization reaction. We subsequently developed a technique utilizing a layer of oil above the polymerization liquid which allowed thin PEG structure polymerization.
In this protocol, we describe the expeditious creation of 3D hydrogel systems for production of microfabricated neural cell and tissue cultures. The dual hydrogel constructs demonstrated herein represent versatile in vitro models that may prove useful for studies in neuroscience involving cell survival, migration, and/or neurite growth and guidance. Moreover, as the protocol can work for many types of hydrogels and cells, the potential applications are both varied and vast.

Simple techniques are described for the rapid production of microfabricated neural culture systems using a digital micromirror device for dynamic mask projection lithography on regular cell culture substrates. These culture systems may be more representative of natural biological architecture, and the techniques described could be adapted for numerous applications.

Increasingly, patterned cell culture environments are becoming a relevant technique to study cellular characteristics, and many researchers believe in the ...

Preparation of Hydroxy-PAAm Hydrogels for Decoupling the Effects of Mechanotransduction Cues

It is now well established that many cellular functions are regulated by interactions of cells with physicochemical and mechanical cues of their extracellular matrix (ECM) environment. Eukaryotic cells constantly sense their local microenvironment through surface mechanosensors to transduce physical changes of ECM into biochemical signals, and integrate these signals to achieve specific changes in gene expression. Interestingly, physicochemical and mechanical parameters of the ECM can couple with each other to regulate cell fate. Therefore, a key to understanding mechanotransduction is to decouple the relative contribution of ECM cues on cellular functions.
Here we present a detailed experimental protocol to rapidly and easily generate biologically relevant hydrogels for the independent tuning of mechanotransduction cues in vitro. We chemically modified polyacrylamide hydrogels (PAAm) to surmount their intrinsically non-adhesive properties by incorporating hydroxyl-functionalized acrylamide monomers during the polymerization. We obtained a novel PAAm hydrogel, called hydroxy-PAAm, which permits immobilization of any desired nature of ECM proteins. The combination of hydroxy-PAAm hydrogels with microcontact printing allows to independently control the morphology of single-cells, the matrix stiffness, the nature and the density of ECM proteins. We provide a simple and rapid method that can be set up in every biology lab to study in vitro cell mechanotransduction processes. We validate this novel two-dimensional platform by conducting experiments on endothelial cells that demonstrate a mechanical coupling between ECM stiffness and the nucleus.

We present a new polyacrylamide hydrogel, called hydroxy-PAAm, that allows a direct binding of ECM proteins with minimal cost or expertise. The combination of hydroxy-PAAm hydrogels with microcontact printing facilitates independent control of many cues of the natural cell microenvironment for studying cellular mechanostransduction.

It is now well established that many cellular functions are regulated by interactions of cells with physicochemical and mechanical cues of their ...

Construction of Modular Hydrogel Sheets for Micropatterned Macro-scaled 3D Cellular Architecture

Hydrogels can be patterned at the micro-scale using microfluidic or micropatterning technologies to provide an in vivo-like three-dimensional (3D) tissue geometry. The resulting 3D hydrogel-based cellular constructs have been introduced as an alternative to animal experiments for advanced biological studies, pharmacological assays and organ transplant applications. Although hydrogel-based particles and fibers can be easily fabricated, it is difficult to manipulate them for tissue reconstruction. In this video, we describe a fabrication method for micropatterned alginate hydrogel sheets, together with their assembly to form a macro-scale 3D cell culture system with a controlled cellular microenvironment. Using a mist form of the calcium gelling agent, thin hydrogel sheets are easily generated with a thickness in the range of 100 - 200 &#181;m, and with precise micropatterns. Cells can then be cultured with the geometric guidance of the hydrogel sheets in freestanding conditions. Furthermore, the hydrogel sheets can be readily manipulated using a micropipette with an end-cut tip, and can be assembled into multi-layered structures by stacking them using a patterned polydimethylsiloxane (PDMS) frame. These modular hydrogel sheets, which can be fabricated using a facile process, have potential applications of in vitro drug assays and biological studies, including functional studies of micro- and macrostructure and tissue reconstruction.

We describe the fabrication of micropatterned hydrogel sheets using a simple process, which can be assembled and manipulated in a freestanding form. Using these modular hydrogel sheets, a simple macro-scaled 3D cell culture system can be generated with a controlled cellular microenvironment.

Hydrogels can be patterned at the micro-scale using microfluidic or micropatterning technologies to provide an in vivo-like three-dimensional (3D) tissue ...

Light-mediated Formation and Patterning of Hydrogels for Cell Culture Applications

Click chemistries have been investigated for use in numerous biomaterials applications, including drug delivery, tissue engineering, and cell culture. In particular, light-mediated click reactions, such as photoinitiated thiol&#8722;ene and thiol&#8722;yne reactions, afford spatiotemporal control over material properties and allow the design of systems with a high degree of user-directed property control. Fabrication and modification of hydrogel-based biomaterials using the precision afforded by light and the versatility offered by these thiol&#8722;X photoclick chemistries are of growing interest, particularly for the culture of cells within well-defined, biomimetic microenvironments. Here, we describe methods for the photoencapsulation of cells and subsequent photopatterning of biochemical cues within hydrogel matrices using versatile and modular building blocks polymerized by a thiol&#8722;ene photoclick reaction. Specifically, an approach is presented for constructing hydrogels from allyloxycarbonyl (Alloc)-functionalized peptide crosslinks and pendant peptide moieties and thiol-functionalized poly(ethylene glycol) (PEG) that rapidly polymerize in the presence of lithium acylphosphinate photoinitiator and cytocompatible doses of long wavelength ultraviolet (UV) light. Facile techniques to visualize photopatterning and quantify the concentration of peptides added are described. Additionally, methods are established for encapsulating cells, specifically human mesenchymal stem cells, and determining their viability and activity. While the formation and initial patterning of thiol-alloc hydrogels are shown here, these techniques broadly may be applied to a number of other light and radical-initiated material systems (e.g., thiol-norbornene, thiol-acrylate) to generate patterned substrates.

We describe a sequential process for light-mediated formation and subsequent biochemical patterning of synthetic hydrogel matrices for three-dimensional cell culture applications. The construction and modification of hydrogels with cytocompatible photoclick chemistry is demonstrated. Additionally, facile techniques to quantify and observe patterns and determine cell viability within these hydrogels are presented.

Click chemistries have been investigated for use in numerous biomaterials applications, including drug delivery, tissue engineering, and cell culture. In ...

Tunable Hydrogels from Pulmonary Extracellular Matrix for 3D Cell Culture

Here we present a method for establishing multiple component cell culture hydrogels for in vitro lung cell culture. Beginning with healthy en bloc lung tissue from porcine, rat, or mouse, the tissue is perfused and submerged in subsequent chemical detergents to remove the cellular debris. Histological comparison of the tissue before and after processing confirms removal of over 95% of double stranded DNA and alpha galactosidase staining suggests the majority of cellular debris is removed. After decellularization, the tissue is lyophilized and then cryomilled into a powder. The matrix powder is digested for 48 hr in an acidic pepsin digestion solution and then neutralized to form the pregel solution. Gelation of the pregel solution can be induced by incubation at 37 &#176;C and can be used immediately following neutralization or stored at 4 &#176;C for up to two weeks. Coatings can be formed using the pregel solution on a non-treated plate for cell attachment. Cells can be suspended in the pregel prior to self-assembly to achieve a 3D culture, plated on the surface of a formed gel from which the cells can migrate through the scaffold, or plated on the coatings. Alterations to the strategy presented can impact gelation temperature, strength, or protein fragment sizes. Beyond hydrogel formation, the hydrogel stiffness may be increased using genipin.

This is a method to create a 3-dimensional cell culture scaffold from pulmonary extracellular matrix. Intact lung is processed into hydrogels that can support the growth of cells in three-dimensions.

Here we present a method for establishing multiple component cell culture hydrogels for in vitro lung cell culture. Beginning with healthy en bloc lung ...

Patterning Bioactive Proteins or Peptides on Hydrogel Using Photochemistry for Biological Applications

There are many biological stimuli that can influence cell behavior and stem cell differentiation. General cell culture approaches rely on soluble factors within the medium to control cell behavior. However, soluble additions cannot mimic certain signaling motifs, such as matrix-bound growth factors, cell-cell signaling, and spatial biochemical cues, which are common influences on cells. Furthermore, biophysical properties of the matrix, such as substrate stiffness, play important roles in cell fate, which is not easily manipulated using conventional cell culturing practices. In this method, we describe a straightforward protocol to provide patterned bioactive proteins on synthetic polyethylene glycol (PEG) hydrogels using photochemistry. This platform allows for the independent control of substrate stiffness and spatial biochemical cues. These hydrogels can achieve a large range of physiologically relevant stiffness values. Additionally, the surfaces of these hydrogels can be photopatterned with bioactive peptides or proteins via thiol-ene click chemistry reactions. These methods have been optimized to retain protein function after surface immobilization. This is a versatile protocol that can be applied to any protein or peptide of interest to create a variety of patterns. Finally, cells seeded onto the surfaces of these bioactive hydrogels can be monitored over time as they respond to spatially specific signals.

In this method, we use photopolymerization and click chemistry techniques to create protein or peptide patterns on the surface of polyethylene glycol (PEG) hydrogels, providing immobilized bioactive signals for the study of cellular responses in vitro.

There are many biological stimuli that can influence cell behavior and stem cell differentiation. General cell culture approaches rely on soluble factors ...

Production of Elastin-like Protein Hydrogels for Encapsulation and Immunostaining of Cells in 3D

Two-dimensional (2D) tissue culture techniques have been essential for our understanding of fundamental cell biology. However, traditional 2D tissue culture systems lack a three-dimensional (3D) matrix, resulting in a significant disconnect between results collected in vitro and in vivo. To address this limitation, researchers have engineered 3D hydrogel tissue culture platforms that can mimic the biochemical and biophysical properties of the in vivo cell microenvironment. This research has motivated the need to develop material platforms that support 3D cell encapsulation and downstream biochemical assays. Recombinant protein engineering offers a unique toolset for 3D hydrogel material design and development by allowing for the specific control of protein sequence and therefore, by extension, the potential mechanical and biochemical properties of the resultant matrix. Here, we present a protocol for the expression of recombinantly-derived elastin-like protein (ELP), which can be used to form hydrogels with independently tunable mechanical properties and cell-adhesive ligand concentration. We further present a methodology for cell encapsulation within ELP hydrogels and subsequent immunofluorescent staining of embedded cells for downstream analysis and quantification.

Recombinant protein-engineered hydrogels are advantageous for 3D cell culture as they allow for complete tunability of the polymer backbone and therefore, the cell microenvironment. Here, we describe the process of recombinant elastin-like protein purification and its application in 3D hydrogel cell encapsulation.

Two-dimensional (2D) tissue culture techniques have been essential for our understanding of fundamental cell biology. However, traditional 2D tissue ...

Measuring Global Cellular Matrix Metalloproteinase and Metabolic Activity in 3D Hydrogels

Three-dimensional (3D) cell culture systems often more closely recapitulate in vivo cellular responses and functions than traditional two-dimensional (2D) culture systems. However, measurement of cell function in 3D culture is often more challenging. Many biological assays require retrieval of cellular material which can be difficult in 3D cultures. One way to address this challenge is to develop new materials that enable measurement of cell function within the material. Here, a method is presented for measurement of cellular matrix metalloproteinase (MMP) activity in 3D hydrogels in a 96-well format. In this system, a poly(ethylene glycol) (PEG) hydrogel is functionalized with a fluorogenic MMP cleavable sensor. Cellular MMP activity is proportional to fluorescence intensity and can be measured with a standard microplate reader. Miniaturization of this assay to a 96-well format reduced the time required for experimental set up by 50% and reagent usage by 80% per condition as compared to the previous 24-well version of the assay. This assay is also compatible with other measurements of cellular function. For example, a metabolic activity assay is demonstrated here, which can be conducted simultaneously with MMP activity measurements within the same hydrogel. The assay is demonstrated with human melanoma cells encapsulated across a range of cell seeding densities to determine the appropriate encapsulation density for the working range of the assay. After 24 h of cell encapsulation, MMP and metabolic activity readouts were proportional to cell seeding density. While the assay is demonstrated here with one fluorogenic degradable substrate, the assay and methodology could be adapted for a wide variety of hydrogel systems and other fluorescent sensors. Such an assay provides a practical, efficient and easily accessible 3D culturing platform for a wide variety of applications.

Here, a protocol is presented for encapsulating and culturing cells in poly(ethylene glycol) (PEG) hydrogels functionalized with a fluorogenic matrix metalloproteinase (MMP)-degradable peptide. Cellular MMP and metabolic activity are measured directly from the hydrogel cultures using a standard microplate reader.

Three-dimensional (3D) cell culture systems often more closely recapitulate in vivo cellular responses and functions than traditional two-dimensional (2D) ...

Controlled Strain of 3D Hydrogels under Live Microscopy Imaging

External forces are an important factor in tissue formation, development, and maintenance. The effects of these forces are often studied using specialized in vitro stretching methods. Various available systems use 2D substrate-based stretchers, while the accessibility of 3D techniques to strain soft hydrogels, is more restricted. Here, we describe a method that allows external stretching of soft hydrogels from their circumference, using an elastic silicone strip as the sample carrier. The stretching system utilized in this protocol is constructed from 3D-printed parts and low-cost electronics, making it simple and easy to replicate in other labs. The experimental process begins with polymerizing thick (&#62;100 &#956;m) soft fibrin hydrogels (Elastic Modulus of ~100 Pa) in a cut-out at the center of a silicone strip. Silicone-gel constructs are then attached to the printed-stretching device and placed on the confocal microscope stage. Under live microscopy the stretching device is activated, and the gels are imaged at various stretch magnitudes. Image processing is then used to quantify the resulting gel deformations, demonstrating relatively homogenous strains and fiber alignment throughout the gel&#8217;s 3D thickness (Z-axis). Advantages of this method include the ability to strain extremely soft hydrogels in 3D while executing in situ microscopy, and the freedom to manipulate the geometry and size of the sample according to the user&#8217;s needs. Additionally, with proper adaptation, this method can be used to stretch other types of hydrogels (e.g., collagen, polyacrylamide or polyethylene glycol) and can allow for analysis of cells and tissue response to external forces under more biomimetic 3D conditions.

The presented method involves uniaxial stretching of 3D soft hydrogels embedded in silicone rubber while allowing live confocal microscopy. Characterization of the external and internal hydrogel strains as well as fiber alignment are demonstrated. The device and protocol developed can assess the response of cells to various strain regimes.

External forces are an important factor in tissue formation, development, and maintenance. The effects of these forces are often studied using specialized ...