Formation of Thick Dense Yttrium Iron Garnet Films Using Aerosol Deposition

Aerosol deposition (AD) is a thick-film deposition process that can produce layers up to several hundred micrometers thick with densities greater than 95% ...

Naval Research Laboratory

We present X-ray photoelectron spectroscopy, van der Pauw Hall mobilities, low-temperature far-infrared magneto transmission (FIR-MT), and atomic force microscopy (AFM) results from graphene films produced by radiative heating in an ultrahigh vacuum (UHV) chamber or produced by radio frequency (RF) furnace annealing in a high vacuum chemical vapor deposition system on Si- and C-face 4H SiC substrates at 1200-1600 degrees C. Although the vacuum level and heating methods are different, graphene films produced by the two methods are chemically similar with the RF furnace annealing typically producing thicker graphene films than UHV. We observe, however, that the formation of graphene on the two faces is different with the thicker graphene films on the C-face RF samples having higher mobility. The FIR-MT showed a 0(-1) --> 1(0) Landau level transition with a square root B dependence and a line width consistent with a Dirac fermion with a mobility >250,000 cm(2) x V(-1) x s(-1) at 4.2 K in a C-face RF sample having a Hall-effect carrier mobility of 425 cm(2) x V(-1) x s(-1) at 300 K. AFM shows that graphene grows continuously over the varying morphology of both Si and C-face substrates.

Comparison of epitaxial graphene on Si-face and C-face 4H SiC formed by ultrahigh vacuum and RF furnace production.

The remarkable electronic properties of graphene strongly depend on the thickness and geometry of graphene stacks. This wide range of electronic tunability is of fundamental interest and has many applications in newly proposed devices. Using the mid-infrared, magneto-optical Kerr effect, we detect and identify over 18 interband cyclotron resonances (CR) that are associated with ABA and ABC stacked multilayers as well as monolayers that coexist in graphene that is epitaxially grown on 4H-SiC. Moreover, the magnetic field and photon energy dependence of these features enable us to explore the band structure, electron-hole band asymmetries, and mechanisms that activate a CR response in the Kerr effect for various multilayers that coexist in a single sample. Surprisingly, we find that the magnitude of monolayer Kerr effect CRs is not temperature dependent. This unexpected result reveals new questions about the underlying physics that makes such an effect possible.

Magneto-optical fingerprints of distinct graphene multilayers using the giant infrared Kerr effect.

Melanization due to the inactivation of the homogentisate-1,2-dioxygenase gene (hmgA) has been demonstrated to increase stress resistance, persistence, and virulence in some bacterial species but such pigmented mutants have not been observed in pathogenic members of the Vibrio Harveyi clade. In this study, we used Vibrio campbellii ATCC BAA-1116 as model organism to understand how melanization affected cellular phenotype, metabolism, and virulence. An in-frame deletion of the hmgA gene resulted in the overproduction of a pigment in cell culture supernatants and cellular membranes that was identified as pyomelanin. Unlike previous demonstrations in Vibrio cholerae, Burkholderia cepacia, and Pseudomonas aeruginosa, the pigmented V. campbellii mutant did not show increased UV resistance and was found to be ~2.7 times less virulent than the wild type strain in Penaeus monodon shrimp virulence assays. However, the extracted pyomelanin pigment did confer a higher resistance to oxidative stress when incubated with wild type cells. Microarray-based transcriptomic analyses revealed that the hmgA gene deletion and subsequent pyomelanin production negatively effected the expression of 129 genes primarily involved in energy production, amino acid, and lipid metabolism, and protein translation and turnover. This transcriptional response was mediated in part by an impairment of the quorum sensing regulon as transcripts of the quorum sensing high cell density master regulator LuxR and other operonic members of this regulon were significantly less abundant in the hmgA mutant. Taken together, the results suggest that the pyomelanization of V. campbellii sufficiently impairs the metabolic activities of this organism and renders it less fit and virulent than its isogenic wild type strain.

Evan R. Glaser

Physics of Electronic Materials Branch

Naval Research Laboratory

Formation of Thick Dense Yttrium Iron Garnet Films Using Aerosol Deposition

Evan R. Glaser

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Physics of Electronic Materials Branch

Naval Research Laboratory

Formation of Thick Dense Yttrium Iron Garnet Films Using Aerosol Deposition

Physics of Electronic Materials Branch