We acknowledge the financial support of the NSF award CMMI-1000724.

1A. Primary Monolayer Formation on Silicon
<ol>
	<li>Cut silicon wafer into 1cm2 substrates, dust and rinse with water and filtered ethanol.</li>
	<li>Remove organic contamination by submerging the silicon substrates in a glass dish containing Nano strip at 75&ordm;C. After 15 minutes, rinse each substrate with deionized, filtered water.</li>
	<li>Place each substrate in a 5&#37; HF solution (Warning: HF is an extremely dangerous material) to remove the native oxide layer. After 5 minutes dry the oxide-free silicon with nitrogen</li>
	<li>To produce a chlorinated substrate, immediately submerge each oxide-free silicon piece in a scintillation vial containing 2 ml of saturated PCl5 in chlorobenzene. This solution should be filtered to 0.2 &mu;m. </li>
	<li>Assemble a vial condenser on top of each vial and place them in a heatblock set to 112&deg;C for one hour. </li>
	<li>After reaction is complete, let vials cool and rinse each surface with chlorobenzene and dry under filtered nitrogen.</li>
	<li>To form a propenyl-terminates substrate, place each chlorinated silicon surface in a pressure vial containing 4 ml of propenyl magnesium chloride. Place each pressure vial in a heatblock at 130 &deg;C for 24 hours. </li>
	<li>Take each pressure vial out of the heatblock and let cool.</li>
	<li>Rinse each surface quickly with DCM and ethanol and dry under filtered nitrogen.</li>
</ol>
1B. Primary Monolayer Formation on Germanium
<ol>
	<li>Cut germanium wafer into 1cm2 substrates, dust and rinse with water and filtered ethanol.</li>
	<li>Remove organic contamination by submerging the surfaces in a glass dish containing acetone for 20 minutes</li>
	<li>Place each surface in a 10&#37; HCl solution for 15 minutes. This process simultaneously removes the native oxide layer and chlorinates the surface. After 5 minutes dry the substrates with nitrogen.</li>
	<li>To form an octyl-terminated substrate, place each chlorinated germanium surface in a pressure vial containing 4 ml of octyl magnesium chloride (2 mM). Place each pressure vial in a heatblock at 130 &deg;C for 48 hours. </li>
	<li>Take each pressure vial out of the heatblock and let cool to room temperature.</li>
	<li>Rinse each surface quickly with DCM and ethanol and dry under filtered nitrogen.</li>

</ol>
2. NHS Substrate Functionalization on Silicon and Germanium
<ol>
	<li>Prepare a filtered 0.1 M NHS-diazirine solution in carbon tetrachloride. Warning: Keep light exposure to a minimum. </li>
	<li>Pipet a few drops of the solution onto the methyl terminated surfaces. Allow solution to spread across the entire surface.</li>
	<li>Place the surfaces under a UV lamp (&#9744;=254 nm, 4400/cm2 at 0.74 inches). Allow the surfaces to react under UV light for 30 minutes, then add more NHS-diazirine to the surface and let the reaction proceed for an additional 30 minutes. </li>
	<li>Rinse the NHS modified surfaces with DCM and ethanol and dry under filtered nitrogen.</li>
</ol>
3. Small Molecule Functionalization
<ol>
	<li>React NHS-modified substrates in a 20 mM tert-butyl carbamoyl (Boc-) ethylenediamine solution in dichloromethane (DCM) for two hours at room temperature. </li>
	<li>After the reaction, rinse the Boc-modified substrate with DCM and ethanol. </li>
	<li>Deprotect the Boc modified substrate using 25&#37; trifluoroacetic acid (TFA) in DCM for one hour at room temperature. </li>
	<li>Rinse the resulting surface with DCM, ethanol and 10&#37; (w/v) potassium bicarbonate in water and dry under filtered nitrogen. </li>
	<li>Analyze all surfaces by XPS to determine the elemental composition. </li>
</ol>
4. Acidic Polyurethane Acrylate Stamp (PUA) Preparation
<ol>
	<li>Dilute acrylate A by 30&#37; with trimethylolpropane ethoxylate triacrylate B to reduce viscosity. Add photoinitiators C and D to the reaction mixture (Figure 6).</li>
	<li>Add sodium 2-mercaptoethanesulfonate (0.2 g, 1.22 mmol) to a 4N HCl solution in dioxane (10 ml) and stir at room temperature for 2 minutes.</li>
	<li>Filter off the sodium chloride first through a fine glass filter and then through a 0.2 &mu;m PTFE membrane syringe filter to afford a clear solution of 2-mercaptoethanesulfonic acid in dioxane. </li>
	<li>Evaporate dioxane under reduced pressure </li>
	<li>React the resulting sulfonic acid with 2 ml of the polyurethane-acrylate prepolymeric mixture at room temperature and then under vacuum at 50 &deg;C. Be sure to completely free the mixture from trapped air bubbles.</li>
	<li>Cool the resulting solution to room temperature and polymerize between two glass microscope slides or a glass slide and a master by exposure to UV light for 2 hours at room temperature. </li>
	<li>After polymerization, carefully peel the stamp off the master and wash the stamp with ethanol and water and dry with filtered nitrogen. </li>
</ol>
5. Catalytic Printing and SEM/AFM Analysis
<ol>
	<li>Place the corresponding polyurethane-acrylate stamp on top of the NHS-modified substrate at room temperature for one minute with no external load to hold them together. </li>
	<li>After the reaction, separate the stamp and substrate.</li>
	<li>Rinse the substrate with ethanol, water, and ethanol then dry with filtered nitrogen. </li>
	<li>Rinse the stamp with ethanol, water, and ethanol then dry with filtered nitrogen.</li>
	<li>Keep stamps at room temperature before the next application.</li>
	<li>Analyze the produced pattern using contact mode lateral atomic force microsopy (AFM) and scanning electron microscopy (SEM)</li>
</ol>
6. Protein Patterning and Fluorescent Microscopy
<ol>
	<li>Submerge the NHS-patterned bifunctional substrate in Lysine-N,N-diacetic acid (20 mM) and Et3N (100 mM) in DMF:H20 (1:1) at room temperature for 1 hr and then rinsed with water and ethanol. </li>
	<li>Incubate the substrates in a 50 mM NiSO4 solution for 5 min at room temperature. </li>
	<li>Rinse the chelated substrates excessively with water and binding buffer (20 mM NaP, 250 mM NaCl, 10mM imidazole, pH 7.5) and submerge in a filtered GFP solution (&tilde;40 &mu;M) for 1 hr at 0&deg;C. </li>
	<li>Immediately rinse the substrates with binding buffer followed by PBS (pH 7.4). </li>
	<li>Keep substrates hydrated in PBS at 0&deg;C until they were ready for fluorescence microscopy analysis.</li>
</ol>
7. Protein Patterning and Fluorescent Microscopy
<ol>
	<li>Submerge the NHS-patterned bifunctional substrate in Lysine-N,N-diacetic acid (20 mM) and Et3N (100 mM) in DMF:H20 (1:1) at room temperature for 1 hr and then rinsed with water and ethanol. </li>
	<li>Incubate the substrates in a 50 mM NiSO4 solution for 5 min at room temperature. </li>
	<li>Rinse the chelated substrates excessively with water and binding buffer (20 mM NaP, 250 mM NaCl, 10mM imidazole, pH 7.5) and submerge in a filtered GFP solution (&tilde;40 &mu;M) for 1 hr at 0&deg;C. </li>
	<li>Immediately rinse the substrates with binding buffer followed by PBS (pH 7.4). </li>
	<li>Keep substrates hydrated in PBS at 0&deg;C until they were ready for fluorescence microscopy analysis.</li>
</ol>
8. Representative Results: 
An example of soft-lithographic catalytic nano patterning is shown in Figure 7. The approach creates chemoselective patterns on oxide-free silicon and germanium, which can be orthogonally functionalized with dissimilar chemical and biological moieties. The reaction between the NHS-functioanlized substrate and the catalytic patterned stamp leads to the hydrolysis of NHS moieties in areas of conformal contact, yielding a patterned bifunctional substrate bearing regions of NHS activated and free carboxylic acids. Due to the diffusion free nature of our method, we achieve resolution close to that of photolithography. For example, Figure 7 shows 125 nm features, which were uniformly reproduced across the entire silicon substrate surface. Remarkably, the catalytic stamp can be reused multiple times without losing efficiency.
Chemoselective functionalization of patterned semiconductors with biomolecules opens up the prospect of integrating traditional electronic materials with highly selective biological substrates for applications in sensing, diagnostic, and analytical areas of research. An example of such functionalization is shown in Figure 8, where NHS-patterned silicon was selectively functionalized with protein molecules. By exploiting the differential reactivities of activated and free carboxylic acids, we first affixed nitrilotriacetic acid-terminated (NTA) heterobifunctional linkers to the NHS-functionalized regions, and then used the resulting NTA-patterned surface as a template for the selective attachment of hexa-histidine-tagged GFP. Figure 8b clearly shows differential fluorescence intensity between GFP-modified and hydrolyzed free carboxylic acid regions. The size and shape of the replicated features are consistent between both NHS patterned surface (Figure 8a) and GFP-modified surface (Figure 8b), confirming the remarkable stability of carbon-passivated surfaces and the selectivity of the stamping approach. The protocol is not limited to His-tagged protein, and can be used to pattern other biomolecules including DNA and antibodies.
<img src="/files/ftp_upload/3478/3478fig1.jpg" alt="Figure 1"/> Figure 1.&nbsp;General scheme representing catalytic microcontact printing
<img src="/files/ftp_upload/3478/3478fig2.jpg" alt="Figure 2"/> Figure 2.&nbsp;Structure of bi-layered molecular system on Ge and Si. Primary alkyl monolayer forms stable Ge-C or Si-C bonds with the substrate and provides a chemically inert and close packed system that protects the underlying surface from degradation.(b) Secondary overlayer forms stable C-C bonds with primary protective layer and provides terminal functional groups
<img src="/files/ftp_upload/3478/3478fig3.jpg" alt="Figure 3"/> Figure 3.&nbsp;Reaction schemes representing formation of primary protective monolayers on Si (A) and Ge (B)
<img src="/files/ftp_upload/3478/3478fig4.jpg" alt="Figure 4"/> Figure 4.&nbsp;Chemical functionalization of the primary protective monolayer with a heterobifunctional carbene donor
<img src="/files/ftp_upload/3478/3478fig5.jpg" alt="Figure 5"/> Figure 5.&nbsp;Reaction scheme demonstrating small molecule modifications of NHS-functionalized substrates and the corresponding XPS spectra
<img src="/files/ftp_upload/3478/3478fig6.jpg" alt="Figure 6"/> Figure 6.&nbsp;Composition of the catalytic pre-polymeric mixture, polymerization conditions, and SEM images of the patterned sulfonic acid-modified stamp and the corresponding PMMA-Si master
<img src="/files/ftp_upload/3478/3478fig7.jpg" alt="Figure 7"/> Figure 7.&nbsp;SEM and AFM friction images of patterned SAMs on Si and Ge with an acidic stamp
<img src="/files/ftp_upload/3478/3478fig8.jpg" alt="Figure 8"/> Figure 8.&nbsp;Soft-lithographic patterning and functionalization of passivated silicon with organic and biological molecules. a: SEM image of the patterned NHS-modified substrate. b: Fluorescent micrograph of GFP modified substrate.

<ol>
	<li>Kumar, A., Abbott, N. L., Kim, E., Biebuyck, H. A., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Patterned+Self-Assembled+Monolayers+and+Mesoscale+Phenomena.">Patterned Self-Assembled Monolayers and Mesoscale Phenomena.</a> Accounts. Chem. Res. 28 (5), 219-226 (1995).</li><li>Kumar, A., Biebuyck, H. A., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Patterning+Self-Assembled+Monolayers:+Applications+in+Materials+Science.">Patterning Self-Assembled Monolayers: Applications in Materials Science.</a> Langmuir. 10 (5), 1498-1511 (1994).</li><li>Kumar, A., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Features+of+gold+having+micrometer+to+centimeter+dimensions+can+be+formed+through+a+combination+of+stamping+with+an+elastomeric+stamp+and+an+alkanethiol+"ink"+followed+by+chemical+etching.">Features of gold having micrometer to centimeter dimensions can be formed through a combination of stamping with an elastomeric stamp and an alkanethiol "ink" followed by chemical etching.</a> Applied Physics Letters. 63 (14), 2002-2004 (1993).</li><li>Wilbur, J. L., Kumar, A., Biebuyck, H. A., Kim, E., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microcontact+printing+of+self-assembled+monolayers:+applications+in+microfabrication.">Microcontact printing of self-assembled monolayers: applications in microfabrication.</a> Nanotechnology. 7 (4), 452-457 (1996).</li><li>Wilbur, J. L., Kumar, A., Kim, E., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microfabrication+by+microcontact+printing+of+self-assembled+monolayers.">Microfabrication by microcontact printing of self-assembled monolayers.</a> Advanced Materials (Weinheim, Germany). 6 (7/8), 600-604 (1994).</li><li>Ruiz, S. A., Chen, C. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microcontact+printing:+a+tool+to+pattern.">Microcontact printing: a tool to pattern.</a> Soft Matter. 3 (2), 168-177 (2007).</li><li>Perl, A., Reinhoudt, D. N., Huskens, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microcontact+Printing:+Limitations+and+Achievements.">Microcontact Printing: Limitations and Achievements.</a> Advanced Materials (Weinheim, Germany). 21 (22), 2257-2268 (2009).</li><li>Kumar, A., Biebuyck, H. A., Abbott, N. L., Whitesides, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+use+of+self-assembled+monolayers+and+a+selective+etch+to+generate+patterned+gold+features.">The use of self-assembled monolayers and a selective etch to generate patterned gold features.</a> J. Am. Chem. Soc. 114 (23), 9188-9191 (1992).</li><li>Ravoo, B. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Microcontact+chemistry:+surface+reactions+in+nanoscale+confinement.">Microcontact chemistry: surface reactions in nanoscale confinement.</a> Journal of Materials Chemistry. 19 (47), 8902-8906 (2009).</li><li>Biebuyck, H. A., Larsen, N. B., Delamarche, E., Michel, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Lithography+beyond+light:+Microcontact+printing+with+monolayer+resists.">Lithography beyond light: Microcontact printing with monolayer resists.</a> Ibm. J. Res. Dev. 41 (1-2), 159-170 (1997).</li><li>Delamarche, E., Schmid, H., Bietsch, A., Larsen, N. B., Rothuizen, H., Michel, B., Biebuyck, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Transport+Mechanisms+of+Alkanethiols+during+Microcontact+Printing+on+Gold.">Transport Mechanisms of Alkanethiols during Microcontact Printing on Gold.</a> J. Phys. Chem. B. 102 (18), 3324-3334 (1998).</li><li>Larsen, N. B., Biebuyck, H., Delamarche, E., Michel, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Order+in+microcontact+printed+self-assembled+monolayers.">Order in microcontact printed self-assembled monolayers.</a> J Am Chem Soc. 119 (13), 3017-3026 (1997).</li><li>Michel, B., Bernard, A., Bietsch, A., Delamarche, E., Geissler, M., Juncker, D., Kind, H., Renault, J. P., Rothuizen, H., Schmid, H., Schmidt-Winkel, P., Stutz, R., Wolf, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Printing+meets+lithography:+Soft+approaches+to+high-resolution+printing.">Printing meets lithography: Soft approaches to high-resolution printing.</a> IBM Journal of Research and Development. 45 (5), 697-719 (2001).</li><li>Libioulle, L., Bietsch, A., Schmid, H., Michel, B., Delamarche, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Contact-Inking+Stamps+for+Microcontact+Printing+of+Alkanethiols+on+Gold.">Contact-Inking Stamps for Microcontact Printing of Alkanethiols on Gold.</a> Langmuir. 15 (2), 300-304 (1999).</li><li>Sharpe, R. B. A., Burdinski, D., Huskens, J., Zandvliet, H. J. W., Reinhoudt, D. N., Poelsema, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Spreading+of+16-Mercaptohexadecanoic+Acid+in+Microcontact+Printing.">Spreading of 16-Mercaptohexadecanoic Acid in Microcontact Printing.</a> Langmuir. 20 (20), 8646-8651 (2004).</li><li>Workman, R. K., Manne, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Molecular+Transfer+and+Transport+in+Noncovalent+Microcontact+Printing.">Molecular Transfer and Transport in Noncovalent Microcontact Printing.</a> Langmuir. 20 (3), 805-815 (2004).</li><li>Li, X. -. M., Peter, M., Huskens, J., Reinhoudt, D. N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Catalytic+Microcontact+Printing+without+Ink.">Catalytic Microcontact Printing without Ink.</a> Nano Lett. 3 (10), 1449-1453 (2003).</li><li>Shestopalov, A. A., Clark, R. L., Toone, E. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Inkless+Microcontact+Printing+on+Self-Assembled+Monolayers+of+Fmoc-Protected+Aminothiols.">Inkless Microcontact Printing on Self-Assembled Monolayers of Fmoc-Protected Aminothiols.</a> J. Am. Chem. Soc. 129 (145), 13818-13819 (2007).</li><li>Shestopalov, A. A., Clark, R. L., Toone, E. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Catalytic+Microcontact+Printing+on+Chemically+Functionalized+H-Terminated+Silicon.">Catalytic Microcontact Printing on Chemically Functionalized H-Terminated Silicon.</a> Langmuir. 26 (3), 1449-1451 (2010).</li><li>Shestopalov, A. A., Clark, R. L., Toone, E. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Inkless+Microcontact+Printing+on+SAMs+of+Boc-+and+TBS-Protected+Thiols.">Inkless Microcontact Printing on SAMs of Boc- and TBS-Protected Thiols.</a> Nano Lett. 10 (1), 43-46 (2010).</li><li>Snyder, P. W., Johannes, M. S., Vogen, B. N., Clark, R. L., Toone, E. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Biocatalytic+Microcontact+Printing.">Biocatalytic Microcontact Printing.</a> J. Org. Chem. 72 (19), 7459-7461 (2007).</li><li>Morris, C. J., Shestopalov, A. A., Gold, B. H., Clark, R. L., Toone, E. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Patterning+NHS-Terminated+SAMs+on+Germanium.">Patterning NHS-Terminated SAMs on Germanium.</a> Langmuir. 27 (10), 6486-6489 (2011).</li><li>Shestopalov, A. A., Morris, C. J., Vogen, B. N., Hoertz, A., Clark, R. L., Toone, E. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Soft-Lithographic+Approach+to+Functionalization+and+Nanopatterning+Oxide-Free+Silicon.">Soft-Lithographic Approach to Functionalization and Nanopatterning Oxide-Free Silicon.</a> Langmuir. 27 (10), 6478-6485 (2011).</li></ol>

We have nothing to disclose

The presented protocol is a form or of inkless microcontact printing that can be universally applied to any substrate capable of supporting simple well-ordered monolayers. In this method, a stamp-immobilized catalyst transfers a pattern to a surface bearing corresponding functional groups. Because the process does not rely on ink transfer from stamp to surface the diffusive resolution limitation of traditional and reactive &mu;CP is obviated, permitting routine manufacturing of nanoscale objects. The incorporation of a primary highly-ordered molecular system provides complete protection of the underlying semiconductor from oxidation damage. At the same time, the method supports immobilization of bulky reactive groups by utilizing a secondary reactive overlayer; together the system achieves both protection and functionalization.
The technique begins with the formation of stable carbon-surface bonds allowing for chemically inert primary monolayer which serves as an effective barrier to oxide formation. Formation of a secondary reactive overlayer provides terminal NHS functional groups that serve as attachment points for a variety of chemical and biological moieties. This stable bilayered molecular system is subsequently patterned using our catalytic &mu;CP approach. The approach presented in this study offers a general method for patterning semiconductor substrates with a broad range of organic and biological materials. The ability to create patterned organic-semiconductor interfaces without expensive, complex instrumentation offers numerous opportunities in fields such as electronics, nanotechnology, biochemistry and biophysics.

<table border="1">
<tbody>
<tr>
	<th>Name of the reagent</th>
	<th>Company/model</th>
</tr>
<tr>
	<td>XPS spectrometer</td>
	<td>Kratos Axis Ultra</td>
</tr>
<tr>
	<td>Atomic force microscope</td>
	<td>Veeco D3100</td>
</tr>
<tr>
	<td>SEM-FEG microscope</td>
	<td>FEI XL30</td>
</tr>
<tr>
	<td>Fluorescent microscope</td>
	<td>Zeiss Axio Imager</td>
</tr>
<tr>
	<td>Heatblock</td>
	<td>VWR</td>
</tr>
<tr>
	<td>Vacuum pump</td>
	<td>Boc Edwards</td>
</tr>
<tr>
	<td>Water purification system</td>
	<td>Millipore</td>
</tr>
<tr>
	<td>TESP silicon probes</td>
	<td>Veeco</td>
</tr>
<tr>
	<td>Silicon</td>
	<td></td>
</tr>
<tr>
	<td>Pressure Vials</td>
	<td>Chemglass</td>
</tr>
<tr>
	<td>Vacuum manifold</td>
	<td>Chemglass</td>
</tr>
<tr>
	<td>UV Lamp</td>
	<td>UVP</td>
</tr>
<tr>
	<td>Stamp Material</td>
	<td>See references 20 and 18</td>
</tr>
<tr>
	<td>PFTE syringe filters</td>
	<td>VWR</td>
</tr>
<tr>
	<td>Nano Strip</td>
	<td>Cyantek</td>
</tr>
<tr>
	<td>HCl</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Ethanol</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Acetone</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>HF</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Chlorobenzene</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>PCl5</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Propenyl Magnesium Chloride</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Octyl Magnesium Chloride</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Carbon TetraChloride</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Boc protected ethylenediamine</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>TFA</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Sodium 2-mercaptoethanesulfonate </td>
	<td>Sigma</td>
</tr>
<tr>
	<td>4N HCl solution in dioxane</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Lysine-N,N-diacetic acid</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>Et3N</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>DMF</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>NiSO4</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>NaP</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>NaCl</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>imidazole</td>
	<td>Sigma</td>
</tr>
<tr>
	<td>PBS</td>
	<td>Sigma</td>
</tr>
</tbody>
</table>

soft lithographic functionalization and patterning oxide-free silicon and germanium

The development of hybrid electronic devices relies in large part on the integration of (bio)organic materials and inorganic semiconductors through a stable interface that permits efficient electron transport and protects underlying substrates from oxidative degradation. Group IV semiconductors can be effectively protected with highly-ordered self-assembled monolayers (SAMs) composed of simple alkyl chains that act as impervious barriers to both organic and aqueous solutions. Simple alkyl SAMs, however, are inert and not amenable to traditional patterning techniques. The motivation for immobilizing organic molecular systems on semiconductors is to impart new functionality to the surface that can provide optical, electronic, and mechanical function, as well as chemical and biological activity. 
Microcontact printing (&mu;CP) is a soft-lithographic technique for patterning SAMs on myriad surfaces.1-9 Despite its simplicity and versatility, the approach has been largely limited to noble metal surfaces and has not been well developed for pattern transfer to technologically important substrates such as oxide-free silicon and germanium. Furthermore, because this technique relies on the ink diffusion to transfer pattern from the elastomer to substrate, the resolution of such traditional printing is essentially limited to near 1 &mu;m.10-16
In contrast to traditional printing, inkless &mu;CP patterning relies on a specific reaction between a surface-immobilized substrate and a stamp-bound catalyst. Because the technique does not rely on diffusive SAM formation, it significantly expands the diversity of patternable surfaces. In addition, the inkless technique obviates the feature size limitations imposed by molecular diffusion, facilitating replication of very small (&lt;200 nm) features.17-23 However, up till now, inkless &mu;CP has been mainly used for patterning relatively disordered molecular systems, which do not protect underlying surfaces from degradation.
Here, we report a simple, reliable high-throughput method for patterning passivated silicon and germanium with reactive organic monolayers and demonstrate selective functionalization of the patterned substrates with both small molecules and proteins. The technique utilizes a preformed NHS-reactive bilayered system on oxide-free silicon and germanium. The NHS moiety is hydrolyzed in a pattern-specific manner with a sulfonic acid-modified acrylate stamp to produce chemically distinct patterns of NHS-activated and free carboxylic acids. A significant limitation to the resolution of many &mu;CP techniques is the use of PDMS material which lacks the mechanical rigidity necessary for high fidelity transfer. To alleviate this limitation we utilized a polyurethane acrylate polymer, a relatively rigid material that can be easily functionalized with different organic moieties. Our patterning approach completely protects both silicon and germanium from chemical oxidation, provides precise control over the shape and size of the patterned features, and gives ready access to chemically discriminated patterns that can be further functionalized with both organic and biological molecules. The approach is general and applicable to other technologically-relevant surfaces.

Watch this Scientific Journal Video about Soft Lithographic Functionalization and Patterning Oxide-free Silicon and Germanium at JoVE.com

Soft Lithographic Functionalization and Patterning Oxide-free Silicon and Germanium

Here we describe a simple method for patterning oxide-free silicon and germanium with reactive organic monolayers and demonstrate functionalization of the patterned substrates with small molecules and proteins. The approach completely protects surfaces from chemical oxidation, provides precise control over feature morphology, and provides ready access to chemically discriminated patterns.

The development of hybrid electronic devices relies in large part on the integration of (bio)organic materials and inorganic semiconductors through a ...

soft-lithographic-functionalization-patterning-oxide-free-silicon

Research

JoVE Journal

Bioengineering

14.6K Görüntüleme.  Duke University. Burada, küçük moleküller ve proteinlerin desenli yüzeylerin desenlendirme oksit-silisyum ve germanyum ve reaktif organik mono tabakaları göstermek işlevsellik için basit bir yöntem açıklanmaktadır. Bu yaklaşım tamamen kimyasal oksidasyon yüzeyleri korur özelliği morfolojisi üzerinde hassas kontrol sağlar, ve kimyasal ayrımcılık desenleri hazır erişim sağlar.