Name: adsorption device based on a langatate crystal microbalance for high temperature high pressure gas adsorption in zeolite h-zsm-5
Uploaded: 2016-08-25T14:00:00
Duration: 9 min 46 s
Description: Watch this Scientific Journal Video about Adsorption Device Based on a Langatate Crystal Microbalance for High Temperature High Pressure Gas Adsorption in Zeolite H-ZSM-5 at JoVE.com

This research has been funded by Deutsche Forschungsgemeinschaft (DFG) within the framework of the priority program 1570: porous media with defined pore system in process engineering - modeling, application, synthesis, under grant numbers DI 696/9-1 to -3 and SCHW 478/23-1 to -3.

Caution: Please consult all relevant material safety data sheets (MSDS) before use. Several of the chemicals used in the synthesis of zeolite H-ZSM-5 are acutely toxic and carcinogenic. Nanomaterials may have additional risks compared to their bulk counterpart. Please use all appropriate safety practices when performing a nanocrystal reaction including the use of engineering controls (fume hood, glovebox) and personal protective equipment (safety glasses, gloves, lab coat, full length pants, closed-toe shoes). Moreover, pay special attention when, performing the adsorption measurements with methanol and DME, since both are flammable and explosive dangerous materials.
1. Synthesis of Zeolite H-ZSM-5 on the LCM
<ol>
	<li>Preparation of a zeolite synthesis mixture 
	Note: The final synthesis mixture had the following molar composition as adapted from de la Iglesia et al.7: 1 SiO2 : 50 H2O : 0.07 Na2O : 0.024 TPA2O : 0.005 Al2O3. Thus, the theoretical Si/Al molar ratio of the synthesized zeolite H-ZSM-5 is 100.
	<ol>
		<li>Dissolve 0.14 g sodium hydroxide in 20.30 g de-ionized water via stirring. Alternatively, mix 3.64 g of 1 M NaOH with 16.8 g de-ionized water.</li>
		<li>Add 1.16 g tetrapropylammonium hydroxide (TPAOH) solution, and stir the solution until it appears clear.</li>
		<li>Add 5.0 g tetraethyl orthosilicate (TEOS) solution dropwise, and stir the solution until it appears clear.</li>
		<li>Keep stirring, while adding 0.09 g aluminum nitrate nonahydrate (Al(NO3)3&#183;9H2O, solid) into the solution.</li>
		<li>Keep stirring until the solid aluminum nitrate nonahydrate is dissolved. Note that the prepared zeolite synthesis mixture should be used within 5 hr due to its aging.</li>
	</ol>
	</li>
	<li>Synthesis of zeolite ZSM-5 on the LCM via SAC3
	<ol>
		<li>Clean the LCM before the zeolite synthesis
		<ol>
			<li>Wash the LCM thoroughly with the de-ionized water.</li>
			<li>Put the LCM in a beaker with the de-ionized water, and clean it in an ultrasound bath.</li>
			<li>Dry the LCM at 80 &#176;C in an oven.</li>
		</ol>
		</li>
		<li>Zeolite synthesis
		<ol>
			<li>Carefully place several drops of the prepared zeolite synthesis mixture on the electrode in the center of the LCM as shown in Figure 1 using a pipette, since only the zeolite deposited on the gold electrode can cause the resonant frequency shift of the LCM8. Moreover, avoid spreading the synthesis mixture on the connection points of the gold electrodes to the oscillator, since the zeolite on the connection points would significantly reduce the electroconductivity and thus the measurement sensitivity of the LCM. In addition, removing the zeolite crystals on the connection points after the deposition will destroy the electrodes.</li>
			<li>Dry the LCM with the synthesis mixture at 80 &#176;C for 2 hr to obtain a highly viscous gel-like phase on it.</li>
			<li>Add a small amount of de-ionized water (about 10 ml) in a Teflon-lined autoclave (80 ml) in order to produce the steam during the zeolite synthesis.</li>
			<li>Put the Teflon holder in the autoclave, which supports the LCM horizontally above the liquid water at the bottom of the autoclave during the zeolite synthesis.</li>
			<li>Keep the autoclave in an oven at 150 &#176;C for 48 hr to synthesize the zeolite on the LCM via the SAC method.</li>
			<li>Right after the SAC, wash the coated LCM with the de-ionized water and dry it at 80 &#176;C for 2 hr.</li>
			<li>Remove the organic template in the zeolite crystals by calcination in a high-temperature oven under an oxidative atmosphere. Program the oven as follows: a) Increase the temperature from ambient to 450 &#176;C at a rate of 3 &#176;C min-1; b) Keep the temperature at 450 &#176;C for 4 hr; c) Decrease the temperature from 450 &#176;C to room temperature at a rate of 3 &#176;C min-1.</li>
			<li>Dissolve 26.75 g ammonium chloride (NH4Cl, solid) in 0.4 L de-ionized water. Add more de-ionized water in the solution so that the final NH4Cl solution is 0.5 L and has the concentration of 1 mol dm-3.</li>
			<li>Put the coated LCM into the NH4Cl solution (0.2 L) in a beaker, and ion-exchange the Na-ZSM-5 crystals coated on the LCM at 20 &#176;C for 2 hr. Repeat the ion-exchange using 0.2 L fresh NH4Cl solution to get the NH4-ZSM-5 crystals.</li>
			<li>Obtain the H-ZSM-5 by final calcination using the same parameters as mentioned in Step 1.2.2.7.</li>
		</ol>
		</li>
	</ol>
	</li>
</ol>
2. Adsorption Measurements Using the LCM-based Adsorption Measurement Device3
Note: In this work, the LCM without coating and the one coated with H-ZSM-5 (prepared in the last section) is termed &#34;reference LCM&#34; and &#34;sample LCM&#34;, respectively. Moreover, the sample LCM before zeolite deposition is termed &#34;unloaded sample LCM&#34;. In a previous publication in Journal of Physical Chemistry C3, a detailed description of the LCM-based adsorption measurement device can be found. In this work, the operation of the device for gas adsorption measurements is presented in this short protocol and in the video protocol in detail.
<ol>
	<li>Preparation before adsorption measurements
	<ol>
		<li>Tests on the effects of temperature and pressure on the difference in resonant frequencies of the reference and unloaded sample LCMs
		<ol>
			<li>Clean the O-ring, the LCM holder, and the sample chamber with acetone and pressed air.</li>
			<li>Put the reference and unloaded sample LCMs in a beaker with de-ionized water and clean them in an ultrasound bath.</li>
			<li>Carefully place the clean reference and unloaded sample LCMs on the LCM holder, which is connected to the oscillator via high temperature resistant electric cables.</li>
			<li>Pretest the installed LCMs using the oscillator to ensure that the resonant frequencies can be detected successfully.</li>
			<li>Close the sample chamber, and evacuate it by a vacuum pump.</li>
			<li>Change the pressure in the sample chamber via dosing pure N2.</li>
			<li>Control the temperature inside the sample chamber by a temperature controller.</li>
			<li>Measure the resonant frequencies of the reference and unloaded sample LCMs in the studied temperature and pressure ranges, i.e., 50-150 &#176;C and 0-16 bar, in order to know the effect of temperature and pressure on the difference in resonant frequencies of the reference and unloaded sample LCMs (<img alt="Equation 2" src="/files/ftp_upload/54413/54413eq2.jpg" /> in Step 2.2.4). The tests show that <img alt="Equation 2" src="/files/ftp_upload/54413/54413eq2.jpg" /> is significantly affected by the temperature (1,200 to 3,000 Hz at 50-150 &#176;C), whereas the gas pressure has no significant effect (change of <img alt="Equation 2" src="/files/ftp_upload/54413/54413eq2.jpg" /> smaller than 300 Hz in the pressure range of 0-16 bar). Use the determined values of <img alt="Equation 2" src="/files/ftp_upload/54413/54413eq2.jpg" /> in the Sauerbrey equation in Step 2.2.4 to calculate the adsorbed amount of gases on the zeolite.</li>
		</ol>
		</li>
		<li>Activation of sample LCM
		<ol>
			<li>Clean the O-ring, the LCM holder, and the sample chamber with acetone and pressed air.</li>
			<li>Put the reference LCM in a beaker with de-ionized water, and clean it in an ultrasound bath.</li>
			<li>Carefully place the clean reference LCM and sample LCM on the LCM holder, which is connected to the oscillator via high temperature resistant electric cables.</li>
			<li>Pretest the placed LCMs using the oscillator to ensure that the resonant frequencies can be detected successfully.</li>
			<li>Close the sample chamber, and evacuate it by a vacuum pump.</li>
			<li>Activate the sample LCM at high temperatures (at least 50 &#176;C higher than the temperatures of the adsorption measurements, 200 &#176;C in this work) in vacuum condition overnight to ensure that only a negligible gas amount is adsorbed on the H-ZSM-5.</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>Adsorption measurements 
	Note: In this work, the adsorption measurement of CO2 at 50 &#176;C is presented to give an example. The obtained data from the measurement (e.g., resonant frequencies) and the calculated masses of adsorbed CO2 on the H-ZSM-5 can be found in Table S1 of the Supporting Information of our previous publication3.
	<ol>
		<li>Adjust the temperature inside the sample chamber at the desired temperature of the adsorption measurements (i.e., 50 &#177; 0.1 &#176;C) by a temperature controller, under vacuum conditions, i.e., only with a negligible amount of adsorbed gas.</li>
		<li>Connect the oscillator to the sample LCM, and measure its resonant frequency by the supporting software of the oscillator via fitting the experimental data with a Butterworth-Van Dyke equivalent circuit model.</li>
		<li>Switch the connection of the oscillator to the reference LCM, and measure its resonant frequency.</li>
		<li>Use the measured resonant frequencies of the sample and reference LCMs under vacuum conditions to determine the mass of H-ZSM-5 deposited on the sample LCM (without adsorbed gas) according to the Sauerbrey equation2, 8: 
		<img alt="Equation 3" src="/files/ftp_upload/54413/54413eq3.jpg" />&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160;&#160; 
		where <img alt="Equation 4" src="/files/ftp_upload/54413/54413eq4.jpg" /> is the difference in mass in g, <img alt="Equation 5" src="/files/ftp_upload/54413/54413eq5.jpg" /> is the number of the harmonic at which the crystal is driven (in this study, <img alt="Equation 6" src="/files/ftp_upload/54413/54413eq6.jpg" />), <img alt="Equation 7" src="/files/ftp_upload/54413/54413eq7.jpg" /> is the difference in resonant frequencies of reference and sample LCMs in Hz, <img alt="Equation 2" src="/files/ftp_upload/54413/54413eq2.jpg" /> is the difference of the resonant frequencies between the reference and unloaded sample LCM in Hz, <img alt="Equation 8" src="/files/ftp_upload/54413/54413eq8.jpg" /> is the density of the langatate crystal (6.13 g cm&#8722;3)4, <img alt="Equation 9" src="/files/ftp_upload/54413/54413eq9.jpg" /> is the effective piezoelectrically stiffened shear modulus of the langatate crystal (1.9&#215;1012 g cm&#8722;1 sec&#8722;2)4, <img alt="Equation 10" src="/files/ftp_upload/54413/54413eq10.jpg" /> is the resonant frequency of the reference LCM, i.e., the unloaded LCM, <img alt="Equation 11" src="/files/ftp_upload/54413/54413eq11.jpg" />, the area of the LCM (1.539 cm2)3. 
		Note: In this work, the mass of H-ZSM-5 deposited on the gold electrode in the center of the LCM is 0.502 mg, which causes a resonant frequency shift of 14,100 Hz at 50 &#176;C.</li>
		<li>Control the gas pressure of CO2 inside the sample chamber by dosing pure gas from the gas cylinder via a mass flow controller (for methanol and DME, from the evaporator manually via a dosing valve into the chamber), or by evacuation via a vacuum pump. Here, use a pressure range of CO2 adsorption measurements of 0-16 bar as shown in Figure 2.</li>
		<li>Wait until equilibrium conditions and a stable temperature have been reached, e.g., the temperature varies within 50 &#177; 0.1 &#176;C.</li>
		<li>Connect the oscillator to the sample LCM, and measure its resonant frequency after exposure to the gas at a given pressure.</li>
		<li>Switch the connection of the oscillator to the reference LCM, and measure its resonant frequency under the same conditions.</li>
		<li>According to the Sauerbrey equation shown above, calculate the total mass of H-ZSM-5 deposited on the sample LCM and gas adsorbed on the H-ZSM-5 under this gas pressure. By subtracting the mass of H-ZSM-5 (without adsorbed gas) determined in Step 2.2.4, the mass of CO2 adsorbed on the H-ZSM-5 under this gas pressure is obtained.</li>
		<li>Repeat the resonant frequency measurements for sample and reference LCMs for varying pressures, in order to obtain all the masses of CO2 adsorbed on the H-ZSM-5 sample under different gas pressures.</li>
		<li>Finally, obtain the gas adsorption isotherm at 50 &#176;C in the studied pressure range of 0-16 bar via calculating all the masses of CO2 adsorbed on the H-ZSM-5 sample under different gas pressures according to Step 2.2.9.</li>
		<li>For adsorption isotherms at other temperatures, change the stable temperature using the temperature controller, and repeat Steps 2.2.1 to 2.2.11.</li>
		<li>Fit the adsorption isotherms with adsorption models like Langmuir models via the least squares method to determine the adsorption parameters like adsorption capacities, adsorption enthalpies, and adsorption entropies (see previous publication3 and its Supporting Information).</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Tsionsky, V., Gileadi, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Use+of+the+Quartz+Crystal+Microbalance+for+the+Study+of+Adsorption+from+the+Gas+Phase.">Use of the Quartz Crystal Microbalance for the Study of Adsorption from the Gas Phase.</a> Langmuir. 10, 2830-2835 (1994).</li><li>Venkatasubramanian, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gas+Adsorption+Characteristics+of+Metal-Organic+Frameworks+via+Quartz+Crystal+Microbalance+Techniques.">Gas Adsorption Characteristics of Metal-Organic Frameworks via Quartz Crystal Microbalance Techniques.</a> J. Phys. Chem. C. 116, 15313-15321 (2012).</li><li>Ding, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Investigation+of+High-Temperature+and+High-Pressure+Gas+Adsorption+in+Zeolite+H-ZSM-5+via+Langatate+Crystal+Microbalance:+CO2,+H2O,+Methanol+and+Dimethyl+Ether.">Investigation of High-Temperature and High-Pressure Gas Adsorption in Zeolite H-ZSM-5 via Langatate Crystal Microbalance: CO2, H2O, Methanol and Dimethyl Ether.</a> J. Phys. Chem. C. 119, 23478-23485 (2015).</li><li>Davulis, P. M., Pereira da Cunha, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-Temperature+Langatate+Elastic+Constants+and+Experimental+Validation+up+to+900+&#176;C.">High-Temperature Langatate Elastic Constants and Experimental Validation up to 900 &#176;C.</a> IEEE Trans Ultrason Ferroelectr Freq Control. 57, 59-65 (2010).</li><li>Ding, W., Li, H., Pfeifer, P., Dittmeyer, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Crystallite-Pore+Network+Model+of+Transport+and+Reaction+of+Multicomponent+Gas+Mixtures+in+Polycrystalline+Microporous+Media.">Crystallite-Pore Network Model of Transport and Reaction of Multicomponent Gas Mixtures in Polycrystalline Microporous Media.</a> Chem. Eng. J. 254, 545-558 (2014).</li><li>Ding, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Simulation+of+One-Stage+Dimethyl+Ether+Synthesis+over+Core/Shell+Catalyst+in+Tube+Reactor.">Simulation of One-Stage Dimethyl Ether Synthesis over Core/Shell Catalyst in Tube Reactor.</a> Chem Ing Tech. 87, 702-712 (2015).</li><li>de la Iglesia, O., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+of+Pt/ZSM-5+Films+on+Stainless+Steel+Microreactors.">Preparation of Pt/ZSM-5 Films on Stainless Steel Microreactors.</a> Catal. Today. 125, 2-10 (2007).</li><li>Sauerbrey, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Verwendung+von+Schwingquartzen+zur+W&#228;gung+d&#252;nner+Schichten+und+zur+Mikrow&#228;gung.">Verwendung von Schwingquartzen zur W&#228;gung d&#252;nner Schichten und zur Mikrow&#228;gung.</a> Zeitschrift f&#252;r Physik. 155, 206-222 (1959).</li><li>Wirawan, S. K., Creaser, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=CO2+Adsorption+on+Silicalite-1+and+Cation+Exchanged+ZSM-5+Zeolites+Using+a+Step+Change+Response+Method.">CO2 Adsorption on Silicalite-1 and Cation Exchanged ZSM-5 Zeolites Using a Step Change Response Method.</a> Microporous Mesoporous Mater. 91, 196-205 (2006).</li><li>Choudhary, V. R., Mayadevi, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adsorption+of+Methane,+Ethane,+Ethylene,+and+Carbon+Dioxide+on+High+Silica+Pentasil+Zeolites+and+Zeolite-like+Materials+Using+Gas+Chromatography+Pulse+Technique.">Adsorption of Methane, Ethane, Ethylene, and Carbon Dioxide on High Silica Pentasil Zeolites and Zeolite-like Materials Using Gas Chromatography Pulse Technique.</a> Sep. Sci. Technol. 28, 2197-2209 (1993).</li><li>Choudhary, V. R., Mayadevi, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Adsorption+of+Methane,+Ethane,+Ethylene,+and+Carbon+Dioxide+on+Silicalite-I.">Adsorption of Methane, Ethane, Ethylene, and Carbon Dioxide on Silicalite-I.</a> Zeolites. 17, 501-507 (1996).</li><li>Zhu, W. D., Hrabanek, P., Gora, L., Kapteijn, F., Moulijn, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Role+of+Adsorption+in+the+Permeation+of+CH4+and+CO2+through+a+Silicalite-1+Membrane.">Role of Adsorption in the Permeation of CH4 and CO2 through a Silicalite-1 Membrane.</a> Ind. Eng. Chem. Res. 45, 767-776 (2006).</li></ol>

The authors have nothing to disclose.

In this work, the successful synthesis of the zeolite H-ZSM-5 crystals on the gold electrode in the center of the LCM sensor by SAC is demonstrated, i.e., the zeolite is successfully loaded on the LCM sensor without covering the connection points of the gold electrodes to the oscillator. Thus, the zeolite can oscillate together with the LCM sensor, while the LCM sensor keeps its good electroconductivity and measurement sensitivity. Compared to the conventional QCM devices which are limited below 80 &#176;C, the LCM device presented in this work is successfully used for the adsorption measurements at temperatures as high as 150 &#176;C, i.e., at or close to the temperature of reactions in industry. However, the present LCM device is limited below 200 &#176;C. At temperatures higher than 200 &#176;C, the measurement uncertainty may exceed the mass of the adsorbed gas, since, with the increasing temperature above 150 &#176;C, the mass of the adsorbed gas has a significant decrease, whereas the measurement uncertainty increases significantly due to the decreasing temperature control precision. Thus, in future experiments, a new method should be developed to deposit more zeolite on the LCM, which causes more gas to adsorb, and moreover compensates the effect of the temperature and pressure on <img alt="Equation 2" src="/files/ftp_upload/54413/54413eq2.jpg" />. This could help to extend the application range of the LCM device to higher temperatures.
During the experiment, the critical steps in the zeolite synthesis are Steps 1.2.2.1, 1.2.2.4, 1.2.2.5 and 1.2.2.7, while those in the adsorption measurements are Steps 2.1.1.3, 2.1.1.4, 2.2.1, 2.2.5 and 2.2.6. In Step 1.2.2.1, avoid placing too much of the synthesis mixture on the LCM, which would spread on the connection points of the gold electrodes. In Step 1.2.2.4, carefully put the Teflon holder with the LCM in the autoclave to ensure that the LCM is horizontal and does not contact the liquid water at the bottom. In Steps 1.2.2.5 and 1.2.2.7, do not use a higher temperature in the zeolite synthesis and calcination, since our previous experiments show that it leads to degradation of the LCM. In the adsorption measurements, the position of the LCM sensors has a significant effect on the connectivity of the LCM sensors to the oscillator, and therefore on the quality of the resonant frequency signals. Therefore, pay special attention to Steps 2.1.1.3 and 2.1.1.4, in which the LCMs are loaded on the holder and pretested. The LCMs should be in the position that they are connected with the oscillator via the connection points of the electrodes (indicated in Figure 1). This is mandatory to obtain high quality resonant frequency signals enabling high measurement accuracy. In addition, in Steps 2.2.1 and 2.2.6, ensure that a stable temperature is achieved before the measurements, since this also increases the measurement accuracy. Moreover, in Step 2.2.5, feed the gas slowly, in order to have a small change of the temperature inside. This helps the temperature to become stable again after a short time.
Since the SAC synthesis method for zeolite H-ZSM-5 on the LCM sensor could be extended to other zeolites easily, the LCM-based adsorption measurement device is expected to be used for them as well. Moreover, due to its high accuracy and low cost, this device is expected to be applicable to any material, which could be coated on the LCM, in order to investigate its adsorption properties at high temperatures.

Adsorption properties strongly influence the performance of catalytic materials, hence precise knowledge of these properties can assist in characterization, design and optimization of such materials. However, the adsorption properties are generally judged from single-component adsorption measurements often at room temperatures or even under liquid nitrogen conditions, and therefore an extension to practical situations may lead to a severe deviation from the real behavior. In situ adsorption measurements on catalytic materials, especially at high temperature and high pressure conditions, still remain a great challenge.
An adsorption measurement device based on a quartz crystal microbalance (QCM) is advantageous over the commercialized volumetric and gravimetric methods in a way that it is highly accurate for mass sorption applications, satisfactorily stable in a controlled environment, and more affordable1-2. However, the conventional QCM analysis is limited to temperatures below 80 &#176;C1-2. In order to overcome this limitation, we developed an adsorption measurement device based on a high-temperature high-frequency oscillating microbalance (langatate crystal microbalance, LCM)3, which can realize the adsorption measurements in principle at temperatures as high as 200-300 &#176;C, owing to the absence of crystalline-phase transitions up to its melting point (1,470 &#176;C)4. The LCMs used in this work have an AT-cut (i.e., the plate of the crystal microbalance contains the x axis of the crystal and is inclined by 35&#176;15&#39; from the z axis) and a resonant frequency of 5 MHz. This device was applied to the adsorption measurements of CO2, H2O, methanol, and dimethyl ether (DME), each in gaseous state, on zeolite H-ZSM-5 in the temperature range of 50-150 &#176;C and pressure range of 0-18 bar3, aiming at the validation of simulation models for the optimization of bifunctional core-shell catalysts for one-stage production of DME from the synthesis gas5-6. How to operate this device for gas adsorption measurements is presented in the protocol section.
Prior to the adsorption measurements, zeolite H-ZSM-5 crystallites (0.502 mg) were synthesized on the gold electrode in the center of the LCM by the steam-assisted crystallization (SAC) method according to de la Iglesia et al.7, in such a way that the zeolite crystallites remain attached to the oscillating microbalance. As shown in Figure 1, the LCM used in the adsorption measurement device has polished gold electrodes on both sides, which help to connect the LCM to an oscillator. Since the zeolite crystals on the connection points of the gold electrodes to the oscillator would significantly reduce the electroconductivity (as indicated in Figure 1) and thus the measurement sensitivity of the LCM, the zeolite H-ZSM-5 crystals were deposited on the LCM via the SAC method not covering these connection points3. The details about the synthesis of zeolite H-ZSM-5 on LCM are briefly summarized in the following protocol section and shown in the video protocol in detail.

<table border="0" cellpadding="0" cellspacing="0" width="813">
	<tbody>
		<tr height="49">
			<td height="49" style="height:50px;width:239px;">tetraethyl orthosilicate (TEOS), other name: tetraethoxysilane</td>
			<td style="width:213px;">Alfa Aesar</td>
			<td style="width:135px;">A14965</td>
			<td style="width:227px;">purity &#62; 98&#160;%, acutely toxic, inflammable and explosive&#160;</td>
		</tr>
		<tr height="50">
			<td height="50" style="height:51px;width:239px;">aluminum nitrate nonahydrate: Al(NO3)3*9H2O</td>
			<td style="width:213px;">Chempur</td>
			<td style="width:135px;">000176</td>
			<td style="width:227px;">purity &#62; 98.5&#160;%</td>
		</tr>
		<tr height="53">
			<td height="53" style="height:54px;width:239px;">tetrapropylammonium hydroxide: (TPAOH)</td>
			<td style="width:213px;">Sigma-Aldrich</td>
			<td style="width:135px;">254533</td>
			<td style="width:227px;">1&#160;mol&#160;dm-3 aqueous solution, skin corrosive</td>
		</tr>
		<tr height="32">
			<td height="32" style="height:33px;width:239px;">sodium hydroxide: NaOH</td>
			<td style="width:213px;">Merck</td>
			<td style="width:135px;">106498</td>
			<td style="width:227px;">purity &#62; 99&#160;%, skin corrosive</td>
		</tr>
		<tr height="32">
			<td height="32" style="height:33px;width:239px;">Ammonium chloride: NH4Cl</td>
			<td style="width:213px;">Merck</td>
			<td style="width:135px;">101145</td>
			<td style="width:227px;">purity &#62; 99.8&#160;%, harmful</td>
		</tr>
		<tr height="34">
			<td height="34" style="height:35px;width:239px;">Carbon dioxide (CO2)</td>
			<td style="width:213px;">Air Liquide</td>
			<td style="width:135px;">---</td>
			<td style="width:227px;">purity &#62; 99.7&#160;%</td>
		</tr>
		<tr height="53">
			<td height="53" style="height:54px;width:239px;">high-pressure stainless steel chamber</td>
			<td style="width:213px;">B&#252;chi AG, Uster, Switzerland</td>
			<td style="width:135px;">Midiclave</td>
			<td style="width:227px;">Volume = 300 mL, up to 200 bar, 300 &#176;C</td>
		</tr>
		<tr height="72">
			<td height="72" style="height:73px;width:239px;">langatate crystal microbalance sensors</td>
			<td style="width:213px;">C3 Prozess- and Analysentechnik GmbH, Munich, Germany</td>
			<td style="width:135px;">---</td>
			<td style="width:227px;">Diameter: 14 mm, resonant frequency: 5 MHz</td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:239px;">high-frequency oscillating microbalance</td>
			<td style="width:213px;">Gamry Instruments, Warminster, USA</td>
			<td style="width:135px;">eQCM 10M</td>
			<td style="width:227px;">Frequency range: 1 MHz - 10 MHz (15 MHz), resolution: 20 mHz</td>
		</tr>
	</tbody>
</table>

adsorption device based on a langatate crystal microbalance for high temperature high pressure gas adsorption in zeolite h-zsm-5

We present a high-temperature and high-pressure gas adsorption measurement device based on a high-frequency oscillating microbalance (5 MHz langatate crystal microbalance, LCM) and its use for gas adsorption measurements in zeolite H-ZSM-5. Prior to the adsorption measurements, zeolite H-ZSM-5 crystals were synthesized on the gold electrode in the center of the LCM, without covering the connection points of the gold electrodes to the oscillator, by the steam-assisted crystallization (SAC) method, so that the zeolite crystals remain attached to the oscillating microbalance while keeping good electroconductivity of the LCM during the adsorption measurements. Compared to a conventional quartz crystal microbalance (QCM) which is limited to temperatures below 80 &#176;C, the LCM can realize the adsorption measurements in principle at temperatures as high as 200-300 &#176;C (i.e., at or close to the reaction temperature of the target application of one-stage DME synthesis from the synthesis gas), owing to the absence of crystalline-phase transitions up to its melting point (1,470 &#176;C). The system was applied to investigate the adsorption of CO2, H2O, methanol and dimethyl ether (DME), each in the gas phase, on zeolite H-ZSM-5 in the temperature and pressure range of 50-150 &#176;C and 0-18 bar, respectively. The results showed that the adsorption isotherms of these gases in H-ZSM-5 can be well fitted by Langmuir-type adsorption isotherms. Furthermore, the determined adsorption parameters, i.e., adsorption capacities, adsorption enthalpies, and adsorption entropies, compare well to literature data. In this work, the results for CO2 are shown as an example.

Figure 1 shows the photographs, light microscopy and scanning electron microscopy (SEM) images of the coated and uncoated LCM sensor (left), as well as their X-ray diffraction (XRD) patterns (right). From both, light and scanning electron microscopy (Figure 1b and c), the connection points of the gold electrodes to the oscillator are less covered with zeolite crystals than the center region of the LCM. Most of the zeolite crystals on top of the LCM-sensor are isolated and show characteristic rounded-boat morphology, with the (010)-plane predominantly facing up. Besides, some crystals additionally show the typical intergrowth behavior (&#34;twinned crystals&#34;). Moreover, the loaded H-ZSM-5 (Si/Al molar ratio of 100 according to the composition of the synthesis mixture) on the langatate crystal has been investigated by XRD and wavelength-dispersive X-ray (WDX) spectroscopy3.
In Figure 2, CO2 adsorption isotherms for the H-ZSM-5 zeolite obtained with the LCM device in the temperature range of 50-150 &#176;C and pressure range of 0-16 bar, as well as the fit of the single site Langmuir isotherm model to the experimental data, are shown to give a representative example. As shown in Figure 2, the determined adsorption isotherms of CO2 were fitted with a single site Langmuir isotherm well. Figure 3 shows the diagram of ln(K&#39;i) vs. 1,000/T for CO2 as derived from the adsorption isotherms, i.e., the temperature dependence of the adsorption constants determined from the fit of the adsorption isotherms. The adsorption enthalpies and entropies of CO2 were determined by fitting with the van&#39;t Hoff equation (see the Supporting Information of the previous publication3). The results of the model fitting show that the adsorption capacity, adsorption enthalpy and adsorption entropy for CO2 in H-ZSM-5 are 4.0 &#177; 0.2 mmol g-1, 15.3 &#177; 0.5 kJ mol-1 and 56.3 &#177; 1.5 J mol-1 K-1, respectively3.
The high quality of the fit of the single site Langmuir isotherm and the van&#39;t Hoff equation as shown in Figures 2 and 3 supports the assumption of a constant adsorption capacity (i.e., saturation loading) and enthalpy (i.e., heat of adsorption) to be valid at least for the range of conditions used. Moreover, the adsorption parameters of CO2 determined by the LCM-based adsorption measurement device in this work compare well to values reported in literature9-12, i.e., the adsorption capacity, adsorption enthalpy and adsorption entropy reported for CO2 in MFI-type zeolites vary in the range of 2.1-3.8 mmol g-1, 19-28.7 kJ mol-1, and 43.7-82.7 J mol-1 K-1, respectively, in the temperature range of 30-200 &#176;C and pressure range of 0-5 bar.
<img alt="Figure 1" src="/files/ftp_upload/54413/54413fig1.jpg" /> 
Figure 1. Coated langatate crystal microbalance sensor (left). (a) Photographs of the coated and uncoated sensor (right), (b) light microscopy and (c) scanning electron microscopy images. The X-ray diffraction patterns of coated and uncoated LCM sensor (right). This figure has been modified from a previous publication3. Reprinted with the permission of American Chemical Society (Copyright 2015). <a href="https://www.jove.com/files/ftp_upload/54413/54413fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" src="/files/ftp_upload/54413/54413fig2.jpg" /> 
Figure 2. Adsorption isotherms for CO2 in H-ZSM-5 at 50 (<img alt="Equation 12" src="/files/ftp_upload/54413/54413eq12.jpg" />), 75 (<img alt="Equation 13" src="/files/ftp_upload/54413/54413eq13.jpg" />), 100 (<img alt="Equation 14" src="/files/ftp_upload/54413/54413eq14.jpg" />), and 150 &#176;C (<img alt="Equation 15" src="/files/ftp_upload/54413/54413eq15.jpg" />). The symbols represent the experimental data, the error bars indicate the measurement uncertainty of the resonant frequencies caused by, e.g., the temperature instability, and calculated according to the Sauerbrey equation as described in Step 2.2.4, and the lines represent the fit of the single site Langmuir isotherm model to the experimental data. This figure has been modified from a previous publication3. Reprinted with the permission of American Chemical Society (Copyright 2015). <a href="https://www.jove.com/files/ftp_upload/54413/54413fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" src="/files/ftp_upload/54413/54413fig3.jpg" /> 
Figure 3. ln(Ki) vs. 1,000/T to determine adsorption enthalpies and entropies for CO2. This figure has been modified from a previous publication3. Reprinted with the permission of American Chemical Society (Copyright 2015). <a href="https://www.jove.com/files/ftp_upload/54413/54413fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

Watch this Scientific Journal Video about Adsorption Device Based on a Langatate Crystal Microbalance for High Temperature High Pressure Gas Adsorption in Zeolite H-ZSM-5 at JoVE.com

Adsorption Device Based on a Langatate Crystal Microbalance for High Temperature High Pressure Gas Adsorption in Zeolite H-ZSM-5

A protocol for high-temperature and high-pressure gas adsorption measurements on zeolite H-ZSM-5 using an adsorption measurement device based on a langatate crystal microbalance is presented. Prior to the adsorption measurements, the synthesis of zeolite H-ZSM-5 on the langatate crystal microbalance sensor by the steam-assisted crystallization (SAC) method is demonstrated.

We present a high-temperature and high-pressure gas adsorption measurement device based on a high-frequency oscillating microbalance (5 MHz langatate ...

Research

JoVE Journal

Engineering

Synthesis and Microdiffraction at Extreme Pressures and Temperatures

High pressure compounds and polymorphs are investigated for a broad range of purposes such as determine structures and processes of deep planetary ...

Fiber Optic Distributed Sensors for High-resolution Temperature Field Mapping

The reliability of computational fluid dynamics (CFD) codes is checked by comparing simulations with experimental data. A typical data set consists ...

Applying X-ray Imaging Crystal Spectroscopy for Use as a High Temperature Plasma Diagnostic

X-ray spectra provide a wealth of information on high temperature plasmas; for example electron temperature and density can be inferred from line ...

A High Performance Impedance-based Platform for Evaporation Rate Detection

This paper describes the method of a novel impedance-based platform for the detection of the evaporation rate. The model compound hyaluronic acid was ...

Nanostructured Ag-zeolite Composites as Luminescence-based Humidity Sensors

Small silver clusters confined inside zeolite matrices have recently emerged as a novel type of highly luminescent materials. Their emission has high ...

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia YSZ Scaffolds by In Situ Carbon Templating Xerogels

We demonstrate a method for the high temperature fabrication of porous, nanostructured yttria-stabilized-zirconia (YSZ, 8 mol% yttria - 92 mol% zirconia) ...

Preparation and High-temperature Anti-adhesion Behavior of a Slippery Surface on Stainless Steel

Anti-adhesion surfaces with high-temperature resistance have a wide application potential in electrosurgical instruments, engines, and pipelines. A ...

Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way

To improve the accuracy of the chloride distribution along the depth of cement paste under cyclic wet-dry conditions, a new method is proposed to obtain a ...

Method for Recording Broadband High Resolution Emission Spectra of Laboratory Lightning Arcs

Lightning is one of the most common and destructive forces in nature and has long been studied using spectroscopic techniques, first with traditional ...

Radio Frequency Magnetron Sputtering of GdBa2Cu3O7&#8722;&#948;/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 (STO) Single-crystal Substrates

Radio Frequency Magnetron Sputtering of GdBa2Cu3O7ÃƒÆ’Ã‚Â¢Ãƒâ€¹Ã¢â‚¬Â 'ÃƒÆ’Ã…Â½Ãƒâ€šÃ‚Â´/ La0.67Sr0.33MnO3 Quasi-bilayer Films on SrTiO3 STO Single-crystal Substrates

Here, we demonstrate a method of coating ferromagnetic La0.67Sr0.33MnO3 (LSMO) nanoparticles on (001) SrTiO3 (STO) single-crystal substrates by radio ...