Name: chemical precipitation method for the synthesis of nb2o5 modified bulk nickel catalysts with high specific surface area
Uploaded: 2018-02-19T15:00:00
Description: Watch this Scientific Journal Video about Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area at JoVE.com

We gratefully acknowledge the financial support provided by National Key Research &#38; Development Program of the Ministry of Science and Technology of China (2016YFB0600305), National Natural Science Foundation of China (Nos. 21573031 and 21373038), Program for Excellent Talents in Dalian City (2016RD09) and Technological and Higher Education Institute of Hong Kong (THEi SG1617105 and THEi SG1617127).

Caution: For the proper handling methods, properties and toxicities of the chemicals described in this paper, refer to the relevant material safety data sheets (MSDS). Some of the chemicals used are toxic and carcinogenic and special cares must be taken. Nanomaterials may potentially pose safety hazards and health effects. Inhalation and skin contact should be avoided. Safety precaution must be exercised, such as performing the catalyst synthesis in the fume hood and catalyst performance evaluation with ...

<ol>
	<li>Zhou, Y., Yang, M., Sun, K., Tang, Z., Kotov, N. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Similar+topological+origin+of+chiral+centers+in+organic+and+nanoscale+inorganic+structures:+effect+of+stabilizer+chirality+on+optical+isomerism+and+growth+of+CdTe+nanocrystals.">Similar topological origin of chiral centers in organic and nanoscale inorganic structures: effect of stabilizer chirality on optical isomerism and growth of CdTe nanocrystals.</a> J. Am. Chem. Soc. 132 (17), 6006-6013 (2010).</li><li>Zhou, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Optical+Coupling+Between+Chiral+Biomolecules+and+Semiconductor+Nanoparticles:+Size-Dependent+Circular+Dichroism+Absorption.">Optical Coupling Between Chiral Biomolecules and Semiconductor Nanoparticles: Size-Dependent Circular Dichroism Absorption.</a> Angew. Chem. Int. Ed. 50, 11456-11459 (2011).</li><li>Li, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Reversible+plasmonic+circular+dichroism+of+Au+nanorod+and+DNA+assemblies.">Reversible plasmonic circular dichroism of Au nanorod and DNA assemblies.</a> J. Am. Chem. Soc. 134 (7), 3322-3325 (2012).</li><li>Zhu, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Manipulation+of+collective+optical+activity+in+one-dimensional+plasmonic+assembly.">Manipulation of collective optical activity in one-dimensional plasmonic assembly.</a> ACS Nano. 6 (3), 2326-2332 (2012).</li><li>Liu, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Gold+nanorod@chiral+mesoporous+silica+core-shell+nanoparticles+with+unique+optical+properties.">Gold nanorod@chiral mesoporous silica core-shell nanoparticles with unique optical properties.</a> J. Am. Chem. Soc. 135 (26), 9659-9664 (2013).</li><li>Han, B., Zhu, Z., Li, Z., Zhang, W., Tang, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Conformation+Modulated+Optical+Activity+Enhancement+in+Chiral+Cysteine+and+Au+Nanorod+Assemblies.">Conformation Modulated Optical Activity Enhancement in Chiral Cysteine and Au Nanorod Assemblies.</a> J. Am. Chem. Soc. 136, 16104-16107 (2014).</li><li>Rao, C. N. R., Gopalakrishnan, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=.">.</a> New Directions in Solid State Chemistry. , (1989).</li><li>Zhu, H., Rosenfeld, D. C., Anjum, D. H., Caps, V., Basset, J. -. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Green+Synthesis+of+Ni-Nb+Oxide+Catalysts+for+Low-Temperature+Oxidative+Dehydrogenation+of+Ethane.">Green Synthesis of Ni-Nb Oxide Catalysts for Low-Temperature Oxidative Dehydrogenation of Ethane.</a> ChemSusChem. 8, 1254-1263 (2015).</li><li>Heracleous, E., Lemonidou, A. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ni-Nb-O+Mixed+Oxides+as+Highly+Active+and+Selective+Catalysts+for+Ethene+Production+via+Ethane+Oxidative+Dehydrogenation.+Part+I:+Characterization+and+Catalytic+Performance.">Ni-Nb-O Mixed Oxides as Highly Active and Selective Catalysts for Ethene Production via Ethane Oxidative Dehydrogenation. Part I: Characterization and Catalytic Performance.</a> J. Cat. 237, 162-174 (2006).</li><li>Savova, B., Loridant, S., Filkova, D., Millet, J. M. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ni-Nb-O+Catalysts+for+Ethane+Oxidative+Dehygenation.">Ni-Nb-O Catalysts for Ethane Oxidative Dehygenation.</a> Appl. Catal. A. 390 (1-2), 148-157 (2010).</li><li>Heracleous, E., Delimitis, A., Nalbandian, L., Lemonidou, A. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=HRTEM+Characterization+of+the+Nanostructural+Features+formed+in+Highly+Active+Ni-Nb-O+Catalysts+for+Ethane+ODH.">HRTEM Characterization of the Nanostructural Features formed in Highly Active Ni-Nb-O Catalysts for Ethane ODH.</a> Appl. Catal. A. 325 (2), 220-226 (2007).</li><li>Skoufa, Z., Heracleous, E., Lemonidou, A. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Unraveling+the+Contribution+of+Structural+Phases+in+Ni-Nb-O+mixed+oxides+in+Ethane+Oxidative+Dehydrogenation.">Unraveling the Contribution of Structural Phases in Ni-Nb-O mixed oxides in Ethane Oxidative Dehydrogenation.</a> Catal. Today. 192 (1), 169-176 (2012).</li><li>Heracleous, E., Lemonidou, A. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ni-Me-O+Mixed+Metal+Oxides+for+the+Effective+Oxidative+Dehydrogenation+of+Ethane+to+Ethylene+-+Effect+of+Promoting+Metal+Me.">Ni-Me-O Mixed Metal Oxides for the Effective Oxidative Dehydrogenation of Ethane to Ethylene - Effect of Promoting Metal Me.</a> J. Cat. 270, 67-75 (2010).</li><li>Zhu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Nb+Effect+in+the+Nickel+Oxide-Catalyzed+Low-Temperature+Oxidative+Dehydrogenation+of+Ethane.">Nb Effect in the Nickel Oxide-Catalyzed Low-Temperature Oxidative Dehydrogenation of Ethane.</a> J. Cat. 285, 292-303 (2012).</li><li>Sadovskaya, E. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Mixed+Spinel-type+Ni-Co-Mn+Oxides:+Synthesis,+Structure+and+Catalytic+Properties.">Mixed Spinel-type Ni-Co-Mn Oxides: Synthesis, Structure and Catalytic Properties.</a> Catal. Sustain. Energy. 3, 25-31 (2016).</li><li>Alvarez, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ni-Nb-Based+Mixed+Oxides+Precursors+for+the+Dry+Reforming+of+Methane.">Ni-Nb-Based Mixed Oxides Precursors for the Dry Reforming of Methane.</a> Top. Catal. 54, 170-178 (2011).</li><li>Jin, S., Guan, W., Tsang, C. -. W., Yan, D. Y. S., Chan, C. -. Y., Liang, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Enhanced+hydroconversion+of+lignin-derived+oxygen-containing+compounds+over+bulk+nickel+catalysts+though+Nb2O5+modification.">Enhanced hydroconversion of lignin-derived oxygen-containing compounds over bulk nickel catalysts though Nb2O5 modification.</a> Catal. Lett. 147, 2215-2224 (2017).</li><li>Taghavinezhad, P., Haghighi, M., Alizadeh, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=CO2/O2-oxidative+dehydrogenation+of+ethane+to+ethylene+over+highly+dispersed+vanadium+oxide+on+MgO-promoted+sulfated-zirconia+nanocatalyst:+Effect+of+sulfation+on+catalytic+properties+and+performance.">CO2/O2-oxidative dehydrogenation of ethane to ethylene over highly dispersed vanadium oxide on MgO-promoted sulfated-zirconia nanocatalyst: Effect of sulfation on catalytic properties and performance.</a> Korean J. Chem. Eng. 34 (5), 1346-1357 (2017).</li><li>Muralidharan, G., Subramanian, L., Nallamuthu, S. K., Santhanam, V., Kumar, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Effect+of+Reagent+Addition+Rate+and+Temperature+on+Synthesis+of+Gold+Nanoparticles+in+Microemulsion+Route.">Effect of Reagent Addition Rate and Temperature on Synthesis of Gold Nanoparticles in Microemulsion Route.</a> Ind. Eng. Chem. Res. 50 (14), 8786-8791 (2011).</li><li>Sosa, Y. D., Rabelero, M., Trevi&#241;o, M. E., Saade, H., L&#243;pez, R. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-Yield+Synthesis+of+Silver+Nanoparticles+by+Precipitation+in+a+High-Aqueous+Phase+Content+Reverse+Microemulsion.">High-Yield Synthesis of Silver Nanoparticles by Precipitation in a High-Aqueous Phase Content Reverse Microemulsion.</a> J. Nanomater. , 1-6 (2010).</li><li>Morterra, C., Cerrato, G., Pinna, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Infrared+spectroscopic+study+of+surface+species+and+of+CO+adsorption:+a+probe+for+the+surface+characterization+of+sulfated+zirconia+catalysts.">Infrared spectroscopic study of surface species and of CO adsorption: a probe for the surface characterization of sulfated zirconia catalysts.</a> Spectrochim. Acta. A Molecul. Biomolecul. Spectrosc. 55, 95-107 (1998).</li><li>Yang, F., Wang, Q., Yan, J., Fang, J., Zhao, J., Shen, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Preparation+of+High+Pore+Volume+Pseudoboehmite+Doped+with+Transition+Metal+Ions+through+Direct+Precipitation+Method.">Preparation of High Pore Volume Pseudoboehmite Doped with Transition Metal Ions through Direct Precipitation Method.</a> Ind. Eng. Chem. Res. 51 (47), 15386-15392 (2012).</li><li>Saleh, R., Djaja, N. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Transition-metal-doped+ZnO+nanoparticles:+Synthesis,+characterization+and+photocatalytic+activity+under+UV+light.">Transition-metal-doped ZnO nanoparticles: Synthesis, characterization and photocatalytic activity under UV light.</a> Spectrochim. Acta. A Molecul. Biomolecul. Spectrosc. 130, 581-590 (2014).</li><li>Ertis, I. F., Boz, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+Characterization+of+Metal-Doped+(Ni,+Co,+Ce,+Sb)+CdS+Catalysts+and+Their+Use+in+Methylene+Blue+Degradation+under+Visible+Light+Irradiation.">Synthesis and Characterization of Metal-Doped (Ni, Co, Ce, Sb) CdS Catalysts and Their Use in Methylene Blue Degradation under Visible Light Irradiation.</a> Modern Research in Catalysis. 6, 1-14 (2017).</li><li>Jin, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cleavage+of+Lignin-Derived+4-O-5+Aryl+Ethers+over+Nickel+Nanoparticles+Supported+on+Niobic+Acid-Activated+Carbon+Composites.">Cleavage of Lignin-Derived 4-O-5 Aryl Ethers over Nickel Nanoparticles Supported on Niobic Acid-Activated Carbon Composites.</a> Ind. Eng. Chem. Res. 54 (8), 2302-2310 (2015).</li><li>Rojas, E., Delgado, J. J., Guerrero-P&#233;rez, M. O., Ba&#241;ares, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Performance+of+NiO+and+Ni-Nb-+O+Active+Phases+during+the+Ethane+Ammoxidation+into+Acetonitrile.">Performance of NiO and Ni-Nb- O Active Phases during the Ethane Ammoxidation into Acetonitrile.</a> Catal. Sci. Technol. 3 (12), 3173-3182 (2013).</li><li>Lee, S. -. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Raman+Spectroscopic+Studies+of+Ni-W+Oxide+Thin+Films.">Raman Spectroscopic Studies of Ni-W Oxide Thin Films.</a> Solid State Ionics. 140 (1), 135-139 (2001).</li><li>Mondal, A., Mukherjee, D., Adhikary, B., Ahmed, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cobalt+nanoparticles+as+recyclable+catalyst+for+aerobic+oxidation+of+alcohols+in+liquid+phase.">Cobalt nanoparticles as recyclable catalyst for aerobic oxidation of alcohols in liquid phase.</a> J. Nanopart. Res. 18 (5), 1-12 (2016).</li><li>Wang, K., Yang, L., Zhao, W., Cao, L., Sun, Z., Zhang, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+facile+synthesis+of+copper+nanoparticles+supported+on+an+ordered+mesoporous+polymer+as+an+efficient+and+stable+catalyst+for+solvent-free+sonogashira+coupling+Reactions.">A facile synthesis of copper nanoparticles supported on an ordered mesoporous polymer as an efficient and stable catalyst for solvent-free sonogashira coupling Reactions.</a> Green Chem. 19, 1949-1957 (2017).</li><li>Song, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-Selectivity+Electrochemical+Conversion+of+CO2+to+Ethanol+using+a+Copper+Nanoparticle/N-Doped+Graphene+Electrode.">High-Selectivity Electrochemical Conversion of CO2 to Ethanol using a Copper Nanoparticle/N-Doped Graphene Electrode.</a> Chemistry Select. 1, 6055-6061 (2016).</li></ol>

One of the common methods to prepare the nickel-doped bulk niobium oxide nanoparticles is rotary evaporation method.9 By employing various pressure and temperature conditions during the process of rotary evaporation, the precipitation of Ni-Nb-O particles commerce with the slow removal of the solvent. In contrast to the rotary evaporation method, the chemical precipitation method reported in this study has received increasing attention to prepare the nanoparticles as this do not require the remova...

The preparation of nanocomposites has received increasing attention due to their crucial application in various field. To prepare Ni-Nb-O mixed oxide nanoparticles,1,2,3,4,5,6 different methods have been developed such as dry mixing method,7,8 evaporation method,9,10,11,12,13 sol gel method,14 thermal decomposition method,15 and auto-combustion.16 In a typical evaporation method9, aqueous solutions containing the appropriate amount of metal precursors, nickel nitrate hexahydrate and ammonium niobium oxalate were heated at 70 &#176;C. After the removal of solvent and further drying and calcination, the mixed oxide was obtained. These oxide catalysts exhibit excellent catalytic activity and selectivity towards the oxidative dehydrogenation (ODH) of ethane, which is related to the electronic and structural rearrangement induced by the incorporation of niobium cations in the NiO lattice.11 The insertion of Nb drastically decreases the electrophilic oxygen species, which is responsible for the oxidation reactions of ethane12. As a result, extensions of this method have been done on the preparation of different types of mixed Ni-Me-O oxides, where Me = Li, Mg, Al, Ga, Ti and Ta.13 It is found that the variation of metal dopants could alter the unselective and electrophilic oxygen radicals of NiO, thus systematically tune the ODH activity and selectivity towards ethane. However, generally the surface area of these oxides is relatively small (&#60; 100 m2/g), due to the extended phase segregation and formation of large Nb2O5 crystallites, and thus hampered their uses in other catalytic applications.
Dry mixing method, also known as the solid-state grinding method, is another commonly used method to prepare the mixed-oxide catalysts. Since the catalytic materials are obtained in a solvent-free way, this method provides a promising green and sustainable alternative to the preparation of mixed-oxide. The highest surface area obtained by this method is 172 m2/g for Ni80Nb20 at calcination temperature of 250 &#176;C.8 However, this solid-state method is not reliable as reactants are not well mixed on the atomic scale. Therefore, for better control of chemical homogeneity and specific particle size distribution and morphology, other suitable methods to prepare Ni-Nb-O mixed oxide nanoparticles are still being sought.7
Among various strategies in the development of nanoparticles, chemical precipitation serves as one of the promising methods to develop the nanocatalysts, since it allows the complete precipitation of the metal ions. Also, nanoparticles of higher surface areas are commonly prepared by using this method. To improve the catalytic properties of Ni-Nb-O nanoparticles, we herein report the protocol for the synthesis of a series of Ni-Nb-O mixed oxide catalysts with high surface area by chemical precipitation method. We demonstrated that the Nb:Ni molar ratio is a crucial factor in determining the catalytic activity of the oxides towards the hydrodeoxygenation of lignin-derived organic compounds. With high Nb:Ni ratio above 0.087, inactive NiNb2O6 species were formed. Ni0.92Nb0.08O, which had the largest surface area (173 m2/g), exhibits fold-like nanosheets structures and showed the best activity and selectivity towards the hydrodeoxygenation of anisole to cyclohexane.

<table>
	<tbody>
		<tr>
			<td>Niobium(V) oxalate hydrate, 98%</td>
			<td>Alfa</td>
			<td>L04481902</td>
			<td></td>
		</tr>
		<tr>
			<td>Nickel nitrate hexahydrate, 99%</td>
			<td>Aladdin</td>
			<td>N108891</td>
			<td></td>
		</tr>
		<tr>
			<td>Sodium hydroxide, 98%</td>
			<td>Aladdin</td>
			<td>S111501</td>
			<td></td>
		</tr>
		<tr>
			<td>Ammonium hydroxide, 23-25%</td>
			<td>Aladdin</td>
			<td>A112077</td>
			<td></td>
		</tr>
		<tr>
			<td>Anisole, 99%</td>
			<td>Sinopharm</td>
			<td>81001728</td>
			<td></td>
		</tr>
		<tr>
			<td>Diphenyl ether, 98%</td>
			<td>Aladdin</td>
			<td>D110644</td>
			<td></td>
		</tr>
		<tr>
			<td>Phenol, 98%</td>
			<td>Sinopharm</td>
			<td>100153008</td>
			<td></td>
		</tr>
		<tr>
			<td>2-Methoxyphenol, 98%</td>
			<td>Sinopharm</td>
			<td>30114526</td>
			<td></td>
		</tr>
		<tr>
			<td>Vanillin, 99.5%</td>
			<td>Sinopharm</td>
			<td>69024316</td>
			<td></td>
		</tr>
		<tr>
			<td>Potassium hydroxide, AR</td>
			<td>Aladdin</td>
			<td>P112284</td>
			<td></td>
		</tr>
		<tr>
			<td>N,N-Dimethylformamide, 99.5%</td>
			<td>Sinopharm</td>
			<td>40016462</td>
			<td></td>
		</tr>
		<tr>
			<td>2-Bromoacetophenone,98%</td>
			<td>Aladdin</td>
			<td>B103328</td>
			<td></td>
		</tr>
		<tr>
			<td>Diethyl ether,99.5%</td>
			<td>Sinopharm</td>
			<td>10009318</td>
			<td></td>
		</tr>
		<tr>
			<td>Decane,98%</td>
			<td>Aladdin</td>
			<td>D105231</td>
			<td></td>
		</tr>
		<tr>
			<td>Dodecane,99%</td>
			<td>Aladdin</td>
			<td>D119697</td>
			<td></td>
		</tr>
		<tr>
			<td>Niobic acid</td>
			<td>CBMM</td>
			<td>1313968</td>
			<td></td>
		</tr>
		<tr>
			<td>Heating and Drying Oven</td>
			<td></td>
			<td></td>
			<td>DHG Series (shanghai jinghong laboratory instrument co. ltd)</td>
		</tr>
		<tr>
			<td>Autoclave Reactor</td>
			<td></td>
			<td></td>
			<td>CJF-0.05&#8212;0.1L (Dalian Tongda Equipment Technology Development Co., Ltd)</td>
		</tr>
		<tr>
			<td>Tube&#160;furnace</td>
			<td></td>
			<td></td>
			<td>SK2-1-10/12 (Luoyang Huaxulier Electric Stove Co., Ltd)</td>
		</tr>
		<tr>
			<td>Heating magnetic stirrer</td>
			<td></td>
			<td></td>
			<td>DF-101 (Yu Hua Instrument Co. Ltd.)</td>
		</tr>
		<tr>
			<td>Rotary evaporator</td>
			<td></td>
			<td></td>
			<td>RE-3000A (Shanghai Yarong Biochemical Instrument Factory)</td>
		</tr>
		<tr>
			<td>Synthetic air</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Hydrogen gas</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>Argon gas</td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
	</tbody>
</table>

chemical precipitation method for the synthesis of nb2o5 modified bulk nickel catalysts with high specific surface area

We demonstrate a method for the synthesis of NixNb1-xO catalysts with sponge-like and fold-like nanostructures. By varying the Nb:Ni ratio, a series of NixNb1-xO nanoparticles with different atomic compositions (x = 0.03, 0.08, 0.15, and 0.20) have been prepared by chemical precipitation. These NixNb1-xO catalysts are characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and scanning electron microscopy. The study revealed the sponge-like and fold-like appearance of Ni0.97Nb0.03O and Ni0.92Nb0.08O on the NiO surface, and the larger surface area of these NixNb1-xO catalysts, compared with the bulk NiO. Maximum surface area of 173 m2/g can be obtained for Ni0.92Nb0.08O catalysts. In addition, the catalytic hydroconversion of lignin-derived compounds using the synthesized Ni0.92Nb0.08O catalysts have been investigated.

X-ray diffraction (XRD) patterns (Figure 1 and Figure 2), BET surface areas, temperature-programmed reduction of hydrogen with hydrogen (H2-TPR), scanning electron microscopy (SEM) equipped with an energy-dispersive X-ray (EDX) analyzer, X-ray photoelectron spectroscopy (XPS) were collected for the nanoparticles NiO, Ni-Nb-O and Nb2O5 oxides17 (Figure 3...

Watch this Scientific Journal Video about Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area at JoVE.com

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area

A protocol for the synthesis of sponge-like and fold-like Ni1-xNbxO nanoparticles by chemical precipitation is presented.

Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area

We demonstrate a method for the synthesis of NixNb1-xO catalysts with sponge-like and fold-like nanostructures. By varying the Nb:Ni ratio, a series of ...

The overall goal of this chemical precipitation technique is to prepare niobium oxide modified nickel catalysts with high specific surface area for hydro conversion of lignin derived compounds. This method can help answer key questions in the nano-material fields, such as how the modified pore size and surface areas of nano-materials for catalytic applications. The main advantage of this technique is that the chemical precipitation methods allow the uniform dispersion of metal components and can be readily used to prepare nano-particles with relatively larger surface areas.The implications of this technique extend toward the development of NiNbO catalysts because it can provide a simple strategy to effectively improve the structures and the catalytic properties of nano-materials. Generally, individuals new to this method will struggle because the preparation procedure is quite different from other conventional methods, such as dry mixing and the evaporation method. To begin preparing the nickel niobium oxide catalyst with a molar ratio of niobium to nickel plus niobium at 0.03, add 100 milliliters of deionized water to a 250 milliliter three neck, round-bottom flask equipped with a stir bar.Add 0.4 grams of niobium five oxalate hydrate and 0.7 grams of nickel nitrate. Use a heating magnetic stir to heat the solution to 70 degrees Celsius, while stirring at 50 RPM, until the precipitate disappears. After this, raise the temperature to 80 degrees Celsius, at a rate of two degrees Celsius per minute.Add a mixed basic solution containing aqueous ammonium hydroxide and sodium hydroxide to the reaction mixture drop wise until the Ph reaches 9.0. While stirring, raise the temperature to 120 degrees Celsius at a rate of two degrees Celsius per minute. This step is especially difficult to learn because constant control must be maintained over both the rate at which the basic solution is added and at the solution's page.Stir the solution overnight at 50 RPM and 120 degrees Celsius until the green color has completely disappeared from the solution. Then use inductively coupled plasma optical emissions spectroscopy to ensure that the remaining nickel nitrate has precipitated completely. Using a buchner flask, filter the solution to collect the solid.Wash the solid with deionized water repeatedly for 20 minutes. Collect the washed solid in a watch glass. Use a dry oven to dry the solid for 12 hours at 110 degrees Celsius.Then use a tube furnace to calcine the solids in synthetic air at 450 degrees Celsius for five hours. After this collect one gram of the prepared catalyst. To begin, transfer one gram of the nickel niobium oxide catalyst to the tube furnace and reduce them in a hydrogen atmosphere at 400 degrees Celsius for two hours.After this, passivate the reduced cyclist under argon overnight. The next day, dissolve 1.1712 grams of anesol and 0.2928 grams of n-dodecane in 20 milliliters of n-decane resulting in an internal standard to be used during quantitative gas chromatography analysis. Quickly transfer the reduced catalyst to the autoclave reactor, avoiding prolonged exposure with air.Seal the reactor and purge with hydrogen gas repeatedly at three MPA. Then set the reactor to atmospheric pressure and the stirring speed to 700 RPM. Begin heating to the desired temperature at a rate of two degrees Celsius per minute.After this, cool and analyze the deoxygenated products as outlined in the text protocol. In this study, nickel niobium oxide catalysts with various atomic compositions are synthesized. X-ray diffraction analysis for the mixed oxide formed by nickel nitrate and hydrated niobium five oxalate corresponds with that observed for hydrated nickel oxalate.Similarly, the peaks observed in the precipitate, after calcination for two hours at 700 degrees Celsius, correspond to those seen in nickel niobate's crystalline phase. X-ray diffraction analysis of the synthesized nanoparticles, after calcination for five hours at 450 degrees Celsius, reveals main diffraction peaks that correspond to those seen in the crystalline nickel two oxide. However, analysis after calcination at 700 degrees Celsius reveals peaks corresponding to the mixed phase, indicating the existence of an amorphous phase after calcination at 450 degrees Celsius which were not present in the nickel niobium composite phase.Next, scanning electron microscopy analysis is performed. While pure nickel two oxide is seen to have a well-defined nanosheet crystalline structure, the synthesized nanoparticles have a foam-like and sponge-like appearance. Once mastered, this technique for catalyst preparation can be done in 48 hours, if it is performed properly.While attempting this procedure, it's important to remember to monitor the Ph using a calibrated Ph meter and to carefully control the rate of addition of the base. Following this procedure, we can prepare catalyst with different metal standards in order to answer additional questions like how to optimize the hydro conversions of anesol. Though this method can provide insight into the development of catalysts for hydro deoxygenation of anesol, it can also be applied to prepare other mixed matter, nano-materials for different catalytic processes.This technique paves the way for researchers in the field of nano-technologies to use chemical precipitation methods to synthesize niobium five oxide modified nickel with different surface areas and the applications in the hydro conversion process. After watching this video, you should have a good understanding of how to carefully prepare the catalyst to obtain high specific surface area by a chemical precipitation method. Don't forget that working with hydronized niobium oxinades can be extremely toxic and in addition the sodium hydroxide autoclave reactor require careful handling.

chemical-precipitation-method-for-synthesis-nb2o5-modified-bulk

Research

JoVE Journal

Chemistry

Gyroid Nickel Nanostructures from Diblock Copolymer Supramolecules

Nanoporous metal foams possess a unique combination of properties - they are catalytically active, thermally and electrically conductive, and furthermore, have high porosity, high surface-to-volume and strength-to-weight ratio. Unfortunately, common approaches for preparation of metallic nanostructures render materials with highly disordered architecture, which might have an adverse effect on their mechanical properties. Block copolymers have the ability to self-assemble into ordered nanostructures and can be applied as templates for the preparation of well-ordered metal nanofoams. Here we describe the application of a block copolymer-based supramolecular complex - polystyrene-block-poly(4-vinylpyridine)(pentadecylphenol) PS-b-P4VP(PDP) - as a precursor for well-ordered nickel nanofoam. The supramolecular complexes exhibit a phase behavior similar to conventional block copolymers and can self-assemble into the bicontinuous gyroid morphology with two PS networks placed in a P4VP(PDP) matrix. PDP can be dissolved in ethanol leading to the formation of a porous structure that can be backfilled with metal. Using electroless plating technique, nickel can be inserted into the template&#39;s channels. Finally, the remaining polymer can be removed via pyrolysis from the polymer/inorganic nanohybrid resulting in nanoporous nickel foam with inverse gyroid morphology.

This article describes the preparation of well-ordered nickel nanofoams via electroless metal deposition onto nanoporous templates obtained from self-assembled diblock copolymer based supramolecules.

Nanoporous metal foams possess a unique combination of properties - they are catalytically active, thermally and electrically conductive, and furthermore, ...

A Method to Manipulate Surface Tension of a Liquid Metal via Surface Oxidation and Reduction

Controlling interfacial tension is an effective method for manipulating the shape, position, and flow of fluids at sub-millimeter length scales, where interfacial tension is a dominant force. A variety of methods exist for controlling the interfacial tension of aqueous and organic liquids on this scale; however, these techniques have limited utility for liquid metals due to their large interfacial tension.
Liquid metals can form soft, stretchable, and shape-reconfigurable components in electronic and electromagnetic devices. Although it is possible to manipulate these fluids via mechanical methods (e.g., pumping), electrical methods are easier to miniaturize, control, and implement. However, most electrical techniques have their own constraints: electrowetting-on-dielectric requires large (kV) potentials for modest actuation, electrocapillarity can affect relatively small changes in the interfacial tension, and continuous electrowetting is limited to plugs of the liquid metal in capillaries.
Here, we present a method for actuating gallium and gallium-based liquid metal alloys via an electrochemical surface reaction. Controlling the electrochemical potential on the surface of the liquid metal in electrolyte rapidly and reversibly changes the interfacial tension by over two orders of magnitude ( &#820;500 mN/m to near zero). Furthermore, this method requires only a very modest potential (&#60; 1 V) applied relative to a counter electrode. The resulting change in tension is due primarily to the electrochemical deposition of a surface oxide layer, which acts as a surfactant; removal of the oxide increases the interfacial tension, and vice versa. This technique can be applied in a wide variety of electrolytes and is independent of the substrate on which it rests.

We present a method to control the interfacial energy of a liquid metal in an electrolyte via electrochemical deposition (or removal) of a surface oxide layer. This simple method can control the capillary behavior of gallium-based liquid metals by tuning the interfacial energy rapidly, significantly, and reversibly using modest voltages.

Controlling interfacial tension is an effective method for manipulating the shape, position, and flow of fluids at sub-millimeter length scales, where ...

Protocol for the Synthesis of Ortho-trifluoromethoxylated Aniline Derivatives

Molecules bearing trifluoromethoxy (OCF3) group often show desired pharmacological and biological properties. However, facile synthesis of trifluoromethoxylated aromatic compounds remains a formidable challenge in organic synthesis. Conventional approaches often suffer from poor substrate scope, or require use of highly toxic, difficult-to-handle, and/or thermally labile reagents. Herein, we report a user-friendly protocol for the synthesis of methyl 4-acetamido-3-(trifluoromethoxy)benzoate using 1-trifluoromethyl-1,2-benziodoxol-3(1H)-one (Togni reagent II). Treating methyl 4-(N-hydroxyacetamido)benzoate (1a) with Togni reagent II in the presence of a catalytic amount of cesium carbonate (Cs2CO3) in chloroform at RT afforded methyl 4-(N-(trifluoromethoxy)acetamido)benzoate (2a). This intermediate was then converted to the final product methyl 4-acetamido-3-(trifluoromethoxy)benzoate (3a) in nitromethane at 120 &#176;C. This procedure is general and can be applied to the synthesis of a broad spectrum of ortho-trifluoromethoxylated aniline derivatives, which could serve as useful synthetic building blocks for the discovery and development of new pharmaceuticals, agrochemicals, and functional materials.

Protocol for the Synthesis of Ortho-trifluoromethoxylated Aniline Derivatives

An operationally simple procedure for the synthesis of ortho-trifluoromethoxylated aniline derivatives via a two-step sequence of O-trifluoromethylation of N-aryl-N-hydroxyacetamide followed by thermally induced intramolecular OCF3-migration is reported.

Molecules bearing trifluoromethoxy (OCF3) group often show desired pharmacological and biological properties. However, facile synthesis of ...

Facile Synthesis of Worm-like Micelles by Visible Light Mediated Dispersion Polymerization Using Photoredox Catalyst

Presented herein is a protocol for the facile synthesis of worm-like micelles by visible light mediated dispersion polymerization. This approach begins with the synthesis of a hydrophilic poly(oligo(ethylene glycol) methyl ether methacrylate) (POEGMA) homopolymer using reversible addition-fragmentation chain-transfer (RAFT) polymerization. Under mild visible light irradiation (&#955; = 460 nm, 0.7 mW/cm2), this macro-chain transfer agent (macro-CTA) in the presence of a ruthenium based photoredox catalyst, Ru(bpy)3Cl2 can be chain extended with a second monomer to form a well-defined block copolymer in a process known as Photoinduced Electron Transfer RAFT (PET-RAFT). When PET-RAFT is used to chain extend POEGMA with benzyl methacrylate (BzMA) in ethanol (EtOH), polymeric nanoparticles with different morphologies are formed in situ according to a polymerization-induced self-assembly (PISA) mechanism. Self-assembly into nanoparticles presenting POEGMA chains at the corona and poly(benzyl methacrylate) (PBzMA) chains in the core occurs in situ due to the growing insolubility of the PBzMA block in ethanol. Interestingly, the formation of highly pure worm-like micelles can be readily monitored by observing the onset of a highly viscous gel in situ due to nanoparticle entanglements occurring during the polymerization. This process thereby allows for a more reproducible synthesis of worm-like micelles simply by monitoring the solution viscosity during the course of the polymerization. In addition, the light stimulus can be intermittently applied in an ON/OFF manner demonstrating temporal control over the nanoparticle morphology.

This article describes a process for producing polymeric self-assembled nanoparticles using visible light mediated dispersion polymerization. Using low energy visible light to control the polymerization allows for the reproducible formation of self-assembled worm-like micelles at high solids content.

Presented herein is a protocol for the facile synthesis of worm-like micelles by visible light mediated dispersion polymerization. This approach begins ...

Synthesis and Testing of Supported Pt-Cu Solid Solution Nanoparticle Catalysts for Propane Dehydrogenation

A convenient method for the synthesis of bimetallic Pt-Cu catalysts and performance tests for propane dehydrogenation and characterization are demonstrated here. The catalyst forms a substitutional solid solution structure, with a small and uniform particle size around 2 nm. This is realized by careful control over the impregnation, calcination, and reduction steps during catalyst preparation and is identified by advanced in situ synchrotron techniques. The catalyst propane dehydrogenation performance continuously improves with increasing Cu:Pt atomic ratio.

A convenient method for the synthesis of 2 nm supported bimetallic nanoparticle Pt-Cu catalysts for propane dehydrogenation is reported here. In situ synchrotron X-ray techniques allow for the determination of the catalyst structure, which is typically unobtainable using laboratory instruments.

A convenient method for the synthesis of bimetallic Pt-Cu catalysts and performance tests for propane dehydrogenation and characterization are ...

Synthesis of Platinum-nickel Nanowires and Optimization for Oxygen Reduction Performance

Platinum-nickel (Pt-Ni) nanowires were developed as fuel cell electrocatalysts, and were optimized for the performance and durability in the oxygen reduction reaction. Spontaneous galvanic displacement was used to deposit Pt layers onto Ni nanowire substrates. The synthesis approach produced catalysts with high specific activities and high Pt surface areas. Hydrogen annealing improved Pt and Ni mixing and specific activity. Acid leaching was used to preferentially remove Ni near the nanowire surface, and oxygen annealing was used to stabilize near-surface Ni, improving durability and minimizing Ni dissolution. These protocols detail the optimization of each post-synthesis processing step, including hydrogen annealing to 250 &#176;C, exposure to 0.1 M nitric acid, and oxygen annealing to 175 &#176;C. Through these steps, Pt-Ni nanowires produced increased activities more than an order of magnitude than Pt nanoparticles, while offering significant durability improvements. The presented protocols are based on Pt-Ni systems in the development of fuel cell catalysts. These techniques have also been used for a variety of metal combinations, and can be applied to develop catalysts for a number of electrochemical processes.

&#160; The protocol describes the synthesis and electrochemical testing of platinum-nickel nanowires. Nanowires were synthesized by the galvanic displacement of a nickel nanowire template. Post-synthesis processing, including hydrogen annealing, acid leaching, and oxygen annealing were used to optimize nanowire performance and durability in the oxygen reduction reaction.

Platinum-nickel (Pt-Ni) nanowires were developed as fuel cell electrocatalysts, and were optimized for the performance and durability in the oxygen ...

Synthesis of Substrate-Bound Au Nanowires Via an Active Surface Growth Mechanism

Advancing synthetic capabilities is important for the development of nanoscience and nanotechnology. The synthesis of nanowires has always been a challenge, as it requires asymmetric growth of symmetric crystals. Here, we report a distinctive synthesis of substrate-bound Au nanowires. This template-free synthesis employs thiolated ligands and substrate adsorption to achieve the continuous asymmetric deposition of Au in solution at ambient conditions. The thiolated ligand prevented the Au deposition on the exposed surface of the seeds, so the Au deposition only occurs at the interface between the Au seeds and the substrate. The side of the newly deposited Au nanowires is immediately covered with the thiolated ligand, while the bottom facing the substrate remains ligand-free and active for the next round of Au deposition. We further demonstrate that this Au nanowire growth can be induced on various substrates, and different thiolated ligands can be used to regulate the surface chemistry of the nanowires. The diameter of the nanowires can also be controlled with mixed ligands, in which another &#34;bad&#34; ligand could turn on the lateral growth. With the understanding of the mechanism, Au nanowire-based nanostructures can be designed and synthesized.

We report a solution-based method to synthesize substrate-bound Au nanowires. By tuning the molecular ligands used during the synthesis, the Au nanowires can be grown from various substrates with different surface properties. Au nanowire-based nanostructures can also be synthesized by adjusting the reaction parameters.

Advancing synthetic capabilities is important for the development of nanoscience and nanotechnology. The synthesis of nanowires has always been a ...

Synthesis and Bioconjugation of Thiol-Reactive Reagents for the Creation of Site-Selectively Modified Immunoconjugates

Maleimide-bearing bifunctional probes have been employed for decades for the site-selective modification of thiols in biomolecules, especially antibodies. Yet maleimide-based conjugates display limited stability in vivo because the succinimidyl thioether linkage can undergo a retro-Michael reaction. This, of course, can lead to the release of the radioactive payload or its exchange with thiol-bearing biomolecules in circulation. Both of these processes can produce elevated activity concentrations in healthy organs as well as decreased activity concentrations in target tissues, resulting in reduced imaging contrast and lower therapeutic ratios. In 2018, we reported the creation of a modular, stable, and easily accessible phenyloxadiazolyl methyl sulfone reagent &#8212; dubbed &#8216;PODS&#8217; &#8212; as a platform for thiol-based bioconjugations. We have clearly demonstrated that PODS-based site-selective bioconjugations reproducibly and robustly create homogenous, well-defined, highly immunoreactive, and highly stable radioimmunoconjugates. Furthermore, preclinical experiments in murine models of colorectal cancer have shown that these site-selectively labeled radioimmunoconjugates exhibit far superior in vivo performance compared to radiolabeled antibodies synthesized via maleimide-based conjugations. In this protocol, we will describe the four-step synthesis of PODS, the creation of a bifunctional PODS-bearing variant of the ubiquitous chelator DOTA (PODS-DOTA), and the conjugation of PODS-DOTA to the HER2-targeting antibody trastuzumab.

In this protocol, we will describe the synthesis of PODS, a phenyoxadiazolyl methyl sulfone-based reagent for the site-selective attachment of cargos to the thiols of biomolecules, particularly antibodies. In addition, we will describe the synthesis and characterization of a PODS-bearing bifunctional chelator and its conjugation to a model antibody.

Maleimide-bearing bifunctional probes have been employed for decades for the site-selective modification of thiols in biomolecules, especially antibodies. ...

Imine Metathesis by Silica-Supported Catalysts Using the Methodology of Surface Organometallic Chemistry

With this protocol, a well-defined singlesite silica-supported heterogeneous catalyst [(&#8801;Si-O-)Hf(=NMe)(&#951;1-NMe2)] is designed and prepared according to the methodology developed by surface organometallic chemistry (SOMC). In this framework, catalytic cycles can be determined by isolating crucial intermediates. All air-sensitive materials are handled under inert atmosphere (using gloveboxes or a Schlenk line) or high vacuum lines (HVLs, &#60;10-5 mbar). The preparation of SiO2-700 (silica dehydroxylated at 700 &#176;C) and subsequent applications (the grafting of complexes and catalytic runs) requires the use of HVLs and double-Schlenk techniques. Several well-known characterization methods are used, such as Fourier-transform infrared spectroscopy (FTIR), elemental microanalysis, solid-state nuclear magnetic resonance spectroscopy (SSNMR), and state-of-the-art dynamic nuclear polarization surface enhanced NMR spectroscopy (DNP-SENS). FTIR and elemental microanalysis permit scientists to establish the grafting and its stoichiometry. 1H and 13C SSNMR allows the structural determination of the hydrocarbon ligands coordination sphere. DNP SENS is an emerging powerful technique in solid characterization for the detection of poorly sensitive nuclei (15N, in our case). SiO2-700 is treated with about one equivalent of the metal precursor compared to the amount of surface silanol (0.30 mmol&#183;g-1) in pentane at room temperature. Then, volatiles are removed, and the powder samples are dried under dynamic high vacuum to afford the desired materials [(&#8801;Si-O-)Hf(&#951;2&#960;-MeNCH2)(&#951;1-NMe2)(&#951;1-HNMe2)]. After a thermal treatment under high vacuum, the grafted complex is converted into metal imido silica complex [(&#8801;Si-O-)Hf(=NMe)(&#951;1-NMe2)]. [(&#8801;Si-O-)Hf(=NMe)(&#951;1-NMe2)] effectively promotes the metathesis of imines, using the combination of two imine substrates, N-(4-phenylbenzylidene)benzylamine, or N-(4-fluorobenzylidene)-4-fluoroaniline, with N-benzylidenetert-butylamine as substrates. A significantly lower conversion is observed with the blank runs; thus, the presence of the imido group in [(&#8801;Si-O-)Hf(=NMe)(&#951;1-NMe2)] is correlated to the catalytic performance.

A new group IV metal catalyst for imine metathesis is prepared by grafting amine metal complex onto dehydroxylated silica. Surface metal fragments are characterized using FT-IR, elemental microanalysis, and solid-state NMR spectroscopy. Further dynamic nuclear polarization surface enhanced NMR spectroscopy experiments complement the determination of the coordination sphere.

With this protocol, a well-defined singlesite silica-supported heterogeneous catalyst [(&#8801;Si-O-)Hf(=NMe)(&#951;1-NMe2)] is designed and prepared ...

Tuning the Acidity of Pt/ CNTs Catalysts for Hydrodeoxygenation of Diphenyl Ether

We herein present a method for the synthesis of HNbWO6, HNbMoO6, HTaWO6 solid acid nanosheet modified Pt/CNTs. By varying the weight of various solid acid nanosheets, a series of Pt/xHMNO6/CNTs with different solid acid compositions (x = 5, 20 wt%; M = Nb, Ta; N = Mo, W) have been prepared by carbon nanotube pretreatment, protonic exchange, solid acid exfoliation, aggregation and finally Pt particles impregnation. The Pt/xHMNO6/CNTs are characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and NH3-temperature programmed desorption. The study revealed that HNbWO6 nanosheets were attached on CNTs, with some edges of the nanosheets being bent in shape. The acid strength of the supported Pt catalysts increases in the following order: Pt/CNTs &#60; Pt/5HNbWO6/CNTs &#60; Pt/20HNbMoO6/CNTs &#60; Pt/20HNbWO6/CNTs &#60; Pt/20HTaWO6/CNTs. In addition, the catalytic hydroconversion of lignin-derived model compound: diphenyl ether using the synthesized Pt/20HNbWO6 catalyst has been investigated.

A protocol for the synthesis of HNbWO6, HNbMoO6, HTaWO6 solid acid nanosheet modified Pt/CNTs is presented.

We herein present a method for the synthesis of HNbWO6, HNbMoO6, HTaWO6 solid acid nanosheet modified Pt/CNTs. By varying the weight of various solid acid ...