Synthesis and Reaction Chemistry of Nanosize Monosodium Titanate

This paper describes the synthesis and peroxide-modification of nanosize monosodium titanate (nMST), along with an ion-exchange reaction to load the ...

Savannah River National Laboratory

Fe(III)-carboxylate nanoscale metal-organic frameworks (NMOFs) with the MIL-101 structure were synthesized using a solvothermal technique with microwave heating. The approximately 200 nm particles were characterized using a variety of methods, including SEM, PXRD, nitrogen adsorption measurements, TGA, and EDX. By replacing a percentage of the bridging ligand (terephthalic acid) with 2-amino terephthalic acid, amine groups were incorporated into the framework to provide sites for covalent attachment of biologically relevant cargoes while still maintaining the MIL-101 structure. In proof-of-concept experiments, an optical contrast agent (a BODIPY dye) and an ethoxysuccinato-cisplatin anticancer prodrug were successfully incorporated into the Fe(III)-carboxylate NMOFs via postsynthetic modifications of the as-synthesized particles. These cargoes are released upon the degradation of the NMOF frameworks, and the rate of cargo release was controlled by coating the NMOF particles with a silica shell. Potential utility of the new NMOF-based nanodelivery vehicles for optical imaging and anticancer therapy was demonstrated in vitro using HT-29 human colon adenocarcinoma cells.

Postsynthetic modifications of iron-carboxylate nanoscale metal-organic frameworks for imaging and drug delivery.

Hybrid nanomaterials, composed of both inorganic and organic components, have recently been examined as promising platforms for imaging and therapeutic applications. This unique class of nanomaterials can not only retain beneficial features of both the inorganic and organic components, but also provides the ability to systematically tune the properties of the hybrid material through the combination of functional components. This feature article will summarize recent advances in the design and synthesis of hybrid nanomaterials and their applications in biological and biomedical areas. The hybrid nanomaterials to be discussed fall into two main categories, silica based materials and nanoscale metal-organic frameworks. Their applications as imaging contrast agents and nanotherapeutics will be highlighted.

Hybrid nanomaterials for biomedical applications.

Mesoporous silica nanospheres (MSNs) are a promising material for magnetic resonance imaging (MRI) contrast agents. In this paper multifunctional MSNs with cleavable Gd(III) chelates are synthesized and characterized, and their applicability as MRI contrast agents is demonstrated both in vitro and in vivo. The MSNs contain Gd(III) chelates that are covalently linked via a redox-responsive disulfide moiety. The MSNs are further functionalized with polyethylene glycol (PEG) and an anisamide ligand to improve their biocompatibility and target specificity. The effectiveness of MSNs as an MRI imaging contrast agent and their targeting ability are successfully demonstrated in vitro using human colon adenocarcinoma and pancreatic cancer cells. Finally, the capability of this platform as an in vivo MRI contrast agent is tested using a 3T scanner. The Gd(III) chelate was quickly cleaved by the blood pool thiols and eliminated through the renal excretion pathway. Further tuning of the Gd(III) chelate release kinetics is needed before the MSN system can be used as target-specific MRI contrast agents in vivo.

Multifunctional mesoporous silica nanospheres with cleavable Gd(III) chelates as MRI contrast agents: synthesis, characterization, target-specificity, and renal clearance.

Several mesoporous silica nanoparticle (MSN) contrast agents have been synthesized using a co-condensation method to incorporate two different Gd(3+) complexes at very high loadings (15.5-28.8 wt %). These MSN contrast agents, with an MCM-41 type pore structure, were characterized using a variety of methods including SEM and TEM, nitrogen adsorption measurements, thermogravimetric analysis (TGA), direct current plasma (DCP) spectroscopy, and powder X-ray diffraction (PXRD). The magnetic resonance (MR) relaxivities of these contrast agents were determined using a 3 T MR scanner. The r 1 relaxivities of these nanoparticles range from 4.1 to 8.4 mM(-1)s(-1) on a per Gd basis. Additionally, the MSN particles were functionalized with an organic fluorophore and cancer cell targeting peptide to allow for demonstration of both the optical and MR contrast enhancing capabilities in vitro.

Mesoporous Silica Nanoparticles with Co-Condensed Gadolinium Chelates for Multimodal Imaging.

Previous studies report that microsized monosodium titanates (MSTs) deliver metal ions and species to mammalian cells and bacteria with cell-specific and metal-specific effects. In this study, we explored the use of MST and a new synthesized nanosized monosodium titanate (nMST) to deliver gold(III), cisplatin, or platinum(IV) to two human cell lines with different population doubling times, in vitro. The effect was measured using a fluorescent mitochondrial activity assay (CellTiter-Blue(®) Assay). This fluorescence assay was implemented to mitigate optical density measurement errors owing to particulate titanate interference and allowed for the studies to be extended to higher titanate concentrations than previously possible. Overall, native MST significantly (p < 0.05) decreased mitochondrial activity of both cell types by 50% at concentrations of >50 mg/L. Native nMST significantly suppressed the rapidly dividing cell line (by 50%) over untreated cultures, but had no effect on the more slowly dividing cells. For both cell types, increased titanate concentrations resulted in increased effects from delivered metals. However, there was no difference in the effect of metal delivered from micro- versus nano-sized MST.

Kathryn M. L. Taylor-Pashow

Savannah River National Laboratory

Synthesis and Reaction Chemistry of Nanosize Monosodium Titanate